SOLDER ALLOY
An alloy suitable for use in a ball grid array or chip scale package, the alloy comprising from 0.05-1.5 wt. % copper; from 2.5-5 wt. % silver; one or both of from 0.005-0.3 wt % nickel and/or from 0.003-0.3 wt % chromium; from 0-0.1 wt. % phosphorus; from 0-0.1 wt. % germanium; from 0-0.1 wt. % gallium; from 0-0.3 wt. % of one or more rare earth elements; from 0-0.3 wt. % indium; from 0-0.3 wt. % magnesium; from 0-0.3 wt. % calcium; from 0-0.3 wt. % silicon; from 0-0.3 wt. % aluminium; from 0-0.3 wt. % zinc; from 0-2 wt. % bismuth; from 0-1 wt. % antimony; from 0-0.2 wt % manganese; from 0-0.3 wt % cobalt; from 0-0.3 wt % iron; and from 0-0.1 wt % zirconium; and the balance tin, together with unavoidable impurities.
This application is a continuation-in-part of PCT application PCT/GB2006/003167, filed Aug. 24, 2006 and claiming priority to U.S. provisional application 60/710,917, filed Aug. 24, 2005, and this application also claims priority to U.S. provisional application 60/949,064, filed Jun. 11, 2007, the entire disclosures of which are incorporated herein by reference.
FIELD OF THE INVENTIONThe present invention relates to an alloy and, in particular, a lead-free solder alloy. The alloy is particularly, though not exclusively, suitable for use in ball grid arrays and chip scale packages in the form of solder spheres.
BACKGROUND OF THE INVENTIONFor environmental reasons, there is an increasing demand for lead-free replacements for lead-containing conventional alloys. Many conventional solder alloys are based around the tin-copper eutectic composition, Sn-0.7 wt. % Cu, and tin-silver eutectic composition, 96.5 wt. % Sn-3.5 wt. % Ag.
A ball grid array joint is a bead of solder between two substrates, typically circular pads. Arrays of these joints are used to mount chips on circuit boards.
The drop shock reliability of solder joints has become a major issue for the electronic industry partly because of the ever increasing popularity of portable electronics and partly due to the transition to lead-free solders. Most of the commonly recommended lead-free solders are high tin alloys which have relatively higher strength and modulus. This plays a critical role in the reliability of lead-free solder joints. Further, even though metallurgically, it is the tin in the solder alloys that principally participates in the solder joint formation, details of the IMC (intermetallic compound) layers formed with tin-lead and lead-free alloys are essentially the same. The markedly different process conditions for tin-lead and lead-free alloys also bear on solder joint quality. Brittle failure of solder joints in drop shock occurs at or in the interfacial IMC layer(s). This is due to the inherent brittle nature of the IMC, defects within or at IMC interfaces or transfer of stress to the interfaces as a result of the low ductility of the bulk solder.
There are a number of requirements for a solder alloy to be suitable for use in ball grid arrays (BGA) and chip scale packages (CSP). First, the alloy must exhibit good wetting characteristics in relation to a variety of substrate materials such as copper, nickel, nickel phosphorus, nickel boron (“electroless nickel”). Solder alloys tend to dissolve the substrate and to form an intermetallic compound at the interface with the substrate. For example, tin in the solder alloy will react with the substrate at the interface to form an intermetallic. If the substrate is copper, then a layer of Cu6Sn5 will be formed. Such a layer typically has a thickness of from a fraction of a micron to a few microns. At the interface between this layer and the copper substrate an intermetallic compound of Cu3Sn may be present. Such an intermetallic compound may result in a brittle solder joint.
In some cases, voids occur, which may contribute to premature fracture of a stressed joint.
Other important factors are (i) the presence of intermetallics in the alloy itself, which results in stronger mechanical properties, (ii) oxidation resistance in multiple reflow, and (iii) alloy stability. This latter consideration is important for applications where the alloy is held in a tank or bath for long periods of time.
SUMMARY OF THE INVENTIONThe present invention aims to address at least some of the problems associated with the prior art and to provide an improved solder alloy.
Accordingly, the present invention provides an alloy suitable for use in a ball grid array or chip scale package, the alloy comprising:
from 0.05-1.5 wt. % copper;
from 2.5-5 wt. % silver;
one or both of from 0.005-0.3 wt % nickel and/or from 0.003-0.3 wt % chromium;
from 0-0.1 wt. % phosphorus;
from 0-0.1 wt. % germanium;
from 0-0.1 wt. % gallium;
from 0-0.3 wt. % of one or more rare earth elements;
from 0-0.3 wt. % indium;
from 0-0.3 wt. % magnesium;
from 0-0.3 wt. % calcium;
from 0-0.3 wt. % silicon;
from 0-0.3 wt. % aluminium;
from 0-0.3 wt. % zinc;
from 0-2 wt. % bismuth;
from 0-1 wt. % antimony;
from 0.008-0.2 wt % manganese;
from 0.01-0.3 wt % cobalt;
from 0.02-0.3 wt % iron;
from 0.008-0.1 wt % zirconium; and
the balance tin, together with unavoidable impurities.
Corresponding reference characters indicate corresponding parts throughout the drawings.
DESCRIPTION OF THE EMBODIMENT(S) OF THE INVENTIONThe present invention will now be further described. In the following passages different aspects of the invention are defined in more detail. Each aspect so defined may be combined with any other aspect or aspects unless clearly indicated to the contrary. In particular, any feature indicated as being preferred or advantageous may be combined with any other feature or features indicated as being preferred or advantageous.
Copper forms an eutectic with tin, lowering the melting point and increasing the alloy strength. A copper content in the hyper-eutectic range increases the liquidus temperature but further enhances the alloy strength. In one embodiment, the alloy preferably comprises from 0.1 to 1 wt. % Cu, more preferably from 0.1 to 0.9 wt. % Cu, still more preferably from 0.1 to 0.8 wt. % Cu. In another embodiment, the alloy preferably comprises from 0.15 to 1 wt. % Cu, more preferably from 0.5 to 0.9 wt. % Cu, still more preferably from 0.6 to 0.8 wt. % Cu. Specific examples of preferred alloys are ones containing 0.1 wt. % Cu, 0.5 wt. % Cu, and 0.7 wt. % Cu.
Silver lowers the melting point and improves the wetting properties of the solder to copper and other substrates. The alloy preferably comprises from 2.5 to 5 wt. % Ag, more preferably from 3 to 4.5 wt. % Ag, still more preferably from 3 to 4 wt. % Ag. Most preferably, the alloy comprises from 3 to 3.5 wt. % Ag.
A high silver content (i.e. preferably ≧2.5 wt. %, more preferably ≧3 wt. %) has been found to be beneficial because it provides higher resistance against the fracture of solder joints during temperature cycling. The net result of the thermo-mechanical stress experienced in the solder joints during temperature cycling is re-crystallization and grain growth followed by grain boundary sliding under the stress. Cracks propagate as a result of, for example, micro-void coalescence along grain boundaries. Crack propagation therefore can be reduced for alloys for which grain motion is minimized. The presence of particle phases like Ag3Sn in SnAgCu alloys at or intersecting boundaries is a cause for the more limited grain boundary siding in such alloys. For higher silver content alloys, there is a greater amount of Ag3Sn intermetallic compound in the bulk of the solder, which results in improved fatigue resistance. However, too high a silver content can have an adverse affect on drop shock resistance and for this reason the silver content preferably does not exceed 5 wt. %, more preferably it does not exceed 4 wt. %, still more preferably it does not exceed 3.5 wt. %.
The presence of nickel in the alloy is beneficial in terms of mechanical properties (as demonstrated by improved ball pull) and also solder spread. The alloy may comprise from 0.005 to 0.3 wt. % nickel, preferably from 0.01 to 0.3 wt % nickel, more preferably 0.02 to 0.3 wt %, more preferably 0.02 to 0.2 wt %, still more preferably 0.03 to 0.15 wt %, still more preferably 0.04 to 0.12 wt %. A particularly advantageous range is 0.04 to 0.08 wt % nickel. Ball pull results indicate that there is a reproducible correlation between improved ball pull and solder spread and the optimum nickel content in these respects has been found to be 0.03 to 0.07 wt %, preferably 0.04 to 0.06 wt %, more preferably approximately 0.05 wt %. The same is also confirmed by drop shock test results. The performance with 0.5 wt % nickel is poorer than 0.05% nickel (however, good results are also obtained at approximately 0.1 wt % nickel). For this reason, the nickel content should not exceed approximately 0.3 wt % nickel.
The presence of chromium in the alloy is also beneficial in terms of mechanical properties (as demonstrated by improved ball pull). However, chromium on its own (i.e. without nickel) has little or no effect on solder spread. Surprisingly, however, in conjunction with nickel an improvement in solder spread is observed. The alloy may comprise from 0.003 to 0.3 wt. % chromium, preferably from 0.005 to 0.3 wt % chromium, more preferably 0.01 to 0.2 wt %, more preferably 0.01 to 0.1 wt %, still more preferably 0.01 to 0.07 wt %. The optimum is 0.02 to 0.06 wt % chromium, preferably 0.02 to 0.04 wt %, more preferably approximately 0.03 wt %. However, good results are also obtained at approximately 0.05 wt %. In the manufacture of the alloy, in order to achieve the required alloying effect, it is advantageous to add the chromium to the tin and other components by first alloying some or all of the chromium with some or all of the copper.
Nickel and chromium may act as intermetallic compound growth modifiers and grain refiners. For example, while not wishing to be bound by theory, it is believed that nickel forms an intermetallic with tin and with the copper to form a CuNiSn intermetallic and the presence of the low solubility elements in the intermetallic slows the diffusion of Cu and thereby reduces the amount of IMC that forms over time. It has been found that growth rates of the CuNiSn intermetallics are less than in nickel-free alloys.
Chromium has a low solubility in tin but alloys with copper. Chromium is therefore preferably alloyed via the copper component in the solder and thereby it is proposed that it will limit the formation of Cu6Sn5 IMC in the bulk solder. The presence of the intermetallics affects the microstructure developed on cooling the alloy from the molten to the solid state. A finer grain structure is observed, which further benefits the appearance and strength of the alloy.
Up to 0.3 wt % chromium in combination with up to 0.3 wt % nickel and 2.5 to 5 wt % silver results in an alloy with improved properties. In particular, it has been found that alloys containing the nickel and chromium additions have a reduced ball pull force for the so called Mode 2 failure. Mode 2 is the preferred failure mode. It is necking and tensile failure in the solder, not at the interface.
Chromium has also been found to soften the alloy and improve oxidation resistance. With regard to tarnish performance, a small quantity (˜50 ppm) of phosphorus addition may advantageously be used. The presence of nickel in the alloy also provides reasonable protection against tarnish resistance of solder spheres.
The sum of nickel and chromium is preferably from 0.008 to 0.6 wt %, more preferably 0.01 to 0.2 wt %, still more preferably 0.01 to 0.15 wt %. The optimum combined amount of nickel and chromium is 0.05 to 0.12 wt %.
It has surprising been found that the presence of both nickel and chromium in the alloys according to the present invention has a very positive effect on mechanical properties. The addition of either nickel or chromium results in some improvement in mechanical properties, as demonstrated by high strain rate testing performance and ball pull data. However, it has been found that there is a synergistic effect between nickel and chromium: the collective effect of the nickel and chromium additions is greater than the sum of the individual effects. In particular, the alloys according to the present invention can show >80% reduction in mode 4 failures as demonstrated by drop shock evaluations.
The combination of nickel and chromium in the alloys according to present invention therefore offers high drop shock reliability and also improved solder spread.
If present, the alloy preferably comprises from 0.02-0.2 wt. % of at least one of cobalt and/or iron, more preferably from 0.02-0.1 wt. % of at least one of cobalt and/or iron.
If present, the alloy preferably comprises from 0.005-0.3 wt. % magnesium. In this case, improved properties can be obtained by the presence of from 0.02-0.3 wt % Fe.
If present, the alloy preferably comprises from 0.01-0.15 wt % manganese, more preferably from 0.02-0.1 wt % manganese.
Cobalt, manganese, iron, antimony, and zirconium may also act as intermetallic compound growth modifiers and grain refiners.
Indium, zinc, magnesium, calcium, gallium and aluminium may act as diffusion compensators. The addition of appropriate fast diffusing species can be effective in balancing what otherwise would be a net atom flux away from, for example, the solder-substrate interface, resulting in void formation (Horsting or Kirkendall). Indium has been found to have a beneficial effect on solder wetting. Indium lowers the melting point of the solder. Indium may also act to reduce the formation of voids in the solder joint. Indium may also improve the strength of the Sn-rich matrix. Zinc has been found to act in a similar manner to indium. The alloy may optionally contain up to 0.3 wt. % indium, for example 0.05-0.3 wt. % indium, preferably from 0.1-0.2 wt. % indium.
The alloy may optionally comprise from 0.01-0.3 wt. % calcium, more preferably from 0.1-0.2 wt. % calcium.
The alloy may optionally comprise from 0.01-0.3 wt. % silicon, more preferably from 0.1-0.2 wt. % silicon.
The alloy may optionally comprise from 0.01-0.3 wt. % zinc, more preferably from 0.1-0.2 wt. % zinc.
The alloy may optionally comprise from 0.05-1 wt. % antimony, more preferably from 0.1-0.5 wt. % antimony.
Aluminium (as well as chromium, germanium, silicon and phosphorous) may be beneficial in terms of oxidation reduction. The alloy may optionally comprise from 0.008-0.3 wt. % aluminium, more preferably from 0.1-0.2 wt. % aluminium.
Phosphorus, germanium and gallium may act as dross reducers. The alloy may optionally contain up to 0.1 wt. % of one or more of each of phosphorus, germanium and gallium.
Bismuth may act to improve wetting and fatigue resistance. Bismuth can lower the solidus temperature and improve strength through precipitation hardening while suppressing the formation of large Ag3Sn IMC in the bulk solder. The alloys according to the present invention may contain up to 2 wt. % bismuth, more preferably up to 1 wt. %, still more preferably up to 0.5 wt. % bismuth, for example 0.05 to 0.5 wt. %.
If present, the alloy preferably comprises up to 0.05 wt. % of one or more rare earth elements. The one or more rare earth elements preferably comprise two or more elements selected from cerium, lanthanum, neodymium and praseodymium.
The alloys according to the present invention are lead-free or essentially lead-free. The alloys offer environmental advantages over conventional lead-containing solder alloys.
The alloys according to the present invention will typically be supplied as a solder sphere for CSP applications but may also be supplied as bar, stick or ingot, optionally together with a flux. The alloys may also be provided in the form of a wire, for example a cored wire, which incorporates a flux, a sphere or a preform cut or stamped from a strip or solder. These may be alloy only or coated with a suitable flux as required by the soldering process. The alloys may also be supplied as a powder blended with a flux to produce a solder paste.
The alloys according to the present invention may be used in molten solder baths as a means to solder together two or more substrates and/or for coating a substrate.
It will be appreciated that the alloys according to the present invention may contain unavoidable impurities, although, in total, these are unlikely to exceed 1 wt. % of the composition. Preferably, the alloys contain unavoidable impurities in an amount of not more than 0.5 wt. % of the composition, more preferably not more than 0.3 wt. % of the composition, still more preferably not more than 0.1 wt. % of the composition.
The alloys according to the present invention may consist essentially of the recited elements. It will therefore be appreciated that in addition to those elements which are mandatory (i.e. Sn, Cu. Ag, and at least one of Ni and/or Cr) other non-specified elements may be present in the composition provided that the essential characteristics of the composition are not materially affected by their presence.
The alloys will typically comprise at least 90 wt. % tin, preferably from 94 to 97.4 wt. %. Accordingly, the present invention further provides an alloy for use in a ball grid array or chip scale package, the alloy comprises:
from 94-97.4 wt % tin;
from 0.05-1.5 wt. % copper;
from 2.5-5 wt. % silver;
one or both of from 0.005-0.3 wt. % nickel and/or from 0.003-0.3 wt. % chromium;
from 0-0.1 wt. % phosphorus;
from 0-0.1 wt. % germanium;
from 0-0.1 wt. % gallium;
from 0-0.3 wt. % of one or more rare earth elements;
from 0-0.3 wt. % indium;
from 0-0.3 wt. % magnesium;
from 0-0.3 wt. % calcium;
from 0-0.3 wt. % silicon;
from 0-0.3 wt. % aluminium;
from 0-0.3 wt. % zinc;
from 0-2 wt. % bismuth;
from 0-1 wt. % antimony;
from 0.008-0.2 wt % manganese;
from 0.01-0.3 wt % cobalt;
from 0.02-0.3 wt % iron; and
from 0.008-0.1 wt % zirconium;
together with unavoidable impurities.
The alloys according to the present invention are particularly well suited to applications involving ball grid arrays or chip scale packages. Accordingly, the present invention also provides for the use of a solder alloy as herein described in a ball grid array or chip scale package.
The following are examples of preferred alloy compositions in accordance with the present invention which show surprisingly good mechanical properties (eg high drop shock reliability) and also improved solder spread. The collective effect of the nickel and chromium additions is greater than the sum of the individual effects.
The present invention also provides for a ball grid array or chip scale package joint comprising the solder alloy composition as herein described.
Having described the invention in detail, it will be apparent that modifications and variations are possible without departing from the scope of the invention defined in the appended claims.
EXAMPLESThe following are non-limiting examples to further describe the present invention.
Example 1An alloy was prepared by melting Sn in a cast iron crucible (alternatively a ceramic crucible can be used). To the molten Sn was added an alloy of Sn-3 wt % Cu, and alloys of Sn-5 wt % Ag and Sn-0.35 wt % Ni. These additions were made with the alloy bath temperature at 350° C. The bath was cooled to 300° C. for the addition of phosphorus in the form of an alloy Sn-0.3% P.
The alloy was sampled to verify the composition of
The alloy composition was then jetted as a metal stream into an inerted vertical column. The metal stream was spherodised by the application of magnetostrictive vibrational energy applied through the melt pot and at or near the exit orifice.
Equally, the alloy composition could be punched and then spherodised as a sphere.
The alloy, provided in the form of a sphere, can be used in a ball grid array joint or chip scale package. Flux is printed or pin transferred to the pads of a CSP. The spheres are then pick and placed or shaken through a stencil onto the fluxed pads. The package is then reflowed in a standard reflow oven at a peak temperature of between 240° C. and 260° C.
Alloy and solder joint performance was assessed in packages aged at 150° C. for up to 1000 hours. IMC growth was measured by standard metallographic techniques. Mechanical ball pull testing was used to assess solder joint failure mode (brittle or ductile).
Example 2The following alloy composition was prepared in a similar manner to Example 1 (all wt. %)
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 3The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 4The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 5Alloys have been prepared corresponding to the compositions of Examples 1 to 4 where Ge is substituted for the phosphorus content.
Example 6The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 7The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 8The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 9The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 10The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 11The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 12The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 13The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 14The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 15The following alloy composition was prepared in a similar manner to Example 1.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
Example 16The following alloy composition was prepared in a similar manner to Example 1.
In the context of this example,
Ball pull tests are well known in the field of metallurgy and solder alloys. The experimental work was conducted on Dage 4000 and Dage 4000 HS Ball Pull and Ball Shear systems. The Dage 4000 machine is capable of performing ball pull test at speeds up to 15 mm/sec while the Dage 4000 HS can do the same test up to 1000 mm/sec. All the tests were carried out using 18 mil (450 μm) spheres assembled on CABGA100 substrates with NiAu pad finish. Spheres were assembled using a water-soluble paste flux (Alpha WS9180-M3) that was stencil printed on the substrates. Spheres were placed using a simple manual alignment assembly setup and reflowed in air, in a seven-zone convection reflow oven.
With regard to the alloys tested, two silver SnAgCu base alloys were used having the silver, copper, and tin contents shown in the below table I:
Ni and Cr were added to these alloys to form the following alloy compositions:
Base alloy: SAC305 modified by adding Ni to yield an alloy having the components and percentages
Base alloy: SAC405 modified by adding Ni to yield an alloy having the components and percentages
Base alloy: SAC305 modified by adding Cr to yield an alloy having the components and percentages
Base alloy: SAC305 modified by adding Cr to yield an alloy having the components and percentages
Base alloy: SAC305 modified by adding Ni to yield an alloy having the components and percentages
Base alloy: SAC305 modified by adding Ni to yield an alloy having the components and percentages
Similar results were obtained for SAC405.
This alloy may be provided in the form of a sphere and used in a ball grid array joint or chip scale package.
When introducing elements of the present invention or the preferred embodiments(s) thereof, the articles “a”, “an”, “the” and “said” are intended to mean that there are one or more of the elements. The terms “comprising”, “including” and “having” are intended to be inclusive and mean that there may be additional elements other than the listed elements.
In view of the above, it will be seen that the several objects of the invention are achieved and other advantageous results attained.
As various changes could be made in the above compositions and processes without departing from the scope of the invention, it is intended that all matter contained in the above description and shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense.
Claims
1. An alloy suitable for use in a ball grid array or chip scale package, the alloy comprising:
- from 0.05-1.5 wt. % copper;
- from 2.5-5 wt. % silver;
- one or both of from 0.005-0.3 wt % nickel and/or from 0.003-0.3 wt % chromium;
- from 0-0.1 wt. % phosphorus;
- from 0-0.1 wt. % germanium;
- from 0-0.1 wt. % gallium;
- from 0-0.3 wt. % of one or more rare earth elements;
- from 0-0.3 wt. % indium;
- from 0-0.3 wt. % magnesium;
- from 0-0.3 wt. % calcium;
- from 0-0.3 wt. % silicon;
- from 0-0.3 wt. % aluminium;
- from 0-0.3 wt. % zinc;
- from 0-2 wt. % bismuth;
- from 0-1 wt. % antimony;
- from 0-0.2 wt % manganese;
- from 0-0.3 wt % cobalt;
- from 0-0.3 wt % iron; and
- from 0-0.1 wt % zirconium; and
- the balance tin, together with unavoidable impurities.
2. An alloy as claimed in claim 1 comprising from 0.02-0.3 wt % nickel.
3. An alloy as claimed in claim 2 comprising from 0.02 to 0.2 wt % nickel.
4. An alloy as claimed in claim 1 comprising from 0.005 to 0.3 wt % chromium.
5. An alloy as claimed in claim 4 comprising from 0.01 to 0.2 wt % chromium.
6. An alloy as claimed in claim 1 comprising from 0.1 to 1 wt. % Cu.
7. An alloy as claimed in claim 6 comprising from 0.1 to 0.9 wt. % Cu.
8. An alloy as claimed in claim 1 comprising from 3 to 4 wt. % Ag.
9. An alloy as claimed in claim 8 comprising from 3 to 3.5 wt. % Ag.
10. An alloy as claimed in claim 1 comprising from 0.02-0.2 wt. % of at least one of cobalt and iron.
11. An alloy as claimed in claim 1 comprising from 0.01-0.3 wt. % magnesium.
12. An alloy as claimed in claim 1 comprising from 0.02-0.3 wt. % iron.
13. An alloy as claimed in claim 1 comprising from 0.01-0.15 wt. % manganese.
14. An alloy as claimed in claim 1 comprising from 0.05-0.3 wt. % indium.
15. An alloy as claimed in claim 1 comprising from 0.01-0.3 wt. % calcium.
16. An alloy as claimed in claim 1 comprising from 0.01-0.3 wt. % silicon.
17. An alloy as claimed in claim 1 comprising from 0.008-0.3 wt. % aluminium.
18. An alloy as claimed in claim 1 comprising from 0.01-0.3 wt. % zinc.
19. An alloy as claimed in claim 1 comprising from 0.05-1 wt. % antimony.
20. An alloy as claimed in claim 1 comprising from 0.05 to 1 wt. % bismuth.
21. An alloy as claimed in claim 1, wherein said one or more rare earth elements comprises one or more elements selected from cerium, lanthanum, neodymium and praseodymium.
22. An alloy as claimed in claim 1 comprising from 0.1 to 0.8 wt. % Cu, from 3 to 4 wt. % Ag, from 0.03 to 0.15 wt % nickel and/or from 0.01 to 0.07 wt % chromium.
23. An alloy as claimed in claim 1 in the form of a bar, a stick, a solid or flux cored wire, a foil or strip, a preform, or a powder or paste (powder plus flux blend), or solder spheres for use in ball grid array joints, or a pre-formed solder piece.
24. A soldered ball grid array or chip scale package joint comprising an alloy as defined in claim 1.
25. Use of an alloy as defined in claim 1 in a ball grid array or chip scale package.
Type: Application
Filed: Feb 25, 2008
Publication Date: Jul 3, 2008
Applicant: FRY'S METALS, INC. (South Plainfield, NJ)
Inventors: Brian G. Lewis (Branford, CT), Bawa Singh (Voorhees, NJ), John Laughlin (Tucson, AZ), Ranjit Pandher (Plainsboro, NJ)
Application Number: 12/036,528
International Classification: C22C 13/00 (20060101);