Medical balloons and methods of making the same
Medical balloons are provided that have enhanced properties, such as thinner walls, enhanced tensile strength, and/or electrical conductivity. Methods are also disclosed.
This disclosure relates to medical balloons, and to methods of making the same.
BACKGROUNDThe body includes various passageways such as arteries, other blood vessels, and other body lumens. These passageways sometimes become occluded, e.g., by a tumor or restricted by plaque. To widen an occluded body vessel, balloon catheters can be used, e.g., in angioplasty.
A balloon catheter can include an inflatable and deflatable balloon carried by a long and narrow catheter body. The balloon is initially folded around the catheter body to reduce the radial profile of the balloon catheter for easy insertion into the body.
During use, the folded balloon can be delivered to a target location in the vessel, e.g., a portion occluded by plaque, by threading the balloon catheter over a guide wire emplaced in the vessel. The balloon is then inflated, e.g., by introducing a fluid into the interior of the balloon. Inflating the balloon can radially expand the vessel so that the vessel can permit an increased rate of blood flow. After use, the balloon is deflated and withdrawn from the body.
In another technique, the balloon catheter can also be used to position a medical device, such as a stent or a stent-graft, to open and/or to reinforce a blocked passageway. For example, the stent can be delivered inside the body by a balloon catheter that supports the stent in a compacted or reduced-size form as the stent is transported to the target site. Upon reaching the site, the balloon can be inflated to deform and to fix the expanded stent at a predetermined position in contact with the lumen wall. The balloon can then be deflated and the catheter withdrawn. Stent delivery is further discussed in Heath, U.S. Pat. No. 6,290,721.
One common balloon catheter design includes a coaxial arrangement of an inner tube surrounded by an outer tube. The inner tube typically includes a lumen that can be used for delivering the device over a guide wire. Inflation fluid passes between the inner and outer tubes. An example of this design is described in Arney et al., U.S. Pat. No. 5,047,045.
In another common design, the catheter includes a body defining a guide wire lumen and an inflation lumen arranged side-by-side. Examples of this arrangement are described in Wang et al., U.S. Pat. No. 5,195,969.
SUMMARYGenerally, medical balloons are disclosed that include a balloon wall that includes a composite material that includes a polymeric material and a filler within the polymeric material. The polymeric material includes a reaction product of a first polymeric material that includes first polymer chains having a plurality of spaced first groups, and a second polymeric material that includes second polymer chains having a plurality of spaced apart second groups that react with the first groups. For example, the first and second groups can react by forming a covalent bond, an ionic bond or mixtures of such bonds. The first and second groups can also react by forming hydrogen bonds.
In one aspect, the disclosure features medical balloons that include a balloon wall that includes a composite material that includes a polymeric material and a filler within the polymeric material. The polymeric material includes a reaction product of a first polymeric material that includes first polymer chains having a plurality of spaced apart carboxylic acid groups, and a second polymeric material that includes second polymer chains having a plurality of spaced apart primary amino groups, hydroxyl groups, thiol groups, or mixtures of these groups. For example, the amino groups, hydroxyl groups and thiol groups can react with the carboxylic acid groups to form, respectively, amide, ester and thioester groups.
In another aspect, the disclosure features medical balloons that include a balloon wall that includes a composite material that includes a polymeric material and a filler within the polymeric material. The composite polymeric material has a conductivity of greater than 40 S/cm. For example, such a balloon can be used therapeutically to treat a lumen with, or as a result of, an electrical current.
In another aspect, the disclosure features medical balloons that include a balloon wall that includes a composite material that includes a polymeric material and a filler within the polymeric material. The composite polymeric material has a tensile strength of greater than 40 MPa. For example, a high tensile strength can allow for thin and ultra-thin cross-sections.
In another aspect, the disclosure features a medical balloon that includes chitosan and/or a reaction product of chitosan and another polymer, such as a polymer having carboxylic acid groups or another electrophilic group, such as an isocyanate group.
Embodiments of the medical balloons can have one or more of the following features. The first polymeric material is or includes polyacrylic acid, polymethacrylic acid, poly(ethylene-co-acrylic acid), poly(2-ethylacrylic acid), poly(2-propylacrylic acid), melt blends of any of these or copolymers of any of these. The first polymeric material is or includes polyacrylic acid. The second polymeric material is or includes chitosan, poly[dimethylsiloxane-co-(3-aminopropyl)methylsiloxane], polyvinyl alcohol, poly(vinyl alcohol-co-vinyl acetate), poly(styrene-co-allyl alcohol), melt blends of any of these or copolymers of any of these. The second polymeric material is or includes chitosan. The first polymer chains each have between about 6 and about 10,000 carboxylic acid groups. A total number of primary amino groups, hydroxyl groups and/or thiol groups combined on each of the second polymer chains is between about 6 and about 10,000. A number average molecular weight of the first polymeric material is between about 2,500 and about 350,000, measured relative to polyethylene glycol standards in tetrahydrofuran, chloroform or chlorobenzene. A number average molecular weight of the second polymeric material is between about 2,500 and about 350,000, measured relative to polyethylene glycol standards in tetrahydrofuran, chloroform or chlorobenzene. The filler has a maximum dimension of less than 1000 nm. The filler is or includes allotropes of carbon, allotropes of carbon functionalized with hydrogen bonding groups (e.g., hydrogen bond acceptors and/or donors), metals, metal oxides, metalloid oxides, clays, ceramics or mixtures of any of these. The filler is or includes tubular structures made substantially of carbon. The tubular structures each have a single wall. The filler is or includes structures having hydrogen-bonding groups (e.g., acceptors and/or donors) extending from an outer portion of each structure. Each structure is more than 95 percent by weight carbon. The filler is dispersed substantially homogenously throughout the polymeric material. The filler is arranged in discrete longitudinal layers through a thickness of the composite material. The filler is or includes structures substantially spherical in shape, each having a diameter of less than 1000 nm. The filler is or includes a polymeric filler different from the first or second polymeric material, or the reaction product. The reaction product is or includes an ionic complex between the first and second polymeric materials. The reaction product is or includes an acid base complex of the first and second polymeric materials. The reaction product is or includes reacted first chains covalently bonded to reacted second chains by amide, ester or thioester bonds. The reacted first polymer chains are intermingled with reacted second polymer chains throughout a thickness of the composite material. The composite material is or includes a first layer comprising reacted first polymeric material, and a second layer comprising reacted second polymeric material having filler dispersed therein. The first layer also has filler dispersed therein. The composite material further includes a third layer that is or includes reacted second polymeric material. The third layers also has filler dispersed therein. The first layer is or includes a bulk first polymeric material portion that is or includes substantially unreacted first polymeric material and a reacted first polymeric portion extending from the bulk first polymeric portion, and the second layer is or includes a bulk second polymeric material portion that is or includes substantially unreacted second polymeric material and a reacted second polymeric portion extending from the bulk second polymeric portion. The composite material has a tensile strength of greater than 40 MPa. The composite material has an electrical conductivity of greater than 50 S/cm. The composite material has voids therein. The composite material has a porosity of greater than 75 percent. The composite material is coated with a material that includes a therapeutic agent or includes a therapeutic agent therein. The composite material further includes a drug conjugate that can release a drug. The balloon is coated with a material that includes a therapeutic agent therein and/or thereon.
In another aspect, the disclosure features methods of making medical balloons that include providing a substrate and depositing first and second polymeric materials and/or a reaction product of the first and second polymeric materials onto the substrate. The first polymeric material includes first polymer chains having a plurality of spaced apart carboxylic acid groups, and the second polymeric material includes second polymer chains having a plurality of spaced apart primary amino groups, hydroxyl groups, thiol groups, or mixtures of these groups.
Embodiments of the methods can have one or more of the following features. The first and second polymeric materials are deposited concurrently. The first or second polymeric materials are deposited before the other polymeric material. The first and second polymeric materials are deposited by spraying the respective polymers onto the substrate from a solution or a dispersion of each respective polymer. The solution or dispersion of the first and/or second polymeric materials includes a filler having a maximum dimension of less than 1000 nm. The methods further include removing the substrate. The removing of the substrate includes melting the substrate. The substrate is or includes ice. The removing of the substrate includes dissolving the substrate.
Embodiments and/or aspects may include one or more of the following advantages. Balloons can be provided that are formed of a polymeric material that includes additives and particulates, e.g., carbon particulates, that are evenly dispersed, and not excessively aggregated, so that balloon properties are uniform and reproducible. Techniques for forming the balloons include combining two polymers, a dispersive polymer and a balloon polymer, by applying the polymers to a pre-form, the polymers being applied, e.g., concurrently from two separate solutions, or in a series of steps, e.g., two, three or five steps. Balloons can be provided in which properties, such as puncture resistance, scratch resistance, burst strength, tensile strength, porosity, drug release, and electrical and thermal conductivity, are enhanced for a given application. Balloons can be provided that are formed entirely of, or that include as part of their structure, composite materials that are highly loaded with a filler, e.g., carbon nanotubes. In such composites, the filler can be homogeneously dispersed throughout the composite, providing for uniformity in the properties of balloons formed of or carrying such composites. Balloons can be provided that are porous. Such porosity can be used to make drug-eluting balloons. Balloons can be provided that have a high electrical and/or thermal conductivity. For example, balloons can be provided that are formed entirely of, or that include as part of their structure, composite materials that have an electrical conductivity of greater than 50 S/cm, e.g., greater than 60, 70, 80, 90, 100, 175, 200, 250 or even greater than 300 S/cm. Also, for example, balloons can be provided that are formed entirely of, or that include as part of their structure, composite materials that have a high tensile strength, e.g., greater than 100 MPa, e.g., greater than 150, 250, or even greater than 300 MPa, enabling thin and ultra-thin walled balloons.
All publications, patent applications, patents, and other references mentioned herein are incorporated by reference herein in their entirety for all that they contain.
The details of one or more embodiments of the disclosure are set forth in the accompanying drawings, and in the description below. Other features and advantages will be apparent from the description and drawings, and from the claims.
Referring to
Referring also now to
The balloon polymeric material is a material that has suitable balloon properties, e.g., mechanical properties such as tensile strength and reacts with the dispersive polymer. For example (and by reference to
The dispersive polymer enhances dispersion of additives and reduces aggregation. For example (and by reference to
The filler can be, e.g., an allotrope of carbon (e.g., diamond, graphite, C60, C70, C540, a single or multi-wall carbon tube, or amorphous carbon), a functionalized allotrope of carbon (e.g., functionalized with hydrogen bonding groups such as hydrogen bond acceptors and/or donors), a metal, a metal oxide (e.g., titanium dioxide), a metalloid oxide (e.g., silicon dioxide), a clay (e.g., kaolin), a ceramic (e.g., silicon carbide or titanium nitride), a polymeric material, different from the first or second polymeric material or a reaction product of the first and second polymeric materials, or mixtures or any of these fillers. If desired, the carbon nanotubes can encapsulate atoms other than carbon, such as a metal, which can, e.g., enhance radiopacity.
In embodiments, the composite includes, e.g., between about 10 percent by weight filler and about 70 percent by weight filler, e.g., between about 20 percent and about 60 percent, or between about 30 percent and about 58 percent by weight filler. When flexibility is a desirable attribute, it is often desirable to maintain the amount of filler to less than about 20 weight percent.
In embodiments, some of the filler particles have a maximum dimension of not more than about 1000 nm, e.g., not more than about 750 nm, 600 nm, 500 nm, 400 nm, 250 nm, 150 nm, or not more than about 100 nm. In embodiments, each filler particle has a maximum dimension of between about 100 nm and about 1000 nm, e.g., between about 150 nm and about 800 nm, or between about 200 nm and 600 nm.
In embodiments, the filler includes structures having hydrogen-bonding groups extending from an outer portion of each structure, e.g., carboxylic acid groups, amide groups, hydroxyl groups, or silinol groups. These groups can aid in the dispersion of the particles in solution during preparation of the composite.
Referring now to
In embodiments, the filler includes carbon nanotubes that are functionalized and that have an overall diameter, e.g., between about 3 nm and about 25 nm, e.g., between about 4 nm and about 10 nm. In embodiments, the carbon nanotubes can have a length of between about 300 nm and about 1600 nm, e.g., between about 500 nm and about 1000 nm.
Carbon nanotubes, and some of their properties, including dipersibility in a solvent are described in more detail by Moulton et al., Carbon, 43, 1879-1884 (2005); Jiang et al., Electrochemistry Communications, 7, 597-601 (2005); and Shim et al., Langmuir, 21(21), 9381-9385 (2005).
If desired, the filler can include structures that are substantially spherical in shape, each having a diameter of less than about 1000 nm, e.g., less than about 750 nm, 600 nm, 500 nm, 350 nm, 200 nm, 125 nm or even less than 75 nm. In embodiments, the filler can include structures that each have a diameter between about 50 nm and about 900 nm, e.g., between about 100 nm and about 750 nm or between about 250 nm and about 600 nm. In embodiments, blends of fillers, such as blends of tubular structures and spherical structures are utilized.
In embodiments, the reaction product features an ionic complex between the first and second polymeric materials, such as an acid/base adduct of the first and second polymeric materials. Ionic complexes are described by Wang et al., Journal Applied Polymer Science, 65, 1445-1450 (1997); and Palloma et al., Biomaterials, 24, 1459-1468 (2003). In other embodiments, the reaction product features reacted first chains, which are covalently bonded to reacted second chains by amide, ester and/or thioester bonds. In still other embodiments, the reaction product includes portions that are ionic in nature, and portions which include reacted first chains covalently bonded to reacted second chains. Reaction products that include both ionic complex portions and covalently bonded portions are described by Berger et al., European Journal of Pharmaceutics and Biopharmaceutics, 57, 19-34 (2004).
The reacted first and second polymeric chains of the composite can take on a variety of forms and structures. For example, the reacted first polymer chains can be intermingled with reacted second polymer chains throughout a thickness of the composite material, or the reacted first and second polymeric materials can form distinct layers, e.g., alternating layers throughout a thickness of the composite material. In a specific example, the composite material includes a first layer that includes reacted first polymeric material, and a second layer that includes reacted second polymeric material having filler dispersed therein. If desired, e.g., for enhanced mechanical properties, the first layer can also have a filler dispersed therein. Also, if desired, the composite material can further include a third layer that includes a second polymeric material that, optionally, has a filler dispersed therein.
The composite material can have a high tensile strength, e.g., the tensile strength can be greater than about 40 MPa, e.g., greater than about 50 MPa, 75 MPa, 100 MPa, or even greater than about 150 MPa. In addition, the composite material can have a high electrical conductivity, e.g., greater than about 50 S/cm, e.g., greater than about 60 S/cm, 75 S/cm, 100 S/cm, 150 S/cm, 200 S/cm, even greater than about 300 S/cm.
In embodiments, the composite material has a tensile strength of greater than about 60 MPa and an electrical conductivity of greater than about 100 S/cm, or greater than about 100 MPa and a conductivity of greater than about 300 S/cm.
If desired, the composite can have voids, e.g., interconnected voids, that provide a porous composite. For example, the voids can have a maximum dimension that is greater than 500 nm, e.g., greater than 750 nm, 1,000 nm, 1,500 nm, or even greater than 2,500 nm. The voids can provide a porosity that is, e.g., greater than 75 percent, e.g., greater than 80 percent, 85 percent, 90 percent, or even greater than 95 percent, as measured using mercury porosimetry. If desired, the porous structure can be filled with a therapeutic agent so that the agent can be delivered from the balloon during deployment of a medical device.
Referring now to
In an alternative embodiment, the substrate is coated with chitosan and then polyacrylic acid prior to removal of the substrate. In yet another embodiment, the substrate is removed after heat treatment. For example, the substrate can be formed of poly(vinylalcohol), which can withstand at least 150° C. during the heat treatment. After heat treatment, the polyvinyl alcohol can be dissolved away.
In embodiments, the heat treatment regimen includes heating the composite for 6-8 hours at 150-200° C. Optionally, the heat treatment can be performed under vacuum to drive off any water formed as a reaction product. In embodiments, the polyacrylic acid solution is maintained at a pH or from about 2 to about 6, e.g., about 3 to about 5, or from about 3.25 to about 4.0.
Referring now as well to
In embodiments, the balloon wall has a thickness T′ that is between about 0.0001 inch and about 0.040 inch, e.g., between about 0.0002 inch and about 0.010 inch, or between about 0.0005 inch and about 0.005 inch. The polyacrylic acid layers 122′ and 124′ have a thickness T1′ and T3′, respectively, between about 0.00003 inch and about 0.028 inch, e.g., between about 0.00009 inch and about 0.020 inch, or between about 0.0002 inch and about 0.008 inch. T1′ and T3′ can be substantially the same or they can be different. The chitosan/filler layer has a thickness T2′ that is between about 0.00001 inch and about 0.028 inch, e.g., between about 0.0001 and about 0.020 inch, or between about 0.0001 and about 0.006 inch.
Referring now as well to
Referring now to
In some embodiments, a porous balloon is provided by including a water-soluble filler, e.g., sodium chloride or glucose, in the chitosan solution in an anhydrous solvent and/or the polyacrylic acid solution in an anhydrous solvent. After applying the solutions, removing the solvent and heat treating, the water-soluble material can be removed from the formed balloon, e.g., by sonicating in a water bath to provide a porous structure.
In other embodiments, during the formation of the balloon, one or more cutting members are attached to the balloon to form a cutting balloon. Cutting balloons are described in O'Brien U.S. Pat. No. 7,070,576 and Radisch, U.S. Pat. No. 7,011,670.
Referring now as well to
Any of the composites described herein can be made porous by incorporating dissolvable polymeric particles, e.g., having a diameter of from about 500 nm to about 2,500 nm, into the composites during their formation. Removal of the particles can be achieved by dissolving the particles with a solvent from the formed composites.
Any component of any balloon can include a therapeutic agent therein and/or thereon. Also, any balloon can be coated with a material that includes a therapeutic agent therein and/or thereon. Electroporation and iontophoresis can be used to assist in the delivery of a therapeutic agent. For example, when a therapeutic agent is utilized in a conductive composite, delivery of the therapeutic can be aided by applying an electric field to the conductive composite, e.g., between about 5 V/cm and about 2.5 kV/cm, between about 25 V/cm and about 1.5 kV/cm or between about 50 kV/cm and about 1 kV/cm. In some embodiments, the electric field is applied in a pulsing manner. For example, the pulse length can be from about 50 μs to about 30 ms, from about 100 μs to about 25 ms or from about 150 μs to about 20 ms. Generally, electroporation is described by Davalos et al., Microscale Thermophysical Engineering, 4:147-159 (2000). A power supply for a pulsed power supply for electroporation has been described by Grenier, a thesis presented to the University of Waterloo, Ontario, Canada, in a work entitled “Design of a MOSFET-Based Pulsed Power Supply for Electroporation” (2006).
In general, the therapeutic agent can be a genetic therapeutic agent, a non-genetic therapeutic agent, or cells. Therapeutic agents can be used singularly, or in combination. Therapeutic agents can be, e.g., nonionic, or they may be anionic and/or cationic in nature. One therapeutic agent for a vascular application is one that inhibits restenosis. A specific example of one such therapeutic agent that inhibits restenosis is paclitaxel or derivatives thereof, e.g., docetaxel. Soluble paclitaxel derivatives can be made by tethering solubilizing moieties off the 2′ hydroxyl group of paclitaxel, such as —COCH2CH2CONHCH2CH2(OCH2)nOCH3 (n being, e.g., 1 to about 100 or more). Li et al., U.S. Pat. No. 6,730,699 describes additional water soluble derivatives of paclitaxel.
Exemplary non-genetic therapeutic agents include: (a) anti-thrombotic agents such as heparin, heparin derivatives, urokinase, PPack (dextrophenylalanine proline arginine chloromethylketone), and tyrosine; (b) anti-inflammatory agents, including non-steroidal anti-inflammatory agents (NSAID), such as dexamethasone, prednisolone, corticosterone, budesonide, estrogen, sulfasalazine and mesalamine; (c) anti-neoplastic/antiproliferative/anti-miotic agents such as paclitaxel, 5-fluorouracil, cisplatin, vinblastine, vincristine, epothilones, endostatin, angiostatin, angiopeptin, rapamycin (sirolimus), biolimus, tacrolimus, everolimus, monoclonal antibodies capable of blocking smooth muscle cell proliferation, and thymidine kinase inhibitors; (d) anesthetic agents such as lidocaine, bupivacaine and ropivacaine; (e) anti-coagulants such as D-Phe-Pro-Arg chloromethyl ketone, an RGD peptide-containing compound, heparin, hirudin, antithrombin compounds, platelet receptor antagonists, anti-thrombin antibodies, anti-platelet receptor antibodies, aspirin, prostaglandin inhibitors, platelet inhibitors and tick antiplatelet peptides; (f) vascular cell growth promoters such as growth factors, transcriptional activators, and translational promotors; (g) vascular cell growth inhibitors such as growth factor inhibitors, growth factor receptor antagonists, transcriptional repressors, translational repressors, replication inhibitors, inhibitory antibodies, antibodies directed against growth factors, bifunctional molecules consisting of a growth factor and a cytotoxin, bifunctional molecules consisting of an antibody and a cytotoxin; (h) protein kinase and tyrosine kinase inhibitors (e.g., tyrphostins, genistein, quinoxalines); (i) prostacyclin analogs; (j) cholesterol-lowering agents; (k) angiopoietins; (l) antimicrobial agents such as triclosan, cephalosporins, aminoglycosides and nitrofurantoin; (m) cytotoxic agents, cytostatic agents and cell proliferation affectors; (n) vasodilating agents; (o) agents that interfere with endogenous vasoactive mechanisms; (p) inhibitors of leukocyte recruitment, such as monoclonal antibodies; (q) cytokines, (r) hormones; and (s) antispasmodic agents, such as alibendol, ambucetamide, aminopromazine, apoatropine, bevonium methyl sulfate, bietamiverine, butaverine, butropium bromide, n-butylscopolammonium bromide, caroverine, cimetropium bromide, cinnamedrine, clebopride, coniine hydrobromide, coniine hydrochloride, cyclonium iodide, difemerine, diisopromine, dioxaphetyl butyrate, diponium bromide, drofenine, emepronium bromide, ethaverine, feclemine, fenalamide, fenoverine, fenpiprane, fenpiverinium bromide, fentonium bromide, flavoxate, flopropione, gluconic acid, guaiactamine, hydramitrazine, hymecromone, leiopyrrole, mebeverine, moxaverine, nafiverine, octamylamine, octaverine, oxybutynin chloride, pentapiperide, phenamacide hydrochloride, phloroglucinol, pinaverium bromide, piperilate, pipoxolan hydrochloride, pramiverin, prifinium bromide, properidine, propivane, propyromazine, prozapine, racefemine, rociverine, spasmolytol, stilonium iodide, sultroponium, tiemonium iodide, tiquizium bromide, tiropramide, trepibutone, tricromyl, trifolium, trimebutine, tropenzile, trospium chloride, xenytropium bromide, ketorolac, and pharmaceutically acceptable salts thereof.
Exemplary genetic therapeutic agents include anti-sense DNA and RNA as well as DNA coding for: (a) anti-sense RNA, (b) tRNA or rRNA to replace defective or deficient endogenous molecules, (c) angiogenic factors including growth factors such as acidic and basic fibroblast growth factors, vascular endothelial growth factor, epidermal growth factor, transforming growth factor α and β, platelet-derived endothelial growth factor, platelet-derived growth factor, tumor necrosis factor α, hepatocyte growth factor and insulin-like growth factor, (d) cell cycle inhibitors including CD inhibitors, and (e) thymidine kinase (“TK”) and other agents useful for interfering with cell proliferation. Also of interest is DNA encoding for the family of bone morphogenic proteins (“BMP's”), including BMP-2, BMP-3, BMP-4, BMP-5, BMP-6 (Vgr-1), BMP-7 (OP-1), BMP-8, BMP-9, BMP-10, BMP-11, BMP-12, BMP-13, BMP-14, BMP-15, and BMP-16. Currently preferred BMP's are any of BMP-2, BMP-3, BMP-4, BMP-5, BMP-6 and BMP-7. These dimeric proteins can be provided as homodimers, heterodimers, or combinations thereof, alone or together with other molecules. Alternatively, or in addition, molecules capable of inducing an upstream or downstream effect of a BMP can be provided. Such molecules include any of the “hedgehog” proteins, or the DNA's encoding them.
Vectors for delivery of genetic therapeutic agents include viral vectors such as adenoviruses, gutted adenoviruses, adeno-associated virus, retroviruses, alpha virus (Semliki Forest, Sindbis, etc.), lentiviruses, herpes simplex virus, replication competent viruses (e.g., ONYX-015) and hybrid vectors; and non-viral vectors such as artificial chromosomes and mini-chromosomes, plasmid DNA vectors (e.g., pCOR), cationic polymers (e.g., polyethyleneimine, polyethyleneimine (PEI)), graft copolymers (e.g., polyether-PEI and polyethylene oxide-PEI), neutral polymers PVP, SP1017 (SUPRATEK), lipids such as cationic lipids, liposomes, lipoplexes, nanoparticles, or micro particles, with and without targeting sequences such as the protein transduction domain (PTD).
Other EmbodimentsA number of embodiments have been described. Nevertheless, it will be understood that various modifications may be made without departing from the spirit and scope of the disclosure.
For example, while
While
While
While
The balloon formed can be of any desired longitudinal or transverse cross-section by selecting a corresponding substrate. For example, the substrate can be selected to provide a balloon suitable for delivering a bifurcated endoprosthesis. For example, a substrate can be used having one or more “bulges”.
Still other embodiments are in the following claims.
Claims
1. A medical balloon comprising:
- a balloon wall comprising a composite material comprising a polymeric material; and a filler within the polymeric material,
- wherein the polymeric material comprises a reaction product of a first polymeric material comprising first polymer chains having a plurality of carboxylic acid groups, and a second polymeric material comprising second polymer chains having a plurality of amino groups, hydroxyl groups, thiol groups, or mixtures of these groups.
2. The medical balloon of claim 1, wherein the first polymeric material is selected from the group consisting of polyacrylic acid, polymethacrylic acid, poly(ethylene-co-acrylic acid), poly(2-ethylacrylic acid), poly(2-propylacrylic acid) and mixtures thereof.
3. The medical balloon of claim 1, wherein the second polymeric material is selected from the group consisting of chitosan, poly[dimethylsiloxane-co-(3-aminopropyl)methylsiloxane], polyvinyl alcohol, poly(vinyl alcohol-co-vinyl acetate), poly(styrene-co-allyl alcohol) and mixtures thereof.
4. The medical balloon of claim 1, wherein the first polymer chains each have between about 6 and about 10,000 carboxylic acid groups.
5. The medical balloon of claim 1, wherein a total number of primary amino groups, hydroxyl groups and/or thiol groups combined on each of the second polymer chains is between about 6 and about 10,000.
6. The medical balloon of claim 1, wherein a number average molecular weight of the first polymeric material is between about 2,500 and about 350,000, measured relative to polyethylene glycol standards.
7. The medical balloon of claim 1, wherein a number average molecular weight of the second polymeric material is between about 2,500 and about 350,000, measured relative to polyethylene glycol standards.
8. The medical balloon of claim 1, wherein the filler is selected from the group consisting of allotropes of carbon, allotropes of carbon functionalized with hydrogen bonding groups, metals, metal oxides, metalloid oxides, clays, ceramics and mixtures thereof.
9. The medical balloon of claim 1, wherein the filler is dispersed substantially homogenously throughout the polymeric material.
10. The medical balloon of claim 1, wherein the filler is arranged in discrete longitudinal layers through a thickness of the composite material.
11. The medical balloon of claim 1, wherein the reaction product comprises an ionic complex between the first and second polymeric materials.
12. The medical balloon of claim 1, wherein the reaction product comprises an acid base complex of the first and second polymeric materials.
13. The medical balloon of claim 1, wherein the reaction product comprises reacted first chains covalently bonded to reacted second chains by amide, ester and/or thioester bonds.
14. The medical balloon of claim 1, wherein reacted first polymer chains are intermingled with reacted second polymer chains throughout a thickness of the composite material.
15. The medical balloon of claim 1, wherein the composite material comprises a first layer comprising reacted first polymeric material, and a second layer comprising reacted second polymeric material having filler dispersed therein.
16. The medical balloon of claim 15, wherein the first layer also has filler dispersed therein.
17. The medical balloon of claim 1, wherein the first layer includes a bulk first polymeric material portion comprising substantially unreacted first polymeric material and a reacted first polymeric portion extending from the bulk first polymeric portion, and wherein the second layer includes a bulk second polymeric material portion comprising substantially unreacted second polymeric material and a reacted second polymeric portion extending from the bulk second polymeric portion.
18. The medical balloon of claim 1, wherein the composite material has a tensile strength of greater than 40 MPa.
19. The medical balloon of claim 1, wherein the composite material has an electrical conductivity of greater than 50 S/cm.
20. A medical balloon comprising:
- a balloon wall comprising a composite material comprising a polymeric material; and a filler within the polymeric material,
- wherein the composite polymeric material has a conductivity of greater than 40 S/cm.
21. The medical balloon of claim 20, wherein the polymeric material comprises a reaction product of a first polymeric material comprising first polymer chains having a plurality of spaced apart carboxylic acid groups, and a second polymeric material comprising second polymer chains having a plurality of spaced apart primary amino groups, hydroxyl groups, thiol groups, or mixtures of these groups.
22. A medical balloon comprising:
- a balloon wall comprising a composite material comprising a polymeric material; and a filler within the polymeric material,
- wherein the composite polymeric material has a tensile strength of greater than 40 MPa.
23. The medical balloon of claim 22, wherein the tensile strength is greater than 75 MPa.
24. The medical balloon of claim 22, wherein the polymeric material comprises a reaction product of a first polymeric material comprising first polymer chains having a plurality of spaced apart carboxylic acid groups, and a second polymeric material comprising second polymer chains having a plurality of spaced apart primary amino groups, hydroxyl groups, thiol groups, or mixtures of these groups.
25. A method of making a medical balloon, the method comprising:
- providing a substrate; and
- depositing first and second polymeric materials and/or a reaction product of the first and second polymeric materials onto the substrate,
- wherein first polymeric material comprises first polymer chains having a plurality of carboxylic acid groups, and the second polymeric material comprises second polymer chains having a plurality of amino groups, hydroxyl groups, thiol groups, or mixtures of these groups.
26. The method of claim 25, wherein the first and second polymeric materials are deposited concurrently.
27. The method of claim 25, wherein one of the first or second polymeric materials are deposited before the other polymeric material.
28. The method of claim 25, wherein the first and second polymeric materials are deposited by spraying the respective polymers onto the substrate from a solution or a dispersion of each respective polymer.
29. The method of claim 25, further comprising removing the substrate.
Type: Application
Filed: May 18, 2007
Publication Date: Nov 20, 2008
Inventors: Jan Weber (Maastricht), Liliana Atanasoska (Edina, MN)
Application Number: 11/804,654