HYDROGENATION OF ESTERS WITH RU/BIDENTATE LIGANDS COMPLEXES

Abstract

The present invention relates to the field of catalytic hydrogenation and, more particularly, to the use of Ru complexes with bidentate ligands, having one amino or imino coordinating group and one phosphino coordinating group, in hydrogenation processes for the reduction of esters or lactones into the corresponding alcohol or diol respectively.

Description

CROSS-REFERENCE TO RELATED APPLICATION(S)

This application is a division of application Ser. No. 11/854,106 filed Sep. 12, 2007, which is a continuation of International application PCT/IB2006/051027 filed on Apr. 4, 2006, the entire content of each of which is expressly incorporated herein by reference thereto.

TECHNICAL FIELD

The present invention relates to the field of catalytic hydrogenation and, more particularly, to the use of Ru complexes with bidentate ligands, in hydrogenation processes for the reduction of esters or lactones into the corresponding alcohol or diol respectively.

BACKGROUND

Reduction of an ester functional group to the corresponding alcohol is one of the fundamental reactions in organic chemistry, and is used in a large number of chemical processes. In general, two main types of processes are known to achieve such a transformation. Such types of processes are the following:

a) hydride processes, in which a silyl or metal hydride salt, such as LiAlH₄, is used;
b) hydrogenation processes, in which molecular hydrogen is used.

From a practical point of view, hydrogenation processes are more attractive as they can be run using small amounts of catalyst (typically 10 to 1000 ppm relative to the substrate) and in the presence of small quantities or even in the absence of solvent. Furthermore, hydrogenation processes do not require the use of highly reactive and expensive hydrides, and do not produce important amounts of aqueous waste.

One of the mandatory and characterizing elements of hydrogenation processes is the catalyst or the catalytic system which is used to activate the molecular hydrogen in view of the reduction. The development of useful catalysts or catalytic systems for the hydrogenation of an ester functional group represents still an important need in chemistry.

Amongst the few catalysts or catalytic systems known to perform such reductions one may cite the ruthenium/phosphine complexes, obtained by the reaction of ruthenium oxide or carboxylate precursor with a mono-, di- or tri-phosphine ligand (an example of which is described by Elsevier et al. in Chem. Commun., 1998, 1367). In this type of complex the ruthenium metal is coordinated only by “acac” ligands and phosphine atoms, limiting thus the diversity of the ligand structure and coordination sphere around the metal center. As a consequence of such little diversity the tuning of the activity and of the performance of the hydrogenation process is not easy. Furthermore, the experimental conditions require very high pressures (at least 70-130 bars) and temperatures (120-180° C.).

Therefore, there is a need for hydrogenation processes using alternative catalysts or pre-catalysts, preferably having a greater diversity in the ligand structures and coordination spheres around the metal center and allowing the use of softer experimental conditions.

SUMMARY OF THE INVENTION

The present invention now relates about a hydrogenation process for the reduction of esters, or the like, into alcohols in the presence of a base and at least one complex in the form of a ruthenium complex of a bidentate ligand wherein the coordinating groups consist of one amino or imino group and one phosphino group. The invention relates also about new ligands and complexes useful for carrying the invention process.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

In order to overcome the problems aforementioned, the present invention relates to processes for the reduction by hydrogenation, using molecular H₂, of a C₃-C₇₀ substrate containing one or two esters, or lactones, functional groups into the corresponding alcohol, or diol, characterized in that the process is carried out in the presence of a base and at least one catalyst or pre-catalyst in the form of a ruthenium complex of a bidentate ligand wherein the coordinating groups consist of one amino or imino group and one phosphino group.

According to an embodiment of the invention, the amino group is a primary (i.e. NH₂) or a secondary (i.e. NH) amino group.

According to a particular embodiment of the invention, the substrate can be a compound of formula (I)

wherein R^a and R^b represent, simultaneously or independently, a linear, branched or cyclic C₁-C₃₀ aromatic, alkyl or alkenyl group, optionally substituted; or
R^a and R^b are bonded together and form a C₄-C₂₀ saturated or unsaturated group, optionally substituted.

The corresponding alcohols (i.e., (II-a) and (II-b)), or the corresponding diol (II′), of the substrate (I), are of formula

wherein R^a and R^b are defined as in formula (I).

A compound of formula (II) (i.e. II-a or II-b) will be obtained in the case where R^a and R^b are not bonded together, while a compound of formula (II′) will be obtained in the case where R^a and R^b are bonded together.

It is understood that by “a linear, branched or cyclic . . . aromatic, alkyl, or alkenyl group” it is meant that the R^a or R^b can be in the form of, e.g., a linear alkyl group or can also be in the form of a mixture of the type of groups, e.g. a specific R^a may comprise a linear alkyl, a branched alkenyl, a (poly)cyclic alkyl and an aryl moiety, unless a specific limitation to only one type is mentioned. Similarly, in all the below embodiments of the invention when a group is mentioned as being in the form of more than one type of topology (e.g. linear, cyclic or branched) and/or unsaturation (e.g. alkyl, aromatic or alkenyle) it is meant also a group which may comprise moieties having any one of the topologies or unsaturations, as above explained.

A particular embodiment of the invention's process is shown in Scheme 1:

According to a further embodiment of the invention, the substrate is an ester, or lactone, that will provide an alcohol, or a diol, that is useful in the pharmaceutical, agrochemical or perfumery industry as final product or as an intermediate. Particularly preferred substrate is an ester, or lactone, that will provide an alcohol, or diol, which is useful in the perfumery industry as final product or as an intermediate.

According to another embodiment of the invention, the substrate is a C₅-C₃₀ compound of formula (I), and in particular one may cite those wherein R^a and R^b represent simultaneously or independently a linear, branched or cyclic C₁-C₃₀ aromatic or alkyl group optionally substituted, or a cyclic C₅-C₃₀ alkenyl group optionally substituted; or R^a and R^b are bonded together and form a C₄-C₂₀ saturated or unsaturated linear, branched, mono-, di- or tri-cyclic group, optionally substituted.

According to a further embodiment of the invention the substrate is a C₅-C₂₀ compound of formula (I), wherein R^a and R^b represent simultaneously or independently a linear, branched or cyclic C₅-C₁₈ aromatic or alkyl group, optionally substituted, or a cyclic C₅-C₁₈ alkenyl group, optionally substituted; or R^a and R^b are bonded together and form a C₄-C₂₀ saturated or unsaturated linear, branched, mono-, di- or tri-cyclic group, optionally substituted.

Furthermore, according to a yet further embodiment, when R^a and/or R^b represent an alkenyl group then the carbon-carbon double bond is not terminal and is not conjugated.

Possible substituents of R^a and R^b are one, two or three halogen, OR NR^c₂ or R^c groups, in which R^c is a hydrogen atom, a halogenated C₁-C₂ group or a C₁ to C₁₀ cyclic, linear or branched alkyl, or alkenyl group, preferably a C₁ to C₄ linear or branched alkyl or alkenyl group. As other possible substituents one may also cite a group COOR^c, which can also be reduced to the corresponding alcohol during the invention's process, according to the molar amount of H₂ used, as well known by a person skilled in the art.

Non-limiting examples of substrates are alkyl cinnamates, sorbates or salycilates, alkyl esters of natural (fatty or not) acids, Sclareolide, spirolactones, allylic ester, di alkyl diesters, (un)substituted benzoic esters, and β-γ unsaturated esters. In particular, the substrate can be selected from the group consisting of sclareolide, C₉-C₁₅ spirolactones and C₁-C₄ alkyl esters of 4-methyl-6-(2,6,6-trimethyl-1-cyclohexen-1-yl)-3-hexenoic acid. One can also cite the di alkyl esters of 1,4-dicarboxylate-cyclohexane, the di C_1-5 alkyl esters of the C_2-10 alkanediyl-dicarboxylates, C_1-5 alkyl cyclopropanecarboxylates, mono-, di- or tri-methoxybenzoic esters.

The process of the invention is characterized by the use, as catalyst or pre-catalyst (hereinafter referred to as complexes unless specified otherwise), of a ruthenium complex as described above. The complex can be in the form of an ionic or neutral species.

According to an embodiment of the invention, the ruthenium complex can be of the general formula

[Ru(L2)_b(L′)_aY₂]  (1)

wherein L2 represents a bidentate ligand wherein the coordinating groups consist of one amino or imino group and one phosphino group;
L′ represents a C₃-C₇₀ mono-phosphine (L1-P) or a molecule of solvent (L1-S);
b is 1 and a is 1 or 2 or b is 2 and a is 0; and
each Y represents, simultaneously or independently, CO, a hydrogen or halogen atom, a hydroxyl group, or a C₁-C₆ alkoxy or carboxylic radical. Alternatively, Y may also represent a BH₄ or AlH₄ group.

In a particular embodiment of the invention the L2 ligand may be a C₄-C₄₀ compound.

In a particular embodiment of the invention, in formula (1), each Y represents, simultaneously or independently, a hydrogen or chlorine atom, a hydroxy radical, a C₁ to C₆ alkoxy radical, such as a methoxy, ethoxy or isopropoxy radical, or a C₁ to C₆ acyloxy radical such as a CH₃COO or CH₃CH₂COO radical. More preferably, each Y represents, simultaneously or independently, a hydrogen or chlorine atom, a methoxy, ethoxy or isopropoxy radical, or a CH₃COO or CH₃CH₂COO radical.

Y may also be a solvent, the term “solvent” has to be understood according to the usual meaning in the art and includes compounds used as diluent in the preparation of the complex or during the invention's process, non limiting examples are dimethylsulfoxide, acetonitrile, dimethylformamide, an alcohol (e.g. an C₁-C₄ alcohol), or also THF, acetone, pyridine or a C₃-C₈ ester or the substrate of the invention's process.

According to a particular embodiment of the invention, there can be used as complex a compound of one of the formulae

[(L2)₂Y₂]  (2)

[(L2)(L1-P)_c(L1-S)_2-c′Y₂]  (2′)

wherein L2 and Y have the meaning indicated above, c is 1 or 2, and c′ is 0, 1 or 2.

The complexes of formula (2) represent a preferred embodiment of the invention.

According to any one of the above-mentioned embodiment, the bidentate ligand L2 can be a compound of one of the formulae

wherein the dotted line indicates a single or double bond;
z is 0 or 1 when the carbon-nitrogen bond with the dotted line represents a single or double bond respectively;
R¹ represents a hydrogen atom, a linear, branched or cyclic C₁ to C₁₀ alkyl or alkenyl group optionally substituted;
R^1′ and R^1″, when taken separately, represents a hydrogen atom, a linear, branched or cyclic C₁ to C₉ alkyl or alkenyl group optionally substituted or a C₆ to C₁₀ aromatic group optionally substituted; the R^1′ or R^1″, when taken together, form a saturated or unsaturated ring optionally substituted, having 5 to 12 atoms and including the carbon atom to which the R^1′ and R^1″ groups are bonded;
R² and R³, when taken separately, represent, simultaneously or independently, a linear, branched or cyclic C₁ to C₈ alkyl or alkenyl group optionally substituted, a C₆ to C₁₀ aromatic group optionally substituted, or an OR^2′ or NR^2′R^3′ group, R^2′ and R^3′ being a C₁ to C₈ alkyl or alkenyl group; the groups R² and R³, when taken together, may form a saturated or unsaturated ring optionally substituted, having 5 to 10 atoms and including the phosphorus atom to which the R² and R³ groups are bonded;
R⁶ and R⁷ represent, simultaneously or independently, a hydrogen atom, a linear, branched or cyclic C₁ to C₁₀ alkyl or alkenyl group optionally substituted, a C₆-C₁₀ aromatic group optionally substituted, or an OR^4′ or NR^4′R^5′ group, R^4′ and R^5′ being a linear, branched or cyclic C₁ to C₁₀ alkyl or alkenyl group; R⁶ and R¹ or R⁶ and R^1″, taken together, may form a saturated or unsaturated heterocycle, optionally substituted and optionally containing one or two additional nitrogen or oxygen atoms, containing 5 to 10 atoms and including the carbon atoms and the N atom to which the R⁶ or R¹, or R^1″, group are bonded respectively; and
Q represents:

• • a group of formula

• • wherein n is an integer from 1 to 4, and
  • R⁴ and R⁵ represent, simultaneously or independently, a hydrogen atom, a linear, branched or cyclic C₁ to C₁₀ alkyl or alkenyl group optionally substituted, a C₆-C₁₀ aromatic group optionally substituted, or an OR^4′ or NR^4′R^5′ group, R^4′ and R^5′ being a linear, branched or cyclic C₁ to C₁₀ alkyl or alkenyl group; two distinct R⁴ and/or R⁵ groups, taken together, may form a C₅ to C₈, or even up to C₁₀, saturated ring optionally substituted, including the carbon atoms to which each of the R⁴ or R⁵ group is bonded; or
  • a group of formula

• • wherein n is an integer from 2 to 4, and
  • two distinct adjacent R⁴ groups, taken together, form a C₅ to C₈, or even up to C₁₀, aromatic ring optionally substituted or a C₅-C₁₂ metallocenediyl optionally substituted, including the carbon atoms to which each of the R⁴ group are bonded; or
  • three distinct adjacent R⁴ groups, taken together, form a naphthalene ring optionally substituted, including the carbon atoms to which each of the R⁴ groups are bonded.

According to en embodiment by “aromatic group or ring” it is meant a phenyl or naphthyl derivative.

According to another embodiment of the invention, Q represents a linear C₂-C₅ alkylene radical optionally substituted, a ferrocenediyl optionally substituted or a biphenyldiyl or binaphthildiyl radical optionally substituted.

Possible substituents of R^1′, R^1″ and R¹ to R⁷ and Q are one or two halogen, C₁ to C₁₀ alkoxy or polyalkyleneglycols groups, halo- or perhalo-hydrocarbon, COOR, NR₂, quaternary amine or R groups, wherein R is a C₁ to C₆ alkyl, or a C₅ to C₁₂ cycloalkyl, aralkyl (such as benzyl, phenethyl etc.) or aromatic group, the latter being also optionally substituted by one, two or three halogen, sulfonates groups or C₁-C₈ alkyl, alkoxy, amino, nitro, sulfonates, halo- or perhalo-hydrocarbon or ester groups. By “halo- or perhalo-hydrocarbon” it is meant groups such as CF₃ or CClH₂ for instance.

To our surprise, the ligands of formula (2-A′) are new, when the dotted line represents a double bong and z is 0, at the exception of 2-(diphenylphosphino)-N-(phenylmethylene)-cyclohexanamine, and therefore are also an object of the present invention.

The complexes according to the invention having as ligand a compound of formula (2-A′), when the dotted line represents a double bong and z is 0, are also new, at the exception of dichloro[[N(Z), 1R,2R]-2-(diphenylphosphino-κP)—N-(phenylmethylene)cyclohexanamine-κN](triphenylphosphine)-Ruthenium, and are therefore also another object of the present invention.

In a particular embodiment of formula (2-A), L2 is a bidentate N—P ligand of general formula

in which R¹ represents a hydrogen atom, a linear, branched or cyclic C₁ to C₆ alkyl or alkenyl group optionally substituted;
R² and R³ represent, simultaneously or independently, a linear, branched or cyclic C₁ to C₆ alkyl group optionally substituted, a phenyl or naphthyl group optionally substituted; or the groups R² and R³, taken together, form a saturated or unsaturated ring optionally substituted, having 5, 6 or 7 atoms and including the phosphorus atom to which the R² and R³ groups are bonded;
R⁶ and R⁷ represent, simultaneously or independently, a hydrogen atom, a linear or branched C₁ to C₄ alkyl group optionally substituted, a phenyl ring optionally substituted; R⁶ and R¹, taken together, may form a saturated or unsaturated heterocycle, optionally substituted and optionally containing one additional nitrogen or oxygen atoms, containing 5 or 6 atoms and including the carbon atoms and the N atom to which the R⁶ or R¹ group are bonded respectively; and
Q represents:

• • a group of formula

• • wherein n is an integer from 2 or 3, and
  • R⁴ and R⁵ represent, simultaneously or independently, a hydrogen atom, a linear or branched C₁ to C₄ alkyl group optionally substituted, a phenyl ring optionally substituted; or two distinct R⁴ and/or R⁵ groups, taken together, form a C₅ to C₁₀ saturated ring optionally substituted including the carbon atoms to which each of the R⁴ or R⁵ group is bonded; or
  • a group of formula

• • wherein n is an integer from 1 to 3, and
  • two distinct adjacent R⁴ groups, taken together, form a C₅ to C₁₀ aromatic ring optionally substituted or a C₅-C₁₂ ferrocenediyl optionally substituted, including the carbon atoms to which each of the R⁴ group are bonded; or
  • three distinct adjacent R⁴ groups, taken together, form a naphthalene ring optionally substituted, including the carbon atoms to which each of the R⁴ group are bonded.

Possible substituents of R¹ to R⁷, in particular when the groups are or contain phenyl groups or moieties, are one or two halogen, CF₃ groups or C₁ to C₅ alkoxy or polyalkyleneglycols groups, COOR, NR₂ or R groups, wherein R is a C₁ to C₄ alkyl, or a C_5-6 cycloalkyl, aralkyl or aromatic group, the latter being also optionally substituted as above defined.

A particular embodiment of formula (2-B) is represented by formula (2-C) or (2-D)

wherein the dotted lines in formula (2-D) indicate the presence of a phenyl or a naphthyl group;
d represents 1 or 2;
R¹ represents a hydrogen atom or a C₁ to C₄ linear or branched alkyl group possibly substituted;
R² and R³ represent a linear, branched or cyclic C₁ to C₆ alkyl group optionally substituted or an phenyl group optionally substituted; and
R⁶ and R⁷ represent, simultaneously or independently, a hydrogen atom, a linear or branched C₁ to C₄ alkyl group optionally substituted, or an phenyl group optionally substituted; or R⁶ and R¹, taken together, form a saturated heterocycle, optionally substituted and optionally containing an additional nitrogen or oxygen atoms, such as a 2-pyrrolidine, a 2-piperidine or a 2-morpholine.

Possible substituents of R¹ to R³, R⁶ and R⁷, in particular when the groups are or contain phenyl groups or moieties, are one or two halogen, C₁ to C₅ alkoxy or polyalkyleneglycols groups, COOR, NR₂ or R groups wherein R is a C₁ to C₄ alkyl, or a C_5-6 cycloalkyl, aralkyl or aromatic group, the latter being also optionally substituted as defined above.

In an alternative embodiment, the ligand of formula (2-A) is a bidentate N—P ligand of general formula

in which Q, R¹, R², R³ are defined as for formula (2-B) or (2-D);
R⁶ represents a hydrogen atom, a linear or branched C₁ to C₄ alkyl group or an phenyl group optionally substituted; or R⁶, when taken together with R¹, forms a C₃-C₉ C═N function-containing heterocycle optionally substituted and optionally containing one additional nitrogen or oxygen atom.

Possible substituents of Q and R¹ to R⁶, in particular when the groups are or contain phenyl groups or moieties, are one or two halogen, CF₃ groups or C₁ to C₅ alkoxy or polyalkyleneglycols groups, C₁ to C₄ alkyl groups, or C₅ to C₁₀ cycloalkyl, aralkyl or phenyl groups, the latter being also optionally substituted as defined above.

Alternatively one may use a complex wherein the ligand of formula (2-A′) is a bidentate N—P ligand of general formula

wherein R², R³, R⁶ and R⁷ are as defined for (2-B) or (2-D), Q is defined as in formula (2-B); and
R^1′ and R^1″, when taken separately, represents a hydrogen atom, a linear, branched or cyclic C₁ to C₆ alkyl group optionally substituted or a phenyl group optionally substituted; or the R^1′ or R^1″, when taken together, form a saturated ring optionally substituted, having 5 to 7 atoms and including the carbon atom to which the R^1′ and R^1″ groups are bonded; R⁶ and R^1″, taken together, may form a saturated or unsaturated heterocycle, optionally substituted and optionally containing one or two additional nitrogen or oxygen atoms, containing 5 or 6 atoms and including the carbon atoms and the N atom to which the R⁶ or R^1″, group are bonded respectively.

Alternatively, yet in the embodiments, R^1′ and R^1″, when taken separately, represents a hydrogen atom, a linear or branched C₁ to C₄ alkyl group optionally substituted or a phenyl group optionally substituted; or the R^1′ or R^1″, when taken together, form a saturated ring optionally substituted, having 5 to 7 atoms and including the carbon atom to which the R^1′ and R^1″ groups are bonded.

Possible substituents of R^1″, R^1″, R², R³, Q, R⁶ and R⁷, in particular when the groups are or contain phenyl groups or moieties, are one or two halogen, CF₃ groups or C₁ to C₅ alkoxy or polyalkyleneglycols groups, C₁ to C₄ alkyl groups, or C₅ to C₁₀ cycloalkyl, aralkyl or phenyl groups, the latter being also optionally substituted as above defined.

It is understood that, in any of the above embodiments, the ferrocenediyl, as well as the metallocenediyl above mentioned, can be in the form of a ferrocene-1,1′-diyl or of a ferrocene-1,2-diyl.

A particular embodiment of formula (2-E) is a ligand of formula (2-F), (2-F′), (2-G) or (2-G′)

wherein the dotted lines in formula (2-G) or (2-G′) indicate the presence of a phenyl or a naphthyl group; e represents 1 or 2, and in particular 1;
R¹, R², R³, are defined as in formula (2-E), R^1′ is defined as R¹ in formula (2-E); and
R⁶ represents a hydrogen atom, a linear or branched C₁ to C₄ alkyl group optionally substituted, or a phenyl group optionally substituted; or R⁶, when taken together with R¹, forms a C₃-C₉ C═N function-containing heterocycle optionally substituted and optionally containing one additional nitrogen or oxygen atom such as a 2-pyridyl, a 1-oxazolinyl, a 2-imidazolyl or a 2-isoquinolinyl group.

Possible substituents of R¹ to R³ and R⁶, in particular when the groups are or contains phenyl groups or moieties, are one or two halogen, C₁ to C₅ alkoxy or polyalkyleneglycols groups, C₁ to C₄ alkyl groups, or C₅ to C₁₀ cycloalkyl, aralkyl or phenyl groups, the latter being also optionally substituted as above defined.

In all the above embodiments when it is the that “R² and R³, when taken together, may form a saturated or unsaturated ring . . . ”, one can cite a trivial example of such type of R² and R³ taken together the following: diphenyl or dinaphthyl group (which will form an unsaturated 5 atom ring) or a —(CH₂)₅— group (which will form a saturated 6 atom ring).

Furthermore, in all the above embodiments, a particularly appreciated mode of realization is the one where the R² and R³ groups are aromatic groups optionally substituted.

In a particular embodiment of the invention the L′ ligand may be a preferably C₃-C₃₀ mono-phosphine, and in particular of formula PR^d₃, wherein R^d is a C₁-C₁₂ group, such as linear, branched or cyclic alkyl, alkoxy or aryloxy group optionally substituted, substituted or unsubstituted phenyl, diphenyl or naphthyl or di-naphthyl group, or a solvent such as THF, acetone, pyridine an C₃-C₈ ester or an C₁-C₄ alcohol. Possible substituents are those cited above for L2.

The processes of the invention are particularly attractive when are used complexes of the (2) [Ru(L2)₂Y₂] wherein Y represents H or Cl, and L2 represents a ligand of the formula (2-H):

wherein R¹ represents a hydrogen atom or a methyl group, Ph is phenyl radical.

The ligands described above can be obtained by applying standard general methods which are well known in the state of the art and by the person skilled in the art. Therefore, their preparation does not require a specific description. For example one may revert to WO 02/22526.

In a general way, the complexes of formula (1) can be prepared and isolated prior to their use in the process according to the general methods described in the literature. A method is described in the Example.

Moreover, the complexes can be prepared in situ, by several methods, in the hydrogenation medium, without isolation or purification, just before their use.

One of the possible procedures to advantageously prepare in situ a complex of formula (1) consists in reacting an appropriate Ru complex of formula [Ru(“diene”)(“allyl”)₂], wherein “diene” represents a cyclic or linear hydrocarbon containing two carbon-carbon double bonds, conjugated or not, such as for example 1,5-cyclooctadiene (COD) or norbornadiene, and “allyl” represents a linear or branched C₃ to C₈ hydrocarbon radical containing one carbon-carbon double bond such as methylallyl or allyl, with a non coordinating acid such as HBF₄Et₂O, and then treating the resulting solution with the required amount of a ligands L2, and if necessary of ligand L′, such as defined previously, to give a solution of a catalyst according to formula (1). Furthermore, the mixture thus obtained can also be treated with a base in the presence of a primary or secondary alcohol. Furthermore, the complexes of formula (1) can be prepared by reacting an appropriate Ru complex such as, [RuCl₂(PPh₃)₃], [RuCl₂(cod)] or [RuCl₂(arene)]₂ with the required amount of a ligands L2, and if necessary of ligand L′, such as defined previously (cod representing a cyclooctadiene and arene being e.g. a benzene or naphthalene).

It is also understood that the complex of formula (I) can also be obtained in situ from complexes which have a similar formula or are cationic or anionic, for examples a complex (I) wherein Y has another meaning or a complex of formula [Ru(L2)₂(solvent)₂](Anion)₂, wherein the anion is a non-coordinating one, which in presence of, for example an alcohol and a base, are converted into a compound of formula (I).

To carry out the processes of the invention it is required also to use a base. The base can be the substrate itself, if the latter is basic, a corresponding alcoholate or any base having preferentially a pK_a above 11. According to a particular embodiment of the invention the base may have a pK_a above 14. It is also understood that preferably the base does not reduce itself a substrate of formula (1). As non-limiting examples one may cite the following type of base: alcoholate, hydroxides, alkaline or alkaline-earth carbonates, phosphazines, amides, basic alox, siliconates (i.e. silicium derivatives having SiO⁻ or SiRO⁻ groups), hydrides such as NaBH₄, NaH or KH.

One can cite, as non-limiting examples, alkaline or alkaline-earth metal carbonates, such as cesium carbonate, an alkaline or alkaline-earth metal hydroxides, C_1-10 amidures, C_10-26 phosphazine or an alcoholate of formula (R¹³O)₂M or R¹³OM′, wherein M is an alkaline-earth metal, M′ is an alkaline metal or an ammonium NR¹⁴₄⁺, R¹³ stands for hydrogen or a C₁ to C₆ linear or branched alkyl radical and R¹⁴ stands for a C₁ to C₁₀ linear or branched alkyl radical, such as sodium or potassium alcoholates. Of course, other suitable bases can be used.

According to an embodiment of the invention, the base is an alkaline alcoholate of formula R¹³OM′.

As previously mentioned the processes of the invention consist in the hydrogenation of a substrate using a ruthenium complex and a base. A typical process implies the mixture of the substrate with the ruthenium complex, a base and optionally a solvent, and then treating such a mixture with molecular hydrogen at a chosen pressure and temperature.

The complexes of the invention, an essential parameter of the process, can be added to the reaction medium in a large range of concentrations. As non-limiting examples, one can cite as complex concentration values those ranging from 50 ppm to 50000 ppm, relative to the amount of substrate. Preferably, the complex concentration will be comprised between 100 and 20000 ppm. It goes without saying that the optimum concentration of complex will depend, as the person skilled in the art knows, on the nature of the latter, on the nature of the substrate and on the pressure of H₂ used during the process, as well as the desired time of reaction.

Useful quantities of base, added to the reaction mixture, may be comprised in a relatively large range. One can cite, as non-limiting examples, ranges between 5 to 50000 molar equivalents, relative to the complex (e.g. base/com=5 to 50000), preferably 20 to 2000, and even more preferably between 50 and 1000 molar equivalents.

The hydrogenation reaction can be carried out in the presence or absence of a solvent. When a solvent is required or used for practical reasons, then any solvent current in hydrogenation reactions can be used for the purposes of the invention. Non-limiting examples include aromatic solvents such as toluene or xylene, hydrocarbon solvents such as hexane or cyclohexane, ethers such as tetrahydrofuran or MTBE, polar solvents such as primary or secondary alcohols such as isopropanol or ethanol, or mixtures thereof. The choice of the solvent is a function of the nature of the complex and the person skilled in the art is well able to select the solvent most convenient in each case to optimize the hydrogenation reaction.

In the hydrogenation process of the invention, the reaction can be carried out at a H₂ pressure comprised between 10⁵ Pa and 80×10⁵ Pa (1 to 80 bars) or even more if desired. Again, a person skilled in the art is well able to adjust the pressure as a function of the catalyst load and of the dilution of the substrate in the solvent. As examples, one can cite typical pressures of 1 to 50×10⁵ Pa (1 to 50 bar).

The temperature at which the hydrogenation can be carried out is comprised between 0° C. and 120° C., more preferably in the range of between 50° C. and 100° C. Of course, a person skilled in the art is also able to select the preferred temperature as a function of the melting and boiling point of the starting and final products as well as the desired time of reaction or conversion.

EXAMPLES

The invention will now be described in further detail by way of the following examples, wherein the temperatures are indicated in degrees centigrade and the abbreviations have the usual meaning in the art.

All the procedures described hereafter have been carried out under an inert atmosphere unless stated otherwise. Hydrogenations were carried out in open glass tubes placed inside a stainless steel autoclave. H₂ gas (99.99990%) was used as received. All substrates and solvents were distilled from appropriate drying agents under Ar. NMR spectra were recorded on a Bruker AM-400 (1H at 400.1 MHz, ¹³C at 100.6 MHz, and ³¹P at 161.9 MHz) spectrometer and normally measured at 300 K, in CDCl₃ unless indicated otherwise. Chemical shifts are listed in ppm.

Example 1

A) Preparation of Complexes [RuCl₂(L-1)_n], [RuCl₂(L-2)₂], [RuCl₂(L-4)₂]

a) Preparation of the Complex Dichloro bis[2-(Diphenylphosphino)ethylamine]Ruthenium ([RuCl₂(L-1)₂])

Under argon, a round-bottomed Schlenck flask, equipped with a magnetic stirring bar, was charged with RuCl₂(PPh₃)₃ (418.6 mg, 0.436 mmol) and toluene (6 mL). Then under stirring, a solution of 2-(diphenylphosphino)ethylamine (201.6 mg, 0.879 mmol) in toluene (3 mL) was added, more toluene (3 mL) was added to rinse. Then the dark-brown solution was heated in an oil bath at 100° C. for six hours. The resulting yellow suspension was cooled to room temperature, and filtered under argon. The yellow solid was rinsed with toluene until the filtrate was colourless and then dried in-vacuo. The desired complex (258.4 mg, 0.41 mmol, 94%) was then collected as a pale-yellow solid. ³¹P{¹H}-NMR analysis showed the presence of two species the major one being the trans-chloride-cis-phosphorous complex (75%) and the minor one being the cis-chloride-cis-phosphorous complex (25%).

¹H-NMR (CD₂Cl₂): δ (A) 7.24 (m, 4H), 7.16 (m, 8H), 7.07 (m, 8H), 3.78 (brs, 4H, NH₂), 3.22 (m, 4H), 2.70 (brs, 4H).

¹³C{¹H}-NMR (CD₂Cl₂): δ (A) 137.1 (Carom), 133.9 (t, J=5 Hz, CHarom), 129.2 (CHarom), 127.6 (t, J=5 Hz, CHarom), 41.9 (CH₂), 33.3 (t, J=13.5 Hz, CH₂).

³¹P{¹H}-NMR (CD₂Cl₂): A (75%) δ=62.6 ppm (s); B (25%) δ=67.5 ppm (d, J=32 Hz), 56.2 ppm (d, J=32 Hz).

b) Preparation of the Complex Dichloro[2-(Diphenylphosphino) ethylamine][triphenylphosphine]Ruthenium ([RuCl₂(L-1)(PPh₃)])

Under argon, a round-bottomed Schlenck flask, equipped with a magnetic stirring bar, was charged with RuCl₂(PPh₃)₃ (20.0 g, 20.9 mmol) and THF (160 mL). Then under stirring, neat 2-(diphenylphosphino)ethylamine (4.83 g, 21.1 mmol) was added over five minutes. Next, the reaction mixture was stirred at room temperature for three hours. During that time, the dark ruthenium suspension quickly dissolves before precipitating back as a pink solid. Reaction mixture was then filtered under nitrogen (dark filtrate). The obtained solid was washed with THF (3×40 ml) and then MTBE. The pink solid was then dried in-vacuo overnight to afford the ruthenium complex as a pink solid (14.0 g, 21 mmol).

³¹P{¹H}-NMR analysis showed the presence of several ruthenium species, and also showed the presence of free triphenylphosphine probably liberated by product evolution in solution, as the solid was washed several times with THF.

³¹P{¹H}-NMR (CD₂Cl₂): δ=59.96 (d, J=30.7 Hz), 59.46 (t, J=35.1 Hz), 58.51 (s), 44.64 (d, J=30.7 Hz), 44.29 (d, J=30.7 Hz), −4.84 (s, free PPh₃).

c) Preparation of the Complex Dichloro bis[3-(Diphenylphosphino)-1-propylamine]Ruthenium ([RuCl₂(L-2)₂])

Under argon, a round-bottomed Schlenck flask, equipped with a magnetic stirring bar, was charged with RuCl₂(PPh₃)₃ (1.028 g, 1.07 mmol) and with a solution of 3-(diphenylphosphino)-1-propylamine (566.8 mg, 2.33 mmol) in toluene (5 mL). More toluene (5 mL) was added to rinse. Then the dark-brown solution was heated in an oil bath at 100° C. for 16 h. The resulting brick-orange suspension was cooled to room temperature, and added to pentane (50 mL) with stirring. The yellow solid was collected by filtration, washed with pentane (2×3 mL) and dried in vacuo to provide the desired complex (672.6 mg, 1.02 mmol, 95%) as a yellow-mustard solid. ³¹P{¹H}-NMR analysis showed the presence of two species.

¹H-NMR (CD₂Cl₂): δ (A) 7.19 (t, J=7.2 Hz, 4H), 7.14 (m, 8H), 7.05 (t, J=7.2 Hz, 8H), 3.28 (brs, 4H), 3.02 (brs, 4H), 2.66 (m, 4H), 2.0 (m, 4H).

¹³C-NMR (CD₂Cl₂): δ (A) 138.4 (t, J=19.2 Hz, Carom), 134.2 (t, J=4.8 Hz, CHarom), 129.0 (CHarom), 127.5 (t, J=4.8 Hz, CHarom), 41.3 (CH₂), 26.9 (t, J=13.6 Hz, CH₂), 24.7 (CH₂).

³¹P{¹H}-NMR (CD₂Cl₂): A (82%) δ=33.5 ppm (s), B (18%) δ=49.8 ppm (s).

d) Preparation of the Complex Dichloro bis-2-[2-(diisobutylphosphino)ethyl]pyridine Ruthenium ([RuCl₂(L-4)₂])

Under argon, a round-bottomed Schlenck flask, equipped with a magnetic stirring bar, was charged with RuCl₂(PPh₃)₃ (535.2 mg, 0.56 mmol) and with a solution of 2-[2-(diisobutylphosphino)ethyl]pyridine (306.5 mg, 1.22 mmol) in toluene (3 mL). More toluene (2×1 mL) was added to rinse. Then the dark-brown solution was heated in an oil bath at 100° C. for 6 h. The resulting red solution was cooled to room temperature, and the solvent removed in vacuo to give an orange solid. The solid was dissolved in CH₂Cl₂ (3 mL), MeOH (15 mL) was added and the solution was concentrated in vacuo until a yellow precipitate forms. The solid was recovered by filtration, washed with MeOH (1 mL) and dried in vacuo to give the desired complex (458.9 mg). ³¹P{¹H}-NMR analysis showed the presence of free PPh₃ (44 wt %). The solid (425.8 mg) was dissolved in CH₂Cl₂ (10 mL), and the solution added to a suspension of CuCl (86.1 mg, 0.87 mmol) in CH₂Cl₂ (10 mL). More CH₂Cl₂ (5 mL) was added to rinse. The solution was stirred for 5 min. and then the solvent was removed in vacuo. The resulting solid was triturated with a mixture of hexane (25 mL)/CH₂Cl₂ (5 mL) and then filtered over a pad of Celite. The pad was further washed with hexane/CH₂Cl₂ (5/1, 3×5 mL). The combined filtrate was concentrated in vacuo until precipitation of a yellow solid occurred. The solid was recovered by filtration and dried in vacuo to give the desired complex (152.1 mg, 0.22 mmol, 40%) as a yellow solid, free of triphenylphosphine.

¹H-NMR (CD₂Cl₂): δ 8.18 (d, J=5.9 Hz, 1H), 7.69 (ddd, J=1.5, 7.2, 7.7 Hz, 1H), 7.2 (d, J=7.2 Hz, 1H), 6.84 (ddd, J=1.5, 5.9, 7.2 Hz, 1H), 4.5 (brs, 1H), 2.9 (brs, 1H), 2.5 (brs, 1H), 2.3 (brs, 2H), 2.1 (brs, 1H), 1.99 (brs, 1H), 1.68 (brd, J=14 Hz, 2H), 1.55 (brs, 1H), 0.8-1.2 (brm, 12H).

¹³C-NMR (CD₂Cl₂): δ 167.6 (Carom), 158.5 (CHarom), 136.9 (CHarom), 124.2 (CHarom), 121.5 (CHarom), 40.0 (brs, CH₂), 36.6 (brs, CH₂), 33.2 (CH₂), 26.1 (CH₃), 25.7 (CH₃), 25.3 (CH), 19.7 (t, J=10.4 Hz, CH₂).

³¹P{¹H}-NMR (CD₂Cl₂): δ=40.2 ppm (s).

B) Preparation of Imino-phosphine Ligands (L-6 to L-10)

a) Preparation of N-[2-(diphenylphosphino)ethyl]-N-[phenylmethylene]amine (L-6)

Under argon, a solution of 2-diphenylphosphino-ethylamine (590.3 mg, 2.57 mmol) and benzaldehyde (275.0 mg, 2.59 mmol) in ethanol (15 mL) was heated at 65° C. (oil bath) for 4 h. Then, the solvent was removed in-vacuo to give the desired product (>98% by ¹H-NMR) as a colourless oil which solidified on standing (733.9 mg, 2.31 mmol, 90%).

¹H-NMR (CD₂Cl₂): δ 8.2 (s, 1H, CH═N), 7.68-7.62 (m, 2H), 7.49-7.43 (m, 4H), 7.4-7.28 (m, 9H), 3.71 (ddt, J=1, 8, 9 Hz, 2H), 2.45 (ap t, J=8 Hz, 2H).

¹³C-NMR (CD₂Cl₂): δ 161.3 (CH C═N), 139.2 (d, J=12.9 Hz, Carom), 136.7 (Carom), 133.1 (d, J=18.6 Hz, CHarom), 130.9 (CHarom), 128.91 (CHarom), 128.86 (CHarom), 128.8 (d, J=6.5 Hz, CHarom), 128.4 (CHarom), 58.7 (d, J=21 Hz, CH₂), 30.1 (d, J=12.9 Hz, CH₂).

³¹P{¹H}-NMR (CD₂Cl₂): δ=−18.5 ppm (s).

b) Preparation of N-[(3,5-Dimethylphenyl)methylene]-N-[2-(diphenylphosphino)ethyl]amine (L-7)

Under Argon, a Solution of 2-Diphenylphosphino-Ethylamine (652.2 Mg, 2.84 Mmol) and 3,5-dimethyl-benzaldehyde (387.4 mg, 2.89 mmol) in ethanol (15 mL) was heated at 65° C. (oil bath) for 4 h. Then, the solvent was removed in-vacuo to give the desired product (>98% by ¹H-NMR) as a colourless oil (993.2 mg, 2.8 mmol, quantitative).

¹H-NMR (CD₂Cl₂): δ 8.13 (s, 1H, CH═N), 7.48-7.42 (m, 4H), 7.35-7.29 (m, 6H), 7.25 (s, 2H), 7.04 (s, 1H), 3.68 (dq, J=1.3, 7.7 Hz, 2H), 2.44 (t, J=7.7 Hz, 2H), 2.3 (s, 6H).

¹³C-NMR (CD₂Cl₂): δ 161.7 (CH C═N), 139.2 (d, J=13.7 arom), 138.5 (Carom), 136.6 (Carom), 133.1 (d, J=19.4 Harom), 132.6 (CHarom), 128.9 (CHarom), 128.8 (d, J=6.5 CHarom), 126.2 (CHarom), 58.7 (d, J=21 Hz, CH₂), 30.2 (d, J=12.9 Hz, CH₂), 21.2 (CH₃).

³¹P{¹H}-NMR (CD₂Cl₂): δ=−18.5 ppm (s).

c) Preparation of N-[cyclohexylmethylene]-N-[2-(diphenylphosphino)ethyl]amine (L-8)

Under argon, a solution of 2-diphenylphosphino-ethylamine (619.0 mg, 2.7 mmol) and cyclohexane carbaldehyde (306.2 mg, 2.73 mmol) in ethanol (15 mL) was heated at 65° C. (oil bath) for 4 h. Then, the solvent was removed in-vacuo to give the desired product (>98% by ¹H-NMR) as a colourless liquid (880.5 mg, 2.7 mmol, quantitative).

¹H-NMR (CD₂Cl₂): δ 7.47-7.39 (m, 5H), 7.35-7.28 (m, 6H), 3.42 (q, J=8.2 Hz, 2H), 2.32 (t, J=7.7 Hz, 2H), 2.12-2.01 (m, 1H), 1.77-1.67 (m, 4H), 1.67-1.58 (m, 1H), 1.34-1.1 (5H)

¹³C-NMR (CD₂Cl₂): δ 169.2 (CH═N), 139.2 (d, J=13.7 Hz, Carom), 133.1 (d, J=19.4 Hz, CHarom), 128.9 (CHarom), 128.8 (d, J=6.5 Hz, CHarom), 58.5 (d, J=20.2 Hz, CH₂), 43.6 (CH), 30.2 (d, J=12.1 Hz, CH₂), 29.9 (CH₂), 36.5 (CH₂), 25.9 (CH₂).

³¹P{¹H}-NMR (CD₂Cl₂): δ=−18.9 ppm (s).

d) Preparation of N-benzylidene-N-[3-(diphenylphosphino)propyl]amine (L-9)

Under argon, a solution of 3-diphenylphosphino-propylamine (631.2 mg, 2.6 mmol) and benzaldehyde (278.1 mg, 2.6 mmol) in ethanol (15 mL) was heated at 65° C. (oil bath) for 4 h. Then, the solvent was removed in-vacuo to give the desired product (>98% by ¹H-NMR) as a white solid (822.3 mg, 2.5 mmol, 96%).

¹H-NMR (CD₂Cl₂): δ 8.24 (s, CH═N), 7.72-7.68 (m, 2H), 7.45-7.37 (m, 7H), 7.33-7.28 (m, 6H), 3.66 (dt, J=1.0, 6.7 Hz, 2H), 2.13 (dd, J=5.4, 7.9, 10.5 Hz, 2H), 1.85-1.75 (m, 2H).

¹³C-NMR (CD₂Cl₂): δ 161.3 (CH C═N), 139.9 (d, J=13.7 Hz, Carom), 136.9 (Carom), 133.1 (d, J=18.6 Hz, CHarom), 130.8 (CHarom), 128.9 (CHarom), 128.8 (CHarom), 128.7 (d, J=6.5 Hz, CHarom), 128.4 (CHarom), 62.5 (d, J=12.9 Hz, CH₂), 27.8 (d, J=16.9 Hz, CH₂), 25.8 (d, J=11.3 Hz, CH₂).

³¹P{¹H}-NMR (CD₂Cl₂): δ=−15.9 ppm (s).

e) Preparation of N-benzylidene-N-[3-(diisobutylphosphino)propyl]amine (L-10)

Under argon, a solution of 3-diisobutylphosphino-propylamine (428.5 mg, 2.11 mmol) and benzaldehyde (226.9 mg, 2.14 mmol) in ethanol (15 mL) was heated at 65° C. (oil bath) for 4 h. Then, the solvent was removed in-vacuo to give the desired product (>98% by ¹H-NMR) as a colourless liquid (614.1 mg, 2.1 mmol, quantitative).

¹H-NMR (CD₂Cl₂): δ 8.27 (s, 1H), 7.73-7.68 (m, 2H), 7.43-7.38 (m, 3H), 3.63 (t, J=6.7 Hz, 2H), 1.82-1.74 (m, 2H), 1.73-1.64 (m, 2H), 1.41-1.37 (m, 2H), 1.35-1.22 (m, 4H), 0.98 (d, J=6.7 Hz, 6H), 0.97 (d, J=6.7 Hz, 6H).

¹³C-NMR (CD₂Cl₂): δ 160.9 (CH C═N), 136.9 (Carom), 130.7 (CHarom), 128.9 (CHarom), 128.3 (CHarom), 63.1 (d, J=11.3 Hz, CH₂), 39.5 (d, J=13.7 Hz, CH₂), 27.7 (d, J=12.9 Hz, CH₂), 26.9 (d, J=13.7 Hz, CH), 26.7 (d, J=12.9 Hz, CH₂), 24.53 (d, J=8.9 Hz, CH₃), 24.45 (d, J=8.1 Hz, CH₃).

³¹P{¹H}-NMR (CD₂Cl₂): δ=−39.6 ppm (s).

The structure of the ligands is reported in Table 1:

TABLE 1
Structure of ligands (L-1 to L-10) used
in complexes of formula (1)
structure name
          L-1
          L-2
          L-3
          L-4
          L-5
          L-6
          L-7
          L-8
          L-9
          L-10

Ligands L-1 and L-2 are commercially available (Fluka). Ligands L-3 and L-4 were prepared according to Rautenstrauch, V. et al. in WO 02/22526 A2.

C) Preparation of Complexes [RuCl₂(L-6 to L-10)₂]

See below example 2b) for the in-situ generation of these complexes.

Example 2

Catalytic Hydrogenation of Various Esters Using Complexes of Formula (1)

a) Using Pre Formed Complex

A typical catalytic hydrogenation using RuCl₂(L-1)₂ as pre-catalyst is described below with methyl benzoate as substrate:

Under argon, a solution of methyl benzoate (3.249 g, 24 mmol) in THF (2 mL) was added with a syringe, followed by more THF (2×1 mL), to a Keim autoclave equipped with a glass liner containing [RuCl₂(L-1)₂] (7.5 mg, 0.012 mmol, 0.05 mol %), solid NaOMe (128.2 mg, 2.4 mmol, 10 mol %) and THF (12.5 mL). The autoclave was pressurised with hydrogen gas at 50 bars and placed in a thermostatted oil bath set at 100° C. After 2 h 30 min, the autoclave was removed from the oil bath, and cooled in a cold-water bath. Then, the reaction mixture was diluted with citric acid 10% w/w (25 mL) and extracted with MTBE (100 mL). The organic phases was washed with aq. sat. NaCl (3×50 mL). Gas chromatography after silylation showed the following products: benzyl alcohol (97.5%), benzoic acid (2.5%). Then, the organic phase was washed successively with aq. KOH 1 M (50 mL) and aq. sat. NaCl (3×50 mL), and dried over MgSO₄ anh. Filtration and removal of the solvent in vacuo gave a yellow liquid (3.486 g). Purification by Kugelrohr distillation (130-140° C./8.5 mbar) gave pure benzyl alcohol (2.081 g, 19 mmol, 80%) as a colourless liquid.

¹H NMR (CDCl₃, 400 MHz): δ 7.38-7.25 (m, 5H), 4.65 (s, 2H), 2.02 (s, 1H).

¹³C NMR (CDCL₃, 100 MHz): δ 140.9 (s), 128.6 (d), 127.6 (d), 126.9 (d), 62.3 (t).

b) Using In-Situ Formed Complex

A typical catalytic hydrogenation using in-situ formed RuCl₂(L-6)₂ as pre-catalyst is described below for methyl benzoate as substrate:

Under argon, a solution of methyl benzoate (2.729 g, 20 mmol) in THF (2 mL) was added with a syringe, followed by more THF (2×1 mL), to a Keim autoclave equipped with a glass liner containing [RuCl₂(para-cymene)]₂ (6.9 mg, 0.01 mmol, 0.05 mol %), ligand L-6 (15.4 mg, 0.05 mmol, 0.24 mol %), solid NaOMe (106.2 mg, 2 mmol, 10 mol %) and THF (6 mL). Then a solution of tridecane (338.1 mg, 1.83 mmol), as internal standard, is added in THF (2 mL), followed by more THF (2×1 mL). The autoclave was then pressurised with hydrogen gas at 50 bars and placed in a thermostatted oil bath set at 100° C. After 1 h, the autoclave was removed from the oil bath, and cooled in a cold-water bath. An aliquot (0.3 mL) was withdrawn and diluted with MTBE (5 mL). The organic phase was washed with aq. sat. NaCl (5 mL), filtered through Celite and analysed. GC yield based on the internal standard gave the yield of 81% in benzyl alcohol.

Using methyl benzoate as a test substrate several complexes with ligands described in Table 1, bases and solvent were tested under these conditions. The resulted are summarized in Table 2.

TABLE 2
Hydrogenation of methyl benzoate using [RuCl2(L)n]
Test	Complex	Com/Base	Base	Solvent	Conv.
1	[RuCl2(PPh3)3]	4000/1000000	NaOMe	THF	0
2	[(RuCl2(Cym))2]	500/100000	NaOMe	THF	0
3	[RuCl2(L-1)2]	1000/1000000	NaOMe	THF	0 1)
4	[RuCl2(L-1)2]	1000/1000000	NaOMe	THF	86
5	[RuCl2(L-1)2]	1000/100000	NaOMe	THF	97
6	[RuCl2(L-1)2]	1000/100000	NaOMe	THF	98 2)
7	[RuCl2(L-1)2]	500/100000	NaOMe	THF	98 (81) 3a)
8	[RuCl2(L-1)2]	1000/100000	NaOMe	THF	75 4)
9	[RuCl2(L-1)2]	1000/100000	NaOMe	THF	93 5)
10	[RuCl2(L-1)2]	2000/100000	NaOMe	THF	32 6)
11	[RuCl2(L-1)2]	1000/1000000	NaOMe	MTBE	87
12	[RuCl2(L-1)2]	1000/1000000	NaOMe	Toluene	87
13	[RuCl2(L-1)2]	1000/1000000	NaOMe	iPrOH	87
14	[RuCl2(L-1)2]	1000/1000000	NaOMe	EtOH	87
15	[RuCl2(L-1)2]	1000/1000000	NaOMe	MeOH	20
16	[RuCl2(L-1)2]	1000/1000000	NaOEt	THF	83
17	[RuCl2(L-1)2]	1000/1000000	NaOtBu	THF	96 (85) 7)
18	[RuCl2(L-1)2]	1000/1000000	NaOH	THF	49
19	[RuCl2(L-1)2]	5000/1000000	NaHMDS 8)	THF	23 9)
20	[RuCl2(L-1)(PPh3)]	1000/1000000	NaOMe	THF	22
21	[RuCl2(L-2)2]	1000/1000000	NaOMe	THF	70
22	[RuCl2(L-2)2]	1000/100000	NaOMe	THF	54 2)
23	[RuCl2(L-3)2]	500/100000	NaOMe	THF	6 2)
24	[RuCl2(L-4)2]	500/100000	NaOMe	THF	7 3)
25	[RuCl2(L-5)2]	500/100000	NaOMe	THF	31 2)
27	[RuCl2(L-6)2]	500/100000	NaOMe	THF	81 2)
28	[RuCl2(L-7)2]	500/100000	NaOMe	THF	91 2)
29	[RuCl2(L-8)2]	500/100000	NaOMe	THF	82 2)
30	[RuCl2(L-9)2]	500/100000	NaOMe	THF	11 2)
31	[RuCl2(L-10)2]	500/100000	NaOMe	THF	8 2)
Com/Base: molar ratio in ppm relative to the substrate.
Conv. = conversion (in %, analysed by GC) of methyl benzoate into benzyl alcohol after 1 hour. Reaction conditions: H2 gas (50 bars), 100° C., solvent (1.4 M).
1) Test performed under an atmosphere of argon.
2) Catalyst generated in-situ with L (0.22 mol %) and [(RuCl2(Cym))2] (0.05 mol %). Indicated is GC yield based on internal standard.
3) Test performed during 2 h 30 min; a) isolated yield in brackets; b) indicated is GC yield based on internal standard.
4) Test performed at 50° C.
5) Test performed under H2 gas of 20 bars.
6) Test performed under H2 gas of 10 bars. GC yield based on internal standard in brackets.
7) Isolated yield in brackets.
8) NaHMDS: Sodium bis(trimethylsilyl)amide.
9) Test performed during 2 hours.

Several others esters (see Table 3) were hydrogenated under identical conditions as reported in Table 4 with RuCl₂(L-1)₂. The reaction conditions were identical to those reported above for methyl benzoate.

TABLE 3
Structure and name of substrates used
Substrate	Structure	Name
1		Methyl benzoate
2		Butyl benzoate
3		iso-Propyl benzoate
4		tert-Butyl benzoate
5		Methyl 4-methylbenzoate
6		Methyl 4-methoxybenzoate
7		Methyl 4-(dimethylamino)benzoate
8		Methyl 4-chlorobenzoate
9		Methyl 4-(trifluoromethyl)benzoate
10		Methyl 3-(dimethylamino)benzoate
11		Methyl phenylacetate
12		Methyl 3-phenylpropanoate
13		Methyl cyclohexanecarboxylate
14		Methyl octanoate
15		Butyl 3-(4,4-dimethylcyclohexyl) propanoate
16		Methyl perhydro-2-naphthylacetate
17		Dimethyl pentanedioate
18		Methyl 3-cyclohexene-1-carboxylate
19		Butyl 3-(4,4-Dimethyl-1-cyclohexen-1-yl) propanoate
20		3H-Benzo[c]furan-1-one
21		8,8-Dimethyl-1-oxaspiro[4.5]decan-2-one
22		8-tert-Butyl-1-oxa-spiro[4.5]decan-2-one
23		8,12-Epoxy-13,14,15,16-tetranorlabdan-12-one (Sclareolide)
24		5-Pentyl-dihydro-furan-2-one
25		6-Pentyl-tetrahydro-pyran-2-one

TABLE 4
Results obtained using the general conditions described above
	Substrate		Isolated
Test	(Table 3)	Conversion (%)	yield (%)
1	1	98	81
2	2	98	85
3	3	97	79
4	4	98	78
5	5	97	93
6	6	94	75
7	7	93	77 1)
8	8	88	67
9	9	72	46
10	10	99	92
11	11	98	82
12	12	56	37
13	13	94	82
14	14	86	75
15	15	56	45 2)
16	16	97	82 3)
17	17	94	72
18	18	71	59 4)
19	19	81	80 1)
20	19	93	90 2)
21	20	97	76
22	21	79	56 4)
23	22	75	68 4)
24	23	97	91 5)
25	24	98	91 6)
26	25	98	93 6)
Conversion: (in %, analysed by GC after silylation) of ester to alcohol after 2 h 30 min.
Reaction conditions: Substrate (20 mmol), H2 gas (50 bars), RuCl2(L-1)2 0.05 mol %, NaOMe 10 mol %, THF (14 mL) at 100° C. during 2 h 30 min.
1) Reaction run for 4 h.
2) Reaction run with KOMe (10 mol %) in THF during 5 h at 100° C. with H2 gas (30 bars).
3) Reaction run for 6 h.
4) Reaction run with S/C = 1000 and S/B = 1 during 1 h at 100° C. with H2 gas (50 bars).
5) Reaction run with KOMe (10 mol %) in toluene during 6 h at 100° C. with H2 gas (30 bars).
6) Reaction run with KOMe (10 mol %) in toluene during 4 h at 100° C. with H2 gas (50 bars).

Claims

1. A process for the reduction by hydrogenation, using molecular H2, of a C3-C70 substrate containing one or two ester or lactone functional groups into its corresponding alcohol or diol, which comprises carrying out the process in the presence of a base and at least one complex in the form of a ruthenium complex of formula

[Ru(L2)b(L′)aY2]  (1)

wherein L2 represents a C4-C40 bidentate ligand wherein the coordinating groups consist of one amino or imino group and one phosphino group;

L′ represents a C3-C70 mono-phosphine or a molecule of solvent;

b is 1 and a is 1 or 2 or b is 2 and a is 0; and

each Y represents, simultaneously or independently, CO, a hydrogen or halogen atom, a hydroxyl group, a BH4 or ALH4 group or a C1-C6 alkoxy or carboxylic radical.

2. The process according to claim 1, wherein the amino group is a NH2 or NH group.

3. The process according to claim 1, wherein the ruthenium complex is of formula

[Ru(L2)2Y2]  (2)

wherein L2 and Y have the meaning indicated in claim 1.

4. The process according to claim 1, wherein L2 is a compound of one of the formulae

wherein the dotted line indicates a single or double bond;

z is 0 or 1 when the carbon-nitrogen bond with the dotted line represents a single or double bond respectively;

R1 represents a hydrogen atom, a linear, branched or cyclic C1 to C10 alkyl or alkenyl group optionally substituted;

R1′ and R1″, when taken separately, represents a hydrogen atom, a linear, branched or cyclic C1 to C9 alkyl or alkenyl group optionally substituted or a C6 to C10 aromatic group optionally substituted; the R1′ or R1″, when taken together, form a saturated or unsaturated ring optionally substituted, having 5 to 12 atoms and including the carbon atom to which the R1′ and R1″ groups are bonded;

R2 and R3, when taken separately, represent, simultaneously or independently, a linear, branched or cyclic C1 to C8 alkyl or alkenyl group optionally substituted, a C6 to C10 aromatic group optionally substituted, or an OR2′ or NR2′R3′ group, R2′ and R3′ being a C1 to C8 alkyl or alkenyl group; or the groups R2 and R3, when taken together, form a saturated or unsaturated ring optionally substituted, having 5 to 10 atoms and including the phosphorus atom to which the R2 and R3 groups are bonded;

R6 and R7 represent, simultaneously or independently, a hydrogen atom, a linear, branched or cyclic C1 to C10 alkyl or alkenyl group optionally substituted, a C6-C10 aromatic group optionally substituted, or an OR4′ or NR4′R5′ group, R4′ and R5′ being a linear, branched or cyclic C1 to C10 alkyl or alkenyl group; R6 and R1 or R6 and R1″, taken together, may form a saturated or unsaturated heterocycle, optionally substituted and optionally containing one or two additional nitrogen or oxygen atoms, containing 5 to 10 atoms and including the carbon atoms and the N atom to which the R6 or R1, or R1″, group are bonded respectively; and

Q represents: a group of formula

wherein n is an integer from 1 to 4, and R4 and R5 represent, simultaneously or independently, a hydrogen atom, a linear, branched or cyclic C1 to C10 alkyl or alkenyl group optionally substituted, a C6-C10 aromatic group optionally substituted, or an OR4′ or NR4′R5′ group, R4′ and R5′ being a linear, branched or cyclic C1 to C10 alkyl or alkenyl group; two distinct R4 and/or R5 groups, taken together, may form a C5 to C10, saturated ring optionally substituted, including the carbon atoms to which each of the R4 or R5 group is bonded; or a group of formula

wherein n is an integer from 2 to 4, and two distinct adjacent R4 groups, taken together, form a C5 to C10, aromatic ring optionally substituted or a C5-C12 metallocenediyl optionally substituted, including the carbon atoms to which each of the R4 group are bonded; or three distinct adjacent R4 groups, taken together, form a naphthalene ring optionally substituted, including the carbon atoms to which each of the R4 groups are bonded;

and wherein the substituents of R1′, R1″ and R1 to R7 and Q are one or two halogen, C1 to C10 alkoxy or polyalkyleneglycols groups, halo- or perhalo-hydrocarbon, COOR, NR2, quaternary amine or R groups, wherein R is a C1 to C6 alkyl, or a C5 to C12 cycloalkyl, aralkyl or aromatic group, the latter being also optionally substituted by one, two or three halogen, sulfonates groups or C1-C8 alkyl, alkoxy, amino, nitro, sulfonates, halo- or perhalo-hydrocarbon or ester groups.

5. The process according to claim 1, wherein L2 is a ligand of formula

in which R1 represents a hydrogen atom, a linear, branched or cyclic C1 to C6 alkyl or alkenyl group optionally substituted;

R2 and R3 represent, simultaneously or independently, a linear, branched or cyclic C1 to C6 alkyl group optionally substituted, a phenyl or naphthyl group optionally substituted; or the groups R2 and R3, taken together, form a saturated or unsaturated ring optionally substituted, having 5, 6 or 7 atoms and including the phosphorus atom to which the R2 and R3 groups are bonded;

R6 and R7 represent, simultaneously or independently, a hydrogen atom, a linear or branched C1 to C4 alkyl group optionally substituted, a phenyl ring optionally substituted; R6 and R1, taken together, may form a saturated or unsaturated heterocycle, optionally substituted and optionally containing one additional nitrogen or oxygen atoms, containing 5 or 6 atoms and including the carbon atoms and the N atom to which the R6 or R1 group are bonded respectively; and

Q represents: a group of formula

wherein n is an integer from 2 or 3, and R4 and R5 represent, simultaneously or independently, a hydrogen atom, a linear or branched C1 to C4 alkyl group optionally substituted, a phenyl ring optionally substituted; or two distinct R4 and/or R5 groups, taken together, form a C5 to C10 saturated ring optionally substituted including the carbon atoms to which each of the R4 or R5 group is bonded; or a group of formula

wherein n is an integer from 1 to 3, and two distinct adjacent R4 groups, taken together, form a C5 to C10 aromatic ring optionally substituted or a C5-C12 ferrocenediyl optionally substituted, including the carbon atoms to which each of the R4 group are bonded; or three distinct adjacent R4 groups, taken together, form a naphthalene ring optionally substituted, including the carbon atoms to which each of the R4 group are bonded.

6. The process according to claim 1, wherein L2 is a ligand of formula (2-C) or (2-D)

wherein the dotted lines in formula (2-D) indicate the presence of a phenyl or a naphthyl group;

d represents 1 or 2;

R1 represents a hydrogen atom or a C1 to C4 linear or branched alkyl group possibly substituted;

R2 and R3 represent a linear, branched or cyclic C1 to C6 alkyl group optionally substituted or an phenyl group optionally substituted; and

R6 and R7 represent, simultaneously or independently, a hydrogen atom, a linear or branched C1 to C4 alkyl group optionally substituted, or an phenyl group optionally substituted; or R6 and R1, taken together, form a saturated heterocycle, optionally substituted and optionally containing an additional nitrogen or oxygen atoms.

7. The process according to claim 1, wherein L2 is a ligand of formula

in which R1 represents a hydrogen atom, a linear, branched or cyclic C1 to C6 alkyl or alkenyl group optionally substituted;

R2 and R3 represent, simultaneously or independently, a linear, branched or cyclic C1 to C6 alkyl group optionally substituted, a phenyl or naphthyl group optionally substituted; or the groups R2 and R3, taken together, form a saturated or unsaturated ring optionally substituted, having 5, 6 or 7 atoms and including the phosphorus atom to which the R2 and R3 groups are bonded;

Q represents: a group of formula

wherein n is an integer from 2 or 3, and R4 and R5 represent, simultaneously or independently, a hydrogen atom, a linear or branched C1 to C4 alkyl group optionally substituted, a phenyl ring optionally substituted; or two distinct R4 and/or R5 groups, taken together, form a C5 to C10 saturated ring optionally substituted including the carbon atoms to which each of the R4 or R5 group is bonded; or a group of formula

wherein n is an integer from 1 to 3, and two distinct adjacent R4 groups, taken together, form a C5 to C10 aromatic ring optionally substituted or a C5-C12 ferrocenediyl optionally substituted, including the carbon atoms to which each of the R4 group are bonded; or three distinct adjacent R4 groups, taken together, form a naphthalene ring optionally substituted, including the carbon atoms to which each of the R4 group are bonded; and

R6 represents a hydrogen atom, a linear or branched C1 to C4 alkyl group or an phenyl group optionally substituted; or R6, when taken together with R1, forms a C3-C9 C═N function-containing heterocycle optionally substituted and optionally containing one additional nitrogen or oxygen atom.

8. The process according to claim 1, wherein L2 is a ligand of formula (2-F) or (2-G)

wherein the dotted lines in formula (2-G) indicate the presence of a phenyl or a naphthyl group; e represents 1 or 2;

R1 and R1′ represent, simultaneously or independently, a hydrogen atom, a linear, branched or cyclic C1 to C6 alkyl or alkenyl group optionally substituted;

R2 and R3, represent, simultaneously or independently, a linear, branched or cyclic C1 to C6 alkyl group optionally substituted, a phenyl or naphthyl group optionally substituted; or the groups R2 and R3, taken together, form a saturated or unsaturated ring optionally substituted, having 5, 6 or 7 atoms and including the phosphorus atom to which the R2 and R3 groups are bonded;

R6 represents a hydrogen atom, a linear or branched C1 to C4 alkyl group optionally substituted, or a phenyl group optionally substituted; or R6, when taken together with R1, forms a C3-C9 C═N function-containing heterocycle optionally substituted and optionally containing one additional nitrogen or oxygen atom.

9. The process according to claim 1, wherein the base has a pKa above 14.

10. The process according to claim 1, wherein the base is an alkaline or alkaline-earth metal carbonates, an alkaline or alkaline-earth metal hydroxides, C1-10 amidures, C10-26 phosphazine or an alcoholate of formula (R13O)2M or R13OM′, wherein M is an alkaline-earth metal, M′ is an alkaline metal or an ammonium NR144+, R13 stands for hydrogen or a C1 to C6 linear or branched alkyl radical and R14 stands for a C1 to C10 linear or branched alkyl radical.

11. The process according claim 1, wherein the substrate is a compound of formula (1)

wherein Ra and Rb represent, simultaneously or independently, a linear, branched or cyclic C1-C30 aromatic, alkyl or alkenyl group optionally substituted; or

Ra and Rb are bonded together and form a C4-C20 saturated or unsaturated group, optionally substituted;

and wherein the substituents of Ra and Rb are a COORc, group, one, two or three halogen, ORc, NRc2 or Rc groups, in which Rc is a hydrogen atom, a halogenated C1-C2 group or a C1 to C10 cyclic, linear or branched alkyl, or alkenyl group.