Abstract

A method is used to form an intermetal dielectric layer. According to the invention, an unbiased-unclamped fluorinated silicate glass layer used as a protection layer is formed by high density plasma chemical vapor deposition on a biased-clamped fluorinated silicate glass layer formed by high density plasma chemical vapor deposition to prevent the biased-clamped fluorinated silicate glass layer from being exposed in a planarization process.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The invention relates to a method for forming an integrated circuit, and more particularly, to a method for forming an intermetal dielectric layer with multilevel interconnects.

[0003] 2. Description of the Related Art

[0004] In an integrated circuit with two or more levels of interconnects, an intermetal dielectric layer must be placed between the levels for isolation. Generally, the intermetal dielectric layer must have characteristics such as good reliability, good mechanical stability, good compatibility, low water absorption capability, etc.

[0005] A typical material for the intermetal dielectric layer is silicon oxide that has a dielectric constant of about 4. However, since a device having a higher operation speed requires a material having a lower dielectric constant as the intermetal dielectric layer, fluorinated silicon glass (FSG) having a dielectric constant of about 3.5 is replacing the silicon oxide as the intermetal dielectric layer.

[0006] According to the prior art, the method to form the intermetal dielectric layer is as follows. A plurality of metal conductive lines is formed on a substrate. The plurality of metal conductive lines is distributed in two regions, respectively, a tied conductive line region (i.e. a dense line region) having a higher distribution density and a loose conductive line region (i.e. a iso line region) having a lower distribution density. A biased-clamped FSG layer is formed on the substrate by high density plasma chemical vapor deposition (HDPCVD), and fills gaps between metal lines. Before the biased-clamped FSG layer is formed, the process further comprises forming a silicon glass liner layer by HDPCVD. The silicon glass liner layer is used to prevent the metal lines from being attacked by fluorine. Then, an oxide layer is formed as a cap layer on the biased-clamped FSG layer by plasma enhanced chemical vapor deposition (PECVD). A chemical mechanical polishing process is subsequently performed on the oxide layer.

[0007] Due to different distribution densities, the spacing between conductive lines in different regions (the tied conductive line region and the loose conductive line region) is different. This may result in a large step height difference between the tied conductive line region and the loose conductive line region after the biased-clamped FSG layer and the cap layer are formed. Thus, the polishing stop for chemical mechanical polishing is difficult to control, and over-polishing easily arises. As a result, the biased-clamped FSG layer may be exposed. Since the amount of fluorine in the biased-clamped FSG layer is difficult to control, and the biased-clamped FSG layer exhibits intrinsically hydrophilic behavior, the biased-clamped FSG layer easily absorbs water when the biased-clamped FSG layer contacts is in contact with an aqueous base slurry during chemical mechanical polishing process. Thus, the reaction product produced during chemical mechanical polishing process can result in metal corrosion, oxide degradation. peeling at the metal/intermetal dielectric layer interface, and an increased dielectric constant. Furthermore, when a metal plug is formed, the HF can poison the metal plug. the contact resistance is increased and the increased contact resistance can affect the subsequent process.

SUMMARY OF THE INVENTION

[0008] According to above, the invention provides a method for forming an improved intermetal dielectric layer. In order to prevent the biased-clamped FSG layer from being exposed, the method provides an unbiased-unclamped FSG layer as a protect layer on the biased-clamped FSG layer.

[0009] The method comprises the following steps. A plurality of metal lines is formed on a substrate. A biased-clamped FSG layer is formed on the substrate by HDPCVD. An unbiased-unclamped FSG layer as a protection layer is formed on the biased-clamped FSG layer by HDPCVD. An oxide layer as a cap layer is formed on the protection layer. A planarization process is performed on the oxide layer.

[0010] The unbiased-unclamped FSG layer is used as a protection layer in the invention to prevent the biased-clamped FSG layer from being exposed during a planarization process and attacked by water.

[0011] It is to be understood that both the foregoing general description and the following detailed description are exemplary, and are intended to provide further explanation of the invention as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

[0012] FIG. 1A through FIG. 1C are schematic, cross-sectional views showing a process for forming an intermetal dielectric layer according to a first preferred embodiment of the invention;

[0013] FIG. 2 shows the relationship between the penetration depth (nm) in the unbiased-clamped FSG layer and hydrogen concentration using Secondary Ion Mass Spectroscopy (SIMS); and

[0014] FIG. 3 shows the relationship between the penetration depth (nm) in the unbiased-clamped FSG layer and fluorine concentration using Secondary Ion Mass Spectroscopy.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] FIGS. 1A through FIG. 1C are schematic, cross-sectional views showing a process for forming an intermetal dielectric layer according to a first preferred embodiment of the invention.

[0016] Referring to FIG. 1A, a substrate 100 is provided. A plurality of metal conductive lines 102a, 102b, and 102c is formed on the substrate 100. A tied conductive line region 104a and a loose conductive line region 104b consist of the plurality of metal conductive lines 102a, 102b, and 102c.

[0017] Referring to FIG. 1B, a dielectric layer 106 is formed on the substrate 100. Due to different spacings among the metal conductive lines 102a, 102b, and 102c, the height of the dielectric layer 106 is not uniform. The dielectric layer 106 comprises biased-clamped fluorinated silicon glass (FSG) formed by, for example, high density plasma chemical vapor deposition (HDPCVD). The dielectric constant of the biased-clamped FSG is about 3.5, which depends on the process variation. The FSG is widely used as an intermetal dielectric material because of its low dielectric constant, capability of decreasing capacitance between interconnects, and good gap-filling capability.

[0018] In addition, before forming the dielectric layer 106, an undoped silicon glass liner layer can be formed on the substrate 100 by, for example, HDPCVD. Since the undoped silicate glass liner layer has good compatibility with the FSG layer, the undoped silicate glass liner layer can promote adhesion between the FSG layer and another material layer and benefit the subsequent process.

[0019] Although the dielectric constant of the undoped silicon glass liner layer is about 4.1, it is very thin; thus, the undoped silicon glass liner layer does not affect the overall dielectric constant of the internetal dielectric layer.

[0020] A protection layer 108 is formed on the dielectric layer 106. The protection layer 108 comprises unbiased-unclamped FSG formed by, for example, HDPCVD. The dielectric constant of the unbiased-unclamped FSG is about 3.5, which thickness depends on the process. “Unbiased” means that no bias is applied during performing the HDPCVD, and “unclamped” means that there is no helium cooling device on the backside of the substrate 100 during the deposition, or that no helium cooling process is performed on the substrate 100 during the deposition.

[0021] Since the depositing rate of the unbiased-unclamped FSG layer (the protection layer 108) formed by HDPCVD is greater than that of the biased-clamped FSG layer (the dielectric layer 106) formed by HDPCVD, the throughout is not affected by the process of first forming the dielectric layer 106 to a thinner thickness than in the prior art and then forming the protection layer 108 to an adequate thickness.

[0022] Since the dielectric constant of the protection layer 108 is nearly the same as that of the dielectric layer 106, the protection layer 108 does not affect the overall dielectric constant of the intermetal dielectric layer.

[0023] A cap layer 110 is formed on the protection layer 108. The cap layer 110 is, for example, an oxide layer formed by HDPCVD or by PECVD. Referring to FIG. 1C, a planarization process such as chemical mechanical polishing (CMP) is performed on the cap layer 110.

[0024] Since the unbiased-unclamped FSG layer has a lower water absorption capability than the conventional FSG layer, if the unbiased-unclamped FSG layer is exposed due to the chemical mechanical polishing process, the unbiased-unclamped FSG layer does not react with an aqueous slurry or water to produce hydrogen fluoride (HF). Thus, the protection layer 108 can prevent the dielectric layer 106 from being over-etched as occurred in the prior art.

[0025] FIG. 2 shows the relationship between the penetration depth (nm) in the unbiased-unclamped FSG layer and hydrogen concentration using Secondary Ion Mass Spectroscopy (SIMS). FIG. 3 shows the relationship between the penetration depth (nm) in the unbiased-clamped FSG layer and fluorine concentration using secondary ion mass spectroscopy.

[0026] Referring to FIG. 2 and Table 1, there is no obvious change in the hydrogen concentrations before and after CMP. This indicates that the unbiased-unclamped FSG layer efficiently prevents the HF from being produced, and further prevents metal corrosion, oxide degradation, peeling at the metal/intermetal dielectric layer interface, and an increased dielectric constant. 1 TABLE 1 Fluorine concentration in Hydrogen concentration in percentage (%)* percentage (%)** Before the 13.17 0.140 CMP After the CMP 13.13 0.126 *obtained by Fourier Transfer Infra-Red **obtained by Secondary Ion Mass Spectroscopy

[0027] Referring to FIG. 3 and Table 1, there is no obvious variation in the fluorine concentrations before and after CMP. This indicates that the unbiased-unclamped FSG layer efficiently prevents the HF from being produced, and further prevents metal corrosion, oxide degradation, peeling at the metal/intermetal dielectric layer interface. and an increased dielectric constant.

[0028] In addition, the invention not only applies to the multilevel interconnect process, but also applies to, for example, the metal plug process, the dual damascene process, the dielectric layer depositing process between the conductive lines, etc.

[0029] Other embodiments of the invention will appear to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. It is intended that the specification and examples be considered as exemplary only, with a true scope and spirit of the invention being indicated by the following claims.

Claims

1. A method for forming an intermetal dielectric layer, comprising:

providing a substrate;

forming a plurality of metal conductive lines on the substrate, wherein a tied conductive line region and a loose conductive line region consist of the plurality of metal conductive lines,

forming an intermetal dielectric layer on the substrate;

forming a protection layer on the intermetal dielectric layer wherein the protection layer is thinner than the intermetal dielectric layer;

forming a cap layer on the protection layer; and

performing a planarization process.

2. The method for forming the intermetal dielectric layer according to

claim 1 wherein the intermetal dielectric layer comprises fluorinated silicon glass.

3. The method for forming the intermetal dielectric layer according to

claim 1. wherein the formation of the intermetal dielectric layer comprises biased-clamped high density plasma chemical vapor deposition.

4. The method for forming the intermetal dielectric layer according to

claim 3. wherein the biased-clamped high density plasma chemical vapor deposition is performed under a bias and helium cooling is employed.

5. The method for forming the intermetal dielectric layer according to

claim 1, wherein the protection layer comprises fluorinated silicon glass.

6. The method for forming the intermetal dielectric layer according to

claim 1, wherein the formation of the protection dielectric layer comprises unbiased-unclamped high density plasma chemical vapor deposition.

7. The method for forming the intermetal dielectric layer according to

claim 6, wherein the unbiased-unclamped high density plasma chemical vapor deposition is performed without a bias and without helium cooling.

8. The method for forming the intermetal dielectric layer according to

claim 1, wherein the protection layer is used as a stop layer.

9. The method for forming the intermetal dielectric layer according to

claim 1, wherein the cap layer comprises an oxide layer.

10. The method for forming the intermetal dielectric layer according to

claim 1, wherein the formation of the cap layer comprises plasma enhanced chemical vapor deposition.

11. The method for forming the intermetal dielectric layer according to

claim 1, wherein before forming the intermetal dielectric layer, the process further comprises forming a undoped silicon glass layer.

12. The method for forming the intermetal dielectric layer according to claim l wherein the planarization process comprises a chemical mechanical polishing process.

13. A method for forming an intermetal dielectric layer, comprising:

providing a substrate;

forming a plurality of metal conductive lines on the substrate;

forming a first dielectric layer on the substrate;

forming a second dielectric layer on the first dielectric layer;

forming a cap layer on the second dielectric layer; and

performing a planarization process.

14. The method for forming the intermetal dielectric layer according to

claim 13, wherein the formation of the intermetal dielectric layer comprises biased-clamped high density plasma chemical vapor deposition.

15. The method for forming the intermetal dielectric layer according to

claim 14, wherein the biased-clamped high density plasma chemical vapor deposition is performed under a bias and helium cooling is employed.

16. The method for forming the intermetal dielectric layer according to

claim 13 wherein the formation of the protection dielectric layer comprises unbiased-unclamped high density plasma chemical vapor deposition.

17. The method for forming the intermetal dielectric layer according to

claim 16, wherein the unbiased-unclamped high density plasma chemical vapor deposition is performed without a bias and without helium cooling.

18. The method for forming the intermetal dielectric layer according to

claim 13, wherein the cap layer comprises an oxide layer.

19. The method for forming the intermetal dielectric layer according to

claim 13 wherein the second dielectric layer is used as a stop layer.

20. The method for forming the intermetal dielectric layer according to

claim 13, wherein before forming the first dielectric layer, the process further comprises forming an undoped silicon glass layer.

21. A method for forming an intermetal dielectric layer, wherein the method applies to a substrate and a plurality of metal conductive lines is formed on the substrate, the method comprising:

forming a dielectric layer on the substrate;

forming a protection layer on the dielectric layer;

forming a cap layer on the protection layer; and

performing a planarization process.

22. The method for forming the intermetal dielectric layer according to

claim 21, wherein the formation of the intermetal dielectric layer comprises biased-clamped high density plasma chemical vapor deposition.

23. The method for forming the intermetal dielectric layer according to

claim 22, wherein the biased-clamped high density plasma chemical vapor deposition is performed under a bias and helium cooling is employed.

24. The method for forming the intermetal dielectric layer according to

claim 21, wherein the protection layer comprises fluorinated silicon glass.

25. The method for forming the intermetal dielectric layer according to

claim 21, wherein the formation of the protection dielectric layer comprises unbiased-unclamped high density plasma chemical vapor deposition.

26. The method for forming the intermetal dielectric layer according to

claim 25, wherein the unbiased-unclamped high density plasma chemical vapor deposition is performed without a bias and without helium cooling.

27. The method for forming the intermetal dielectric layer according to

claim 21, wherein the cap layer comprises an oxide layer.

28. The method for forming the intermetal dielectric layer according to

claim 21, wherein the second dielectric layer is used as a stop layer.