BEARING STEEL

- JFE Steel Corporation

A bearing steel contains C: 0.56% by mass or more and 0.70% by mass or less, Si: 0.15% by mass or more and less than 0.50% by mass, Mn: 0.60% by mass or more and 1.50% by mass or less, Cr: 0.50% by mass or more and 1.10% by mass or less, P: 0.025% by mass or less, S: 0.025% by mass or less, Al: 0.005% by mass or more and 0.500% by mass or less, O: 0.0015% by mass or less, N: 0.0030% by mass or more and 0.015% by mass or less, and a remainder of Fe and incidental impurities. The bearing steel has a composition such that the eutectic carbide formation index Ec satisfies 0<Ec≦0.25.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description
RELATED APPLICATIONS

This is a §371 of International Application No. PCT/JP2010/071778, with an international filing date of Nov. 30, 2010 (WO 2011/065592, published Jun. 3, 2011), which is based on Japanese Patent Application No. 2010-242668, filed Oct. 28, 2010, and Japanese Patent Application No. 2009-272929, filed Nov. 30, 2009, the subject matter of which is incorporated by reference.

TECHNICAL FIELD

This disclosure relates to a bearing steel having excellent rolling contact fatigue life characteristics and suitable as a bearing material for use in automobiles, wind power, transport machines, electrical machines, precision machines, and other general industrial machinery.

BACKGROUND

High-carbon chromium steel (JIS G4805 standard SUJ2) has been widely used as a bearing steel of this type. In general, one of the important properties of bearing steels is excellent rolling contact fatigue life characteristics. It is generally believed that the rolling contact fatigue life of steel is shortened by the presence of non-metallic inclusions or eutectic carbide in the steel.

It has been believed in recent studies that non-metallic inclusions in steel are mainly responsible for the decrease in rolling contact fatigue life. Thus, bearing life has been improved by reducing the oxygen content of steel to control the number and size of non-metallic inclusions in the steel.

For example, Japanese Unexamined Patent Application Publication Nos. 1-306542 and 3-126839 propose techniques for controlling the composition, shape, or distribution of an oxide-based non-metallic inclusion in steel. However, the manufacture of a bearing steel containing a decreased number of non-metallic inclusions requires expensive converter steelmaking machines or extensive modifications of conventional facilities, which entails an immense economic burden.

Japanese Unexamined Patent Application Publication No. 7-127643 discloses a technique for improving the rolling contact fatigue life characteristics by controlling the centerline segregation rate of carbon and the oxygen and sulfur contents of steel. However, as described above, a further reduction in oxygen content to manufacture a bearing steel containing a decreased number of non-metallic inclusions requires expensive converter steelmaking machines or extensive modifications of conventional facilities, which entails an immense economic burden.

Thus, not only the decrease in the number of non-metallic inclusions in steel, but also the decrease in the eutectic carbide content of steel have received attention. For example, although a high-carbon chromium steel, which contains 0.95% by mass or more C, is very hard and has high wear resistance, the central portion of a casting steel has a high degree of segregation (hereinafter referred to as “centerline segregation”). Furthermore, enormous eutectic carbide is formed in the casting steel, which shortens the rolling contact fatigue life. Thus, the central portion of the casting steel is removed as waste or subjected to diffusion treatment (hereinafter referred to as “soaking”) for a long period of time to sufficiently eliminate the centerline segregation and the eutectic carbide.

Regarding such a segregation problem, Japanese Patent No. 3007834 discloses a method in which steel is controlled to have a specific composition such as C: 0.6% to 1.2% by mass, and the total cross-sectional area of carbide having a thickness of 2 μm or more and with respect to the center line of a longitudinal cross section through the shaft center of a wire or rod-shaped rolled steels, existing in a central region within ⅛×D (D: the width of the longitudinal section) from the axis, including the axis of the longitudinal section, is 0.3% or less of the area of the longitudinal section. Japanese Patent No. 3007834 also quantitatively shows the influence of the amount of enormous carbide on the rolling contact fatigue life characteristics, indicating the presence of enormous eutectic carbide in steel that shortens the rolling contact fatigue life.

Japanese Unexamined Patent Application Publication No. 5-271866 discloses a bearing steel that has a specific composition such as C: 0.50% to 1.50% by mass and Sb: 0.0010% to 0.0150% by mass, a decreased amount of decarburized layer, and high thermal process productivity. It is an object of Japanese Unexamined Patent Application Publication No. 5-271866 to improve thermal process productivity by the addition of Sb to decrease formation of a decarburized layer in steel and thereby eliminate the cutting or grinding process after the thermal process. However, Sb may be highly toxic to humans and should therefore be treated carefully. Furthermore, addition of Sb results in the condensation of Sb in the central segregation zone, worsening centerline segregation. A portion containing condensed Sb can be locally hardened to have a different hardness from the base material. The different hardness may induce rolling contact fatigue fracture, shortening the rolling contact fatigue life.

To eliminate centerline segregation in the casting of a high-carbon chromium bearing steel and enormous eutectic carbide formed in the central segregation zone, for example, Japanese Unexamined Patent Application Publication No. 3-75312 discloses a method for rolling a casting material into a billet and soaking the billet.

However, because of nonuniform steel temperature in soaking, a soaking temperature exceeding the solidus line in a portion could initiate melting in the portion again and induce a eutectic reaction, forming further enormous eutectic carbide.

Thus, in some applications of bearings, low-carbon alloy steel may be used in place of high-carbon chromium steel. For example, case-hardened steel is most commonly used after high-carbon chromium steel. However, case-hardened steel contains 0.23% by mass or less C and moderate amounts of Mn, Cr, Mo, and Ni or the like to achieve necessary quench hardenability and mechanical strength. The surface of case-hardened steel is hardened by carburization or carbonitriding to improve fatigue strength.

For example, Japanese Patent No. 4066903 discloses a case-hardened steel that can be carburized in a short period of time, wherein the case-hardened steel has a specific chemical composition, such as C: 0.10% to 0.35%, and the activation energy of carbon diffusion in the steel defined by Q=34140−605[% Si]+183[% Mn]+136[% Cr]+122[% Mo] is 34000 kcal or less.

Likewise, Japanese Patent No. 4050829 discloses a technique regarding a carburized material that has excellent rolling contact fatigue characteristics, wherein the carburized material has a specific chemical composition such as C: 0.1% to 0.45%, the austenite grain size number of a carburized layer is 7 or more, the carbon content of the surface ranges from 0.9% to 1.5%, and the retained austenite content of the surface ranges from 25% to 40%.

Although carburization or carbonitriding can improve the rolling contact fatigue life characteristics, it may increase the manufacturing costs or decrease the yield because of a large strain or dimension change, thus increasing product cost.

Some applications of bearing steels require a large section. This requires extensive modifications of carburization or carbonitriding facilities, which entail an immense economic burden.

With a year-by-year increase in the scale of wind power, transport machines, and general industrial machinery, there has been an urgent need to further increase the section of bearing steels. Methods for manufacturing steel ingots are broadly divided into ingot casting and continuous casting. Bearing steels having a small section to a large section, which are hitherto manufactured by continuous casting steel, can be provided by manufacturing ingot casting steel to answer the upsizing tendency. However, steels manufactured by the ingot casting (hereinafter referred to as “ingot steels”) have a particular problem that enormous eutectic carbide is formed in a segregation zone such as a V-segregation zone or an inverse V-segregation zone. This is because ingot steels have a higher degree of segregation and consequently a higher frequency of enormous eutectic carbide than continuously casting steels. Thus, it is important to decrease the formation of eutectic carbide.

Accordingly, it could be helpful to provide a method for decreasing formation of eutectic carbide in the segregation zone in bearing steels particularly made of ingot steels, as well as continuously casting steels.

SUMMARY

We discovered that the amounts of C, Si, Mn, Cr, and Al added to a conventional bearing steel are limited to a specific range and a eutectic carbide formation index is newly introduced and limited to a specific range. Thus, we found that these limitations can avoid formation of enormous eutectic carbide in the V-segregation zone or the inverse V-segregation zone, which are particularly problematic in ingot steels, and a bearing steel having excellent rolling contact life characteristics can be provided.

More specifically, we manufactured a bearing steel made of an ingot steel in which the amounts of C, Si, Mn, Cr, and Al are altered and the eutectic carbide formation index Ec having the formula (1) described below is altered. As a result of extensive studies on the structure and the rolling contact fatigue life characteristics of the bearing steel, we found that a steel, even made of an ingot steel, having a composition and Ec in specific ranges can be free of eutectic carbide in the steel and have improved rolling contact fatigue life characteristics.

We thus provide:

1. A bearing steel having a composition containing

C: 0.56% by mass or more and 0.70% by mass or less,

Si: 0.15% by mass or more and less than 0.50% by mass,

Mn: 0.60% by mass or more and 1.50% by mass or less,

Cr: 0.50% by mass or more and 1.10% by mass or less,

P: 0.025% by mass or less,

S: 0.025% by mass or less,

Al: 0.005% by mass or more and 0.500% by mass or less,

O: 0.0015% by mass or less,

N: 0.0030% by mass or more and 0.015% by mass or less, and

a remainder of Fe and incidental impurities,

wherein eutectic carbide formation index Ec defined by the formula (1) satisfies

0<Ec≦0.25,

wherein


Ec=(−0.07×[% Si]−0.03×[% Mn]+0.04×[% Cr]−0.36×[% Al]+0.79)−[% C]  (1)

wherein [ ] indicates the amount of component described in parentheses (% by mass).

2. The bearing steel according to 1 described above, wherein the composition further contains one or more selected from

Cu: 0.005% by mass or more and 0.5% by mass or less,

Ni: 0.005% by mass or more and 1.00% by mass or less, and

Mo: 0.01% by mass or more and 0.5% by mass or less.

3. The bearing steel according to 1 or 2 described above, wherein the composition further contains one or more selected from

W: 0.001% by mass or more and 0.5% by mass or less,

Nb: 0.001% by mass or more and 0.1% by mass or less,

Ti: 0.001% by mass or more and 0.1% by mass or less,

Zr: 0.001% by mass or more and 0.1% by mass or less, and

V: 0.002% by mass or more and 0.5% by mass or less.

4. The bearing steel according to any one of 1 to 3 described above, wherein the composition further contains

B: 0.0002% by mass or more and 0.005% by mass or less.

Summarizing these aspects 1 to 4, a bearing steel has a composition containing

C: 0.56% by mass or more and 0.70% by mass or less, Si: 0.15% by mass or more and less than 0.50% by mass, Mn: 0.60% by mass or more and 1.50% by mass or less, Cr: 0.50% by mass or more and 1.10% by mass or less, P: 0.025% by mass or less, S: 0.025% by mass or less, Al: 0.005% by mass or more and 0.500% by mass or less, O: 0.0015% by mass or less, and N: 0.0030% by mass or more and 0.015% by mass or less,

and optionally at least one of (A) to (C):

(A) one or more selected from Cu: 0.005% by mass or more and 0.5% by mass or less, Ni: 0.005% by mass or more and 1.00% by mass or less, and Mo: 0.01% by mass or more and 0.5% by mass or less,

(B) one or more selected from W: 0.001% by mass or more and 0.5% by mass or less, Nb: 0.001% by mass or more and 0.1% by mass or less, Ti: 0.001% by mass or more and 0.1% by mass or less, Zr: 0.001% by mass or more and 0.1% by mass or less, and V: 0.002% by mass or more and 0.5% by mass or less, and

(C) B: 0.0002% by mass or more and 0.005% by mass or less,

and a remainder of Fe and incidental impurities,

wherein eutectic carbide formation index Ec defined by the formula (I) satisfies 0<Ec≦0.25.

A bearing steel having much better rolling contact fatigue life characteristics than conventional bearing steels can be stably manufactured. In particular, ingot steels can be used to manufacture bearing steels having a small section to those having a large section. Our bearing steels also contribute to upsizing of wind power generators, transport machines, and general industrial machinery, providing industrially advantageous effects.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph showing the evaluation result of the rolling contact fatigue life (vertical axis: B10 life ratio) as a function of Ec (horizontal axis: % by mass).

FIG. 2 is a view illustrating the sampling position and the test surface size in sampling for microstructure observation from a steel billet after square forging.

FIG. 3 is a view illustrating the sampling position and the test specimen size in sampling for the evaluation of rolling contact life from a steel billet after square forging.

FIG. 4 is a view illustrating the sampling position and the test surface size in sampling for microstructure observation from a steel billet after circular forging.

FIG. 5 is a view illustrating the sampling position and the test surface size in sampling for the evaluation of rolling contact life from a steel billet after circular forging.

FIG. 6 is a view illustrating the sampling position and the test specimen size in sampling for the evaluation of machinability from a steel billet after square forging.

FIG. 7 is a view illustrating the sampling position and the test specimen size in sampling for the evaluation of machinability from a steel billet after circular forging.

 DETAILED DESCRIPTION

Our bearing steels will be described in detail below.

First, reasons for limiting the percentage of each component of the composition of the bearing steel will be described below.

C: 0.56% by mass or more and 0.70% by mass or less

C can increase the strength of steel and effectively improve the rolling contact fatigue life characteristics of steel. The C content is 0.56% by mass or more. On the other hand, the C content of more than 0.70% by mass results in the formation of enormous eutectic carbide during the casting of the material, shortening the rolling contact fatigue life. Thus, the C content is 0.56% by mass or more and 0.70% by mass or less.

Si: 0.15% by mass or more and less than 0.50% by mass

Si can act as a deoxidizing agent, increase the strength of steel owing to solid-solution hardening, and improve the rolling contact fatigue life characteristics of steel. Si is added to produce these effects. 0.15% by mass or more Si is added to produce these effects. However, addition of 0.50% by mass or more Si results in deterioration in the machinability and the forgeability of steel. Si can be bound to oxygen in steel and remain as an oxide in the steel, causing deterioration in the rolling contact fatigue life characteristics. Furthermore, Si condensed in a segregation zone facilitates formation of eutectic carbide. Thus, the upper limit of Si is less than 0.50% by mass.

Mn: 0.60% by mass or more and 1.50% by mass or less

Mn can be added to improve quench hardenability, increase the toughness of steel, and improve the rolling contact fatigue life characteristics of steel. 0.60% by mass or more Mn is added. However, the addition of more than 1.50% by mass Mn results in deterioration in machinability. Furthermore, Mn condensed in a segregation zone facilitates formation of eutectic carbide. Thus, the upper limit of Mn is 1.50% by mass.

Cr: 0.50% by mass or more and 1.10% by mass or less

In the same manner as in Mn, Cr can be added to increase the toughness of steel and improve the rolling contact fatigue life characteristics of steel. 0.50% by mass or more Cr is added. However, addition of more than 1.10% by mass Cr results in deterioration in machinability. Thus, the upper limit of Cr is 1.10% by mass.

P: 0.025% by mass or less

P is a detrimental element that can decrease the base material toughness or the rolling contact fatigue life of steel and is preferably decreased as much as possible. In particular, the P content of more than 0.025% by mass results in a significant decrease in base material toughness and rolling contact fatigue life. Thus, the P content is 0.025% by mass or less, preferably 0.020% by mass or less. It is industrially difficult to achieve the P content of 0%. Thus, the P content is often 0.003% by mass or more.

S: 0.025% by mass or less

S is contained in steel as a non-metallic inclusion MnS. Since bearing steels contain a decreased amount of oxide, which can often induce rolling contact fatigue, a large amount of MnS in steel can shorten the rolling contact fatigue life. Thus, S is preferably decreased as much as possible. The S content is 0.025% by mass or less, preferably 0.020% by mass or less. It is industrially difficult to achieve the S content of 0%. Thus, the S content is often 0.0001% by mass or more.

Al: 0.005% by mass or more and 0.500% by mass or less

Al can act as a deoxidizing agent, form a nitride and decrease the size of austenite grains, and improve the toughness and the rolling contact fatigue life characteristics. Al is added to produce these effects. 0.005% by mass or more Al is added to produce these effects. However, addition of more than 0.500% by mass Al results in formation of a coarse oxide type inclusion in steel, causing deterioration in the rolling contact fatigue life characteristics of steel. Furthermore, Al condensed in a segregation zone facilitates formation of eutectic carbide. Thus, the upper limit of the Al content is 0.500% by mass, preferably 0.450% by mass or less.

O: 0.0015% by mass or less

O can be bound to Si or Al to form a hard oxide-based non-metallic inclusion, shortening the rolling contact fatigue life. Thus, O is preferably decreased as much as possible and is 0.0015% by mass or less. It is industrially difficult to achieve an O content of 0%. Thus, the O content is often 0.0003% by mass or more.

N: 0.0030% by mass or more and 0.015% by mass or less

N can be bound to Al to form a nitride-based non-metallic inclusion, decrease the size of austenite grains, and improve the toughness and the rolling contact fatigue life characteristics. Thus, 0.003% by mass or more N is added. However, the addition of more than 0.015% by mass N results in formation of a large number of nitride-based inclusions in steel, causing deterioration in the rolling contact fatigue life characteristics. This also results in the presence of a large amount of N that does not form a nitride in steel (free N), thus decreasing the toughness of steel. Thus, the upper limit of the N content is 0.015% by mass, preferably 0.010% by mass or less.

Eutectic carbide formation index Ec: 0<Ec≦0.25

We smelted steels having various compositions in a vacuum melting furnace. The resulting steel ingot was examined for the presence of eutectic carbide. Regression calculation on the result was performed with various selected sets of parameters (main influential elements). As a result, it was found that the eutectic carbide index Ec defined by the formula (1) must satisfy 0<Ec≦0.25 as a steel composition with which formation of eutectic carbide can be decreased.


Ec=(−0.07×[% Si]−0.03×[% Mn]+0.04×[% Cr]−0.36×[% Al]+0.79)−[% C]  (1)

wherein [ ] indicates the amount of component described in parentheses (% by mass).

We manufactured bearing steels having the compositions and Ec's listed in Table 1 and examined their rolling contact fatigue life characteristics. The rolling contact fatigue life characteristics were performed by the test method described below in the examples.

Bearing steels were manufactured under fixed conditions to examine the presence of eutectic carbide and the influence of the composition and Ec on the rolling contact fatigue life characteristics. More specifically, after smelting in a converter, an ingot steel (ingot) having a 1350 mm×1250 mm section (top side) and a 1280×830 mm section (bottom side) was formed by ingot casting. The ingot steel was forged to have a 550 mm square section. Test specimens for observing formed eutectic carbide illustrated in FIG. 2 and rolling contact fatigue test specimens illustrated in FIG. 3 were sampled from the forged steel billet. The presence of eutectic carbide, the rolling contact fatigue life characteristics, and machinability (determined from the tool life ratio) were examined by the test method described below.

Each of the test specimens was sampled from a portion of the forged steel billet corresponding to the bottom of the ingot steel.

TABLE 1 (% by mass) Steel No. C Si Mn P S Cr Al O N Ec Note A-1 1.05 0.25 0.45 0.016 0.008 1.45 0.025 0.0010 0.0031 −0.24 Reference steel A-2 0.70 0.46 1.23 0.018 0.005 0.51 0.021 0.0011 0.0030 0.03 Inventive steel A-3 0.70 0.49 1.50 0.011 0.005 0.51 0.121 0.0010 0.0038 −0.01 Comparative steel A-4 0.62 0.32 0.97 0.010 0.006 0.88 0.024 0.0008 0.0052 0.15 Inventive steel A-5 0.57 0.16 0.74 0.015 0.003 0.71 0.021 0.0009 0.0049 0.21 Inventive steel A-6 0.48 0.19 0.58 0.011 0.005 1.09 0.033 0.0009 0.0045 0.31 Comparative steel A-7 0.56 0.22 0.62 0.008 0.002 1.00 0.028 0.0008 0.0036 0.23 Inventive steel A-8 0.55 0.23 0.63 0.007 0.003 0.95 0.021 0.0009 0.0042 0.24 Comparative steel A-9 0.56 0.16 0.60 0.007 0.003 1.00 0.037 0.0007 0.0035 0.23 Inventive steel A-10 0.56 0.16 0.58 0.009 0.003 1.05 0.036 0.0008 0.0031 0.23 Comparative steel A-11 0.70 0.50 1.50 0.012 0.003 0.51 0.340 0.0011 0.0042 −0.09 Comparative steel A-12 0.67 0.39 0.95 0.008 0.002 0.56 0.035 0.0010 0.0035 0.07 Inventive steel

Table 2 shows the evaluation results of rolling contact fatigue life and machinability (determined from the tool life ratio). FIG. 1 shows the relationship between the evaluation results of rolling contact fatigue life (vertical axis: B10 life ratio) and Ec (horizontal axis: % by mass). As shown in that figure, enormous eutectic carbide is formed in steel when Ec is 0 or less. Even an increase in Ec in this range cannot significantly improve the rolling contact fatigue life relative to the level of a reference material. When Ec is more than 0, eutectic carbide is not formed, and the rolling contact fatigue life is markedly improved. However, Ec of more than 0.25 resulted in a decrease in the amount of C added and consequently a decrease in the strength and the rolling contact fatigue life of steel after quenching. Thus, when Ec is in the range of 0<Ec≦0.25, eutectic carbide is not formed in steel, and therefore the rolling contact fatigue life characteristics are improved. Even when Ec is within our range, A-8 having a C content outside our range and A-10 having a Mn content outside our range had a decreased strength and consequently a shortened rolling contact fatigue life.

TABLE 2 Test results Presence of Rolling contact Steel eutectic fatigue life Tool life Symbol in No. carbide Ec (B10 life ratio) ratio Note FIG. 1 A-1 Yes −0.24 1.00 1.00 Reference steel A-2 No 0.03 1.16 1.21 Inventive steel ♦ A-3 Yes −0.01 1.06 1.20 Comparative steel ♦ A-4 No 0.15 1.32 1.22 Inventive steel ♦ A-5 No 0.21 1.25 1.24 Inventive steel ♦ A-6 No 0.31 1.07 1.24 Comparative steel ▪ A-7 No 0.23 1.17 1.20 Inventive steel ♦ A-8 No 0.24 1.08 1.20 Comparative steel ▴ A-9 No 0.23 1.16 1.21 Inventive steel ♦ A-10 No 0.23 1.09 1.20 Comparative steel ▴ A-11 Yes −0.09 1.03 1.18 Comparative steel ♦ A-12 No 0.07 1.23 1.22 Inventive steel ♦

The reason for limiting Ec to produce a steel free of eutectic carbide is that, as described above, formation of eutectic carbide in steel can cause rolling contact fatigue originating from the eutectic carbide, which causes deterioration in the rolling contact fatigue life characteristics.

Formation of eutectic carbide can be decreased even with an ingot steel manufactured by ingot casting. Thus, our concepts are particularly effective when applied to ingot steels manufactured by ingot casting. It is also effective to use ingot steels to manufacture bearing products having a small section to those having a large section.

In addition to these base components, the following components can appropriately be added.

(A) One or more selected from Cu: 0.005% to 0.5% by mass, Ni: 0.005% to 1.00% by mass, and Mo: 0.01% to 0.5% by mass

Cu, Ni, and Mo can improve the quench hardenability, the strength after tempering, and the rolling contact fatigue life characteristics of steel and can be selectively added in accordance with the strength required (more specifically, any one of Cu, Ni, Mo, Cu+Ni, Cu+Mo, Ni+Mo, and Cu+Ni+Mo can be selectively added). The amounts to be added are preferably 0.005% by mass or more for Cu and Ni and 0.01% by mass or more for Mo to produce such effects. However, addition of more than 0.5% by mass Cu or Mo or more than 1.00% by mass Ni results in deterioration in machinability of the steel. Thus, Cu, Ni, and Mo are preferably added in amounts equal to or below these upper limits.

Likewise, to increase the strength or improve the rolling contact fatigue life characteristics of steel, in addition to the components described above, the following components may be added to our bearing steel.

(B) One or more of W: 0.001% to 0.5% by mass, Nb: 0.001% to 0.1% by mass, Ti: 0.001% to 0.1% by mass, Zr: 0.001% to 0.1% by mass, and V: 0.002% to 0.5% by mass

W, Nb, Ti, Zr, and V can improve the quench hardenability, the strength after tempering, and the rolling contact fatigue life characteristics of steel and can be selectively added in accordance with the strength required (more specifically, any one of W, Nb, Ti, Zr, V, W+Nb, W+Ti, W+Zr, W+V, Nb+Ti, Nb+Zr, Nb+V, Ti+Zr, Ti+V, Zr+V, W+Nb+Ti, W+Nb+Zr, W+Nb+V, W+Ti+Zr, W+Ti+V, W+Zr+V, Nb+Ti+Zr, Nb+Ti+V, Nb+Zr+V, Ti+Zr+V, W+Nb+Ti+Zr, W+Nb+Ti+V, W+Nb+Zr+V, W+Ti+Zr+V, Nb+Ti+Zr+V, and W+Nb+Ti+Zr+V can be selectively added). The amounts to be added are preferably 0.001% by mass or more for W, Nb, Ti, and Zr and 0.002% by mass or more for V to produce such effects. However, addition of more than 0.5% by mass W or V or more than 0.1% by mass of Nb, Ti, or Zr results in deterioration in machinability of the steel. Thus, these elements are preferably added in amounts equal to or below these upper limits.

(C) B: 0.0002% to 0.005% by mass

B can improve quench hardenability and thereby increase the strength of steel after tempering and improve the rolling contact fatigue life characteristics of steel. B can be added to steel on an as-needed basis 0.0002% by mass or more of B is preferably added to produce these effects. However, addition of more than 0.005% by mass B results in deterioration in workability. Thus, 0.0002% to 0.005% by mass B is preferably added.

When an element other than the base components is added, any combination of elements of (A), (B), and (C) groups is available. More specifically, an element selected from any one element group may be added, elements selected from each of two element groups may be added, or elements selected from each of all the element groups may be added.

In our bearing steel, the components other than the components described above are Fe and incidental impurities. Examples of the incidental impurities include, but are not limited to, Sn, Sb, As, and Ca.

A bearing steel having the composition described above is smelted in a vacuum melting furnace or a converter and further by a known refining method such as a degassing process, and is then formed into a cast billet by ingot casting or continuous casting. Even when a cast billet is formed by ingot casting by which eutectic carbide is particularly easily precipitated, formation of eutectic carbide can be prevented. Thus, our concepts can be applied to ingot steels (with which large cast billets can be manufactured). Cast billets are subsequently subjected to a forming process, such as rolling or forging, to produce bearing components.

EXAMPLES Example 1

A steel having a composition listed in Table 3 was smelted by converter refining and a degassing process and then formed into a cast billet having a size listed in Table 4 by ingot casting or continuous casting. The cast billet was heated to a temperature of 1000° C. to 1350° C. in a furnace and then forged to have a section size listed in Table 4. The presence of eutectic carbide and the rolling contact fatigue life characteristics of the forged product were examined as described below.

Presence of Eutectic Carbide

The presence of eutectic carbide was examined by taking a sample for microstructure observation from a (T1/2, T2/2) portion (central portion) and a (T1/2, T2/4) portion (T1=T2 denote a side length of a square-forged steel billet: FIG. 2) or a D/4 portion and a D/2 portion (D denotes the diameter of a circular-forged steel billet: FIG. 4) of a forged steel billet such that the section in the drawing direction became a surface to be observed, etching the sample with 3% nital, and observing the sample with a scanning electron microscope (SEM) at a magnification ratio of 500. The test area was 10 mm×10 mm. Each test specimen was sampled from a portion of the forged steel billet corresponding to the bottom of an ingot steel.

Rolling Contact Fatigue Life Characteristics

The rolling contact fatigue life characteristics are preferably determined in actual use after forging, cutting, quenching, and tempering. However, this requires a long term. Thus, the rolling contact fatigue life characteristics were determined with a thrust type rolling contact fatigue machine as described below. A 60 mmφ×5.3 mm disk was cut from a (T1/2, T2/4) portion (T1=T2 denote a side length of a square-forged steel billet: FIG. 3) or a D/4 portion (D denotes the diameter of a circular-forged steel billet: FIG. 5) of a forged steel billet, was heated at 950° C. for 20 minutes, and was quenched with an oil at 25° C. The disk was then tempered at 170° C. for 1.5 hours and was flat-polished to 60 mmφ×5 mm. The test surface was mirror-finished. The test specimen thus prepared was subjected to a rolling contact fatigue test under a maximum Hertzian contact stress of 5.8 GPa with a thrust rolling contact fatigue machine in which a steel ball rolled on the circumference of a circle having a diameter of approximately 38 mm, Each of the test specimens was sampled from a portion of the forged steel billet corresponding to the bottom of an ingot steel or a continuously casting steel.

The rolling contact fatigue life characteristics were determined as described below. The stress loading frequency when the test specimen underwent detachment was measured for 10 to 15 test specimens. The relationship between the cumulative probability and the stress loading frequency was organized using Weibull probability paper. After that, the cumulative probability 10% (hereinafter referred to as B10 life) was determined. The rolling contact fatigue life characteristics were judged to be improved when the B10 life was improved by 10% or more with respect to a reference steel (A-1: SUJ2 equivalent steel).

Machinability

Machinability is preferably determined in actual processing after forging, cutting, quenching, and tempering. However, this requires a long term. Thus, machinability was determined in a turning test (lathe turning test of the outer surface) as described below. A 60 mmφ×270 mm round bar was cut from a (T1/2, T2/4) portion (T1=T2 denote a side length of a square-forged steel billet: FIG. 6) or a D/4 portion (D denotes the diameter of a circular-forged steel billet: FIG. 7) of a forged steel billet, was heated at 950° C. for 20 minutes and quenched with an oil at 25° C. The bar was then tempered at 170° C. for 1.5 hours. Machinability of the test specimen thus prepared was determined with a lathe turning tester. The turning test was performed with a superhard (P10) cutting tool without a lubricant at a cutting speed of 120 mm/min, a feed speed of 0.2 m/rev, and a depth of cut of 1.0 mm. The amount of time elapsed to the time the flank wear of the tool was 0.2 mm was considered to be the tool life. The degree of reduction in life (tool life ratio=tool life/tool life of SUJ2 equivalent steel) was determined by dividing the tool life for each steel by the tool life for the reference steel (A-1: SUJ2 equivalent steel). Machinability was judged to be improved when the tool life ratio was improved by 15% or more with respect to the reference steel.

TABLE 3 Chemical components (% by mass) Steel No. C Si Mn P S Cr Al O N Cu Ni A-1 1.05 0.25 0.45 0.016 0.008 1.45 0.025 0.0010 0.0031 — — B-1 0.62 0.33 0.98 0.010 0.006 0.87 0.025 0.0010 0.0033 0.01 0.01 B-2 0.60 0.26 0.85 0.011 0.005 0.80 0.025 0.0009 0.0031 0.02 0.02 B-3 0.69 0.45 1.44 0.015 0.006 0.53 0.490 0.0011 0.0041 — — B-4 0.56 0.42 1.00 0.012 0.005 0.52 0.005 0.0010 0.0035 0.24 0.75 B-5 0.69 0.16 0.61 0.015 0.009 0.94 0.031 0.0009 0.0042 — — B-6 0.59 0.44 1.43 0.012 0.006 0.93 0.020 0.0008 0.0043 — — B-7 0.70 0.49 1.53 0.011 0.005 0.51 0.111 0.0009 0.0087 — — B-8 0.60 0.24 0.97 0.010 0.007 0.95 0.025 0.0014 0.0042 0.21 0.11 B-9 0.47 0.45 1.48 0.011 0.009 0.96 0.029 0.0011 0.0049 — — B-10 0.92 0.21 0.77 0.015 0.006 0.95 0.033 0.0010 0.0044 — — B-11 0.62 0.70 0.92 0.011 0.005 0.72 0.032 0.0011 0.0062 0.18 0.09 B-12 0.69 0.49 1.49 0.012 0.006 0.50 0.211 0.0009 0.0042 — — B-13 0.63 0.25 1.20 0.011 0.006 0.89 0.049 0.0005 0.0081 — — B-14 0.70 0.33 0.97 0.009 0.007 0.51 0.005 0.0007 0.0055 — — B-15 0.57 0.49 1.44 0.008 0.006 0.52 0.022 0.0009 0.0042 — — B-16 0.69 0.21 0.61 0.015 0.009 0.93 0.035 0.0007 0.0041 — — B-17 0.65 0.49 1.12 0.011 0.008 0.55 0.005 0.0009 0.0059 — — B-18 0.56 0.16 1.05 0.015 0.008 1.10 0.080 0.0009 0.0059 — — B-19 0.57 0.17 0.73 0.012 0.007 0.72 0.010 0.0007 0.0045 0.01 0.02 B-20 0.63 0.25 0.88 0.013 0.007 0.81 0.530 0.0007 0.0045 0.01 0.02 B-21 0.63 0.34 0.89 0.009 0.003 0.83 0.026 0.0008 0.0039 — — B-22 0.56 0.35 0.99 0.012 0.005 0.99 0.041 0.0010 0.0041 — — B-23 0.70 0.49 1.54 0.011 0.006 0.51 0.112 0.0009 0.0034 — — B-24 0.60 0.25 0.77 0.009 0.007 0.83 0.025 0.0011 0.0036 — — B-25 0.66 0.20 1.01 0.011 0.005 0.99 0.022 0.0010 0.0041 — — B-26 0.69 0.16 0.99 0.012 0.005 0.77 0.035 0.0010 0.0033 0.22 0.43 B-27 1.05 0.25 0.45 0.016 0.008 1.45 0.025 0.0010 0.0031 — — B-28 0.64 0.25 0.86 0.008 0.001 0.78 0.028 0.0009 0.0035 — — B-29 0.61 0.34 0.93 0.017 0.003 0.86 0.029 0.0008 0.0032 — — B-30 0.67 0.38 0.91 0.009 0.001 1.20 0.025 0.0010 0.0035 — — B-31 0.67 0.34 0.89 0.011 0.002 0.40 0.033 0.0009 0.0035 — — B-32 0.80 0.26 0.91 0.010 0.003 0.95 0.027 0.0008 0.0042 — — B-33 0.60 0.25 0.79 0.011 0.004 0.85 0.027 0.0008 0.0020 — — B-34 0.61 0.26 0.81 0.011 0.004 0.88 0.023 0.0010 0.0160 — — Steel No. Mo W Nb Ti Zr V B Ec Note A-1 — — — — — — — −0.24 Reference steel B-1 0.33 — — — — — — 0.14 Inventive steel B-2 0.33 — — — — — — 0.17 Inventive steel B-3 0.45 — — — — — — −0.13 Comparative steel B-4 — — 0.012 — — — — 0.19 Inventive steel B-5 — — — — — — 0.0012 0.10 Inventive steel B-6 0.41 — — — — — — 0.16 Inventive steel B-7 — — — 0.002 — 0.110 — −0.01 Comparative steel B-8 — — — — 0.003 — — 0.17 Inventive steel B-9 0.41 — — — — — — 0.27 Comparative steel B-10 — — — — — — — −0.14 Comparative steel B-11 — — — — — — — 0.11 Comparative steel B-12 — 0.53 — — — — — −0.03 Comparative steel B-13 0.33 — — — — — — 0.12 Inventive steel B-14 0.15 — 0.045 — — — — 0.06 Inventive steel B-15 — — — — — — 0.16 Inventive steel B-16 0.15 0.35 — — — — — 0.03 Inventive steel B-17 — — — 0.011 — — — 0.09 Inventive steel B-18 — — — 0.011 — — — 0.20 Inventive steel B-19 0.28 — — — — — — 0.21 Inventive steel B-20 0.28 — — — — — — −0.04 Comparative steel B-21 0.31 — — — — — — 0.13 Inventive steel B-22 — — — — — — — 0.20 Inventive steel B-23 — — 0.015 0.013 — — — −0.01 Comparative steel B-24 — — 0.011 — — 0.055 — 0.17 Inventive steel B-25 0.29 — — — — — — 0.12 Inventive steel B-26 — — 0.011 — — — — 0.08 Inventive steel B-27 — — 0.011 — — — — −0.24 Comparative steel B-28 0.26 — — — — — — 0.13 Inventive steel B-29 0.32 — — — — — — 0.15 Inventive steel B-30 — — — — — — — 0.11 Comparative steel B-31 — — — — — — — 0.07 Comparative steel B-32 — — — — — — — −0.03 Comparative steel B-33 — — — — — — — 0.17 Comparative steel B-34 — — — — — — — 0.16 Comparative steel

TABLE 4 Billet Size after Casting and after Forging Heating Section of billet (mm) Section after forging (mm) temperature Steel No. Top Bottom Material Shape*1 Size*2 (° C.) Note A-1 1350 × 1250 1280 × 830 Ingot steel □ 550 1150 Reference steel B-1 1330 × 1230 1280 × 860 Ingot steel □ 700 1150 Inventive steel B-2 1100 × 1100  860 × 860 Ingot steel □ 650 1100 Inventive steel B-3 1000 × 1000  700 × 700 Ingot steel ◯ 550 1150 Comparative steel B-4 1250 × 1150 1180 × 730 Ingot steel ◯ 600 1150 Inventive steel B-5 1450 × 1350 1380 × 930 Ingot steel □ 750 1100 Inventive steel B-6 900 × 900  700 × 700 Ingot steel ◯ 450 1250 Inventive steel B-7 1330 × 1230 1280 × 860 Ingot steel □ 600 1050 Comparative steel B-8 1330 × 1230 1280 × 860 Ingot steel □ 600 1000 Inventive steel B-9 1100 × 1100  860 × 860 Ingot steel □ 450 1150 Comparative steel B-10 1450 × 1350 1380 × 930 Ingot steel □ 750 1050 Comparative steel B-11 1450 × 1350 1380 × 930 Ingot steel ◯ 750 1150 Comparative steel B-12 900 × 900  700 × 700 Ingot steel ◯ 450 1100 Comparative steel B-13 1330 × 1230 1280 × 860 Ingot steel ◯ 800 1200 Inventive steel B-14 1330 × 1230 1280 × 860 Ingot steel □ 700 1250 Inventive steel B-15 1450 × 1350 1380 × 930 Ingot steel □ 600 1150 Inventive steel B-16 1450 × 1350 1380 × 930 Ingot steel ◯ 600 1150 Inventive steel B-17 1100 × 1100  860 × 860 Ingot steel □ 450 1350 Inventive steel B-18 1250 × 1150 1180 × 730 Ingot steel ◯ 500 1000 Inventive steel B-19 1100 × 1100  860 × 860 Ingot steel ◯ 400 1050 Inventive steel B-20 1250 × 1150 1180 × 730 Ingot steel □ 550 1100 Comparative steel B-21 1400 × 300  1400 × 300 Continuously casted steel □ 450 1150 Inventive steel B-22 1400 × 300  1400 × 300 Continuously casted steel □ 600 1200 Inventive steel B-23 1400 × 300  1400 × 300 Continuously casted steel □ 450 1100 Comparative steel B-24 1400 × 300  1400 × 300 Continuously casted steel □ 550 1100 Inventive steel B-25 1400 × 300  1400 × 300 Continuously casted steel ◯ 650 1150 Inventive steel B-26 1400 × 300  1400 × 300 Continuously casted steel ◯ 600 1150 Inventive steel B-27 1400 × 300  1400 × 300 Continuously casted steel □ 550 1150 Comparative steel B-28 1330 × 1230 1280 × 860 Ingot steel □ 650 1270 Inventive steel B-29 1330 × 1230 1280 × 860 Ingot steel □ 650 1250 Inventive steel B-30 1330 × 1230 1280 × 860 Ingot steel □ 650 1250 Comparative steel B-31 1330 × 1230 1280 × 860 Ingot steel □ 650 1250 Comparative steel B-32 1330 × 1230 1280 × 860 Ingot steel □ 650 1250 Comparative steel B-33 1330 × 1230 1280 × 860 Ingot steel □ 650 1250 Comparative steel B-34 1330 × 1230 1280 × 860 Ingot steel □ 650 1250 Comparative steel *1: ◯ denotes round forging, □ denotes square forging. *2: Diameter for round forging, Side length for square forging

Table 5 shows the presence or absence of eutectic carbide, the rolling contact fatigue life characteristics, and the results of machinability test. It was shown that steels B-1 to B-2, B-4 to B-6, B-8, B-13 to B-19, B-21 to B-22, B-24 to B-26, and B-28 to B-29, which satisfy our composition and Ec contained no eutectic carbide in the steel and had excellent rolling contact fatigue life characteristics. In contrast, steels B-3, B-7, B-12, and B-23, which have a composition within our range, but Ec outside our range contained eutectic carbide in the steel and had a shortened rolling contact fatigue life. Steels B-9 to B-11, B-20, B-27, and B-31 to B-34, which have a composition outside our range, had a shortened rolling contact fatigue life. Steel B-30, which has Ec within our range, but a Cr content outside our range, had insufficient machinability.

TABLE 5 Test results Presence Rolling of contact Steel eutectic fatigue life Tool life No. carbide Ec (Bn life ratio) ratio Note A-1 Yes −0.24 1.00 1.00 Reference steel B-1 No 0.13 1.16 1.21 Inventive steel B-2 No 0.17 1.19 1.22 Inventive steel B-3 Yes −0.14 1.08 1.18 Comparative steel B-4 No 0.19 1.18 1.22 Inventive steel B-5 No 0.16 1.17 1.20 Inventive steel B-6 Yes −0.01 1.09 1.22 Comparative steel B-7 No 0.17 1.18 1.23 Inventive steel B-8 No 0.27 1.09 1.25 Comparative steel B-9 Yes −0.14 1.05 1.12 Comparative steel B-10 No 0.11 1.07 1.21 Comparative steel B-11 Yes −0.04 1.08 1.20 Comparative steel B-12 No 0.12 1.17 1.20 Inventive steel B-13 No 0.05 1.13 1.19 Inventive steel B-14 No 0.16 1.18 1.23 Inventive steel B-15 No 0.08 1.13 1.20 Inventive steel B-16 No 0.09 1.13 1.21 Inventive steel B-17 No 0.20 1.12 1.17 Inventive steel B-1S No 0.21 1.12 1.23 Inventive steel B-19 Yes −0.04 1.08 1.15 Comparative steel B-20 No 0.14 1.17 1.23 Inventive steel B-21 No 0.13 1.15 1.23 Inventive steel B-22 No 0.14 1.18 1.22 Inventive steel B-23 No 0.20 1.11 1.21 Inventive steel B-24 No 0.16 1.12 1.22 Inventive steel B-25 No 0.06 1.11 1.21 Inventive steel B-26 No 0.20 1.15 1.22 Inventive steel B-27 No 0.16 1.19 1.22 Inventive steel B-28 No 0.06 1.15 1.21 Inventive steel B-29 No 0.10 1.14 1.12 Comparative steel B-30 No 0.07 1.08 1.21 Comparative steel B-31 No −0.03 1.07 1.16 Comparative steel B-32 No 0.16 1.08 1.22 Comparative steel B-33 No 0.16 1.07 1.13 Comparative steel

INDUSTRIAL APPLICABILITY

Bearing steels having excellent rolling contact fatigue life characteristics can be manufactured at low cost, and industrially very valuable bearing steels can be provided.

Claims

1. A bearing steel having a composition comprising:

C: 0.56% by mass or more and 0.70% by mass or less,
Si: 0.15% by mass or more and less than 0.50% by mass,
Mn: 0.60% by mass or more and 1.50% by mass or less,
Cr: 0.50% by mass or more and 1.10% by mass or less,
P: 0.025% by mass or less,
S: 0.025% by mass or less,
Al: 0.005% by mass or more and 0.500% by mass or less,
O: 0.0015% by mass or less,
N: 0.0030% by mass or more and 0.015% by mass or less, and
a remainder of Fe and incidental impurities,
wherein eutectic carbide formation index Ec defined by formula (1) satisfies
0<Ec≦0.25,
wherein Ec=(−0.07×[% Si]−0.03×[% Mn]+0.04×[% Cr]−0.36×[% Al]+0.79)−[% C]  (1)
wherein [ ] indicates the amount of component described in parentheses (% by mass).

2. The bearing steel according to claim 1, wherein the composition further comprises one or more selected from the group consisting of:

Cu: 0.005% by mass or more and 0.5% by mass or less,
Ni: 0.005% by mass or more and 1.00% by mass or less, and
Mo: 0.01% by mass or more and 0.5% by mass or less.

3. The bearing steel according to claim 1, wherein the composition further comprises one or more selected from the group consising of:

W: 0.001% by mass or more and 0.5% by mass or less,
Nb: 0.001% by mass or more and 0.1% by mass or less,
Ti: 0.001% by mass or more and 0.1% by mass or less,
Zr: 0.001% by mass or more and 0.1% by mass or less, and
V: 0.002% by mass or more and 0.5% by mass or less.

4. The bearing steel according to claim 1, wherein the composition further comprises B: 0.0002% by mass or more and 0.005% by mass or less.

5. The bearing steel according to claim 2, wherein the composition further comprises one or more selected from the group consisting of:

W: 0.001% by mass or more and 0.5% by mass or less,
Nb: 0.001% by mass or more and 0.1% by mass or less,
Ti: 0.001% by mass or more and 0.1% by mass or less,
Zr: 0.001% by mass or more and 0.1% by mass or less, and
V: 0.002% by mass or more and 0.5% by mass or less.

6. The bearing steel according to claim 2, wherein the composition further comprises B: 0.0002% by mass or more and 0.005% by mass or less.

7. The bearing steel according to claim 3, wherein the composition further comprises B: 0.0002% by mass or more and 0.005% by mass or less.

8. The bearing steel according to claim 5, wherein the composition further comprises B: 0.0002% by mass or more and 0.005% by mass or less.

Patent History
Publication number: 20130017117
Type: Application
Filed: Nov 30, 2010
Publication Date: Jan 17, 2013
Applicant: JFE Steel Corporation (Tokyo)
Inventors: Minoru Honjo (Okayama), Kazukuni Hase (Okayama), Hideto Kimura (Aichi)
Application Number: 13/512,668
Classifications
Current U.S. Class: Nickel Containing (420/91); Over 0.1 Percent Aluminum Containing, But Less Than 4 Percent (420/103); Chromium Containing, But Less Than 9 Percent (420/104); Tungsten Containing (420/114)
International Classification: C22C 38/18 (20060101); C22C 38/44 (20060101); C22C 38/32 (20060101); C22C 38/26 (20060101); C22C 38/28 (20060101); C22C 38/24 (20060101); C22C 38/42 (20060101); C22C 38/22 (20060101);