METHOD OF FABRICATING AN OPENING WITH DEEP ULTRA-VIOLET PHOTORESIST

Abstract

A method of fabricating an opening with a deep ultra-violet photoresist layer. An insulating layer is formed on a substrate having a device structure. A deep ultraviolet photoresist layer with a first opening is formed on the insulating layer and a hard mask layer is then formed on the surface and the sidewalls of the deep ultra-violet photoresist layer. The first opening is used to pattern the insulating layer to form a second opening within the insulating layer wherein the hard mask layer is to protect the deep ultra-violet photoresist layer. The deep ultra-violet photoresist layer and the hard mask layer are removed to expose the insulating layer and a desired opening is thus accomplished.

Description

CROSS-REFERENCE TO RELATED APPLICATION

[0001] This application claims priority benefit of Taiwan application Ser. No. 87106062, filed Apr. 21, 1998, the full disclosure of which is incorporated herein by reference.

BACKGROUND OF THE INVENTION

[0002] 1. Field of the Invention

[0003] The invention relates to a method of fabricating an opening, and more particularly to a method of fabricating an opening formed by deep ultra-violet photoresist (DUV PR).

[0004] 2. Description of the Related Art

[0005] Deep ultra-violet photoresist is necessary for the semiconductor process with the size of 0.25 &mgr;m or less. It can be employed in, for example, oxide layer etching. The DUV PR is exposed under a deep ultra-violet light and developed to define the oxide layer. An opening for a contact, via or damascene is then formed by developing the DUV PR. DUV PR is used to reduce the width of the opening but the material of the DUV PR is soft and not high temperature compatible. Thus erosion and reflow of the DUV PR easily occurs while etching the oxide layer which requires high ion energy. Thus, the side profile of the DUV PR isn't entirely vertical and it is difficult to precisely control the width of the opening. A commonly employed method of preventing overetching of the DUV PR is to increase the thickness of the DUV PR. However, the increment of the thickness prevents the photoresist from being properly exposed and successfully developed, because of focus of depth. Therefore increasing the thickness of the DUV PR as described above doesn't solve the problem.

SUMMARY OF THE INVENTION

[0006] It is therefore an object of the invention to overcome the problem of erosion and reflow of the DUV PR. The width of the opening can be reduced as much as possible to follow the trend towards smaller size . The quality of the opening width can also be controlled in a stable fashion.

[0007] To achieve these objects and advantages, and in accordance with the purpose of the invention, as embodied and broadly described herein, the invention is directed towards a method of fabricating an opening with deep ultra-violet photoresist. An insulating layer is formed over a substrate where devices are formed thereon. A DUV PR layer with a first opening is then formed on the insulating layer. A hard mask layer is formed on the DUV PR layer and a second opening is next formed within the insulating layer by using the first opening to define the insulating layer. The hard mask is used to protect the DUV PR layer. The DUV PR layer and the hard mask are removed to expose the insulating layer and a desired second opening is thus formed.

[0008] It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention, as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

[0009] FIGS. 1A-1D is a cross sectional view of the formation of an opening in a preferred embodiment according to the invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0010] This invention is about a method of fabricating an opening within the insulating layer In the semiconductor process, the opening for the contact, via or damascene can be formed by this invention. The example below is made in reference to an opening for a via.

[0011] In FIG. 1A, a substrate 100 has device structures (not shown) and a conductive layer 102 formed on it. The conductive layer 102 is, for example, a metal layer or polysilicon with dopant. An insulating layer 106 (or dielectric layer), such as a silicon oxide layer, is formed over the substrate 100. A DUV PR layer 106 with an opening 108 is then formed on the insulating layer, with the opening 108 located over a via opening formed within the insulating layer 104 in the subsequent process. With the short wave length of deep ultra-violet light, the resolution of the light source improves and the width of the opening 108 can be narrower to follow the needs of design rule.

[0012] Next, in FIG. 2B, a hard mask layer 110 is formed on the surface of the DUV PR 106. The hard mask layer 110 includes a silicon layer, which is formed by silylation. If a plasma treatment is performed after silylation, the silicon layer can become an oxide layer or a nitride layer as oxygen or nitrogen is pumped into the plasma chamber. The opening 108 within the DUV PR 110 is used to define the insulating layer 104, and an opening 112 is then formed within the insulating layer 104, exposing the surface of the conductive layer 102 as shown in FIG. 2C. The opening 112 can be formed by dry etching.

[0013] The material character of the DUV PR 106 is soft, and as previously mentioned, suffers erosion and reflow by etchant as the opening 112 is formed within the insulating layer 104. This makes it impossible to achieve a thoroughly vertical opening 112. The hard mask layer 110 is deliberately formed with hard material on the surface of the DUV PR 106 to protect DUV PR 106. In addition, the hard mask layer 110 is formed on the DUV PR 106 and the width of the opening 108 in FIG. 1B can be reduced. Therefore the width of the opening 112 in FIG. IC is also narrower as the insulating layer 104 is defined by the opening 108. For example, the hard mask layer 110 swells after its formation and the width of the opening 108, designed to be about 0.25 &mgr;m wide, can be reduce to 0.15 &mgr;m because of swelling of the hard mask layer 110. This particular characteristics can improve the pattern resolution beyond the limitation of lithography. During the etching process of the opening 112, the hard mask layer 110 and the insulating layer 104 are etched at the same time. Since the material character of the hard mask layer 110 is stronger, the etching rate is slower and the DUV PR layer 106 can be protected from overetching. After the etching process, a portion of hard mask layer 110a a is still left on the profile of the of the hard mask layer's 110 sidewalls because the etching rate of the hard mask layer 110 is slower than the DUV PR layer 106. The existence of the residual hard mask layer 110 can keep the profile of the sidewalls straight and the width of the opening 112 can be better controlled.

[0014] Referring to FIG. 1D, the DUV PR layer 106 and the residual hard mask layer 110a are next removed to expose the surface of the insulating layer 106 and an opening 112 with the desired width is formed. After that, a conductive layer can be deposited into the opening 112 and the subsequent process can be continued.

[0015] The opening 112 is used as a via hole, and the conductive layer is exposed after the formation of the opening 112. If the opening is formed for a contact hole, after forming the opening, the doped region is exactly exposed. Furthermore, the opening is for damascene and it usually exposes the conductive layer. Therefore this invention is applied in the formation of via holes, contact holes or even the openings for damascene.

[0016] A DUV PR layer and a silylation process are applied; as a result, a hard mask layer can be formed on the DUV PR layer after exposing the DUV PR and the hard mask layer is used to protect the DUV PR from overetching. Because the DUV PR layer and the hard mask layer have different levels of etching selectivity to overcome the problem of overetching the DUV PR , the width of the contact or via can be reduced without suffering the limitation of photolithography.

[0017] Other embodiments of the invention will appear to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. It is intended that the specification and examples be considered exemplary only, with the true scope and spirit of the invention being indicated by the following claims.

Claims

1. A method of fabricating an opening wherein a substrate having a device structure is provided, comprising:

forming an insulating layer over the substrate;

forming a deep ultra-violet photoresist layer with a first opening on the insulating layer wherein the deep ultra-violet photoresist layer has a surface and sidewalls;

forming a hard mask layer on the surface and sidewalls of the deep ultra-violet photoresist layer;

forming a second opening by defining the insulating layer using the first opening of the deep ultra-violet photoresist layer; and

removing the deep ultra-violet photoresist layer and the hard mask layer to expose the insulating layer

2. The method according to

claim 1, wherein the said step of defining the insulating layer using the first opening of the deep ultra-violet photoresist layer includes defining the insulating layer by dry etching.

3. The method according to

claim 1, wherein as the said step of defining the insulating layer is performed, a portion of the hard mask layer is removed from the surface of the deep ultra-violet photoresist and a portion of the hard mask layer is left on the sidewalls of the deep ultra-violet photoresist layer.

4. The method according to

claim 1, wherein the hard mask layer includes a silicon layer.

5. The method according to

claim 4, wherein the silicon layer is formed by silylation.

6. The method according to

claim 1, wherein the hard mask layer includes a silicon oxide layer.

7. The method according to

claim 6, wherein the silicon oxide layer is formed after silylation and a plasma treatment is performed in the presence of oxygen.

8. The method according to

claim 1, wherein the hard mask layer includes a nitride layer.

9. The method according to

claim 8, wherein the nitride layer is formed after silylation and a plasma treatment is performed in the presence of nitrogen.

10. The method according to

claim 1, wherein the insulating layer includes an oxide layer

11. The method according to

claim 1, wherein the width of the first opening can be controlled by the deep ultra-violet photoresist layer which can reduce the size of the first opening.

12. A method of fabricating an opening wherein a substrate having a device structure and a metal layer formed thereon is provided, comprising:

forming a dielectric layer over the substrate;

forming a deep ultra-violet photoresist layer with a first opening on the dielectric layer wherein the deep ultra-violet photoresist layer has a surface and sidewalls;

forming a hard mask layer on the surface and the sidewalls of the deep ultra-violet photoresist layer;

forming a via hole by defining the dielectric layer using the first opening of the deep ultra-violet photoresist layer to expose the metal layer; and

removing the deep ultra-violet photoresist layer the hard mask layer to expose the dielectric layer,

wherein as the said step of defining the dielectric layer is performed, a portion of the hard mask layer is removed from the surface of the deep ultra-violet photoresist and a portion of the hard mask layer is left on the sidewalls of the deep ultra-violet photoresist layer.

13. The method according to

claim 11, wherein the hard mask layer includes a silicon layer formed by silylation

14. The method according to

claim 11, wherein the hard mask layer includes a silicon oxide layer, which is formed after silylation, and a plasma treatment is performed with surrounding of oxygen.

15. The method according to

claim 11, wherein the hard mask layer includes a nitride layer, which is formed after silylation, and a plasma treatment is performed with surrounding of nitrogen.

16. A method of fabricating an opening wherein a substrate having a device structure and a doped region formed thereon is provided, comprising:

forming an insulating layer over the substrate;

forming a deep ultra-violet photoresist layer with a first opening on the insulating layer wherein the deep ultra-violet photoresist layer has a surface and sidewalls;

forming a hard mask layer on the surface and the sidewalls of the deep ultra-violet photoresist layer;

forming a contact hole by defining the insulating layer using the first opening of the deep ultra-violet photoresist layer to expose the doped region; and

removing the deep ultra-violet photoresist layer the hard mask layer to expose the insulating layer,

wherein as the said step of defining the insulating layer is performed, a portion of the hard mask layer is removed from the surface of the deep ultra-violet photoresist and a portion of the hard mask layer is left on the sidewalls of the deep ultra-violet photoresist layer.

17. The method according to

claim 15, wherein the hard mask layer includes a silicon layer formed by silylation.

18. The method according to

claim 15, wherein the hard mask layer includes a silicon oxide layer, which is formed after silylation, and a plasma treatment is performed in the presence of oxygen

19. The method according to

claim 15, wherein the hard mask layer includes a nitride layer, which is formed after silylation, and a plasma treatment is performed in the presence of nitrogen.