Stabilizers for improved open time of aqueous coatings

A stabilizer composition comprising an AB type polymer for use in increasing Open Time of aqueous coating compositions is disclosed. The stabilizers compositions are of utility in many aqueous compositions including paints, stains, varnishes, adhesives and inks. Of particular interest is the use of the stabilizer compositions for in increasing the Open Time of latex paints as well as alkyd emulsion paints.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description
RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application Ser. No. 60/793,291, filed on Apr. 19, 2006, which is incorporated herein by reference in its entirety.

FIELD OF THE INVENTION

The present invention relates to a method of increasing the Open Time of an aqueous coating. More particularly, this invention relates to a method of increasing the Open Time of a coating of a water-borne latex paint using a new stabilizer.

BACKGROUND OF THE INVENTION

Open Time is a property of paint that is of high importance to the painter. It is defined as the maximum time paint can be re-worked prior to demonstrating permanently the deformations brought to the paint, such as brush-marks, etc. Water-borne latex paints are known to suffer from a rather short Open Time in comparison to solvent borne paints. The origin of this difference lies in the fact that the binder in water borne paints is not soluble in the continuous phase (water). However, some improvements can be made to extend the Open Time by addition of co-solvents. The demand for lowering VOC (Volatile Organic Compound) in paint requires other solutions for extending Open Time than the addition of co-solvents.

One of the traditional methods to improve Open Time of paint is to add co-solvents, and coalescing agents. The use of glycols or high-boiling solvents is known. However, this is undesirable in paints intended to meet the Volatile Organic Compound limits that are in place today. Another disadvantage of the addition of addition of solvents is the lowering of block resistance, and dirt pick-up can become a problem. EP 1500589 states that an Open Time of 10 min is considered optimal.

EP1500689A1 publication describe the preparation and composition of a water borne coating of an acrylic latex prepared and stabilized with a protective colloid, pigments and extenders, wetting agents or leveling agents, coalescents, and thickener. The coating composition relies upon the presence of PVOH (polyvinyl alcohol) as stabilizer; also, PVOH copolymerized with ethylene (marketed by Kuraray Co. Ltd.) can be used or partial acetylation of the OH groups. Although intended for solvent free paints, EP 1500689 shows the improved Open Time in a gloss paint contains nearly 10% of coalescing agents and co-solvents (nearly 10% PG (propylene glycol) and Texanol® ester alcohol, available from Eastman Chemicals).

U.S. Pat. No. 6,303,189 Patent discloses the addition of a polyurethane (PU) dispersion to an aqueous coating, where Tg (glass transition temperature) of the polyurethane dispersion is less than that of the latex polymer. The PU dispersions have small particle size (30 nm) and a low Tg (˜−50° C.-˜−10° C.). Yet the level of co-solvent (propylene glycol) still was roughly 9.4 wt %.

EP 593,151A1 publication describes an improvement in Open Time by developing a latex having still reactable groups, or mix the latex with compounds that have complementary reactable groups.

WO 02/32980 publication demonstrates the preparation and use of a water dispersible (self) crosslinkable polyurethane, having a relatively low molecular weight. This binder crosslinks by various possible chemical reactions.

EP 62,106A1 publication discloses the manufacturing of acrylate latex and styrene-acrylic latex stabilized with PVOH as protective colloid. Preferably, the latex is stabilized without surfactants.

EP 538,571A1 publication discloses the preparation of latex via a surfactant free emulsion polymerization of a selected mixture of monomers with selected PVOHs. This patent does not mention Open Time as a critical parameter to be improved.

U.S. Pat. No. 4,552,908 discloses an improvement of Open Time in paints by using low molecular weight oligomers that are water dispersible film formers, and having coupling moieties.

U.S. Pat. No. 5,270,380 also discloses the use of a binder that has reactable groups.

U.S. Pat. No. 6,040,368 discloses the preparation and use of a latex with acetoacetate, acetoacetamide, cyanoacetate and cyanoacetamide as pendant groups. Also disclosed is the use of polyether monoamine or diamine having primary amine or secondary amine functionality and an alkylpolyglucoside. These polymers are coupled through reaction of the diamine with the acetoacetate to form enamine structures.

U.S. Pat. No. 6,762,230 discloses a coating with coalescent and a latex polymer, in which the coalescent may be reactable.

SUMMARY OF THE INVENTION

This invention relates to a method of increasing the Open Time of a coating. The method comprises the manufacturing and use of additives that prolong the Open Time of water borne paints and may have a degree of rheological functionality.

This invention relates to a stabilizer composition for use in increasing Open Time of an aqueous coating composition comprising an AB type polymer. The B of the AB type polymer may be any type of water-soluble/water dispersible oligomer or polymer. The A of the AB type polymer is covalently connected to B and is a “comb type” of structure that has the following formula:

In the above formula, R comprises a C1 to C30 hydrocarbon, which may be linear or branched, aliphatic or aromatic or combinations thereof. R1 may be H, CH3, or C2H5. R2 may be CH2O, CO2, CONH, or CH2. The identity of the R2 can be the same or different in each occurrence of the AB type polymer. R3 may be either an H or OH. The “n” denotes an integer from 1 to 100. The “m” may be either 0 or 1.

The aqueous coating composition which the stabilizer of the present invention may be used can selected from the group consisting of paints, stains, varnishes, adhesives and inks.

The stabilizers of the present invention are particularly suitable for use in increasing the Open Time in architectural latex paint, but may also be employed in alkyd emulsion paints to increase its Open Time.

DETAILED DESCRIPTION OF THE INVENTION

It has been surprisingly found that Open Time in paints can be significantly increased by using a stabilizer of the present invention. This stabilizer may be made at a preliminary stage in the paint manufacturing process or it may be added after the paint has been formulated thereby overcoming the necessity of requiring the stabilizer to be already in the latex preparation stage. Thus, it is easier and more versatile to use. It also shows the benefits in truly solvent free paints where Open Time is a problem.

The stabilizer composition of the present invention is of use in increasing Open Time of an aqueous coating composition and is an AB type polymer. The “B” segment of the AB type polymer may be any type of water-soluble/water dispersible oligomer or polymer. The B segment may be selected from the group consisting of polyethylene glycol, polyactalpolyether (PAPE), acrylate, acrylamide and polyethylene oxide. A preferred “B” of use in the present invention is polyethylene glycol. Another preferred “B” of use in the present invention is polyactalpolyether (PAPE). The polyethylene glycols that are of use in the stabilizers of the present invention may be selected from the group consisting of monomethylpolyethylene glycol and hydroxypolyethylene glycol. The polyethylene glycol may be a methoxy-end-capped polyethylene glycol. The “B” of use in the present invention may be a mono functional oligomer.

The “A” of the AB type polymer is covalently connected to “B” and has the following formula:

In the above formula, R comprises a C1 to C30 hydrocarbon, which may be linear or branched, aliphatic or aromatic or combinations thereof. R1 may be H, CH3, or C2H5. R2 may be CH2O, CO2, CONH, or CH2. The identity of the R2 can be the same or different in each occurrence of the AB type polymer. R3 may be either an H or OH. The “n” denotes an integer from 1 to 100. The “m” may be either 0 or 1.

The “A” may be selected from the group consisting of polyphenoxy glycidyl ether, methylphenyl glycidyl ether, ethylhexylglycidyl ether, phenyl glycidyl ether, and alkali glycidyl ether. Preferably the “A” is methylphenyl glycidyl ether or ethylhexylglycidylether.

The stabilizers of the present invention are of particular use in increasing the Open Time in aqueous compositions. In addition to the stabilizer, the aqueous compositions also contain a film-forming polymer. In many architectural paints, the film-forming polymer is a latex. In other end uses, the film-forming polymers may be used and selected from the group consisting alkyl acrylates, alkoxy acrylates, alkyl methacrylates, alkoxy methacrylates, vinyl esters of saturated carboxylic acids monoolefins and conjugated dienes.

The film-forming polymer typically contains at least one ethylenically unsaturated monomer. This ethylenically unsaturated monomer may be selected from the group consisting of acrylic acid, methacrylic acid, butyl acrylate, methyl methacrylate, 2-ethylhexyl acrylate, acrilic esters, styrene, vinyl ethers, vinyl and vinylidene halides, N-vinyl pyrrolidone, ethylene, propylene or greater alpha-olefins, allyl amines, allyl esters of saturated monocarboxylic acids and amides thereof, allyl acetate, allyl propionate, allyl lactate, their amides, mixtures thereof and mixtures thereof.

These stabilizers are useful by post-addition in the paint, but are not restricted to addition in this stage, i.e. these additives might also be employed in the pigment paste preparation (grinding stage), in preparing the aqueous continuous phase, and also can be employed as stabilizer in preparing the latex. Therefore, the stabilizer composition may be added to the aqueous solution before the film-forming polymer is dispersed or emulsified in the aqueous solution, after the film-forming polymer is dispersed or emulsified or at the same time the film-forming polymer is dispersed or emulsified.

The dosage level at which these stabilizers work is extremely low, in contrast to the use of co-solvents, that require a high dosage level before showing apparent differences in Open Time. The stabilizer composition of the present invention may bu used at dosage levels of above about 0 to about 10 wt % of the aqueous coating composition, preferably about 0.1 to about 3 wt %, more preferably 0.5 to about 1 wt % of the aqueous coating composition.

The invention is based on the concept of delaying the film formation of binder particles or film-forming polymers in the paint by improving their stability toward coalescence and coagulation. This was already noted as being the major driving force behind Open Time.

These stabilizers contain a moiety that has a very high affinity for the latex particles and another part that is highly soluble in the continuous phase of the paint formulation.

The high affinity for latex part is chemically constructed in such a way that desorption from the latex is extremely unlikely. Thus, the stabilizer of the present invention may be viewed as being irreversibly adsorpted to the latex particle.

The stabilizers of this invention can be used as post-stabilizers but also may be employed as thickener for the paint thereby affecting the paint's rheological properties and may stabilize the paint during production of the paint. When employed as thickener, these chemicals described in the inventions serve to prolong Open Time of paint.

The stabilizers of the present invention are of utility in may be used in many aqueous compositions selected from the group consisting of paints, stains, varnishes, adhesives and inks. Of particular interest, is the use of the stabilizers of the present inventions in increasing the Open Time of latex paints. The stabilizers of the present invention are also of utility in increasing the Open Time of alkyd emulsion paints.

One of the advantages of the current invention is the applicability in various systems. The additives described in this invention can be used in the latex preparation, in the paint preparation as thickener, and as post additive after complete paint is prepared. Also, combinations of the use are possible. One advantage of this invention is in creating excellent stability of the binder articles in the system (either during latex manufacturing, or as post stabilizer), most probably due to a very good adsorption on the latex. This is one of the major advantages over the use of regular surfactants that tend to desorb whenever this is more energetically more favorable.

The stabilizers of the present invention may be used as surfactants, dispersants, encapsulants, stabilizers for emulsion polymerization and of alkyd emulsions as well as other dispersions.

The aqueous compositions are typically formulated with other components to impart desired properties on the product in use as well as the final product. These additional components may be selected from the group consisting of pigments, fillers, thickeners, biocides, mildewcides, surfactants, dispersants and defoamers.

Definitions

“Open Time”: the length of time a coating remains wet enough to allow for brushing in at the laps, synonymous to Wet Edge time.

“Wet edge”: the edge of a wet painted area which remains workable.

The examples are merely set forth for illustrative purposes, but it is to be understood that other modifications of the present invention can be made by skilled artisans in the related industry without departing from the spirit and scope of the invention. The parts and percentages used in the examples being by weight unless otherwise indicated.

Examples 1, 2, 3, 4 and 5 are presented to describe the synthesis routes for preparing the stabilizers of the present invention.

EXAMPLE 1

As shown, the stabilizer is of the AB type, where the composition of the B was polyethylene oxide, A was polyphenoxy glycidyl ether an the stabilizer was produced according to the below Scheme 1.

A mixture of PEG-Monomethyl (Mw=5 K, 41.5 g), NaOH (0.7 g) was heated to 80° C. for 1 hour, methylphenyl glycidyl ether (7.0 g) was added. The mixture was heated at 120° C. for 8 hours. The product was dissolved in toluene (200 mL) and precipitated in hexane (600 mL) giving a solid (45 g) after washing and drying. It was designated 1A.

Similarly, another composition of polyphenyl glycidyl ether comb with PEG-O-Me was made from PEG-O-Me (60 g), NaOH (1 g) and phenyl glycidyl ether (12.5 g). The product was designated as 1B.

In the above experiments, the comb material was made from a mono-functional PEG oligomer. It is also convenient to make this mono functional oligomer through a hydrolysable multi-functional oligomer. The hydrolysable linkage could be an acid-sensitive connective groups, such as acetal, ester, or a base sensitive connective groups, such as carbonate, ester, or amide.

EXAMPLE 2

The following examples show hydroxy-PEG-polyhydrophobe oligomers made by hydrolysis of telechelic-polyhydrophobe-PEG-acetal oligomers.

Hydroxy-PEG (4K)-polyphenyl glycidyl ether was used in the production of stabilizer material.

A mixture of PEG (4K, 60 g), NaOH (1.3 g) was heated to 80° C. for 1 hr. Dibromomethane was added (1.3 g) and the reaction mixture was continued at 80° C. for 2 hr. Methylphenylglycidyl ether (4 g) was added. The reaction was kept at 120° C. for 4 hr. After cooled down to 80° C., 50 mL of toluene, H2SO4 (3 mL, 3M) and water (3 mL) were added and the mixture was stirred for 4 hr. The product was isolated by precipitation in hexane (500 mL) and by soaking in IPA (500 mL). After drying, 62 g of material was collected. SEC gave 90% mono-capped material. 1H NMR indicated that the material has 5% hydrophobe by weight. The product was designated as 2A.

Hydroxy-PEG (8K)-polyphenyl glycidyl ether was used in the production of stabilizer material.

A mixture of PEG (8K, 60 g), NaOH (1.3 g) was heated to 80° C. for 1 hr. Dibromomethane was added (0.65 g) and the reaction mixture was continued at 80° C. for 2 hr. Methylphenylglycidyl ether (4.25 g) was added. The reaction was kept at 120° C. for 4 hr. After cooled down to 80° C., 50 mL of toluene, H2SO4 (3 mL, 3M) and water (3 mL) were added and the mixture was stirred for 4 hr. The product was isolated by precipitation in hexane (500 mL) and by soaking in IPA (500 mL). After drying, 63 g of material was collected. SEC gave 80% mono-capped material. 1H NMR indicated that the material has 5% hydrophobe by weight. The product was designated as 2B.

Hydroxy-PEG (20K)-polyphenyl glycidyl ether was used in the production of stabilizer material.

A mixture of PEG (20 K, 53 g), NaOH (1.3 g) was heated to 80° C. for 1 hr. Dibromomethane was added (0.23 g) and the reaction mixture was continued at 80° C. for 2 hr. Methylphenylglycidyl ether (7 g) was added. The reaction was kept at 120° C. for 4 hr. After cooled down to 80° C., 50 mL of toluene, H2SO4 (3 mL, 3M) and water (3 mL) were added and the mixture was stirred for 4 hr. The product was isolated by precipitation in hexane (500 mL) and by soaking in IPA (500 mL). After drying, 57 g of material was collected. SEC gave 85% mono-capped material. 1H NMR indicated that the material has 7.9% hydrophobe by weight. The product was designated as 2C.

Other examples were produced using similar methods as above examples 2A, 2B and 2C. These one example is described as comprising PEG (12K)/PGME (60 g/14 g), estimated to comprise 30% double combs in the “A” section of the polymer. This product was designated as 2D. Another example is described as comprising PEG (20K)/PGME (60 g/14 g), estimated to comprise 30% double combs in the “A” section of the polymer. This product was designated as 2E. Another example is described as comprising PEG (12K)/PGME (60 g/4 g), estimated to comprise 30% double combs in the “A” section of the polymer. This product was designated as 2F. Another example is described as comprising PEG (20K)/PGME (60 g/4 g), estimated to comprise 30% double combs in the “A” section of the polymer. This product was designated as 2G.

EXAMPLE 3

Preparation of various stabilizers of the present invention; 3A; 3B; 3C, 3D; 3E; 3F; 3G, 3H and 3I.

The reaction was carried out in a 500 ml 3-neck round bottom flask, which was equipped with a temperature controlled heating mantle, thermo-couple, reflux condenser (on top connected with gas bubbler to visualize gas-flow), rubber septum to inject chemicals, nitrogen inlet, stirrer motor, glass stirrer rod with removable Teflon blade, gas seal and bearing.

PEG 8K or PEG 10K (60 g) and NaOH (1.23 g) were blended under N2 blanket and heated to 80° C. and kept for 15 min. while stirring in order to dissolve the NaOH. The products 3A and 3C were made using methoxy-end-capped PEG (mono capped) instead of regular PEG. The product 3H, was similar to 3A except that it comprises 16% MPGE by weight instead of 17% MPGE found in 3A.

The crosslinker (preheated at 50° C.) DBM (dibromomethane) was added by syringe via the septum; the amount DBM used was exactly 0.5 mole of the PEG used. The mixture was kept at 80° C. for 1 hour in order to react. The products 3A and 3C were made without this coupling step. In the 3B, 3D, 3E, and 3F products, dibromomethane was used. In the preparation of 3B and 3G, 10 ml of toluene were added after reaction with dibromomethane.

After reaction, the hydrophobic reagent (e.g. alkali glycidyl ether) was injected via the septum, in an amount of 7.58 gram (=12 wt %) MPGE or 10.2 g (=17 wt %) MPGE or 11.57 g (=15% EHGE, ethylhexylglycidyl ether). The temperature was raised to 120° C. and kept at that temperature for 2 hours. After reaction, the temperature was decreased to 100° C.

For the hydrolysis step, H2SO4 1.5 M (about 12 ml) was added, and allowed to react for 4 hours. The product 31 was solid HM-PAPE (C16-PAPE) which was hydrolyzed.

The procedure after hydrolysis depended of the presence of toluene in the reaction mixture.

In the case when no toluene was present, the reaction mixture was poured into an aluminum pan and cooled down to room temperature. The product was scooped out of the pan and was further purified.

When toluene was present, an additional 100 g of toluene was added to the reaction mixture. The temperature was kept at 80° C. for 15 minutes. Upon stirring, the mixture was cooled down to room temperature.

The reaction mixture was decanted and precipitated in 200 g of hexane and further purified.

The purification of the product was carried out as follows: The precipitate in hexane was filtrated under “vacuum” using a Buchi-funnel equipped with a S&S rundfilter 5893 Ø90 mm Ref. no. 300209. After filtration the residue was scooped out of the funnel, ground in a mortar, and put back again in the Buchi-funnel. The residue was then washed with totally 100 g ethyl acetate (EA) as follows: The EA was added until all reaction product was covered by liquid, then filtering was carried out under atmospheric conditions until the residue had a ‘dry’ appearance, then a very low “vacuum” (1000 mbar) was applied until the bulk of the liquid was passed. Then full vacuum was applied until all liquid was passed. This procedure was repeated until all EA was used. After this, the same wash procedure was carried out with hexane. The product was further dried for 12 hr at 45° C.

EXAMPLE 4

PEG 4K (12 g) and PEG 5K (45 g) and NaOH (2.88 g) were blended under N2 blanket and heated to 80° C. to let the PEG melt. The mixture was kept at 80° C. and 2.16 g of pre-heated (50° C.) trimethylolpropanenethoxylate (TMPE) was added through injection. The mixture was kept at 80° C. for 1 hour in order to react. The crosslinker, preheated at 50° C., DBM (2.08 gram in 15 ml toluene) was added by syringe via the septum. The mixture was kept at 80° C. for 1 hour in order to react. After reaction, the hydrophobic reagent (e.g., alkali glycidylether) was injected via the septum in an amount of 10.13 grams (=16 wt %) MPGE or 9.33 (=14 wt %) EHGE (ethylhexylglycidylether) or 10.67 g (=16 wt % EHGE). The temperature was raised to 120° C. and kept at that temperature for 2 hours. Another 100 grams of toluene was added and the reaction mix was decanted and precipitated in 200 g hexane. The precipitate in hexane was further purified as described above.

EXAMPLE 5 Preparation of Various Stabilizers (Invention)

The reaction steps to produce the samples 5A, 5B, 5C, 5D, 5E are set forth below and were produced according to the below schematic representation.

Compositions of stabilizers produced in Examples 1-5 are listed below in Table 1.

TABLE 1 Designation Chemical Description 1A MPEG (5K)/PGME (41.5 g/7 g) single chain comb NaOH 0.7/45 1B MPEG (5K)/PGME (60 g/12.5 g) single chain comb 1 g/70 2D PEG (12K)/PGME (60 g/14 g) estimated 30% double combs 2E PEG (20K)/PGME (60 g/14 g) estimated 30% double combs 2F PEG (12K)/PGME (60 g/4 g) estimated 30% double combs 2G PEG (20K)/PGME (60 g/4 g) estimated 30% double combs 3A Linear 5K 17% MPGE 3B Linear 8K 12% MPGE 3E Linear 15K 12% MPGE 3C Linear 10K 12% MPGE 3D Linear 8K 12% MPGE 4A Branched 6K 16% MPGE 4B Branched 6K 14% C8 4C Branched 6K 16% C8 3H Linear 5k 16% MPGE 3G Linear 5k 16% C8 3E Linear 10K 12% MPGE 3I Linear 8k unknown % C16 5E MPGE-PEG 4K SO3Na 5D MPGE-PEG 12K SO3Na 5A MPGE-PEG 12K 5B MPGE-PEG 5C MPGE-PEG SO3Na

EXAMPLE 6 Use of the Stabilizer Polymer Materials as Additives in Water Borne Latex Paints

This Example 6 describes the use of the stabilizer polymers of the present invention as additives in various water borne paint formulations.

The stabilizers were added to the paint formulation after preparing the complete paint. Mixing and equilibrating of the paint+stabilizer was carried out by gentle tumbling overnight (A&D paints).

The paints were individually prepared. The additive was dissolved in water in high concentrations prior to addition to the paint, and mixed for 1 hour with the base paint, by using a Caframo type RZR1 laboratory mixer fitted with a 2-inch diameter, 3-vane propeller blade. The paint was subsequently thickened by using an amount of thickener that without the stabilizer would have resulted in a paint viscosity of 100 KU viscosity.

Of all paints the Open Time was evaluated according to the following procedures:

Open Time X-test A&D:

A 100 μm or 200 μm drawdown of the test paint is applied on a Leneta scrub test panels (form P121-10N). Immediately after drawing down the paint, eight X-shaped crosses were made in the film. The “X”s were drawn using an eraser from the head of a pencil. The “X” should be made so that no paint is visible on the drawdown card at a width of 5 mm. Prior to recoating of “X”s, the paint brush (Copenhagen Gold Marine #16) was prepared. The preparation of the brush was accomplished by coating the brush with paint to be tested and then applying paint to a drawdown card with a minimum of twenty strokes. Depending on the expected Open Time, the first recoating of an “X” was started between 1 and 10 minutes after the wet film application. Just before recoating 0.6 g paint was applied in the center of the “X”. This recoating was accomplished with a minimum of 20 strokes or until the brush drag increased due to severe resistance of the brush.

The same procedure was then repeated every 2 minutes until the “X” stayed visible through the fresh paint.

After the test was completed, the test panel was allowed to dry overnight.

Open Time X-test RC

A 10 mil drawdown of the test paint was applied on a plain block Leneta scrub chart. Immediately after drawing down the paint, six X-shaped crosses were made in the film using the eraser head of a pencil. The “X” was made so that no paint was visible on the drawdown card at a width of one-quarter inch. Prior to recoating of “X”s, the paint brush (1½″ brush) was prepared. The preparation of the brush was accomplished by coating the brush with paint to be tested and then applying paint to a drawdown card with a minimum of twenty strokes. Following preparation of the brush, the brush was once again loaded with fresh paint to the point of just being wet. Three minutes after the wet film application, step A, the first recoating of an “X” was performed. This recoating was accomplished with a minimum of 20 strokes or until the brush drag increased due to severe resistance of the brush.

The same procedure was then repeated every minute until the workability was not realistic anymore due to setting-up of the first applied layer. Between these two minute intervals, the paint brush was covered in aluminum foil to reduce the risk of drying. After the test was completed, the test panel was allowed to dry overnight.

The results of enhancement in Open Time upon using the invention as additive are set forth in Tables 3, 4, 5, 6, and 10.

Open Time Test Method

Materials needed for Open Time testing:

Paints to be examined

Glass plate or other apparatus for making drawdowns

Leneta Standard Range Anti-Sag Meter (3-12 mils)

Leneta Plain Black Drawdown Chart (Form BH)

Stopwatch or other timing device

Plastic transfer pipettes (for transferring paint to Leneta chart)

1½ inch wide paint brush

Adhesive tape

    • 1. The tape was used to secure the Leneta BH chart to a flat, level surface in preparation for paint drawdown and testing. These charts were larger than the opacity charts typically used for drawdowns.
    • 2. The test paint was drawn down using the Standard Range Anti-Sag Meter, down the middle of the chart lengthwise.
    • 3. The stopwatch was started immediately after the drawdown had been made. The test was performed in one-minute intervals.
    • 4. After one minute had passed on the stopwatch, the paint brush was dipped into the test paint and applied across the stripes of paint made by the anti-sag meter. The paint was brushed on from the 12-mil stripe to the 3-mil stripe (right to left), for a total of 20 strokes.
    • 5. Step 3 was repeated at two minutes, three minutes, etc, until there is no longer room for another stripe to be painted across the chart. This usually happened after 6 or 7 stripes had been painted.
    • 6. The stopwatch was turned off after final stripe had been painted on the Leneta chart.
    • 7. The tape was removed from the Leneta chart and Leneta chart from drawdown area.
    • 8. The newly painted chart was allowed to dry overnight at ambient conditions before evaluating.
    • 9. The endpoint was considered to be at what time a narrow ridge of dried paint was visible on the right edge of the 5-mil strip of paint. This varied from paint to paint. The ridge should be a complete and unbroken line through the brushed-out area of paint.

Notes on Procedure:

    • 10. If no endpoint was visible after 7 minutes had elapsed, another Leneta chart was prepared for the test paint by following Steps 1-3, above. However, the painting was begun across the drawdown at 7 minutes, rather than 1 minute. Continued painting strips in one-minute intervals as per the original procedure outlined above. This variant will take Open Times out to 13 minutes, which usually is sufficient to determine an endpoint.

A replicate series of paint samples/drawdowns can be used to determine an average value for Open Time. A minimum of two charts is recommended; however, for screening purposes, one chart may be satisfactory. Use pass controls or fail controls as required if testing different formulations of a given paint type.

COMPARATIVE EXAMPLE 1

Use of regular surfactants and cosolvents additives in water borne latex paints as a comparison to the stabilizers of the present invention are described.

The procedure was followed as described in Example 6 with the exception that now a regular surfactant or co-solvents were employed as additive in place of the stabilizers of the present invention. The results of Open Time measurements are mentioned in Tables 14 and 15.

EXAMPLE 7

Use of the stabilizers of the present invention as rheology modifiers in water borne latex paints is described.

Paints were prepared according to the formulations mentioned in Table 2. The stabilizers of the present invention were employed as rheology modifier. In Table 7, 8, 9, 11, 12 and 13, data are presented showing the performance of these paint formulations.

EXAMPLE 8

Use of the stabilizers of the present invention as additives in water borne alkyd emulsion paint formulations is disclosed.

The results of enhancement in Open Time upon using the stabilizer of the present invention as additive are mentioned in Table 10.

Furthermore these materials may be used as post-additive in water borne coatings. Also these compounds can be used as rheology modifier in water borne coating thus serving dual functions.

TABLE 2 Paint formulations used A&D Semi-gloss paint with VOC free acrylic latex: Ingredient parts by weight water 56 AMP 90 2 Dispex GA 40 6 Dehydran 1293 5 Preventol D7 2 Tioxide RHD2 179 Omyacarb CL extra 79 (disperse 20 min 4000 t) Surfynol 104E 6 Neocryl XK 96 501 Dehydran 1293 9 Thickener x Water 155 Total 1000 A&D solvent free PVC 70 flat paint: Ingredient parts by weight water 164 Calgon N 3 Lopon 894 3 Agitan 315 3 Tioxide TR-92 100 China-Clay Speswhite 50 Polestar 200 P 50 Omyacarb 2 GU 264 Micro Talc WT 1 47 Agitan 315 1 Prevantol D7 2 Water 25 Mowilith LDM 1871 158 Thickener x Water 130 Total 1000 Vinyl-Acrylic (UCAR 379G) interior semi-gloss pastel base paint (57 g/l VOC): Designation Ingredient parts by weight Grind Water 140.0 Hegman >6 Propylene glycol 8.0 Texanol 5.0 Tamol 731A 10.0 Tergitol NP-9 3.0 AMP-95 2.5 Drew Plus I-475 2.0 Ti-pure R-900 200.0 Polygloss 90 50.0 Letdown Drew Plus L-475 2.0 Hold Latex 400.0 Thickener & Water 200.0 Total 1022.5 Paint properties: % PVC: 27.1 % Vol solid: 31.7 % coalescent: 6.8 % volatile: 53.06 % water 51.54 VOC (g/l)): 56 Density, lbs/gallon: 10.56 25 PVC Zero VOC interior semi-gloss paint Desig- parts by parts by nation Ingredient weight Ingredient weight Grind Water 136.3 Water 136.3 Tamol 731A 12.0 Tamol 731A 12.0 Ammonia 2.5 Ammonia 2.5 Strodex PK-90 2.0 Strodex PK-90 2.0 Trition CF-10 2.0 Trition CF-10 2.0 Drew Plus L-475 1.5 Drew Plus L-475 1.5 Proxel GXL 1.5 Proxel GXL 1.5 Ti-pure R-706 230.0 Ti-pure R-706 230.0 Atomite 30.0 Atomite 30.0 Attagel 50 5.0 Attagel 50 5.0 Hold UCAR 300 452.0 Optive 130 497.2 Drew Plus L-475 3.0 Drew Plus L-475 3.0 Thickener & Water 151.5 Thickener & water 106.3 Total 1061.5 Total 1061.5 Paint % PVC: 24.8 % Vol solid: 35.0 % weight properties: solids: 48.6 Density, lbs/gallon: 10.6 VOC (g/l)): <1 For a <50 g/l VOC paint to each paint (1061.5 parts) 18.0 parts of ethyleneglycol was added.

Vinyl-Acrylic (UCAR 300) Interior Flat Paint (PVC 60):

TABLE 3 Open Time of A&D semi gloss paint upon post-addition of stabilizer additive % added Sample code stabilizer Brookfield Thickener added (weight on Open Time (min), viscosity Paint code used in paint stabilizer total paint) conditions (C., % RH) (mPa · s) TK 070604 C Aquaflow ® none 0 5 (20° C., 60% RH) 2250 NLS 200 rheological modifier TK 070604 C Aquaflow ® none 0 4 (21° C., 60%) NLS 200 rheological modifier TK 070604 C Aquaflow ® none 0 3.75 (22° C., 60%) NLS 200 rheological modifier TK 070604 C Aquaflow ® 1A 0.1 3.5 (22° C., 60%) NLS 200 rheological modifier TK 070604 C Aquaflow ® 1A 0.5 5 (22° C., 60%) NLS 200 rheological modifier TK 070604 C Aquaflow ® 1A 1 8 (21° C., 60%) 1900 NLS 200 rheological modifier TK 070604 C Aquaflow ® 1A 2.5 8 (21° C., 60%) 2300 NLS 200 rheological modifier TK 070604 C Aquaflow ® 1A 5 8 (21° C., 60%) 2000 NLS 200 rheological modifier TK 080604 E Natroso ® l 250 none 0 3 (20° C., 60% RH) 9500 HBR HEC TK 080604 E Natrosol ® 250 none 0 3.5 (21° C., 60%) HBR HEC TK 080604 E Natrosol ® 250 none 0 4.5 (22° C., 60%) HBR HEC TK 080604 E Natrosol ® 250 1B 0.1 5.5 (22° C., 60%) HBR HEC TK 080604 E Natrosol ® 250 1B 0.5 6.5 (22° C., 60%) HBR HEC TK 080604 E Natrosol ® 250 1B 1 6 (21° C., 60%) 8000 HBR HEC TK 080604 E Natrosol ® 250 1B 2.5 6 (21° C., 60%) HBR HEC TK 080604 E Natrosol ® 250 1B 5 6 (21° C., 60%) 7900 HBR HEC Aquaflow ® NLS 200 rheological modifier is available from Hercules Incorporated. Natrosol ® 250 HBR hydroxyethylcellulose is available from Hercules Incorporated.

TABLE 4 Open Time of A&D semi gloss paint upon post-addition of 1 wt % stabilizer additive Open Conditions Stormer ICI Sag Product Product Time (RH(%), viscosity viscosity Leneta NYPC resistance code composition (min) T(° C.)) (KU) (cP) leveling leveling (□m) none — 4.5 60%, 20° — 95 9 5 350 3A Lin 5K 17% 7 60%, 20° 81 60 9 5 300 MPGE 3B Lin 8K 12% 7 60%, 20° >150 220 1 1 600 MPGE none — 4.5 55%, 20° 102 95 9 5 350 3D Lin 15K 12% 6.5 55%, 20° — 85 9 5 300 MPGE 3E Lin 10K 12% 6.5 55%, 20° 108 110 9 5 350 MPGE 3F Lin 8K 12% 7 55%, 20° — 110 9 5 350 MPGE none — 5 55%, 21.5° 102 — — — — 4A Brnch 6K 6.5*) 55%, 21.5° 89 — — — — 16% MPGE 4B Brnch 6K 6.5 55%, 21.5° — — — — — 14% C8 4C Brnch 6K 6.5 55%, 21.5° — — — — — 16% C8 4A Brnch 6K 7.5 55%, 21.5° 89 — — — — 16% MPGE None 4.5 55%, 21° — — — — — 3G Lin 10K 12% 7 55%, 21° — — — — — MPGE 3I Lin 8K C16 7 55%, 21° — — — — — 3C Lin 5K 15% 6.5 55%, 21° — — — — — C8 *0.5 wt % used instead of 1 wt %

TABLE 5 Open Time of A&D PVC 70 flat paint upon post-addition of stabilizer additive Open Time Conditions Product code Product Composition (min) (RH(%), T(° C.)) None — 4.5 55%, 21, 5° 5C MPGE-PEG 4K SO3Na 6 55%, 22° 5B MPGE-PEG 12K SO3Na 5.5 55%, 22° 5A MPGE-PEG 12K 5.5 55%, 22° None — 4 55%, 21° 5D MPGE-PEG 5 55%, 21° 5E MPGE-PEG SO3Na 5.6 55%, 21° 5C MPGE-PEG 4K SO3Na 6.5 55%, 21°

TABLE 6 Open Time of RC 0-VOC semi gloss paint (PVC 25) upon post-addition of stabilizer additive % added Sample stabilizer Open Time (min), Stormer ICI Latex used Thickener used in code added (weight on conditions viscosity viscosity in paint paint stabilizer total paint) (F., % RH) (KU) (Poise) Optive 130 Aquaflow ® NLS 200 none 0 1.5 (73 F., 50% RH) 109 0.53 rheological modifier Optive 130 Aquaflow ® NLS 200 1A 1.5 3.5 (73 F., 50% RH) 84 0.65 rheological modifier Optive 130 Aquaflow ® NLS 200 1B 1.5 3 (73 F., 50% RH) 87 0.60 rheological modifier UCAR 300 Natrosol ® 250 MBR none 0 1.5 (73 F., 50% RH) 103 0.62 HEC UCAR 300 Natrosol ® 250 MBR 1A 0.95 3 (73 F., 50% RH) 107 0.80 HEC UCAR 300 Natrosol ® 250 MBR 1B 1.5 4 (73 F., 50% RH) 94 0.90 HEC Natrosol ® 250 MBR hydroxyethylcellulose is available from Hercules Incorporated.

TABLE 7 Open Time of RC semi gloss pastel base with UCAR 379G latex, 57g/l VOC paints having the Stabilizer additives as single paint thickener Stormer ICI Open Thickener Carrier for viscosity viscosity Time code thickener TE (wt %) (KU) (Poise) (min) Leveling X33487- Water/Butylcarbitol 1.47 98 1.254 8 5 95BC (75/25) Aquaflow ® Water/Butylcarbitol 0.58 101 1.19 5.5 6 NLS 200 (80/20) rheological modifier

TABLE 8 Open Time of RC 25 PVC Zero VOC interior semi-gloss paint based on UCAR 300, having the Stabilizer additives as single paint thickener ICI Open Stormer viscosity 60° Sag Leneta Time Stabilizer TE (wt %) viscosity (KU) (Poise) gloss resistance Leveling (min) Aquaflow ® 0.46 100 2 NLS 200 rheological modifier MBR 0.68 101 0.6 43.3 16  1 1 2G 1.99 103 2.5 34.5 8 10 5 2F 2.07 101 2.3 33.6 6 10 5.5 2E 0.56 107 0.5 46.6 24+ 5 3 2D 0.42 98 0.3 42.7 24+ 6 3

TABLE 9 Open Time of RC 25 PVC Zero VOC interrior semi-gloss paint based on UCAR 300, having the Stabilizer additives as rheology modifier in combination with Aquaflow NLS 200 Wt % Stormer Open Time (min), Stabilizer Wt % NLS 200 viscosity measured by Stabilizer on paint on paint (KU) Open Time (min) different operator None 0 0.46 100 <3 <3 Triton CF-10 0.40 0.56 98 3 <3 1B 1 0.56 102 <3 <3 2F 1 0.21 99 4.5 6 2G 1 0.21 101 5 6 2G 0.5 0.28 96 <3 <3

TABLE 10 Open Time of A&D alkyd emulsion paint upon post-addition of stabilizer additive Thick- Sample % added ener code stabilizer used added (weight on Open Time (min), Paint code in paint stabilizer total paint) conditions (C, % RH) DK100602 None 0 4.5 (19.5° C., 55% RH) 1A 1 5 (19.5° C., 55% RH) 1A 1.85 5 (19.5° C., 55% RH) 1B 1 5 (19.5° C., 55% RH) 1B 2.5 5 (19.5° C., 55% RH)

TABLE 11 Open Time of RC 0-VOC semi gloss paint (PVC 25) with Rovace 990 as latex upon post-addition of stabilizer additive Weight % Open Time Test Additive code additive Method (minutes) None 0 3 Ethyleneglycol 3 9 3B 1 7.5 3H I 6.5 3H 0.5 5.5 3G 1 7

TABLE 12 Open Time of RC 0-VOC semi gloss paint (PVC 25) with Rhoplex ® SG30 as latex upon post-addition of stabilizer additive Weight % Open Time Test Additive code additive Method minutes None 0 3.8 Ethyleneglycol 3 10 3B 2 4.7

TABLE 13 Open Time of RC 60 PVC paint with UCAR 300 as latex upon post- addition of stabilizer additive Weight % Open Time Test Additive code additive Method minutes None 10 4 Ethyleneglycol 3 9 4A 2 7 3D 2 7

TABLE 14 Open Time of A&D semi gloss paint upon post-addition of regular surfactant (comparison) % added Open Sample stabilizer Time (min), Thickener code added (weight on conditions Paint code used in paint stabilizer total paint) (° C., % RH) TK 070604 C Aquaflow ® None 0 3.5 (22° C., NLS 200 50%) rheological modifier TK 070604 C Aquaflow ® Triton CF-10 0.5 3.5 (22° C., NLS 200 50%) rheological modifier TK 080604 E Natrosol ® 250 none 0 4 (22° C., HBR HEC 50%) TK 080604 E Natrosol ® 250 Triton CF-10 0.5 4 (22° C., HBR HEC 50%) Triton CF 10 is a commonly used surfactant in paint, a 100% nonionic

TABLE 15 Open Time of RC 0-VOC semi gloss paint (PVC 25) upon post-addition of solvents (comparison) Sample code % added stabilizer Latex used added (weight on latex Open Time in paint Thickener used in paint stabilizer solids) (min) Optive 130 10% solution of HMPE (NLS Archer ™ RC 6 3 200 type) reactive coalescent, available from ADM Brands Optive 130 10% solution of HMPE (NLS Velate ® 368 alkyl 6 2 200 type) benzoate ester, available from Vesicol Chemical Corporation Optive 130 10% solution of HMPE (NLS Benzoflex ® 9- 6 2.5 200 type) 88 plasticizer, available from Vesicol Chemical Corporation Optive 130 10% solution of HMPE (NLS Benzoflex ® 2088 6 3 200 type) plasticizer, available from Vesicol Chemical Corporation Optive 130 10% solution of HMPE (NLS Texanol ™ ester 6 2 200 type) alcohol, available from Eastman Chemical Optive 130 10% solution of HMPE (NLS Butylcarbitol 6 3 200 type) Optive 130 10% solution of HMPE (NLS Ethylene glycol 6 4 200 type) Optive 130 10% solution of HMPE (NLS None 0 2.5 200 type)

Although the invention has been illustrated by the above Examples, this is not to be construed as being limited thereby, but rather, the invention encompasses the generic area as hereinbefore disclosed. Various modifications and embodiments can be made without departing from the spirit and scope of the invention.

Claims

1. A stabilizer composition for use in increasing Open Time of an aqueous coating composition comprising an AB type polymer, wherein B comprises any type of water-soluble/water dispersible oligomer or polymer and wherein A, covalently connected to B, comprises a structure that has the following formula: wherein R comprises a C1 to C30 hydrocarbon, which may be linear or branched, aliphatic or aromatic or combinations thereof:

R1, comprises H, CH3, or C2H5;
R2 comprises CH2O, CO2, CONH, or CH2 and wherein R2 can be the same or different;
R3 comprises H or OH;
n is an integer from 1 to 100; and
m is either 0 or 1.

2. The stabilizer composition of claim 1, wherein “B” is selected from the group consisting of polyethylene glycol, polyactalpolyether (PAPE), acrylate, acrylamide and polyethylene oxide.

3. The stabilizer composition of claim 2, wherein “B” comprises polyethylene glycol.

4. The stabilizer composition of claim 2, wherein “B” comprises polyactalpolyether (PAPE).

5. The stabilizer composition of claim 3, wherein the polyethylene glycol may be selected from the group consisting of monomethylpolyethylene glycol and hydroxypolyethylene glycol.

6. The stabilizer composition of claim 1, wherein “B” comprises a mono functional oligomer.

7. The stabilizer composition of claim 3, wherein the polyethylene glycol further comprises a methoxy-end-capped polyethylene glycol.

8. The stabilizer composition of claim 1, wherein “A” is selected from the group consisting of polyphenoxy glycidyl ether, methylphenyl glycidyl ether, ethylhexylglycidyl ether, phenyl glycidyl ether, and alkali glycidyl ether.

9. The stabilizer composition of claim 3, wherein “A” comprises methylphenyl glycidyl ether.

10. The stabilizer composition of claim 3, wherein “A” comprises ethylhexylg lycidylether.

11. An aqueous coating composition comprising: wherein R comprises a C1 to C30 hydrocarbon, which may be linear or branched, aliphatic or aromatic or combinations thereof:

a film-forming polymer, and
a stabilizer composition comprising an AB type polymer, wherein B comprises any type of water-soluble/water dispersible oligomer or polymer and wherein A, covalently connected to B, comprises a structure that has the following formula:
R1, comprises H, CH3, or C2H5;
R2 comprises CH2O, CO2, CONH, or CH2 and wherein R2 can be the same or different;
R3 comprises H or OH;
n is an integer from 1 to 100; and
m is either 0 or 1.

12. The aqueous coating composition of claim 11, wherein the film-forming polymer comprises a latex.

13. The aqueous coating composition of claim 12, wherein the film-forming polymer may be selected from the group consisting alkyl acrylates, alkoxy acrylates, alkyl methacrylates, alkoxy methacrylates, vinyl esters of saturated carboxylic acids monoolefins and conjugated dienes.

14. The aqueous coating composition of claim 11 further comprising one or more of an additional component selected from the group consisting of pigments, fillers, thickeners, biocides, mildewcides, surfactants, dispersants and defoamers.

15. The aqueous coating composition of claim 11, wherein the stabilizer composition comprises above about 0 to about 10 wt % of the aqueous coating composition.

16. The aqueous coating composition of claim 15, wherein the stabilizer composition comprises about 0.1 to about 3 wt % of the aqueous coating composition.

17. The aqueous coating composition of claim 15, wherein the stabilizer composition comprises about 0.5 to about 1 wt % of the aqueous coating composition.

18. The aqueous coating composition of claim 11, wherein the stabilizer composition further comprises “B” selected from the group consisting of polyethylene glycol, polyactalpolyether (PAPE), acrylate, acrylamide and polyethylene oxide.

19. The aqueous coating composition of claim 18, wherein “B” comprises polyethylene glycol.

20. The aqueous coating composition of claim 18, wherein “B” comprises polyactalpolyether (PAPE).

21. The aqueous coating composition of claim 11, wherein the stabilizer composition further comprises “A” selected from the group consisting of polyphenoxy glycidyl ether, methylphenyl glycidyl ether, ethylhexylglycidyl ether, phenyl glycidyl ether, and alkali glycidyl ether.

22. The aqueous coating composition of claim 21, wherein “A” comprises methylphenyl glycidyl ether.

23. The aqueous coating composition of claim 21, wherein “A” comprises ethylhexylglycidylether.

24. The aqueous coating composition of claim 11, wherein the aqueous coating composition is selected from the group consisting of paints, stains, varnishes, adhesives and inks.

25. The aqueous coating composition of claim 24, wherein the aqueous coating composition comprises a paint.

26. A method of producing an aqueous coating composition having increased Open Time comprising the steps of: wherein the stabilizer composition comprises an AB type polymer, wherein B comprises any type of water-soluble/water dispersible oligomer or polymer and wherein A, covalently connected to B, comprises a structure that has the following formula: wherein R comprises a C1 to C30 hydrocarbon, which may be linear or branched, aliphatic or aromatic or combinations thereof:

dispersing or emulsifying a film-forming polymer in an aqueous solution, and
adding an amount of a stabilizer composition to the aqueous solution to form the aqueous composition having increased Open Time,
R1 comprises H, CH3, or C2H5;
R2 comprises CH2O, CO2, CONH or CH2 and wherein R2 can be the same or different;
R3 comprises H or OH;
n is an integer from 1 to 100; and
m is either 0 or 1.

27. The method of claim 26, wherein stabilizer composition is added to the aqueous solution before the film-forming polymer is dispersed or emulsified in the aqueous solution.

28. The method of claim 26, wherein stabilizer composition is added to the aqueous solution after the film-forming polymer is dispersed or emulsified in the aqueous solution.

29. The method of claim 26, wherein stabilizer is added to the aqueous solution at the same time the film-forming polymer is dispersed or emulsified in the aqueous solution.

Patent History
Publication number: 20140011946
Type: Application
Filed: Apr 19, 2007
Publication Date: Jan 9, 2014
Patent Grant number: 8859684
Inventors: Kirill Bakeev (Newark, DE), Sung Gun Chu (Hockessin, DE), Tara Lyn Everett (Wilmington, DE), Dirk Kruythoff (Dordrecht), Dekai Loo (Wilmington, DE), Tuyen Thanh Nguyen (Newark, DE), Willemina Geesien Salomons (Steenbergen), Dirk Kruythoff (Dordrecht)
Application Number: 11/788,344