THIN FILM TRANSISTOR, DISPLAY DEVICE HAVING THIN FILM TRANSISTOR, AND METHOD FOR MANUFACTURING THE SAME
A thin film transistor with excellent electric characteristics, a display device having the thin film transistor, and methods for manufacturing the thin film transistor and the display device are proposed. The thin film transistor includes a gate insulating film formed over a gate electrode, a microcrystalline semiconductor film formed over the gate insulating film, a pair of buffer layers formed over the microcrystalline semiconductor film, a pair of semiconductor films to which an impurity element imparting one conductivity type is added and which are formed over the pair of buffer layers, and wirings formed over the pair of semiconductor films to which the impurity element imparting one conductivity type is added. A part of the gate insulating film or the entire gate insulating film, and/or a part of the microcrystalline semiconductor or the entire microcrystalline semiconductor includes the impurity element which serves as a donor.
Latest SEMICONDUCTOR ENERGY LABORATORY CO., LTD. Patents:
- Display Apparatus
- Light-Emitting Apparatus, Display Device And Electronic Appliance
- Display device and method for manufacturing display device
- Display device having light-receiving region between first-and-second-emitting regions
- Display device, display module, and electronic device including semi-transmissive layer
1. Field of the Invention
The present invention relates to a thin film transistor, a display device having the thin film transistor at least in a pixel portion, and a method for manufacturing the thin film transistor and the display device.
2. Description of the Related Art
In recent years, technology for forming thin film transistors using a thin semiconductor film (with a thicknesses of from several tens of nanometers to several hundreds of nanometers, approximately) formed over a substrate having an insulating surface has been attracting attention. Thin film transistors are applied to a wide range of electronic devices such as ICs or electro-optical devices, and prompt development of thin film transistors that are to be used as switching elements in display devices, in particular, is being pushed.
As a switching element in a display device, a thin film transistor including an amorphous semiconductor film, a thin film transistor including a polycrystalline semiconductor film, or the like is used. As a method for forming a polycrystalline semiconductor film, a technique is known in which a pulsed excimer laser beam is processed into a linear shape with an optical system, and an amorphous silicon film is scanned with the linear beam, thereby being crystallized.
As a switching element in a display device, further, a thin film transistor including a microcrystalline semiconductor film is used (see Reference 1: Japanese Published Patent Application No. H4-242724; and Reference 2: Japanese Published Patent Application No. 2005-49832).
SUMMARY OF THE INVENTIONA thin film transistor including a polycrystalline semiconductor film has advantages that the field effect mobility thereof is two or more orders of magnitude higher than that of a thin film transistor including an amorphous semiconductor film, and that a pixel portion and a peripheral driver circuit of a display device can be formed over one substrate. However, the thin film transistor including a polycrystalline semiconductor film requires a more complicated process than the thin film transistor including an amorphous semiconductor film because of crystallization of the semiconductor film. Thus, there are problems such as a reduction in yield and an increase in cost.
Further, an inverted-staggered thin film transistor including a microcrystalline semiconductor film has problems in that the crystallinity of an interface region between a gate insulating film and a microcrystalline semiconductor film is low and electric characteristics are poor.
In view of the above problems, it is an object of the present invention to provide a thin film transistor having excellent electric characteristics, a display device having the thin film transistor, and a method for manufacturing the thin film transistor and the display device.
An aspect of the present invention is a thin film transistor including a gate insulating film formed over a gate electrode, a microcrystalline semiconductor film formed over the gate insulating film, a pair of buffer layers formed over the microcrystalline semiconductor film, a pair of semiconductor films to which an impurity element imparting one conductivity type is added and which is formed over the pair of buffer layers, and wirings formed over the pair of semiconductor films to which the impurity element imparting one conductivity type is added; in which a part of the gate insulating film or the entire gate insulating film, and/or a part of the microcrystalline semiconductor film or the entire microcrystalline semiconductor film includes an impurity element which serves as a donor.
Further, typically, a feature of the thin film transistor of the present invention is that a region of the microcrystalline semiconductor film which is in contact with the gate insulating film includes the impurity element which serves as a donor. In that case, the entire microcrystalline semiconductor film can include the impurity element which serves as a donor. Further, only a region of the microcrystalline semiconductor film which is in contact with the gate insulating film can include the impurity element which serves as a donor. In that case, a first microcrystalline semiconductor film including the impurity element which serves as a donor is formed in the region which is in contact with the gate insulating film, and a second microcrystalline semiconductor film is formed over the first microcrystalline semiconductor film. The second microcrystalline semiconductor film does not include the impurity element which serves as a donor at a higher concentration than the detection limit of secondary ion mass spectrometry (SIMS).
Alternatively, a feature of the thin film transistor of the present invention is that the gate insulating film includes the impurity element which serves as a donor.
Further alternatively, a feature of the thin film transistor of the present invention is that a first microcrystalline semiconductor film that is in contact with a gate insulating film, a second microcrystalline semiconductor film that is in contact with the first microcrystalline semiconductor film and includes an impurity element which serves as a donor, and a third microcrystalline semiconductor film that is in contact with the second microcrystalline semiconductor film including the impurity element which serves as a donor are formed. The first microcrystalline semiconductor film and the third microcrystalline semiconductor film do not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS.
Here, the gate insulating film or the microcrystalline semiconductor film includes the impurity element which serves as a donor at a peak concentration of from 6×1015 to 3×1018 atoms/cm3 inclusive, preferably from 3×1016 to 3×1017 atoms/cm3 inclusive. Further, the concentration of the impurity element which serves as a donor is determined by the peak value of the concentration distribution (concentration profile) which is measured by SIMS.
Another feature of the present invention is that a gate insulating film or a microcrystalline semiconductor film which includes an impurity element which serves as a donor is formed and a thin film transistor is formed in which the microcrystalline semiconductor film serves as a channel formation region. In the microcrystalline semiconductor film that serves as a channel formation region, the peak concentration of the impurity element which serves as a donor is from 6×1015 to 3×1018 atoms/cm3 inclusive, preferably from 3×1016 to 3×1017 atoms/cm3 inclusive.
Typically, a gate insulating film is formed over a gate electrode; gas including an impurity element which serves as a donor is introduced into a reaction chamber, and then a microcrystalline semiconductor film including the impurity element which serves as a donor is formed over the gate insulating film, using deposition gas including silicon or germanium, and hydrogen; and a thin film transistor is manufactured using the microcrystalline semiconductor film.
Alternatively, a gate insulating film is formed over a gate electrode; a first microcrystalline semiconductor film including an impurity element which serves as a donor is formed over the gate insulating film, using gas including the impurity element which serves as a donor, deposition gas including silicon or germanium, and hydrogen; a second microcrystalline semiconductor film is formed over the first microcrystalline semiconductor film, using deposition gas including silicon or germanium, and hydrogen; and a thin film transistor is manufactured using the first microcrystalline semiconductor film and the second microcrystalline semiconductor film.
Further alternatively, a gate insulating film including an impurity element which serves as a donor is formed over a gate electrode, using gas including the impurity element which serves as a donor, and deposition gas including silicon or germanium; a microcrystalline semiconductor film including the impurity element which serves as a donor is formed over the gate insulating film including the impurity element which serves as a donor, using deposition gas including silicon or germanium, and hydrogen; and a thin film transistor is manufactured using the microcrystalline semiconductor film.
Further alternatively, a protective film including an impurity element which serves as a donor is formed on an inner wall of a reaction chamber of a plasma CVD apparatus, using gas including the impurity element which serves as a donor, deposition gas including silicon or germanium, and hydrogen; then, a substrate provided with a gate electrode is carried in the reaction chamber; a gate insulating film is formed over the gate electrode; a microcrystalline semiconductor film is formed over the gate insulating film, using deposition gas including silicon or germanium, and hydrogen; and a thin film transistor is manufactured using the microcrystalline semiconductor film.
Further alternatively, gas including an impurity element which serves as a donor is fed into a reaction chamber of a plasma CVD apparatus; then, a gate insulating film including the impurity element which serves as a donor is formed over a substrate provided with a gate electrode; a microcrystalline semiconductor film is formed over the gate insulating film, using deposition gas including silicon or germanium, and hydrogen; and a thin film transistor is manufactured using the microcrystalline semiconductor film.
Further alternatively, a gate insulating film is formed over a substrate provided with a gate electrode; gas including an impurity element which serves as a donor is fed into a reaction chamber of a plasma CVD apparatus; then, a microcrystalline semiconductor film including the impurity element which serves as a donor is formed over the gate insulating film, using deposition gas including silicon or germanium, and hydrogen; and a thin film transistor is manufactured using the microcrystalline semiconductor film including the impurity element which serves as a donor.
Further alternatively, a first gate insulating film is formed over a substrate provided with a gate electrode; gas including an impurity element which serves as a donor is fed into a reaction chamber of a plasma CVD apparatus; then, a second gate insulating film including the impurity element which serves as a donor is formed over the first gate insulating film, using non-deposition gas including oxygen or nitrogen, and deposition gas including silicon; a microcrystalline semiconductor film is formed over the second gate insulating film; and a thin film transistor is manufactured using the microcrystalline semiconductor film.
Further alternatively, a first gate insulating film is formed over a substrate provided with a gate electrode; a second gate insulating film is formed over the first gate insulating film; then, gas including an impurity element which serves as a donor for a semiconductor is fed into a reaction chamber of a plasma CVD apparatus; subsequently, a third gate insulating film including the impurity element which serves as a donor is formed over the second gate insulating film, using non-deposition gas including oxygen or nitrogen, and deposition gas including silicon; a microcrystalline semiconductor film is formed over the third gate insulating film, using deposition gas including silicon or germanium, and hydrogen; and a thin film transistor is manufactured using the microcrystalline semiconductor film.
The impurity element which serves as a donor is phosphorus, arsenic, or antimony.
A gate insulating film including an impurity element which serves as a donor is formed over a gate electrode, or an impurity element which serves as a donor is adsorbed onto a gate insulating film, whereby crystallinity can be increased at an interface with the gate insulating film in forming the microcrystalline semiconductor film. Thus, a thin film transistor can be manufactured in which the microcrystalline semiconductor film whose crystallinity has been increased at the interface with the gate insulating film is used for a channel formation region.
Further, with regard to a microcrystalline semiconductor film in contact with a gate insulating film, forming a microcrystalline semiconductor film including an impurity element which serves as a donor can increase the speed of carrier travel in the microcrystalline semiconductor film, so that a thin film transistor with high field effect mobility and high on-current can be manufactured.
The peak concentration of the impurity element which serves as a donor and is included in the gate insulating film or the microcrystalline semiconductor film is set to be from 6×1015 to 3×1018 atoms/cm3 inclusive, preferably from 3×1016 to 3×1017 atoms/cm3 inclusive, so that an accumulation-type thin film transistor (i.e., a thin film transistor in which a channel formation region includes an n-type impurity element at a low concentration) can be manufactured. When the peak concentration of the impurity element which serves as a donor and is included in the gate insulating film or the microcrystalline semiconductor film is lower than 6×1015 atoms/cm3, the amount of the impurity element which serves as a donor is insufficient, and thus an increase in the field effect mobility and in the on-current cannot be expected. Further, when the peak concentration of the impurity element which serves as a donor and is included in the gate insulating film or the microcrystalline semiconductor film is higher than 3×1018 atoms/cm3, the threshold value shifts to the minus side of the gate voltage, and the transistor does not function well; therefore, it is preferable that the concentration of the impurity element which serves as a donor be from 6×1015 to 3×1018 atoms/cm3 inclusive, preferably from 3×1016 to 3×1017 atoms/cm3 inclusive.
Further, a buffer layer is formed successively over the microcrystalline semiconductor film, whose crystallinity at the interface with the gate insulating film has been increased, and source and drain regions and source and drain wirings are formed over the buffer layer, so that a thin film transistor is formed.
Another feature of the present invention is that a pixel electrode connected to the thin film transistor is formed and a display device is manufactured.
Further, thin film transistors (TFTs) are manufactured using the microcrystalline semiconductor film of the present invention, and a display device is manufactured using the thin film transistors for a pixel portion and further for a driver circuit. Since the microcrystalline semiconductor film of the present invention has high crystallinity at the interface with the gate insulating film, a thin film transistor including the microcrystalline semiconductor film has a field effect mobility of from 2.5 to 10 cm2/V·sec, which is 5 to 20 times as high as that of a thin film transistor including an amorphous semiconductor film; thus, a part of the driver circuit or the entire driver circuit can be formed over the same substrate as that of the pixel portion, so that a system-on-panel can be manufactured.
Display devices include light-emitting devices and liquid crystal display devices. A light-emitting device includes a light-emitting element and a liquid crystal display device includes a liquid crystal element. A light-emitting element includes, in its category, an element whose luminance is controlled with current or voltage; specifically, an organic electroluminescent (EL) element and an inorganic EL element.
In addition, the display devices include a panel in which a display element is sealed, and a module in which an IC and the like including a controller are mounted on the panel. The present invention relates to one mode of an element substrate before the display element is completed in a manufacturing process of the display device, and the element substrate is provided with a means for supplying current to the display element in each of a plurality of pixels. Specifically, the element substrate may be in a state of being provided with only a pixel electrode of the display element, a state after a conductive film to be a pixel electrode is formed and before the conductive film is etched to form the pixel electrode, or any other states.
A display device in this specification means an image display device, a light-emitting device, or a light source (including a lighting device). Further, the display device includes any of the following modules in its category: a module including a connector such as a flexible printed circuit (FPC), tape automated bonding (TAB) tape, or a tape carrier package (TCP); a module having TAB tape or a TCP which is provided with a printed wiring board at the end thereof; and a module having an integrated circuit (IC) which is directly mounted on a display element by a chip on glass (COG) method.
According to the present invention, a microcrystalline semiconductor film which has high crystallinity from an interface with an insulating film can be formed, and a thin film transistor with excellent electric characteristics can be manufactured using the microcrystalline semiconductor film for a channel formation region. Further, a display device having the thin film transistor can be manufactured.
In the accompanying drawings:
Hereinafter, embodiment modes and embodiments of the present invention are described with reference to the drawings. Note that the present invention is not limited to the following description, and it is easily understood by those skilled in the art that the modes and details disclosed herein can be modified in various ways without departing from the spirit and scope of the present invention. Therefore, the present invention should not be interpreted as being limited to the description of the embodiment modes to be given below. In the structures of the present invention to be described hereinafter, reference numerals which designate the same parts are used in common in different drawings.
Embodiment Mode 1This embodiment mode describes structures of a thin film transistor which has high crystallinity at an interface between a microcrystalline semiconductor film and a gate insulating film, and has higher field effect mobility and higher on-current than a thin film transistor having a conventional microcrystalline semiconductor film in a channel formation region, with reference to
In a thin film transistor shown in
The microcrystalline semiconductor film 61 includes the impurity element which serves as a donor at a peak concentration of from 6×1015 to 3×1018 atoms/cm3 inclusive, preferably from 3×1016 to 3×1017 atoms/cm3 inclusive. Further, the microcrystalline semiconductor film 61 including the impurity element which serves as a donor has a thickness of from 1 to 50 nm inclusive. Examples of the microcrystalline semiconductor film are a microcrystalline silicon film, a microcrystalline silicon film including germanium, and the like. Further, examples of the impurity element which serves as a donor are phosphorus, arsenic, antimony, and the like.
The peak concentration of the impurity element which serves as a donor and is included in the microcrystalline semiconductor film is set to be in the above range, whereby the interface between the gate insulating film 52b and the microcrystalline semiconductor film 61 can have improved crystallinity and the microcrystalline semiconductor film 61 can have lower resistivity; thus, a thin film transistor with high mobility and high on-current can be manufactured. When the peak concentration of the impurity element which serves as a donor and is included in the microcrystalline semiconductor film is lower than 6×1015 atoms/cm3, the amount of the impurity element which serves as a donor is insufficient, and thus an increase in the field effect mobility and in the on-current cannot be expected. Further, when the peak concentration of the impurity element which serves as a donor and is included in the microcrystalline semiconductor film is higher than 3×1018 atoms/cm3, the threshold value shifts to the minus side of the gate voltage, and the transistor does not function well; therefore, it is preferable that the concentration of the impurity element which serves as a donor be from 6×1015 to 3×1018 atoms/cm3 inclusive, more preferably from 3×1016 to 3×1017 atoms/cm3 inclusive.
The microcrystalline semiconductor film here is a film including a semiconductor having an intermediate structure between amorphous and crystalline (including single crystalline and polycrystalline) structures. This semiconductor is in a third state, in which the semiconductor is stable in free energy, and is a crystalline semiconductor having short-range order and lattice distortion; columnar or needle-like crystals with a diameter of from 0.5 to 20 nm have grown in a direction of the normal to the surface of the substrate. Further, an amorphous semiconductor is present between a plurality of microcrystalline semiconductors. A Raman spectrum of microcrystalline silicon, which is a typical example of a microcrystalline semiconductor, is located in lower wave numbers than 520 cm−1, which represents a peak of a Raman spectrum of single crystalline silicon. That is to say, a peak of a Raman spectrum of microcrystalline silicon lies between 520 cm−1 and 480 cm−1, which represent a peak of a Raman spectrum of single crystalline silicon and that of amorphous silicon, respectively. Furthermore, the microcrystalline semiconductor film includes hydrogen or halogen at 1 at. % or more in order to terminate a dangling bond. The microcrystalline semiconductor film may further include a rare gas element such as helium, argon, krypton, or neon to further promote lattice distortion, so that the stability is enhanced and a favorable microcrystalline semiconductor film can be obtained. Such description about a microcrystalline semiconductor film is disclosed in, for example, U.S. Pat. No. 4,409,134.
The microcrystallines semiconductor film 61 including the impurity element which serves as a donor and the microcrystalline semiconductor film 58 are each formed with a thickness of from 1 to 200 nm inclusive, preferably from 1 to 100 nm inclusive, more preferably from 1 to 50 nm inclusive. The microcrystalline semiconductor film 61 including the impurity element which serves as a donor functions as a channel formation region of the thin film transistor which is completed later; if the thickness of the microcrystalline semiconductor film 61 is small, the microcrystalline semiconductor film 61 and also the microcrystalline semiconductor film 58 serve as the channel formation region of the thin film transistor which is completed later. When at least the microcrystalline semiconductor film 61 including the impurity element which serves as a donor is formed with a thickness of from 1 to 50 nm inclusive, the thin film transistor can be a complete depletion type.
Further, it is preferable that a concentration of oxygen and a concentration of nitrogen in the microcrystalline semiconductor film each be less than ten times that of the impurity element which serves as a donor, typically lower than 3×1019 atoms/cm3, preferably lower than 3×1018 atoms/cm3; and that a concentration of carbon be lower than or equal to 3×1018 atoms/cm3. Low concentrations of oxygen, nitrogen, and carbon in the microcrystalline semiconductor film can suppress generation of defects in the microcrystalline semiconductor film. Furthermore, oxygen and/or nitrogen in the microcrystalline semiconductor film hinders crystallization. Therefore, the microcrystalline semiconductor film includes oxygen and nitrogen at relatively low concentrations and includes the impurity element which serves as a donor, whereby the crystallinity of the microcrystalline semiconductor film can be enhanced.
The microcrystalline semiconductor film including the impurity element which serves as a donor of this embodiment mode includes the impurity element which serves as a donor; therefore, by adding an impurity element which serves as an acceptor to the microcrystalline semiconductor film which serves as the channel formation region of the thin film transistor at the same time as or after formation of the microcrystalline semiconductor film, the threshold value can be controlled. A typical example of the impurity element which serves as an acceptor is boron, and impurity gas such as B2H6 or BF3 is preferably mixed into silicon hydride at from 1 to 1000 ppm, preferably from 1 to 100 ppm. Further, a concentration of boron is preferably set to be approximately one-tenth that of the impurity element which serves as a donor, e.g., from 1×1014 to 6×1016 atoms/cm3.
An amorphous semiconductor film, an amorphous semiconductor film including halogen such as fluorine or chlorine, or an amorphous semiconductor film including nitrogen is used as the pair of buffer layers 73. The buffer layers 73 have a thickness of from 50 to 200 nm. Examples of the amorphous semiconductor film are an amorphous silicon film, an amorphous silicon film including germanium, and the like.
The pair of buffer layers 73, which are formed of an amorphous semiconductor film, have a larger energy gap and a higher resistivity than the microcrystalline semiconductor film 58; further, mobility in the pair of buffer layers 73 is one-fifth to one-tenth that of the microcrystalline semiconductor film 58. In the thin film transistor which is completed later, therefore, the buffer layers 73 function as high resistant regions and thus can reduce leakage current which is generated between the source and drain regions 72 and the microcrystalline semiconductor film 61.
For the substrate 50, an alkali-free glass substrate manufactured by a fusion method or a float method, such as barium borosilicate glass, aluminoborosilicate glass, or aluminosilicate glass; a ceramic substrate; a plastic substrate which has high heat resistance enough to withstand a process temperature of this manufacturing process; or the like can be used. Further, a metal (e.g., stainless steel alloy) substrate whose surface is provided with an insulating film may be used.
The gate electrode 51 is formed of a metal material. As a metal material, aluminum, chromium, titanium, tantalum, molybdenum, copper, or the like is used. The gate electrode 51 is preferably formed of aluminum or a stacked-layer structure of aluminum and a barrier metal. As a barrier metal, a metal with a high melting point, such as titanium, molybdenum, or chromium, is used. A barrier metal is preferably provided in order to prevent hillocks and oxidation of aluminum.
The gate electrode 51 is formed with a thickness of from 50 to 300 nm inclusive. The thickness of from 50 to 100 nm inclusive of the gate electrode 51 can prevent a disconnection of a semiconductor film and a wiring, which are formed later. Further, the thickness of from 150 to 300 nm inclusive of the gate electrode 51 can lower the resistance of the gate electrode 51, and increase the size of the substrate.
Since the semiconductor film and the wiring are formed over the gate electrode 51, the gate electrode 51 is preferably processed to have a tapered end portion so that the semiconductor film and the wiring thereover are not disconnected. Further, although not illustrated, a wiring or a capacitor wiring which is connected to the gate electrode can also be formed at the same time when the gate electrode is formed.
The gate insulating films 52a and 52b can each be formed using a silicon oxide film, a silicon nitride film, a silicon oxynitride film, or a silicon nitride oxide film with a thickness of from 50 to 150 nm. This embodiment mode presents an example in which a silicon nitride film or a silicon nitride oxide film is formed as the gate insulating film 52a, and a silicon oxide film or a silicon oxynitride film is formed as the gate insulating film 52b to form a stacked-layer structure. Instead of a two-layer structure, the gate insulating film can be formed using a single layer of a silicon oxide film, a silicon nitride film, a silicon oxynitride film, or a silicon nitride oxide film.
By forming the gate insulating film 52a using a silicon nitride film or a silicon nitride oxide film, adhesion between the substrate 50 and the gate insulating film 52a is increased, and further, impurities from the substrate 50 can be prevented from diffusing into the microcrystalline semiconductor film 61 including the impurity element which serves as a donor when a glass substrate is used for the substrate 50. Furthermore, oxidation of the gate electrode 51 can be prevented. That is to say, film peeling can be prevented, and electric characteristics of the thin film transistor which is completed later can be improved. Further, the gate insulating films 52a and 52b each having a thickness of greater than or equal to 50 nm are preferable because the gate insulating films 52a and 52b having the above thickness can alleviate reduction in coverage which is caused by unevenness due to the gate electrode 51.
Note that a silicon oxynitride film means a film that includes more oxygen than nitrogen, and includes oxygen, nitrogen, silicon, and hydrogen at concentrations ranging from 55 to 65 at. %, 1 to 20 at. %, 25 to 35 at. %, and 0.1 to 10 at. %, respectively. Further, a silicon nitride oxide film means a film that includes more nitrogen than oxygen, and includes oxygen, nitrogen, silicon, and hydrogen at concentrations ranging from 15 to 30 at. %, 20 to 35 at. %, 25 to 35 at. %, and 15 to 25 at. %, respectively.
If an n-channel thin film transistor is formed, the semiconductor films 72 to which the impurity element imparting one conductivity type is added may be doped with phosphorus, which is a typical impurity element; for example, impurity gas such as PH3 may be added to silicon hydride. If a p-channel thin film transistor is formed, the semiconductor films 72 to which the impurity element imparting one conductivity type is added may be doped with boron, which is a typical impurity element; for example, impurity gas such as B2H6 may be added to silicon hydride. The semiconductor films 72 to which the impurity element imparting one conductivity type is added include phosphorus or boron at a concentration of from 1×1019 to 1×1021 atoms/cm3, thereby having ohmic contact with the conductive film; thus, the semiconductor films 72 to which the impurity element imparting one conductivity type is added function as the source and drain regions. The semiconductor films 72 to which the impurity element imparting one conductivity type is added can be formed using a microcrystalline semiconductor or an amorphous semiconductor. The semiconductor films 72 to which the impurity element imparting one conductivity type is added are formed with a thickness of from 2 to 50 nm inclusive. Reduction in the thickness of the semiconductor film to which the impurity element imparting one conductivity type is added can improve the throughput.
The wirings 71a to 71c are preferably formed with a single layer or stacked layers using aluminum; copper; or an aluminum alloy to which an element for preventing hillocks or an element for improving heat resistance property, such as silicon, titanium, neodymium, scandium, or molybdenum, is added. Alternatively, a film in contact with the semiconductor film to which the impurity element imparting one conductivity type is added may be formed of titanium, tantalum, molybdenum, or tungsten, or nitride of such an element; and aluminum or an aluminum alloy may be formed thereover to form a stacked-layer structure. Further alternatively, top and bottom surfaces of aluminum or an aluminum alloy may be each covered with titanium, tantalum, molybdenum, tungsten, or nitride thereof to form a stacked-layer structure. This embodiment mode shows the conductive film having a three-layer structure of the wirings 71a to 71c; a stacked-layer structure in which the wirings 71a and 71c are formed using molybdenum films and the conductive film 71b is formed using an aluminum film, or a stacked-layer structure in which the wirings 71a and 71c are formed using titanium films and the wiring 71b is formed using an aluminum film is formed.
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate insulating films 52a and 52b, the microcrystalline semiconductor film 61 including the impurity element which serves as a donor, the microcrystalline semiconductor film 58 not including the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS, and the buffer layers 73 is schematically shown by curves 41 and 42 in
As shown in
It is not essential that the impurity element which serves as a donor in the microcrystalline semiconductor film be included only in a part on the gate insulating film side. As shown in
In a thin film transistor shown in
A feature of this mode is that the microcrystalline semiconductor film 61 including the impurity element which serves as a donor is formed between the gate insulating film 52b and the pair of buffer layers 73. It is preferable that the peak concentration of the impurity element which serves as a donor be from 6×1015 to 3×1018 atoms/cm3 inclusive, more preferably from 3×1016 to 3×1017 atoms/cm3 inclusive. Further, the microcrystalline semiconductor film 61 including the impurity element which serves as a donor has a thickness of from 5 to 100 nm inclusive, preferably from 10 to 50 nm inclusive. Furthermore, the peak concentration of the impurity element which serves as a donor may satisfy the above range in the entire microcrystalline semiconductor film 61; or the concentration of the impurity element which serves as a donor may have a peak at or around the interface between the gate insulating film 52b and the microcrystalline semiconductor film 61, and may decrease from the gate insulating film 52b toward the pair of buffer layers 73. Still furthermore, when the peak concentration of oxygen and the peak concentration of nitrogen in the microcrystalline semiconductor film 61 including the impurity element which serves as a donor are each less than ten times that of the impurity element which serves as a donor and further when the peak concentration of the impurity element which serves as an acceptor (a typical example is boron) is less than or equal to one-tenth that of the impurity element which serves as a donor, crystallinity of the microcrystalline semiconductor film including the impurity element which serves as a donor can be increased further.
The peak concentration of the impurity element which serves as a donor and is included in the microcrystalline semiconductor film is set to be in the above range, whereby the interface between the gate insulating film 52b and the microcrystalline semiconductor film 61 can have improved crystallinity and the microcrystalline semiconductor film 61 can have lower resistivity; thus, a thin film transistor with high field effect mobility and high on-current can be manufactured. When the peak concentration of the impurity element which serves as a donor and is included in the microcrystalline semiconductor film is lower than 6×1015 atoms/cm3, the amount of the impurity element which serves as a donor is insufficient, and thus an increase in the field effect mobility and in the on-current cannot be expected. Further, when the peak concentration of the impurity element which serves as a donor and is included in the microcrystalline semiconductor film is higher than 3×1018 atoms/cm3, the threshold value shifts to the minus side of the gate voltage, and the transistor does not function well; therefore, it is preferable that the concentration of the impurity element which serves as a donor be from 6×1015 to 3×1018 atoms/cm3 inclusive, preferably from 3×1016 to 3×1017 atoms/cm3 inclusive.
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate insulating films 52a and 52b, the microcrystalline semiconductor film 61 including the impurity element which serves as a donor, and the buffer layers 73 is schematically shown by curves 47 and 48 in
As shown by the curve 47 in
Next, a different mode from the above is presented with reference to
In the thin film transistor shown in
It is preferable that the peak concentration of phosphorus in the gate insulating film 59 including the impurity element which serves as a donor be from 6×1015 to 3×1018 atoms/cm3 inclusive, preferably from 3×1016 to 3×1017 atoms/cm3 inclusive. Further, the microcrystalline semiconductor film 58 has a thickness of from 1 to 50 nm inclusive.
The gate insulating film 52a can be formed using a similar material to that of the gate insulating film 52a shown in
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate insulating film 52a, the gate insulating film 59 including the impurity element which serves as a donor, the microcrystalline semiconductor film 58, and the buffer layers 73 is schematically shown by curves 43, 44, and 45 in
As shown in
Although a mode is presented here in which the gate insulating film 52a does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS and only the gate insulating film 59 includes the impurity element which serves as a donor, the present invention is not limited to this structure. For example, a gate insulating film may consist of one layer and may include an impurity element which serves as a donor. With SIMS, concentration distribution of the impurity element which serves as a donor in the stacked-layer portion including a gate insulating film 59a including an impurity element which serves as a donor, the microcrystalline semiconductor film 58, and the buffer layers 73 in the above case is schematically shown by the curve 44 in
In
In a thin film transistor shown in
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate insulating film 52a, the gate insulating film 59 including the impurity element which serves as a donor, the microcrystalline semiconductor film 61 including the impurity element which serves as a donor, and the buffer layers 73 is schematically shown by a curve 35 in
As shown in
A feature of this mode is that the gate insulating film 59, which is in contact with the microcrystalline semiconductor film 58 or the microcrystalline semiconductor film 61 including the impurity element which serves as a donor, includes the impurity element which serves as a donor. When the gate insulating film 59 on the microcrystalline semiconductor film 58 or 61 side includes the impurity element which serves as a donor, the impurity element which serves as a donor is deposited on a surface of the gate insulating film 59, whereby crystallinity of the microcrystalline semiconductor film 58 or 61 can be increased in starting deposition of the microcrystalline semiconductor film 58 or 61.
Further, another feature is that the gate insulating film on the gate electrode 51 side includes the impurity element which serves as a donor. When the gate insulating film on the gate electrode 51 side includes the impurity element which serves as a donor, the impurity element can be diffused into the gate insulating film on the microcrystalline semiconductor film side at a low concentration. Accordingly, crystallinity can be increased at the interface between the gate insulating film 59 and the microcrystalline semiconductor film 58 or 61 and resistivity of the microcrystalline semiconductor film 58 or 61 can be reduced; thus, a thin film transistor with high field effect mobility and high on-current can be manufactured.
When the peak concentration of the impurity element which serves as a donor and is included in the gate insulating film 59 is lower than 6×1015 atoms/cm3, the amount of the impurity element which serves as a donor is insufficient, and thus an increase in the field effect mobility and in the on-current cannot be expected. Further, when the peak concentration of the impurity element which serves as a donor and is included in the gate insulating film 59 is higher than 3×1018 atoms/cm3, the threshold value shifts to the minus side of the gate voltage, and the transistor does not function well; therefore, it is preferable that the concentration of the impurity element which serves as a donor be from 6×1015 to 3×1018 atoms/cm3 inclusive, preferably from 3×1016 to 3×1017 atoms/cm3 inclusive.
By forming the microcrystalline semiconductor film 61 including the impurity element which serves as a donor over the gate insulating film 59 including the impurity element which serves as a donor, crystallinity of the microcrystalline semiconductor film 61 can be increased in starting deposition of the microcrystalline semiconductor film 61; in addition, resistivity of the microcrystalline semiconductor film can be reduced further because the impurity element which serves as a donor is included also in the microcrystalline semiconductor film 61, which functions as a channel. Thus, a thin film transistor with high on-current and high field effect mobility can be manufactured.
Next, a different mode from the above is presented with reference to
In a thin film transistor shown in
It is preferable that the peak concentration of the impurity element which serves as a donor in the gate insulating films 59a and 59b including the impurity element which serves as a donor and in the microcrystalline semiconductor film 61 including the impurity element which serves as a donor be from 6×1015 to 3×1018 atoms/cm3 inclusive, more preferably from 3×1016 to 3×1017 atoms/cm3 inclusive.
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate electrode 51, the gate insulating films 59a and 59b including the impurity element which serves as a donor, the microcrystalline semiconductor film 61 including the impurity element which serves as a donor, and the buffer layers 73 is schematically shown by a curve 46 in
As shown in
The thin film transistor shown in
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate insulating films 59a and 59b including the impurity element which serves as a donor, the microcrystalline semiconductor film 61 including the impurity element which serves as a donor, the microcrystalline semiconductor film 58, and the buffer layers 73 is schematically shown by a curve 33 in
As shown in
Forming the microcrystalline semiconductor film 58 over the microcrystalline semiconductor film 61 including the impurity element which serves as a donor can prevent the impurity element which serves as a donor in the microcrystalline semiconductor film 61 from being diffused into the pair of buffer layers 73. If the impurity element which serves as a donor is diffused into the pair of buffer layers 73, which are high resistant regions, resistance of the pair of buffer layers 73 decreases and leakage current flows between the microcrystalline semiconductor film 61 including the impurity element which serves as a donor and the source and drain regions 72, thereby degrading switching characteristics. Therefore, it is preferable to form the microcrystalline semiconductor film 58 not including the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS between the microcrystalline semiconductor film 61 including the impurity element which serves as a donor and the pair of buffer layers 73. The shape of the curve 33, which shows concentration distribution of the impurity element which serves as a donor, is not limited to that shown in
In
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate insulating films 59a and 59b including the impurity element which serves as a donor, the microcrystalline semiconductor film 58, and the buffer layers 73 is schematically shown by a curve 34 in
As shown in
Next, a different mode from the above is presented with reference to
In the thin film transistor shown in
A feature of this mode is that the second microcrystalline semiconductor film 64 including the impurity element which serves as a donor is formed between the first microcrystalline semiconductor film 58a and the third microcrystalline semiconductor film 58b, which do not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS. It is preferable that the peak concentration of the impurity element which serves as a donor be from 6×1015 to 3×1018 atoms/cm3 inclusive, more preferably from 3×1016 to 3×1017 atoms/cm3 inclusive.
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate insulating films 52a and 52b, the first microcrystalline semiconductor film 58a, the second microcrystalline semiconductor film 64 including the impurity element which serves as a donor, the third microcrystalline semiconductor film 58b, and the buffer layer 73 is schematically shown by a curve 49 in
As shown in
In the above manner, the accumulation-type thin film transistor in which the gate insulating film and/or the microcrystalline semiconductor film includes the impurity element which servers as a donor is formed, whereby crystallinity can be increased at the interface between the gate insulating film and the microcrystalline semiconductor film, and resistivity of the microcrystalline semiconductor film can be reduced; thus, a thin film transistor with high field effect mobility and high on-current can be manufactured.
Further, forming a channel formation region with a microcrystalline semiconductor film suppresses variation in threshold voltage, improves field effect mobility, and lowers subthreshold swing (S value); thus, a thin film transistor can achieve high performance. Accordingly, a display device can be driven at a high frequency, whereby the panel size can be increased and pixels in the display device can be made with high density.
Embodiment Mode 2This embodiment mode presents a thin film transistor in which a gate insulating film has a different structure from that of the thin film transistors shown in Embodiment Mode 1, with reference to
Instead of the gate insulating films 52a and 52b of the thin film transistor shown in
Further, instead of the two gate insulating films 52a and 52b, as shown in
As the gate insulating films 52a and 52b, which are first and second layers, a silicon nitride film, a silicon nitride oxide film, a silicon oxide film, or a silicon oxynitride film can be formed by a plasma CVD method or a sputtering method in a similar manner to Embodiment Mode 1. As the gate insulating film 59c including the impurity element which serves as a donor, which is a third layer, a silicon nitride film or a silicon nitride oxide film with a thickness of from 1 to 5 nm approximately which includes phosphorus, arsenic, or antimony can be formed.
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate insulating films 52a and 52b, the gate insulating film 59c including the impurity element which serves as a donor, the microcrystalline semiconductor film 58, and the pair of buffer layers 73 is schematically shown by a curve 36 in
As shown in
Instead of the microcrystalline semiconductor film 58 shown in
Next, with SIMS, concentration distribution of the impurity element which serves as a donor in a stacked-layer portion including the gate insulating films 52a and 52b, the gate insulating film 59c including the impurity element which serves as a donor, the microcrystalline semiconductor film 61 including the impurity element which serves as a donor, and the pair of buffer layers 73 is schematically shown by a curve 37 in
As shown in
When a silicon nitride film or a silicon nitride oxide film with a thickness of from 1 to 5 nm approximately, or a silicon nitride film or a silicon nitride oxide film which includes an impurity element which serves as a donor and has a thickness of from 1 to 5 nm approximately is formed as the gate insulating film 52c or 59c, which is the third layer, a plasma CVD method can be employed. Further, it is also possible to have the gate insulating film 52b undergo nitridation treatment with high-density plasma to form a silicon nitride layer on a surface of the gate insulating film 52b. By high-density plasma nitridation, a silicon nitride layer that includes nitrogen at a higher concentration can be obtained. The high-density plasma is generated by use of high-frequency microwaves, for example, microwaves with a frequency of 2.45 GHz. With high-density plasma, which has the characteristic of having a low electron temperature, a layer can be formed with less plasma damage and fewer defects compared to a layer formed by conventional plasma treatment because the kinetic energy of an active species is low. In addition, with use of high-density plasma, carrier mobility can be increased because the level of roughness on the surface of the gate insulating film 52b can be reduced.
In a microcrystalline semiconductor film, an amorphous semiconductor and a crystalline semiconductor are mixed. Thus, when the amorphous semiconductor comes to be in contact with silicon oxide or silicon oxynitride, hydrogen in the amorphous semiconductor tends to react with the silicon oxide or the silicon oxynitride, so that hydrogen concentration in the microcrystalline semiconductor film decreases and the interface between the gate insulating film and the microcrystalline semiconductor film deteriorates. Therefore, a silicon nitride film or a silicon nitride oxide film with a small thickness that is formed as a base film for the microcrystalline semiconductor film can serve as a blocking film for preventing hydrogen from diffusing, so that deterioration of the interface between the gate insulating film and the microcrystalline semiconductor film can be reduced.
It is possible to apply the above structure of the gate insulating film to the gate insulating film of the thin film transistors shown in
This embodiment mode describes processes for manufacturing the thin film transistors described in Embodiment Mode 1.
With regard to a thin film transistor including a microcrystalline semiconductor film, an n-channel thin film transistor has higher field effect mobility than a p-channel thin film transistor; thus, an n-channel thin film transistor is more suitable for a driver circuit. Further, it is preferable that all the thin film transistors formed over one substrate have the same polarity so that the number of manufacturing steps is reduced. In description of this embodiment mode, an n-channel thin film transistor is used.
First, manufacturing processes of the thin film transistors shown in
As shown in
The gate electrode 51 is formed by a sputtering method, a CVD method, a plating method, a printing method, a droplet discharge method, or the like using any of the metal materials described in Embodiment Mode 1. In this embodiment mode, a molybdenum film is formed as a conductive film over the substrate 50 by a sputtering method and is etched with use of a resist mask that is formed using a first photomask, whereby the gate electrode 51 is formed.
Each of the gate insulating films 52a and 52b can be formed by a CVD method, a sputtering method, or the like using a silicon oxide film, a silicon nitride film, a silicon oxynitride film, or a silicon nitride oxide film.
Next, after an impurity element which serves as a donor is adsorbed onto the gate insulating film 52b, a microcrystalline semiconductor film is deposited by a plasma CVD method using a deposition gas including silicon or germanium, and hydrogen, whereby a microcrystalline semiconductor film 57 including the impurity element which serves as a donor is formed.
As a typical example of a method for forming a microcrystalline semiconductor film including an impurity element which serves as a donor, a process for forming a microcrystalline silicon film including phosphorus is described in chronological order with reference to
First, vacuum evacuation is performed in a reaction chamber to a predetermined degree of vacuum (hereinafter, such a pressure is called as NP (Normal Pressure)). In the case of high vacuum evacuation, vacuum evacuation is performed with use of a turbo molecular pump or the like to obtain a pressure lower than 10−1 Pa as a degree of vacuum. Alternatively, vacuum evacuation may be performed with use of a cryopump to reduce a pressure in the reaction chamber to be lower than 10−5 Pa, i.e., to an ultrahigh vacuum. In addition, preferably, a heat treatment is performed to the reaction chamber so as to degas the inner wall of the reaction chamber. Further, the temperature is stabilized by operating a heater for heating the substrate. The substrate heating temperature is from 100 to 300° C., preferably from 120 to 220° C.
In the precoating treatment 441, the inner wall of the reaction chamber of the plasma CVD apparatus is precoated with a film having a composition that is the same as or similar to the gate insulating film. Accordingly, it is possible to prevent a metal used to form the reaction chamber from entering the gate insulating film as an impurity. In other words, by covering the inner wall of the reaction chamber with the film having a composition that is the same as or similar to the gate insulating film, the inner wall of the reaction chamber can be prevented from being etched by plasma, and the concentration of the impurity which enters the gate insulating film from the reaction chamber can be reduced.
In the substrate carrying-in 442, the substrate is carried into the reaction chamber from a load lock chamber connected to the reaction chamber. The pressure in the reaction chamber at this time is the same as that in the load lock chamber (hereinafter such a pressure is called as LP (Load Lock Pressure)).
In the film formation treatment (1) 443 for forming the gate insulating film 52a, source gases, which are hydrogen, silane, and ammonia in this example, are introduced and mixed, so that a pressure in the reaction chamber reaches a predetermined value (hereinafter such a pressure is called as SP (Setting Pressure)), and a silicon nitride film is formed by glow discharge plasma which is generated by application of high-frequency power. Nitrogen may also be introduced in addition to the above source gases. After the gate insulating film 52a is formed, introduction of the above source gases is halted, and the power is turned off, and then, generation of plasma is halted.
In the vacuum evacuation treatment 444, vacuum evacuation is performed in the reaction chamber to a predetermined degree of vacuum.
In the film formation treatment (2) 445 for forming the gate insulating film 52b, source gases, which are hydrogen, silane, and dinitrogen monoxide in this example, are introduced and mixed, and a silicon oxynitride film is formed by glow discharge plasma which is generated by application of high-frequency power. After the gate insulating film 52b is formed, introduction of the above source gases is halted, and the power is turned off, and then, generation of plasma is halted.
In the vacuum evacuation treatment 446, vacuum evacuation is performed in the reaction chamber to a predetermined degree of vacuum.
In the flush treatment 447, gas including an impurity element which serves as a donor is introduced to the reaction chamber, and the impurity element which serves as a donor is adsorbed onto the surface of the gate insulating film 52b, furthermore, onto the inner wall of the reaction chamber. In this embodiment mode, 0.001% to 1% phosphine (diluted with hydrogen or silane) is introduced to the reaction chamber. Phosphine is not necessarily diluted with hydrogen or silane. In addition to the gas including the impurity element which serves as a donor, deposition gas including silicon or germanium may be introduced as designated by a dashed line 461 or hydrogen may be introduced as designated by a dashed line 462, to the reaction chamber. By introducing deposition gas including silicon or germanium, or hydrogen to the reaction chamber, an impurity such as oxygen, nitrogen, or fluorine in the reaction chamber can be discharged from the reaction chamber, so that contamination of a film to be formed can be prevented.
In the film formation treatment (3) 448 for forming the microcrystalline semiconductor film 57 including the impurity element which serves as a donor, deposition gas including silicon or germanium, which is silane in this example, hydrogen, and/or rare gas are introduced and mixed in the reaction chamber, and a microcrystalline semiconductor film is formed by glow discharge plasma which is generated by application of high-frequency power. Silane is diluted with hydrogen and/or rare gas to be 10 to 2000 times thinner. Therefore, a large amount of hydrogen and/or rare gas is needed. The substrate heating temperature is from 100 to 300° C., preferably from 120 to 220° C. It is preferable that the film be formed at temperatures of from 120 to 220° C. so that a growing surface of the microcrystalline silicon film may be inactivated with hydrogen to promote growth of microcrystalline silicon. At this time, the microcrystalline semiconductor grows using the impurity element which serves as a donor and is adsorbed onto the surface of the gate insulating film 52b, which is phosphorus in this example, as a crystal nucleus. Thus, an amorphous semiconductor is not formed in an early stage of deposition of the semiconductor film, and crystals grow in a direction of the normal to the gate insulating film 52b, so that a microcrystalline semiconductor film with high crystallinity in which column-like microcrystalline semiconductors are present can be formed. In addition, the impurity element which serves as a donor and is adsorbed onto the surface of the gate insulating film 52b is included in the microcrystalline semiconductor film, so that a highly conductive microcrystalline semiconductor film 57 including the impurity element which serves as a donor can be formed.
Further, an energy band width may be adjusted to be from 0.9 to 1.1 eV by mixing germanium hydride or germanium fluoride such as GeH4 or GeF4 into gas such as silane. By adding germanium to silicon, the temperature characteristics of a thin film transistor can be changed.
In the substrate carrying-out 449, the substrate is carried out of the reaction chamber and carried into the load lock chamber connected to the reaction chamber. The pressure in the reaction chamber at this time is the same as that in the load lock chamber.
The film formation treatment (3) 448 for forming the microcrystalline semiconductor film 57 including the impurity element which serves as a donor is carried out after the flush treatment 447 in this embodiment mode. However, instead of these treatments, the microcrystalline semiconductor film 57 including the impurity element which serves as a donor can be formed without the flush treatment 447 as follows: deposition gas including silicon or germanium, hydrogen, and/or rare gas, and gas including an impurity element which serves as a donor are introduced and mixed, and the microcrystalline semiconductor film 57 including the impurity element which serves as a donor is formed by glow discharge plasma which is generated by application of high-frequency power.
In a conventional method for forming a microcrystalline semiconductor film, an amorphous semiconductor layer is formed in an early stage of deposition due to impurities except the impurity element which serves as a donor, lattice mismatch, or the like. In an inverted-staggered thin film transistor, carriers flow in a region of a microcrystalline semiconductor film which is near to the gate insulating film. Thus, when an amorphous semiconductor layer is formed at the interface between a gate insulating film and the microcrystalline semiconductor film, field effect mobility decreases, and further, the amount of current reduces, so that electric characteristics of the thin film transistor deteriorate.
However, by forming the microcrystalline semiconductor film including the impurity element which serves as a donor over the gate insulating film as in this embodiment mode, crystallinity in a film thickness direction can be improved, and crystallinity at the interface between the gate insulating film and the microcrystalline semiconductor film can be improved.
Next, as shown in
Next, as shown in
As the buffer layer 54, an amorphous semiconductor film can be formed by a plasma CVD method using deposition gas including silicon or germanium. Alternatively, by diluting deposition gas including silicon or germanium with one or plural kinds of rare gases selected from helium, argon, krypton, and neon, an amorphous semiconductor film can be formed. Furthermore, an amorphous semiconductor film including hydrogen can be formed using hydrogen with a flow rate of 1 to 10 times, preferably 1 to 5 times as high as that of deposition gas including silicon or germanium. In addition, halogen such as fluorine or chlorine, or nitrogen may be added to the above hydrogenated semiconductor film.
Still furthermore, as the buffer layer 54, an amorphous semiconductor film can be formed by sputtering a semiconductor such as silicon or germanium, which is used as a target, with hydrogen or rare gas.
The buffer layer 54 is preferably formed using an amorphous semiconductor film which does not include crystal grains. Therefore, if the buffer layer 54 is formed by a high-frequency plasma CVD method with a frequency of several tens of MHz to several hundreds MHz or a microwave plasma CVD method, film formation conditions are preferably controlled such that an amorphous semiconductor film does not include crystal grains.
The buffer layer 54 is partly etched to be a pair of buffer layers in a later step for forming source and drain regions. At this time, the pair of buffer layers function as high resistant regions; thus, typically, it is preferable to form the buffer layer 54 with a thickness of from 30 to 500 nm inclusive, preferably from 50 to 200 nm inclusive. In a display device including a thin film transistor to which a high voltage (e.g., approximately 15 V) is applied, typically, in a liquid crystal display device, if the buffer layer 54 is formed thickly, withstand voltage is increased, so that deterioration of the thin film transistor can be prevented even if a high voltage is applied to the thin film transistor.
Since the buffer layer 54 is formed using an amorphous semiconductor film or an amorphous semiconductor film including hydrogen, nitrogen, or halogen, the buffer layer 54 has a larger energy gap and higher resistivity than the microcrystalline semiconductor film 53 and low mobility which is one-fifth to one-tenth that of the microcrystalline semiconductor film 53. Therefore, in a thin film transistor to be completed later, the buffer layers formed between the source and drain regions and the microcrystalline semiconductor film 53 function as high resistant regions and the microcrystalline semiconductor film 57 including the impurity element which serves as a donor functions as a channel formation region. Accordingly, off-current of the thin film transistor can be reduced. In addition, when the thin film transistor is used as a switching element of a display device, the display device can have an improved contrast.
The buffer layer 54 can also be formed at temperatures of from 300 to 400° C. by a plasma CVD method after forming the microcrystalline semiconductor film 53. By this treatment, hydrogen is supplied to the microcrystalline semiconductor film 53, and the same effect as hydrogenizing the microcrystalline semiconductor film 53 can be obtained. In other words, by depositing the buffer layer 54 over the microcrystalline semiconductor film 53, hydrogen is diffused into the microcrystalline semiconductor film 53, so that a dangling bond can be terminated.
By forming the buffer layer 54 after forming the microcrystalline semiconductor film 57 including the impurity element which serves as a donor without forming the microcrystalline semiconductor film 53, the thin film transistor as shown in
With regard to the semiconductor film 55 to which the impurity element imparting one conductivity type is added, in the case where an n-channel thin film transistor is formed, phosphorus may be added as a typical impurity element, and impurity gas such as PH3 may be added to silicon hydride. When a p-channel thin film transistor is formed, boron may be added as a typical impurity element, and impurity gas such as B2H6 may be added to silicon hydride. The semiconductor film 55 to which the impurity element imparting one conductivity type is added can be formed of a microcrystalline semiconductor or an amorphous semiconductor. The semiconductor film 55 to which the impurity element imparting one conductivity type is added is formed with a thickness of from 2 to 50 nm inclusive. By forming a semiconductor film to which an impurity element imparting one conductivity type is added with a small thickness, throughput can be improved.
Then, the resist mask 56 is formed over the semiconductor film 55 to which the impurity element imparting one conductivity type is added.
The resist mask 56 is formed by a photolithography technique. Here, using a second photomask, the resist mask 56 is formed by exposing a resist that is applied on the semiconductor film 55 to which the impurity element imparting one conductivity type is added to light and developing the resist.
Next, the microcrystalline semiconductor film 57 including the impurity element which serves as a donor, the microcrystalline semiconductor film 53, the buffer layer 54, and the semiconductor film 55 to which the impurity element imparting one conductivity is added are etched to be separated using the resist mask 56, whereby a microcrystalline semiconductor film 61 including the impurity element which serves as a donor, a microcrystalline semiconductor film 58, a buffer layer 62, and a semiconductor film 63 to which the impurity element imparting one conductivity type is added are formed as shown in
With side surfaces of end portions of the microcrystalline semiconductor film 61, the microcrystalline semiconductor film 58, and the buffer layer 62 having inclines, the microcrystalline semiconductor film 58 and the source and drain regions have a larger distance therebetween, so that leakage current between the microcrystalline semiconductor film 61 and the source and drain regions formed over the buffer layer can be prevented. In addition, leakage current between wirings and the microcrystalline semiconductor film 61 can also be prevented. The inclination angle of the side surfaces of the end portions of the microcrystalline semiconductor film 61, the microcrystalline semiconductor film 58, and the buffer layer 62 is from 30° to 90°, preferably from 45° to 80°. With such an angle, disconnection of the wirings due to a step shape can be prevented.
Next as shown in
The resist mask 66 can be formed in a manner similar to the resist mask 56.
Next, as shown in
Then, the semiconductor film 63 to which the impurity element imparting one conductivity type is added is etched to be separated using the resist mask 66. As a result, a pair of source and drain regions 72 can be formed as shown in
Next, dry etching is performed under such a condition that the exposed microcrystalline semiconductor film 58 is not damaged and an etching rate with respect to the microcrystalline semiconductor film 58 is low. Through this dry etching step, an etching residue on the microcrystalline semiconductor film 58 between the source region and the drain region, a residue of the resist mask, and a contamination source in an apparatus used for removal of the resist mask can be removed, whereby the source region and the drain region can be insulated surely. As a result, leakage current of the thin film transistor can be reduced, so that a thin film transistor with small off-current and high withstand voltage can be manufactured. A chlorine gas can be used for an etching gas, for example.
Through the above process, a channel-etched thin film transistor 74 can be formed.
Next, as shown in
Next, as shown in
The pixel electrode 77 can be formed of a light-transmitting conductive material such as indium oxide including tungsten oxide, indium zinc oxide including tungsten oxide, indium oxide including titanium oxide, indium tin oxide including titanium oxide, indium tin oxide (ITO), indium zinc oxide, or indium tin oxide to which silicon oxide is added.
The pixel electrode 77 can be formed using a conductive composition including a conductive high-molecular compound (also referred to as a conductive polymer). It is preferable that a pixel electrode formed using a conductive composition have sheet resistance of less than or equal to 10000 Ω/square, and light transmittance of greater than or equal to 70% at a wavelength of 550 nm. In addition, the resistivity of the conductive high-molecular compound which is included in the conductive composition is preferably less than or equal to 0.1 Ω·cm.
As the conductive high-molecular compound, a “π electron conjugated conductive high-molecular compound” can be used. Examples thereof include polyaniline and derivatives thereof, polypyrrole and derivatives thereof, polythiophene and derivatives thereof, and copolymers of two or more kinds of them.
In this embodiment mode, the pixel electrode 77 is formed as follows: an ITO film is formed by a sputtering method, and a resist is applied on the ITO film, exposed to light, and developed using a fifth photomask, thereby forming a resist mask; then, the ITO film is etched using the resist mask to form the pixel electrode 77.
Accordingly, a thin film transistor and an element substrate that can be used for a display device can be formed.
Next, a process for manufacturing the thin film transistor shown in
As in the step shown in
Next, as shown in
As a typical example of a method for forming the gate insulating film 59 including the impurity element which serves as a donor, a process for forming a silicon oxynitride film including phosphorus is described in chronological order with reference to
The precoating treatment 441, the substrate carrying-in 442, the film formation treatment (1) 443 for forming the gate insulating film 52a, the vacuum evacuation treatment 444, the vacuum evacuation treatment 446, and the substrate carrying-out 449 are the same as in
In the film formation treatment (2) 450 for forming the gate insulating film 59 including the impurity element which serves as a donor, gas including the impurity element which serves as a donor is introduced to source gas for forming the gate insulating film. In this embodiment mode, silane, dinitrogen monoxide, and 0.001% to 1% phosphine (diluted with hydrogen or silane) are introduced to the reaction chamber, and a silicon oxynitride film including phosphorus is formed by glow discharge plasma. After the gate insulating film 59 including the impurity element which serves as a donor is formed, introduction of the above source gas is halted, and the power is turned off, and then, generation of plasma is halted.
In the film formation treatment (3) 451 for forming the microcrystalline semiconductor film 53, deposition gas including silicon or germanium, which is silane in this example, hydrogen, and/or rare gas are introduced and mixed in the reaction chamber, and a microcrystalline semiconductor film is formed by glow discharge plasma which is generated by application of high-frequency power. Silane is diluted with hydrogen and/or rare gas to be 10 to 2000 times thinner. Therefore, a large amount of hydrogen and/or rare gas is needed. The substrate heating temperature is from 100 to 300° C., preferably from 120 to 220° C. After the microcrystalline semiconductor film 53 is formed, introduction of the above source gas is halted, and the power is turned off, and then, generation of plasma is halted.
In order to form a microcrystalline semiconductor film which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS as the microcrystalline semiconductor film 53, the following process is carried out. When the gate insulating film 59 including the impurity element which serves as a donor begins to be deposited, gas including the impurity element which serves as a donor, which is phosphine in this example, is introduced to the reaction chamber, and then, introduction of phosphine is halted, and a silicon oxynitride film is formed, so that almost all phosphorus in the reaction chamber is included in the silicon oxynitride film. Therefore, the microcrystalline semiconductor film 53, which is formed later, does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS. Alternatively, after the gate insulating film 59 including the impurity element which serves as a donor is formed, the substrate is carried out of the reaction chamber, and the inside of the reaction chamber is cleaned, and then, the substrate is carried into the reaction chamber again and the microcrystalline semiconductor film 53 is formed, whereby the microcrystalline semiconductor film 53, which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS, can be formed. Further alternatively, after the gate insulating film 59 including the impurity element which serves as a donor is formed, the substrate is carried out of the reaction chamber, and the microcrystalline semiconductor film 53 is formed in a different reaction chamber, whereby the microcrystalline semiconductor film 53, which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS, can be formed.
Further, by forming a microcrystalline semiconductor film including an impurity element which serves as a donor instead of the microcrystalline semiconductor film 53 in
Next, through the steps shown in
Next, another manufacturing method of the thin film transistor shown in
As a typical example of a method for forming the gate insulating film 59 including the impurity element which serves as a donor, a process for forming a silicon oxynitride film including phosphorus is described in chronological order with reference to
The precoating treatment 441, the substrate carrying-in 442, the film formation treatment (1) 443 for forming the gate insulating film 52a, the vacuum evacuation treatment 444, the vacuum evacuation treatment 446, the film formation treatment (3) 451 for forming the microcrystalline semiconductor film 53, and the substrate carrying-out 449 are the same as in
In the flush treatment 447, gas including the impurity element which serves as a donor is introduced to the reaction chamber, and the impurity element which serves as a donor is adsorbed onto the surface of the gate insulating film 52a, furthermore, onto the inner wall of the reaction chamber. In this embodiment mode, 0.001% to 1% phosphine (diluted with hydrogen or silane) is introduced to the reaction chamber. In addition to the gas including the impurity element which serves as a donor, hydrogen may be introduced as designated by a dashed line 462, or deposition gas including silicon or germanium may be introduced as designated by a dashed line 461, to the reaction chamber.
In the film formation treatment (2) 457 for forming the gate insulating film 59 including the impurity element which serves as a donor, source gases, which are hydrogen, silane, and dinitrogen monoxide in this example, are introduced to the reaction chamber, and a silicon oxynitride film is formed by glow discharge plasma which is generated by application of high-frequency power. At this time, the silicon oxynitride film is deposited while taking in the impurity element which serves as a donor and is deposited over the surface of the gate insulating film 52a and is adsorbed onto the surface of the inner wall of the reaction chamber, which is phosphorus in this example. Thus, a silicon oxynitride film including phosphorus can be formed. After the gate insulating film 59 including the impurity element which serves as a donor is formed, introduction of the above source gas is halted, and the power is turned off, and then, generation of plasma is halted.
In the film formation treatment (3) 451 for forming the microcrystalline semiconductor film 53, in order to form a microcrystalline semiconductor film which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS, the following process is carried out. When the gate insulating film 59 including the impurity element which serves as a donor begins to be deposited, gas including the impurity element which serves as a donor, which is phosphine in this example, is introduced to the reaction chamber, and then, introduction of phosphine is shalted, and a silicon oxynitride film is formed, so that almost all phosphorus in the reaction chamber is included in the silicon oxynitride film. Therefore, the microcrystalline semiconductor film 53, which is formed later, does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS. Alternatively, after the gate insulating film 59 including the impurity element which serves as a donor is formed, the substrate is carried out of the reaction chamber, and the inside of the reaction chamber is cleaned, and then, the substrate is carried into the reaction chamber again, and the microcrystalline semiconductor film 53 is formed, whereby the microcrystalline semiconductor film 53, which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS, can be formed. Further alternatively, after the gate insulating film 59 including the impurity element which serves as a donor is formed, the substrate is carried out of the reaction chamber, and the microcrystalline semiconductor film 53 is formed in a different reaction chamber, whereby the microcrystalline semiconductor film 53, which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS, can be formed.
Next, through the steps shown in
Further, by forming a microcrystalline semiconductor film including an impurity element which serves as a donor instead of the microcrystalline semiconductor film 53, the thin film transistor as shown in
Next, a process for manufacturing the thin film transistor shown in
As in the step shown in
Next, after a film including the impurity element which serves as a donor is formed as a protective film on the inner wall of a reaction chamber of a plasma CVD apparatus, the substrate 50 is carried into the reaction chamber, and then, gate insulating films and a microcrystalline semiconductor film are deposited over the gate electrode 51. In this case, by making the inside of the reaction chamber vacuum and by generating plasma, the impurity element which serves as a donor is released from the protective film formed on the inner wall of the reaction chamber to the inside of the reaction chamber. The gate insulating films and the microcrystalline semiconductor film are formed while taking in the impurity element which serves as a donor and is released from the protective film, so that gate insulating films each including the impurity element which serves as a donor and a microcrystalline semiconductor film including the impurity element which serves as a donor can be formed over the gate electrode 51.
As a typical example of a method for forming gate insulating films and a microcrystalline semiconductor film each including an impurity element which serves as a donor, a process for forming a silicon nitride film including phosphorus, a silicon oxynitride film including phosphorus, and a microcrystalline silicon film including phosphorus is described in chronological order with reference to
In the precoating treatment 452, the inner wall of the reaction chamber of the plasma CVD apparatus is precoated with, as a protective film, a film having composition that is the same as or similar to the gate insulating film including the impurity element which serves as a donor. In this embodiment mode, 0.001% to 1% phosphine (diluted with hydrogen), deposition gas including silicon or germanium, which is silane in this example, hydrogen, and at least one of ammonia, dinitrogen monoxide, and nitrogen are introduced to the reaction chamber. Then, by glow discharge plasma, a silicon oxynitride film including phosphorus, a silicon oxide film including phosphorus, a silicon nitride film including phosphorus, or a silicon nitride oxide film including phosphorus is formed. Accordingly, it is possible to prevent a metal used to form the reaction chamber from entering the gate insulating films as an impurity and to add the impurity element which serves as a donor to the gate insulating films and the microcrystalline semiconductor film, which are formed later.
In the substrate carrying-in 442, the substrate is carried into the reaction chamber from a load lock chamber connected to the reaction chamber. Before and after the substrate carrying-in, the pressure in the reaction chamber is reduced for performing vacuum evacuation. At that time, the impurity element which serves as a donor is released from the precoating protective film formed on the inner wall of the reaction chamber into the inside of the reaction chamber.
In the film formation treatment (1) 453 for forming the gate insulating film 59a including the impurity element which serves as a donor, source gases, which are hydrogen, silane, and ammonia in this example, are introduced and mixed. Then, a silicon nitride film is deposited by glow discharge plasma which is generated by application of high-frequency power, while taking in the impurity element which serves as a donor and is released into the inside of the reaction chamber, which is phosphorus in this example. When glow discharge plasma spreads to the inner wall of the reaction chamber, the impurity element which serves as a donor, which is phosphorus in this example, is released from the precoating protective film formed on the inner wall of the reaction chamber, in addition to the above source gases. Accordingly, a silicon nitride film including phosphorus can be formed. Nitrogen may also be introduced to the reaction chamber in addition to the above source gases. After the gate insulating film 59a including the impurity element which serves as a donor is formed, introduction of the above source gas is halted, and the power is turned off, and then, generation of plasma is halted.
In the vacuum evacuation treatment 444, vacuum evacuation is performed in the reaction chamber to a predetermined degree of vacuum.
In the film formation treatment (2) 454 for forming the gate insulating film 59b including the impurity element which serves as a donor, source gases, which are hydrogen, silane, and dinitrogen monoxide in this example, are introduced and mixed. Then, a silicon oxynitride film is deposited by glow discharge plasma which is generated by application of high-frequency power, while taking in the impurity element which serves as a donor and is released into the inside of the reaction chamber, which is phosphorus in this example. After the gate insulating film 59b including the impurity element which serves as a donor is formed, introduction of the above source gases is halted, and the power is turned off, and then, generation of plasma is halted.
In the vacuum evacuation treatment 446, vacuum evacuation is performed in the reaction chamber to a predetermined degree of vacuum.
In the film formation treatment (3) 455 for forming the microcrystalline semiconductor film 67 including the impurity element which serves as a donor, deposition gas including silicon or germanium, which is silane in this example, hydrogen, and/or rare gas are introduced and mixed in the reaction chamber, and a microcrystalline semiconductor film is formed by glow discharge plasma which is generated by application of high-frequency power. Silane is diluted with hydrogen and/or rare gas to be 10 to 2000 times thinner. Therefore, a large amount of hydrogen and/or rare gas is needed. The substrate heating temperature is from 100 to 300° C., preferably from 120 to 220° C. At this time, the microcrystalline semiconductor film is deposited while taking in the impurity element which serves as a donor and is released into the inside of the reaction chamber, and thus, a microcrystalline semiconductor film including phosphorus is formed. Therefore, an amorphous semiconductor is not formed in an early stage of deposition of the semiconductor film, and crystals grow in a direction of the normal to the gate insulating film 59b, and a microcrystalline semiconductor film with high crystallinity in which column-like microcrystalline semiconductors are present can be formed. Further, a highly conductive microcrystalline semiconductor film including the impurity element which serves as a donor can be formed.
This mode has a feature that the gate insulating films 59a and 59b and the microcrystalline semiconductor film 67 each including the impurity element which serves as a donor are formed. It is preferable that a peak concentration of the impurity element which serves as a donor be from 6×1015 to 3×1018 atoms/cm3 inclusive, more preferably 3×1016 to 3×1017 atoms/cm3 inclusive.
In the substrate carrying-out 449, the substrate is carried out of the reaction chamber and carried into a load lock chamber connected to the reaction chamber. The pressure in the reaction chamber at this time is the same as that in the load lock chamber.
Next, as shown in
When a microcrystalline semiconductor film 53 which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS is formed instead of the microcrystalline semiconductor film 67 including the impurity element which serves as a donor as shown in
Next, another method for manufacturing the thin film transistor shown in
The precoating treatment 441, the substrate carrying-in 442, and the substrate carrying-out 449 are the same as in
In the flush treatment 447, gas including an impurity element which serves as a donor is introduced to a reaction chamber, and the impurity element which serves as a donor is adsorbed onto the substrate 50, the surface of the gate electrode 51, and furthermore, onto the inner wall of the reaction chamber. In this embodiment mode, 0.001% to 1% phosphine (diluted with hydrogen) is introduced to the reaction chamber. In addition to the gas including the impurity element which serves as a donor, hydrogen may be introduced as designated by a dashed line 462, or deposition gas including silicon or germanium may be introduced as designated by a dashed line 461, to the reaction chamber. By introducing the deposition gas including silicon or germanium to the reaction chamber, an impurity such as oxygen, nitrogen, or fluorine in the reaction chamber can be discharged from the reaction chamber, which can prevent a film to be formed from being contaminated.
In the film formation treatment (1) 456 for forming the gate insulating film 59a including the impurity element which serves as a donor, source gases, which are hydrogen, silane, and ammonia in this example, are introduced and mixed, and a silicon nitride film is formed by glow discharge plasma which is generated by application of high-frequency power. Nitrogen may be introduced to the reaction chamber in addition to the above source gases. At this time, the silicon nitride film is deposited while taking in the impurity element which serves as a donor and is adsorbed onto the substrate 50, the gate electrode 51, and furthermore, the surface of the inner wall of the reaction chamber, which is phosphorus in this example. Thus, a silicon nitride film including phosphorus can be formed. After the gate insulating film 59a including the impurity element which serves as a donor is formed, introduction of the above source gases is halted, and the power is turned off, and then, generation of plasma is halted.
In the vacuum evacuation treatment 444, vacuum evacuation is performed in the reaction chamber to a predetermined degree of vacuum.
In the film formation treatment (2) 457 for forming the gate insulating film 59b including the impurity element which serves as a donor, source gases, which are hydrogen, silane, and dinitrogen monoxide in this example, are introduced and mixed, and a silicon oxynitride film is formed by glow discharge plasma which is generated by application of high-frequency power. At this time, the silicon oxynitride film is deposited while taking in the impurity element which serves as a donor and is deposited over the surface of the gate insulating film 59a including the impurity element which serves as a donor, and the impurity element which serves as a donor and is adsorbed onto the surface of the inner wall of the reaction chamber, which is phosphorus in this example. Thus, a silicon oxynitride film including phosphorus can be formed as the gate insulating film 59b including the impurity element which serves as a donor. After the gate insulating film 59b including the impurity element which serves as a donor is formed, introduction of the above source gases is halted, and the power is turned off, and then, generation of plasma is halted.
In the vacuum evacuation treatment 446, vacuum evacuation is performed in the reaction chamber to a predetermined degree of vacuum.
In the film formation treatment (3) 455 for forming the microcrystalline semiconductor film 67 including the impurity element which serves as a donor, deposition gas including silicon or germanium, which is silane in this example, hydrogen, and/or rare gas are introduced and mixed in the reaction chamber, and a microcrystalline semiconductor film is formed by glow discharge plasma which is generated by application of high-frequency power. Silane is diluted with hydrogen and/or rare gas to be 10 to 2000 times thinner. Therefore, a large amount of hydrogen and/or rare gas is needed. The substrate heating temperature is from 100 to 300° C., preferably from 120 to 220° C. It is preferable that the film be formed at temperatures of from 120 to 220° C. so that a growing surface of the microcrystalline silicon film is inactivated with hydrogen to promote growth of microcrystalline silicon. At this time, the microcrystalline semiconductor film is deposited while taking in the impurity element which serves as a donor and is released into the inside of the reaction chamber, so that a microcrystalline semiconductor film including phosphorus is formed. Thus, an amorphous semiconductor is not formed in an early stage of deposition of the semiconductor film, and crystals grow in a direction of the normal to the gate insulating film 59b including the impurity element which serves as a donor, and a microcrystalline semiconductor film with high crystallinity in which column-like microcrystalline semiconductors are present can be formed. Further, since the microcrystalline semiconductor film includes the impurity element which serves as a donor and is deposited over the surface of the gate insulating film 59b including the impurity element which serves as a donor, a highly conductive microcrystalline semiconductor film including the impurity element which serves as a donor can be formed.
This mode has a feature that the gate insulating films 59a and 59b and the microcrystalline semiconductor film 67 each including the impurity element which serves as a donor are formed. It is preferable that a peak concentration of the impurity element which serves as a donor is from 6×1015 to 3×1018 atoms/cm3 inclusive, more preferably from 3×1016 to 3×1017 atoms/cm3 inclusive.
In the substrate carrying-out 449, the substrate is carried out of the reaction chamber and carried into a load lock chamber connected to the reaction chamber. The pressure in the reaction chamber at this time is the same as that in the load lock chamber.
Next, as shown in
When a microcrystalline semiconductor film 53 which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS is formed instead of the microcrystalline semiconductor film 67 including the impurity element which serves as a donor as shown in
Next, a method for manufacturing the thin film transistor shown in
As a typical example of a method for forming the gate insulating film 59c including the impurity element which serves as a donor, a process for forming a silicon nitride film including phosphorus is described in chronological order with reference to
The precoating treatment 441, the substrate carrying-in 442, the film formation treatment (1) 443 for forming the gate insulating film 52a, the vacuum evacuation treatment 444, the film formation treatment (2) 445 for forming the gate insulating film 52b, the vacuum evacuation treatment 446, and the substrate carrying-out 449 are the same as in
In the flush treatment 447, gas including an impurity element which serves as a donor is introduced to the reaction chamber, and the impurity element which serves as a donor is adsorbed onto the surface of the gate insulating film 52b, furthermore, onto the inner wall of the reaction chamber. In this embodiment mode, 0.001% to 1% phosphine (diluted with hydrogen) is introduced to the reaction chamber. In addition to the gas including the impurity element which serves as a donor, hydrogen may be introduced as designated by a dashed line 462, or deposition gas including silicon or germanium may be introduced as designated by a dashed line 461, to the reaction chamber.
In the film formation treatment (4) 458 for forming the gate insulating film 59c including the impurity element which serves as a donor, source gases of the gate insulating film, which are hydrogen, silane, and ammonia in this example, are introduced and mixed, and a silicon nitride film is formed by glow discharge plasma which is generated by application of high-frequency power. At this time, the silicon nitride film is deposited while taking in the impurity element which serves as a donor and is deposited over the surface of the gate insulating film 59b, and the impurity element which serves as a donor and is adsorbed onto the surface of the inner wall of the reaction chamber, which is phosphorus here. Thus, a silicon nitride film including phosphorus can be formed. After the gate insulating film 59c including the impurity element which serves as a donor is formed, introduction of the above source gases is halted, and the power is turned off, and then, generation of plasma is halted.
In the vacuum evacuation treatment 459, vacuum evacuation is performed in the reaction chamber to a predetermined degree of vacuum.
After that, the microcrystalline semiconductor film 53 is formed over the gate insulating film 59c including the impurity element which serves as donor.
In the film formation treatment (3) 451 for forming the microcrystalline semiconductor film 53, in order to form a microcrystalline semiconductor film which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS, the amount of gas including the impurity element which serves as a donor, which is phosphine in this example, to be introduced to the reaction chamber is controlled in the flush treatment 447, so that the microcrystalline semiconductor film 53, which is formed later, does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS. Alternatively, after the gate insulating film 59c including the impurity element which serves as a donor is formed, the substrate is carried out of the reaction chamber, and the inside of the reaction chamber is cleaned, and then, the substrate is carried into the reaction chamber again, and the microcrystalline semiconductor film 53 is formed, whereby the microcrystalline semiconductor film 53, which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS, can be formed. Further alternatively, after the gate insulating film 59c including the impurity element which serves as a donor is formed, the substrate is carried out of the reaction chamber, and the microcrystalline semiconductor film 53 is formed in a different reaction chamber, whereby the microcrystalline semiconductor film 53, which does not include the impurity element which serves as a donor at a higher concentration than the detection limit of SIMS, can be formed.
In a method for forming the gate insulating film 59c including the impurity element which serves as a donor, after the flush treatment 447, the gate insulating film 52b may be nitrided with high-density plasma, whereby a silicon nitride layer including the impurity element which serves as a donor can be formed on the surface of the gate insulating film 52b. The high-density plasma is generated by use of high-frequency microwaves, for example, microwaves with a frequency of 2.45 GHz. With high-density plasma, which has the characteristic of having a low electron temperature, a layer can be formed with less plasma damage and fewer defects compared to a layer formed by conventional plasma treatment because the kinetic energy of an active species is low. In addition, with use of high-density plasma, carrier mobility can be increased because the level of roughness on the surface of the gate insulating film 52b can be reduced.
Further, the gate insulating film 59c including the impurity element which serves as a donor can also be formed using gas including the impurity element which serves as a donor as designated by a dashed line 463 shown in
After that, by performing the same process as the process for manufacturing the thin film transistor in Embodiment Mode 1, the thin film transistor as shown in
In the process of this embodiment mode, glow discharge plasma is generated by applying high-frequency power with a frequency of from 1 to 20 MHz, typically 13.56 MHz; or high-frequency power with a frequency in the VHF band of 20 to 120 MHz approximately.
In the film formation treatment of the microcrystalline semiconductor film, helium may be added as rare gas to reaction gas, in addition to silane and hydrogen. Helium has an ionization energy of 24.5 eV, which is the highest among all the gases, and a metastable state thereof lies in a level of 20 eV approximately, which is a little lower than the above ionization energy; thus, to be ionized, helium requires as low as 4 eV, which is the difference between the ionization energy and the metastable energy, while keeping electric discharge. Therefore, helium starts to discharge electricity at the lowest voltage among all the gases. Because of the above property, helium can stably retain plasma. Further, uniform plasma can be formed with helium, and thus a plasma density can be uniform even when a microcrystalline silicon film is deposited over a large substrate.
In the thin film transistor manufactured in this embodiment mode, the gate insulating film and/or the microcrystalline semiconductor film includes the impurity element which serves as a donor. Thus, crystallinity of the microcrystalline semiconductor film at the interface with the gate insulating film is high and crystallinity of the microcrystalline semiconductor film can be improved. Accordingly, a thin film transistor including the microcrystalline semiconductor film has higher field effect mobility and higher on-current than a thin film transistor including an amorphous semiconductor film or a conventional microcrystalline semiconductor film. Thus, with the use of a thin film transistor in which a channel formation region is formed of the microcrystalline semiconductor film for switching a display element, the area of the channel formation region, that is, the area of the thin film transistor can be decreased. Accordingly, the area of the thin film transistor in each pixel is reduced, whereby the aperture ratio of the pixel can be increased. Accordingly, the display device can have high definition.
Since the channel formation region of the thin film transistor manufactured in this embodiment mode is formed using a microcrystalline semiconductor film, resistivity thereof is lower than that of a channel formation region formed using an amorphous semiconductor film. Therefore, a thin film transistor including the microcrystalline semiconductor film 53 has such current-voltage characteristics that a curve showing the current-voltage characteristics has a rising portion with a steep slope, and is excellent in response speed as a switching element; and thus can operate at high speed. With the use of the microcrystalline semiconductor film in a channel formation region of a thin film transistor, variation in a threshold voltage of a thin film transistor can be suppressed. Therefore, a display device with less variation of electric characteristics can be manufactured.
Further, in the thin film transistor manufactured in this embodiment mode, an amorphous semiconductor film with high resistivity is formed as the buffer layer between the microcrystalline semiconductor film which serves as a channel formation region and the semiconductor film to which the impurity element imparting one conductivity type is added and which functions as source and drain regions. Although off-current flows through the buffer layer, off-current can be suppressed because the buffer layer is a high-resistance region.
Next, as an example of a plasma CVD apparatus with which the above reaction chamber is provided, an example of a structure which is suitable for deposition of a gate insulating film and a microcrystalline semiconductor film is described.
Each reaction chamber is used for a different purpose, depending on the kind of a thin film to be formed. For example, an insulating film such as a gate insulating film is formed in the first reaction chamber 400a; a microcrystalline semiconductor film which forms a channel and a buffer layer are formed in the second reaction chamber 400b; and a semiconductor film to which an impurity element imparting one conductivity type is added and which forms a source and a drain is formed in the third reaction chamber 400c. It is needless to say that the number of the reaction chambers is not limited to three, and can be increased or decreased as needed. One film may be formed in one reaction chamber, or a plurality of films may be formed in one reaction chamber.
A turbo-molecular pump 419 and a dry pump 420 are connected to each reaction chamber as an exhaust unit. The exhaust unit is not limited to a combination of these vacuum pumps and can employ other vacuum pumps as long as they can evacuate the reaction chamber to a degree of vacuum of approximately 10−5 to 10−1 Pa. A butterfly valve 417 is provided between the exhaust unit 430 and each reaction chamber, which can interrupt vacuum evacuation, and a conductance valve 418 can control exhaust velocity to adjust the pressure in each reaction chamber.
The second reaction chamber 400b in which a microcrystalline semiconductor film is formed may be connected to a cryopump 421 which performs vacuum evacuation to an ultrahigh vacuum. By use of the cryopump 421, the reaction chamber can be evacuated to an ultrahigh vacuum of a pressure of lower than 10−5 Pa. In this embodiment mode, the inside of the reaction chamber is set to be an ultrahigh vacuum with a pressure of lower than 10−5 Pa, which is effective in reducing the oxygen concentration in the microcrystalline semiconductor film. Consequently, the oxygen concentration in the microcrystalline semiconductor film 53 can be set to be less than or equal to 1×1016 atoms/cm3. With the reduced oxygen concentration in the microcrystalline semiconductor film, defects in the film can be reduced, whereby crystallinity can be improved and thus carrier mobility can be improved.
A gas supply unit 408 includes a cylinder 410 filled with gas used for the process, such as rare gas or semiconductor source gas typified by silane, a stop valve 412, a mass flow controller 413, and the like. A gas supply unit 408g is connected to the first reaction chamber 400a and supplies gas for forming a gate insulating film. A gas supply unit 408i is connected to the second reaction chamber 400b and supplies gas for forming a microcrystalline semiconductor film and a buffer layer. A gas supply unit 408n is connected to the third reaction chamber 400c and supplies gas for forming an n-type semiconductor film, for example. In addition, phosphine, which is one of gases including an impurity element which serves as a donor, is supplied to the first reaction chamber 400a and the second reaction chamber 400b. A gas supply unit 408a supplies argon, and a gas supply unit 408f supplies etching gas used for cleaning the inside of the reaction chambers. Thus, the gas supply units 408a and 408f are provided in common for each reaction chamber.
A high-frequency power supply unit 403 for generating plasma is connected to each reaction chamber. The high-frequency power supply unit 403 includes a high-frequency power source 404 and a matching box 406.
A microcrystalline semiconductor film, a buffer layer, and a semiconductor film to which an impurity element imparting one conductivity type is added may be formed successively in one reaction chamber. Specifically, a substrate provided with a gate insulating film is carried into a reaction chamber, and a microcrystalline semiconductor film, a buffer layer, and a semiconductor film to which an impurity element imparting one conductivity type is added are formed therein successively. Then, after the substrate is carried out of the reaction chamber, the inside of the reaction chamber is cleaned with fluorine radicals. However, even when the inside of the reaction chamber is cleaned, an impurity element which serves as a donor remains in the reaction chamber in some cases. When a substrate provided with a gate insulating film is carried into such a reaction chamber and a microcrystalline semiconductor film is formed, the microcrystalline semiconductor film includes the impurity element which serves as a donor. Accordingly, a microcrystalline semiconductor film which has high crystallinity at the interface with a gate insulating film and includes an impurity element which serves as a donor can be formed.
Next, a method for manufacturing a thin film transistor which is different from that in the above mode is described with reference to
In a similar manner to
The resist 80 can be a positive type or a negative type. In this case, a positive resist is used.
Next, the resist 80 is irradiated with light using a multi-tone photomask 159 as a second photomask, to expose the resist 80 to light.
Next, light exposure using the multi-tone photomask 159 is described with reference to
A multi-tone photomask can achieve three levels of light exposure to obtain an exposed portion, a half-exposed portion, and an unexposed portion; one-time exposure and development process allows a resist mask with regions of plural thicknesses (typically, two kinds of thicknesses) to be formed. Thus, the use of a multi-tone photomask can reduce the number of photomasks.
Typical examples of a multi-tone photomask include a gray-tone mask 159a shown in
As shown in
For the light-transmitting substrate 163, a substrate having a light-transmitting property, such as a quartz substrate, can be used. The light-blocking portion 164 and the diffraction grating 165 can be formed using a light-blocking material such as chromium or chromium oxide, which absorbs light.
When the gray-tone mask 159a is irradiated with light for exposure, a light transmittance 166 of the light-blocking portion 164 is 0% and that of a region where neither the light-blocking portion 164 nor the diffraction grating 165 is provided is 100%, as shown in
As shown in
When the half-tone mask 159b is irradiated with light for exposure, a light transmittance 169 of the light blocking portion 168 is 0% and that of a region where neither the light-blocking portion 168 nor the semi-light-transmitting portion 167 is provided is 100%, as shown in
After the light exposure using the multi-tone photomask is performed, development is carried out, whereby a resist mask 81 having regions with different thicknesses can be formed, as shown in
Next, with the resist mask 81, the microcrystalline semiconductor film 57 including the impurity element which serves as a donor, the microcrystalline semiconductor film 53, the buffer layer 54, the semiconductor film 55 to which the impurity element imparting one conductivity type is added, and the conductive films 65a to 65c are etched to be separated. As a result, a microcrystalline semiconductor film 61 including the impurity element which serves as a donor, a microcrystalline semiconductor film 58, a buffer layer 62, a semiconductor film 63 to which the impurity element imparting one conductivity type is added, and conductive films 85a to 85c can be formed as shown in
Next, ashing is performed on the resist mask 81. As a result, the area and the thickness of the resist are reduced. At this time, the resist in a region with a small thickness (a region overlapping with part of the gate electrode 51) is removed to form a separated resist mask 86 as shown in
Next, the conductive films 85a to 85c are etched to be separated using the resist mask 86, whereby pairs of wirings 92a to 92c can be formed as shown in
Next, the semiconductor film 63 to which the impurity element imparting one conductivity type is added is etched using the resist mask 86, so that a pair of source and drain regions 88 are formed. Note that, in this etching step, a part of the buffer layer 62 is also etched to form a pair of buffer layers 87. The source and drain regions and the pair of buffer layer can be formed in the same process. In addition, the end portions of the wirings 92a to 92c are not aligned with those of the source and drain regions 88, and the end portions of the source and drain regions 88 are formed outside those of the wirings 92a to 92c. After that, the resist mask 86 is removed.
Next, dry etching is performed under such a condition that the exposed microcrystalline semiconductor film 61 is not damaged and an etching rate with respect to the microcrystalline semiconductor film 61 is low. Through this dry etching step, an etching residue on the microcrystalline semiconductor film 61 between the source region and the drain region, a residue of the resist mask, and a contamination source in an apparatus used for removal of the resist mask can be removed, whereby the source region and the drain region can be insulated surely. As a result, leakage current of the thin film transistor can be reduced, so that a thin film transistor with small off-current and high withstand voltage can be manufactured. A chlorine gas can be used for an etching gas, for example.
As shown in
Through the above process, a channel-etched thin film transistor 83 can be formed. In addition, the thin film transistor can be formed using two photomasks.
Next, as shown in
Next, a part of the protective insulating film 76a is etched using a resist mask formed using a third photomask, so that a contact hole is formed. Next, a pixel electrode 77 is formed in the contact hole, to be in contact with the wiring 92c. In this example, an ITO film is formed as the pixel electrode 77 by a sputtering method, and then, a resist is applied on the ITO film. Then, the resist is exposed to light and developed using a fourth photomask, thereby forming a resist mask. Then, the ITO film is etched using the resist mask to form the pixel electrode 77.
Through the above process, a thin film transistor and an element substrate which has the thin film transistor and can be used for a display device can be formed.
Next, a process in which a contact hole and a capacitor element can be formed with one photomask is described below. Cross-sectional views taken along lines C-D in
After the step shown in
Next, the protective insulating film 76a and the insulating film 102 having the recessed portions are entirely etched (etch back), and a part of the protective insulating film 76a is etched, whereby an insulating film 103 having a contact hole 112a that exposes the wiring 92c and a recessed portion 112b over the capacitor wiring 51c is formed as shown in
Next, ashing is performed on the insulating film 103 and the areas of the contact hole 112a and the recessed portion 112b are widened, so that a contact hole 113a and a recessed portion 113b are formed. Since the protective insulating film 76a is not formed of a photosensitive organic resin but formed of an inorganic insulating film, it is not processed by ashing. Therefore, the contact hole 113a, which has a top shape of double circles when seen from above, is formed over the wirings.
After that, a pixel electrode 77 is formed, and a capacitor element including the capacitor wiring 51c, the gate insulating films 52a and 52b, the protective insulating film 76a, and the pixel electrode 77 can be formed.
Through the above process, the contact hole connecting the pixel electrode and the wiring, and the capacitor element can be formed with the use of only one multi-tone photomask.
Further, in
Although this embodiment mode describes a channel-etched thin film transistor, a microcrystalline semiconductor film can also be used for a channel formation region of a channel protective thin film transistor.
In accordance with this embodiment mode, an inverted-staggered thin film transistor with high electric characteristics and an element substrate provided with the inverted-staggered thin film transistor can be manufactured.
This embodiment mode describes an inverted-staggered thin film transistor as a thin film transistor, but the present invention is not limited thereto. A method for forming an insulating film and a microcrystalline semiconductor film each including an impurity element which serves as a donor can be applied to a staggered thin film transistor, a top gate thin film transistor, and the like. Specifically, an insulating film functioning as a base film and/or a microcrystalline semiconductor film is made to include an impurity element which serves as a donor, and a gate insulating film and a gate electrode are formed over the microcrystalline semiconductor film, whereby a thin film transistor having a microcrystalline semiconductor film with high crystallinity at the interface with the insulating film can be manufactured. Accordingly, a thin film transistor with excellent electric characteristics can be formed.
Embodiment Mode 4In this embodiment mode, a liquid crystal display device including the thin film transistor described in Embodiment Mode 1 is described below as one mode of a display device. Here, a vertical alignment (VA) mode liquid crystal display device is described with reference to
In this pixel structure, a plurality of pixel electrodes 624 and 626 is included in one pixel, and thin film transistors 628 and 629 are connected to the pixel electrodes 624 and 626, respectively, through a planarization film 622. The thin film transistors 628 and 629 are driven by different gate signals. That is, a pixel of multi-domain design has a structure in which a signal applied to each of the pixel electrodes 624 and 626 is independently controlled.
The pixel electrode 624 is connected to the thin film transistor 628 through a wiring 618 in a contact hole 623. In a contact hole 627, the pixel electrode 626 is connected to the thin film transistor 629 through a wiring 619. A gate wiring 602 of the thin film transistor 628 and a gate wiring 603 of the thin film transistor 629 are separated so that different gate signals can be given thereto. In contrast, a wiring 616 functioning as a data line is used in common for the thin film transistors 628 and 629. The thin film transistors 628 and 629 can be manufactured by the methods described in Embodiment Mode 3.
The pixel electrodes 624 and 626 have different shapes and are separated by a slit 625. The pixel electrode 626 surrounds the pixel electrode 624, which has a V-shape. The thin film transistors 628 and 629 make the timing of applying voltages to the pixel electrodes 624 and 626 different from each other, thereby controlling alignment of liquid crystals. By supplying different gate signals to the gate wirings 602 and 603, operation timing of the TFTs 628 and 629 can be different. Further, an alignment film 648 is formed over the pixel electrodes 624 and 626.
A counter substrate 601 is provided with a light-blocking film 632, a coloring film 636, and a counter electrode 640. In addition, a planarizing film 637 is formed between the coloring film 636 and the counter electrode 640, thereby preventing alignment disorder of liquid crystals. Further, an alignment film 646 is formed on the counter electrode 640.
In this specification, a substrate, a coloring film, a light-blocking film, and a planarization film form a color filter. Either the light-blocking film or the planarization film, or neither of them is not necessarily formed over the substrate.
The coloring film has a function of preferentially transmitting light of a predetermined wavelength range among light of the wavelength range of visible light. In general, a coloring film which preferentially transmits light of a wavelength range of red light, a coloring film which preferentially transmits light of a wavelength range of blue light, and a coloring film which preferentially transmits light of a wavelength range of green light are combined to be used for a color filter. However, the combination of the coloring films is not limited to the above.
The pixel electrode 624, a liquid crystal layer 650, and the counter electrode 640 overlap with each other to form a first liquid crystal element. Further, the pixel electrode 626, the liquid crystal layer 650, and the counter electrode 640 overlap with each other to form a second liquid crystal element. Furthermore, the multi-domain structure is made in which the first liquid crystal element and the second liquid crystal element are provided for one pixel.
Although a vertical alignment (VA) mode liquid crystal display device is described here, the element substrate formed in accordance with Embodiment Mode 1 can also be applied to an FFS mode liquid crystal display device, an IPS mode liquid crystal display device, a TN mode liquid crystal display device, and the like.
The liquid crystal display device can be manufactured through the above process. Since an inverted-staggered thin film transistor with small off-current and high electric characteristics is used for the liquid crystal display device of this embodiment mode, the liquid crystal display device has high contrast and high visibility.
Embodiment Mode 5In this embodiment mode, a light-emitting display device including the thin film transistor described in Embodiment Mode 1 is described below as one mode of a display device; a structure of a pixel included in the light-emitting display device is described here.
Here, a display device including a light-emitting element utilizing electroluminescence is shown as a light-emitting device. Light-emitting elements utilizing electroluminescence are classified into two types according to whether a light-emitting material is an organic compound or an inorganic compound. In general, the former is referred to as an organic EL element, and the latter as an inorganic EL element. In this embodiment mode, the process for manufacturing the thin film transistor in accordance with Embodiment Mode 1 can be used.
In an organic EL element, voltage is applied to the light-emitting element, so that electrons are injected from an electrode into a layer including a light-emitting organic compound, and holes are injected from the other electrode into the layer including the light-emitting organic compound, and there flows electric current. These carriers (electrons and holes) are recombined, so that the light-emitting organic compound is placed in an excited state. The light-emitting organic compound emits light in returning to a ground state from the excited state. Because of such mechanism, such a light-emitting element is called a “light-emitting element of a current excitation type.”
Inorganic EL elements are classified into dispersive inorganic EL elements and thin film inorganic EL elements. A dispersive inorganic EL element includes a light-emitting layer in which particles of a light-emitting material are dispersed in a binder, and light emission mechanism thereof is donor-acceptor recombination light emission, in which a donor level and an acceptor level are utilized. In a thin film inorganic EL element, a light-emitting layer is sandwiched between dielectric layers, and the dielectric layers are sandwiched between electrodes. Light emission mechanism of the thin film inorganic EL element is local light emission, in which inner-shell electron transition of a metal ion is utilized. Here, an organic EL element is described as a light-emitting element. In addition, although the description is made using channel-etched thin film transistors as a switching thin film transistor that controls input of a signal to a first electrode and a driving thin film transistor which controls driving of a light-emitting element, a channel protective thin film transistor can also be used as appropriate.
In
A gate electrode of the first thin film transistor 74a is connected to a scanning line 51a. One of a source and a drain is connected to wirings 71a to 71c which functions as a signal line. The other of the source and the drain is electrically connected to a gate electrode 51b of the second thin film transistor 74b. One of a source and a drain of the second thin film transistor 74b is connected to power supply lines 93a to 93c, and the other of the source and the drain is electrically connected to a first electrode 79 of a display device. A gate electrode, a gate insulating film, and the power supply line 93a of the second thin film transistor 74b form a capacitor element 96, and the other of the source and the drain of the first thin film transistor 74a is electrically connected to the capacitor element 96.
The capacitor element 96 corresponds to a capacitor element for holding a voltage between the gate and the source or between the gate and the drain (hereinafter referred to as a gate voltage) of the second thin film transistor 74b when the first thin film transistor 74a is in an off-state, and is not necessarily provided.
In this embodiment mode, the first thin film transistor 74a and the second thin film transistor 74b can be each formed using the thin film transistor described in Embodiment Mode 1. In addition, although each of the first thin film transistor 74a and the second thin film transistor 74b is an n-channel thin film transistor in this example, the first thin film transistor 74a and the second thin film transistor 74b may also be formed using an n-channel thin film transistor and a p-channel thin film transistor, respectively. Furthermore, both the first thin film transistor 74a and the second thin film transistor 74b may be formed using p-channel thin film transistors.
A protective insulating film 76 is formed over the first thin film transistor 74a and the second thin film transistor 74b. A planarization film 78 is formed over the protective insulating film 76. The first electrode 79 is formed to be connected to a wiring 93f in a contact hole formed in the planarization film 78 and the protective insulating film 76. The planarization film 78 is preferably formed using an organic resin such as acrylic, polyimide, or polyamide, or a siloxane polymer. Since the first electrode 79 has a recessed portion in the contact hole, a partition wall 91 having an opening is provided to cover the recessed portion of the first electrode 79. In the opening of the partition wall 91, an EL layer 92 is formed so as to be in contact with the first electrode 79, and a second electrode 93 is formed so as to cover the EL layer 92. Further, a protective insulating film 95 is formed so as to cover the second electrode 93 and the partition wall 91.
A light-emitting element 94 having a top emission structure is shown as a light-emitting element. The light-emitting element 94 with a top emission structure can emit light even over the first thin film transistor 74a or the second thin film transistor 74b; thus, a light emission area can be increased. However, if the layers located under the EL layer 92 are uneven, the thickness is nonuniform due to unevenness, and the second electrode 93 and the first electrode 79 are short-circuited, so that a display defect is caused. Therefore, it is preferable to provide the planarization film 78.
The light-emitting element 94 corresponds to a region where the first electrode 79 and the second electrode 93 sandwich the EL layer 92. In the case of the pixel shown in
As the first electrode 79 functioning as a cathode, a known conductive film can be used as long as it has a low work function and reflects light. For example, Ca, Al, CaF, MgAg, AlLi, or the like is preferably used. The EL layer 92 may be formed using a single layer or by stacking a plurality of layers. When the EL layer 92 is formed using a plurality of layers, an electron-injection layer, an electron-transporting layer, a light-emitting layer, a hole-transporting layer, and a hole-injecting layer are stacked in this order over the first electrode 79. It is not necessary to form all of these layers. The second electrode 93 functioning as an anode is formed using a light-transmitting conductive material such as indium oxide including tungsten oxide, indium zinc oxide including tungsten oxide, indium oxide including titanium oxide, indium tin oxide including titanium oxide, indium tin oxide (ITO), indium zinc oxide, or indium tin oxide to which silicon oxide is added.
A light-emitting element having a top emission structure, in which light is emitted from a side opposite to a substrate, is described here; however, a light-emitting element having a bottom emission structure, in which light is emitted from the substrate side, or a light-emitting element having a dual emission structure, in which light is emitted from both the substrate side and the side opposite to the substrate, can also be employed as appropriate.
Although an organic EL element is described here as a light-emitting element, an inorganic EL element can also be provided as a light-emitting element.
This embodiment mode describes an example in which a thin film transistor for controlling the driving of a light-emitting element (the driving thin film transistor) is electrically connected to the light-emitting element; however, a thin film transistor for controlling current may be connected between the driving thin film transistor and the light-emitting element.
Through the above process, a light-emitting display device can be manufactured. The light-emitting display device of this embodiment mode can have high contrast and high visibility because an inverted-staggered thin film transistor with small off-current and excellent electric characteristics is used.
Embodiment Mode 6This embodiment mode describes a structure of a display panel which is one mode of a display device of the present invention.
Both the signal line driver circuit and the scanning line driver circuit may be formed over the same substrate as the pixel portion.
Further, when a driver circuit is formed separately, a substrate provided with the driver circuit is not necessarily attached to a substrate provided with a pixel portion, and may be attached to, for example, an FPC.
Furthermore, only a part of the signal line driver circuit or only a part of the scanning line driver circuit may be formed over the same substrate as the pixel portion with use of a thin film transistor in which a microcrystalline semiconductor film is used for a channel formation region, and the rest may be formed separately and electrically connected to the pixel portion.
As shown in
Note that there is no particular limitation on a connection method of the substrate formed separately, and a known method such as a COG method, a wire bonding method, or a TAB method can be used. Further, a connection position is not limited to the position illustrated in
The signal line driver circuit used in the present invention includes a shift register and an analog switch. In addition to the shift register and the analog switch, another circuit such as a buffer, a level shifter, or a source follower may be included. Moreover, the shift register and the analog switch are not necessarily provided. For example, a different circuit such as a decoder circuit by which a signal line can be selected may be used instead of the shift register, or a latch or the like may be used instead of the analog switch.
Embodiment Mode 7Display devices or the like that are obtained according to the present invention can be used for active matrix display panels. That is to say, the present invention can be carried out in all electronic devices in which these display panels are incorporated into display portions.
Examples of such electronic devices include cameras such as video cameras and digital cameras, displays that can be mounted on a person's head (goggle-type displays), car navigation systems, projectors, car stereos, personal computers, portable information terminals (e.g., mobile computers, mobile phones, and electronic books). Examples of these devices are illustrated in
As illustrated in
Further, in the television device, a sub-screen 2008 may be formed using a second display panel and may be used to display channel number, volume, and the like, in addition to the main screen 2003. In this structure, the main screen 2003 may be formed with a liquid crystal display panel, and the sub-screen 2008 may be formed with a light-emitting display panel. Furthermore, the main screen 2003 may be formed with a light-emitting display panel, and the sub-screen 2008 may be formed with a light-emitting display panel, and the sub-screen 2008 may be configured to be capable of flashing on and off.
As other external circuits, a video signal amplifier circuit 925 that amplifies a video signal among signals received by a tuner 924, a video signal process circuit 926 that converts the signals output from the video signal amplifier circuit 925 into color signals corresponding to their respective colors of red, green, and blue, a control circuit 927 that converts the video signal so that the video signal can match input specification of the driver IC, and the like are provided on an input side of the video signal. The control circuit 927 outputs signals to both a scanning line side and a signal line side. In a case of digital driving, a signal divide circuit 928 may be provided on the signal line side and an input digital signal may be divided into m pieces and supplied.
Among signals received by the tuner 924, an audio signal is sent to an audio signal amplifier circuit 929 and is supplied to a speaker 933 through an audio signal process circuit 930. A control circuit 931 receives control information of a receiving station (reception frequency) or sound volume from an input portion 932 and transmits signals to the tuner 924 and the audio signal process circuit 930.
Needless to say, the present invention is not limited to a use for television devices, and can be applied to a variety of applications such as monitors of personal computers, or display media that have a large area, such as information display boards in railway stations, airports, and the like, or street-side advertisement display boards.
The display device described in any of the preceding embodiment modes is applied to the main screen 2003 and the sub-screen 2008, so that mass productivity of the television device can be improved.
A portable computer illustrated in
A gate insulating film was formed over a glass substrate; flushing treatment was performed using phosphine, which is a gas including an impurity element which serves as a donor; then, a microcrystalline silicon film was formed.
As the gate insulating film, a silicon oxynitride film with a thickness of 100 nm was formed over a glass substrate with a thickness of 0.7 mm by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 50 W; the film formation temperature was 280° C.; the flow rates of silane gas and dinitrogen monoxide were 30 sccm and 1200 sccm, respectively; and the pressure was 40 Pa.
Subsequently, gas including phosphine was introduced to a reaction chamber to perform flushing treatment. The conditions at this time were as follows:
(Condition 1)
flow rate of 0.1% PH3 (diluted with Ar): 500 sccm
(Condition 2)
flow rate of SiH4: 100 sccm; flow rate of 0.5% PH3 (diluted with H2): 170 sccm
(Condition 3)
flow rate of SiH4: 100 sccm; flow rate of H2: 153 sccm; flow rate of 0.5% PH3/H2: 17 sccm
Next, a microcrystalline silicon film with a thickness of 50 nm was formed over the gate insulating film by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 50 W; the film formation temperature was 280° C.; the flow rates of silane gas and hydrogen were 10 sccm and 1500 sccm, respectively; and the pressure was 280 Pa.
The substrate was carried out of the reaction chamber and the inside of the reaction chamber was cleaned with fluorine radicals. Then, the substrate was carried in the reaction chamber again.
Next, an amorphous silicon film was formed as a buffer layer over the microcrystalline silicon film. The amorphous silicon film was formed with a thickness of 100 nm over the microcrystalline silicon film by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 60 W; the film formation temperature was 280° C.; the flow rates of silane gas and hydrogen were 280 sccm and 300 sccm, respectively; and the pressure was 170 Pa. At this time, on each of the substrates which had undergone the flushing treatment under the conditions 1 to 3, secondary ion mass spectroscopy (SIMS) was performed in a direction of the depth from a surface of the substrate.
In
Concentrations of phosphorus in the microcrystalline silicon films in
- Sample under Condition 1: 5×1016 to 2×1018 atoms/cm3
- Sample under Condition 2: 6×1016 to 3×1018 atoms/cm3
- Sample under Condition 3: 3×1016 to 2×1017 atoms/cm3
As is seen from the above, by forming a microcrystalline silicon film after phosphine flushing treatment, the microcrystalline silicon film including phosphorus can be formed.
Embodiment 2A gate insulating film including phosphorus, which is an impurity element which serves as a donor, was formed over a glass substrate, and then a microcrystalline silicon film was formed.
As the first gate insulating film, a silicon oxynitride film including phosphorus with a thickness of 10 nm was formed over a glass substrate with a thickness of 0.7 mm by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 50 W; the film formation temperature was 280° C.; and the pressure was 40 Pa. The conditions of the flow rates of source gases were as follows:
(Condition 4)
flow rate of SiH4: 30 sccm; flow rate of N2O: 1200 sccm; flow rate of 0.5% PH3 (diluted with H2): 60 sccm
(Condition 5)
flow rate of SiH4: 30 sccm; flow rate of N2O: 1200 sccm; flow rate of 0.5% PH3 (diluted with H2): 6 sccm
Subsequently, the second gate insulating film was formed over the first gate insulating film. As the second gate insulating film, a silicon oxynitride film with a thickness of 100 nm was formed over the glass substrate by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 50 W; the film formation temperature was 280° C.; the flow rates of silane gas and dinitrogen monoxide were 30 sccm and 1200 sccm, respectively; and the pressure was 40 Pa.
Next, as a microcrystalline silicon film, a microcrystalline silicon film with a thickness of 50 nm was formed over the gate insulating film by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 50 W; the film formation temperature was 280° C.; the flow rates of silane gas and hydrogen were 10 sccm and 1500 sccm, respectively; and the pressure was 280 Pa.
The substrate was carried out of the reaction chamber and the inside of the reaction chamber was cleaned with fluorine radicals. Then, the substrate was carried in the reaction chamber again.
Next, an amorphous silicon film was formed as a buffer layer over the microcrystalline silicon film. The amorphous silicon film was formed with a thickness of 100 nm over the microcrystalline silicon film by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 60 W; the film formation temperature was 280° C.; the flow rates of silane gas and hydrogen were 280 sccm and 300 sccm, respectively; and the pressure was 170 Pa. At this time, on each of the substrates over which the first gate insulating film had been formed under the conditions 4 and 5, secondary ion mass spectroscopy (SIMS) was performed in a direction of the depth from a surface of the substrate.
In
Concentrations of phosphorus in the microcrystalline silicon films in
- Sample under Condition 4: 3×1016 to 7×1017 atoms/cm3
- Sample under Condition 5: 3×1016 to 2×1017 atoms/cm3
Although the concentration of phosphorus in the silicon oxynitride film cannot be measured accurately in
As is seen from the above, by forming a microcrystalline silicon film after forming a gate insulating film including phosphorus, the microcrystalline silicon film and the gate insulating film can include phosphorus. In other words, the gate insulating film and the microcrystalline silicon film that include phosphorus can be formed.
Embodiment 3After precoating the inside of a reaction chamber of a plasma CVD apparatus with a protective film, a glass substrate was carried in the reaction chamber, and a first gate insulating film, a second gate insulating film, a microcrystalline silicon film, and an amorphous silicon film for functioning as a buffer layer were formed.
The inside of the reaction chamber was precoated with the protective film. The condition at this time was as follows:
(Condition 6)
An amorphous silicon film including phosphorus with a thickness of 50 nm was formed as the protective film on an inner wall of a reaction chamber under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 370 W; and the pressure was 170 Pa. Further, the conditions of the flow rates of source gases were as follows:
(Condition 6)
flow rate of SiH4: 100 sccm; flow rate of 0.5% PH3 (diluted with H2): 170 sccm
(Condition 7)
A silicon nitride film, a silicon oxynitride film, and an amorphous silicon film were stacked as the protective film. At this time, the silicon nitride film was formed with a thickness of 110 nm on an inner wall of a reaction chamber under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 370 W; the flow rates of silane, hydrogen, nitrogen, and ammonia were 10 sccm, 500 sccm, 550 sccm, and 140 sccm, respectively; and the pressure was 100 Pa. Further, the silicon oxynitride film was formed with a thickness of 110 nm over the silicon nitride film by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 50 W; the film formation temperature was 280° C.; the flow rates of silane gas and dinitrogen monoxide were 30 sccm and 1200 sccm, respectively; and the pressure was 40 Pa. Furthermore, the amorphous silicon film was formed with a thickness of 200 nm over the silicon oxynitride film by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 120 W; the film formation temperature was 280° C.; the flow rate of silane gas was 300 sccm; and the pressure was 170 Pa.
Subsequently, a substrate (a glass substrate with a thickness of 0.7 mm) was carried in the reaction chamber, and then as the first gate insulating film, a silicon nitride film with a thickness of 100 nm was formed over the glass substrate by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 370 W; the film formation temperature was 280° C.; the flow rates of silane, hydrogen, nitrogen, and ammonia were 10 sccm, 500 sccm, 550 sccm, and 140 sccm, respectively; and the pressure was 100 Pa.
Then, the second gate insulating film was formed over the first gate insulating film. As the second gate insulating film, a silicon oxynitride film with a thickness of 100 nm was formed over the first gate insulating film by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 50 W; the film formation temperature was 280° C.; the flow rates of silane gas and dinitrogen monoxide were 30 sccm and 1200 sccm, respectively; and the pressure was 40 Pa.
Next, a microcrystalline silicon film with a thickness of 50 nm was formed over the gate insulating film by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 50 W; the film formation temperature was 280° C.; the flow rates of silane gas and hydrogen were 10 sccm and 1500 sccm, respectively; and the pressure was 280 Pa.
The substrate was carried out of the reaction chamber and the inside of the reaction chamber was cleaned with fluorine radicals. Then, the substrate was carried in the reaction chamber again.
Next, an amorphous silicon film was formed as a buffer layer over the microcrystalline silicon film. The amorphous silicon film was formed with a thickness of 100 nm over the microcrystalline silicon film by a plasma CVD method under the following condition: the RF power source frequency was 13.56 MHz; the power of the RF power source was 60 W; the film formation temperature was 280° C.; the flow rates of silane gas and hydrogen were 280 sccm and 300 sccm, respectively; and the pressure was 170 Pa. At this time, on each of the substrates over which the films were formed in the reaction chamber which had undergone precoating under the conditions 6 and 7, secondary ion mass spectroscopy (SIMS) was performed in a direction of the depth from a surface of the substrate.
In
Concentrations of phosphorus in the microcrystalline silicon films in
- Sample under Condition 6: 5×1016 to 1×1017 atoms/cm3
- Sample under Condition 7: 3×1016 to 5×1016 atoms/cm3
As is seen from the above, by forming a gate insulating film and a microcrystalline silicon film after precoating an inside of a reaction chamber of a plasma CVD apparatus with an amorphous silicon film including phosphorus as a protective film, the microcrystalline silicon film can include phosphorus.
Embodiment 4In this embodiment, the lifetime of carriers which are included in a microcrystalline silicon film formed over an insulating film was measured. An influence of the insulating film on the microcrystalline silicon film is described below.
The silicon nitride film 122 was formed under a similar condition to that of the silicon nitride film which was formed as the first gate insulating film in Embodiment 3. Further, the silicon oxynitride film 123 was formed under a similar condition to that of the silicon oxynitride film which was formed as the second gate insulating film in Embodiment 3. Furthermore, the microcrystalline silicon film 124 was formed under a similar condition to that of the microcrystalline silicon film in Embodiment 3. Still furthermore, the silicon nitride films 125 to 127 were formed under a similar condition to that of the silicon nitride film 122.
In Samples 1 to 5, the lifetime of carriers included in the microcrystalline silicon film was measured by a microwave photoconductivity decay method (a μ-PCD method). In the μ-PCD method, the microcrystalline silicon film was irradiated with pulsed laser beams to measure the lifetime of carriers from when an excessive amount of carriers are generated in the microcrystalline silicon film and until when the carriers are recombined and disappear. Generation of the carriers increases the conductivity of the microcrystalline silicon film, and thus the reflectance of microwaves with which the microcrystalline silicon film is irradiated changes in accordance with the excessive carrier density. The time of decrease in the reflectance of the microwaves is measured, whereby the lifetime of carriers can be measured.
In this embodiment, with the use of a crystallinity evaluation equipment for a thin polysilicon film in which microwaves are used (produced by KOBELCO RESEARCH INSTITUTE, INC.), Samples 1 to 5 were irradiated with microwaves with a frequency of 13.56 MHz and with third harmonics of a YLG laser with a wavelength of 349 nm, and the phase contrast of the microwaves, which changes according to generation of carriers, was measured with a voltmeter for measuring a phase contrast of microwaves.
This embodiment presents calculation results of a donor concentration of a microcrystalline semiconductor film including an impurity element which functions as the donor in a thin film transistor, and of electric characteristics of the thin film transistor.
Here, a microcrystalline semiconductor film to which an impurity element is not added is referred to as μc-Si (i); a microcrystalline semiconductor film to which an impurity element (e.g., phosphorus) which serves as a donor is added is referred to as μc-Si (n−); a buffer layer to which an impurity element is not added is referred to as a-Si (i); an amorphous semiconductor film to which an impurity element (e.g., phosphorus) imparting one conductivity type is added is referred to as a-Si (n−); and an amorphous semiconductor film to which a large amount of impurity element (e.g., phosphorus) imparting one conductivity type is added so that the amorphous semiconductor film can have conductivity is referred to as a-Si (n+).
When an impurity element is added to a microcrystalline semiconductor film or an amorphous semiconductor film, the impurity concentration is defined as the number of atoms of the added impurity element per unit volume. Further, if the added impurity element is a fifth group element or a third group element, the impurity concentration is multiplied by the activation rate, which is defined as the donor concentration or the acceptor concentration. The activation rate of a microcrystalline semiconductor film is from 40 to 60%, typically 50%; the activation rate of an amorphous semiconductor film is from 1 to 5%, typically 3%. Therefore, the peak concentration of the impurity element which serves as a donor is two times as high as the donor concentration which was calculated in this embodiment.
A device model which was used for the simulation is described below.
A device simulator “ATLAS” developed by Silvaco Data Systems Inc. was used for the device simulation. Table 1 shows model parameter of a-Si and μc-Si, which were used for the device simulation. In the device simulation, modeling of a-Si and μc-Si was achieved mainly by defining the state density. Specifically, the model parameter of a-Si was determined by defining such parameter as shown in Table 1 as appropriate, and the DC characteristics of an inverted-staggered a-Si TFT was calculated with the use of a device simulator. Further, the model parameter of μc-Si was defined so that the maximum filed effect mobility which was determined by the DC characteristics of the inverted-staggered μc-Si TFT which was calculated with a device simulator may be approximately 10 times as high as the maximum filed effect mobility which was determined by the DC characteristics of the inverted-staggered a-Si TFT which was calculated with a device simulator.
Next,
An insulating substrate is used, which is assumed to be a glass substrate (with a thickness of 0.5 μm) including silicon oxide (with a dielectric constant of 4.1) as its main component. Although an insulating substrate with a thickness of 0.5 mm, 0.7 mm, or the like is often used in an actual manufacturing process, the thickness of the insulating substrate is defined so as to be sufficiently large so that an electric field at a lower surface of the insulating substrate does not have influence on the TFT characteristics, in consideration of calculation efficiency.
A gate electrode with a stacked-layer structure of aluminum (Al) and molybdenum (Mo) (with a total thickness of 150 nm) is formed over the insulating substrate. The work function of molybdenum (Mo) is assumed to be 4.6 eV. In the device structure shown in
A gate insulating film with a stacked-layer structure of a silicon nitride film (with a dielectric constant of 7.0 and a thickness of 110 nm) and a silicon oxynitride film (with a dielectric constant of 4.1 and a thickness of 110 nm) is formed over the gate electrode.
A μc-Si (n−) (with a thickness varied to be 10 nm, 20 nm, and 50 nm; and a donor concentration varied to be 1×1015 to 5×1017 atoms/cm3) and a μc-Si (i) (with a thickness varied to be 90 nm, 80 nm, and 50 nm) are stacked over the gate insulating film. Over the μc-Si (i), further, a first a-Si (i) (with a thickness of 50 nm) is formed on the left and a second a-Si (i) (with a thickness of 50 nm) is formed on the right.
A first a-Si (n+) (with a thickness of 50 nm) and a second a-Si (n+) (with a thickness of 50 nm) are formed over the first a-Si (i) and the second a-Si (i), respectively. In
A source electrode and a drain electrode that have a stacked-layer structure (with a thickness of 300 nm) of molybdenum (Mo), and aluminum (Al) are formed over the first a-Si (n+) and the second a-Si (n+), respectively. It is assumed that ohmic contact is formed between the molybdenum and each of the first a-Si (n+) and the second a-Si (n+). In the device structure shown in
Results of the device simulation are presented below.
Vg-Id characteristics are presented below based on the result of the device simulation.
A shift in the threshold voltage which is caused by adding an impurity element to a semiconductor layer corresponds to a minus shift in the Id curve in the direction of the Vg axis which is caused by increasing the donor concentration in the Vg-Id characteristics.
On-current is presented below based on the result of the device simulation.
As is apparent from
When the donor concentration is 1×1015 atoms/cm3, it can be considered that the microcrystalline semiconductor film substantially does not include a donor, i.e., an impurity element which serves as a donor.
Threshold voltages are presented below based on the result of the device simulation.
An increase in the donor concentration shifts the threshold voltage toward the minus side.
Subthreshold swings are presented below based on the result of the device simulation.
Adding the impurity element to the semiconductor layer increases the subthreshold swing due to the impurity diffusion.
Maximum filed effect mobility is presented below based on the result of the device simulation.
To examine the maximum filed effect mobility, it is necessary to consider the field effect mobility in more detail. Thus, such a device structure as shown in
In
The drain current flows through the drain electrode 216, the drain region 212, the second semiconductor layer 208, a region in the first semiconductor layer 206 which is near to an interface with the gate insulating film 204, the second semiconductor layer 208, the source region 210, and the source electrode 214.
In an actual device structure, typically, the resistance Rd is formed in the second semiconductor layer 208 with a thickness of approximately 200 nm. Typically, further, the resistance Rc(on) is formed in the first semiconductor layer 206 with a length of approximately 6 μm. Therefore, when the resistance value per unit length of the portion of the second semiconductor layer 208 which is depleted is approximately 30 times or more as high as that of the portion of the first semiconductor layer 206 which is inverted, it is probable that the resistance Rd will have the greatest influence on the drain current. Furthermore, when the resistance value per unit length of the portion of the second semiconductor layer 208 which is depleted is approximately 30 times or less as high as that of the portion of the first semiconductor layer 206 which is inverted, it is probable that the resistance Rc(on) will have the greatest influence on the drain current.
It is probable that the resistance Rc(on) decreases from a value which is much higher than the resistance Rd to a value which is as high as or almost as high as the resistance Rd, and further to a value which is much lower than the resistance Rd as the gate voltage increases. Further, it is probable that the drain current increases suddenly as the resistance Rc(on) decreases from a value much higher than the resistance Rd to a value which is as high as or almost as high as the resistance Rd. On the other hand, when the resistance Rc(on) comes to have a value which is much lower than the resistance Rd, a decrease in the resistance Rc(on) has less influence on the drain current. Further, it is probable that the resistance Rd decreases as the drain voltage increases.
The field effect mobility can be considered as the rate of increase in the drain current Id with respect to an increase in the gate voltage Vg. That is to say, when the drain voltage is low (the resistance Rd is high), the field effect mobility has a maximum value as the gate voltage increases. Further, when the drain voltage is high (the resistance Rd is low), the field effect mobility increases monotonously as the gate voltage increases.
In addition to the above examination, in consideration of the minus shift of Id curve in the direction of the Vg axis which is caused by increasing the donor concentration, description is made on
In
On the other hand, when the drain voltage is low (Vd=1 V), there arise some patterns of tendency, as shown in
When the semiconductor layer to which the impurity element is added has a large thickness, for example, in the result of μc-Si (n−) with a thickness of 50 nm in
When the donor concentration is 1×1015 atoms/cm3, the microcrystalline semiconductor film can be regarded as not including a donor substantially, i.e., not including the impurity element which serves as a donor substantially.
Since the thin film transistor of the present invention can operate at high speed, the frame frequency can be increased in operating a liquid crystal display device. Here, characteristics of a thin film transistor which can be manufactured in a pixel portion of a liquid crystal display device in which display characteristics of moving images are improved and which is capable of smooth display by quadrupling the frame frequency (e.g., 480 Hz or 400 Hz) and interpolating image data, and the concentration of the impurity element which serves as a donor which is included in a channel formation region and contributes to achieving the characteristics were calculated.
The specification of the liquid crystal display device which is used in this simulation is as follows:
- HDTV: (number of pixels: 1920×1080) 1125 p, 11.7 inches (278.4 mm×156.6 mm)
- VA mode
- pixel capacity: 88 fF
- gate signal line (sheet resistance: 0.3 Ω/square; line width: 7 μm) resistance: 11.9 kΩ; capacity: 495 pF
- video signal line (sheet resistance: 0.14 Ω/square; line width 5 μm) resistance: 4.4 kΩ; capacity: 126 pF
- pixel TFT: L/W=6 μm/15 μm
- driving voltage of the gate signal line: 24 V
- video signal: 4.5 to 17.5 V
In the circuit shown in
Characteristics of a pixel TFT which are required for quadruple frame rate display are as follows:
- on-current: higher than or equal to 4.11×10−6 A (Vd=1 V, Vg=20 V); higher than or equal to 5.54×10−4 A (Vd=14 V, Vg=20 V)
- threshold voltage: lower than or equal to 0.5 V (Vd=1 V); lower than or equal to 1.94 V (Vd=14 V)
- subthreshold swing: less than or equal to 0.836 V/dec. (Vd=1 V); less than or equal to 0.845 V/dec. (Vd=14 V)
- field effect mobility: greater than or equal to 5.46 cm2/Vs (Vd=1 V); greater than or equal to 69.4 cm2/Vs (Vd=14 V)
The thin film transistor in which the microcrystalline silicon film is used for the channel formation region has less variation in the threshold voltage than a thin film transistor in which amorphous silicon is used for a channel formation region, and thus the threshold voltage was set to be higher than or equal to −3 V.
In
Therefore, when a thin film transistor in which a microcrystalline silicon film with a donor concentration of from 8×1015 to 5×1017 atoms/cm3 is used for a channel formation region is formed in a pixel portion and is used as a switching element of a liquid crystal element, a liquid crystal display device capable of quadruple frame rate display can be manufactured.
This application is based on Japanese Patent Application serial No. 2007-262739 filed with Japan Patent Office on Oct. 5, 2007 and Japanese Patent Application serial No. 2007-267085 filed with Japan Patent Office on Oct. 12, 2007 the entire contents of which are hereby incorporated by reference.
Claims
1. A thin film transistor comprising:
- a gate insulating film including an impurity element which serves as a donor, which is formed over a gate electrode;
- a microcrystalline semiconductor film which is formed over the gate insulating film including the impurity element which serves as a donor;
- a pair of buffer layers which are formed over the microcrystalline semiconductor film;
- a pair of semiconductor films to which an impurity element imparting one conductivity type is added and which is formed over the pair of buffer layers; and
- wirings which are formed over the pair of semiconductor films to which the impurity element imparting one conductivity type is added.
2. A thin film transistor comprising:
- a gate insulating film which is formed over a gate electrode;
- a microcrystalline semiconductor film including an impurity element which serves as a donor, which is formed over the gate insulating film;
- a pair of buffer layers which are formed over the microcrystalline semiconductor film including the impurity element which serves as a donor;
- a pair of semiconductor films to which an impurity element imparting one conductivity type is added and which are formed over the pair of buffer layers; and
- wirings which are formed over the pair of semiconductor films to which the impurity element imparting one conductivity type is added.
3. A thin film transistor comprising:
- a gate insulating film which is formed over a gate electrode;
- a first microcrystalline semiconductor film including an impurity element which serves as a donor, which is formed over the gate insulating film;
- a second microcrystalline semiconductor film which is formed over the first microcrystalline semiconductor film including the impurity element which serves as a donor;
- a pair of buffer layers which are formed over the second microcrystalline semiconductor film;
- a pair of semiconductor films to which an impurity element imparting one conductivity type is added and which are formed over the pair of buffer layers; and
- wirings which are formed over the pair of semiconductor films to which the impurity element imparting one conductivity type is added.
4. The thin film transistor according to claim 3, wherein the second microcrystalline semiconductor film does not include the impurity element which serves as a donor at a higher concentration than a detection limit of secondary ion mass spectrometry (SIMS).
5. A thin film transistor comprising:
- a gate insulating film including an impurity element which serves as a donor, which is formed over a gate electrode;
- a microcrystalline semiconductor film including the impurity element which serves as a donor, which is formed over the gate insulating film including the impurity element which serves as a donor;
- a pair of buffer layers which are formed over the microcrystalline semiconductor film including the impurity element which serves as a donor;
- a pair of semiconductor films to which an impurity element imparting one conductivity type is added and which are formed over the pair of buffer layers; and
- wirings which are formed over the pair of semiconductor films to which the impurity element imparting one conductivity type is added.
6. The thin film transistor according to claim 1, wherein a peak concentration of the impurity element which serves as a donor and which is included in the gate insulating film including the impurity element which serves as a donor, the microcrystalline semiconductor film including the impurity element which serves as a donor, or the first microcrystalline semiconductor film including the impurity element which serves as a donor, which is determined by secondary ion mass spectrometry (SIMS), is greater than or equal to 6×1015 atoms/cm3 and less than or equal to 3×1018 atoms/cm3.
7. The thin film transistor according to claim 2, wherein a peak concentration of the impurity element which serves as a donor and which is included in the gate insulating film including the impurity element which serves as a donor, the microcrystalline semiconductor film including the impurity element which serves as a donor, or the first microcrystalline semiconductor film including the impurity element which serves as a donor, which is determined by secondary ion mass spectrometry (SIMS), is greater than or equal to 6×1015 atoms/cm3 and less than or equal to 3×1018 atoms/cm3.
8. The thin film transistor according to claim 3, wherein a peak concentration of the impurity element which serves as a donor and which is included in the gate insulating film including the impurity element which serves as a donor, the microcrystalline semiconductor film including the impurity element which serves as a donor, or the first microcrystalline semiconductor film including the impurity element which serves as a donor, which is determined by secondary ion mass spectrometry (SIMS), is greater than or equal to 6×1015 atoms/cm3 and less than or equal to 3×1018 atoms/cm3.
9. The thin film transistor according to claim 5, wherein a peak concentration of the impurity element which serves as a donor and which is included in the gate insulating film including the impurity element which serves as a donor, the microcrystalline semiconductor film including the impurity element which serves as a donor, or the first microcrystalline semiconductor film including the impurity element which serves as a donor, which is determined by secondary ion mass spectrometry (SIMS), is greater than or equal to 6×1015 atoms/cm3 and less than or equal to 3×1018 atoms/cm3.
10. The thin film transistor according to claim 1, wherein the impurity element which serves as a donor is phosphorus, arsenic, or antimony.
11. The thin film transistor according to claim 2, wherein the impurity element which serves as a donor is phosphorus, arsenic, or antimony.
12. The thin film transistor according to claim 3, wherein the impurity element which serves as a donor is phosphorus, arsenic, or antimony.
13. The thin film transistor according to claim 5, wherein the impurity element which serves as a donor is phosphorus, arsenic, or antimony.
14. A display device comprising a pixel electrode which is in contact with one of the wirings of the thin film transistor according to claim 1.
15. A display device comprising a pixel electrode which is in contact with one of the wirings of the thin film transistor according to claim 2.
16. A display device comprising a pixel electrode which is in contact with one of the wirings of the thin film transistor according to claim 3.
17. A display device comprising a pixel electrode which is in contact with one of the wirings of the thin film transistor according to claim 5.
Type: Application
Filed: Sep 26, 2008
Publication Date: Apr 9, 2009
Applicant: SEMICONDUCTOR ENERGY LABORATORY CO., LTD. (Atsugi-shi)
Inventors: Shunpei YAMAZAKI (Setagaya), Yoshiyuki KUROKAWA (Sagamihara), Yasuhiro JINBO (Atsugi), Satoshi KOBAYASHI (Atsugi), Daisuke KAWAE (Atsugi)
Application Number: 12/238,517
International Classification: H01L 29/49 (20060101);