Flux cored preforms for brazing

- Lucas-Milhaupt, Inc.

A wire preform suitable for use in brazing components to one another. The preform is made from a length of wire having a core of flux material, and a longitudinal seam or gap that extends over the length of the wire. The seam is formed so that when heated, the flux material flows from the core and out of the seam. The length of wire is in the form of a loop having a certain circumference so that when the preform is heated, the flux material disperses uniformly from the circumference of the preform for evenly treating the surface of a component on which the preform is placed. The length of wire may include a silver alloy.

Skip to: Description  ·  Claims  ·  References Cited  · Patent History  ·  Patent History
Description
CROSS-REFERENCE(S) TO RELATED APPLICATION(S)

Notice: More than one reissue application has been filed for the reissue of U.S. Pat. No. 6,830,632. The present reissue application is a divisional reissue application of U.S. Ser. No. 11/639,356, now U.S. Pat. No. Re. 42,329. A continuation of this present reissue application, U.S. Ser. No. 13/010,144 has also been filed.

FIELD OF THE INVENTION

    • The present invention is directed to wire preforms for use in brazing.

DISCUSSION OF THE KNOWN ART

The brazing process typically involves joining ferrous and non-ferrous metal components together by positioning a brazing composition (such as an aluminum or silver-bearing metal alloy) and a flux adjacent to or between surfaces of the components to be joined, also known as the faying surfaces. To form the joint, the metal alloy and flux and the faying surfaces are heated to a temperature typically above the melting temperature of the alloy but below the melting temperature of the components to be joined. The alloy then melts, flows into the faying surfaces by capillary action and forms a seal that bonds the faying surfaces to one another.

A flux composition is often applied to the faying surfaces prior to brazing. In one application, a flux can be selected so that, when applied, it does one or more of the following: (1) removes oxides ordinarily present on the faying surfaces; (2) promotes the flow of the molten brazing alloy when heated to a temperature above its melting point; and (3) inhibits further oxide formation on the faying surfaces.

Flux cored wire ring preforms for brazing are known to have been made using an aluminum/silicon metal alloy. When heated, the alloy tends to men melt quickly enough to allow the core flux material to disperse fairly evenly and to enable satisfactory joints to be made. A known supplier of flux cored aluminum rin ring preforms is Omni Technologies Corporation.

Initial attempts to make silver alloy flux cored braze ring preforms using the same design principles as the aluminum preforms were met with little initial success, however. Specifically, when the silver preforms were heated, the flux would not disperse evenly about the rings but, rather, would exit only from opposite ends of the silver wire forming the preforms before melting of the wire itself. As a result the braze joints were poor.

Accordingly, there is a need for a flux cored braze ring preform that, during heating, will disperse its core flux material evenly about the ring and onto a surface to be treated for brazing. In particular, there is a need for such preforms made of silver alloys.

SUMMARY OF THE INVENTION

The present invention is directed to a flux cored brazing preform. A metal alloy is provided as an elongated thin sheet that is rolled around its long axis so as to encase a flux material. The rolled metal alloy sheet thus forms a flux cored wire having a longitudinal seam through which the flux material, when in a molten state, can exit.

The flux cored wire is then shaped into a braze ring preform which when heated allows the encased flux material to flow uniformly from the seam about the circumference of the preform, and to disperse evenly for treating a surface to be brazed.

BRIEF DESCRIPTION OF THE DRAWINGS

In the drawing:

FIG. 1 is a flow chart depicting a method of producing lengths of seamed brazing wire for shaping into brazing preforms according to the invention: ;

FIG. 2 is a cross sectional view of the brazing wire produced according to FIG. 1; and

FIGS. 3 to 5 show brazing preforms according to the invention.

DETAILED DESCRIPTION OF THE INVENTION

In general, seamed flux cored brazing wires can be produced in accordance with procedures disclosed in French Patent Application no. 78 12546, published Nov. 25, 1977, and the seam area of the rolled sheet of metal may be modified as described herein. Other seamed flux cored brazing or welding wires are disclosed in, for example, U.S. Pat. No. 3,935,414 (Jan. 27, 1976); U.S. Pat. No. 1,629,748 (May 24, 19271); U.S. Pat. No. 4,379,811 (Apr. 12, 1983); U.S. Pat. No. 2,958,941 (Nov. 8, 1960); U.S. Pat. No. 4,396,822 (Aug. 2, 1983); U.S. Pat. No. 3,642,998 (Nov. 24, 1970); and Japanese Patent No. 63-303694 (Dec. 1, 1988).

As represented in FIG. 1, a narrow elongate elongated strip of a metal alloy which may have been coiled onto a spool to facilitate the feeding thereof during the manufacturing process is formed into a U-shape U-shaped channel by a first die. The U-shaped channel is passed through a trough by pulling the strip in a direction away from the spool or other dispensing apparatus. A powdered flux material is conveyed from a dispenser so as to drop from the dispenser into a trough which contains the U-shaped channel and to over-fill the trough. A vibrating apparatus is typically employed to vibrate the trough in order to fill the strip. Optionally, lasers may be employed to ensure that the amount of flux that fills the metal alloy strip is sufficient to form an adequate brazed joint. The filled strip is passed out of the trough, though through a second die where the filled channel begins to close. The wire then passes through a third die where the wire is closed and a butt seam is formed with the opposing side edge portions of the strip.

The wire then passes through a fourth die which forces an edge portion of the seam inward, e.g., about 0.005″ to 0.010″. This portion is maintained to about 45 degrees or less of the circumference of the wire, and leaves a gap between the opposed edge portions of strip. The inner edge portion extends toward the center of the cored wire, and the space between the edge portions contains flux. See , see FIG. 2 , . It is believed that this creates a path for the flux in the center of the core to release from the core.

The wire then passes through a fifth die where the wire is formed to its final size diameter, while maintaining the seam as described above. The flux cored wire is then packaged on spools and other suitable packaging systems.

The metal alloy strip can be any of the following alloys, among others: aluminum-silicone; zinc-aluminum; copper zinc; silver-copper-zinc; silver-copper-zinc-tin; silver copper-zinc-tin-nickel; silver-copper-zinc-nickel; silver-copper-tin; silver-copper-zinc-manganese-nickel; silver-copper-zinc-cadmium; and silver-copper-zinc-cadmium and nickel.

The flux-cored brazing wire formed as described above can subsequently be formed to into brazing preforms having any desired shape, such as a circle or oval. The preforms can then be placed between or adjacent to faying surfaces of components to be joined. The preforms and the faying surfaces are then heated to a suitable brazing temperature sufficient to melt the flux and the brazing alloy and, thus, bond the faying surfaces. The components are then cooled to solidify the brazing alloy and to secure the bond between the faying surfaces.

As shown in cross section in FIG. 2, the flux cored wire 10 includes the rolled metal alloy sheet 12 that defines an encasing perimeter that extends around the flux material 14 of the core. An inner angled edge portion 16 of the sheet 12 is embedded in the flux material 14. Moving counter-clockwise in FIG. 2, the inner angled edge portion 16 of the sheet 12 emerges from the core and the sheet 12 extends around the flux material, and an outer edge portion 18 of the sheet 12 confronts the sheet 12 in the vicinity of the location where inner angled edge portion 16 of the sheet 12 emerges from the core, thereby forming a seam 20. Between the inner angled edge portion 16 and the outer edge portion of the sheet, there is a gap 22, in which a portion of the flux material 14 resides. Also, the inner angled edge portion 16 is surrounded by flux material.

The metal alloy strip 12 may be formed or bowed into a brazing wire having a cross section of any desired shape and size. For example, the strip 12 may be rolled about its longitudinal axis in a substantially circular manner to form the wire 10 in FIG. 2. Once rolled, a length of the wire may be shaped, twisted or molded into various shapes, for example, adopting a configuration that is complementary to the various angles and sizes of the surfaces to be brazed. In specific embodiments, as illustrated in FIGS. 3 to 5, the wire can be formed into braze rings or helical loops having a circular cross-section, and further having a wire diameter between about 0.031 and 0.125 inches.

As mentioned, the seamed, flux cored brazing wire 10 may be manufactured by other techniques that are known in the art. For example, roll forming technology, alone and in combination with dies, can be employed to produce a cored wire. The cored wires may also be produced with a gap to allow flux dispersion from the seam.

Cored wire with a butt seam may also be produced, and due to other factors (like an oval, square or other shape of preforms made from the wire) the flux will be allowed to escape from the seam during brazing.

FIGS. 3 to 5 demonstrate flux distribution along the seam of flux-coated wire preforms made according to the invention. A copper coupon 40 is held in place by a clamping device 42 and suspended in the horizontal position. A flux-cored ring (preform 44 made from a length of seamed flux cored wire) is set upon the top surface of the copper coupon 40. Heat (from a propane, butane or similar torch) is applied to the bottom of the coupon.

When the flux-cored preform 44 reaches a temperature between 500 and 1100° F., flux can be seen dispersing from the wire seam uniformly along the full circumference of the preform 44 as shown in FIG. 4. Note the metal alloy strip is still in solid form, but the flux is being uniformly dispensed from the seam around the entire ring preform.

FIG. 5 shows a multi-turn helical loop preform 50 according to the invention, wherein the coupon 40 and the preform 50 are heated sufficient to cause molten flux material to disperse uniformly from a seam along the inner circumference of the preform, and the then evenly over the top surface of the coupon 40.

While there have been described what are at present considered to be the preferred embodiments of this invention, it will be obvious to those skilled in the art that various changes and modifications may be made thin without departing from the true spirit and scope of the invention defined by the following claims.

Claims

1. A wire preform suitable for use in brazing components to one another, comprising:

a length of wire having a core of a flux material, and a longitudinal seam or gap extending over the length of the wire wherein the seam is formed so that when heated, the flux material flows from the core and out of the seam of the wire; and
the length of wire is in the form of a loop having a certain circumference so that when the preform is heated, flux material is dispersed uniformly from the circumference of the preform for evenly treating a component surface on which the preform is disposed.

2. A wire preform according to claim 1, wherein the length of wire is formed from an elongate metal sheet, and the seam of the wire is defined by an inner edge portion of the sheet and a confronting outer edge portion of the sheet.

3. A wire preform according to claim 2, wherein the inner edge portion of the metal sheet is angled to be embedded in the flux material.

4. A wire preform according to claim 1, wherein the seam on the length of wire is on the inner circumference of the preform.

5. A wire preform according to claim 1, wherein the length of wire is helical in form.

6. A wire preform according to claim 5, wherein the seam on the circumference of the preform.

7. A wire preform according to claim 1, wherein the wire has a diameter of between about 0.031 inch and 0.125 inch.

8. A wire preform according to claim 1, wherein the length of wire comprises a silver alloy.

9. A preform comprising:

a length of metal having a core of a flux material for joining components to one another, and a longitudinal gap extending over the length of the metal;
wherein the gap is formed to allow the flux material to evenly flow from the core and out of the gap of the metal; and
wherein the length of metal is formed into a ring, and the gap of the metal is defined by an inner circumference portion of the ring.

10. The preform of claim 9, wherein the preform may be at least one of: an oval, a square, a multi-form helical loop; a braze ring; a helical shape having a circular cross-section; and a wire having a diameter between about 0.031 and about 0.125 inches.

11. The preform of claim 9, wherein when the preform reaches a temperature between approximately 500 and approximately 1100 degrees F., flux is dispersed from the gap uniformly along a circumference of the preform.

12. The preform of claim 9, wherein the flux has a melting temperature of approximately 500 and approximately 1100 degrees F., and wherein the metal has a melting temperature at least above the melting temperature of the flux.

13. A material for joining components to one another comprising:

a length of metal formed into a U-shaped channel by a die;
a core of flux in the U-shaped channel created by passing the channel through a trough by pulling the length of metal in a direction away from a dispensing apparatus;
at least one wall of metal around the core; and
a path for the flux from the core to aid in release of the flux;
wherein the metal then passes through another die and is formed to its final size diameter, while maintaining the path;
wherein when the metal is heated, the flux is dispersed from the core to evenly treat a component surface;
wherein the flux has a melting temperature and the length of metal has a melting temperature at least above the melting temperature of the flux.

14. The material of claim 13, wherein the material is then packaged in spools.

15. The material of claim 13, wherein the metal is an alloy of at least one of the following: aluminum-silicon; zinc-aluminum; copper zinc; silver-copper-zinc; silver-copper-zinc-tin; silver copper-zinc-tin-nickel; silver-copper-zinc-nickel; silver-copper-tin; silver-copper-zinc-manganese-nickel; silver-copper-zinc-cadmium; and silver-copper-zinc-cadmium.

16. The material of claim 13, wherein the length of metal is a narrow elongate strip coiled onto a spool to facilitate feeding of the length of metal during a manufacturing process.

17. The material of claim 13, wherein the material is formed into a brazing wire having a size and a cross section of a desired shape and adopting a configuration that is complementary to various angles and sizes of surfaces to be brazed.

18. The material of claim 13, wherein the core has a cross-section in the shape of an oval.

19. The material of claim 13, wherein the core has a cross-section defined by at least first and second walls that are substantially perpendicular to one another.

20. The material of claim 19 wherein the core has a cross-section in the shape of a square.

21. The material of claim 13 is in the shape of a helical loop.

22. The material of claim 13 is formed into a braze ring preform.

23. The material of claim 13 wherein the core has a circular cross-section.

24. The material of claim 13 wherein the length of metal wrapped around the core has a diameter between about 0.031 and about 0.125 inches.

25. The material of claim 13 wherein a butt seam is formed between opposed ends of the length of metal, and wherein the path is defined at the butt seam.

26. The material of claim 13 arranged into a preform having an inner perimeter surface and an outer perimeter surface, wherein the butt seam is formed along the inner perimeter surface.

27. The material of claim 13 wherein the path is formed by overlapping portions of the metal.

28. The material of claim 13, wherein the metal's final size diameter includes a measurement of cross sectional width for any shape.

29. The material of claim 13, wherein the dies may include any manufacturing die, including roll forming dies.

30. A material for joining components to one another comprising:

a length of metal formed into a U-shaped channel by a die;
a core of flux in the U-shaped channel created by passing the channel through a trough by pulling the length of metal in a direction away from a dispensing apparatus;
at least one wall of metal around the core; and
a path for the flux from the core to aid in release of the flux;
wherein the metal then passes through another die and is formed to its final size and shape, while maintaining the path;
wherein when the metal is heated, the flux is dispersed from the core to evenly treat a component surface;
wherein the flux has a melting temperature and the length of metal has a melting temperature at least above the melting temperature of the flux.
Referenced Cited
U.S. Patent Documents
400869 April 1889 Norton et al.
607504 July 1898 Crowther
1650905 December 1925 Mills
1629748 May 1927 Stoody
1865169 July 1927 Candy
1968618 February 1932 Padgett et al.
1972315 September 1934 Ramey
2005189 June 1935 Herr
2055276 September 1936 Brownsdon et al.
2279284 April 1942 Wasserman
2442087 March 1945 Kennedy
2465503 October 1947 Woods
2499641 March 1950 Goody
2565477 August 1951 Crowell et al.
2785285 March 1953 Bernard
2927043 March 1960 Stetson
2958941 November 1960 Goerg
3033713 May 1962 Bielenberg et al.
3051822 August 1962 Bernard et al.
3077131 February 1963 McShane
3162551 December 1964 Short
3198560 August 1965 Collins
3239125 March 1966 Sherlock
3245141 April 1966 Gruetjen
3290772 December 1966 Crouch
3318729 May 1967 Siegle et al.
3365565 January 1968 Claussen
3452419 July 1969 Hillert
3534390 October 1970 Woods et al.
3542998 November 1970 Huff
3555240 January 1971 Gloor et al.
3558851 January 1971 Oku
3610663 October 1971 Lago
3619429 November 1971 Torigai et al.
3620830 November 1971 Kramer
3620869 November 1971 Stump et al.
3639721 February 1972 Hubbel
3642998 February 1972 Jennings
3688967 September 1972 Arikawa et al.
3695795 October 1972 Jossick
3703254 November 1972 Maierson et al.
3745644 July 1973 Moyer et al.
3935414 January 27, 1976 Ballass et al.
3967036 June 29, 1976 Sadowski
3980859 September 14, 1976 Leonard
4041274 August 9, 1977 Sadowski
4121750 October 24, 1978 Schoer et al.
4134196 January 16, 1979 Yamaji et al.
4174962 November 20, 1979 Frantzreb, Sr. et al.
4214145 July 22, 1980 Zvanut et al.
4301211 November 17, 1981 Sloboda
4379811 April 12, 1983 Puschner et al.
4396822 August 2, 1983 Kishida et al.
4430122 February 7, 1984 Pauga
4447472 May 8, 1984 Minnick et al.
4493738 January 15, 1985 Collier et al.
4497849 February 5, 1985 Hughes et al.
4571352 February 18, 1986 Aoki
4587097 May 6, 1986 Rabinkin et al.
4587726 May 13, 1986 Holmgren
4624860 November 25, 1986 Alber et al.
4708897 November 24, 1987 Douchy
4762674 August 9, 1988 Cheng et al.
4785092 November 15, 1988 Nanba et al.
4800131 January 24, 1989 Marshall et al.
4831701 May 23, 1989 Yutaka
4900895 February 13, 1990 Marshall
4901909 February 20, 1990 George
4993054 February 12, 1991 Ujari
5098010 March 24, 1992 Carmichael et al.
5175411 December 29, 1992 Barber
5184767 February 9, 1993 Estes
5280971 January 25, 1994 Tokutake et al.
5316206 May 31, 1994 Syslak et al.
5360158 November 1, 1994 Conn et al.
5418072 May 23, 1995 Baldantoni et al.
5575933 November 19, 1996 Ni
5749971 May 12, 1998 Ni
5759707 June 2, 1998 Belt et al.
5781846 July 14, 1998 Jossick
5791005 August 11, 1998 Grabowski et al.
5806752 September 15, 1998 Van Evans et al.
5820939 October 13, 1998 Popoola et al.
5903814 May 11, 1999 Miura et al.
5917141 June 29, 1999 Naquin
6093761 July 25, 2000 Schofalvi
6204316 March 20, 2001 Schofalvi
6244397 June 12, 2001 Kars
6248860 June 19, 2001 Sant'Angelo et al.
6264062 July 24, 2001 Lack et al.
6277210 August 21, 2001 Schuster
6317913 November 20, 2001 Kilmer et al.
6344237 February 5, 2002 Kilmer et al.
6376585 April 23, 2002 Schofalvi et al.
6395223 May 28, 2002 Schuster et al.
6409074 June 25, 2002 Katoh et al.
6417489 July 9, 2002 Blankenship et al.
6426483 July 30, 2002 Blankenship et al.
6432221 August 13, 2002 Seseke-Koyro et al.
6497770 December 24, 2002 Watsuji et al.
6680359 January 20, 2004 Schoenheider
6713593 March 30, 2004 Ree et al.
6733598 May 11, 2004 Swidersky et al.
6830632 December 14, 2004 Fuerstenau et al.
6846862 January 25, 2005 Schofalvi et al.
6864346 March 8, 2005 Schoenheider
6881278 April 19, 2005 Amita et al.
7337941 March 4, 2008 Scott et al.
7442877 October 28, 2008 Kmata et al.
20020005230 January 17, 2002 Watsuji et al.
20030203137 October 30, 2003 Teshima et al.
20040009358 January 15, 2004 Scott et al.
20040171721 September 2, 2004 Esemplare
20050129855 June 16, 2005 Kamata et al.
20090077736 March 26, 2009 Loberger et al.
20110023319 February 3, 2011 Fukaya et al.
Foreign Patent Documents
4936179 July 1980 AU
878006 January 1980 BE
1146025 May 1983 CA
1303605 June 1992 CA
2931040 February 1980 DE
60120250 April 2007 DE
323379 February 1980 DK
0991697 April 2000 EP
1127653 August 2001 EP
483021 April 1980 ES
7812546 November 1977 FR
2432360 February 1980 FR
692710 June 1953 GB
1180735 February 1970 GB
1481140 July 1977 GB
2027617 February 1980 GB
48459 January 1985 IE
152853 April 1984 IN
1193704 August 1988 IT
55045591 March 1980 JP
62034698 February 1987 JP
63040697 February 1988 JP
63303694 December 1988 JP
1066093 March 1989 JP
2179384 July 1990 JP
3005094 January 1991 JP
H3-5094 January 1991 JP
3204169 September 1991 JP
4371392 December 1992 JP
6007987 January 1994 JP
11347783 December 1999 JP
2002512655 April 2002 JP
7905877 February 1980 NL
792504 February 1980 NO
7906495 February 1980 SE
WO99/00444 January 1999 WO
WO9900444 January 1999 WO
WO00/39172 July 2000 WO
WO00/52228 September 2000 WO
WO00/64626 November 2000 WO
WO02/00569 January 2002 WO
WO02/31023 April 2002 WO
WO03/068447 August 2003 WO
WO03/089176 October 2003 WO
7903893 July 1980 ZA
Other references
  • International Search Report dated Dec. 21, 2007; PCT/US06/043856 filed Nov. 9, 2006.
  • Written Opinion of the ISA dated May 10, 2008.; PCT/US06/043856 filed Nov. 9, 2006.
  • International Preliminary Report on Patentability dated May 14, 2008; PCT/US06/043856 filed Nov. 9, 2006.
  • International Search Report dated Dec. 4, 2008; PCT/US08/064871 filed May 27, 2008.
  • Written Opinion of the ISA dated Nov. 25, 2009; PCT/US08/064871 filed May 27, 2008.
  • International Preliminary Report dated Dec. 1, 2009; PCT/US08/064871 filed May 27, 2008.
  • International Search Report dated Apr. 9, 2008; PCT/US07/025309 filed Dec. 11, 2007.
  • Written Opinion of the ISA dated Jun. 11, 2009; PCT/US07/025309 filed Dec. 11, 2007.
  • International Preliminary Report dated Jun. 16, 2009; PCT/US07/025309 filed Dec. 11, 2007.
  • Belohlav, “Understanding Brazing Fundamentals,” The American Welder; Sep.-Oct. 2000; Jul. 11, 2008; <http://www.aws.org/wyamwelder/9-00/fundamentals.html>.
  • International Search Report dated Nov. 8, 2007; PCT/US07/069636 filed May 24, 2007.
  • Written Opinion of the ISA dated Nov. 8, 2007; PCT/US07/069636 filed May 24, 2007.
  • International Preliminary Report dated Nov. 28, 2008; PCT/US07/069636 filed May 24, 2007.
  • European Search Report, dated Jun. 22, 2012 for Application No. PCT/US2006043856.
Patent History
Patent number: RE44343
Type: Grant
Filed: Jul 12, 2010
Date of Patent: Jul 9, 2013
Assignee: Lucas-Milhaupt, Inc. (Cudahy, WI)
Inventors: Charles E. Fuerstenau (Greenville, WI), Alan Belohlav (Belgium, WI)
Primary Examiner: Weiping Zhu
Application Number: 12/834,506
Classifications
Current U.S. Class: Fluxing (148/23)
International Classification: B23K 35/34 (20060101);