PERFORMANCE ENHANCEMENT IN PMOS AND NMOS TRANSISTORS ON THE BASIS OF SILICON/CARBON MATERIAL
A semiconductor device includes a first transistor having first drain and source regions and a first channel region and a second transistor having second drain and source regions and a second channel region. A first silicon/carbon alloy material is embedded in the first drain and source regions, the first silicon/carbon alloy material inducing a first strain component along a first channel length direction of the first channel region. A second silicon/carbon alloy material is embedded in the second drain and source regions, the second silicon/carbon alloy material inducing a second strain component along a second channel length direction of the second channel region, wherein the second strain component is of an opposite type of the first strain component.
Latest GLOBALFOUNDRIES Inc, Patents:
This is a divisional of co-pending application Ser. No. 13/362,763, filed Jan. 31, 2012, which was a divisional of application Ser. No. 12/473,726, filed May 28, 2009, now U.S. Pat. No. 8,154,084, issued Apr. 10, 2012, which claimed priority from German patent application No. 10 2008 035 816.9, filed Jul. 31, 2008.
BACKGROUND OF THE INVENTION1. Field of the Invention
Generally, the present disclosure relates to integrated circuits, and, more particularly, to the formation of different transistor types having strained channel regions by using an embedded strain-inducing material to enhance charge carrier mobility in the channel regions.
2. Description of the Related Art
Integrated circuits have found a widespread applicability in many fields due to the continuous increase of functions that may be provided on a given chip area. Integrated circuits are composed of numerous individual circuit components, such as transistors, wherein several million or even several hundred million individual transistors may be provided in complex devices. Generally, a plurality of process technologies are currently practiced, wherein, for complex circuitry, such as microprocessors, storage chips and the like, CMOS technology is currently the most promising approach due to the superior characteristics in view of operating speed and/or power consumption and/or cost efficiency. During the fabrication of complex integrated circuits using CMOS technology, millions of transistors, i.e., N-channel transistors and P-channel transistors, are formed on a substrate including a crystalline semiconductor layer. A MOS transistor, irrespective of whether an N-channel transistor or a P-channel transistor is considered, comprises so-called PN junctions that are formed by an interface of highly doped drain and source regions with an inversely doped channel region disposed between the drain region and the source region. The conductivity of the channel region, i.e., the drive current capability of the conductive channel, is controlled by a gate electrode formed near to the channel region and separated therefrom by a thin insulating layer. The conductivity of the channel region, upon formation of a conductive channel due to the application of an appropriate control voltage to the gate electrode, depends on the dopant concentration, the mobility of the charge carriers and, for a given extension of the channel region in the transistor width direction, on the distance between the source and drain regions, which is also referred to as channel length. Thus, the reduction of the channel length, and associated therewith the reduction of the channel resistivity, renders the channel length a dominant design criterion for accomplishing an increase in the operating speed of the integrated circuits.
The continuing shrinkage of the transistor dimensions, however, involves a plurality of issues associated therewith that have to be addressed so as to not unduly offset the advantages obtained by steadily decreasing the channel length of MOS transistors. One major problem in this respect is the development of enhanced photolithography and etch strategies to reliably and reproducibly create circuit elements of critical dimensions, such as the gate electrode of the transistors, for a new device generation. Moreover, highly sophisticated dopant profiles, in the vertical direction as well as in the lateral direction, are required in the drain and source regions to provide low sheet and contact resistivity in combination with a desired channel controllability.
The continuous size reduction of the critical dimensions, i.e., the gate length of the transistors, necessitates the adaptation and possibly the new development of highly complex process techniques concerning the above-identified process steps. It has, therefore, been proposed to enhance the channel conductivity of the transistor elements by increasing the charge carrier mobility in the channel region for a given channel length, thereby offering the potential for achieving a performance improvement that is comparable with the advance to a future technology node while avoiding or at least postponing many of the above process adaptations associated with device scaling. One efficient mechanism for increasing the charge carrier mobility is the modification of the lattice structure in the channel region, for instance by creating tensile or compressive stress in the vicinity of the channel region to produce a corresponding strain in the channel region, which results in a modified mobility for electrons and holes, respectively. For example, creating tensile strain in the channel region having a standard (100) surface orientation may increase the mobility of electrons, which, in turn, may directly translate into a corresponding increase in the conductivity. On the other hand, compressive strain in the channel region may increase the mobility of holes, thereby providing the potential for enhancing the performance of P-type transistors. The introduction of stress or strain engineering into integrated circuit fabrication is an extremely promising approach for further device generations, since, for example, strained silicon may be considered as a “new” type of semiconductor material, which may enable the fabrication of fast powerful semiconductor devices without requiring expensive semiconductor materials, while many of the well-established manufacturing techniques may still be used.
In one approach, the hole mobility of PMOS transistors is enhanced by forming a strained silicon/germanium layer in the drain and source regions of the transistors, wherein the compressively strained drain and source regions create uniaxial strain in the adjacent silicon channel region. To this end, the drain and source regions of the PMOS transistors are selectively recessed, while the NMOS transistors are masked, and subsequently the silicon/germanium layer is selectively formed in the PMOS transistor by epitaxial growth. Thus, complex manufacturing steps, such as etch processes, the formation of appropriate etch and growth masks and selective epitaxial growth techniques have to be incorporated into the CMOS process flow.
In other approaches, silicon/carbon material may be used for NMOS transistors to create a desired lattice mismatch specifically in the channel regions of the NMOS transistors, which may frequently be accomplished by ion implantation of carbon into the drain and source regions. However, the performance gain for transistors of different conductivity type on the basis of silicon/carbon alloys may lead to an even more complex process flow, as the various steps for the formation of respective strain layers may have to be appropriately integrated in the complex manufacturing flow, which may result in a less pronounced performance gain than expected.
The present disclosure is directed to various methods and devices that may avoid, or at least reduce, the effects of one or more of the problems identified above.
SUMMARY OF THE INVENTIONThe following presents a simplified summary of the invention in order to provide a basic understanding of some aspects of the invention. This summary is not an exhaustive overview of the invention. It is not intended to identify key or critical elements of the invention or to delineate the scope of the invention. Its sole purpose is to present some concepts in a simplified form as a prelude to the more detailed description that is discussed later.
Generally, the present disclosure relates to techniques and semiconductor devices which enable the manufacture of differently strained semiconductor materials embedded into drain and source areas, wherein at least a semiconductor alloy may be used having a natural lattice constant that is less compared to a natural lattice constant of silicon. For example, in some illustrative aspects disclosed herein, a silicon/carbon alloy may be used in combination with a further semiconductor alloy, such as a silicon/germanium alloy, to provide different types of strain for transistors of different conductivity type, while nevertheless providing an efficient manufacturing strategy, for instance with respect to using appropriate etch stop and spacer layers and/or incorporating appropriate implantation species prior to forming the corresponding semiconductor alloys. Hence, the advantages of each of the different semiconductor alloys may be taken advantage of while not unduly contributing to additional process complexity compared to conventional strategies in which usually a single strain-inducing semiconductor alloy may be used. In other illustrative aspects disclosed herein, a semiconductor material, such as silicon/carbon, which may typically be employed for enhancing characteristics of N-channel transistors, may also be provided in P-channel transistors in combination with sophisticated stress memorization techniques, thereby obtaining a desired type of strain in the P-channel transistors while at the same time enabling enhanced overall manufacturing efficiency and additional gain in transistor performance due to the positive effects of the carbon species in the drain and source areas of the P-channel transistor.
In one exemplary embodiment, a semiconductor device is disclosed that includes, among other things, a first transistor having first drain and source regions and a first channel region and a second transistor having second drain and source regions and a second channel region. The illustrative semiconductor device also includes a first silicon/carbon alloy material embedded in the first drain and source regions, the first silicon/carbon alloy material inducing a first strain component along a first channel length direction of the first channel region. Additionally, disclosed semiconductor device includes a second silicon/carbon alloy material embedded in the second drain and source regions, the second silicon/carbon alloy material inducing a second strain component along a second channel length direction of the second channel region, wherein the second strain component is of an opposite type of the first strain component.
Also disclosed herein is a semiconductor device that includes first and second active regions positioned in a layer of semiconductor material and a first transistor element positioned in and above the first active region, wherein source and drain regions of the first transistor element include a first silicon/carbon alloy material that induces a tensile strain in a channel region of the first transistor element. Additionally, the disclosed semiconductor device further includes, among other things, a second transistor element positioned in and above the second active region, wherein source and drain regions of the second transistor element include a second silicon/carbon alloy material that induces a compressive strain in a channel region of the second transistor element.
The disclosure may be understood by reference to the following description taken in conjunction with the accompanying drawings, in which like reference numerals identify like elements, and in which:
While the subject matter disclosed herein is susceptible to various modifications and alternative forms, specific embodiments thereof have been shown by way of example in the drawings and are herein described in detail. It should be understood, however, that the description herein of specific embodiments is not intended to limit the invention to the particular forms disclosed, but on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the appended claims.
DETAILED DESCRIPTIONVarious illustrative embodiments of the invention are described below. In the interest of clarity, not all features of an actual implementation are described in this specification. It will of course be appreciated that in the development of any such actual embodiment, numerous implementation-specific decisions must be made to achieve the developers' specific goals, such as compliance with system-related and business-related constraints, which will vary from one implementation to another. Moreover, it will be appreciated that such a development effort might be complex and time-consuming, but would nevertheless be a routine undertaking for those of ordinary skill in the art having the benefit of this disclosure.
The present subject matter will now be described with reference to the attached figures. Various structures, systems and devices are schematically depicted in the drawings for purposes of explanation only and so as to not obscure the present disclosure with details that are well known to those skilled in the art. Nevertheless, the attached drawings are included to describe and explain illustrative examples of the present disclosure. The words and phrases used herein should be understood and interpreted to have a meaning consistent with the understanding of those words and phrases by those skilled in the relevant art. No special definition of a term or phrase, i.e., a definition that is different from the ordinary and customary meaning as understood by those skilled in the art, is intended to be implied by consistent usage of the term or phrase herein. To the extent that a term or phrase is intended to have a special meaning, i.e., a meaning other than that understood by skilled artisans, such a special definition will be expressly set forth in the specification in a definitional manner that directly and unequivocally provides the special definition for the term or phrase.
Generally, the present disclosure relates to manufacturing techniques and related semiconductor devices in which field effect transistors of different conductivity type may receive a strained semiconductor material in the drain and/or source regions in order to provide a desired magnitude and/or type of strain in the corresponding channel regions of these transistors. For this purpose, in some illustrative embodiments, different semiconductor alloys may be used, such as silicon/germanium and silicon/carbon, on the basis of an appropriate manufacturing regime in which both materials may be embedded into the drain and source areas of the corresponding transistors by using an appropriately designed layer stack including a spacer layer and an etch stop layer. Furthermore, overall transistor performance for at least one type of transistor may be enhanced by incorporating any desired type of implantation species, such as dopants, non-doping species and the like, prior to forming a respective strained semiconductor material by epitaxial growth techniques. In this case, the electronic characteristics of the drain and source regions may be enhanced on the basis of the additional implantation species, which may be incorporated without creating additional implantation-induced damage, since the implantation process may be performed prior to growing the strained semiconductor material. Consequently, for N-channel transistors, a reduced source/drain junction resistance may be obtained due to a specifically optimized dopant profile. Furthermore, floating body effects in silicon-on-insulator (SOI) transistors may be reduced due to the presence of higher leakage currents of the corresponding PN junctions, which may, therefore, reduce charge carrier accumulation in the body region of the SOI transistors. A corresponding adjustment of the PN junction characteristics may also be accomplished by incorporating an appropriate implantation species prior to actually forming the strained semiconductor material. Additionally, the electron mobility may be enhanced due to the embedded silicon/carbon alloy in the drain and source areas of the N-channel transistor. Similarly, in P-channel transistors, a reduced source and drain resistance may be obtained due to the lower intrinsic resistivity of the silicon/germanium material, and also leakage currents through the PN junctions may be adjusted to a moderately high value, depending on the overall transistor characteristics, thereby also reducing charge carrier accumulation in SOI transistors. Finally, the increased hole mobility in the channel region caused by the embedded silicon/germanium alloy may additionally contribute to the overall enhanced device performance. Furthermore, since both strain-inducing semiconductor materials may be incorporated at a moderately early manufacturing stage, additional strain-inducing mechanisms may be implemented into the overall manufacturing flow substantially without requiring additional process steps. For example, strain-inducing spacer elements and/or strain-inducing dielectric cap layers may be provided in order to further enhance strain in at least one type of transistor.
In other illustrative embodiments disclosed herein, a highly efficient manufacturing sequence may be used in incorporating a silicon/carbon material into transistors of different conductivity type, wherein additional strain-inducing mechanisms may also be used, for instance, in the P-channel transistor to overcompensate for any negative effect of the silicon/carbon material, while at the same time taking advantage of the characteristics of carbon with respect to acting as a diffusion hindering species, which may thus provide dopant profiles of enhanced accuracy in the P-channel transistor. Consequently, in combination with the enhanced electronic characteristics of the drain and source regions of the P-channel transistor and the overcompensated strain component, a significant enhancement of the P-channel transistor may be achieved, wherein, for SOI architectures, reduced floating body effects may also be achieved, while the N-channel transistor may exhibit reduced source/drain junction resistance in combination with increased electron mobility in the channel region due to the embedded silicon/carbon alloy. Also, in this case, charge carrier accumulation in the floating body of SOI N-channel transistors may be reduced by providing PN junctions of increased leakage currents due to the presence of the carbon species.
Furthermore, appropriate active regions may be defined in the semiconductor layer 103 on the basis of appropriate isolation structures, such as shallow trench isolations (not shown), which may also be provided between the transistors 150P, 150N. Furthermore, the transistors 150P, 150N may comprise a gate electrode structure 151 which may include, in this manufacturing stage, an electrode material 151A, which is formed on a gate insulation layer 151B, which separates the electrode material 151A from a channel region 152. The gate electrode material 151A may represent any appropriate material, such as polysilicon and the like, which may even be replaced by a material of enhanced conductivity in a later manufacturing stage, depending on the overall process and device requirements. Similarly, the gate insulation layer 151B may be comprised of any appropriate dielectric material, such as silicon dioxide-based materials, silicon nitride, silicon oxynitride, high-k dielectric materials, such as hafnium oxide, zirconium oxide and the like. Furthermore, the gate electrode structures 151 may include a cap layer 151C which may be comprised of silicon nitride and the like. Furthermore, the semiconductor device 100 may comprise a layer stack 104 that is formed above the transistors 150P, 150N and, in the embodiment shown, may comprise a first layer or spacer layer 104A, above which may be provided a second layer or etch stop layer 104B. In one illustrative embodiment, the spacer layer 104A may be comprised of silicon nitride while the etch stop layer 104B may be formed of silicon dioxide. Thus, in the embodiment shown, the spacer layer 104A and the cap layer 151C may be comprised of material having similar characteristics with respect to a subsequent etch process so that these components may be removed during a common etch sequence. Furthermore, the etch stop layer 104B may have a thickness that is sufficient to provide the desired etch stop capabilities during an etch process for locally providing an etch and growth mask above the transistor 150N. For example, the etch stop layer 104B may be provided with a thickness of approximately 20-50 nm or even more, when provided in the form of a silicon dioxide material. On the other hand, the spacer layer 104A may be provided with an appropriate thickness in a highly conformal manner in order to adjust a desired offset during an etch process for forming cavities in the semiconductor layer 103 in a later manufacturing stage. For instance, a thickness of the spacer layer 104A may range from approximately 1-20 nm in sophisticated applications in which a gate length, i.e., the horizontal extension of the gate electrode material 151A in
The semiconductor device 100 as shown in
In some illustrative embodiments, after the etch process 107 and prior to or after the removal of the mask 105, one or more implantation processes 108 may be performed to incorporate one or more implantation species 108A through exposed surface portions of the cavity 103P. For example, the one or more implantation processes 108 may comprise one or more steps performed on the basis of a non-zero tilt angle, which is to be understood as a non-zero angle with respect to a normal of the semiconductor layer 103 or the buried insulating layer 102. Consequently, any desired implantation species may be incorporated, wherein the positioning of the implantation species 108A may be controlled by the process parameters of the one or more implantation processes 108, such as energy, dose, tilt angle, type of implantation species and the like. In some illustrative embodiments, the implantation species 108A may comprise a dopant species, for instance for counter-doping material of the layer 103 with respect to drain and source areas to be formed in a later manufacturing stage on the basis of a strained semiconductor material to be filled into the cavities 103P. Moreover, in other illustrative embodiments, the implantation species 108A may comprise a dopant for defining at least a portion of drain and source regions, such as an extension region to avoid additional implantation steps in a later manufacturing stage after providing a strained semiconductor material in the cavities 103P. In other illustrative embodiments, respective drain and source extension regions may have been formed in an early manufacturing stage, for instance prior to or after the deposition of the spacer layer 104A, depending on the initial layer thickness thereof. In still other illustrative embodiments, the implantation species 108A may comprise corresponding components, such as nitrogen, carbon and the like, which may result in a reduced diffusion activity of a corresponding dopant species, such as boron, which may be provided in a later manufacturing stage. In this manner, the finally obtained PN junctions of the drain and source regions may be defined with enhanced accuracy on the basis of one or more components of the implantation species 108A. Moreover, the degree of leakage currents through the PN junctions still to be formed may also be adjusted on the basis of the implantation species 108A, thereby enabling a highly efficient stabilization of threshold voltage of the transistor 150P with respect to floating body effects. During the implantation process 108, undue incorporation of the implantation species 108A into the gate electrode material 151A may be suppressed or at least reduced by the spacers 104S and the cap layer 151C. In other embodiments, in which the mask 105 may have been removed at an earlier manufacturing stage, the corresponding shadowing effect during a tilted implantation step of the process 108 may be reduced.
Furthermore, the semiconductor device 100 may comprise a spacer structure 156 formed adjacent to the gate electrode material 151A, wherein the spacer structure 156 may comprise a plurality of individual spacer elements 156A, 156B, depending on the overall process and device requirements. For instance, the drain and source regions 154, at least for one of the transistors 150P, 150N, may be adjusted on the basis of additional implantation processes, during which the corresponding spacer elements 156A, 156B may act as implantation masks. In other illustrative embodiments, additional implantation processes may be substantially avoided after forming the strained semiconductor materials 153P, 153N, respectively, thereby also maintaining lattice damage in these materials at a low level. In this case, the spacer structure 156 may be provided to act as a mask for forming metal silicide regions 155 in a self-aligned manner. In some illustrative embodiments, the spacer structure 156 may comprise a high intrinsic stress level, which may be appropriate for enhancing performance of one of the transistors 150P, 150N. For example, the spacer structure 156 may have a high tensile stress level, thereby providing additional strain in the channel region 152 of the transistor 150N. On the other hand, a negative influence of the internal stress level in the transistor 150P may be overcompensated for by additional stress-inducing mechanisms, such as strain-inducing dielectric layers 116 and 117, which may be provided with high internal tensile stress and compressive stress, respectively. For instance, silicon nitride may be deposited with high internal stress levels, depending on the corresponding process parameters of a plasma enhanced CVD technique. For example, stress levels up to 1 GPa and higher for a tensile silicon nitride material may be obtained, while stress levels of up to 2 GPa and higher may be accomplished for a compressively stressed silicon nitride material. Consequently, by providing a high internal compressive stress level in the layer 117, any tensile internal stress of the spacer structure 156 in the transistor 150P may be compensated for. In other illustrative embodiments, a compressive stress level may be established in the spacer structures 156, when a further pronounced performance gain may be desired in the transistor 150P.
The semiconductor device 100 as shown in
As a consequence, the strained semiconductor materials 153P, 153N may be formed on the basis of selective epitaxial growth techniques, wherein appropriate mask and etch stop layers, such as the layers 104A, 104B (
With reference to
The semiconductor device 200 as shown in
As a result, the present disclosure provides semiconductor devices and methods of forming the same in which strained semiconductor materials, such as silicon/germanium and the like on the one hand and silicon/carbon on the other hand, may be incorporated in the drain and source regions on the basis of a highly efficient manufacturing flow, possibly in combination with additional implant species for further enhancing the overall transistor characteristics so that dopant profiles in combination with increased strain levels may be accomplished. In other cases, a semiconductor material having a natural lattice constant less than a silicon-based material may be used in transistors of different conductivity types, wherein a negative influence of the corresponding initially provided strain component may be overcompensated for by applying a stress memorization technique. Consequently, enhanced overall process uniformity may be achieved due to enhanced conditions during etching the respective cavities and depositing the semiconductor alloy, while at the same time dopant profile characteristics as well as leakage current behavior may be enhanced in both the P-channel transistor and the N-channel transistor, thereby also contributing to enhanced overall device characteristics.
The particular embodiments disclosed above are illustrative only, as the invention may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. For example, the process steps set forth above may be performed in a different order. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. It is therefore evident that the particular embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of the invention. Accordingly, the protection sought herein is as set forth in the claims below.
Claims
1-20. (canceled)
21. A semiconductor device, comprising:
- a first transistor comprising first drain and source regions and a first channel region;
- a first silicon/carbon alloy material embedded in said first drain and source regions, said first silicon/carbon alloy material inducing a first strain component along a first channel length direction of said first channel region;
- a second transistor comprising second drain and source regions and a second channel region; and
- a second silicon/carbon alloy material embedded in said second drain and source regions, said second silicon/carbon alloy material inducing a second strain component along a second channel length direction of said second channel region, said second strain component being of an opposite type of said first strain component.
22. The semiconductor device of claim 21, further comprising a semiconductor material layer positioned above a buried insulating layer, wherein said first and second transistors are positioned in and above said semiconductor material layer.
23. The semiconductor device of claim 21, wherein said first transistor is an N-channel transistor and said second transistor is a P-channel transistor.
24. The semiconductor device of claim 23, wherein said first strain component is a tensile strain and second strain component is a compressive strain.
25. The semiconductor device of claim 21, further comprising a stressed dielectric material layer positioned above each of said first and second transistors.
26. The semiconductor device of claim 25, wherein said stressed dielectric material layer positioned above said first transistor is a first stressed material layer having an internal tensile stress.
27. The semiconductor device of claim 26, wherein said stressed dielectric material layer positioned above said second transistor is a second stressed material layer having an internal compressive stress.
28. The semiconductor device of claim 21, wherein said first transistor comprises a first sidewall spacer structure formed adjacent to a first gate electrode structure and said second transistor comprises a second sidewall spacer structure formed adjacent to a second gate electrode structure, at least one of said first and second sidewall spacer structures comprising a dielectric material having an internal stress level.
29. The semiconductor device of claim 21, wherein a gate electrode structure of at least one of said first and second transistors comprises a conductive metal gate electrode and a gate insulation layer comprising a high-k gate dielectric material.
30. A semiconductor device, comprising:
- a first and second active regions positioned in a layer of semiconductor material;
- a first transistor element positioned in and above said first active region, wherein source and drain regions of said first transistor element comprise a first silicon/carbon alloy material that induces a tensile strain in a channel region of said first transistor element; and
- a second transistor element positioned in and above said second active region, wherein source and drain regions of said second transistor element comprise a second silicon/carbon alloy material that induces a compressive strain in a channel region of said second transistor element.
31. The semiconductor device of claim 30, wherein said layer of semiconductor material is positioned above a buried insulating layer.
32. The semiconductor device of claim 31, wherein said source and drain regions of at least one of said first and second transistor elements extend down to said buried insulating layer.
33. The semiconductor device of claim 30, wherein said first transistor element is an N-channel transistor and said second transistor element is a P-channel transistor.
34. The semiconductor device of claim 30, further comprising a first stressed material layer having a first type of internal stress positioned on said first transistor element.
35. The semiconductor device of claim 34, wherein said first type of internal stress of said first stressed material layer is a tensile stress.
36. The semiconductor device of claim 34, wherein said first stressed material layer is a silicon nitride material layer having an internal tensile stress of at least approximately 1 GPa.
37. The semiconductor device of claim 34, further comprising a second stressed material layer having a second type of internal stress positioned on said second transistor element, wherein said second type of internal stress is opposite of said first type of internal stress.
38. The semiconductor device of claim 37, wherein said second type of internal stress of said second stressed material layer is a compressive stress.
39. The semiconductor device of claim 37, wherein said second stressed material layer is a silicon nitride material layer having an internal compressive stress of at least approximately 2 GPa.
Type: Application
Filed: May 27, 2014
Publication Date: Sep 18, 2014
Applicant: GLOBALFOUNDRIES Inc, (Grand Cayman)
Inventors: Jan Hoentschel (Dresden), Vassilios Papageorgiou (Austin, TX), Belinda Hannon (Austin, TX)
Application Number: 14/287,806
International Classification: H01L 27/092 (20060101); H01L 29/78 (20060101); H01L 29/16 (20060101);