Methods for making substrates and substrates formed therefrom

A method for making substrates for use in optics, electronics, or opto-electronics. The method may include transferring a seed layer onto a receiving support and depositing a useful layer onto the seed layer. The thermal expansion coefficient of the receiving support may be identical to or slightly larger than the thermal expansion coefficient of the useful layer and the thermal expansion coefficient of the seed layer may be substantially equal to the thermal expansion coefficient of the receiving support.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description
FIELD OF THE INVENTION

The present invention relates to methods for making substrates and substrates for use in optics, electronics or opto-electronics and, in particular, substrates which may be used for making solar cells, light-emitting diodes and lasers.

BACKGROUND OF THE INVENTION

In the field of substrates for optics, electronics or opto-electronics, two main types of methods are well known for forming a thin layer on a supporting substrate. According to a first type of method, a thin layer taken from a donor substrate is transferred onto a receiving supporting substrate to obtain substrates including a thin useful layer. Useful layer is the layer of the substrate on which electronic components such as, for example, light-emitting diodes or other components may be made.

According to second type of method, the thin layer is deposited on a receiving supporting substrate by a deposition technique. This deposition technique may notably consist of epitaxy or chemical vapor deposition. Regardless of the type of method used for forming a useful layer on a receiving supporting substrate, in some instances it is necessary to remove at least one portion of the receiving support to obtain a final substrate including at least the useful layer. Such removal of the receiving support results in loss of materials, thereby putting a strain on the manufacturing costs of such substrates.

In order to find a remedy to this drawback, a method for making substrates has been devised which includes a useful thin layer method in which the receiving supporting substrate is removed in order to be recycled. Such a method is described in an alternative embodiment of U.S. Pat. No. 6,794,276, which describes a method for making substrates. This method includes a step for transferring a seed layer on a receiving support by molecular adhesion at a bonding interface, a step for epitaxy of a useful layer on the seed layer and a step for applying stresses in order to lead to removal of the assembly (i.e., removal of the seed layer and of the useful layer from the receiving support at the bonding interface). Seed layer is the material layer which allows development of the epitaxied useful layer.

In U.S. Pat. No. 6,794,276, certain specifications are required for allowing the seed layer to adapt to thermal expansions of the receiving support and the useful layer during heat treatments to which the substrate is subject. For this purpose, it is recommended that the seed layer has sufficiently small thickness, of the order of 0.5 microns, and preferably less than 1,000 Å. U.S. Pat. No. 6,794,276 also mentions the fact that the receiving support consists of a material for which the thermal expansion coefficient is 0.7 to 3 times larger than that of the useful layer. It is specified that the thermal expansion coefficient is the proportionality coefficient of the change in the length of a solid as a function of the initial length of the solid and of its change in temperature according to the following formula:


ΔL=αL0ΔT where α=thermal expansion coefficient

In an alternative embodiment, the method taught by U.S. Pat. No. 6,794,276 allows the receiving supporting substrate to be reused after its removal.

It is desirable to improve the method taught by U.S. Pat. No. 6,794,276. In particular, improvements are needed for reducing the risk of breaking the substrate, deteriorating, cracking the seed layer or the occurrence of a residual deflection of the final substrate making it unusable during the various heat treatments applied to the substrate. These improvements are now provided by the present invention.

SUMMARY OF THE INVENTION

The invention relates to a method for making substrates for optics, electronics, or opto-electronics which includes providing a donor substrate and a receiving substrate, wherein the receiving substrate has a thermal expansion coefficient; operably connecting the donor substrate to the receiving substrate; forming a seed layer on the receiving substrate, wherein the seed layer has a surface and a thermal expansion coefficient; and epitaxy of a useful layer on the seed layer, wherein the useful layer has a thermal expansion coefficient. Advantageously, the thermal expansion coefficient of the receiving substrate is equal to or greater than the thermal expansion coefficient of the useful layer, and the thermal expansion coefficient of the seed layer is about the same as the thermal expansion coefficient of the receiving substrate so that the seed layer and the receiving support expand in substantially the same way to avoid stressing or deforming the seed layer.

In another embodiment, the method for making substrates includes providing a donor substrate and a receiving support; forming a seed layer from the donor substrate; transferring the seed layer onto the receiving support; and forming a useful layer on the seed layer. Again, the thermal expansion coefficient of the receiving support is equal to or greater than the thermal expansion coefficient of the useful layer, and the thermal expansion coefficient of the seed layer is about equal to the thermal expansion coefficient of the receiving support so that the seed layer and the receiving support expand in substantially the same way to avoid stressing or deforming the seed layer.

Thus, during subsequent heat treatments which the structure will undergo, the seed layer and the receiving support may substantially expand in the same way. The receiving support may expand slightly less than the seed layer so that the seed layer may be placed under slight compression avoiding any deterioration of the seed layer.

In a preferred embodiment, the seed layer may consist of a material for which the thermal expansion coefficient is equal to (1+ε) times that of the receiving support, with ε of the order of 0.2, and preferably ε equals 0.1. Further, the useful layer may consist of a material for which the thermal expansion coefficient may be larger than or equal to (1±ε′) times that of the receiving support, with a typical value of 0.2 for ε′. The seed layer and/or the receiving support may be made of, for example, silicon, germanium, silicon carbide, GaN or sapphire. Moreover, the chemical composition of the seed layer, advantageously, may be identical to that of the receiving support.

A composite substrate may be created using the method described herein. The composite substrate may be used for optics, electronics, or opto-electronics, The substrate may have at least one seed layer on a receiving support, and an epitaxied useful layer on the seed layer. The thermal expansion coefficient of the receiving support may be identical to or slightly larger than the thermal expansion coefficient of the useful layer, and the thermal expansion coefficient of the seed layer may be substantially equal to the thermal expansion coefficient of the receiving support so that the seed layer and the receiving support-expand in substantially the same way to avoid stressing or deforming the seed layer.

Other advantages and features will become better apparent from the description which follows of several alternative embodiments, given as non-limiting examples, of the method for making substrates according to the invention as well as of the substrate obtained by the method.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention can be better understood by reference to the following drawings, wherein like references numerals represent like elements. The drawings are merely exemplary to illustrate certain features that may be used singularly or in combination with other features and the present invention should not be limited to the embodiments shown.

FIG. 1 is a schematic illustration of the steps of an exemplary embodiment of a method for making a substrate; and

FIG. 2 is a schematic illustration of the steps of an alternative exemplary embodiment of a method for making a substrate.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

With reference to FIG. 1, the method according to the invention includes a step for implanting atomic species at a determined depth in a donor substrate 1 in order to form a weakened area 2. In step 100, the donor substrate may be boned upon or otherwise adhered onto a receiving substrate 3 by any appropriate means known in the art.

As referred to below, bonding may mean intimate contact of the donor substrate 1 with the receiving substrate 3 in order to join the donor substrate 1 and the receiving substrate 3 by molecular adhesion. Bonding may be obtained according to various methods such as, for example, (1) having a surface of the donor substrate 1 come into direct contact with a surface of the receiving substrate; (2) forming a bonding layer in order to make a connecting layer on the surface of the donor substrate 1, forming a bonding layer in order to make a second connecting layer on the surface of the receiving supporting substrate 3 and having the surfaces of the respective connecting layers of the donor substrate 1 and the donor substrate 3 come into contact with each other; and (3) forming a bonding layer on only one of both substrates.

In one embodiment, the bonding layer may consist of, for example, an insulating layer or a dielectric layer. In such an embodiment, the donor substrate 1 may be bonded onto the receiving substrate 3 by means of a bonding layer 4 deposited on the surface of the donor substrate and/or the receiving substrate 3. In addition, an annealing step may be applied at this stage for strengthening the bonding interface between the bonding layer 4 and the surface of the donor substrate 1 and/or the receiving substrate 3. Nonetheless, bonding may be achieved according to any of the methods known to one skilled in the art.

In step 200, a seed layer 5 may be detached from the donor substrate 1 at the weakened area 2. Thereafter, in step 300 a useful layer 6 may be deposited on the surface of the seed layer 5. In one preferred embodiment, the useful layer 6 may be obtained by epitaxy, which is well known to one skilled in the art, according to step 300. The step 200 for implanting atomic species and for detaching the seed layer 5 corresponds to a SMART-CUT® method, a general description of which is found in the publication Silicon-On-Insulator Technology: Materials to VLSI, 2nd Edition of Jean-Pierre Colinge, Kluwer Academic Publishers, p. 50 and 51. Those skilled in the art will appreciate that detachment of the seed layer 5 and of the donor substrate 1 may be achieved by an operation such as, for example, heat treatment, application of mechanical stresses, chemical etching, or a combination of at least two of these operations.

The seed layer 5 may consist of a material for which the thermal expansion coefficient is equal to (1+ε) times that of the receiving support 3, with ε of the order of 0.2, and preferably ε equals 0.1. It will however be observed that thermal expansion may vary with temperature, with the deposition technique, with the defects present inside the layers and also with the measurement techniques. Thus, when the structure is undergoing heat treatments (e.g., during detachment of the seed layer 5 and the useful layer 6 of the receiving substrate 3) the seed layer 5 and the receiving support 3 will substantially expand in the same way. The receiving support 3 will expand slightly less than the seed layer 5 so that the latter may be placed under slight compression, thereby avoiding deterioration of the seed layer 5.

The useful layer 6 may consist of a material which has a thermal expansion coefficient which is larger than or equal to (1±ε′) times that of the receiving support 3, with the value of ε′ between 0 and 0.8 and, preferably, between 0.2 and 0.3. Expansions of the different layers 5, 6 and the receiving support 3 of the same order of magnitude during heat treatments may be obtained because of the closeness of the thermal expansion coefficients of the useful layer 6, the seed layer 5 and the receiving support 3. In this way, any risk of deterioration of the substrate or occurrence of a residual deflection of the final substrate may be avoided.

The seed layer 5 and/or the receiving support 3 may comprise a material such as, for example, silicon (e.g., {111} silicon), germanium, polycrystalline or monocrystalline silicon carbide, GaN, polycrystalline or monocrystalline AlN, and sapphire. Further, the chemical composition of the seed layer 5 may be identical with that of the receiving support 3.

Between the steps for detaching 200 and for depositing 300 the useful layer, the method may also include steps for preparing the surface of the seed layer 5. These preparation steps may include, for example, polishing, annealing, smooth annealing operations (e.g., under hydrogen), annealing operations for strengthening the bond, sacrificial oxidization interface operations (i.e., for oxidizing and then removing the oxidized material), etching operations, etc.

Step 400 may lead to detachment at the bonding layer 4 of the assembly, consisting of the seed layer 5 and the useful layer 6, from the receiving support 3. If a self-supported substrate is desired, the assembly formed by the seed layer 5 and the useful layer 6 may only be able to be detached from the receiving support 3 if the thickness of the assembly is greater than or equal to 50 μm.

In order to perform the detachment, different techniques may be used. For example, detachment may be accomplished by application of mechanical, thermal, electrostatic stresses; application of any type of etching (wet, dry, gas, etching, plasma etching, etc.) and/or application of any type of etching by irradiation such as laser irradiation (e.g., by chemical etchings at the bonding layer 4), or the like. The receiving substrate 3, which may either be destroyed or recycled in order to reuse it during the making of a new substrate, may then be obtained on the one hand, and a structure consisting of the seed layer 5 and the useful layer 6 may be obtained on the other hand. It will be appreciated that for performing the detachment of the assembly (consisting of the seed layer 5 and the useful layer 6) from the receiving support 3 at the bonding layer 4, chemical etching may advantageously be used if the receiving substrate 3 is intended to be destroyed. On the other hand, if the receiving substrate 3 is intended to be recycled for reuse, mechanical stress or chemical etching of the bonding layer 4 may preferably be used, which provides full detachment of substrate 3. The seed layer may then be removed by any appropriate means known to those skilled in the art.

Thereafter, the useful layer 6 may be transferred onto a final supporting substrate 7. The final support 7 may be made of a material such as, for example, semi-conducting or semi-conductive materials (e.g., silicon, germanium, etc.), metals (e.g., copper), plastic materials and glasses. Since the resultant structure no longer undergoes any heat treatment, the final supporting substrate 7 may be made with any material which has a thermal expansion coefficient and/or a lattice parameter different from those of the useful layer 6.

In a preferred embodiment, the useful layer 6 may be transferred onto the final supporting substrate 7 by bonding. The bond may be obtained by applying a bonding layer 8 on one of the surfaces of the useful layer 6 and/or the final supporting substrate 7. Similar to selecting the final substrate 7, the bonding techniques applied in this step are not limited by temperature resistance, contaminations, the thermal expansion coefficient and/or the lattice parameter of the useful layer 6.

The layer 8 used may comprise, for example, organic layers (e.g., insulating layers of the SiO2, Si3N4, or polyimides), conductive metal interfaces and seals (e.g., palladium silicide Pd2Si, tungsten silicide WSi2, SiAu, or PdIn). The conductive interfaces may then provide the contact on the rear face of the layer.

Moreover, structures may be buried in this bonding layer 8 so that a rear junction contact of a triple junction may thereby be made for producing solar cells. In one embodiment, the buried structure may consist of a triple junction based on amorphous silicon of the n-i-p type. This buried structure may have a lower layer (i.e., a rear contact layer) consisting of metallization, such as silver (Ag) or aluminium (Al), on which a conducting transparent oxide may be deposited. The rear contact layer, on the one hand, may provide an electrical contact with which the triple junction solar cell may be connected and a rear mirror, on the other hand, allowing reflection of light which has not been absorbed by the solar cell. The latter may consist of three amorphous silicon layers (of type n, i and p, respectively) successively deposited on the rear contact layer. It will be appreciated by those skilled in that art that when making LEDs, mirrors may also be buried in the bonding layer 8.

In an alternative embodiment (not illustrated in FIG. 1), the useful layer 6 and the seed layer 5 may be transferred onto the final supporting substrate 7 with or without the bonding layer 8 prior to removing the seed layer 5.

Referring now to FIG. 2, atomic species may be implanted in the same way as previously discussed—at a determined depth of a donor substrate 1—in order to form a weakened area 2. The donor substrate 1 in step 100 may then be adhered on a receiving substrate 3 by any appropriate means. In step 200, a seed layer 5 may be detached from the donor substrate 1 at the weakened area 2. Thereafter, in step 300, a useful layer 6 may be deposited on the surface of the seed layer 5. Detachment of the seed layer 5 and the donor substrate 1 may be achieved by an operation such as, for example, heat treatment, application of mechanical stresses and chemical etching, or a combination of at least two of these operations.

In another alternative embodiment, the seed layer 5 may originate from the thinning of the donor substrate (for example according to a BESOI type method) before depositing the useful layer 6. The final supporting substrate 7 may then be transferred onto the useful layer 6 by means of a bonding layer 8. Stresses may be applied in order detach the structure, which may consist of the seed layer 5, the useful layer 6, the bonding layer 8 and the final supporting substrate 7, from the receiving support 3 at the bonding layer 4. A receiving substrate 3, ready to be recycled, may be obtained on the one hand and a structure consisting of the seed layer 5, the useful layer 6, the bonding layer 8 and the final supporting substrate 7 may be obtained on the other hand. The seed layer 5 may then be removed by any appropriate means in order to obtain the final substrate.

EXAMPLES

Two particular but non-limiting exemplary embodiments of a resultant substrate will be described hereafter with reference to FIG. 2. The substrates are intended for making solar cells (Example 1) and light-emitting diodes (Example 2). It should be noted, however, that the examples are not intended to be limiting as to the fields of application of the invention.

Example 1

According to this example, a weakened area 2 may be made by implanting atomic species at a determined depth in the donor substrate 1 which may be made of, for example, germanium (Ge). The receiving substrate 3, which may also be made of Ge, may be bonded to the donor substrate 1 by means of a bonding layer 4. The bonding layer 4, preferably made of nitride or oxide, may be formed on the face of at least one of the donor 1 or receiving 3 substrates.

As shown in step 200, a seed layer 5 of Ge may be detached from the donor substrate 1 at the weakened area 2 using the SMART-CUT® method as described herein. The seed layer 5 of Ge may have a thermal expansion coefficient (which is also noted as CTE) which varies from 4.6 to 6.67 10−6 for temperatures ranging from 25° C. to 600° C. Detachment of the seed layer 5 and the donor substrate 1 may be achieved by an operation such as, for example, heat treatment, application of mechanical stresses and chemical etching, or a combination of at least two of these operations.

As illustrated in step 300, a useful gallium arsenide layer 6 may then be deposited on the surface of the seed layer 5. The CTE of AsGa may be from 5.00 to 7.4 10−6 for temperatures ranging from 25° C. to 600° C. Different layers, such as, for example, InP, AsGa, GaInP, InGaAs, InGaAlP, or InGaAsN epitaxied layers, may be successively deposited by epitaxy on the deposit of the AsGa layer in order to form an epitaxial stack for making junctions (e.g., triple junctions, quadruple junctions, etc.). It will be appreciated that the useful layer 6 may have a crystalline quality at least equal to the crystalline quality which may be obtained by epitaxy on a massive Ge substrate.

The useful layer 6 and the seed layer 5 may then be transferred onto a final supporting substrate 7. It will be noted that the final support 7 may also be contacted with the epitaxial stack if the latter is made beforehand. The final support 7 may be made of a material such as, for example, semi-conductors (e.g., silicon, germanium), plastic materials and glasses. Transfer of the useful layer 6 and the seed layer 5 onto the final supporting substrate 7 may be performed by bonding. The bond may be performed using a bonding layer 8 made of, for example, insulating layers (e.g., SiO2, Si3N4, etc.), organic layers (e.g., polyimides), metal layers (e.g., palladium silicide Pd2Si and tungsten silicide WSi2), and seals (e.g., SiAu, PdIn, etc.)

The final supporting substrate 7, the seed layer 5 and the useful layer 6 may then be detached by any appropriate means, for example, at the bonding layer 4 from the receiving support 3. The receiving support 3 may thereafter be recycled advantageously. This detachment may be obtained by applying stresses at the bonding interface such as, for example, mechanical stresses, thermal stresses, electrostatic stresses and stresses from laser irradiation. Thereafter, the seed layer may be removed in order to obtain the final substrate

While the foregoing description and drawings represent the preferred embodiments of the present invention, it will be understood that various additions, modifications and substitutions may be made therein without departing from the spirit and scope of the present invention as defined in the accompanying claims. In particular, it will be clear to those skilled in the art that the present invention may be embodied in other specific forms, structures, arrangements, proportions, and with other elements, materials, and components, without departing from the spirit or essential characteristics thereof. One skilled in the art will appreciate that the invention may be used with many modifications of structure, arrangement, proportions, materials, and components and otherwise, used in the practice of the invention, which are particularly adapted to specific environments and operative requirements without departing from the principles of the present invention. The presently disclosed embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims, and not limited to the foregoing description.

Claims

1. A method for making substrates comprising:

providing a donor substrate and a receiving substrate, wherein the receiving substrate has a thermal expansion coefficient;
operably connecting the donor substrate to the receiving substrate;
forming a seed layer on the receiving substrate, wherein the seed layer has a surface and a thermal expansion coefficient; and
epitaxy of a useful layer on the seed layer, wherein the useful layer has a thermal expansion coefficient;
wherein the thermal expansion coefficient of the receiving substrate is equal to or greater than the thermal expansion coefficient of the useful layer, and
wherein the thermal expansion coefficient of the seed layer is about the same as the thermal expansion coefficient of the receiving substrate so that the seed layer and the receiving support expand in substantially the same way to avoid stressing or deforming the seed layer.

2. The method of claim 1 wherein the seed layer forms a surface portion of the donor substrate, the method further comprising forming a weakened area in the donor substrate beneath the seed layer and detaching the donor substrate from the seed layer at the weakened area so that the seed layer remains operably connected to the receiving substrate.

3. The method of claim 2, wherein the step of forming a weakened area comprises implanting atomic species into the donor substrate.

4. The method of claim 1, wherein the step of operably connecting the donor substrate to the receiving substrate includes forming a bonding layer between the seed layer and the receiving substrate.

5. The method of claim 4 further comprising preparing the surface of the seed layer, wherein the preparation step is selected from at least one of the group consisting of polishing, annealing, sacrificial oxidation interface operations and etching.

6. The method of claim 4 further comprising providing a supporting substrate of a material selected from the group consisting of a semi-conductor, metal, plastic and glass, and operably connecting the useful layer to the supporting substrate.

7. The method of claim 6 further comprising detaching the seed layer, the useful layer and the supporting substrate from the receiving substrate and subsequently removing the seed layer from the useful layer and the supporting substrate.

8. The method of claim 7 wherein the step of detaching comprises performing at least one of the operations selected from the groups consisting of heat treatment, application of stresses, irradiation and etching.

9. The method of claim 6, wherein the step of operably connecting the useful layer to the supporting substrate comprises forming a bonding layer between the useful layer and the supporting substrate, wherein the bonding layer is selected from the group consisting of insulating layers, organic layers, metal interfaces and seals.

10. The method of claim 10 further comprising burying a structure in the second bonding layer.

11. The method of claim 1 further comprising forming the seed layer from a material for which the thermal expansion coefficient is (1+ε) times the thermal expansion coefficient of the receiving substrate, and forming the useful layer from a material for which the thermal expansion coefficient is greater than or equal to (1±ε′) times the thermal expansion coefficient of the receiving substrate.

12. The method of claim 1 which further comprises forming at least one of the seed layer and the receiving substrate from a material selected from the group consisting of silicon, germanium, silicon carbide, GaN, AlN and sapphire, and optionally where the chemical composition of the seed layer and that of the receiving substrate are identical.

13. The method of claim 1 further comprising detaching the seed layer and the useful layer from the receiving substrate by performing at least one of the operations selected from the group consisting of heat treatment, application of mechanical, thermal or electrostatic stresses, irradiation and etching.

14. The method of claim 22 further comprising performing an operation selected from the group consisting of dry, wet, gas, chemical and plasma etching or irradiation using a laser.

15. The method of claim 1 further comprising removing the seed layer from the useful layer.

16. The method of claim 1 further comprising reusing the receiving substrate to make another substrate.

17. The method of claim 1, wherein the step of forming the seed layer comprises thinning the donor substrate after bringing the donor substrate into contact with the receiving substrate.

18. A method for making substrates comprising:

providing a donor substrate and a receiving support;
forming a seed layer from the donor substrate;
transferring the seed layer onto the receiving support;
forming a useful layer on the seed layer;
wherein the thermal expansion coefficient of the receiving support is equal to or greater than the thermal expansion coefficient of the useful layer, and
wherein the thermal expansion coefficient of the seed layer is about equal to the thermal expansion coefficient of the receiving support.

19. The method of claim 18 wherein forming the seed layer comprises inserting atomic species into the donor substrate and forming a weakened area beneath the seed layer.

20. The method of claim 18 wherein forming a useful layer comprises epitaxy of the useful layer on the seed layer.

21. The method of claim 18 wherein transferring the seed layer to the receiving support comprises bonding the donor substrate to the receiving support and detaching the seed layer and the useful layer from the receiving support.

22. The method of claim 21 further comprising removing the seed layer from the useful layer and transferring the useful layer onto a supporting substrate.

23. A substrate comprising:

a receiving support having a thermal expansion coefficient;
a seed layer having a thermal expansion coefficient, wherein the seed layer is operably connected to the receiving support; and
a useful layer having a thermal expansion coefficient, the useful layer being operably connected to the seed layer;
wherein the thermal expansion coefficient of the receiving support is greater than or equal to the thermal expansion coefficient of the useful layer, and
wherein the thermal expansion coefficient of the seed layer is about equal to the thermal expansion coefficient of the receiving support so that the seed layer and the receiving support expand in substantially the same way to avoid stressing or deforming the seed layer.

24. The substrate of claim 23, wherein the seed layer is made of a material for which the thermal expansion coefficient is equal to (1+ε) times the thermal expansion coefficient of the receiving support.

25. The substrate of claim 23 wherein the useful layer is made of a material for which the thermal expansion coefficient is greater than or equal to (1±ε′) times the thermal expansion coefficient of the receiving support.

26. The substrate of claim 23, wherein the at least one of the seed layer and the receiving support is made of a material selected from the group consisting of silicon, germanium, silicon carbide, GaN, AlN and sapphire and optionally where the chemical composition of the seed layer and that of the receiving substrate are identical.

27. The substrate of claim 23 further comprising a supporting substrate comprising a material selected from the group consisting of semiconductors, plastic, glass and metal, and optionally including a bonding layer connecting the supporting substrate and the useful layer.

28. The substrate of claim 27 further comprising a structure buried in the bonding layer.

29. The substrate of claim 23 further comprising a bonding layer connecting the seed layer and the receiving support, wherein the bonding layer is comprised of a material selected from the group consisting of insulating layers, organic layers, metal interfaces and sealing layers.

30. The substrate of claim 23, wherein the seed layer and the useful layer has a thickness of at least 50 μm.

Patent History
Publication number: 20070141803
Type: Application
Filed: Aug 16, 2006
Publication Date: Jun 21, 2007
Inventors: Alice Boussagol (Brignoud), Bruce Faure (Grenoble), Bruno Ghyselen (Seyssinet)
Application Number: 11/505,668
Classifications
Current U.S. Class: Bonding Of Plural Semiconductor Substrates (438/455)
International Classification: H01L 21/30 (20060101); H01L 21/46 (20060101);