GRAPHENE ELECTRODE, ENERGY STORAGE DEVICE EMPLOYING THE SAME, AND METHOD FOR FABRICATING THE SAME
The disclosure provides a graphene electrode, an energy storage device employing the same, and a method for fabricating the same. The graphene electrode includes a metal foil, a non-doped graphene layer, and a hetero-atom doped graphene layer. Particularly, the hetero-atom doped graphene layer is separated from the metal foil by the non-doped graphene layer.
Latest INDUSTRIAL TECHNOLOGY RESEARCH INSTITUTE Patents:
- METHOD FOR TREE-BASED MACHINE LEARNING MODEL REDUCTION AND ELECTRONIC DEVICE USING THE SAME
- ALUMINUM ALLOY MATERIAL AND ALUMINUM ALLOY OBJECT AND METHOD FOR MANUFACTURING THE SAME
- ABNORMAL DETECTION CIRCUIT FOR DETECTING THREE-PHASE AC POWER
- IONIC COMPOUND, ABSORBENT AND ABSORPTION DEVICE
- READING DEVICE FOR CAPACITIVE SENSING ELEMENT
The present application is based on, and claims priority from, Taiwan (International) Application Serial Number 101143373, filed Nov. 21, 2012, the disclosure of which is hereby incorporated by reference herein in its entirety.
TECHNICAL FIELDThe disclosure relates to a graphene electrode and, more particularly, to a graphene electrode used in an energy storage device.
BACKGROUNDDue to rising concerns for environmental issues and higher gasoline prices, research and development of electric vehicles have received increased attention.
Conventional lithium ion batteries, however, cannot meet the requirements of high capacity, high power, and fast charging. In order to improve the properties of conventional lithium ion batteries, novel anode materials for replacing graphite material are desired.
Due to the superior electronic conductivity and the porous structure, electrons and lithium ion have high transport/diffusion mobility within a graphene layer. Further, due to the irregular structure of the graphene, the graphene has a higher capacity in comparison with the graphite. Due to the high irreversible capacity and low conductivity, the commercialization of lithium ion batteries employing the graphene electrode, however, cannot be achieved.
SUMMARYOne embodiment of the disclosure provides a graphene electrode and a method for fabricating the same. Since the hetero-atom is doped into the surface of a graphene at a low temperature by a dry-process surface modification treatment, the obtained graphene electrode can have high capacity and low irreversible capacity. On the other hand, the graphene electrode of the disclosure is suitable for being used in energy storage devices.
The graphene electrode of the disclosure includes: a metal foil, a non-doped graphene layer, and a hetero-atom doped graphene layer, wherein the hetero-atom doped graphene layer is separated from the metal foil by the non-doped graphene layer.
The disclosure also provides a method for fabricating the aforementioned graphene electrode. The method includes: providing the metal foil; forming the graphene layer on the metal foil; and subjecting the graphene layer to a dry-process surface modification treatment, thereby doping the hetero-atoms into the graphene layer surface.
According to an embodiment of the disclosure, the disclosure further provides an energy storage device, wherein the energy storage device includes the aforementioned graphene electrode serving as a first electrode, a second electrode, and an isolation membrane disposed between the first electrode and the second electrode.
A detailed description is given in the following embodiments with reference to the accompanying drawings.
The disclosure can be more fully understood by reading the subsequent detailed description and examples with references made to the accompanying drawings, wherein:
In the following detailed description, for purposes of explanation, numerous specific details are set forth in order to provide a thorough understanding of the disclosed embodiments. It will be apparent, however, that one or more embodiments may be practiced without these specific details. In other instances, well-known structures and devices are schematically shown in order to simplify the drawing.
As shown in
The disclosure also provides a method for fabricating the aforementioned graphene electrode.
The dry-process surface modification treatment, for example, can be a plasma modification process. It should be noted that, since the hetero-atoms have to be confined within the surface of the graphene layer rather than the whole graphene layer, the graphene layer or metal foil must not be heated during the dry-process surface modification treatment. Further, a reactive gas is introduced into the reactor of the plasma modification process to dope the hetero-atoms into the graphene layer.
For example, the reactive gas includes a gas containing the hetero-atoms (such as nitrogen gas, ammonia gas, air, or combinations thereof), or a mixture of the gas containing the hetero-atoms (such as nitrogen gas, ammonia gas, air, or combinations thereof) and other gas (such as hydrogen gas, argon gas, oxygen gas, or combinations thereof). According to another embodiment of the disclosure, a carrier gas can be introduced into the reactor of the plasma modification process, in order to stabilize the plasma modification process. The carrier gas can include helium gas, argon gas, nitrogen gas, neon gas, or combinations thereof. The reactor of the plasma modification process can be a low pressure plasma reactor or an atmospheric pressure plasma reactor. In the plasma modification process, the parameters (such as the reactive gas flow, the carrier gas flow, the reaction pressure, the power, the reaction time, and the distances between the graphene layer and electrodes of the reactor) can be optionally adjusted, assuming that the doped amount of hetero-atoms in the hetero-atom doped graphene layer is from 0.1 to 3 atom %, based on the total atomic amount of the hetero-atom doped graphene layer.
According to an embodiment of the disclosure, the method for forming the graphene layer includes the following steps. First, a coating prepared from a graphene-containing composition is formed on the metal foil, wherein the method for forming the coating on the metal foil can be a screen printing, spin coating, bar coating, blade coating, roller coating, or dip coating method.
Next, the coating is subjected to a drying process, obtaining the graphene layer. The drying process can be performed at 40-150° C. for a period of time from 1 min to 10 hrs. Herein, the graphene-containing composition can include a graphene, and a binder. According to other embodiments of the disclosure, the graphene-containing composition can further include a conducting agent. The binder can be an aqueous-based binder, an organic-based binder, such as carboxymethyl cellulose (CMC), styrene butadiene rubber (SBR), or polyvinylidene difluoride (PVdF), or combinations thereof. The conducting agent can be, for example, graphite, carbon black, or combinations thereof.
As shown in
Below, exemplary embodiments will be described in detail with reference to accompanying drawings so as to be easily realized by a person having ordinary knowledge in the art. The inventive concept may be embodied in various forms without being limited to the exemplary embodiments set forth herein. Descriptions of well-known parts are omitted for clarity, and like reference numerals refer to like elements throughout.
EXAMPLESPreparation of the Graphene Electrode
Example 1First, 5.3571 g of DI water, and 0.0337 g of carboxymethyl cellulose (CMC, serving as a binder) were added into a reaction bottle, and stirred by a homogenizer (with a spinning rate of 2000 rpm) for 20 min. Next, 0.0056 g of acetylene black (sold and manufactured by Timcal with a trade number of Super P, serving as a conducting agent), and 0.5 g of graphene were added into the reaction bottle. After stirring for 20 min, 0.0562 g of styrene butadiene rubber (SBR, serving as binder) was added into the reaction bottle. After stirring for 20 min, a graphene-containing slurry was obtained.
Next, the above graphene-containing slurry was coated on a copper foil by blade coating (using the doctor blade (150 μm) to form a coating. After drying at 120° C., a graphene electrode (I) having the graphene layer was obtained. It should be noted that the graphene layer of the graphene electrode (I) was not doped with any hetero-atom.
Example 2The graphene electrode (I) was disposed into a plasma reactor, wherein the copper foil of the graphene electrode (I) directly contacted with a support substrate of the plasma reactor, and the distance between the graphene layer and the electrode of the plasma reactor was 2.2 mm. Next, a nitrogen gas (with a flow of 5 sccm) and a helium gas (with a flow of 5.88 L/min) were introduced into the plasma reactor. Next, the surface of the graphene layer was subjected to a plasma modification process under a pressure of 1 atm, and a RF power of 65W, in order to dope nitrogen atoms into the surface of the graphene layer. It should be noted that no heating process was performed during the plasma modification process. After reacting for 6 sec, a graphene electrode (II) was obtained.
Next, the surface of the graphene electrode (II) was analyzed by an X-ray Photoelectron Spectrometer (XPS) to measure the doping amount of nitrogen atoms of the hetero-atom doped graphene layer of the graphene electrode (II). The results are as shown in
Example 3 was performed as Example 2 except that the flow rate of the nitrogen gas was increased to 30 sccm instead of 5 sccm. The graphene electrode (III) was obtained.
Next, the surface of the graphene electrode (III) was analyzed by an X-ray Photoelectron Spectrometer (XPS) to measure the doping amount of nitrogen atoms of the hetero-atom doped graphene layer of the graphene electrode (III). The results are shown in
Example 4 was performed as Example 1 except that the reaction time was changed to 18 sec instead of 6 sec. The graphene electrode (IV) was obtained.
Next, the surface of the graphene electrode (IV) was analyzed by an X-ray Photoelectron Spectrometer (XPS) to measure the doping amount of nitrogen atoms of the hetero-atom doped graphene layer of the graphene electrode (IV). The results are shown in
According to
Example 5 was performed as Example 2 except that the flow rate of nitrogen gas was changed to 15 sccm and the reaction time was 18 sec instead of the flow rate of 5 sccm and the reaction time of 6 sec. The graphene electrode (V) was obtained.
Example 6Example 6 was performed as Example 2 except that the flow rate of nitrogen gas was adjusted at 30 sccm and the reaction time was 18 sec. The graphene electrode (VI) was obtained. Table 1 showed the parameters of the plasma modification process employed in Example 2-6.
Fabrications of the Battery Having the Graphene Electrode
Example 7The graphene electrode (I) of Example 1 was cut to form an anode (with a diameter of 13 mm) Next, the anode, an isolation membrane (a polyethylene/polypropylene composite film with a thickness of 20 μm), and a lithium layer (serving as a cathode) were assembled. Next, an electrolyte (including ethylene carbonate (EC), ethyl methyl carbonate (EMC), vinylene carbonate (VC), and 1M of LiPF6) was injected into the isolation membrane, and a button-type lithium ion battery (I) was obtained.
Example 8The graphene electrode (IV) of Example 1 was cut to form an anode (with a diameter of 13 mm). Next, the anode, an isolation membrane (a polyethylene/polypropylene composite film with a thickness of 20 μm), and a lithium layer (serving as a cathode) were assembled. Next, an electrolyte (including ethylene carbonate (EC), ethyl methyl carbonate (EMC), vinylene carbonate (VC), and 1M of LiPF6) was injected into the isolation membrane, and a button-type lithium ion battery (II) was obtained.
Example 9The graphene electrode (V) of Example 1 was cut to form an anode (with a diameter of 13 mm). Next, the anode, an isolation membrane (a polyethylene/polypropylene composite film with a thickness of 20 μm), and a lithium layer (serving as a cathode) were assembled. Next, an electrolyte (including ethylene carbonate (EC), ethyl methyl carbonate (EMC), vinylene carbonate (VC), and 1M of LiPF6) was injected into the isolation membrane, and a button-type lithium ion battery (III) was obtained.
Example 10The graphene electrode (VI) of Example 1 was cut to form an anode (with a diameter of 13 mm). Next, the anode, an isolation membrane (a polyethylene/polypropylene composite film with a thickness of 20 μm), and a lithium layer (serving as a cathode) were assembled. Next, an electrolyte (including ethylene carbonate (EC), ethyl methyl carbonate (EMC), vinylene carbonate (VC), and 1M of LiPF6) was injected into the isolation membrane, and a button-type lithium ion battery (IV) was obtained.
Electrical Test
The batteries (I) and (II) of Examples 7-8 were subjected to a charge-discharge test respectively, and the results are shown in
Next, the discharge capacities of the batteries (I) and (II) were evaluated under various C-rates at room temperature, and the results are shown in
Next, the batteries (I), (III), and (IV) were subjected to a cycle life test, and the results are shown in
The batteries (I), (II), and (III) were subjected to a charging and discharging cycle tests and measured for evaluating the irreversible capacity loss and Coulombic efficiencies thereof. The results are shown in Table 2.
As shown in Table 2, the batteries (II) and (III) having the graphene electrode of the disclosure had an increased Coulombic efficiency and a reduced irreversible capacities in comparison with the battery (I) in both the first cycle and second cycle. This means that the graphene electrode subjected to the plasma modification process had stable electrical characteristics.
Accordingly, since the surface of the graphene layer was subjected to a dry-process surface modification treatment, the graphene electrode of the disclosure exhibited improved electrical characteristics (such as high capacity, high carrier mobility, and low irreversible capacity). Therefore, the graphene electrode of the disclosure is suitable for being used in an energy storage device.
It will be apparent to those skilled in the art that various modifications and variations can be made to the disclosed methods and materials. It is intended that the specification and examples be considered as exemplary only, with a true scope of the disclosure being indicated by the following claims and their equivalents.
Claims
1. A graphene electrode, comprising:
- a metal foil;
- a non-doped graphene layer; and
- a hetero-atom doped graphene layer, wherein the hetero-atom doped graphene layer is separated from the metal foil by the non-doped graphene layer.
2. The graphene electrode as claimed in claim 1, wherein the hetero-atoms doped in the hetero-atom doped graphene layer comprise nitrogen atoms, phosphorous atoms, boron atoms, or combinations thereof.
3. The graphene electrode as claimed in claim 1, wherein the doped amount of hetero-atoms in the hetero-atom doped graphene layer is from 0.1 to 3 atom %, based on the total atomic amount of the hetero-atom doped graphene layer.
4. The graphene electrode as claimed in claim 1, wherein the non-doped graphene layer is a single-layer graphene, or graphene nanosheets.
5. The graphene electrode as claimed in claim 1, wherein the hetero-atom doped graphene layer is a single-layer hetero-atom doped graphene, or hetero-atom doped graphene nanosheets.
6. A method for fabricating a graphene electrode, comprising:
- providing the metal foil;
- forming the graphene layer on the metal foil; and
- subjecting the graphene layer to a dry-process surface modification treatment, thereby doping the hetero-atoms into the graphene layer surface.
7. The method as claimed in claim 6, wherein the hetero-atoms comprise nitrogen atoms, phosphorous atoms, boron atoms, or combinations thereof.
8. The method as claimed in claim 6, wherein the hetero-atoms are doped into the surface of the graphene layer, forming the hetero-atom doped graphene layer.
9. The method as claimed in claim 6, wherein the graphene layer has a portion which is not doped with the hetero-atoms.
10. The method as claimed in claim 9, wherein the portion, which is not doped with the hetero-atoms, of the graphene layer is defined as the non-doped graphene layer.
11. The method as claimed in claim 6, wherein the steps for forming the graphene layer comprise:
- forming the coating on the metal foil, wherein the coating is formed from a graphene-containing composition; and
- subjecting the coating to a drying process, obtaining the graphene layer.
12. The method as claimed in claim 11, wherein the graphene-containing composition comprises:
- a graphene; and
- a binder.
13. The method as claimed in claim 12, wherein the binder comprises an aqueous-based binder, an organic-based binder, or combinations thereof.
14. The method as claimed in claim 12, wherein the graphene-containing composition further comprises a conducting agent.
15. The method as claimed in claim 14, wherein the conducting agent comprises graphite, carbon black, or combinations thereof.
16. The method as claimed in claim 6, wherein the dry-process surface modification treatment comprises a plasma modification process.
17. The method as claimed in claim 16, wherein a reactive gas is introduced during the plasma modification process, and the reactive gas comprises nitrogen gas, ammonia gas, air, or combinations thereof.
18. The method as claimed in claim 17, wherein the reactive gas further comprises argon gas, hydrogen gas, oxygen gas, or combinations thereof.
19. The method as claimed in claim 17, wherein a carrier gas is introduced during the plasma modification process, and the carrier gas comprises helium gas, argon gas, nitrogen gas, neon gas, or combinations thereof.
20. An energy storage device, comprising:
- a first electrode, wherein the first electrode is the graphene electrode as claimed in claim 1;
- a second electrode; and
- an isolation membrane disposed between the first electrode and the second electrode.
21. The energy storage device as claimed in claim 20, wherein the energy storage device is a lithium ion battery, supercapacitor or a fuel cell.
Type: Application
Filed: Jul 24, 2013
Publication Date: May 22, 2014
Applicant: INDUSTRIAL TECHNOLOGY RESEARCH INSTITUTE (Chutung)
Inventors: Hsiao-Feng HUANG (Taoyuan City), Ping-Chen CHEN (Taipei City), Chun-Hsiang WEN (Hsinchu City), Wei-Jen LIU (Hsinchu City)
Application Number: 13/949,732
International Classification: H01G 11/38 (20060101); H01M 4/96 (20060101); H01M 4/133 (20060101); H01G 11/32 (20060101); H01M 4/04 (20060101);