Buffer compositions

Buffer compositions comprising semiconductive oxide particles and at least one of (a) a fluorinated acid polymer and (b) a semiconductive polymer doped with a fluorinated acid polymer are provided. Semiconductive oxide particles include metal oxides and bimetallic oxides. Acid polymers are derived from monomers or comonomers of polyolefins, polyacrylates, polymethacrylates, polyimides, polyamides, polyaramides, polyacrylamides, polystrenes. The polymer backbone, side chains, pendant groups or combinations thereof may be fluorinated or highly fluorinated. Semiconductive polymers include polymers or copolymers derived from thiophenes, pyrroles, anilines, and polycyclic heteroaromatics. Methods for preparing buffer compositions are also provided. A buffer composition consisting essentially of semiconductive oxide particles wherein the semiconductive oxide particles comprise a bimetallic oxide selected from indium-tin oxide (“ITO”), indium-zinc oxide (“IZO”), gallium-indium oxide, and zinc-antimony double oxide and a fluorinated acid polymer wherein the fluorinated acid polymer has a formula according to Formula XV: where j≧0, k≧0 and 4≦(j+k)≦199, Q1 and Q2 are F or H, Rf2 is F or a perfluoroalkyl radical having 1-10 carbon atoms either unsubstituted or substituted by one or more ether oxygen atoms, h=0 or 1, i=0 to 3, g=0 or 1, wherein the buffer composition has a work-function greater than 5.0 eV. In some embodiments, the H on the SO3 may be replaced by either Li, Na, or K.

Skip to: Description  ·  Claims  ·  References Cited  · Patent History  ·  Patent History
Description
RELATED U.S. APPLICATIONS

This application claims priority to U.S. provisional application, Ser. No. 60/694,794, filed Jun. 28, 2005.

BACKGROUND INFORMATION

1. Field of the Disclosure

This disclosure relates in general to high work function transparent conductors for use in electronic devices.

2. Description of the Related Art

Organic electronic devices define a category of products that include an active layer. Such devices convert electrical energy into radiation, detect signals through electronic processes, convert radiation into electrical energy, or include one or more organic semiconductor layers.

Organic light-emitting diodes (OLEDs) are organic electronic devices comprising an organic layer capable of electroluminescence. OLEDs containing conducting polymers can have the following configuration;

anode/buffer layer/EL material/cathode

Additional, optional layers, materials or components may be incorporated into this general configuration. The anode is typically any material that has the ability to inject holes into the electroluminescent (“EL”) material, such as, for example, indium/tin oxide (ITO). The anode is optionally supported on a glass or plastic substrate. The buffer layer is typically an electrically conducting polymer and facilitates the injection of holes from the anode into the EL material layer. EL materials include fluorescent compounds, fluorescent and phosphorescent metal complexes, conjugated polymers, and mixtures thereof. The cathode is typically any material (such as, e.g., Ca or Ba) that has the ability to inject electrons into the EL material. At least one of the anode or cathode is transparent or semi-transparent to allow for light emission.

ITO is frequently used as the transparent anode. However, the work function of ITO is relatively low, typically in the range of 4.6 eV. This results in less effective injection of holes into the EL material. In some cases, the work function of ITO can be improved by surface treatment. However, these treatments sometime result in products that are note stable and further result in reduced device lifetime.

Accordingly, there is a need for compositions and layers prepared therefrom to improve the properties of the device.

SUMMARY

There is provided a buffer composition comprising semiconductive oxide particles and at least one of (a) a fluorinated acid polymer and (b) a semiconductive polymer doped with a fluorinated acid polymer.

In another embodiment, there is provided a buffer layer made from the new buffer composition.

In another embodiment, there is provided an electronic device comprising the buffer layer.

The foregoing general description and the following detailed description are exemplary and explanatory and are not restrictive of the invention, as defined in the specification and appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention is illustrated by way of example and not limitation in the accompanying figures.

FIG. 1 is a diagram illustrating contact angle.

FIG. 2 is a schematic diagram of an organic electronic device.

Skilled artisans appreciate that objects in the figures are illustrated for simplicity and clarity and have not necessarily been drawn to scale. For example, the dimensions of some of the objects in the figures may be magnified relative to other objects to help to improve understanding of embodiments.

DETAILED DESCRIPTION

There is provided a buffer composition comprising semiconductive oxide particles and at least one of (a) a fluorinated acid polymer and (b) a semiconductive polymer doped with a fluorinated acid polymer.

Many aspects and embodiments are described herein and are exemplary and not limiting. After reading this specification, skilled artisans will appreciate that other aspects and embodiments are possible without departing from the scope of the invention.

As used herein, the term “semiconductive” refers to material having electrical conductivity greater than insulators but less than good conductors. In one embodiment, a film of a semiconductive material has a conductivity of less than 0.1 S/cm and greater than 10−8 S/cm. The term “fluorinated acid polymer” refers to a polymer having acidic groups, where at least some of the hydrogens have been replaced by fluorine. Fluorination can occur on the polymer backbone, on side chains attached to the backbone, in pendant groups, or in combinations of these. The term “acidic group” refers to a group capable of ionizing to donate a hydrogen ion to a base to form a salt. As used herein, the term “semiconductive polymer” refers to any polymer or oligomer which is inherently or intrinsically capable of electrical conductivity without the addition of carbon black or conductive metal particles. The term “polymer” encompasses homopolymers and copolymers. The term “doped” is intended to mean that the semiconductive polymer has a polymeric counterion derived from a polymeric acid to balance the charge on the conductive polymer.

1. Semiconductive Oxide Particles

In one embodiment, semiconductive oxide materials comprise an oxide of an element selected ken group 2 through group 12 of the periodic table. In one embodiment, semiconductive oxide materials comprise an oxide of an element selected from group 2 and group 12. Group numbers corresponding to columns within the periodic table of the elements use the “New Notation” convention as seen in the CRC Handbook of Chemistry and Physics, 81st Edition (2000), where the groups are numbered from left to right as 1-18.

In one embodiment, the inorganic semiconductive material is an inorganic oxide which may be a bimetallic oxide, such as NixCox-1O3/4 (Science, p 1273-1276, vol 305, Aug. 27, 2004), indium-tin oxide (“ITO”), indium-zinc oxide (“IZO”), gallium-indium oxide, zinc-antimony double oxide and zirconium, or antimony doped oxide.

2. Semiconductive Polymer

Any semiconductive polymer can be used in the new composition. In one embodiment, the semiconductive polymer will form a film which has a conductivity of at least 10−2 S/cm. The conductive polymers suitable for the new composition can be homopolymers, or they can be copolymers of two or more respective monomers. The monomer from which the conductive polymer is formed, is referred to as a “precursor monomer”. A copolymer will have more than one precursor monomer.

In one embodiment, the semiconductive polymer is made from at least one precursor monomer selected from thiophenes, pyrroles, anilines, and polycyclic aromatics. The polymers made from these monomers are referred to herein as polythiophenes, polypyrroles, polyanilines, and polycyclic aromatic polymers, respectively. The term “polycyclic aromatic” refers to compounds having more than one aromatic ring. The rings may be joined by one or more bonds, or they may be fused together. The term ‘aromatic ring’ is intended to include heteroaromatic rings. A “polycyclic heteraromatic” compound has at least one heteroaromatic ring.

In one embodiment, thiophene monomers contemplated for use to form the semiconductive polymer comprise Formula I below:


wherein:

    • R1 is independently selected so as to be the same or different at each occurrence and is selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkylthio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, amidosulfonate, ether sulfonate, ester sulfonate, and urethane; or both R1 groups together may form an alkylene or alkenylene chain completes a 3, 4, 5, 6 or 7-membered aromatic or alicyclic ring, which ring may Optionally include one or more divalent nitrogen, sulfur or oxygen atoms.

As used herein, the term “alkyl” refers to a group derived from an aliphatic hydrocarbon and includes linear, branched and cyclic groups which may be unsubstituted or substituted. The term “heteroalkyl” is intended to mean an alkyl group, wherein one or more of the carbon atoms within the alkyl group has been replaced by another atom, such as nitrogen, oxygen, sulfur, and the like. The term “alkylene” refers to an alkyl group haying two points of attachment.

As used herein, the term “alkenyl” refers to a group derived From an aliphatic hydrocarbon having at least one carbon-carbon double bond, and includes linear, branched and cyclic groups which may be unsubstituted or substituted. The term “heteroalkenyl” is intended to mean alkenyl group, wherein one or more of the carbon atoms within the alkenyl group has been replaced by another atom, such as nitrogen, oxygen, sulfur, and the like. The term “alkenylene” refers to an alkenyl group having two points of attachment.

As used herein, the following terms for substituent groups refer to the formulae given below:

“alcohol” —R3—OH “amido” —R3—C(O)N(R6) R6 “amidosulfonate” —R3—C(O)N(R6) R4—SO3Z “benzyl” —CH2—C6H5 “carboxylate” —R3—C(O)O—Z or —R3—O—C(O)—Z “ether” —R3—(O—R5)p—O—R5 “ether carboxylate” —R3—O—R4—C(O)O—Z or —R3—O—R4—O—C(O)—Z “ether sulfonate” —R3—O—R4—SO3Z “ester sulfonate” —R3—O—C(O)—R4—SO3Z “sulfonimide” —R3—SO2—NH—SO2—R5 “urethane” —R3—O—C(O)—N(R6)2

where all “R” groups are the same or different at each occurrence and:
    • R3 is a single bond or an alkylene group
    • R4 is an alkylene group
    • R5 is an alkyl group
    • R6 is hydrogen or an alkyl group
    • p is 0 or all integer from I to 20
    • Z is H, alkali metal, alkaline earth metal, N(R5)4 or R5
      Any of the above groups may further be unsubstituted or substituted, and any group may have F substituted for one or more hydrogens, including perfluorinated groups. In one embodiment, the alkyl and alkylene groups have from 1-20 carbon atoms.

In one embodiment, in the thiophene monomer, both R1 together form —O—(CHY)in—O—, wherein m is 2 or 3, and Y is the same or different at each occurrence and is selected from hydrogen, halogen, alkyl, alcohol, amidosulfonate, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane, where the Y groups may be partially or fully fluorinated. In one embodiment, all Y are hydrogen. In one embodiment, the polythiophene is poly(3,4-ethylenedioxythiophene). In one embodiment, at least one Y group is not hydrogen. In one embodiment, at least one Y group is a substituent having F substituted for at least one hydrogen. In one embodiment, at least one Y group is perfluorinated.

In one embodiment, the thiophene monomer has Formula I(a):


wherein:.

    • R7 is the same or different at each occurrence and is Selected from hydrogen, alkyl, heteroalkyl, alkenyl, heteroalkenyl, Alcohol, amidosulfonate, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate and urethane, with the proviso that at least one R7 is not hydrogen, and
    • m is 2 or 3.

In one embodiment of Formula I(a), m is two, one R7 is an Alkyl group of more than 5 carbon atoms, and all other R7 are Hydrogen. In one embodiment of Formula I(a), at least one R7 group is fluorinated. In one embodiment, at least one R7 group has at least one fluorine substituent. In one embodiment, the R7 group is fully fluorinated.

In one embodiment of Formula I(a), the R7 substituents on the fused alicyclic ring on the thiophene offer improved solubility of the monomers in water and facilitate polymerization in the presence of the fluorinated acid polymer.

In one embodiment of Formula I(a), m is 2, one R7 is sulfonic acid-propylene-ether-methylene and all other R7 are hydrogen. In one embodiment, m is 2, one R7 is propyl-ether-ethylene and all other R7 are hydrogen. In one embodiment, m is 2, one R7 is methoxy and all other R7 are hydrogen. In one embodiment, one R7 is sulfonic acid difluoromethylene ester methylene (—CH2—O—C(O)—CF2—SO3H), and all other R7 are hydrogen.

In one embodiment, pyrrole monomers contemplated for use to form the semiconductive polymer comprise Formula II below.


where in Formula II:

    • R1 is independently selected so as to be the same or different at each occurrence and is selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkythio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, amidosulfonate, ether carboxylate, ether sulfonate, ester sulfonate, and urethane; or both R1 groups together may form an alkylene or alkenylene chain completing a 3, 4, 5, 6, or 7-membered aromatic or alicyclic ring, which ring may Optionally include one or more divalent nitrogen, sulfur or oxygen atoms; and
    • R2 is independently selected so as to be the same or different at each occurrence and is selected from hydrogen, alkyl, alkenyl, aryl, alkanoyl, alkylthioalkyl, alkylaryl, arylalkyl, amino, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane.

In one embodiment, R1 is the same or different at each occurrence and is independently selected from hydrogen, alkyl, alkenyl, alkoxy, cycloalkyl, cycloalkenyl, alcohol, benzyl, carboxylate, ether, amidosulfonate, ether carboxylate, ether sulfonate, ester sulfonate, urethane, epoxy, silane, siloxane, and alkyl substituted with one or more of sulfonic acid, carboxylic acid, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, cyano, hydroxyl, epoxy, silane, or siloxane moieties.

In one embodiment, R2 is selected from hydrogen, alkyl, and alkyl substituted with one or more of sulfonic acid, carboxylic acid, acrylic acid, phosphoric acid, phosphonic acid, halogen, cyano, hydroxyl, epoxy, silane or siloxane moieties.

In one embodiment, the pyrrole monomer is unsubstituted and both R1 and R2 are hydrogen.

In one embodiment, both R1 together form a 6- or 7-membered alicyclic ring, which is further substituted with a group selected from alkyl, heteroalkyl, alcohol, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane. These groups can improve the solubility of the monomer and the resulting polymer. In one embodiment, both R1 together form a 6- or 7-membered alicyclic ring, which is further substituted with an alkyl group. In one embodiment, both R1 together form a 6- or 7-membered cyclic ring, which is further substituted with an alkyl group having at least 1 carbon atom.

In one embodiment, both R1 together form —O—(CHY)M—O—, where m is 2 or 3, and Y is the same or different at each occurrence and is selected from hydrogen, alkyl, alcohol, benzyl, carboxylate, amidosulfonate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane. In one embodiment, at least one Y group is not hydrogen. In one embodiment, at least one Y group is a substituent having F substituted for at least one hydrogen. In one embodiment, at least one Y group is perfluorinated.

In one embodiment, aniline monomers contemplated for use to form the semiconductive polymer comprise Formula III below.


wherein:

    • a is 0 or an integer from 1 to 4;
    • b is an integer from 1 to 5, with the proviso that a+b=5; and R1 is independently selected so as to be the same or different at each occurrence and is selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkythio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, amidosulfonate, ether sulfonate, ester sulfonate, and urethane; or both R1 groups together may form an alkylene or alkenylene chain completing a 3, 4, 5, 6, or 7-membered aromatic or alicyclic ring, which ring may optionally include one or more dilvanet nitrogen, sulfur or oxygen atoms.

When polymerized, the aniline monomeric unit can have Formula IV(a) or Formula IV(b) shown below, or a combination of both formulae.


where a, b and R1 are as defined above.

In one embodiment, the aniline monomer is unsubstituted and a=0.

In one embodiment, a is not 0 and at least one R1 is fluorinated. In one embodiment, at least one R1 is perfluorinated.

In one embodiment, fused polycyclic heteroaromatic monomers contemplated for use to form the semiconductive polymer have two or more fused aromatic rings, at least one of which is heteroaromatic. In one embodiment, the fused polycyclic heteroaromatic monomer has Formula V:


wherein:

    • Q is S, Se, Te, or NR6;
    • R6 is hydrogen or alkyl;
    • R8, R9, R10, and R11 are independently selected so as to be the same or different at each occurrence and are selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkylthio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, nitrile, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, amidosulfonate, ether sulfonate, ester sulfonate, and methane; and
    • at least one of R8 and R9, R9 and R10, and R10 and R11 together form an alkenylene chain completing a 5 or 6-membered aromatic ring, which ring may optionally Include one or more divalent nitrogen, sulfur or oxygen atoms.

In one embodiment, the fused polycyclic heteroaromatic monomer has Formula V(a), V(b), V(c), V(d), V(e), V(f), and V(g):


wherein:

    • Q is S, Se, Te, or NH; and
    • T is the same or different at each occurrence and is selected from S, NR6, O, SiR63, Se, Te, and PR6;
    • R6 is hydrogen or alkyl.
      The fused polycyclic heteroaromatic monomers may be substituted with groups selected from alkyl, heteroalkyl, alcohol, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane. In one embodiment, the substituent groups are fluorinated. In one embodiment, the substituent groups are fully fluorinated.

In one embodiment, the fused polycyclic heteroaromatic Monomer is a thieno(thiophene). Such compounds have been Discussed in, for example, Macromolecules, 34, 5746-5747 (2001); and Macromolecules, 35, 7281-7286 (2002). In one Embodiment, the thieno(thiophene) is selected from thieno(2,3-b)thiophene, thieno(3,2-b)thiophene, and thieno(3,4-b)thiophene. In one embodiment, the thieno(thiophene) monomer is substituted with at least one group selected from alkyl, heteroalkyl, alcohol, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane. In one embodiment, the substituent groups are fluorinated. In one embodiment, the substituent groups are fully fluorinated.

In one embodiment, polycyclic heteroaromatic monomers contemplated for use to form the copolymer in the new composition comprise Formula VI:


wherein:

    • Q is S, Se, Te, or NR6;
    • T is selected from S, NR6, O, SiR62, Se, Te, and PR6;
    • E is selected from alkenylene, arylene, and heteroarylene;
    • R6 is hydrogen or alkyl;
      • R12 is the same or different at each occurrence, and is selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkythio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, nitrile, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, amidosulfonate, ether sulfonate, ester sulfonate, and urethane; or both R12 groups together may form an alkylene or alkenylene chain completing a 3, 4, 5, 6, or 7-membered aromatic or alicyclic ring, which ring may optionally include one or more divalent nitrogen, sulfur or oxygen atoms.

In one embodiment, the semiconductive polymer is a copolymer of a first precursor monomer and at least one second precursor monomer. Any type of second monomer can be used, so long as it does not detrimentally affect the desired properties of the copolymer. In one embodiment, the second monomer comprises no more than 50% of the copolymer, based on the total number of monomer units. In one embodiment, the second monomer comprises no more than 30%, based on the total number of monomer units. In one embodiment, the second monomer comprises no more than 10%, based on the total number of monomer units.

Exemplary types of second precursor monomers include, but are not limited to, alkenyl, alkynyl, arylene, and heteroarylene. Examples of the second monomers include, but are not limited to, fluorene, oxadiazole, thiadiazole, benzothiadiazole, phenylenevinylene, phenyleneethynylene, pyridine, diazines, and triazines, all of which may be further substituted.

In one embodiment, the copolymers are made by first forming an intermediate precursor monomer having the structure A-B-C, where A and C represent first precursor monomers, which can be the same or different, and B represents a second precursor monomer. The A-B-C intermediate precursor monomer can be prepared using standard synthetic organic techniques, such as Yamamoto, Stille, Grignard metathesis, Suzuki, and Negishi couplings. The copolymer is then formed by conductive polymerization of the intermediate precursor monomer alone, or wish one or more additional precursor monomers.

In one embodiment, the semiconductor polymer is a copolymer of two or more monomers. In one embodiment, the precursor monomers are selected from thiophene, a pyrrole, an aniline, and a polycyclic aromatic.

3. Fluorinated Acid Polymer

The fluorinated acid polymer (hereinafter referred to as “FAP”) can be any polymer which is fluorinated and has acidic groups. As used herein, the term “fluorinated” means that at least one hydrogen bonded to a carbon has been replaced With a fluorine. The term includes partially and fully fluorinated materials. In one embodiment, the fluorinated acid polymer is highly fluorinated. The term “highly fluorinated” means that at least 50% of the avialable hydrogens bonded to a carbon, have been replaced with fluorine. The term “acidic group” refers to a group capable of ionizing to donate a hydrogen ion to a Brønsted base to form a salt. The acidic groups supply an ionizable proton. In one embodiment, the acidic group has a pKa of less than 3. In one embodiment, the acidic group has a pKa of less than 0. In one embodiment, the acidic group has a pKa of less than −5. The acidic group can be attached directly to the polymer backbone, or it can be attached to side chains on the polymer backbone or pendant groups. Examples of acidic groups include, but are not limited to, carboxylic acid groups, sulfonic acid groups, sulfonimide groups, phosphoric acid groups, phosphonic acid groups, and combinations thereof. The acidic groups can all be the same, or the polymer may have more than one type of acidic group.

In one embodiment, the FAP is organic solvent wettable (“wettable FAP”). The term “organic solvent wettable” refers to a material which, when formed into a film, is wettable by organic solvents. The term also includes polymeric acids which are not film-forming alone, but which when doped into a semiconductive polymer will form a film which is wettable. In one embodiment, the organic solvent wettable material forms a film which is wettable by phenylhexane with a contact angle less than 40°.

In one embodiment, the FAP is organic solvent non-wettable (“non-wettable FAP”). The term “organic solvent non-wettable” refers to a material which, when formed into a film, is not wettable by organic solvents. The term also includes polymeric acids which are not film-forming alone, but which when doped into a semiconductive polymer will form a film which is non-wettable. In one embodiment, the organic solvent non-wettable material forms a film on which phenylhexane has a contact angle greater than 40°.

As used herein, the term “contact angle” is intended to mean the angle φ shown in FIG. 1. For a droplet of liquid medium, angle φ is defined by the intersection of the plane of the surface and a line from the outer edge of the droplet to the surface. Furthermore, angle φ is measured after the droplet has reached an equilibrium position on the surface after being applied, i.e., “static contact angle”. The film of the organic solvent wettable fluorinated polymeric acid is represented as the surface. In one embodiment, the contact angle is no greater than 35°. In one embodiment, the contact angle is no greater than 30°. The methods for measuring contact angles are well known.

In one embodiment, the FAP is water-soluble. In one Embodiment, the FAP is dispersible in water. In one embodiment, the FAP forms a colloidal dispersion in water.

In one embodiment, the polymer backbone is fluorinated. Examples of suitable polymeric backbones include, but are not limited to, polyolefins, polyacrylates, polymethacrylates, polyimides, polyamides, polyaramids, polyacrylamides, polystyrenes, and copolymers thereof. In one embodiment, the polymer backbone is highly fluorinated. In one embodiment, the polymer backbone is fully fluorinated.

In one embodiment, the acidic groups are selected from sulfonic acid groups and sulfonimide groups. In one embodiment, the acidic groups are on a fluorinated side chain. In one embodiment, the fluorinated side chains are selected from alkyl groups, alkoxy groups, amido groups, ether groups, and combinations thereof.

In one embodiment, the wettable FAP has a fluorinated olefin backbone, with pendant fluorinated ether sulfonate, fluorinated ester sulfonate, or fluorinated ether sulfonimide groups. In one embodiment, the polymer is a copolymer of 1,1-difluoroethylene and 2-(1,1-difluoro-2-(trifluoromethyl) allyloxy)-1,1,2,2′-tetrafluoroethanesulfonic acid. In one embodiment, the polymer is a copolymer of ethylene and 2-(2-(1,2,2-trifluorovinyloxy)-1,1,2,3,3,3-hexafluoropropoxy)-1,1,2,2-tetrafluoroethanesulfonic acid. These copolymers can be made as the corresponding sulfonyl fluoride polymer and then can be converted to the sulfonic acid form.

In one embodiment, the wettable FAP is homopolymer or copolymer of a fluorinated and partially sulfonated poly(arylene ether sulfone). The copolymer can be a block copolymer. Examples of comonomers include, but are not limited to butadiene, butylene, isobutylene, styrene, and combinations thereof.

In one embodiment, the wettable FAP is a homopolymer or Copolymer of monomers having Formula VII:


where:

    • b is an integer from 1 to 5,
    • R13 is OH or NHR14, and
    • R14 is alkyl, fluoroalkyl, sulfonylalkyl, or sulfonylfluoroalkyl.

In one embodiment, the monomer is “SFS” or SFSI” shown below:


After polymerization, the polymer can be converted to the acid form.

In one embodiment, the wettable FAP is a homopolymer or copolymer of a trifluorostyrene having acidic groups. In one embodiment, the trifluorostyrene monomer has Formula VIII:


where:

    • W is selected from (CF2)q, O(CF2)q, S(CF2)q, (CF2)qO (CF2)r, and SO2(CF2)q,
    • b is independently an integer from 1 to 5,
    • R13 is OH or NHR14, and
    • R14 is alkyl, fluoroalkyl, sulfonylalkyl, or sulfonylfluoroalkyl.
      In one embodiment, the monomer containing W equal to S(CF2)q is polymerized then oxidized to give the polymer containing W equal to SO2(CF2)q. In one embodiment, the polymer containing R13 equal to F is converted its acid form where R13 is equal to OH or NHR14.

In one embodiment, the wettable FAP is a sulfonimide polymer having Formula IX:


where:

    • Rf is selected from fluorinated alkylene, fluorinated heteroalkylene, fluorinated arylene, or fluorinated heteroarylene;
    • Rg is selected from fluorinated alkylene, fluorinated heteroalkylene, fluorinated arylene, fluorinated heteroarylene, arylene, or heteroarylene; and
    • n is at least 4.
      In one embodiment of Formula IX, Rf and Rg are perfluoroalkylene groups. In one embodiment, Rf and Rg are perfluorobutylene groups. In one embodiment, Rf and Rg contain ether oxygens. In one embodiment, n is greater than 20.

In one embodiment, the wettable FAP comprises a fluorinated polymer backbone including a side chain having Formula


where:.

    • Rg is selected from fluorinated alkylene, fluorinated heteroalkylene, fluorinated arylene, fluorinated heteroarylene, arylene, or heteroarylene;
    • R15 is a fluorinated alkylene group or a fluorinated heteroalkylene group;
    • R16 is a fluorinated alkyl or a fluorinated aryl group; and
    • p is 0 or an integer from 1 to 4.

In one embodiment, the wettable FAP has Formula XI:


where:

    • R16 is a fluorinated alkyl or a fluorinated aryl group;
    • a, b, c, d, and e are each independently 0 or an integer from 1 to 4; and
    • n is at least 4.

The synthesis of these fluorinated acid polymers has been described in, for example, A. Feiring et al., J. Fluorine Chemistry 2000, 105, 129-135; A. Feiring et al., Macromolecules 2000, 33, 9262-9271; D. D. Desmarteau, J. Fluorine Chem. 1995, 72, 203-208; A. J. Appleby et al., J. Electrochem. Soc. 1993, 140(1), 109-111; and Desmarteau, U.S. Pat. No. 5,463,005.

In one embodiment, the wettable FAP comprises at least one repeat unit derived from an ethylenically unsaturated compound having Formula XII:

wherein d is 0, 1, or 2;

    • R17 to R20 are independently H, halogen, alkyl or alkoxy of 1 to 10 carbon atoms, Y, C(Rf1)(Rf1)OR21, R4Y or OR4Y;
    • Y is COE2, SO2 E2, or sulfonimide;
    • R21 is hydrogen or an acid-labile protecting group;
    • Rf1 is the same or different at each occurrence and is a fluoroalkyl group of 1 to 10 carbon atoms, or taken together are (CF2)e where e is 2 to 10;
    • R4 is an alkylene group;
    • E2 is OH, halogen, or OR7; and
    • R5 is an alkyl group;
    • with the proviso that at least one of R17 to R20 is Y, R4Y or OR4Y.
      R4, R5, and R17 to R20 may optionally be substituted by halogen or ether oxygen.

Some illustrative, but nonlimiting, examples of representative monomers of Formula XII are presented below:


wherein R21 is a group capable of forming or rearranging to a tertiary cation, more typically an alkyl group of 1 to 20 carbon atoms, and most typically t-butyl.

Compounds of Formula XII wherein d=0, (e.g., Formula XII-a), may be prepared by cycloaddition reaction of unsaturated compounds of structure (XIII) with quadricyclane (tetracyclo[2.2.1.02,603,3]heptane) as shown in the equation below.

The reaction may be conducted at temperatures ranging from about 0° C. to about 200° C., more typically from about 30° C. to about 150° C., in the absence or presence of an inert solvent such as diethyl ether. For reactions conducted at or above the boiling point of one or more at the reagents or solvent, a closed reactor is typically used to avoid loss of volatile components. Compounds of Formula XII with higher values of d (i.e., d=1 or 2) may be prepared by reaction of compounds of structure (XII) with d=0 with cyclopentadiene, as is known in the art.

In one embodiment, the wettable FAP is a copolymer which also comprises a repeat unit derived from at least one fluoroolefin, which is an ethylenically unsaturated compound containing at least one fluorine atom attached to an ethylenically unsaturated carbon. The fluoroolefin comprises 2 to 20 carbon atoms. Representative fluoroolefins include, but are not limited to, tetrafluoroethylene, hexafluoropropylene, chlorotrifluoroethylene, vinylidene fluoride, vinyl fluoride, perfluoro-(2,2-dimethyl-1,3-dioxole), perfluoro-(2-methylene-4-methyl-1,3-dioxolane), CF2=CFO(CF2)4CF═CF2, where t is 1 or 2, and Rf″OCF=CF2 wherein Rf″ is unsaturated fluoroalkyl group of from 1 to about ten carbon atoms. In one embodiment, the comonomer is tetrafluoroethylene.

In one embodiment, the non-wettable FAP comprises a polymeric backbone having pendant groups comprising siloxane sulfonic acid. In one embodiment, the siloxane pendant groups have the formula below:
—OaSi(OH)b-aR223-bR23RjSO3H
wherein:

a is from 1 to b;

b is from 1 to 3;

R22 is a non-hydrolyzable group independently selected from the group consisting of alkyl, aryl, and arylalkyl;

R23 is a bidentate alkylene radical, which may be substituted by one or more ether oxygen atoms, with the proviso that R23 has at least two carbon atoms linearly disposed between Si and Rj; and

    • Rf is a perfluoralkylene radical, which may be substituted by one or more ether oxygen atoms.
      In one embodiment, the non-wettable FAP having pendant siloxane groups has a fluorinated backbone. In one embodiment, the backbone is perfluorinated.

In one embodiment, the non-wettable FAP has a fluorinated backbone and pendant groups represented by the Formula (XIV)


wherein Rf2 is F or a perfluoroalkyl radical having 1-10 carbon atoms either unsubstituted or substituted by one or more ether oxygen atoms, h=0 or 1, i=0 to 3, and g=0 or 1.

In one embodiment, the non-wettable FAP has formula (XV)


where j≧0, k≧0, and 4≦(j+k)≦199, Q1 and Q2 are F or H, Rf2 is F or a perfluoroalkyl radical having 1-10 carbon atoms either unsubstituted or substituted by one or more ether oxygen atoms, h=0 or 1, i=0 to 3, g=0 or 1, and E4 is H or an alkali metal. In one embodiment Rf2 is—CF3, g=1, h=1, and i=1. In one embodiment the pendant group is present at a concentration of 3-10 mol-%.

In one embodiment, Q1 is H, k≧0, and Q2 is F, which may be synthesized according to the teachings of Connolly et al., U.S. Pat. No. 3,282,875. In another preferred embodiment, Q1 is H, Q2 is H, g=0, Rf2 is F, h=1, and i-1, which may be Synthesized according to the teachings of co-pending application Ser. No. 60/105,662. Still other embodiments may be Synthesized according to the various teachings in Drysdale et Al., WO 9831716(A1), and co-pending US applications Choi et al, WO 99/52954(A1), and 60/176,881.

In one embodiment, the non-wettable FAP is a colloid-forming polymeric acid. As used herein, the term “colloid-forming” refers to materials which are insoluble in water, and form colloids when dispersed into an aqueous medium. The colloid-forming polymeric acids typically have a molecular weight in the range of about 10,000 to about 4,000,000. In one embodiment, the polymeric acids have a molecular weight of about 100,000 to about 2,000,000. Colloid particle size typically ranges from 2 nanometers (nm) to about 140 nm. In one embodiment, the colloids have a particle size of 2 nm to about 30 nm. Any colloid-forming polymeric material having acidic protons can be used. In one embodiment, the colloid-forming fluorinated polymeric acid has acidic groups selected from carboxylic groups, sulfonic acid groups, and sulfonimide groups. In one embodiment, the colloid-forming fluorinated polymeric acid is a polymeric sulfonic acid. In one embodiment, the colloid-forming polymeric sulfonic acid is perfluorinated. In one embodiment, the colloid-forming polymeric sulfonic acid is a perfluoroalkylenesulfonic acid.

In one embodiment, the non-wettable colloid-forming FAP, is a highly-fluorinated sulfonic acid polymer (“FSA polymer”). “Highly fluorinated” means that at least about 50% of the total number of halogen and hydrogen atoms in the polymer are fluorine atoms, an in one embodiment at least about 75%, and in another embodiment at least about 90%. In one embodiment, the polymer is perfluorinated. The term “sulfonate functional group” refers to either to sulfonic acid groups or salts of sulfonic acid groups, and in one embodiment alkali metal or ammonium salts. The functional group is represented by the formula —SO3E5 where E5 is a cation, also known as a “counterion”, E5 may be H, Li, Na, K or N(R1) (R2)(R3)(R4), and R1, R2, R3, and R4 are the same or different and are and in one embodiment H, CH3 or C2H5. In another embodiment, E5 is H, in which case the polymer is said to be in the “acid form”. E5 may also be multivalent, as represented by such ions as Ca++, and Al+++, It is clear to the skilled artisan that in the case of multivalent counterions, represented generally as M++, the number of sulfonate functional groups per counterion will be equal to the valence “x”.

In one embodiment, the FSA polymer comprises a polymer backbone with recurring side chains attached to the backbone, the side chains carrying cation exchange groups. Polymers include homopolymers or copolymers of two or more monomers. Copolymers are typically formed from a non-functional monomer and a second monomer carrying the cation exchange group or its precursor, e.g., a sulfonyl fluoride group (—SO2F), which can be subsequently hydrolyzed to a sulfonate functional grop. For example, copolymers of a first fluorinated vinyl monomer together with a second fluorinated vinyl monomer having a sulfonyl fluoride group (—SO2F) can be used. Possible first monomers include tetrafluoroethylene (TFE), hexafluoropropylene, vinyl fluoride, vinylidine fluoride, trifluoroethylene, chlorotrifluoroethylene, perfluoro(alkyl vinyl ether), and combinations thereof. TFE is a preferred first monomer.

In one embodiments, possible second monomers include fluorinated vinyl ethers with sulfonate functional groups or precursor groups which can provide the desired side chain in the polymer. Additional monomers, including ethylene, propylene, and R—CH═CH2 where R is a perfluorinated alkyl group of 1 to 10 carbon atoms, can be incorporated into these polymers if desired. The polymers may be of the type referred to herein as random copolymers, that is, copolymers made by polymerization in which the relative concentrations of the comonomers are kept as constant as possible, so that the distribution of the monomer units along the polymer chain is in accordance with their relative concentrations and relative reactivities. Less random copolymers, made by varying relative concentrations of monomers in the course of the polymerization, may also be used. Polymers of the type called block copolymers, such as that disclosed in European Patent Application No. 1 026 152 A1, may also be used.

In one embodiment, FSA polymers for use in the present invention include a highly fluorinated, and in one embodiment perfluorinated, carbon backbone and side chains represented by the formula
—(O—CF2CFRf3)a—O—CF2CFRf3SO3E5
wherein Rf3 and Rf4 are independently selected from F, Cl, or A perfluorinated alkyl group having 1 to 10 carbon atoms, a=0, 1 or 2, and E5 is H, Li, Na, K or N(R1)(R2)(R3)(R4) and R1, R2, R3, and R4 are the same or different and are and in one embodiment H, CH3 or C2H5. In another embodiment E5 is H. As stated above, E5 may also be multivalent.

In one embodiment, the FSA polymers include, for example, polymers disclosed in U.S. Pat. No. 3,282,875 and in U.S. Pat. Nos. 4,358,545 and 4,940,525. An example of preferred FSA polymer comprises a perfluorocarbon backbone and the side chain represented by the formula
—O—CF2CF(CF3)—O—CF2CF2SO3E5
where X is as defined above. FSA polymers of this type are disclosed in U.S. Pat. No. 3,282,875 and can be made by copolymerization of tetrafluoroethylene (TFE) and the perfluorinated vinyl ether CF2═CF—O—CF2CF(CF3)—O— CF2CF2SO2F, perfluoro(3,6-dioxa-4-methyl-7-octenesulfonyl fluoride) (PDMOF), followed by conversion to sulfonate groups by hydrolysis of the sulfonyl fluoride groups and ion exchanged as necessary to convert them to the desired ionic form. An example of a polymer of the type disclosed in U.S. Pat. Nos. 4,358,545 and 4,940,525 has the side chain —O—CF2CF2SO3E5, wherein E5 is as defined above. This polymer can be made by copolymerization of tetrafluoroethylene (TFE) and the perfluorinated vinyl ether CF2═CF—O—CF2CF2SO2F, perfluoro(3-oxa-4-pentenesulfonyl fluoride) (POPF), followed by hydrolysis and further ion exchange as necessary.

In one embodiment, the FSA polymers for use in this invention typically have an ion exchange ratio of less than about 33. In this application, “ion exchange ratio” or “IXR” is defined as number of carbon atoms in the polymer backbone in relation to the cation exchange groups. Within the range of less than about 33, IXR can be varied as desired for the particular application. In one embodiment, the IXR is about 3 to about 33, and in another embodiment from about 8 to about 23.

The cation exchange capacity of a polymer is often expressed in terms of equivalent weight (EW). For the purposes of this application, equivalent weight (EW) is defined to be the weight of the polymer in acid form required to neutralize one equivalent of sodium hydroxide. In the case of a sulfonate polymer where the polymer has a perfluorocarbon backbone and the side chain is —O—CF2—CF(CF3)—O—CF2—CF2—SO3H (or a salt thereof), the equivalent weight range which corresponds to an IXR of about 8 to about 23 is about 750 EW to about 1500 EW, IXR for this polymer can be related to equivalent weight using the formula: 50 IXR+344=EW. While the same IXR range is used for sulfonate polymers disclosed in U.S. Pat. Nos. 4,358,545 and 4,940,525, e.g., the polymer having the side chain —O—CF2CF2SO3H (or a salt thereof), the equivalent weight is somewhat lower because of the lower molecular weight of the monomer unit containing a cation exchange group. For the preferred IXR range of about 8 to about 23, the corresponding equivalent weight range is about 575 EW to about 1325 EW. IXR for this polymer can be related to equivalent weight using the formula: 50 IXR+178=EW.

The FSA polymers can be prepared as colloidal aqueous dispersions. They may also be in the form of dispersions in other media, examples of which include, but are not limited to, alcohol, water-soluble ethers, such as tetrahydrofuran, mixtures of water-soluble ethers, and combinations thereof. In making the dispersions, the polymer can be used in acid form. U.S. Pat. Nos. 4,433,082, 6,150,426 and WO 03/006537 disclose methods for making of aqueous alcoholic dispersions. After the dispersion is made, the concentration and the dispersing liquid composition can be adjusted by methods known in the art.

Aqueous dispersions of the colloid-forming polymeric acids, including FSA polymers, typically have particle sizes as small as possible and an EW as small as possible, so long as a stable colloid is formed.

Aqueous dispersions of FSA polymer are available commericially as Nafion® dispersions, from E.I. du Pont de Nemours and Company (Wilmington, Del.).

4. Preparing Doped Semiconductive Polymers

In one embodiment, the doped semiconductive polymers are formed by oxidative polymerization of the precursor monomer in the presence of at least one FAP. The doped semiconductive polymers are abbreviated hereinafter as “SCP/FAP”. The polymerization is generally carried out in a homogeneous aqueous solution. In another embodiment, the polymerization for obtaining the electrically conducting polymer is carried out in an emulsion of water and an organic solvent. In general, some water is present in order to obtain adequate solubility of the oxidizing agent and/or catalyst. Oxidizing agents such as ammonium persulfate, sodium persulfate, potassium persulfate, and the like, can be used. A catalyst, such as ferric chloride, or ferric sulfate may also be present. The resulting polymerized product will be a solution, dispersion, or emulsion of the doped semiconductive polymer.

In one embodiment, the method of making an aqueous dispersion of the semiconductive polymer doped with EAP includes forming a reaction mixture by combining water, at least one precursor monomer, at least one FAP, and an oxidizing agent, in any order, provided that at least a portion of the FAP is present when at least one of the precursor monomer and the oxidizing, agent is added. It will be understood that, in the case of semiconductive copolymers, the term “at least one precursor monomer” encompasses more than one type of monomer.

In one embodiment, the method of making an aqueous dispersion of the doped semiconductive polymer includes forming a reaction mixture by combining water, at least one precursor monomer, at least one FAP, and an oxidizing agent, in any order, provided that at least a portion of the FAP is present when at least one of the precursor monomer and the oxidizing agent is added.

In one embodiment, the method of making the doped semiconductive polymer comprises:

    • (a) providing an aqueous solution or dispersion of a FAP;
    • (b) adding an oxidizer to the solutions or dispersion of step (a); and
    • (c) adding at least one precursor monomer to the mixture of step (b).

In another embodiment, the precursor monomer is added to the aqueous solution or dispersion of the FAP prior to adding the oxidizer. Step (b) above, which is adding oxidizing agent, is then carried out.

In another embodiment, a mixture of water and the precursor monomer is formed, in a concentration typically in the range of from about 0.5% by weight to about 4.0% by weight total precursor monomer. This precursor monomer mixture is added to the aqueous solution or dispersion of the FAP, and steps (b) above which is adding oxidizing agent is carried out.

In another embodiment, the aqueous polymerization mixture may include a polymerization catalyst, such as ferric sulfate, ferric chloride, and the like. The catalyst is added before the last step. In another embodiment, a catalyst is added together with an oxidizing agent.

In one embodiment, the polymerization is carried out in the presence of co-dispersing liquids which are miscible with water. Examples of suitable co-dispersing liquids include, but are not limited to ethers, alcohols, alcohol ethers, cyclic ethers, ketones, nitrites, sulfoxides, amides, and combinations thereof. In one embodiment, the co-dispersing liquid is an alcohol. In one embodiment, the co-dispersing liquid is an organic solvent selected from n-propanol, isopropanol, t-butanol, dimethylacetamide, dimethylformamide, N-methylpyrrolidone, and mixtures thereof. In general, the amount of co-dispersing liquid should be less than about 60% by volume. In one embodiment, the amount of co-dispersing liquid is less than about 30% by volume. In one embodiment, the amount of co-dispersing liquid is between 5 and 50% by volume. The use of co-dispersing liquid in the polymerization significantly reduces particle size and improves filter-ability of the dispersions. In addition, buffer materials obtained by this process show an increased viscosity and films prepared from these dispersions are of high quality.

The co-dispersing liquid can be added to the reaction mixture at any point in the process.

In one embodiment, the polymerization is carried out in the presence of a co-acid which is a Brønsted acid. The acid can be an organic acid, such as HCl, sulfuric acid, and the like, or an organic acid, such as acetic acid or p-toluenesulfonic acid. Alternatively, the acid can be a water soluble polymeric acid such as poly(styrenesulfonic acid), poly(2-acrylamido-2-methyl-1-propanesulfonic acid, or the like, or a second fluorinated acid polymer, as described above. Combinations of acids can be used.

The co-acid can be added to the reaction mixture at any point in the process prior to the addition of either the oxidizer or the precursor monomer, whichever is added last. In one embodiment, the co-acid is added before both the precursor monomers and the fluorinated acid polymer, and the oxidizer is added last. In one embodiment the co-acid is added prior to the addition of the precursor monomers, followed by the addition of the fluorinated acid polymer, and the oxidizer is added last.

In one embodiment, the polymerization is carried out in the Presence of both a co-dispersing liquid and a co-acid.

In the method of making the doped semiconductive polymer, the molar ratio of oxidizer to total precursor monomer is generally in the range of 0.1 to 3.0; and in one embodiment is 0.4 to 1.5. The molar ratio of FAP to total precursor monomer is generally in the range of from 0.2 to 10. In one embodiment, the ratio is in the range of 1 to 5. The overall solid content is generally in the range of about 0.5% to 12% in weight percentage; and in one embodiment of about 2% to 6%. The reaction temperature is generally in the range of about 4° C. to 50° C.; in one embodiment about 20° C. to 35° C. The molar ratio of optional co-acid to precursor monomer is about 0.05 to 4. The addition time of the oxidizer influences particle size and viscosity. Thus, the particle size can be reduced by slowing down the addition speed. In parallel, the viscosity is increased by slowing down the addition speed. The reaction time is generally in the range of about 1 to about 30 hours.

(a) pH Treatment

As synthesized, the aqueous dispersions of the doped semiconductive polymers generally have a very low pH. When the semiconductive polymer is doped with a FAP, it has been found that the pH can be adjusted to higher values, without adversely affecting the properties in devices. In one embodiment, the pH of the dispersion can be adjusted to about 1.5 to about 4. In one embodiment, the pH is adjusted to between 2 and 3. It has been found that the pH can be adjusted using known techniques, for example, ion exchange or by titration with an aqueous basic solution.

In one embodiment, the as-formed aqueous dispersion of FAP-doped semiconductive polymer is contacted with at least one ion exchange resin under conditions suitable to remove any remaining decomposed species, side reaction products, and unreacted monomers, and to adjust pH, thus producing a stable, aqueous dispersion with a desired pH. In one embodiment, the as-formed doped semiconductive polymer dispersion is contacted with a first ion exchange resin and a second ion exchange resin, in any order. The as-formed doped semiconductive polymer dispersion can be treated with both the first and second ion exchange resins simultaneously, or it can be treated sequentially with one and then the other. In one embodiment, the two doped semiconductive polymers are combined as-synthesized, and then treated with one or more inn exchange resins.

Ion exchange is a reversible chemical reaction wherein an ion in a fluid medium (such as an aqueous dispersion) is exchanged, for a similarly charged ion attached to an immobile solid particle that is insoluble in the fluid medium. The term “ion exchange resin” is used herein to refer to all such substances. The resin is rendered insoluble due to the crosslinked nature of the polymeric support to which the ion exchanging groups are attached. Ion exchange resins are classified as cation exchangers or anion exchangers. Cation exchangers have positively charged mobile ions available for exchange, typically protons or metal ions such as sodium ions. Anion exchangers have exchangeable ions which are negatively charged, typically hydroxide ions.

In one embodiment, the first ion exchange resin is a cation, acid exchange resin which can be in protonic or metal ion, typically sodium ion, form. The second ion exchange resin is a basic, anion exchange resin. Both acidic, cation including proton exchange resins and basic, anion exchange resins are contemplated for use in the practice of the invention. In one embodiment, the acidic, cation exchange resin is an inorganic acid, cation exchange resin, such as a sulfonic acid cation exchange resin. Sulfonic acid cation exchange resins contemplated for use in the practice of the invention include, for example, sulfonated styrene-divinylbenzene copolymers, sulfonated crosslinked styrene polymers, phenol-formaldehyde-sulfonic acid resins, benzene-formaldehyde-sulfonic acid resins, and mixtures thereof. In another embodiment, the acidic, cation exchange resin is an organic acid, cation exchange resin, such as carboxylic acid, acrylic or phosphorous cation exchange resin. In addition, mixtures of different cation exchange resins can be used.

In another embodiment, the basic, anionic exchange resin is a tertiary amine anion exchange resin. Tertiary amine anion exchange resins contemplated for use in the practice of the invention include, for example, tertiary-aminated styrene-divinylbenzene copolymers, tertiary-aminated crosslinked styrene polymers, tertiary-aminated phenol-formaldehyde resins, tertiary-aminated benzene-formaldehyde resins, and mixtures thereof. In a further embodiment, the basic, anionic exchange resin is a quaternary amine anion exchange resin, or mixtures of these and other exchange resins.

The first and second ion exchange resins may contact the as-formed aqueous dispersion either simultaneously, or consecutively. For example, in one embodiment both resins are added simultaneously to an as-formed aqueous dispersion of an electrically conducting polymer, and allowed to remain in contact with the dispersion for at least about 1 hour, e.g., about 2 hours to about 20 hours. The ion exchange resins can then be removed from the dispersion by filtration. The size of the filter is chosen so that the relatively large ion exchange resin particles will be removed while the smaller dispersion particles will pass through. Without wishing to be bound by theory, it is believed that the ion exchange resins quench polymerization and effectively remove ionic and non-ionic impurities and most of unreacted monomer from the as-formed aqueous dispersion. Moreover, the basic, anion exchange and/or acidic, cation exchange resins renders the acidic sites more basic, resulting in increased pH of the dispersion. In general, about one to five grams of ion exchange resin is used per gram of semiconductive polymer composition.

In many cases, the basic ion exchange resin can be used to adjust the pH to the desired level. In some cases, the pH can be further adjusted with an aqueous basic solution such as a solution of sodium hydroxide, ammonium hydroxide, tetramethylammonium hydroxide, or the like.

5. Preparing Buffer Compositions

The new buffer compositions can be formed by blending the semiconductive oxide particles with the FAP or the SCP/FAP. This can be accomplished by adding an aqueous dispersion of the semiconductive oxide particles to an aqueous dispersion of the FAP or the SCP/FAP. In one embodiment, the composition is further treated using sonication or microfluidization to ensure mixing of the components.

In one embodiment, one or both of the components are isolated in solid form. The solid material can be redispersed in water or in aqueous solution or dispersion of the other component. For example, semiconductive oxide particle solids can be dispersed in an aqueous solution or dispersion of a semiconductive polymer doped with an FAP.

6. Buffer Layers

In another embodiment of the invention, there are provided buffer layers deposited from aqueous dispersions comprising the new buffer compositions. The term “buffer layer” or “buffer material” is intended to mean electrically conductive or semiconductive materials and may have one or more functions in an organic electronic device, including but not limited to, planarization to the underlying layer, charge transport and/or charge injection properties, scavenging of impurities such as oxygen or metal ions, and other aspects to facilitate or to improve the performance of the organic electronic device. The term “layer” is used interchangeably with the term “film” and refers to a coating covering a desired area. The sense of the term is not limited or qualified by considerations of the size of a coated area. The area can be as large as an entire device or as small as a specific functional area such as the actual visual display, or as small as a single sub-pixel.

In one embodiment, the buffer layer is formed using a liquid deposition method. Any liquid deposition method can be used. Continuous liquid deposition techniques, include but are not limited to, spin coating, gravure coating, curtain coating, dip coating, slot-die coating, spray coating, and continuous nozzle coating. Discontinuous liquid deposition techniques include, but are not limited to, ink jet printing, gravure printing, and screen printing.

In another embodiment, there are provided buffer layers deposited from aqueous dispersions comprising the new conductive polymer composition blended with other water soluble or dispersible materials. Examples of types of materials which can be added include, but are not limited to polymers, dyes, coating aids, organic and inorganic conductive inks and pastes, charge transport materials, crosslinking agents, and combinations thereof. The other water soluble or dispersible materials can be simple molecules or polymers. Examples of suitable polymers include, but are not limited to, conductive polymers such as polythiophenes, polyanilines, polypyrroles, polyacetylenes, and combinations thereof.

7. Electronic Devices

In another embodiment of the invention, there are provided electronic devices comprising at least one electroactive layer positioned between two electrical contact layers, wherein the device further includes the new buffer layer. The term “electroactive” when referring to a layer or material is intended to mean a layer or material that exhibits electronic or electro-radiative properties. An electroactive layer material may emit radiation or exhibits a change in concentration of electron-hole pairs when receiving radiation.

As shown in FIG. 2, a typical device, 100, has an anode layer 110, a buffer layer 120, an electronic layer 130, and a cathode layer 150. Adjacent to the cathode layer 150 is an optional electron-injection/transport layer 140.

The device may include a support or substrate (not shown) that can be adjacent to the anode layer 110 or the cathode layer 150. Most frequently, the support is adjacent the anode layer 110. The support can be flexible or rigid, organic or organic. Examples of support materials include, but are not limited to, glass, ceramic, metal, and plastic films.

The anode layer 110 is an electrode that is more efficient for injecting holes compared to the cathode layer 150. The anode can include materials containing a metal, mixed metal, alloys, metal oxide or mixed oxide. Suitable materials include the mixed oxides of the Group 2 elements (i.e., Be, Mg, Ca, Sr, Ba, Ra), the Group 11 elements, the elements in Groups 4, 5, and 6, and the Group 8-10 transition elements. If the anode layer 110 is to be light transmitting, mixed oxides of Groups 12, 13 and 14 elements, such as indium-tin-oxide, may be used. As used herein, the phrase “mixed oxide” refers to oxides having two or more different cations selected from the Group 2 elements or the Groups 12, 13, or 14 elements. Some non-limiting, specific examples of materials for anode layer 110 include, but are not limited to, indium-tin-oxide (“ITO”), Indium-zinc-oxide, aluminum-tin-oxide, gold, silver, copper, and nickel. The anode may also comprise an organic material, especially a conducting polymer such as polyaniline, including exemplary materials as described in “Flexible light-emitting diodes made from soluble conducting polymer,” Nature vol. 357, pp 477 479 (11 Jan. 1992). At least one of the anode and cathode should be at least partially transparent to allow the generated light to be observed.

The anode layer 110 may be formed by a chemical or physical vapor deposition process or spin-cast process. Chemical vapor deposition may be performed as a plasma-enhanced chemical vapor deposition (“PECVD”) or metal organic chemical vapor deposition (“MOCVD”). Physical vapor deposition can include all forms of sputtering, including ion beam sputtering, as well as e-beam evaporation and resistance evaporation. Specific forms of physical vapor deposition include rf magnetrons sputtering and inductively-coupled plasma physical vapor deposition (“IMP-PVD”). These deposition techniques are well known within the semiconductor fabrication arts.

In one embodiment, the anode layer 110 is patterned during a lithographic operation. The pattern may vary as desired. The layers can be formed in a pattern by, for example, positioning a patterned mask or resist on the first flexible composite barrier structure prior to applying the first electrical contact layer material. Alternatively, the layers can be applied as an overall layer (also called blanket deposit) and subsequently patterned using, for example, a patterned resist layer and wet chemical or dry etching techniques. Other processes for patterning that are well known in the art can also be used.

The buffer layer 120 is usually deposited onto substrates using a variety of techniques well-known to those skilled in the art. Typical deposition techniques, as discussed above, include liquid deposition (continuous and discontinuous techniques), and thermal transfer.

An optional layer, not shown, may be present between the buffer layer 120 and the electroactive layer 130. This layer may comprise hole transport materials. Examples of hole transport materials for layer 120 have been summarized for example, in Kirk-Othmer Encyclopedia of Chemical Technology, Fourth Edition, Vol. 18, p. 837-860, 1996, by Y. Wang. Both hole transporting molecules and polymers can be used. Commonly used hole transporting molecules include, but are not limited to: 4,4′,4″-tris(N,N-diphenyl-amino)-triphenylamine (TDATA); 4,4′,4″-tris(N-3-methylphenyl-N-phenylamino)-triphenylamine (MTDATA); N,N′-diphenyl-N,N′-bis(3-methylphenyl)-[1,1′-biphenyl]-4,4′-diamine (TPD); 1,1-bis[(di-4-tolylamino)phenyl]cyclohexane (TAPC); N,N′-bis-(4-methylphenyl)-N,N′-bis(4-ethylphenyl)-[1,1′-(3,3′-dimethyl)biphenyl]-4,4′-diamine (ETPD); tetrakis-(3-methylphenyl)-N,N, N′,N′-2,5-phenylenediamine (PDA); α-phenyl-4-N,N-diphenylaminostyrene (TPS); p-(diethylamino)benzaldehyde diphenylhydrazone (DEH); triphenylamine (TPA); bis[4-(N,N-diethylamino)-2-methylphenyl] (4-methylphenyl)methane (MPMP); 1-phenyl-3-[p-(diethylamino)styryl]-5-[p-(diethylamino)phenyl]pyrazoline (PPR or DEASP); 1,2-trans-bis(9H-carbazol-9-yl)cyclobutane (DCZB); N,N,N′,N′-tetrakis(4-methylphenyl)-(1,1′-biphenyl)-4,4′-diamine (TTB); N,N′-bis(naphthalen-1-yl)-N,N′-bis-(phenyl)benzidine (α-NPB); and porphyrinic compounds, such as copper phthalocyanine. Commonly used hole transporting polymers include, but are not limited to, poly(9,9,-dioctylfluorene-co-N-(4-butylphenyl)diphenylaminer), and the like, polyvinylcarbazole, (phenylmethyl)polysilane, poly(dioxythiophenes), polyanilines, and polypyrroles. It is also possible to obtain hole transporting polymers by doping hole transporting molecules such as those mentioned above into polymers such as polystyrene and polycarbonate.

Depending upon the application of the device, the electroactive layer 130 can be a light-emitting layer that is activated by an applied voltage (such as in a light-emitting diode or light-emitting electrochemical cell), a layer of material that responds to radiant energy and generates a signal with or without an applied bias voltage (such as in a photodector). In one embodiment, the electroactive material is an organic electroluminescent (“EL”) material. Any EL material can be used in the devices, including, but not limited to, small molecule organic fluorescent compounds, fluorescent and phosphorescent metal complexes, conjugated polymers, and mixtures thereof. Examples of fluorescent compounds include, but are not limited to, pyrene, perylene, rubrene, coumarin, derivatives thereof, and mixtures thereof. Examples of metal complexes include, but are not limited to, metal chelated oxinoid compounds, such as tris(8-hydroxyquinolato)aluminum (Alq3); cyclometalated iridium and platinum electroluminescent Compounds, such as complexes of iridium with Phenylpyridine, phenylquinoline, or phenylpyrimidine ligands as disclosed in Petrov et al., U.S. Pat. No. 6,670,645 and Published PCT Applications WO 03/063555 and WO 2004/016710, and organometallic complexes described in, for example, Published PCT Applications WO 03/008424, WO 03/091688, and WO 03/040257, and mixtures thereof. Electroluminescent emissive layers comprising a charge carrying host mateiral and a metal complex have been described by Thompson et al., in U.S. Pat. No. 6,303,238, and by Burrows and Thompson in published PCT applications WO 00/70655 and WO 01/41512. Examples of conjugated polymers include, but are not limited lited to poly(phenylenevinylenes), polyfluorenes, poly(spirobifluorenes), polythiophenes, poly(p-phenylenes), copolymers thereof, and mixtures thereof.

Optional layer 140 can function both to facilitate electron injection/transport, and can also serve as a confinement layer to prevent quenching reactions at layer interfaces. More specifically, layer 140 may promote electron mobility and reduce the likelihood of a quenching reaction if layers 130 and 150 would otherwise be in direct contact. Examples of materials for optional layer 140 include, but are not limited to, metal chelated oxinoid compounds, such as bis(2-methyl-8-quinolinolato)(para-phenyl-phenolato)aluminum(III) (BAIQ), tetra(8-hydroxyquinolato)zirconium (ZrQ), and tris(8-hydroxyquinolato)aluminum (Alq3); azole compounds such as 2-(4-biphenylyl)-5-(4-t-butylphenyl)-1,3,4-oxadiazole (PBD), 3-(4-biphenylyl)-4-phenyl-5-(4-t-butylphenyl)-1,2,4-triazole (TAZ), and 1,3,5-tri(phenyl-2-benzimidazole)benzene (TPBI); quinoxaline derivatives such as 2,3-bis(4-fluorophenyl)quinoxaline; phenanthroline derivatives such as 9,10-diphenylphenanthroline (DPA) and 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline (DDPA); and any one or more combinations thereof. Alternatively, optional layer 140 may be inorganic and comprise BaO, LiF, Li2O, or the like.

The cathode layer 150 is an electrode that is particularly efficient for injecting electrons or negative charge carriers. The cathode layer 150 can be any metal or nonmetal having a lower work function than the first electrical contact layer (in this case, the anode layer 110).

Materials for the cathode layer can be selected from alkali metals of Group I (e.g., Li, Na, K, Rb, Cs,), the Group 2 metals (e.g., Mg, Ca, Ba, or the like), the Group 12 metals, the lanthanides (e.g., Ce, Sm, Eu, or the like), and the actidines (e.g., Th, U, or the like). Materials such as aluminum, indium, Yttrium, and combinations thereof, may also be used. Specific non-limiting examples of materials for the cathode layer 150 include, but are not limited to, barium, lithium, cerium, cesium, europium, rubidium, yttrium, magnesium, samarium, and alloys and combinations thereof.

The cathode layer 150 is usually formed by a chemical or Physical vapor deposition process. In some embodiments, the cathode layer will be patterned, as discussed above in reference to the anode layer 110.

Other layers in the device can be made of any materials Which are know to be useful in such layers upon consideration of the function to be served by such layers.

In some embodiments, an encapsulation layer (not shown) is deposited over the contact layer 150 to prevent entry of undesirable components, such as water and oxygen, into the device 100. Such components can have a deleterious effect on the organic layer 130. In one embodiment, the encapsulation layer is a barrier layer or film. In one embodiment, the encapsulation layer is a glass lid.

Though not depicted, it is understood that the device 100 may comprise additional layers. Other layers that are known in the art or otherwise may be used. In addition, any of the above-described layers may comprise two or more sub-layers or may form a laminar structure. Alternatively, some or all of anode layer 110 the buffer layer 120, the electron transport layer 140, cathode layer 150, and other layers may be treated, especially surface treated, to increase charge carrier transport efficiency or other physical properties of the devices. The choice of materials for each of the component layers is preferably determined by balancing the goals of providing a device with high device efficiency with device operational lifetime considerations, fabrication time and complexity factors and other considerations appreciated by persons skilled in the art. It will be appreciated that determining optimal components, component configurations, and compositional identities would be routine to those of ordinary skill of in the art.

In various embodiments, the different layers have the following ranges of thicknesses anode 110, 500-5000 Å, in one embodiment 1000-2000 Å; buffer layer 120, 50-2000 Å, in one embodiment 200-1000 Å, optional transport layer, 50-2000 Å, in one embodiment 100-1000 Å; photoactive layer 130, 10-2000 Å, in one embodiment 100-1000 Å; optional electron transport layer 140, 50-2000 Å, in one embodiment 100-1000 Å; cathode 150, 200-10000 Å, in one embodiment 300-5000 Å. The location of the electron-hole recombination zone in the device, and thus the emission spectrum of the device, can be affected by the relative thickness of each layer. Thus the thickness of the electron-transport layer should be chosen so that the electron-hole recombination zone is in the light-emitting layer. The desired ratio of layer thicknesses will depend on the exact nature of the materials used.

In operation, a voltage from an appropriate power supply (not depicted) is applied to the device 100. Current therefore passes across the layers of the device 100. Electrons enter the organic polymer layer, releasing photons. In some OLEDs, called active matrix OLED displays, individual deposits of photoactive organic films may be independently excited by the passage of current; leading to individual pixels of light emission. In some OLEDs, called passive matrix OLED displays, deposits of photoactive organic films may be excited by rows and columns of electrical contact layers.

As used herein, the terms “comprises,” “comprising,” “includes,” “including,” “has,” “having” or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, article, or apparatus that comprises a list of elements is not necessarily limited to only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. Further, unless expressly stated to the contrary, “or” refers to an inclusive or and not to an exclusive or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).

As used herein, the term “layer” is used interchangeably with the mon “film” and refers to a coating covering a desired area. The meaning is not affected by the size of the area coated. The area can be as large as art entire device or as small as a specific functional area such as the actual visual display, or as small as a single sub-pixel. Layers and films can be formed by any conventional deposition technique, including vapor deposition, liquid deposition (continuous and discontinuous techniques), and thermal transfer. Continuous deposition techniques, include but are not limited to, spin coating, gravure coating, curtain coating, dip coating, slot-die coating, spray coating, and continuous nozzle coating. Discontinuous deposition techniques include, but are not limited to, ink jet printing, gravure printing, and screen printing.

The term “work function” is intended to mean the minimum energy needed to remove an electron from a material to a point at infinite distance away from the surface.

Also, use of “a” or “an” are employed to describe elements and components of the invention. This is done merely for convenience and to give a general sense of the invention. This description should be read to include one or at least one and the singular also includes the plural unless it is obvious that it is meant otherwise.

Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Although methods and materials similar or equivalent to those described can be used in the practice or testing of the present invention, suitable methods and materials are described below. All publications, patent applications, patents, and other references mentioned herein are incorporated by reference in their entirety. In case of conflict, the present specification, including definitions, will control. In addition, the materials, methods, and examples are illustrative only and not intended to be limiting.

EXAMPLES Example 1

This example illustrates preparation of an aqueous dispersion of antimony double oxide with Nafion®, and conductivity of the film spin-coated from the dispersion. Nafion® is a trade name for poly(perfluoroethylene sulfonic acid) from E.I. do Pont de Nemours and Company (Wilmington, Del.).

In this example, Celnax CX-Z300H purchased from Nissan Chemical Industries, LTD from Houston, Tex. The Celnax is antimony double oxide hydrosol, which contains 30% (w/w) oxide and about 70% water. It has pH 6.9 and particle size of 20 nm using BET method. Thin layer of dried film of the material is bluish green color and almost transparent. 2.0112 g of Celnax was first diluted with 4.9748 g de-ionized water 1.632 g Nafion® dispersion, which contains 12.23% (w/w) Nafion® polymer, was then added to the diluted Celnax dispersion. They mixed easily and formed a stable dispersion without a sign of sedimentation.

A couple of drops of the dispersion were placed on a microscope slide to form a thin, transparent film. The thin film was painted with silver paste to form two parallel lines as electrodes for measurement of resistance. The resistance was converted to conductivity by taking a thickness of the film and separating the two electrodes along the length of the electrodes. Conductivity was determined to be 8×104S/cm. This conductivity is suitable as a buffer layer.

The dried film will be measured for Wf by Ultraviolet Photoelectron Spectroscopy (UPS). Wf energy level is usually determined from second electron cut-off with respect to the position of vacuum level using HeI (21.22 eV) radiation.

Example 2

This example illustrates effect on work-function of the addition of Nafion® to a semiconductive oxide dispersion. Nafion® is a trademark for poly(perfluoroethylenesulfonic acid) from E.I. du Pont de Nemours and Company.

General Procedure of Film Sample Preparation and Kelvin Probe Measurement

Film samples of Kelvin probe measurement for determination of work-function were made by spin-coating of a semiconductive dispersion or an admixture dispersion on 30 mm×30 mm glass/ITO substrates. ITO/glass substrates consist of 15 mm×20 mm ITO area at the center having ITO thickness of from 100 to 150 nm. At one corner of 15 mm×20 mm ITO area, ITO film surface extended to the edge of the glass/ITO serves as electrical contact with Kevlin probe electrode. Prior to spin coating, ITO/glass substrates were cleaned and the ITO sides were subsequently treated with UV-ozone for 10 minutes. Once spin-coated, the deposited materials on the corner of the extended ITO film were removed with a Q-tip wetted with ether water. The exposed ITO pad was for making contact with Kelvin probe electrode. The deposited films were then baked as illustrated in Examples. The baked film samples were then placed on a glass jug flooded with nitrogen before capped with a lid before measurement.

For work-function determination, an ambient-aged gold film was measured first as a reference prior to measurement of samples. The gold film on a same size of glass piece was placed in a cavity cut out at the bottom of a square steel container. On the side of the cavity, there are four retention clips to keep sample piece firmly in place. One of the retention clips is attached with electrical wire for making contact with the Kelvin probe. The gold film was facing up while a Kelvin probe tip protruded from the center of a steel lid was lowered to above the center of the gold film surface. The lid was then screwed tightly onto the square steel container at four corners. A side port on the square steel container was connected with tubing for allowing nitrogen to sweep the Kelvin probe cell continuously while a nitrogen exit port capped with a septum in which a steel needle is inserted for maintaining ambient pressure. The probe settings were then optimized for the probe and only height of the tip was changed through entire measurement. The Kelvin probe was connected to a McAllister KP6500 Kelvin Probe meter having the following parameters: 1) frequency: 230; 2) amplitude: 20; 3) DC offset: varied from sample to sample; 4) upper backing potential: 2 volt; 5) lower backing potential: −2 volt; 6)scan rate: 1; 7) trigger delay: 0; 8) acquisition(A)/data(D) points:1024; 9) A/D rate: L2405 @19.0 cycles: 10) D/A: delay: 200; 11) set point gradient: 0.2; 12) step size: 0.001; 13) maximum gradient deviation: 0.001. As soon as the tracking gradient stabilized, the contact potential difference (“CPD”) in volt between gold film was recorded. The CPD of gold was then referencing the probe tip to (4.7-CPD) eV. The 4.7 eV (electron volt) is work-function of ambient aged gold film surface [Surface Science, 316, (1994), P380]. The CPD of gold was measured periodically while CPD of samples were being determined. Each sample was loaded into the cavity in the same manner as gold film sample with the four retention clips. On the retention clip making electrical contact with the sample care was taken to make sure good electrical contact was made with the exposed ITO pad at one corner. During the CPD measurement a small stream of nitrogen was flowed through the cell continuously without disturbing the probe tip. Once CPD of sample was recorded, the sample work-function or energy potential was then calculated by adding CPD of the sample to the difference of 4.7 eV and CPD of gold.

Tn this example, Celnax CX-Z300H used for illustration was also purchased from Nissan Chemical Industries, LTD from Houston, Tex. The Celnax is antimony double oxide (antimony zirconate) hydrosol, which was determined to contain 274.0% (w/w) oxide and the rest is water. It has pH 6.9 and particle size of 20 nm using BET method. To determine work-function of the semiconductive oxide film, a diluted CX-Z300H was made by mixing 5.004 g of the hydrosol with 13.825 g deionized water. The diluted sample contains only 7.19% (w/w) oxide. It was spin-coated at a speed of 1,800 rpm for 60 seconds on one of the ITO substrates described in the general procedure of film sample preparation. The zinc/antimony double oxide film on the ITO/glass substrate was then baked at 130° C. in air for 10 minutes. Prior to Kelvin probe measurement of the oxide film sample, a gold film was measured first. Contact potential difference (CPD) between gold film and the Kelvin probe tip is 0.663 volt. CPD between the oxide film and Kelvin probe tip was determined to be 0.87 volt. Work-function of the antimony oxide surface was therefore calculated to be 4.91 eV using 4.7 eV for work-function of air-aged gold. This work-function (Wf) data is listed in Table 1 as a control to determine effect of addition of Nafion® on its work-function.

Nafion® used for addition to CX-Z300H has an EW of 1000 and was made using a procedure similar to the procedure in U.S. Pat. No 6,150,426, Example 1, Part 2, except that the temperature is approximately 270° C. As made Nafion® is at 25% (w/w) in water. The 25% dispersion was first diluted to 12% before use. The general procedure for making the mixture was to add the Nafion® to CX-Z300H which was diluted with water first. Final solid concentration was aimed at about 7.2% (w/w) in water, but the ratio of acid-equivalent/1 g double oxide was kept at five different levels. For the example of 5.0×10−4 acid-equivalent/1 g antimony/zinc oxide, 5.0091 g CX-Z300H was added with 17.6691 g deionized water. It was stirred with a roller and than added with 5.6859 g Nafion®. The final solid concentration is 7.18% and the acid-equivalent/1 g oxide is 5.0×10−4. Each dispersion sample listed in Table 1 was made in the same manner and was filtered through a 0.45 μm HV filter onto an ozone-treated ITO substrate for spin-coating at 1,800 RPM for 60 seconds. The spin-coated films were then baked at 130° C. in air for 10 minutes and measured for contact potential difference with Kelvin probe. Table 1 clearly shows that work-function of antimony/zinc double oxide film surface is low, but increases as Nafion® is added to CX-Z300H. High work-function is critical for OLEDs as a buffer layer for device function.

TABLE 1 Effect of acid (Nafion ®) equivalent/1 gram-oxide on work-function (Wf) Acid equivalent/1 g oxide CPD (volt) Wf (eV, ref. To Au) 0 0.87 4.91   1 × 10−4 1.02 5.06 2.6 × 10−4 1.37 5.41 5.6 × 10−4 1.60 5.64 7.2 × 10−4 1.77 5.81 2.5 × 10−3 1.99 6.03

Example 3

This example illustrates the effect of the addition of Poly (VF2/PSEBVE) to a semiconductive oxide dispersion on its work-function.

In this example, Celnax CX-Z300H was also used to determine effect of poly(VF2/PSEBVE) on work-function of zinc/antimony double oxide. Synthesis of of Poly(VF2/PSEBVE) was illustrated later in this example. The procedure described in Example 2 for film preparation of zinc/antimony oxide, and its admixture with Poly(VF2/PSEBVE), and contact potential difference measurement for determination of work-function was closely followed. The work-function data listed in Table 2 clearly shows that work-function of antimony/zinc double oxide film surface is low, but increase as Nafion® is added to CX-Z300H. High work-function is critical for OLEDs as a buffer layer for device function.

Poly(VF2/PSEBVE) used for adding to Celnax CX-Z300H was made as follows.

a) Synthesis of an organic solvent wettable Poly(VF2/PSEBVE) of 1,1-difluoroethylene (“VF2”) and 2-(1,1-difluoro-2-trifluoromethyl)allyloxy)-1,1,2,2-tetrafluoroethanesulfonyl fluoride (“PSEBVE”):

A 400 mL Hastelloy C276 reaction vessel was charged with 160 mL of Vertrel® XF, 4 mL of a 20 wt. % solution of HFPO dimer peroxide in Vertrel® XF, and 143 g of PSEBVE (0.42 mol). The vessel was cooled to −35° C., evacuated to −3 PSIG, and purged with nitrogen. The evacuate/purge cycle was repeated two more times. To the vessel was then added 29 g VF2 (0.45 mol). The vessel was heated to 28° C., which increased the pressure to 92 PSIG. The reaction temperature was maintained at 28° C. for 18 h at which time the pressure had dropped to 32 PSIG. The vessel was vented and the crude liquid material was recovered. The Vertrel® XF was removed in vacuo to afford 110 g of desired copolymer.

b) Conversion of the sulfonyl fluoride copolymer prepared above to sulfonic acid

20 g of dried polymer and 5.0 g lithium carbonate were Refluxed in 100 mL dry methanol for 12 h. The mixture was brought to room temperature and filtered to remove any remaining solids. The methanol was removed in vacuo to isolate the lithium salt of the polymer. The lithium salt of the polymer was then dissolved in water and added with Amberlyst 15, a protonic acid exchange resin which had been washed thoroughly with water until there was no color in the water. The mixture was stirred and filtered. Filtrate was added with fresh Amberlyst 15 resin and filtered again. The step was repeated two more times. Water was then removed from the final filtrates and the solids were then dried in a vacuum oven.

Films made from VF2-PSEBVE acid are wettable by organic solvents. Phenylhexane will have a contact angle less than 40° on the films.

TABLE 2 Effect of acid [poly(VF2/PSEBVE)] equivalent/ gram-oxide on work-function Acid equivalent/1 g oxide CPD Wf (eV, ref. To Au) 0 0.87 4.91 1.0 × 10−4 1.29 5.34 2.5 × 10−4 1.56 5.61 5.0 × 10−4 1.79 5.84 1.0 × 10−3 1.98 6.06 1.7 × 10−3 2.06 6.13

Example 4

This example illustrates the effect of the addition of Poly (E/PSEPVE) to a semiconductive oxide dispersion on its work-function. In this example, Celnax CX-Z300H was also used to determine effect of poly(E/PSEPVE) on work-function of zinc/antimony double oxide. Synthesis of of Poly(E/PSEPVE) was described later in this example. The procedure described in Example 2 for film preparation of zinc/antimony oxide, and its admixture with Poly(E/PSEPVE), and contact potential difference measurement for determination of work-function was closely followed. The work-function data listed in Table 3 clearly shows that addition of Poly(E/PSEPVE) to CX-Z300H has enhanced work-function of antimony/zinc double oxide. High work-function is critical for OLEDs as a buffer layer for device function.

Poly(E/PSEPVE) used for adding to Celnax CX-Z300H was made as follows.

a) Synthesis of an organic solvent wettable Poly(E/PSEPVE) of ethylene (“E”) and 2-(2-(1,2,2-trifluorovinyloxy)-1,1,2,3,3,3-hexafluoropropoxy)-1,1,2,2-tetrafluoroethanesulfonyl Fluoride (“PSEPVE”):

A 210 mL Hastelloy C276 reaction vessel was changed with 60 g of PSEPVE (0.13 mol) and 1 mL of a 0.17 M solution of HFPO dimer peroxide in Vertrel® XF. The vessel was cooled to −35° C., evacuated to −3 PSIG, and purged with nitrogen. The evacuate/purge cycle was repeated two more times. To the vessel was then added 20 g ethylene (0.71 mol) and an additional 900 PSIG of nitrogen gas. The vessel was heated to 24° C., which increased the pressure of 1400 PSIG. The reaction temperature was maintained at 24° C. for 18 h. at which time the pressure had dropped to 1350 PSIG. The vessel was vented and 61.4 g of crude material was recovered. 10 g of this material were dried at 85° C. and 20 milliTorr for 10 h. to give 8.7 g of dried polymer.

b) Conversion of the sulfonyl fluoride copolymer prepared Above to sulfonic acid

A mixture of 19.6 g of dried polymer and 5.6 g lithium carbonate were refluxed in 300 mL of dry methanol for 6 h. The mixture was brought to room temperature and filtered to remove any remaining solids. The methanol was removed in vacuo to afford 15.7 g of the lithium salt of the polymer. The lithium salt of the polymer was then dissolved in water and added with Amberlyst 15, a protonic acid exchange resin which had been washed thoroughly with water until there was no color in the water. The mixture was stirred and filtered. Filtrate was added with fresh Amberlyst 15 resin and filtered again. The step was repeated two more times. Water was then removed from the final filtrates and the solids were then dried in a vacuum oven.

Films made from E-PSEPVE acid are wettable by organic solvents. Phenylhexane will have a contact angle less than 40° on the films.

Example 5

This example illustrates the effect of the addition of Poly (NBD/PSEPVE) to a semiconductive oxide dispersion on its work-function.

In this example, Celnax CX-Z300H was also used to determine effect of poly(NBD/PSEPVE) on work-function of zinc/antimony double oxide. Synthesis of of Poly(NBD/PSEPVE) was described later in this example. The procedure described in Example 2 for film preparation of a mixture of zinc/antimony oxide and Poly(NBD/PSEPVE), and contact potential difference measurement for determination of work-function was closely followed. The work-function data listed in Table 3 clearly shows that addition of Poly(NBD/PSEPVE) to DX-Z300H has enhanced work-function of antimony/zinc double oxide. High work-function is critical for OLEDs as a buffer layer for device function.

Poly(NBD/PSEPVE) used for adding to Celnax CX-Z300H was made as follows.

a) Synthesis of 3,3,4-trifluoro-4-(perfluorosulfonylethoxy) Tricyclo[4.2.1.02,5]-non-7-ene (NBD-PSEVE).

A 1000 mL Hastelloy C276 reaction vessel was charged with a mixture of 2,5-norbornadiene (98%, Aldrich, 100 g), and hydroquinone (0.5 g). The vessel was cooled to −6° C., evacuated to −20 PSIG, and purged with nitrogen. The pressure was again reduced to −20 PSIG and 2-(1,2,2-trifluorovinyloxy)-1,1,2,2-tetrafluoroethanesulfonyl fluoride (305 g) was added. The vessel was agitated and heated to 190° C. at which time the inside pressure was 126 PSIG. The reaction temperature was maintained at 190° C. for 6 h. The pressure dropped to 47 PSIG at which point the vessel was vented and cooled to 25° C.

The crude monomer was distilled using a spinning-band Column (BP=110-120° C. @40 Torr, 2100 RAM) to afford 361 g of colorless liquid consisting of a mixture of isomers. The chemical structure was confirmed by both GCMS and 19F and 1H NMR. MS: m/e 372 (M+); 353 (base, M+−F), 289 (M+-SO2F), 173 (C9H8F34).

b) Synthesis of a TFE and NBD-PSEVE sulfonyl fluoride copolymer.

A 400 mL pressure vessel was swept with nitrogen and charged with 74.4 g (0.20 mL) of NBD-PSEVE, 50 mL of Solkane 365 mfc (1,1,1,3,3-pentrafluorobutane 0.80 g of Perkadox® 16N. The vessel was closed, cooled in dry ice, evacuated, and changed with 30 g (0.30 mol) of TFE. The vessel contents were heated to 50° C. and agitated for 18 hr as the internal pressure decreased from 195 to 164 psi. The vessel was cooled to temperature and vented to one atmosphere. The vessel contents were added slowly to excess hexane. The solid was filtered, washed with hexane and dried in a vacuum oven at about 80° C. There was isolated 32.3 g of the white copolymer. Its fluorine NMR spectrum showed peaks at +44.7 (1F, SO2F), −74 to −87 (2F, OCF2), −95 to −125 (CF2, 4F from NBD-PSEVE and 4F from TFE), −132.1 (1F, CF). From integration of the NMR, polymer composition was calculated to be 48% TFE and 52% NBD-PSEVE. GPC analysis: Mn=9500, Mw=17300, Mw/Mn=1.82 DSC Tg at 207° C. Anal. Found: C, 33.83; H, 1.84; F, 45.57.

c) Hydrolysis of a TFE/NBD-PSEVE sulfonyl fluoride Copolymer for conversion to acid copolymer.

22.53 g (48.5 mmoles —SO2F) TFE/NBD-PSEVE were placed in a 10000 mL distillation flask. This flask was equipped with a magnetic stirrer, condenser and nitrogen inlet adapter. To the flask, 350 mL methanol/water mixture ()1/1) and 19.24 (200 mmoles) ammonium carbonate were added. The Flask was then immersed in an oil bath heated to 75° C. for 24 hours. 19F-NMR shows the absence of −δ40, indicating that sulfonyl fluoride was hydrolyzed to below the detection limit.

The entire content (−376 g) of the hydrolyzed mixture was further treated for conversion to acid. 30 g protonic exchange resins were added to the mixture and left stirred for 1 hr. The resin was filtered and fresh 30 g acid resins were added and left stirred for 15 hrs and filtered again. The filtrate was treated with fresh 20 g acidic resins for half an hour and again the filtrate was treated with fresh 30 g acidic resins for half an hour. The final filtrate was then placed in around bottom flask which was immersed in an oil bath heated to 60° C. Once two thirds of the content were removed through evaporation, the oil bath heat was turned off until the content became dried. Dried solid, which was yellowish, weighed 18.5 g.

A few pieces of the solid was dissolved in water which turned into acidic. A couple of drops of the solution were cast on a microscope slide. It formed a smooth continuous film. The film surface can be wetted easily with p-xylene, which is a common solvent for light emitting materials.

TABLE 3 Effect of acid (5 × 10−4 acid equivalent/1 gram-oxide on work-function CPD vs. Kelvin Work-function Acid Probe Tip (eV; ref. To Au) None (Zinc antimonate) 0.87 4.91 Poly(E/PSEPVE) 1.51 5.64 Poly(NBD/TFE-PSEPVE) 1.42 5.54

Example 6

This example illustrates the effect of the addition of Nafion® dispersed in methanol to a semiconductive oxide dispersion on its work-function. Nafion® is a trademark for poly(perfluoroethylenesulfonic acid) from E.I. du Pont de Nemours and Company (Wilmington, Del., USA).

In this example, Celnax CX-Z641 M used for illustration Was also purchased from Nissan Chemical Industries, LTD from Houston, Tex. The Celnax is antimony double oxide methanosol, which was determined to contain 61.4% (w/w) oxide and the rest is methanol. It has pH 8.2 and particle size of 20 nm by BET method. To determine work-function of the semiconductive oxide film, a diluted CX-Z641 M was made by mixing 14.1889 g of the methanosol with 70.2178 g methanol. The diluted sample contains only 10.03% (w/w) oxide. It was filtered through a 0.45 μm HV filter for spin-coating at a speed of 3,000 rpm for 60 seconds on one of the ITO substrates described in the general procedure of film sample preparation. The zinc/antimony double oxide film on the ITO/glass substrate was then baked at 110° C. for 10 minutes and the thickness of the film was determined to be 100 nm (nanometer). Prior to Kelvin probe measurement of the oxide film sample, a gold film was measured first. Contact potential difference (CPD) between gold film and the Kelvin probe tip is 0.615 volt. Contact potential difference between the oxide film and Kelvin probe tip was determined to be 0.549 volt. Work-function of the antimony oxide surface was therefore calculated to be 4.63 eV using 4.7 eV for work-function of air-aged gold. This work-fuction data is listed in Table 4 as a control to determine effect of addition of Nafion® on its work-function.

Nafion®/methanol dispersion used for adding to CX-Z641 M was made as follow. An aqueous Nafion® dispersion having EW of 1000 was made first using a procedure similar to the procedure in U.S. Pat. No. 6,150,426, Example 1, Part 2, except that the temperature is approximately 270° C. As made aqueous Nafion® dispersion was then freeze-dried to Nafion® solids. 10.5475 g of the freeze-dried Nafion® solids were mixed with 94.2821 g methanol to obtain 10.06% (w/w) Nafion® in methanol. 11.75 g of the methanol-diluted CX-Z641 M dispersion was mixed with 11.68 g of the 10.06% Nafion®/methanol dispersion. The resulting dispersion contains 10.04% (w/w) zinc-antimony oxide/Nafion® in Methanol and has a pH of 0.5. Portion of the dispersion was filtered through a 0.45 μm HV filter for spin-coating at a speed of 5,000 rpm for 60 seconds on one of the ITO substrates described in the general procedure of film sample preparation. The zinc/antimony double oxide film on the ITO/glass substrate was then baked at 110° C. in air for 10 minutes and the film thickness was determined to be 173 nm. Its work-function is listed in Table 4, which shows that Nafion® has enhanced antimony/zinc double oxide from 4.63 eV to 5.37 eV. High work-function is critical for OLEDs as a buffer layer for device function.

A portion of the Nafion®/zinc-antimony oxide/methanol dispersion was adjusted to pH 7.8 with aqueous NH4OH. The dispersion maintains its stability and baked film made from it still has work-function of 5.38 eV.

TABLE 4 Effect of Nafion ® on work-function of zinc/antimony double oxide CPD vs. Kelvin Work-function Acid Probe Tip (eV; ref. To Au) None (Zinc antimonate) 0.549 4.63 Nafion ® added 1.282 5.37 (pH 0.4 dispersion) Nafion ® added first, NH4OH 1.293 5.38 second (pH 7.8 dispersion)

Comparative Example A

This example illustrates device performance of a polymeric light emitting diode on an antimony/zinc double oxide film without containing Nafion®.

The 10.03% (w/w) antimony/zinc double oxide in methanol produced semiconductive oxide films, which had work-function of 4.63 eV as illustrated in Example 6. The work-function is low and this comparative example is to demonstrate its device functions as a buffer layer for a light emitting diode. The 10.03% (w/w) antimony/zinc double oxide in methanol prepared in Example 6 was filtered through 0.45 μm HV filter for spin-coating at a speed of 3,000 rpm for 60 seconds on glass/ITO backlight substrates (30 mm×30 mm) and baked at 130° C. in air for 15 minutes. Each ITO substrate having ITO thickness of 100 to 150 nm consists of 3 pieces of 5 mm×≡mm pixels and 1 piece of 2 mm×2 mm pixel for light emission. The baked zinc/antimony oxide films had thickness of 100 nm. The ITO/glass substrates containing the double oxide film were transferred into a glove box and 76 nm of Lumation Green K2 1303 [1% (w/v) in p-Xylene spun at 1,000 RPM] from Sumitomo Chemicals Company (Japan) were spun on top. The Green K2 layer was baked at 130° C. on a hot plate inside the glove box for 30 minutes before transfer into an evaporator and evaporation of 3 nm of Barium and 250 nm of Aluminum as cathode. Encapsulation was done by epoxy and a glass coverslip. The device had current efficiency less than 0.7 cd/A from above zero to 3,000 nits.

Example 7

This example illustrates the effect of the addition of Nafion® dispersed in methanol on the performance of a semiconductive oxide dispersion of a polymeric light emitting diode.

10.04% (w/w) zinc-antimony oxide/Nafion® in methanol produced semiconductive oxide films which had work-function of 5.37 eV. The work-function is melt higher than that in comparative Example 1, where Nafion® was absent from the double oxide dispersion. This example demonstrates the films' device function as a buffer layer for a light emitting diode. The 10.04% (w/w) zinc-antimony oxide/Nafion® in methanol prepared in Example 6 was filtered through 0.45 μm HV filter for spin-coating at a speed of 5,000 rpm for 60 seconds on glass/ITO backlight substrates (30 mm×30 mm) and baked at 130° C. in air for 15 minutes. The remaining fabrication of the devices was carried out in the same manner as described in Comparative Example 1. The device had current efficiency 11 cd/A from above zero to 10,000 nits. This example clearly shows that addition of Nafion® to antimony-zinc oxide dispersion in methanol has enhanced their work-function and light emitting device performance as a buffer layer.

Comparative Example B

This comparative example illustrates device performance of a polymeric light diode on an antimony/zinc double oxide film without Nafion®.

In this comparative example, 5.99% antimony/zinc oxide dispersion in water was made by adding 19.3706 g deionized water to 5.5143 g CX-Z300H. The resulting dispersion has a pH of 8. The 5.99% (w/w) antimony/zinc double oxide in water was first determined to produce films which had work-function of 4.44 eV. The work-function is low and this comparative example demonstrates the device function as a buffer layer for a light emitting diode. The 5.99% antimony/zinc double oxide in water was also filtered through 0.45 μm HV filter for spin-coating at a speed of 3,000 rpm for 60 seconds on glass/ITO backlight substrates (30 mm×30 min) and baked at 130° C. in air for 15 minutes. Each ITO substrate having ITO thickness of 100 to 150 nm consists of 3 pieces of 5 mm×5 mm pixels and 1 piece of 2 mm×2 mm pixel for light emission. The baked zinc/antimony oxide films had thickness of 35 nm. The ITO/glass substrates containing the double oxide film were transferred into a glovebox and 76 nm of Lumination Green K2 1303 [1% (w/v) in p-Xylene spun at 1,000 RPM] from Sumitomo Chemicals Company (Japan) were spun on top. The Green K2 layers were baked at 130° C. on a hot plate inside the glove box for 30 minutes before transfer into an evaporator and evaporation of 3 nm of Barium and 250 nm of Aluminum as cathode. Encapsulation was done by epoxy and a thin piece of glass lid. The device has current efficiency less than 0.5 cd/A from above zero to 3,000 nits. The device efficiency is too low to be useful.

Example 8

This example illustrates the effect of the addition of Nafion® dispersed in water on the performance of a semiconductive oxide dispersion of a polymeric light diode.

In this example, 7.2% antimony/zinc oxide/Nafion® dispersion in water was made by first adding 17.6348 g of deionized water to 5.6559 g CX-Z300H. To the resulting dispersion was added 5.6559 g Nafion® (12%, w/w) dispersion described in Example 2. The resulting dispersion had a pH of 2.2. The 7.2 (w/w) antimony-zinc oxide/Nafion® in water was first determined to produce semiconductive films which had work-function of 5.23 eV. This work-function is much higher than that of the films produced from the composition without Nafion® in Comparative Example 2. This example demonstrates the device function as a buffer layer for a light emitting diode. The 7.2% antimony/zinc oxide/Nafion® dispersion was filtered through 0.45 μm HV filter for spin-coating at a speed of 1,8000 rpm for 60 seconds on glass/ITO backlight substrates (30 mm×30 mm) and baked at 130° C. in air for 15 minutes. The baked zinc-antimony oxide/Nafion® films had thickness of 35 mm. The remaining fabrication of the devices was carried out in the same manner as described in Comparative Example 2. The device had current efficiency 11 Ed/A from above zero to 10,0000 nits. This example clearly shows that addition of Nafion® to antimony-zinc oxide dispersion in methanol enhanced its work-function and light emitting device performance as buffer layer.

Note that not all of the activities described above in the general description or the examples are required, that a portion of a specific activity may not be required, and that one or more further activities may be performed in addition to those described. Still further, the order in which activities are listed are not necessarily the order in which they are performed.

In the foregoing specification, the concepts have been described with reference to specific embodiments. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the invention as set forth in the claims below. Accordingly, the specification and figures are to be regarded in an illustrative rather than a restrictive sense, and all such modifications are intended to be included within the scope of invention.

Benefits, other advantages, and solutions to problems have Been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any feature(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential feature of any or all the claims.

It is to be appreciated that certain features are, for clarity, described herein in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination. Further, references to values stated in ranges include each and every value within that range subcombination.

Claims

1. A buffer composition consisting essentially of semiconductive oxide particles wherein the semiconductive oxide particles comprise a bimetallic oxide selected from indium-tin oxide (“ITO”), indium-zinc-oxide (“IZO”), gallium-indium oxide, and zinc-antimony double oxide and a fluorinated acid polymer wherein the fluorinated acid polymer has a formula according to Formula XV:

where j≧0, k≧0 and 4≦(j+k)≦199,
Q1 and Q2 are F or H, Rf2 is F or a perfluoroalkyl radical having 1-10 carbon atoms either unsubstituted or substituted by one or more ether oxygen atoms,
h=0 or 1, i=0 to 3, g=0 or 1, and
E4 is H or an alkali metal,
wherein the buffer composition has a work-function greater than 5.0 eV.

2. An electric device comprising a buffer composition of claim 1.

3. A buffer composition consisting essentially of semiconductive oxide particles wherein the semiconductive oxide particles comprise a bimetallic oxide selected from indium-tin oxide (“ITO”), indium-zinc oxide (“IZO”), gallium-indium oxide, and zinc-antimony double oxide and a fluorinated acid polymer wherein the fluorinated acid polymer has a formula according to Formula: wherein the buffer composition has a work-function greater than 5.0 eV.

where j≧0, k≧0 and 4≦(j+k)≦199,
Q1 and Q2 are F or H,
Rf2 is F or a perfluoroalkyl radical having 1-10 carbon atoms either unsubstituted or substituted by one or more ether oxygen atoms,
h=0 or 1, i=0 to 3, g=0 or 1, and
E5 is Li, Na, or K,
Referenced Cited
U.S. Patent Documents
3282875 November 1966 Connolly et al.
4358545 November 9, 1982 Ezzell et al.
4433082 February 21, 1984 Grot et al.
4552927 November 12, 1985 Warren
4731408 March 15, 1988 Jasne
4795543 January 3, 1989 Stetter et al.
4869979 September 26, 1989 Ohtani et al.
4940525 July 10, 1990 Ezzell
4959430 September 25, 1990 Jonas et al.
5002700 March 26, 1991 Otagawa et al.
5069820 December 3, 1991 Jen et al.
5160457 November 3, 1992 Elsenbaumer et al.
5185100 February 9, 1993 Han et al.
5247190 September 21, 1993 Friend et al.
5286413 February 15, 1994 Hannecart et al.
5300575 April 5, 1994 Jonas et al.
5317169 May 31, 1994 Nakano et al.
5378402 January 3, 1995 Cross et al.
5463005 October 31, 1995 Desmarteau
5537000 July 16, 1996 Alivisatos et al.
5705888 January 6, 1998 Staring et al.
5798170 August 25, 1998 Zhang et al.
5863465 January 26, 1999 Kinlen
5917279 June 29, 1999 Elschner et al.
5986400 November 16, 1999 Staring et al.
5994496 November 30, 1999 Van Haare et al.
6097147 August 1, 2000 Baldo et al.
6150426 November 21, 2000 Curtin et al.
6210790 April 3, 2001 Crivello
6303238 October 16, 2001 Thompson et al.
6303943 October 16, 2001 Yu et al.
6319428 November 20, 2001 Michot et al.
6324091 November 27, 2001 Gryko et al.
6337370 January 8, 2002 Bae et al.
6358437 March 19, 2002 Jonas et al.
6515314 February 4, 2003 Duggal et al.
6593690 July 15, 2003 McCormick et al.
6632472 October 14, 2003 Louwet et al.
6670645 December 30, 2003 Grushin et al.
6706963 March 16, 2004 Gaudiana et al.
6717358 April 6, 2004 Liao et al.
6756474 June 29, 2004 Hsu
6830828 December 14, 2004 Thompson et al.
6875523 April 5, 2005 Grushin et al.
6923881 August 2, 2005 Tateishi et al.
6924047 August 2, 2005 Radu et al.
6963005 November 8, 2005 Lecloux et al.
7112369 September 26, 2006 Wang et al.
7166010 January 23, 2007 Lamansky et al.
7189771 March 13, 2007 Hsu
7211824 May 1, 2007 Lazarev
7244797 July 17, 2007 Kurihara et al.
7250461 July 31, 2007 Hsu et al.
7307276 December 11, 2007 Andriessen
7317047 January 8, 2008 Hsu
7338620 March 4, 2008 Hsu et al.
7354532 April 8, 2008 Hsu et al.
7371336 May 13, 2008 Hsu et al.
7390438 June 24, 2008 Hsu et al.
7431866 October 7, 2008 Hsu et al.
7455793 November 25, 2008 Hsu et al.
7462298 December 9, 2008 Hsu et al.
7569158 August 4, 2009 Waller et al.
7593004 September 22, 2009 Spath et al.
7727421 June 1, 2010 Hsu et al.
7749407 July 6, 2010 Hsu et al.
7837901 November 23, 2010 Hsu et al.
8088499 January 3, 2012 Wang et al.
20010019782 September 6, 2001 Igarashi et al.
20010038937 November 8, 2001 Suzuki et al.
20020009680 January 24, 2002 Majumdar et al.
20020017612 February 14, 2002 Yu et al.
20020038999 April 4, 2002 Cao et al.
20020041151 April 11, 2002 Park et al.
20020098377 July 25, 2002 Cao et al.
20020099119 July 25, 2002 Craig
20020127381 September 12, 2002 Will et al.
20020190250 December 19, 2002 Grushin et al.
20020192476 December 19, 2002 Kambe et al.
20030020073 January 30, 2003 Long et al.
20030108771 June 12, 2003 Lecloux et al.
20030118829 June 26, 2003 Hsu
20030213952 November 20, 2003 Iechi et al.
20030222250 December 4, 2003 Hsu
20040009346 January 15, 2004 Jang et al.
20040036067 February 26, 2004 Andriessen
20040072987 April 15, 2004 Groenendaal et al.
20040092700 May 13, 2004 Hsu
20040102577 May 27, 2004 Hsu et al.
20040124504 July 1, 2004 Hsu
20040127637 July 1, 2004 Hsu et al.
20040149952 August 5, 2004 DePenning et al.
20040149962 August 5, 2004 Andriessen
20040206942 October 21, 2004 Hsu
20040217877 November 4, 2004 Kokonaski et al.
20040222413 November 11, 2004 Hsu et al.
20040254297 December 16, 2004 Hsu et al.
20040262599 December 30, 2004 Bernds et al.
20050040374 February 24, 2005 Chittibabu et al.
20050069726 March 31, 2005 Douglas et al.
20050070654 March 31, 2005 Hsu
20050089679 April 28, 2005 Ittel et al.
20050124784 June 9, 2005 Sotzing
20050184287 August 25, 2005 Herron et al.
20050205860 September 22, 2005 Hsu et al.
20050208328 September 22, 2005 Hsu et al.
20050209388 September 22, 2005 Hsu et al.
20050209392 September 22, 2005 Luo et al.
20050222333 October 6, 2005 Hsu
20050224765 October 13, 2005 Hsu et al.
20050224788 October 13, 2005 Hsu et al.
20060051401 March 9, 2006 Manohar
20060076050 April 13, 2006 Williams et al.
20060076557 April 13, 2006 Waller et al.
20060076577 April 13, 2006 Boos et al.
20060113510 June 1, 2006 Luo et al.
20060180810 August 17, 2006 Lee et al.
20060274049 December 7, 2006 Spath et al.
20060289843 December 28, 2006 Hsu et al.
20060292362 December 28, 2006 Hsu et al.
20070045591 March 1, 2007 Hsu et al.
20070069184 March 29, 2007 Hsu et al.
20070069185 March 29, 2007 Hsu et al.
20070096082 May 3, 2007 Gaynor et al.
20080128662 June 5, 2008 Hsu et al.
20080135809 June 12, 2008 Hsu
20080213594 September 4, 2008 Hsu
20080248314 October 9, 2008 Hsu et al.
20080251768 October 16, 2008 Hsu et al.
20080258605 October 23, 2008 Yukinobu
20080283800 November 20, 2008 Hsu
20080296536 December 4, 2008 Hsu et al.
20090008609 January 8, 2009 Yeisley et al.
20090072201 March 19, 2009 Hsu et al.
20090114884 May 7, 2009 Hsu
20090154059 June 18, 2009 Wessling et al.
Foreign Patent Documents
1439029 August 2003 CN
1934725 March 2007 CN
4334390 April 1995 DE
560721 September 1993 EP
440957 March 1996 EP
488321 October 1997 EP
817540 January 1998 EP
593111 June 1998 EP
1026152 August 2000 EP
1191612 March 2002 EP
1191614 March 2002 EP
1231251 August 2002 EP
1286569 February 2003 EP
962943 December 2003 EP
1371709 December 2003 EP
1408563 April 2004 EP
1 026 152 July 2006 EP
1726051 November 2006 EP
2632979 December 1989 FR
2124635 February 1984 GB
62119237 May 1987 JP
02249221 October 1990 JP
04234453 August 1992 JP
05129162 May 1993 JP
09176310 July 1997 JP
11186103 July 1999 JP
11353934 December 1999 JP
2000505249 April 2000 JP
2001006878 January 2001 JP
2001270999 October 2001 JP
2001325831 November 2001 JP
2002500408 January 2002 JP
2002082082 March 2002 JP
2002246177 August 2002 JP
2003187983 July 2003 JP
2003217862 July 2003 JP
2003264083 September 2003 JP
2003297582 October 2003 JP
2004500449 January 2004 JP
2004501494 January 2004 JP
2004502004 January 2004 JP
2004082395 March 2004 JP
2005537348 December 2005 JP
2006500463 January 2006 JP
2006108064 April 2006 JP
2006527277 November 2006 JP
2007502531 February 2007 JP
2007529607 October 2007 JP
200304238 September 2003 TW
9831716 July 1998 WO
9934371 July 1999 WO
9952954 October 1999 WO
0070655 November 2000 WO
0138219 May 2001 WO
0141230 June 2001 WO
0141512 June 2001 WO
0199192 December 2001 WO
0199207 December 2001 WO
0200759 January 2002 WO
0202714 January 2002 WO
0215645 February 2002 WO
02065484 August 2002 WO
02099907 December 2002 WO
03006515 January 2003 WO
03006537 January 2003 WO
03008424 January 2003 WO
WO 03/006537 January 2003 WO
WO 03/008424 January 2003 WO
03012908 February 2003 WO
03040257 May 2003 WO
03046540 June 2003 WO
03050824 June 2003 WO
03063555 July 2003 WO
03074601 September 2003 WO
03091688 November 2003 WO
2004016710 February 2004 WO
2004020444 March 2004 WO
2004020502 March 2004 WO
2004029128 April 2004 WO
2004029133 April 2004 WO
2004029176 April 2004 WO
2004094501 November 2004 WO
2004105150 December 2004 WO
2005003083 January 2005 WO
2005018012 February 2005 WO
2005024853 March 2005 WO
2005041217 May 2005 WO
2005052027 June 2005 WO
2005080525 September 2005 WO
2005090435 September 2005 WO
2005090436 September 2005 WO
2005093872 October 2005 WO
2005121217 December 2005 WO
2006073968 July 2006 WO
2006078264 July 2006 WO
2007002681 January 2007 WO
2007002740 January 2007 WO
2007092296 August 2007 WO
2007120143 October 2007 WO
Other references
  • Extended European Search Report for Application No. EP 10005557.3; Dec. 1, 2010.
  • Extended European Search Report for Application No. EP 06785720.0, counterpart to U.S. Appl. No. 11/476,979; Jun. 30, 2009.
  • Extended European Search Report for Application No. EP 10 01 1570; May 17, 2011.
  • Extended European Search Report for Application No. EP 06785724.3, counterpart to U.S. Appl. No. 11/476,487; May 25, 2011.
  • Extended European Search Report for Application No. EP 06 774 171.0, counterpart to U.S. Appl. No. 11/476,488; Jun. 21, 2011.
  • Extended European Search Report for Application No. 08866235.8, counterpart to U.S. Appl. No. 12/809,895; Mar. 19, 2012.
  • PCT International Search Report for PCT/US2003/030509. Counterpart to U.S. Appl. No. 10/669,422; C. Meiners, Authorized Officer; Feb. 17, 2004.
  • PCT International Search Report for PCT/US2005/008561; G. Wolfbauer, Authorized Officer; Jun. 30, 2005.
  • PCT International Search Report for International Application No. PCT/US2006/25129, counterpart to U.S. Appl. No. 11/476,488; Elizabeth Robinson, Authorized Officer; Feb. 6, 2008.
  • PCT International Search Report for International Application No. PCT/US2006/025128, counterpart to U.S. Appl. No. 11/476,979; Lee W. Young, Authorized Officer; ISA/US; Feb. 29, 2008.
  • PCT International Search Report for International Application No. PCT/US2006/025136, counterpart to U.S. Appl. No. 11/476,487; Randy P. Gulakowski, Authorized Officer; Feb. 29, 2008.
  • International Search Report for International Application No. PCT/US2008/070718, counterpart to U.S. Appl. No. 12/513,793; Benedikt Schlicke, Authorized Officer; Oct. 31, 2008.
  • PCT International Search Report for International Application No. PCT/US2008/088089, counterpart to U.S. Appl. No. 12/809,895; Lee W. Young, Authorized Officer; Feb. 18, 2009.
  • PCT International Search Report for International Application No. PCT/US2009/035079; Lee W. Young Authorized Officer Apr. 9, 2009.
  • Opposition Against EP 1726051 [UC0673EPEPT1], Opposition Document from Herzog Fiesser & Partner; Heraeus Precious Metals GmbH; Sep. 15, 2011 [German].
  • Opposition Against EP 1726051 [UC0673EPEPT1], Opposition Document from Herzog Fiesser & Partner; Heraeus Precious Metals GmbH; Sep. 15, 2011 [English Translation].
  • Opposition Against EP 1726051; Observations of the Patentee; May 31, 2012.
  • Opposition Against EP 1726051; (E6) Experimental Data: PEDOT; May 31, 2012.
  • Opposition Against EP 1726051; Main Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; First Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Second Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Third Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Fourth Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Fifth Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Sixth Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Seventh Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Eighth Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Ninth Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Tenth Auxiliary Request—Claims; May 31, 2012.
  • Opposition Against EP 1726051; Eleventh Auxiliary Request—Claims; May 31, 2012.
  • Opposition against EP 1726051; (E9) Experimental Data: Polypyrrole/Nafion; Jul. 2, 2012.
  • U.S. Appl. No. 10/804,503 (Issued as US Patent 7,317,047; Jan. 8, 2008 and published as US 2004/0206942. This is a US counterpart to opposed patent EP 1726051).
  • U.S. Appl. No. 10/803,114 (published as US Application No. 2005/0209388; Sep. 22, 2005.
  • Aleshin et al., “Transport Properties of Poly(3,4-ethylenedioxythiophene)/poly(styrenesulfonate),” Synthetic Metals, 1998, vol. 94, pp. 173-177.
  • Appleby et al., “Polymeric Perfluoro Bis-Sulfonomides as Possible Fuel Cell Electrolytes,” Journal of the Electrochemical Society, 1993, vol. 140, No. 1, pp. 109-111.
  • Aqad et al; “Synthesis of 3,4-Ethylenedioxyselenophene (EDOS): A Novel Building Block for Electron Rich Conjugated Polymers,” Organic Letters, 2001, vol. 3, pp. 4283-4285.
  • Arnautov et al., “New Dopant-Solvent System for Conductive PAN Films Production,” Synthetic Metals, 1997, vol. 84, No. 1-3, pp. 133-134, Elsevier Science S.A.
  • ASTM, Standard Practice for Testing the Shelf Life of Ink Jet Printer Cartridges, Jul. 2008.
  • Baytron Coating Guide Issue Oct. 2002—Obtained From www.hcstarck-echemicals.com.
  • Baytron H. C. Stark GmbH (Brochure) No Date.
  • Baytron P Vap A1 4083 and Baytron P VP CH 8000 Product Information for Electronic Grades Designed for Use as Hole-Injection Material in OLEDS—Obtained from www.hcstarck-echemicals.com.
  • Baytron Product info from baytron.com; Aug. 1, 2007.
  • Bharathan et al., “Polymer/metal Interfaces and the Performance of Polymer Light-Emitting Diodes,” Journal of Applied Physics, 1998, vol. 84(6), pp. 3207-3211.
  • Brown et al, “Built-in field electroabsorbtion spectroscopy of plymer light-emitting diodes incorporating a doped poly(3,4-ethylene dioxythiophene) hole injection layer,” Applied Physics Letters, AIP, American Institute of Physics, 1999, vol. 75, No. 12, pp. 1679-1681.
  • Cen et al., “1,1,2,2-Tetrafluoro-2-(polyfluoroalkoxy)ethanesulfonic Acids, 1,1,2,2-Tetrafluoro-2-(perfluoroalkoxy)ethanesulfonic Acids, and 2,2′-Oxybis(1,1,2,2-tetrafluoroethanesulfonic acid),” Inorganic Chemistry, 1988, vol. 27, pp. 1376-1377, American Chemical Society.
  • Colvin et al., “Light-Emitting Diodes Made from Cadmium Selenide Nanocrystals and a Semiconducting Polymer,” Nature, 1994, vol. 370, pp. 354-357.
  • “Conductive Polymer,” Definition from Wikipedia, The Free Encyclopedia.
  • Desmarteau, Novel Perfluoinated Ionomers and Ionenes, Journal of Fluorine Chemistry, 1995, vol. 72, pp. 203-208.
  • Downs et al., “Efficient Polymerization of Aniline at Carbon Nanotube Electrodes”, Advanced Materials, 1999, vol. 11, No. 12, pp. 1028-1031.
  • Feiring et al., “Aromatic Monomers with Pendant Fluoroalkylsulfonate and Sulfonimide Groups,” Journal of Fluorine Chemistry, 2000, vol. 105, No. 1, pp. 129-135.
  • Feiring et al., “Novel Aromatic Polymers with Pendant Lithium Perfluoroalkylsulfonate or Sulfinimide Groups,” Macromolecules, 2000, vol. 33, pp. 9262-9271.
  • Fowler et al., “Hydrogen detection by Polyaniline nanofibers on gold and platinum electrodes”, The Journal of Physical Chemistry C, 2001, vol. 113, No. 16, pp. 6444-6449.
  • Gustafsson et al., “Flexible Light-Emitting Diodes Made from Soluble Conducting Polymers,” Nature, 1992, vol. 357, pp. 477-479.
  • Hirai et al; “Electrochemical Behaviors of Polypyrrole, Poly-3-Methyl-thiophene, and Polyaniline Deposited on Nafion-Coated Electrodes,” Journal of the Electrochemical Society, 1988, vol. 135, No. 5, pp. 1132-1137, Electrochemical Society, Manchester, NH.
  • Hsu, “Novel Preparation and Properties of Conductive Polyaniline/Nafion® Film,” Synthetic Metals, 1991, vol. 41-43, pp. 671-674, Elsevier Sequoia, The Netherlands.
  • Huang et al., “Well-Dispersed Single-Walled Carbon Nanotube/Polyaniline Composite Films,” Carbon, vol. 41, 2003, pp. 2731-2736.
  • Iijima et al., Single-Shell Carbon Nanotube of 1-nm Diameter, Nature, 199, vol. 363, pp. 603-605.
  • Ivanov et al., “The Study of Carbon Nanotubules Produced by Catalytic Method,” Chemical Physics Letters, 1994, vol. 223, pp. 329-335.
  • Journet et al., Large-Scale Production of Single-Walled Carbon Nanotubes by the Electric-Arc Technique, Nature, 1997, vol. 388, pp. 756-758.
  • Kim et al., “Enhancement of Electrical Conductivity of Poly(3,4-ethylenedioxythiophene)/Poly(4-styrenesulfonate) by a Change of Solvents,” Synthetic Metals, 2002, vol. 126, No. 2/3, pp. 311-316.
  • Kitani et al., “Properties of Elastic Polyaniline,” Synthetic Metals, 1997, vol. 84, No. 1-3, pp. 83-84, Elsevier Science S.A.
  • Lee et al., Poly(thieno(3,4-b)thiophene) A New Stable Low Band Gap Conducting Polymer, Macromolecules, 2001, vol. 34, pp. 5746-5747.
  • Levi et al., “Polymer and Cathode Emission Studies of Polymer-Based Light-Emitting Diodes Under Strong Electrical Pulse Excitation,” Journal of Applied Physics, 2000, vol. 88, No. 5, pp. 2548-2552.
  • Li et al., “Large-Scale Synthesis of Aligned Carbon Nanotubes,” Science, 1996, vol. 274, pp. 1701-1703.
  • Lim et al., “Degradation of Organic Light-Emitting Devices Due to Formation and Growth of Dark Spots,” Materials Science and Engineering, 2001, pp. 154-159.
  • Madler et al., “Visibly Transparent and Radiopaque Inorganic Organic Composites from Flame-Made Mixed-Oxide Fillers,” Journal of Nanoparticle Research, 2005, vol. 8, No. 3-4, pp. 323-333.
  • Riedel et al., “Tailored Highly Transparent Composite Hole-Injection Layer Consisting of Pedot:PSS and SiO2 Nanoparticles for Efficient Polymer Light-Emitting Diodes,” Advanced Materials, 2011, vol. 23, pp. 740-745.
  • Römpp Chemistry Dictionary, 9th Edition, 1993, pp. 2459-2460 (Machine translation also submitted).
  • Schroedner et al., “Organische Feldeffekttransisoren auf Basis Halbleitender Polymere/Organic Field-Effect Transistors Based on Semiconducting Polymers,” Electrotechnik und Informationstechnik, Springer Verlag, 2003, vol. 120, No. 6, pp. 205-209 (Machine translation also submitted).
  • Schwendeman et al., “Perfluoroalkanoate-substituted PEDOT for Electronic Device Applications,” Advanced Functional Materials, 2003, vol. 13, No. 7, pp. 541-547.
  • Sharpe et al., “Improved Cationic Conductive Polymer,” Calgon Corp. Coating Conference (Proceeding), 1981, pp. 83-87.
  • Simpson et al., “Advances and Applications of Inherently Conductive Polymer Technologies Based on Poly(3,4-Ethylenedioxythiophene),” 2005 AIMCAL Fall Technical Conference.
  • Sotzing et al., “Poly(thieno(3,4-b)thiophene): A p- and n-Dopable Polythiophene Exhibiting High Optical Transparency in the Semiconducting State,” Macromolecules, 2002, vol. 35, pp. 7281-7286.
  • Stejskal et al., “Polyaniline Dispersions 10. Coloured Microparticles of Variable Density Prepared Using Stabilizer Mixtures,” Colloid Polymer Science, vol. 278, 2000, pp. 654-658.
  • Tang et al., “Organic/Inorganic Material for Coating on Metals,” Materials Research Society Symp. Proc., vol. 734, 2003, pp. B.9.57.1-7.
  • Thelakkat et al., “Poly(triarylamine)s- Synthesis and Application in Electroluminescent Devices and Photovoltaics,” Synthetic Metals, 1999, vol. 102, pp. 1125-1128.
  • Thess et al., “Crystalline Ropes of Metallic Carbon Nanotubes,” Science, 1996, vol. 273, pp. 483-487.
  • Wang, “Photoconductive Materials,” Kirk-Othmer Encyclopedia of Chemical Technology, Fourth Edition, 1996, vol. 18, pp. 837-860.
  • Wu et al., “Transparent, Conductive Carbon Nanotube Films,” Science, 2004, vol. 305, pp. 1273-1276.
  • Yuan et al., “Size and morphology effects of ZnO anode nanomaterials for Zn/Ni secondary batteries; Size and morphology effects of ZnO anode nanomaterials for Zn/Ni secondary batteries”, Nanotechnology, 2005, vol. 16, No. 6, pp. 803-808.
  • Yang et al., “The photoelectrochemical properties of TiO2 electrodes modified by quantum sized PbS and thiols”, Synthetic Metals, 2001, vol. 123, No. 2, pp. 267-272.
  • Posthumus, “UV Curable Acrylate Metal Oxide Nanocomposite Coatings,” Druk: Universiteitsdrukkerij Technishe Universiteit Eindhoven, 2004, pp. 1-118.
  • U.S. Appl. No. 60/105,662, filed Oct. 25, 1999, Zhen-Yu Yang et. al.
  • U.S. Appl. No. 60/176,881, filed Jan. 19, 2000, Jose M. Rodriguez Parada.
  • Wu et. al., Transparent, Conductive Carbon Nanotube Films, Science, 2004, vol. 305:1273-1276.
  • Lee et. al., Poly(thieno{3,4-b}thiophene). A New Stable Low Band Gap Conducting Polymer, Macromolecules, 2001, vol. 34:5746-5747.
  • Sotzing et. al., Poly{3,4-b}thiophene): A p- and n-Dopable Polythiophene Exhibiting High Optical Transparency in the Semiconducting State, Macromolecules, 2002, vol. 35:7281-7286.
  • A. Feiring et. al., Aromatic Monomers With Pendant Fluoroalkylsulfonate and Sulfonimide Groups J. Fluorine Chemistry, 2000, vol. 105:129-135.
  • Feiring et. al., Novel Aromatic Polymers With Pendant Lithium Perfluoroalkylsulfonate of Sulfonimide Groups, Macromolecules, 2000, vol. 33:9262-9271.
  • D. Desmarteau, Novel Perfluorinated Ionomers and Ionenes, J. Fluorine Chem., 1995, vol. 72:203-208.
  • A.J. Appleby et. al., Polymeric Perfluoro Bis-Sulfonimides as Possible Fuel Cell Electrolytes J. Electrochem. Soc., 1993, vol. 140:109-111.
  • G. Gustafsson et. al., Flexible Light-Emitting Diodes Made From Soluble Conducting Polymers, Nature, 1992, vol. 357:477-479.
  • Y. Wang, Photoconductive Polymers, Kirk-Othmer Encyclopedia of Chemical Technology, Fourth Edition, 1999, vol. 18:837-860.
  • PCT International Search Report and Written Opinion for International Application No. PCT/US06/25138 dated Feb. 29, 2008.
Patent History
Patent number: RE44853
Type: Grant
Filed: Apr 18, 2012
Date of Patent: Apr 22, 2014
Assignee: E I du Pont de Nemours and Company (Wilmington, DE)
Inventors: Che-Hsiung Hsu (Winston-Salem, NC), Hjalti Skulason (Buellton, CA), Mark Martello (San Clemente, CA)
Primary Examiner: Mark Kopec
Assistant Examiner: Jaison Thomas
Application Number: 13/450,142
Classifications
Current U.S. Class: The Organic Compound Is A Polymer (252/519.33); Zinc Compound (252/519.5); Tin Compound (252/520.1); Rare Earth Metal Compound (252/521.1)
International Classification: H01B 1/12 (20060101); H01B 1/02 (20060101);