Femtosecond Laser Pulse Surface Structuring Methods and Materials Resulting Therefrom
Embodiments of the present invention are generally directed to materials processing methods using femtosecond duration laser pulses, and to the altered materials obtained by such methods. The resulting nanostructured (with or without macro- and micro-structuring) materials have a variety of applications, including, for example, aesthetic applications for jewelry or ornamentation; biomedical applications related to biocompatibility; catalysis applications; and modification of, for example, the optical and hydrophilic properties of materials including selective coloring.
Latest UNIVERSITY OF ROCHESTER Patents:
- DEEP TISSUE SUPER-RESOLUTION ULTRASOUND IMAGING METHOD AND SYSTEM
- Per-channel color barcodes for displays
- Induced pluripotent cell-derived oligodendrocyte progenitor cells for the treatment of myelin disorders
- SUPER-HYDROPHOBIC SURFACES AND METHODS FOR PRODUCING SUPER-HYDROPHOBIC SURFACES
- Method of electrical reconfigurability and an electrical reconfigurable logic gate device instrinsically enabled by spin-orbit materials
This patent application is a continuation-in-part of, and claims priority to, U.S. application Ser. No. 11/862,449 filed on Sep. 27, 2007, as well as to U.S. Provisional Application Ser. No. 60/847,916, filed Sep. 29, 2006, the subject matters of which are herein incorporated by reference in their entireties.FEDERALLY SPONSORED RESEARCH
This invention was made with government support under Contract No. CTS-042506 sponsored by the National Science Foundation. The government may have certain rights in the invention.BACKGROUND
1. Field of the Invention
Embodiments of the invention generally pertain to the field of materials processing and associates processed materials. More particularly, embodiments of the invention are directed to methods for processing materials using femtosecond duration laser pulses, applications of such methods, and materials and/or material properties resulting from such methods. Even more particularly, embodiments of the invention are directed to methods for altering the surface structure of metal materials using femtosecond duration laser pulses, applications of such methods, and materials and/or material properties resulting from such methods, including blackened and colored metals.
2. Description of Related Art
Although materials may be shaped or otherwise altered in a large variety of ways including milling, machining, grinding, etc., in recent years, laser-based alteration of materials has become a common method for a variety of materials processing applications. For example, laser alteration of materials by high energy laser pulses has been used to both create precise hole patterns in metals or metal films as well as for more subtle material alterations such as texturing of metals or metal films by the intense heating/melting/vaporization effects of such high energy laser beams.
Reported methods of laser alteration of materials involves the use of ‘short-duration’ (i.e., nanosecond (ns) and picosecond (ps)) laser pulses. See, for example, U.S. Pat. Nos. 5,635,089 and 4,972,061. U.S. Pat. No. 6,979,798 describes the use of laser pulses of preferably less than 130 femtoseconds (fs) to specifically burn metal links on integrated circuits. Thus the use of ultrashort (ns) duration laser pulses for laser processing of materials may achieve results that are different than those from longer duration (i.e., ‘short’) laser pulses. The duration of a nanosecond laser pulse is long enough for the pulse to interact with the material as it is ejected from the surface. Ultra-short duration, femtosecond (fs) laser pulses, by comparison, are not long enough in duration to interact with the material ejected from the surface of the irradiated substance, since the pulse ends long before the hydrodynamic expansion of the ejected material. Another difference between different laser pulse timescales is that the laser-supported combustion and detonation waves that are commonly generated in a nanosecond duration laser pulse do not occur in an ultra-short fs laser pulse, again offering up the possibility of materials processing effects and resulting material parameters that may be difficult or impossible to obtain with longer duration laser irradiation.
In light of the above observations, advantageous benefits may be obtained from the use of ultra-short, femtosecond pulses in the processing of certain materials and the altered materials or material characteristics resulting from processing with one or more fs laser pulses. Certain advantageous benefits may also be realized by the ability to controllably modify optical properties of a metal.SUMMARY
Embodiments of the invention are directed to methods for processing materials using femtosecond duration (i.e., 1-999 fs) laser pulses, applications of such methods, and altered materials and/or material properties resulting from such methods. Particularly advantageous aspects of the invention are directed to methods for altering the surface structure of metal and other materials by application of one or more femtosecond duration laser pulses, applications of such methods, and altered materials and/or material properties resulting from such methods. According to non-limiting aspects, methods for uniformly coloring, non-uniformly coloring, and blackening a metal or other material, increasing a material's absorptance (up to nearly 100%), increasing a material's surface area, as well as altered materials exhibiting these characteristics are disclosed.
As used herein, the term “colored metal” will mean a metal having a color that is due to a femtosecond laser pulse(s)-induced nanostructuring of the surface of the metal, but not due to artificial or applied coloring, painting, dying, etching, polishing, anodizing, or other non-femtosecond laser pulse(s)-induced nanostructuring of the surface of the metal. The term “color” will have its typical meaning as well as the practical consideration that color is observable over the visible light spectrum. In that regard, however, one skilled in the art will also recognize the relationship between color and the reflectance/absorptance of light by a material, where ‘white’ would correspond to high reflectivity and ‘black’ to high absorptivity. As further used herein, the term “base metal” will mean the metal prior to femtosecond laser surface structuring as it is ready to undergo femtosecond laser pulse(s)-induced nanostructuring of the surface of the metal, in which case it may or may not be polished. According to the embodiments of the invention, the absorptance of the base metal will always be less than the corresponding absorptance of the fs laser-treated material.
Embodiments of the present invention are generally directed to laser-based materials processing using one or more femtosecond duration (i.e., 1-999.99 fs) laser pulses, and to the altered materials obtained by such materials processing. As used herein, the term ‘materials processing’ and ‘surface treatment’ refer to altering the surface structure or restructuring the surface of the material being processed by creating various nanostructures that may or may not be created in combination with additional micro- and macrostructures. Non-limiting examples of nanostructured surfaces in accordance with embodiments and aspects of the invention are shown in the figures and will be described in detail below.
Material alterations obtained in accord with embodiments of the present invention may be defined by a variety of experimental methods for analyzing the alterations obtained (synonymously “the materials processing outcome(s)”); for example, by electron micrographic analysis, by spectroscopic analysis (e.g., absorption of light or other electromagnetic energy by the altered surface), and via other techniques recognized in the art. Material alterations may also be additionally and/or separately defined in terms of theoretical modeling of alterations and the mechanisms by which alterations are generated, e.g., by post-ablation redeposition of material, by the formation of nanostructure-covered, laser induced periodic surface structures (NC-LIPSS), and others described herein and known in the art.
In this regard, the term “ablation” is used to refer to material alterations generally, rather than to any specific process of material alteration. Specifically, “ablation” is defined as occurring by experimental observation, i.e., by the onset of surface damage or alteration to the material being processed, where the surface damage or alteration is typically observed by eye or by SEM analysis (see, e.g., Example 2). Thus the term “ablation” is generic, and is not used to refer to a specific physical process of material alteration, for example, the specific physical process of vaporization or other form of removal of material from a surface, etc.
The structural material alterations described herein below may be defined more precisely as, e.g., “nanostructures,” “nanoscale structure,” “nanoscale roughness,” or “nanoroughness” obtained by femtosecond laser pulse nanostructuring of the material. Other alterations that may or may not occur in the presence of nanostructuring include, without limitation, “microstructures,” “microscale structure,” “microscale roughness,” or “microroughness” obtained by microstructuring effects obtained by femtosecond laser pulse nanostructuring of the material, and “macrostructures,” “macroscale structure,” “macroscale roughness,” or “macroroughness” such as craters or other features obtained by macrostructuring effects obtained by femtosecond laser pulse nanostructuring of the material.
With further regard to nanostructures, terms including but not limited to “nanobranches,” “nanoparticles,” “nanoprotrusions,” “nanocavities,” “nanorims,” “nanopores,” nanospheres” are used to describe nanoscale dimension alterations having the visual appearances under SEM analysis of branches, particles, protrusions, cavities, spheres, channels, etc. With regard to microstructures, for example, “columnar microstructures” is used to refer to microstructures that appear visually under SEM analysis as columns (see, e.g.,
Further with regard to the above terms, SEM analysis may be used to establish quantitative as well as qualitative definitions for macro-, micro-, and nanostructures, and these definitions may be used to define the materials obtained by the materials processing methods according to embodiments and aspects of the invention.
In some non-limiting aspects of the invention, it may be desirable to create essentially a single kind of materials structuring, while in other non-limiting aspects it may be advantageous to create ‘mixed’ structuring. In this context the word “dominated” is used herein to refer to a situation where one type of structuring is prevalent, i.e., where one type of structuring occurs across, e.g. about 80% or more of the surface area of the surface produced by the specified materials processing regime. In general, however, when the surface is “dominated” by nanostructures, for example, it will be understood that other percentage values are explicitly contemplated; i.e., 70, 71, 72, 73, 74, 75 . . . 97, 98, 99% (i.e., counting by 1% intervals) of the surface area is of the structure specified.
Although the above visually-based terms are used herein to classify nanostructuring, microstructuring, and macrostructuring effects according to embodiments of the invention, other methods can be used to categorize these structures. For example, because the absorptance of a material is a function of the intrinsic absorptance, AINTR, and the surface roughness, ASR, alterations to a material that manifest as alterations in surface roughness may be described by absorptance changes rather than, or in addition to, descriptions of macro-, micro-, or nanostructural changes based on changes in the visual appearance. Thus Example 1 below shows in detail how different femtosecond pulse duration laser processing regimes alter absorptance, and how these alterations in absorptance correlate with macro-, micro- and nanostructural changes in the surface of the material.
Further with regard to absorptance, as discussed in Example 1 and particularly shown in
The absorptance values determined in Example 1 are measured calorimetrically; however, absorptance may also be measured by other means, and specifically by methods that allow absorptance to be determined as a function of the wavelength of the light impinging on the sample. Reflectivity may also be measured in addition to, or in substitution for, absorptance, especially in situations where it is desirable to produce a material with favorably altered reflectivity. Reflectivity may be measured by any standard method used for such determinations; examples of reflectivity measurements are provided in, for example, U.S. Pat. No. 4,972,061, the contents of which are incorporated herein by reference in their entirety.
Thus in a non-limiting, exemplary aspect, materials processing methods and resulting altered or treated materials are directed to the field of jewelry. The surface of virtually any metal or metal alloy such as, but not limited to, gold, platinum, silver, stainless steel, various precious metals, decorative metals, and others may be decorated, initialed, patterned, colored, blackened, or otherwise marked via femtosecond laser surface structuring so as to have, for example, altered reflectivity ranging from the reflectivity of the unmarked metal down to essentially 0% reflectivity, depending upon the desired application. In various non-limiting aspects, reflectivity may vary with wavelength (producing different colors) and/or viewing angle.
According to the various embodiments described herein, the materials to be altered by femtosecond laser surface structuring include most generally all metals and alloys thereof, including, but not limited to, gold, aluminum, copper, platinum, titanium, tungsten, stainless steel, and others. The alteration of semiconductor materials and dielectrics are contemplated. Also contemplated are ceramic, glass, and plastic materials.
According to non-limiting aspects, metal materials are intended to include metal films (e.g., thin metal layers coated on glass, silicon or other additional underlying layer) and bulk metals. Bulk metals refer to non-thin films of more than a few hundred nm, particularly more than 1 μm, and more particularly to more than 10 μm in thickness. Thus “bulk metals” refers to metals with the characteristics just recited, whereas “thin films” refers to metals of less than a few hundred nm, including the thin films described in the Examples below.
Further with regard to the materials of the present invention, as shown in the Examples and in, e.g.,
Pulse duration is a function of the laser system used. In various non-limiting embodiments, the laser system is a Ti:sapphire laser system generating 65 fs duration pulses at a central wavelength of 0.8 μm; however, other laser systems generating different fs pulse durations are also contemplated. See, e.g., U.S. Pat. No. 6,979,798 and U.S. Publication No. 2006/0207976A1, the contents of which are incorporated herein by reference in their entireties, for non-limiting descriptions of other such fs duration laser systems, e.g., a Yb-doped fiber laser such as the FPCA uJewel (available from IMRA America, Ann Arbor Mich.). Other such fs duration lasers may include, e.g., dye lasers, Cr:LiSAF lasers, KrF lasers, and others known in the art.
In addition to laser pulse duration, a number of other laser parameters may be varied in various aspects of the present invention in order to obtain the desired materials processing effects, including but not limited to: the polarization of the laser beam (typically horizontally polarized); the diameter of the spot of laser irradiation on the surface of the material sample (typically between 100 and 1200 μm); the wavelength of the laser beam; the energy density, F (fluence), of the laser beam; the number of laser pulses (shots) applied to the material sample; the extent of overlap between multiple laser pulses (shots) applied to the particular region of the material being processed; whether the shots are applied in vacuum or under higher pressure conditions, and others.
According to various non-limiting exemplary embodiments, the fs laser has a central wavelength (lambda) of 0.8 μm. However, other wavelengths in the IR, visible, ultraviolet, infrared, THz frequency, etc., may be advantageously used.
With regard to laser fluence on the surface of the material to be processed, as will be discussed below, contemplated fluences will be sufficient to alter the surface structure of the metal as described herein and will be generally below about 25 J/cm2 at the material surface; i.e., below about 25, 24, 23, 22, 21, 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, 10, 9, 8, 7, 6, 5, 4, 3, 2, or 1 J/cm2. The exact choice of fluence varies, however, depending upon the desired materials processing effects. Thus for example, the summary graphic of
Further with regard to fluence, in an exemplary embodiment the choice of fluence is expressed by reference to the threshold laser fluence (synonymously, the “ablation threshold” or Fabl) required for visible material surface damage under SEM. Thus as described in the Examples, materials processing effects can be calibrated to the ablation threshold, e.g., the fluence specified to obtain a particular effect may be given both in absolute terms of J/cm2 or, alternatively, may be given as a percentage of the ablation threshold, i.e., as 1, 2, 3, 4, 5, . . . , 100, 101, 102, 103, 104, 105, . . . 10,000% (counting by ones) of Fabl.
With regard to laser pulses, embodiments of the present invention may use single- and multi-pulse exposures of materials to obtain desired materials processing effects. Laser “pulse” or synonymously, “shot”, refers to a single laser pulse applied to the sample material using for example an electromechanical shutter to select a single pulse. Multi-pulse or multi-shot situations involve more than a single shot, e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10, etc. (counting by ones) up to thousands, tens-of-thousands, or hundreds-of-thousands of shots. The exact number of pulses or shots chosen will depend upon the desired materials processing outcome, as shown in for example in the summary graphic of
The extent of overlap between shots in a multi-shot situation may be varied in order to obtained desired effects, e.g., by specifying that at least x % of the area of an additional shot or shots overlap with the first or previous shot, where x can be 1 to 100% counting by ones (i.e., 1, 2, 3, 4, 5, . . . , 100%). Such variations may be particularly important when, for example, the portion of the material in the center of the irradiation by the laser pulse or pulses undergoes different alterations as a result of the centrality of the beam than portions of the material at the periphery of the pulse or pulses (see, e.g.,
As a result of shot overlap or other controllable parameters, a variable percentage of a surface may be altered to have the desired structure or structures. For example, a precise scanning pattern of a laser beam across the surface of the material may be used to ensure that a variable percentage of the surface is altered to possess the desired nanostructure(s), microstructure(s), macrostructure(s), or combinations thereof. Contemplated percentages of a surface to be modified range from 1 to 100% counting by ones (i.e., 1, 2, 3, 4, 5, . . . , 100%). As shown in
In addition to specifying the percentage of the surface to be modified, the materials processing effects may also be expressed in terms of a total area modified, e.g., 0.1, 0.2, 0.3, 0.4, 0.5, . . . 10,000 cm2 (counting by 0.1 cm2 units). In this regard, it is advantageous that the embodied materials processing methods produce sufficiently large amounts of altered materials, where these amounts may be specified in terms of the total surface area of the material that has been altered.
The exact surface area or range of surface areas required for any particular application of the present invention will depend upon the application; aesthetic applications such as jewelry, for example, will require relatively small amounts of altered material. In contrast, larger surface areas of altered materials may be required for other applications, e.g., formation of heat absorptive surfaces, or for applications for, e.g., catalysis or materials implantation into the human body for, e.g., dental implants or other situations where nanostructuring is advantageous for cellular growth and penetration into the implant material.
According to non-limiting aspects of the invention, advantageous nanostructured materials processing effects may be obtained under ambient air/pressure conditions. Thus the pressure conditions under which materials processing occurs affect both the threshold laser fluence (synonymously, the “ablation threshold” or Fabl) required for visible material surface damage under SEM and the plasma ignition threshold (Fpl) as assayed by the onset of bright violet radiation from the laser-irradiated spot as measured either by a photomultiplier or an open-shutter camera (see, e.g.,
Additionally, Example 2 below discusses the effects of ambient air versus a highly reactive gas (oxygen) versus an inert gas (helium) on materials processing using ns duration pulses, and concludes that these effects are dependent upon gas pressure, rather than the type of gas environment used. While these effects are expected to be applicable to fs duration pulses as well, non-limiting aspects of the present invention nevertheless contemplate the use of purified gases in addition to ambient air for use with the materials processing regimes. Inert gases may have particularly desirable effects, thus such gases or other purified gas or mixtures of gases may be used in aspects of the present invention.Exemplary Method Embodiments
Embodiments of the invention use pulsed laser beams of femtosecond (fs) duration to obtain nanostructuring of material surfaces with or without microstructuring and/or macrostructuring effects. The specific conditions for generating a particular structure (macro-, micro-, or nano-) or combination of structures is a function of a number of variables including laser pulse duration, laser energy density or fluence (in J/cm2), and the number of pulses or “shots” of the laser beam delivered to a particular region of the material to be altered.
As shown in the Examples below, both on theoretical and experimental grounds, fs pulses produce different materials processing effects than do ps and ns duration pulses. It is also observed that the materials processing effects obtained with fs laser pulses are not a priori uniform; rather, they depend in part upon the specific pulse parameters such as the energy density or fluence of the laser beam and the number of pulses of the laser beam applied to the sample. However, various combinations of beam fluence and shot number may advantageously produce more uniform materials processing results.
Example 1 below will describe the effects of beam fluence and shot number on a gold sample. The results are categorized into four discrete regions of effect, AB, BC, CD, and DE as shown in
As Example 3 will show, the regions defined in Example 1 and shown in
Further confirmation of the general applicability of the three regions of
The apparatus and method embodiments described herein may have utility in a variety of applications including, but not limited to: aesthetic or marking applications such as the application of patterning or coloring to the surface of jewelry; medical applications, e.g., for implantable medical devices, where the novel properties of the laser altered surface of such a device may aide in, for example, integration of cells of a subject into the implant; catalysis, where the properties of the altered materials and particularly the increased surface area of the materials resulting from, e.g., nanostructuring, may improve the ability of the material to catalyze chemical reactions; heat transfer situations, where alterations resulting in increased absorptivity may improve, e.g., the efficiency of solar cells and heat sinks; sensor sensitivity, where the unique alterations to materials described herein may be used in both a sensor's absorbing element to increase the amount of electromagnetic radiation absorbed and also in the shielding around the sensor or sensors to protect them from various forms of stray electromagnetic radiation, thereby helping to improve their signal-to-noise ratios; and, stealth technologies or other technologies where the absorption of electromagnetic energy such as ultraviolet, visible, infrared, terahertz radiation, etc., may cloak, conceal, or otherwise obscure the object coated or shielded with the altered material having the desired absorptive properties.Exemplary Aesthetic or Marking Applications
A non-limiting aspect of the invention is directed to methods for materials processing that produce altered materials for aesthetic or marking applications, for example jewelry or other applications where the nano-, macro-, or micro-structuring of a material's surface may produces desired effects.
The data of Example 1 will show that fs-based laser processing may be used to increase the absorptivity of a material, which can be observed visually as darkening or blackening of the surface region of the material so altered. Accordingly, an embodiment the invention is directed to a method of obtaining the desired markings. A related embodiment is directed to the materials obtained by such processing methods.Exemplary Biomedical Applications
A non-limiting aspect the invention is directed to a method for materials processing that produce materials advantageously suitable for biomedical applications, particularly medical applications where a metal or metal-clad device is to be implanted into a subject, and alterations to the metal or metal cladding may act to improve the biocompatibility of the metal or metal cladding.
In this aspect, suitable materials may include metals, ceramics, composites, and others, that are nanostructured and/or possibly microstructured and then introduced or implanted into a biological milieu such as in bone, in tissue, etc., where biocompatibility is important for successful introduction or implantation. The materials contemplated include any as are known for introduction or implantation into the body, and include, but are not limited to, metals such as titanium, gold, silver, etc., alloys of these metals, composites, etc. The “biological milieu” may include bone, tissue, etc., of a whole organism, or of an isolated component of an organism, e.g., of an isolated organ, teeth, bones, etc. Organisms contemplated include animals, and particularly mammals, including humans.
Example 5 below will discuss alterations to titanium metal using a fs laser method described herein to alter the surface topography of titanium for better biocompatibility, i.e., to provide a surface containing, e.g., pits, pillars, steps, etc., or other structural features that serve as anchors or other attachment, scaffolding, or stimuli for protein and/or cellular integration.
“Biocompatibility” as used herein refers generally to alterations in the surface of a material that increase the ability of that material to integrate into the body, e.g., increase structural integration such as by invasion or interpenetration of the material by cells of the body or proteins or other biological material. Biocompatibility also refers to alterations that increase integration by decreasing rejection of the material by the body, as would occur if the material fails to integrate, i.e., so that the body recognizes the material as non-integrated and thus acts to encapsidate or otherwise reject it.
Biocompatibility may be assayed in a variety of ways. For implants, for example, biocompatibility may be determined by assaying the mechanical strength or stability of the integration of the implant into the body. Thus for example, in osseointegration of dental implants, biocompatibility may be assayed by determining the force required to displace or separate out the implant from the surrounding bone. Biocompatibility may also be determined by directly observing (e.g., by SEM) the extent to which proteins, cells, or other biological materials are able to invade or integrate into the metal or other material altered by the materials processing methods of the present invention. As another non-limiting example of an assay for biocompatibility, methods for measuring cell death or proliferation may be used to determine the extent to which the altered surface topography of the material processed by the laser methods of the present invention results in the activation of cells to proliferate, or the active suppression of cell death mechanisms that would otherwise occur if the cells failed to find themselves in a suitable proliferative environment.Exemplary Catalysis Applications
A non-limiting aspect is directed to a method for fs laser pulse materials processing that can produce materials with desirable catalytic properties; i.e., materials that contain nanostructural and macro- and/or micro-structured alterations that increase catalytic surface area.
Such alterations may be assayed by SEM or other analyses that allow for the determination of the porosity or other increased surface area aspects of the materials altered. Alternatively, catalytic activity may be measured directly by determining the rate at which a reaction is catalyzed by an unaltered material (e.g., platinum) versus the rate of the reaction using an altered material.Exemplary Modifications of the Optical Properties of Materials
An aspect of the invention is directed to a method for altering the optical properties of materials, including, but not limited to, metals such as are provided in Example 6 below. Thus as shown in Example 6, the materials processing methods of the present invention may be used to obtain, e.g., metals which appear to the human observer to have various shades of gray (where “gray” may alternatively be defined as a material having relatively uniform reflectance across the entire visible wavelength), including multiple shades of gray in one metal piece. These materials processing methods may additionally be used to obtain what appear to the human observer to be colored materials (where “colored” may alternatively be defined as a material having preferential reflectance in some regions of the visible spectrum and not in others), e.g., colored metals such as are also described in Example 6, and ‘black’ metal. Although these methods are applied to metals in Example 6, the present invention explicitly contemplates the application of these methods for certain non-metal materials as well.Example 1
Experiments in support of embodiments of the invention have demonstrated that a significant amount of residual thermal energy is deposited in metal samples following multi-shot femtosecond laser ablation. Traditionally, it was commonly believed that one of the most important advantages of femtosecond laser ablation is that the energy deposited by ultrashort laser pulses does not have enough time to move into the bulk sample; therefore, the residual thermal energy remaining in the bulk sample should be negligible. In contrast to this, a significant enhancement in laser light absorption was observed recently by the inventors following ablation. To understand the physical mechanisms of laser energy absorption, the change in absorptance of gold due to structural modifications following multi-shot femtosecond laser ablation was directly measured. The measured data indicates that there is a significant absorption enhancement due to nanostructuring in addition to the known mechanisms of absorption increase via micro- and macro-structuring. Moreover, nanostructuring alone may enhance the absorptance by a factor of about three. The physical mechanism of the total enhanced absorption is due to a combined effect of nano-, micro-, and macro-structural surface modifications induced by femtosecond laser ablation. At a sufficiently high fluence and with a large number of applied pulses, the absorptance of gold surface may reach an absorptance value of nearly 100%.
The absorptance A of a pure metal with a clean surface consists of two components A=AINTR+ASR, where AINTR is the intrinsic absorptance and ASR is the contribution due to surface roughness. For an optically smooth metal surface, ASR is about 1-2% of AINTR, but the role of ASR enhances as the surface roughness increases. For multi-pulse ablation, only the first femtosecond laser pulse interacts with an undamaged surface, since the laser-induced surface structural modification develops long after the ultrashort pulse. In this case, A is governed by AINTR, which can be a function of laser fluence due to laser-induced change in the dielectric constant of the material. All of the subsequent laser pulses interact with a structurally modified surface and their absorption is determined by both AINTR and ASR. The absorption of a single femtosecond laser pulse by an undamaged metal surface is dominated by AINTR. However, the coupling of laser energy to a metal in multi-pulse femtosecond laser ablation has not yet been investigated, where ASR may have a significant value due to surface structural modification.
The instant non-limiting example discusses the effect of surface structural modifications on the absorptance of gold in multi-pulse femtosecond laser ablation when an originally plane and smooth surface transforms into a blind hole. This effect is investigated as a function of the number of applied ablation pulses at various fluences. A reported calorimetry technique allows a direct measurement of laser energy absorbed by the sample. Our data indicate that femtosecond laser-induced surface modification enhances the sample absorptance, which can reach a value close to 100% at a sufficiently high fluence with a large enough number of applied pulses. Scanning electron microscope (SEM) studies show that there is absorption enhancement due to nanostructuring, which, alone was seen to enhance the absorptance by a factor of about three.
Experimentally, an amplified Ti:sapphire laser system was used to generate 60-fs pulses of about 1.5 mJ/pulse at 1 kHz repetition rate at a central wavelength of 800 nm. The laser beam was focused onto a mechanically polished sample surface with a 40-cm-focal-length lens at normal incidence. An electromechanical shutter was used to select the number of pulses, N, applied to the sample. The absorptance of the ablated spot was studied. After ablation of the sample with a chosen number of pulses, we reduced the laser fluence to a level below the ablation threshold. Subsequently, we irradiated the ablated spot again using a train of low-fluence laser pulses that would not induce any further surface modification. A certain amount of energy from this low-fluence pulse train, EA, is absorbed in the skin layer of the sample, dissipates via heat conduction in the sample, and causes a bulk temperature rise ΔT. We measured this temperature rise with a thermocouple battery that allows EA to be determined calorimetrically as EA=CΔT, where C is the known heat capacity of the sample. To measure energy EI incident upon the sample, a certain fraction of incident pulse train energy was split off by a beam splitter and measured with a joulemeter. Having measured EI and EA, the absorptance of the ablated spot could be found as A=EA/EI. Laser-induced surface modifications were then studied using a SEM and an optical microscope.
The optical properties of surface modifications were studied following multi-pulse ablation at single-pulse laser fluences of F=1.1, 0.35, 0.17, and 0.078 J/cm2 in air. The ablation threshold Fabl for a pristine surface was found to be Fabl=0.067 and 0.048 J/cm2 for single-pulse and 500-pulse train irradiation, respectively. The numbers of pulses required to perforate a 1 mm-thick sample at the center of the irradiated spot were determined to be 16,100, 25,000, and 77,000 pulses at F=1.1, 0.35, and 0.17 J/cm2, respectively. This corresponds to average ablation rates of 63, 40, and 13 nm/pulse, indicating that a single laser pulse produces a nanoscale modification in depth. Plots of absorptance versus the number of ablation shots, N, at different F are shown in
The A(N) curves for the ablated surface can be characterized into distinct regions marked with A, B, C, D, and E on A(N) in the case of F=0.17 J/cm2 in
In the second region, BC, the absorptance undergoes a slight decrease as N increases. Typically, this region covers approximately the next 100-300 pulses. Both regions AB and BC extend to a larger number of pulses when the surface is modified at F only slightly above Fabl, as seen from the curve at F=0.078 J/cm2 in
The third region, CD, is characterized by a further enhancement of absorptance with the increase of N. This region extends to N on the order of 10,000 pulses.
The fourth region, DE, was where absorptance reached a maximum value that did not change with further increase of N.
Reference is now made to the SEM pictures of surface morphology shown in
The absorption of laser energy in femtosecond laser ablation may also be altered through re-deposition of ablated material. Examination of the black halo produced around the crater shows that its elemental composition as determined by energy dispersive X-ray analysis is identical to that for a pristine surface; i.e., the black halo is a layer of the ablated and re-deposited gold. SEM images in
Since different surface modifications are superimposed on each other, it is difficult to completely isolate and determine each individual contribution to the enhanced absorptance. Therefore, we provide the following estimations on the contributions of nano-, micro-, and macro-structures induced by femtosecond laser ablation. Since surface nano-structures are the dominant feature in region AB and part of region BC for N<50-100, and the absorptance increases from 0.12 to 0.25-0.33 over these regions (see
Besides the physical mechanisms of enhanced absorption, we also make the following observations about femtosecond laser-matter interactions: First, laser-induced nanostructures alone can enhance the absorptance of Au by a factor of about three following only 1-3 pulses. This result suggests a new direction for future study of optical properties of nanostructures imprinted on a metal surface. Secondly, we produced a new type of microscale periodic structure with much finer nanoscale structures (NC-LIPSS) following ablation with a large number of applied pulses. Thirdly, re-deposition of laser-induced nanoparticles is seen outside of the ablated spot leading to the formation of a nanostructured material known as gold black. Finally, we identified potential new applications of femtosecond laser ablation for modifying optical properties of metals and producing technologically valuable surface coatings such as, but not limited to, gold-black films.Example 2
In this Example, a comparative study of residual thermal effects in aluminum following fs laser ablation was performed. At laser fluences above the ablation threshold where plasmas are produced and at a sufficiently high ambient gas pressure, an enhanced coupling of pulsed laser energy into the sample occurs. Furthermore, in contrast to the conventional understanding that residual thermal energy is negligible in fs-laser ablation, up to 70% of the incident pulse energy can be retained in the sample following single-pulse fs-laser ablation in 1-atm air. The major factors influencing thermal energy coupling to the sample are the laser fluence and ambient gas pressure. Residual thermal energy deposition decreases with reducing ambient gas pressure.
Laser ablation using femtosecond (fs) laser pulses has numerous applications in the field of materials processing and machining and, nanotechnology. Comparative studies have demonstrated that femtosecond laser ablation has advantages over nanosecond ablation in aspects of higher precision, reduced heat-affected zone, and smaller amount of debris around the ablated spot. Following laser ablation, a fraction of absorbed laser energy is retained in the heat-affected zone, dissipates into the bulk of the sample and remains inside as residual thermal energy that induces the bulk temperature of the sample to rise. This is sometimes referred to as the thermal load and is often undesirable in laser micro- and nano-machining.
The coupling of thermal energy into metals has been previously studied for microsecond and nanosecond laser ablation. An enhanced residual thermal energy coupling to metals has been observed when laser fluence is above a certain threshold value. It has been suggested that, in addition to the direct absorption of laser light, energy transfer from laser-produced plasma can contribute to residual heating. However, mechanisms responsible for thermal coupling are still not fully understood.
We have observed an enhanced residual heating of metals following multi-pulse femtosecond laser ablation, where laser-induced surface modification has been found to play a role in enhanced residual heating but, where this alone could not fully account for the observed amount of deposited thermal energy. To exclude the effect of surface modification on residual thermal response, we investigated single-pulse fs ablation. We also studied the residual thermal response of aluminum (Al) following ns-laser ablation to compare with the results for fs-laser ablation. We used a calorimetric technique to study effects of laser pulse duration, ambient gas pressure, and laser wavelength on residual heating of Al. To characterize the residual thermal response, we defined a so-called residual energy coefficient (REC) K=ER/EI, where ER is the residual thermal energy remaining in the sample following ablation and EI is the incident laser pulse energy. By definition, REC is equal to absorptance of the sample material when laser fluence is below the ablation threshold. Enhanced residual heating occurred following both single-pulse ns- and single-pulse fs-laser ablation in ambient gas at a sufficiently high pressure. The major factors governing the residual heating are laser fluence and ambient gas pressure. There is a fundamental difference between multi-pulse versus single-pulse ablation because multi-pulse ablation may induce absorptance change due to accumulated surface modifications from multiple laser shots. This accumulated effect does not occur in single-pulse ablation.
Both ns and fs duration pulse effects were examined. The following three laser systems were used: 1) a ruby laser producing 45-ns pulses (FWHM) at wavelength λ=0.69 μm with pulse energy of 0.6 J; 2) a Nd:YAG laser generating 55-ns pulses at λ=1.06 μm with pulse energy of 1.4 J; and, 3) a Ti:sapphire laser producing 60-fs pulses at λ=0.8 μm with pulse energy of 1.5 mJ. Using each laser system, the laser beam was focused onto an Al sample at normal incidence. A fraction of the incident pulse energy EI was split off using a beamsplitter and measured with a joulemeter to allow EI to be determined.
The residual energy ER that remains in the sample following ablation causes the bulk temperature of the sample to rise by ΔT. Using a thermocouple attached to the Al sample, ΔT was measured after thermal equilibrium was reached in the sample. Knowing the specific heat capacity cp and the mass m of the sample, the residual energy can be obtained from ER=mcpΔT. The thermocouple response time (the time required for achieving a maximum thermocouple signal in our calorimeter) was about 2.5 sec. Using measured EI and ER, the residual thermal energy coefficient K=ER/EI can be found as a function of single-pulse laser fluence F=EI/S, where S is the laser beam area on the sample. The samples were mechanically polished. Measurements were performed in various ambient gases and at different pressures. The sample was translated with an X-Y stage so each subsequent laser pulse was incident on a fresh spot. Two parameters, the ablation threshold Fabl and the plasma ignition threshold Fpl, were determined at the onset of surface damage visible to eye with subsequent examination under a scanning electron microscope (SEM). Fpl was determined by observing the onset of bright violet radiation from the irradiated spot using either a photomultiplier (PMT) or an open-shutter camera, both properly filtered to cut off scattered laser light.
Although embodiments of the invention are directed to fs-duration laser pulses, this Example probes some of the effects of both fs- and ns-duration laser pulses. The dependence of REC on laser fluence F following single-pulse ns-laser ablation in various ambient gases under different pressures on Al are plotted in
Next, we studied the pressure effect on REC; representative curves are plotted in
In vacuum, the laser plasma mainly consists of ionized species of ejected material, while in a gas medium, plasma consists of ionized species of both ablated material and ambient gas. A characteristic feature of ambient gas plasma produced by ns pulses is that the plasma expands due to the generation of laser-supported absorption waves.
The direct absorption of laser energy is a factor that may influence residual heating. According to the Drude model, when the temperature increases material absorptivity should also increase due to an enhanced collision frequency between free electrons and thermally vibrating lattice atoms. Therefore, one should expect an increase in REC with laser fluence due to this enhancement of material absorptivity. However, the fact that REC increases in air while it decreases in vacuum above a certain laser fluence indicates that the temperature-enhanced Drude absorption does not play an essential role in enhanced residual thermal response. This is also confirmed by our estimation of the laser-induced surface temperature using the following formula:
where A is the absorptance, a is the thermal diffusivity, I is the intensity of incident laser light, k is the thermal conductivity, t is the time, T0 is the initial temperature, and θ is the integration variable.
The similar general behavior of REC for Nd:YAG (λ=1.06 μm) and ruby (λ=0.69 μm) lasers shows that laser wavelength is relatively unimportant in the visible and near infrared spectral region. Nevertheless, our experiment clearly demonstrates that REC of the aluminum sample depends mainly on laser fluence and ambient gas pressure following ns-laser ablation.
The dependence of REC on laser fluence for Al following fs-laser ablation in 1-atm air and in vacuum (P=0.01 torr) are plotted in
There are three basic distinctions between ns- and fs-laser ablation. First, fs-laser pulses do not interact with ejected material because hydrodynamic expansion of ablated material from the irradiated area occurs on a timescale much longer than femtosecond pulse duration. Secondly, laser-supported absorption waves that are commonly generated in ns-laser ablation in a gas medium do not exist in fs-laser ablation. Thirdly, a material irradiated with an intense fs-laser pulse can be heated to a solid-density plasma state.Example 3
Unique properties of nanomaterials have been extensively studied in the past and various nanostructures have found numerous applications in optics including enhanced x-ray emission and enhanced absorption in intense light-matter interaction, and optical biosensing, to name a few. Direct surface nanostructuring (i.e., not from ablated plume deposition) may be used in a number of technological applications, for example, manipulation of optical properties of solids, catalysts, dental implants, etc. We performed a detailed study of the morphology of surface nanomodifications produced on bulk metals using a femtosecond laser ablation technique embodied herein. The effects of laser fluence and number of applied pulses on the generated surface nanostructures were studied with a scanning electron microscope (SEM). According to an aspect, a set of optimal laser irradiation conditions for metal surface nanostructuring is disclosed.
In our experiment, we used an amplified Ti:sapphire laser system that consisted of a mode-locked oscillator and a two-stage amplifier including a regenerative amplifier and a two-pass power amplifier. The laser system produces 65-fs pulses with energy around 1 mJ/pulse at a 1 kHz repetition rate with a central wavelength λ=800 nm. To produce ablation, the laser beam is focused normally onto a bulk sample mounted vertically. To measure the incident pulse energy, a certain fraction of the incident light is split off by a beam splitter and measured with a pyroelectric joulemeter. The number of laser shots, N, applied to the sample is controlled using an electromechanical shutter. All experiments were performed in air under atmospheric pressure. The morphology of femtosecond laser-induced surface modifications was studied using a SEM. The studied samples were mechanically polished copper, gold, and platinum. The range of laser fluence used in the ablation was between 0.084 and 9.6 J/cm2. The number of applied pulses was varied from 1 to 5×104 shots. The ablation threshold was determined as the minimum fluence to generate a surface damage seen under the SEM.
A SEM picture of a copper sample surface prior to laser irradiation is shown in
The effect of laser fluence on surface structuring can be seen from analyzing the surface modifications produced at various F and fixed N as shown for example in
To determine the mechanism of nanostructuring, we performed a SEM study on the origin of nanoscale modifications. A representative example of nascent nanostructures following ablation with F=0.35 J/cm2 and N=1 is shown in
Laser-induced periodic surface structures (LIPSS) on solids have been studied in a number of works in the past. Typically, LIPSS show regular groove structure with a period on the incident laser wavelength scale and oriented perpendicularly to the polarization of the incident light. LIPSS are commonly seen following long pulse irradiation on a variety of materials, including semiconductors, metals, and dielectrics.
In contrast to previous work performed mostly at relatively high fluence, we studied the formation of LIPSS on platinum and gold in a special fluence regime, namely, at near damage-threshold fluence. We found a unique type of LIPS S entirely covered with nanostructures. A distinctive feature of the nanostructure-covered LIPSS (NC-LIPSS) is that its period is appreciably less than that of the regular LIPSS whose period is approximately equal to the laser wavelength at normal incident laser light. The reduced period of the nanostructure-covered LIPSS is caused by a significant increase of the real part of the effective refractive index of the air-metal interface when nanostructures develop on a metal surface that affects the propagation of excited surface plasmon polaritons. Nanostructure-covered LIPSS has a variety of potential applications, such as modifying optical properties of materials and chemical catalysts where high surface-to-volume ratio is a crucial factor.
In this experiment, we used an amplified Ti:sapphire laser system that generates 65-fs laser pulses with energy about 1 mJ/pulse at a 1 kHz repetition rate and with a central wavelength λ=0.8 μm. The horizontally-polarized laser beam is focused onto a vertically standing metal sample in air at normal incidence. The number of laser shots, N, applied to the sample is selected with an electromechanical shutter. We studied the evolution of NC-LIPSS on metals following irradiation with N=1, 2, 4, 8, 10, 20, 30, 40, 50, 100, 200, 300, 400, 500 pulses at near damage-threshold fluence. The studied metals were platinum and gold. The laser fluence of the incident light was varied by changing the distance between the focusing lens and sample. To measure the laser pulse energy incident upon the sample, a fraction of the incident laser beam is split off by a beamsplitter and diverted to a pyroelectric joulemeter. The morphology of the produced periodic structures is examined using a scanning electron microscope (SEM). The surface profile is measured with an atomic force microscope (AFM). All sample surfaces were mechanically polished using 0.1 μm grade aluminum oxide powder.
The evolution of surface structures produced on Pt following ablation at near damage-threshold laser fluence of F=0.16 J/cm2 is shown in
The periodic patterns induced by femtosecond laser processing are distinctly different from those produced by longer pulses in two aspects. First, femtosecond laser-induced periodic structures are covered by random nanostructures. Secondly, the LIPSS period induced by femtosecond pulses at normal incidence is appreciably less than the laser wavelength while the period is roughly equal to the wavelength for longer pulses. To account for our observation, we carefully examined the evolution of surface structural modifications on both Pt and Au, and we propose the following mechanism for the formation of NC-LIPSS. The first few laser shots usually produce sparsely and randomly distributed nanostructures. It is known that surface plasmons, both localized and propagating along a surface, can be excited by coupling laser energy into nanostructures. With further increase of the number of laser shots, more nanostructures appear allowing excitation of more localized and propagating surface plasmons. The produced nanoroughness includes nanorods, nanocones, and nanospheres, and these nanostructures will excite propagating cylindrical surface plasmons that subsequently interfere with the incident light. This interference causes the formation of intermediate periodic surface microstructures. As the number of laser shots increases, the intermediate microstructures will grow as well as the area occupied by these structures. The developed intermediate periodic surface microstructures will further excite propagating plane surface plasmons that interfere with the plane incident laser light wave, and this interference will finally result in the permanent extended periodic microstructures.
For normally incident linearly polarized light, the period d of the surface grating formed due to the interference between the incident laser light and the excited surface plasmon wave is given by equation 1 as:
with g|E, where λ is the incident light wavelength, η=Re[∈/(∈+1)]1/2 is the real part of the effective refractive index of the air-metal interface for surface plasmons, ∈ is the dielectric constant of the metal, g is the grating vector, and E is the electrical field vector of the incident wave. For a plane vacuum-metal interface, η is calculated to be 1.0096 at λ=800 nm for Pt (∈1=−15.5 and ∈2=23.5) and 1.022 for Au (∈1=−23.4, ∈2=1.55). Using Eq. (1), the grating period is found to be 0.79 μm for Pt and 0.78 μm for Au. However, the observed period is 0.61 μm for Pt (
Under certain conditions we also produced a large number of nanoprotrusions and nanocavities on a metal surface (see
In this study we performed a femtosecond laser surface treatment of titanium to help determine the potential of this technology for surface structuring of titanium implants. We found find that femtosecond laser processing produces a large variety of nanostructures (nanopores, nanoprotrusions) with a size down to 20 nm, multiple parallel grooved surface patterns with a period on the sub-micron level, microroughness in the range of 1-15 μm with various configurations, smooth surface with smooth micro-inhomogeneities, and smooth surface with sphere-like nanostructures down to 10 nm. Also, we have determined the optimal conditions for producing these surface structural modifications. Femtosecond laser treatment may produce a richer variety of surface structures on titanium for implants and other biomedical applications than long-pulse laser treatments.
Due to good biostability, biocompatibility, mechanical performance, and long-term durability, titanium has been widely used in a variety of biomedical applications such as dental and orthopedic implants, and implantable electronic devices. In numerous in vitro and in vivo studies, surface topography of titanium implants has been shown to be important in enhancing implant performance. It has been shown that both microstructures and nanostructures influence biological processes at implant interfaces. Various methods of implant surface structuring have been studied in the past such as grit-blasting, chemical etching, laser treatment, and the combinations of the various methods. Recent studies have shown that laser processing of implant surfaces provides both suitable surface topography and less surface contamination as compared with other methods. Another advantage of laser processing is that the technique is also suitable for texturing of implants of more complicated shapes. In the past, surface structures have been produced using long-pulse lasers, including nanosecond Nd:YAG laser, copper vapor laser, nanosecond excimer lasers, picosecond Nd:YAG laser, and sub-picosecond excimer laser. Femtosecond lasers have advantages over nanosecond lasers in aspects of higher precision, reduced heat-affected zone, and smaller amount of debris around the ablated spot.
The effects of laser fluence and the number of applied pulses on laser-induced surface topography in titanium are reported herein. We found that a femtosecond laser produces a large variety of nanostructures (nanopores, nanoprotrusions) with a size down to 20 nm, multiple parallel grooved surface patterns with a period on the sub-micron level, microroughness in the range of 1-15 μm with various configurations, smooth surface with smooth micro-inhomogeneities, and smooth surface with sphere-like nanostructures down to 10 nm. Our results suggest that femtosecond laser treatment can produce a richer variety of surface structures on titanium for implants and other biomedical applications than long-pulse laser treatments.
Commercially pure titanium flat plates with a dimension of 15×17×1.5 mm were used in our experiment. The plates were mechanically polished using 0.1-μm-grade aluminum oxide powder and further cleaned with acetone. For surface texturing, we used an amplified Ti:sapphire laser system that generates 65-fs laser pulses with the pulse energy over 1 mJ at a 1 kHz repetition rate with a central wavelength of 0.8 μm. The laser beam is horizontally polarized and was focused at normal incidence onto a vertically standing titanium sample in air at a pressure of 1 atm. For laser beam focusing, we used an achromatic lens with a focal length of 20 cm. The laser fluence of the incident light was varied by changing the distance between the focusing lens and the sample. The diameter of laser-irradiated spots on the titanium sample was varied from 100 to 1200 μm. The number of laser shots, N, applied to the sample was selected with an electromechanical shutter. The surface structuring of titanium was studied following the treatment with laser fluence of F=0.067, 0.084, 0.16, 0.35, 0.48, and 2.9 J/cm2 and the number of applied pulses, N, in the range of 1-30,000. Following femtosecond laser treatment, the topography of surface modifications was studied using a SEM.
As a reference,
It has been shown that implant surface topography is an important factor affecting the behaviors of both proteins and cells on implant surfaces. It is generally accepted that proteins typically respond to surface structural features (pits, pillars, steps) about 1-10 nm, while cells can be sensitive to structural features on the scale of 15 nm-100 μm. It was also found that structured implants have a better mechanical interlocking of the bone-implant interfaces than smooth implant surfaces due to an increased surface area. Also, it has been reported that extended parallel groove structures may cause cells to align and migrate along the grooves, a contact guidance phenomenon. Our SEM study shows that all of these types of surface textures can be produced by femtosecond laser treatment.
Little work has been done on laser fabrication of surface nanostructures on titanium. Our study shows that femtosecond laser technique can produce a large variety of both pure nanostructures (
Examination of shot-to-shot SEM images of surface topography suggests the following mechanism for the formation of nanostructures of the first type. It is seen from
Mechanisms for the formation of nanostructures of the second type cannot be straightforwardly derived from our SEM study. The formation of these nanostructural features may be due to redeposition of ablated nanoparticles back onto the irradiated surface.
Multiple parallel grooved surface patterns for biomedical applications are commonly produced using lithographic or laser holographic techniques. However, fabrication of these type of patterns on biomaterials using a single laser beam has not been reported. Below we discuss the optimal conditions for producing these structures and explain the physical mechanisms of their formation.
Our study shows that optimal conditions for producing periodic groove patterns on titanium are at near-damage-threshold fluence and with the laser shot number in the range between 20 and 800. In the past, multiple parallel grooved surface patterns have been produced by long-pulse lasers and are known as laser-induced periodic surface structures (LIPSS). The formation of LIPSS on metals is believed to result from the interference of the incident laser light with the excited surface plasmon polaritons that result in spatial periodic energy distribution on the surface. Usually, LIPSS shows a regular groove structure with a period on the incident laser wavelength scale and is oriented perpendicularly to the polarization of the incident light. Our results of the evolution of surface structural modifications on titanium suggest the following mechanism for the formation of the observed LIPSS. In our experiment, the first few laser shots produce sparsely and randomly distributed nanostructures. It is known that propagating cylindrical surface plasmons can be excited by coupling laser energy into nanoroughness, and this can give rise to their interference with the incident light. This interference will, first, cause the formation of intermediate periodic surface structures in localized areas of the irradiated spot. An example of such intermediate periodic surface structure can be seen in
For linearly polarized incident laser light, the period d of the surface grating formed due to the interference between the incident laser light wave and the excited surface plasmon wave is given by d=λ/(η±sin θ) with g|E, where in this equation λ is the incident light wavelength, η=Re[∈/(∈+1)1/2 is the real part of the effective refractive index of the air-metal interface for surface plasmons, E is the dielectric constant of the metal, θ is the laser light incidence angle, g is the grating vector, and E is the electrical field vector of the incident wave. The above equation shows that the period of laser-fabricated grating can be varied by changing the laser wavelength, the incidence angle, or the real part of the effective refractive index. An important parameter affecting the cell behavior is known to be groove depth, and this parameter in fabricating LIPSS can be controlled by the number of applied laser shots.
A unique feature of the periodic groove structures produced according to the embodiments herein is that both ridges and grooves are covered with nanoroughness following femtosecond laser treatment, in contrast to rectangular surface grooves fabricated using lithography techniques that usually have smooth ridges and rough floors.
Laser microtexturing of titanium has been studied in the past using long-pulse lasers. It has been shown that laser processing of implant surfaces provides both suitable surface microstructures and the least surface contamination as compared with other methods. As shown in
Some parts of implant surfaces may be required to be smooth. Previously, nanosecond excimer lasers have been used for polishing machined titanium implants, and effects of both polishing and cleaning of the surfaces have been reported). Our study shows that smoothed surface can be also obtained with femtosecond laser treatment, as shown in
It is known that open pores with a diameter in the range of 100-400 μm can improve the strength of bone-implant interfaces. Recently, long-pulse lasers have been used for fabricating 100-300 μm pores on Ti6Al4V implants. Our study shows that pores of this size can be produced with femtosecond laser treatment, as shown in
Another application of femtosecond laser surface structuring to produce the materials processing of the presently embodied invention is to provide the controllable modification of the optical properties of metals, where these optical properties range from the UV to THz spectral range, and where the modifications may be used to create various black, grayed, and colored metals.
As an example,
By varying the materials processing parameters, we have also produced aluminum that appears to be various shades of gray. Thus in the case of the grayed aluminum as shown in
In addition to producing various shades of gray as discussed above, the materials processing methods of the present invention can also produce colored metals; i.e., metals that appear to have a particular color or that appear to have multiple colors.
To produce colored metals, two types of femtosecond laser processing techniques were performed. The first technique involved tailoring laser-induced surface random structures, while the second technique produced femtosecond laser-induced periodic surface structures (FLIPSS). The colored metals produced by the first technique exhibit the same apparent color at various viewing angles, while the colored metals produced by the second technique exhibit different colors at different viewing angles due to a grating effect.
Colored metals produced by the second technique, FLIPSS, exhibit different colors at different viewing angles.
Given the additional advantages of laser processing such as low contamination and capability to process complicated shapes, the black, grayed, and colored metals created by femtosecond laser surface structuring have numerous potential applications in such areas including, but not limited to, photonics, plasmonics, optoelectronics, stealth technology, thermal radiation sources, solar cell absorbers, radiative heat transfer devices, infrared sensing, biooptical devices, thermophotovoltaics, and airborne/space borne devices.
While specific embodiments of the present invention have been described herein, it will be appreciated by those skilled in the art that many equivalents, modifications, substitutions, and variations may be made thereto without departing from the spirit and scope of the invention as defined in the appended claims.
1. A surface-structured metal, comprising:
- a base metal having at least one of a femtosecond laser pulse-induced nanostructured surface and a nanostructure-covered laser-induced periodic surface structure (NC-LIPSS).
2. The surface-structured metal of claim 1, wherein the nanostructure-covered laser-induced periodic surface structure has a period that is less than a period of a non-nanostructure-covered laser-induced periodic surface structure (LIPSSs) in the metal surface.
3. The surface-structured metal of claim 1, wherein the base metal has a polished surface.
4. The surface-structured metal of claim 1, wherein the base metal includes substantially any metal and metal alloy.
5. The surface-structured metal of claim 1, wherein the base metal is one of aluminum, gold, titanium, copper, platinum, tungsten, silver, titanium alloy, aluminum alloy, brass, and stainless steel.
6. The surface-structured metal of claim 1, wherein the surface-structured metal has a colored appearance.
7. The surface-structured metal of claim 6, wherein the surface-structured metal has at least one of a black color, a blue color, a gold color, a yellow color, a gray color, a red color, and a combination thereof.
8. The surface-structured metal of claim 6, wherein the surface-structured metal has an iridescence.
9. The surface-structured metal of claim 1, wherein the base metal is aluminum and the color is black.
10. The surface-structured metal of claim 1, wherein the base metal is aluminum and the color is gold.
11. The surface-structured metal of claim 1, wherein the base metal is titanium and the color is blue.
12. The surface-structured metal of claim 1, wherein the base metal is platinum and the color is gold.
13. The surface-structured metal of claim 6, having a color that changes as a function of viewing angle.
14. The surface-structured metal of claim 6, having a color that is substantially constant as a function of viewing angle.
15. The surface-structured metal of claim 1, having an absorptance equal to or greater than 0.8 for a wavelength that is equal to or greater than about 200 nanometers.
16. The surface-structured metal of claim 1, having an absorptance equal to or greater than 0.2 for a wavelength that is equal to or greater than about 50 micrometers.
17. The surface-structured metal of claim 1, having an absorptance equal to or greater than 0.9.
18. The surface-structured metal of claim 1, having an absorptance equal to or greater than 0.5, wherein the base metal has an absorptance substantially less than 0.5 at normal incidence.
19. The surface-structured metal of claim 1, wherein the surface structure further includes a plurality of microscale aggregates.
20. The surface-structured metal of claim 19, wherein the microscale aggregates further comprise at least one of micropores, microgrooves, and microchannels.
21. The surface-structured metal of claim 19, wherein the surface structure further includes a periodic plurality of elongate grooves.
22. The surface-structured metal of claim 1, wherein the surface structure comprises a plurality of nanobranches.
23. The surface-structured metal of claim 22, wherein the surface structure further comprises a plurality of spherical nanoparticles.
24. The surface-structured metal of claim 1, wherein the surface structure comprises nanostructures having a shape of nanovoids.
25. The surface-structured metal of claim 1, wherein the surface structure comprises redeposited nanoparticles of ablated base metal.
26. The surface-structured metal of claim 1, wherein the base metal is a bulk metal.
27. The surface-structured metal of claim 1, wherein the base metal is a thin film.
28. A surface-structured metal having an induced absorptance that is equal to or greater than 0.8 for a wavelength that is equal to or greater than about 200 nanometers.
29. The surface-structured metal of claim 28, comprising an induced nanostructure in a surface of the metal.
30. The surface-structured metal of claim 28, comprising substantially any metal and metal alloy.
31. The surface-structured metal of claim 29, wherein the induced nanostructure is a nanostructure-covered laser-induced periodic surface structures (NC-LIPSS).
32. The surface-structured metal of claim 29, wherein the induced nanostructure comprises a plurality of nanobranches.
33. The surface-structured metal of claim 32, wherein the induced nanostructure further comprises a plurality of spherical nanoparticles.
34. The surface-structured metal of claim 28, wherein the metal is a bulk metal.
35. The surface-structured metal of claim 28, wherein the metal is a thin film.
36. A method for treating a base metal, comprising:
- exposing a surface region of the base metal to a femtosecond duration laser pulse having a fluence, F, that is sufficient to alter a surface structure of the base metal; and
- altering the surface structure of the base metal by creating a nanostructure in the surface.
37. The method of claim 36, comprising exposing the surface region of the base metal to a single femtosecond duration laser pulse.
38. The method of claim 36, comprising creating a plurality of nanobranch structures.
39. The method of claim 38, further comprising creating a plurality of spherical nanoparticle structures.
40. The method of claim 38, further comprising creating a plurality of nanovoids.
41. The method of claim 38, further comprising creating surface microstructures.
42. The method of claim 36, further comprising creating at least one of micropores, arcuate microgrooves, and central microchannels.
43. The method of claim 36, comprising creating a plurality of nano-covered laser-induced periodic surface structures (NC-LIPSSs).
44. The method of claim 43, further comprising creating a plurality of surface macrostructures.
45. The method of claim 44, comprising scanning a femtosecond duration pulsed laser beam across the surface of the base metal at a selected velocity.
46. The method of claim 45, comprising creating a periodic plurality of grooves.
47. The method of claim 46, wherein the periodic plurality of grooves has a period equal to a translation step between two adjacent laser scanning lines.
48. The method of claim 36, further comprising ablating material from a region of the surface and redepositing the ablated material on the surface.
49. The method of claim 37, comprising exposing the surface region of the base metal to between 1-10 additional femtosecond duration laser pulses.
50. The method of claim 49, comprising exposing the surface region of the base metal to between 10-100 additional femtosecond duration laser pulses.
51. The method of claim 50, comprising exposing the surface region of the base metal to between 100-300 additional femtosecond duration laser pulses.
52. The method of claim 51, comprising exposing the surface region of the base metal to greater than 300 additional femtosecond duration laser pulses.
53. The method of claim 44, wherein the NC-LIPSS has a period, d, that is less than the laser wavelength, λ.
54. The method of claim 53, comprising controlling the period of the NC-LIPSS by controlling at least one of λ, the incidence angle, θ, and the real part of the effective refractive index of an air-metal interface, η, according to the equation d=λ/(η±sin θ).
55. The method of claim 36, comprising polishing the base metal surface prior to exposing the surface to the femtosecond duration laser pulse.
International Classification: B32B 3/02 (20060101); B23K 26/38 (20060101);