Abstract: A steel sheet for obtaining a member which is excellent in fatigue characteristics equal to ordinary high strength steel sheet of the same strength even if applying the hot stamping process and a method of production of the same are provided. Steel sheet for a hot stamped member which includes composition which contains, by mass %, C: 0.15 to 0.35%, Si: 0.01 to 1.0%, Mn: 0.3 to 2.3%, Al: 0.01 to 0.5%, and a balance of Fe and unavoidable impurities, and limit the impurities to P: 0.03% or less, S: 0.02% or less, and N: 0.1% or less, wherein that a standard error of Vicker's hardness at a position of 20 ?m from the steel sheet surface in the sheet thickness direction is 20 or less. This steel sheet is produced by a recrystallization-annealing step of a first stage of heating a cold rolled steel sheet, which is obtained by hot rolling steel containing the above composition and then cold rolling it, by an average heating rate of 8 to 25° C./sec from room temperature to 600 to 700° C.

Abstract: Provided are a high-strength cold-rolled steel sheet having excellent formability, excellent ductility, excellent hole expansibility, and high yield ratio and a method for producing the same. The high-strength cold-rolled steel sheet contains 0.05% to 0.15% C, 0.10% to 0.90% Si, 1.0% to 2.0% Mn, 0.005% to 0.05% P, 0.0050% or less S, 0.01% to 0.10% Al, 0.0050% or less N, and 0.010% to 0.100% Nb, which are chemical components, on a mass basis, the balance being Fe and unavoidable impurities; has a microstructure which is a multi-phase structure containing 90% or more of a ferrite phase and 0.5% to less than 5.0% of a martensite phase on a volume fraction basis, the remainder being low-temperature transformation phases; and has a yield ratio of 70% or more.

Abstract: The invention provides a high strength steel sheet which exhibits excellent chemical convertibility and corrosion resistance after electrodeposition coating even in the case where the steel sheet has a high Si content, and a method for manufacturing such steel sheets. The method includes continuous annealing of a steel sheet which includes, in terms of mass %, C at 0.01 to 0.18%, Si at 0.4 to 2.0%, Mn at 1.0 to 3.0%, Al at 0.001 to 1.0%, P at 0.005 to 0.060% and S at ?0.01%, the balance being represented by Fe and inevitable impurities, while controlling the dew-point temperature of the atmosphere to become not less than ?10° C. when the heating furnace inside temperature is in the range of not less than A° C. and not more than B° C. during the course of heating (A: 600?A?780, B: 800?B?900).

Abstract: The present invention provides a bainite-containing-type high-strength hot-rolled steel sheet. The steel sheet, containing C: greater than 0.07 to 0.2%, Si: 0.001 to 2.5%, Mn: 0.01 to 4%, P: 0.15% or less, S: 0.03% or less, N: 0.01% or less, Al: 0.001 to 2% and a balance being composed of Fe and impurities, has an average value of pole densities of the {100}<011> to {223}<110> orientation group at a sheet thickness center portion being a range of ? to ? in sheet thickness from the surface of the steel sheet is 4.0 or less, and a pole density of the {332}<113> crystal orientation is 4.8 or less, an average crystal grain diameter is 10 ?m or less and vTrs is ?20° C. or lower, and a microstructure is composed of 35% or less in a structural fraction of pro-eutectoid ferrite and a balance of a low-temperature transformation generating phase.

Abstract: The invention provides medical devices comprising high-strength alloys which degrade over time in the body of a human or animal, at controlled degradation rates, without generating emboli. In one embodiment the alloy is formed into a bone fixation device such as an anchor, screw, plate, support or rod. In another embodiment the alloy is formed into a tissue fastening device such as staple. In yet another embodiment, the alloy is formed into a dental implant or a stent.

Abstract: The present invention provides a non-oriented electrical steel sheet at low cost that has excellent magnetic properties and mechanical properties as well as excellent quality of steel sheet. The non-oriented electrical steel sheet has a chemical composition containing, by mass %, Si: 5.0% or less, Mn: 2.0% or less, Al: 2.0% or less, and P: 0.05% or less, in a range satisfying formula (1), and furthermore, C: 0.008% or more and 0.040% or less; N: 0.003% or less, and Ti: 0.04% or less, in a range satisfying formula (2), with the balance composed of Fe and incidental impurities: 300?85[Si %]+16[Mn %]+40[Al %]+490[P %]?430??(1) 0.008?Ti*<1.2[C %]??(2), where Ti*=Ti?3.4[N %].

Abstract: The invention provides a high strength steel sheet which exhibits excellent chemical convertibility and corrosion resistance after electrodeposition coating even in the case where the steel sheet has a high Si content, and a method for manufacturing such steel sheets. The method includes continuous annealing of a steel sheet which includes, in terms of mass %, C at 0.01 to 0.18%, Si at 0.4 to 2.0%, Mn at 1.0 to 3.0%, Al at 0.001 to 1.0%, P at 0.005 to 0.060% and S at ?0.01%, the balance being represented by Fe and inevitable impurities, while controlling the dew-point temperature of the atmosphere to become not more than ?40° C. when the annealing furnace inside temperature is in the range of not less than 750° C.

Abstract: Provided is a steel sheet for a formed member having enhanced ductility, a formed member, and a method for manufacturing the formed member, and more particularly, to a steel sheet for making a formed member having high strength and ductility such as an automotive structural member and a reinforcing member, a formed member, and a method for manufacturing the formed member. The steel sheet for a formed member has enhanced ductility, and includes, by weight %, C: 0.1% to 1.0%, Si+Al: 0.4% to 3.0%, Mn: 0.1% to 5.0%, P: 0.0001% to 0.1%, S: 0.0001% to 0.03%, N: 0.03% or less (but not 0%), and the balance of Fe and inevitable impurities. The formed member having high strength and ductility that can be used for forming an automotive structural member, a reinforcing member, etc. In addition, the formed member can be used for a heat-treatable impact resistant member.

Abstract: A high-strength galvanized steel sheet contains C: 0.010% or more and 0.06% or less, Si: more than 0.5% and 1.5% or less, Mn: 1.0% or more and 3.0% or less, P: 0.005% or more and 0.1% or less, S: 0.01% or less, sol.Al: 0.005% or more and 0.5% or less, N: 0.01% or less, Nb: 0.010% or more and 0.090% or less, and Ti: 0.015% or more and 0.15% or less, on a mass percent basis. The Nb and C contents of the steel satisfy the relation of (Nb/93)/(C/12)<0.20. C* satisfies 0.005?C*?0.025. Ferrite constitutes 70% by area ratio or more of the steel sheet. Martensite constitutes 3% by area ratio or more of the steel sheet. C*=C?(12/93)Nb?(12/48){Ti?(48/14)N}, wherein C, Nb, Ti, and N denote the C, Nb, Ti, and N contents of the steel.

Abstract: A steel having a composition that includes C: 0.05 to 0.15%, Si: 0.2 to 1.2%, Mn: 1.0 to 2.0%, Al: 0.005 to 0.10%, N: 0.006% or less, and at least one selected from Ti: 0.03 to 0.13%, Nb: 0.02 to 0.10%, and V: 0.02 to 0.15% is subjected to rough rolling at a reduction of 80% or more and finish rolling at a finish rolling delivery temperature in the range of 800 to 950° C. The finish rolled sheet is subjected to cooling including cooling the finish rolled sheet from the finish rolling delivery temperature to a cooling end temperature in the range of 550 to 610° C. at an average cooling rate of 25° C./sec. or more and cooling the finish rolled sheet from the cooling end temperature of the previous process to a coiling temperature at an average cooling rate of 100° C./sec. or more.

Abstract: An electron-beam welded joint including, by mass %, C: 0.02% to 0.1%, Si: 0.03% to 0.30%, Mn: 1.5% to 2.5%, Ti: 0.005 to 0.015%, N: 0.0020 to 0.0060%, O: 0.0010% to 0.0035%, Nb: 0% to 0.020%, V: 0% to 0.030%, Cr: 0% to 0.50%, Mo: 0% to 0.50%, Cu: 0% to 0.25%, Ni: 0% to 0.50%, B: 0% to 0.0030%, S: limited to 0.010% or less, P: limited to 0.015% or less, Al: limited to 0.004% or less, and a balance consisting of iron and unavoidable impurities, wherein an index value CeEB is 0.49% to 0.60%, a number of oxides having an equivalent circle diameter of 1.0 ?m or more is 20 pieces/mm2 or less, and a number of oxides having an equivalent circle diameter of 0.05 ?m or more and less than 0.5 ?m is 1×103 pieces/mm2 to 1×105 pieces/mm2 at a thickness center portion.

Abstract: A low Ni and high N austenitic-ferritic stainless steel is disclosed. It includes an austenitic-ferritic stainless steel having high formability and punch stretchability, crevice corrosion resistance, corrosion resistance at welded part, or excellent intergranular corrosion resistance, from a stainless steel structured by mainly austenite phase and ferrite phase, and consisting essentially of 0.2% or less C, 4% or less Si, 12% or less Mn, 0.1% or less P, 0.03% or less S, 15 to 35% Cr, 3% or less Ni, and 0.05 to 0.6% N, by mass, by adjusting the percentage of the austenite phase in a range from 10 to 85%, by volume. Furthermore, it includes an austenitic-ferritic stainless steel having higher formability by adjusting the amount of (C+N) in the austenite phase to a range from 0.16 to 2% by mass.

Abstract: The present invention provides high strength hot rolled steel plate for line-pipes superior in low temperature toughness, and a method of production of the same, containing, by mass %, C: 0.01 to 0.1%, Si: 0.05 to 0.5%, Mn: 1 to 2%, P: ?0.03%, S: ?0.005%, O: ?0.003%, Al: 0.005 to 0.05%, N: 0.0015 to 0.006%, Nb: 0.005 to 0.08%, and Ti: 0.005 to 0.02%, where N?14/48×Ti>0% and Nb?93/14×(N?14/48×Ti)>0.005%, and a balance of Fe and unavoidable impurities, said steel plate characterized in that its microstructure is a continuously cooled transformed structure, a reflected X-ray intensity ratio {211}/{111} of the {211} plane and {111} plane parallel to the plate surface in the texture at the center of plate thickness is 1.1 or more, and an in-grain precipitate density of the precipitates of Nb and/or Ti carbonitrides is 1017 to 1018/cm3.

Abstract: The invention provides a steel material with satisfactory hydrogen embrittlement resistance, and particularly it relates to high-strength steel with satisfactory hydrogen embrittlement resistance and a strength of 1200 MPa or greater, as well as a process for production thereof. At least one simple or compound deposit of oxides, carbides or nitrides as hydrogen trap sites which trap hydrogen with a specific trap energy is added to steel, where the mean sizes, number densities, and length-to-thickness ratios (aspect ratio) are in specific ranges. By applying the specific steel components and production process it is possible to obtain high-strength steel with excellent hydrogen embrittlement resistance.

Abstract: The present invention provides a wire rod with a composition at least including: C: 0.95-1.30 mass %; Si: 0.1-1.5 mass %; Mn: 0.1-1.0 mass %; Al: 0-0.1 mass %; Ti: 0-0.1 mass %; P: 0-0.02 mass %; S: 0-0.02 mass %; N: 10-50 ppm; O: 10-40 ppm; and a balance including Fe and inevitable impurities, wherein 97% or more of an area in a cross-section perpendicular to the longitudinal direction of the wire rod is occupied by a pearlite, and 0.5% or less of an area in a central area in the cross-section and 0.5% or less of an area in a first surface layer area in the cross-section are occupied by a pro-eutectoid cementite.

Abstract: The present invention provides a bake-hardenable high-strength cold-rolled steel sheet having excellent bake hardenability, cold aging resistance, and deep-drawability, and reduced planar anisotropy, containing chemical components in % by mass of: C: 0.0010% to 0.0040%, Si: 0.005% to 0.05%, Mn: 0.1% to 0.8%, P: 0.01% to 0.07%, S: 0.001% to 0.01%, Al: 0.01% to 0.08%, N: 0.0010% to 0.0050%, Nb: 0.002% to 0.020%, and Mo: 0.005% to 0.050%, a value of [Mn %]/[P %] being in the range of 1.6 to 45, where [Mn %] is an amount of Mn and [P %] is an amount of P, an amount of C in solid solution obtained from [C %]?(12/93)×[Nb %] being in the range of 0.0005% to 0.

Abstract: A thin high strength steel sheet having excellent formability has a composition which includes, by mass %, 0.08 to 0.15% of C, 0.5 to 1.5% of Si, 0.5 to 1.5% of Mn, 0.01 to 0.1% of Al, and 0.005% or less of N to form a hot rolled sheet is conducted.

Abstract: A high-strength cold rolled steel sheet having excellent deep drawability and bake hardenability, with a tensile strength ?440 MPa, an average r-value ?1.20 and a bake hardening value ?40 MPa, is obtained by subjecting a steel raw material having a chemical composition including C: 0.010-0.06 mass %, Si: more than 0C:\Users\ejensen\Desktop\!TEMP\.5 mass % but not more than 1.5 mass %, Mn: 1.0-3.0 mass %, Nb: 0.010-0.090 mass %, Ti: 0.015-0.15 mass % and satisfying (Nb/93)/(C/12)<0.20 to hot rolling, cold rolling and then to annealing including steps of heating to a temperature of 800-900° C. while a temperature region of 700-800° C. is an average heating rate <3° C./s, and soaking and thereafter cooling at a rate ?5° C./s from the soaking temperature to a cooling stop temperature ?500° C. to thereby form a microstructure including ferrite phase with an area ratio ?70% and martensite phase with an area ratio ?3%.

Abstract: Embodiments of the present disclosure comprise carbon steels and methods of manufacture. In one embodiment, a double austenizing procedure is disclosed in which a selected steel composition is formed and subjected to heat treatment to refine the steel microstructure. In one embodiment, the heat treatment may comprise austenizing and quenching the formed steel composition a selected number of times (e.g., 2) prior to tempering. In another embodiment, the heat treatment may comprise subjecting the formed steel composition to austenizing, quenching, and tempering a selected number of times (e.g., 2). Steel products formed from embodiments of the steel composition in this manner (e.g., seamless tubular bars and pipes) will possess high yield strength, at least about 175 ksi (about 1200 MPa) while maintaining good toughness.

Abstract: A high strength hot-rolled steel sheet with a tensile strength of not less than 590 MPa which exhibits excellent bake hardenability and stretch-flangeability has a chemical composition including, in terms of mass %, C at 0.040 to 0.10%, Si at not more than 0.3%, Mn at 1.7 to 2.5%, P at not more than 0.030%, S at not more than 0.005%, Al at not more than 0.1% and N at 0.006 to 0.025%, and microstructure wherein a bainite phase represents not less than 60%, the total of a ferrite phase and a pearlite phase represents not more than 10%, and the bainite phase includes grains among which cementite grains have been precipitated at not less than 1.4×104 grains/mm2 and the cementite grains have an average grain diameter of not more than 1.5 ?m.

Abstract: A high strength steel sheet excellent in warm stamp formability and a method for manufacturing the same. The steel has a composition containing, in terms of % by mass, C: 0.01 to 0.2%, Si: 0.5% or lower, Mn: 2% or lower, P: 0.03% or lower, S: 0.01% or lower, Al: 0.07% or lower, and N: 0.01% or lower and further containing one or two or more elements selected from Ti, Nb, V, Mo, W, and B.

Abstract: A method of hot forming a steel blank into an article the method including the following steps: d) cooling a heated steel blank to form an article during hot forming, starting at a starting temperature T2 above Ar3; to an interrupt temperature T3 in the range of 400-550° C. at a cooling rate V2 of at least 25° C./s; e) immediately further cooling the article from the interrupt temperature T3 to ambient temperature at a cooling rate V3 of 0.2-10° C./s, wherein the interrupt temperature T3 and cooling rate V3 are selected such that the article thus obtained has multiphase microstructure including by volume fraction: 55-90% of bainitic ferrite 5-15% of retained austenite 5-30% martensite.

Abstract: This profiled wire, of NACE grade, made of low-alloy carbon steel intended to be used in the offshore oil exploitation sector, is characterized in that it has the following chemical composition, expressed in percentages by weight of the total mass: 0.75<% C<0.95; 0.30<% Mn<0.85; Cr?0.4%; V?0.16%; Si?1.40% and preferably ?0.15%; and optionally no more than 0.06% Al, no more than 0.1% Ni and no more than 0.

Abstract: A method for manufacturing such steel sheet includes continuous annealing of a steel sheet which includes, in terms of mass %, C at 0.01 to 0.18%, Si at 0.4 to 2.0%, Mn at 1.0 to 3.0%, Al at 0.001 to 1.0%, P at 0.005 to 0.060% and S at ?0.01%, the balance being represented by Fe and inevitable impurities, in such a manner that the dew point of the atmosphere is controlled to become not more than ?45° C. during the course of soaking when the annealing furnace inside temperature is in the range of not less than 820° C. and not more than 1000° C. as well as that the dew point of the atmosphere is controlled to become not more than ?45° C. during the course of cooling when the annealing furnace inside temperature is in the range of not less than 750° C.

Abstract: In a cold-rolled steel sheet in relation with the present invention, metallurgical structure of the steel sheet is made a mixture structure including bainite, residual austenite and tempered martensite, particularly, when the metallurgical structure is observed with a scanning electron microscope, bainite is constituted of composite structure of high temperature range forming bainite with 1 ?m or above average distance between neighboring residual austenite and/or carbide and low temperature range forming bainite with below 1 ?m average distance between neighboring residual austenite and/or carbide, and when the area ratio of the high temperature range forming bainite with respect to total metallurgical structure is made a and the total area ratio of the low temperature range forming bainite and the tempered martensite with respect to the total metallurgical structure is made b, a: 20-80%, b: 20-80%, and a+b: 70% or above are satisfied.

Abstract: A steel sheet including C at 0.05 to 0.15%, Si at 0.2 to 1.2%, Mn at 1.0 to 2.0%, P at not more than 0.04%, S at not more than 0.0030%, Al at 0.005 to 0.10%, N at not more than 0.005% and Ti at 0.03 to 0.13%, the balance being Fe and inevitable impurities, includes surface regions having an area fraction of bainite of less than 80% and an area fraction of a ferrite phase with a grain diameter of 2 to 15 ?m of not less than 10%, the surface regions extending from both surfaces of the steel sheet each to a depth of 1.5 to 3.0% relative to a total sheet thickness, as well as an inner region other than the surface regions having an area fraction of a bainite phase of more than 95%, and has a tensile strength of not less than 780 MPa.

Abstract: The steel sheet includes C: 0.04 to 0.12%, Si: 0.5 to 1.2%, Mn: 1.0 to 1.8%, P: not more than 0.03%, S: not more than 0.0030%, Al: 0.005 to 0.20%, N: not more than 0.005% and Ti: 0.03 to 0.13%, the balance being Fe and inevitable impurities, includes a microstructure containing a bainite phase at an area fraction exceeding 95% and having an average grain diameter of not more than 3 ?m, has a difference ?Hv1 of not more than 50 between a Vickers hardness value at 50 ?m from the surface and a Vickers hardness value at ¼ of a sheet thickness, has a difference ?Hv2 of not more than 40 between the Vickers hardness value at ¼ of the sheet thickness and a Vickers hardness value at ½ of the sheet thickness.

Abstract: A steel is subjected to a hot rolling step, a cold rolling step, and an annealing step having a maximum achieving temperature: 800° C. to 900° C., two-step heating, and two-step cooling. The two-step heating includes first-step heating to (maximum achieving temperature—(10° C. to 50° C.)) at an average temperature raising rate: 0.5° C. to 5.0° C./s and second-step heating in which the temperature raising time from that temperature range to the maximum achieving temperature is specified to be 30 to 150 s. Two-step cooling includes first-step cooling to cool from the maximum achieving temperature at a cooling rate of 10° C. to 40° C./s and second-step cooling to cool to a temperature range of 400° C. to 500° C. at a cooling rate of 0.2 to 0.8 times the first-step cooling rate for a cooling time of 0.2 to 0.8 times the total cooling time.

Abstract: A method for producing a motor vehicle component having two regions, with different strength is disclosed. A first one of the two regions has a high strength and a second one of the two regions has a higher ductility and lower strength relative to the first region. In a motor vehicle component produced with the method, the first region has a strength between 1400 and 1600 MPa at a breaking elongation A5>13% and the second region has a tensile strength between 950 and 1050 MPa at a breaking elongation A5>16%.

Abstract: A hot-rolled steel sheet has an average value of the X-ray random intensity ratio of a {100} <011> to {223} <110> orientation group at least in a sheet thickness central portion that is in a sheet thickness range of ? to ? from a steel sheet surface of 1.0 to 6.0, an X-ray random intensity ratio of a {332} <113> crystal orientation of 1.0 to 5.0, rC which is an r value in a direction perpendicular to a rolling direction of 0.70 to 1.10, and r30 which is an r value in a direction that forms an angle of 30° with respect to the rolling direction of 0.70 to 1.10.

Abstract: A high-strength cold rolled steel sheet has excellent formability and crashworthiness and includes, on a mass % basis, C: 0.05 to 0.3%, Si: 0.3 to 2.5%. Mn: 0.5 to 3.5%, P: 0.003 to 0.100%, 5: 0.02% or less, Al: 0.010 to 0.5%, the balance being iron and unavoidable impurities, the high-strength cold rolled steel sheet having a microstructure including 20% or more of ferrite on an area fraction basis, 10 to 60% of tempered martensite on an area fraction basis, 0 to 10% of martensite on an area fraction basis, and 3 to 15% of retained austenite on a volume fraction basis.

Abstract: A predetermined composition is had, when a C content is represented by (C %), in a case of (C %) being not less than 0.35% nor more than 0.65%, a volume fraction of pearlite is 64×(C %)+52% or more, and in a case of (C %) being greater than 0.65% and 0.85% or less, the volume fraction of pearlite is not less than 94% nor more than 100%, and a structure of the other portion is composed of one or two of proeutectoid ferrite and bainite. Further, in a region to a depth of 1.0 mm from a surface, a volume fraction of pearlite block having an aspect ratio of 2.0 or more is not less than 70% nor more than 95%, and a volume fraction of pearlite having an angle between an axial direction and a lamellar direction on a cross section parallel to the axial direction of 40° or less is 60% or more with respect to all pearlite.

Abstract: Described is a high tensile strength hot rolled steel sheet having high strength and formability, and a manufacturing method. It has tensile strength?980 MPa and excellent formability, and specifically identified ranges by mass % of C, Si, Mn, P, S, N, Al, Ti, V, Solute V, and Solute Ti; (ii) microstructure with fine carbides dispersion precipitated therein, the fine carbides containing Ti and V and having the average particle diameter<10 nm, as well as volume ratio with respect to the entire microstructure?0.007; and matrix as ferrite phase having area ratio with respect to the entire microstructure?97%. C, Ti, V, S and N satisfy (1) Ti?0.08+(N/14×48+S/32×48) and (2) 0.8?(Ti/48+V/51)/(C/12)?1.2, where “C”, “Ti”, “V”, “S” and “N” represent contents (mass %) of corresponding elements, respectively.

Abstract: A method for manufacturing a hot-rolled sheet is provided, wherein the method attains grain refinement of the steel sheet containing C, Si, and Mn, wherein the grain size thereof is set to particularly below average of 2 ?m, which has ferrite grain with equiaxed morphology, which has high formability in forming, and the ferrite grain-size deviation in the thickness direction is uniformed down to the level not higher than a predetermined amount whereby uniform formability in forming is high. The method includes a first rolling for rolling the sheet such that the total rolling reduction is 80% or more or the average grain size is 30 ?m or less in a form of single phase of austenite, a second rolling of a single-pass, a third rolling being conducted thereafter, and a following cooling.

Abstract: A high strength hot-rolled steel sheet has a tensile strength of not less than 780 MPa and exhibits excellent stretch flangeability and excellent fatigue resistance. A steel has a composition containing C at 0.05 to 0.15%, Si at 0.2 to 1.2%, Mn at 1.0 to 2.0%, P at not more than 0.04%, S at not more than 0.005%, Ti at 0.05 to 0.15%, Al at 0.005 to 0.10% and N at not more than 0.007%.

Abstract: A high strength steel sheet contains, in percent by mass, 0.03 to 0.2% of C, 0.5 to 2.5% of Si, 1 to 3.0% of Mn, 0.01 to 0.5% of Cr, 0.01 to 0.5% of Mo, 0.02 to 0.15% of Al, 0.15% or less of Ti, 0.15% or less of No, and 0.15% or less of V; wherein the remainder includes Fe and inevitable impurities, and the content of Si satisfies the following formula (1), ??4.1?[Si]??2.4??(1), provided, ?=6.9×([C]+[Mn]/6+[Cr]/5+[Mo]/4+[Ti]/15+[Nb]/17+[V]/14)1/2 is given, wherein [ ] shows the quantity (mass percent) of each element contained in the steel sheet. The high strength steel sheet is improved in formability (particularly, elongation), and excellent in balance between strength and elongation.

Abstract: A high strength press-formed member includes a steel sheet constituting the member including a composition including by mass %, C: 0.12% to 0.69%, Si: 3.0% or less, Mn: 0.5% to 3.0%, P: 0.1% or less, S: 0.07% or less, Al: 3.0% or less, N: 0.010% or less, Si+Al: at least 0.

Abstract: A cold rolled steel sheet with excellent bendability contains C at 0.15 to 0.30%, Si at 0.01 to 1.8%, Mn at 1.5 to 3.0%, P at not more than 0.05%, S at not more than 0.005%, Al at 0.005 to 0.05% and N at not more than 0.005%, the balance being Fe and inevitable impurities, and has a steel sheet superficial soft portion satisfying: Hv(S)/Hv(C)?0.8??(1) wherein Hv(S) is hardness of the steel sheet superficial soft portion, and Hv(C) is hardness of a steel sheet core portion, 0.10?t(S)/t?0.30??(2) wherein t(S) is thickness of the steel sheet superficial soft portion, and t is the sheet thickness.

Abstract: A high-strength cold-rolled steel sheet includes, by mass %, C: 0.10% to 0.40%, Mn: 0.5% to 4.0%, Si: 0.005% to 2.5%, Al: 0.005% to 2.5%, Cr: 0% to 1.0%, and a balance of iron and inevitable impurities, in which an amount of P is limited to 0.05% or less, an amount of S is limited to 0.02% or less, an amount of N is limited to 0.006% or less, the microstructure includes 2% to 30% of retained austenite by area percentage, martensite is limited to 20% or less by area percentage in the microstructure, an average particle size of cementite is 0.01 ?m to 1 ?m, and 30% to 100% of the cementite has an aspect ratio of 1 to 3.

Abstract: Disclosed is an ultra high strength steel plate with at least 1100 MPa of tensile strength that has both an excellent strength-stretch balance and excellent bending workability, and a method for producing the same. The metal structure of the steel plate has martensite, and the soft phases of bainitic ferrite and polygonal ferrite. The area of the aforementioned martensite constitutes 50% or more, the area of the aforementioned bainitic ferrite constitutes 15% or more, and the area of the aforementioned polygonal ferrite constitutes 5% or less (including 0%). When the circle-equivalent diameter of the aforementioned soft phases is measured, the coefficient of variation (standard deviation/mean value) is less or equal to 1.0. The ultra high strength steel plate has at least 1100 MPa of tensile strength.

Abstract: On a cross section with a sheet width direction of a high-strength hot-rolled steel sheet set as a normal line, with regard to an inclusion having a major diameter of 3.0 ?m or more, a maximum of a major diameter/minor diameter ratio expressed by (a major diameter of the inclusion)/(a minor diameter of the inclusion) is 8.0 or less, and a sum total of a rolling direction length per 1 mm2 cross section of a predetermined inclusion group composed of plural inclusions each having a major diameter of 3.0 ?m or more and a predetermined extended inclusion having a length in a rolling direction of 30 ?m or more is 0.25 mm or less. The plural inclusions composing the predetermined inclusion group congregate in both the rolling direction and a direction perpendicular to the rolling direction 50 ?m or less apart from each other. The predetermined extended inclusion is spaced over 50 ?m apart from all the inclusions each having a major diameter of 3.

Abstract: Provided is a steel pipe for a linepipe having high compressive strength, a heavy wall thickness and sour gas resistance. The steel pipe has the composition which contains by mass % 0.02 to 0.06% C, 0.01 to 0.5% Si, 0.8 to 1.6% Mn, 0.012% or less P, 0.0015% or less S, 0.01 to 0.08% Al, 0.005 to 0.050% Nb, 0.005 to 0.025% Ti, 0.0005 to 0.0035% Ca, 0.0020 to 0.0060% N, and Fe and unavoidable impurities as a balance. The steel pipe has metal microstructure where a fraction of bainite is 80% or more, a fraction of M-A constituent is 2% or less and an average grain size of bainite is 5 ?m or less.

Abstract: A seamless steel pipe for line pipe having high strength and high toughness contains, by mass percent, C: 0.02 to 0.10%, Si: at most 0.5%, Mn: 0.5 to 2.0%, Al: 0.01 to 0.1%, P: at most 0.03%, S: at most 0.005%, Ca: at most 0.005%, and N: at most 0.007%, and further contains at least one selected from a group consisting of Ti: at most 0.008%, V: less than 0.06%, and Nb: at most 0.05%, the balance being Fe and impurities. A carbon equivalent Ceq defined by Formula (1) is at least 0.38, a content of Ti, V and Nb satisfies Formula (2), and the size of carbo-nitride containing at least one of Ti, V, Nb and Al is at most 200 nm, Ceq=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15??(1) Ti+V+Nb<0.06??(2).

Abstract: A steel material has a composition of C: 0.02 to 0.2%, Si: 0.01 to 0.5%, Mn: 0.5 to 2.5%, P: 0.05% or lower, S: 0.05% or lower, Al: 0.1% or lower, and N: 0.01% or lower and, as required, one or two or more elements selected from Cu: 0.01 to 2%, Ni: 0.01 to 5%, Cr: 0.01 to 3%, Mo: 0.01 to 2%, Nb: 0.1% or lower, V: 0.1% or lower, Ti: 0.1% or lower, B: 0.01% or lower, Ca: 0.01% or lower, and REM: 0.1% or lower in terms of % by mass, and the balance Fe with inevitable impurities, in which the microstructure at the ¼ position of the plate thickness contains ferrite and a hard phase, the area fraction of the hard phase is 50 to 90%, and the average aspect ratio of the ferrite is 1.5 or more.

Abstract: A high-strength cold-rolled steel sheet having high chemical convertibility and a tensile strength of 590 MPa or more and a method for producing such a steel sheet are provided. The steel sheet contains, in terms of percent by mass, C: 0.05 to 0.3%, Si: 0.6 to 3.0%, Mn: 1.0 to 3.0%, P: 0.1% or less, S: 0.05% or less, Al: 0.01 to 1%, N: 0.01% or less, and the balance being Fe and unavoidable impurities. The coverage ratio of reduced iron on a steel sheet surface is 40% or more. In order to produce such a steel sheet, an oxidation treatment is performed after cold rolling. Subsequently, annealing is conducted in a furnace in a 1 to 10 vol % H2+balance N2 gas atmosphere with a dew point of ?25° C. or less.

Abstract: The invention relates to a steel sheet having a tensile strength of 1180 MPa or more, which excels in workability and cold brittleness resistance. The high-strength steel sheet contains 0.10% to 0.30% of C, 1.40% to 3.0% of Si, 0.5% to 3.0% of Mn, 0.1% or less of P, 0.05% or less of S, 0.005% to 0.20% of Al, 0.01% or less of N, 0.01% or less of O, as well as Fe and inevitable impurities. The steel sheet has: (i) a ferrite volume fraction of 5% to 35% and a bainitic ferrite and/or tempered martensite volume fraction of 60% or more; (ii) a MA constituent volume fraction of 6% or less (excluding 0%); and (iii) a retained austenite volume fraction of 5% or more.

Abstract: A steel sheet, including: as chemical components, by mass %, 0.05% to 0.35% of C; 0.05% to 2.0% of Si; 0.8% to 3.0% of Mn; 0.01% to 2.0% of Al; equal to or less than 0.1% of P; equal to or less than 0.05% of S; equal to or less than 0.01% of N; and the balance including iron and inevitable impurities, wherein an area ratio of equal to or higher than 50% of a total of a ferrite phase, a bainite phase, and a tempered martensite phase is contained, an area ratio of equal to or higher than 3% of a retained austenite phase is contained, and crystal grains of the retained austenite phase having a number ratio of equal to or higher than 50% satisfy Expression 1, assuming carbon concentration at a position of center of gravity is Cgc and a carbon concentration at a grain boundary is Cgb.

Abstract: This steel plate for cold forging includes a hot-rolled steel plate, wherein the hot-rolled steel plate includes: in terms of percent by mass, C: 0.13% to 0.20%; Si: 0.01% to 0.8%; Mn: 0.1% to 2.5%; P: 0.003% to 0.030%; S: 0.0001% to 0.008%; Al: 0.01% to 0.07%; N: 0.0001% to 0.02%; and O: 0.0001% to 0.0030%, with a remainder being Fe and inevitable impurities, an A value represented by the following formula (1) is in a range of 0.0080 or less, a thickness of the hot-rolled steel plate is in a range of 2 mm to 25 mm, and an area percentage of pearlite bands having lengths of 1 mm or more in a region of 4/10t to 6/10t when a plate thickness is indicated by t in a cross section of a plate thickness that is parallel to a rolling direction of the hot-rolled steel plate is in a range of not more than a K value represented by the following formula (2), A value=O%+S%+0.033Al%??(1) K value=25.5×C%+4.5×Mn%?6??(2).

Abstract: An austenitic stainless steel having low nickel and molybdenum and exhibiting comparable corrosion resistance and formability properties to higher nickel and molybdenum alloys comprises, in weight %, up to 0.20 C, 2.0-9.0 Mn, up to 2.0 Si, 16.0-23.0 Cr, 1.0-5.0 Ni, up to 3.0 Mo, up to 3.0 Cu, 0.1-0.35 N, up to 4.0 W, up to 0.01 B, up to 1.0 Co, iron and impurities, the steel having a ferrite number of less than 10 and a MD30 value of less than 20° C.

Abstract: This high strength hot-rolled steel sheet includes: in terms of percent by mass, C: 0.05 to 0.12%; Si: 0.8 to 1.2%; Mn: 1.6 to 2.2%; Al: 0.30 to 0.6%; P: 0.05% or less; S: 0.005% or less; and N: 0.01% or less, with the remainder being Fe and unavoidable impurities, wherein a microstructure includes specific ranges (in area %) of ferrite phases as well as martensite phases, and a maximum concentration of Al detected by a glow discharge emission spectroscopic analysis is in a range of 0.75 mass % or less in a region from a surface of the steel sheet to a thickness of 500 nm after being acid-pickled.