Abstract: A sintered titanium carbide tool steel composition is provided comprising by weight about 15% to 40% primary grains of titanium carbide dispersed through a steel matrix making up the balance, the composition of said steel matrix consisting essentially by weight of about 3% to 7% chromium, about 2% to 6% molybdenum, about 2% to 8% nickel, about 0.2% to 0.6% carbon and the balance essentially iron.

Abstract: Relates to a sintered age-hardenable titanium carbide tool steel comprising by volume about 15% to 50% primary grains of titanium carbide dispersed through a high cobalt-containing steel matrix making up the balance, said matrix consisting essentially by weight of about 10% to 25% cobalt, about 5% to 20% chromium, about 0.5% to 5% molybdenum, 0 to 2% nickel, 0 to 0.15% carbon and essentially the balance at least about 50% iron.

Abstract: A sintered compact for use in a cutting tool and a method of producing the same are disclosed. The compact comprises 95 to 20 volume % of diamond finer than one micron in size and the balance binder also finer than one micron selected from the group of WC, (MoW)C, WC base cemented carbide and (MoW)C base cemented carbide.The method comprises pulverizing a diamond powder by using cemented carbide balls and a pot having a cemented carbide lining, mixing the diamond powder with a powder abraded from the balls and pot to produce a powder mix finer than one micron containing 95 to 20 volume % of diamond, heat-treating the powder mix in vacuum so as to degas, and hot-pressing the powder mix under high pressure at high temperature within the stable range of diamond.

Abstract: Method for hard-facing metal substrates is disclosed using a hard facing material consisting essentially of combined vanadium, tungsten and carbon and from about 5 to about 40% by weight of chromium carbide with up to 15% by weight in the aggregate of cobalt, iron, molybdenum and nickel.

Abstract: A method is provided for treating a metal working tool element made of cemented carbide materials, as hereinafter described, comprising the operation of implanting into a working surface of the tool element ions of a material such as to modify the implanted region of the working surface of the tool element in such a way as to prevent adhesion between the matrix metal of the cemented carbide tool element and a metal being worked by the tool element. Metal working tool elements so treated are also disclosed.