Abstract: A method for bonding stainless steel members includes: contacting a first stainless steel member with a second stainless steel member that has a strain exceeding 50% reduction; and heating the first and second stainless steel members to a re-crystallization initiation temperature or higher, after the contacting.

Abstract: A corrosion-resistant, hot and cold formable and weldable steel for use in hydrogen-induced technology with high resistance to hydrogen embrittlement has the following composition: 0.01 to 0.4 percent by mass of carbon, ?3.0 percent by mass of silicon, 0.3 to 30 percent by mass of manganese, 10.5 to 30 percent by mass of chromium, 4 to 12.5 percent by mass of nickel, ?1.0 percent by mass of molybdenum, ?0.2 percent by mass of nitrogen, 0.5 to 8.0 percent by mass of aluminum, ?4.0 percent by mass of copper, ?0.1 percent by mass of boron, ?1.0 percent by mass of tungsten, ?5.0 percent by mass of cobalt, ?0.5 percent by mass of tantalum, ?2.0 percent by mass of at least one of the elements: niobium, titanium, vanadium, hafnium and zirconium, ?0.3 percent by mass of at least one of the elements: yttrium, scandium, lanthanum, cerium and neodymium, the remainder being iron and smelting-related steel companion elements.

Abstract: A process of manufacturing a steel alloy for railway components is provided. The process involves providing an alloy comprising, in weight percentage, from 0.21 to 0.27 carbon, from 0.80 to 1.20 manganese, from 0.35 to 0.60 silicon, up to 0.02 phosphorus, up to 0.02 sulfur, from 0.55 to 0.65 chromium, from 0.45 to 0.55 molybdenum, from 1.75 to 2.05 nickel, and from 0.005 to 0.030 titanium; casting the alloy; normalizing the alloy; heat treating the alloy; and tempering the alloy, wherein the tempering occurs at 400-700° C. for 1-5 hours.

Abstract: Provided is a martensitic stainless-steel sheet having a reduced anisotropy in workability and fatigue resistance which are attributable to oxide based inclusions. A martensitic stainless-steel sheet which has a steel composition that contains, in terms of mass %, 0.030 to 0.300% C, 0.20 to 2.50% Si, 0.15 to 4.00% Mn, 0.01 to 1.00% Ni, 11.00 to 15.00% Cr, 0.001 to 0.100% N, 0.0001 to 0.0350% Al, 0 to 0.50% V, 0 to 0.50% Nb, 0 to 0.50% Ti, 0 to 0.020% B, and a balance of Fe and unavoidable impurities, and that has a value of ?max, determined by the following equation (1), of 80.0 or greater, and in which oxide based inclusions are observed in the metallographic structure, the oxide based inclusions having a converted composition comprising up to 30 mass % or less Al2O3, 20 to 60 mass % SiO2, and 15 to 70 mass % MnO.

Abstract: A Cr-containing ferritic stainless steel sheet is desired with improved corrosion resistance and rust resistance as well as improved ridging resistance. To achieve these results, the ferritic stainless steel sheet derives the relationship between Ap, which shows the ?-phase rate at 1100° C. due to a predetermined ingredient, and Sn in ferritic stainless steel which becomes a dual phase structure of ?+? in the hot rolling temperature region, applies and adds Sn, and hot rolls the steel to give a total rolling rate of 15% or more in 1100° C. or higher hot rolling to thereby obtain ferritic stainless steel sheet which has good ridging resistance, which also has excellent corrosion resistance and rust resistance, and which can be applied to general durable consumer goods, wherein 0.060?Sn?0.634?0.0082Ap and 10?Ap?70.

Abstract: An end block is disclosed. The end block may include a body extending between a front side, a back side, a left side, a right side, a top side and a bottom side. Furthermore, the body may include a first bore extending through the body between an inlet port and an outlet port and a cylinder bore extending between a cylinder port and the first bore. Moreover, the body may include a precipitation hardened martensitic stainless steel comprising between 0.08% and 0.18% by weight carbon, between 10.50% and 14.00% by weight chromium, between 0.65% and 1.15% by weight nickel, between 0.85% and 1.30% by weight copper, iron, and a first precipitate comprising the copper.

Abstract: A process for designing and manufacturing a cavitation erosion resistant component. The process includes selecting a base material for use in a cavitation erosion susceptible environment and conducting a uniaxial loading test on a sample of the selected material. Thereafter, atomic force microscopy (AFM) topography on a surface of the tested sample is conducted and used to provide a surface strain analysis. The process also includes crystal plasticity finite element modeling (CPFEM) of uniaxial loading and CPFEM nanoindentation of the selected material over a range of values for at least one microstructure parameter. A subrange of microstructure parameter values that correlate to CPFEM nanoindentation results that provide increased CE resistance is determined. Finally, a component having an average microstructure parameter value that falls within the subrange of microstructure parameter values is manufactured.

Abstract: There is provided an austenitic stainless steel for high-pressure hydrogen gas consisting, by mass percent, of C: 0.10% or less, Si: 1.0% or less, Mn: 3% or more to less than 7%, Cr: 15 to 30%, Ni: 10% or more to less than 17%, Al: 0.10% or less, N: 0.10 to 0.50%, and at least one kind of V: 0.01 to 1.0% and Nb: 0.01 to 0.50%, the balance being Fe and impurities, wherein in the impurities, the P content is 0.050% or less and the S content is 0.050% or less, the tensile strength is 800 MPa or higher, the grain size number (ASTM E112) is No. 8 or higher, and alloy carbo-nitrides having a maximum diameter of 50 to 1000 nm are contained in the number of 0.4/?m2 or larger in cross section observation.

Abstract: A rolled steel bar for machine structural use includes a predetermined chemical composition comprising, by mass %, C: 0.45% to 0.65%, Si: higher than 1.00% to 1.50%, Mn: higher than 0.40% to 1.00%, P: 0.005% to 0.050%, S: 0.020% to 0.100%, V: 0.08% to 0.20%, Ti: 0% to 0.050%; Ca: 0% to 0.0030%, Zr: 0% to 0.0030%, Te: 0% to 0.0030%, and a remainder including Fe and impurities, wherein the impurities include: Cr: 0.10% or lower, Al: lower than 0.01%, and N: 0.0060% or lower. In the rolled steel bar for machine structural use, K1 obtained from “K1=C+Si/7+Mn/5+1.54×V” is 0.95 to 1.05, K2 obtained from “K2=139?28.6×Si+105×Mn?833×S?13420×N” is more than 35, a Mn content and a S content satisfy Mn/S?8.0, and a total decarburized depth of a surface layer is 500 ?m or less.

Abstract: A rolled steel bar for machine structural use includes a predetermined chemical composition comprising, by mass %, C: 0.45% to 0.65%, Si: higher than 1.00% to 1.50%, Mn: higher than 0.40% to 1.00%, P: 0.005% to 0.050%, S: 0.020% to 0.100%, V: 0.08% to 0.20%, Ti: 0% to 0.050%; Ca: 0% to 0.0030%, Zr: 0% to 0.0030%, Te: 0% to 0.0030%, and a remainder including Fe and impurities, wherein the impurities include: Cr: 0.10% or lower, Al: lower than 0.01%, and N: 0.0060% or lower. In the rolled steel bar for machine structural use, K1 obtained from “K1=C+Si/7+Mn/5+1.54×V” is 0.95 to 1.05, K2 obtained from “K2=139?28.6×Si+105×Mn?833×S?13420×N” is more than 35, K3 obtained from “K3=137×C?44.0×Si” is 10.7 or more, a Mn content and a S content satisfy Mn/S?8.0, and a total decarburized depth in a surface layer is 500 ?m or less.

Abstract: There is provided an austenitic stainless steel for high-pressure hydrogen gas consisting, by mass percent, of C: 0.10% or less, Si: 1.0% or less, Mn: 3% or more to less than 7%, Cr: 15 to 30%, Ni: 10% or more to less than 17%, Al: 0.10% or less, N: 0.10 to 0.50%, and at least one kind of V: 0.01 to 1.0% and Nb: 0.01 to 0.50%, the balance being Fe and impurities, wherein in the impurities, the P content is 0.050% or less and the S content is 0.050% or less, the tensile strength is 800 MPa or higher, the grain size number (ASTM E112) is No. 8 or higher, and alloy carbo-nitrides having a maximum diameter of 50 to 1000 nm are contained in the number of 0.4/?m2 or larger in cross section observation.

Abstract: A martensitic Cr-containing steel having excellent corrosion resistance, SSC resistance, and IGHIC resistance is provided. A martensitic Cr-containing steel according to the present invention includes: a chemical composition consisting of, by mass %, Si: 0.05 to 1.0%, Mn: 0.1 to 1.0%, Cr: 8 to 12%, V: 0.01 to 1.0%, sol. Al: 0.005 to 0.10%, with the balance being Fe and impurities, wherein an effective Cr amount defined by “Cr?16.6×C” is not less than 8%, and an Mo equivalent defined by “Mo+0.5×W” is 0.03 to 2%; a micro-structure wherein a grain size number of prior-austenite crystal grain is not less than 8.0; and a yield strength of less than 379 to 551 MPa, wherein a grain-boundary segregation ratio of Mo and W is not less than 1.5.

Abstract: A steel pipe is formed by performing pipe making of a raw material having a composition containing C: 0.05% or less, Si: 0.50% or less, Mn: 0.20% to 1.80%, P: 0.030% or less, S: 0.005% or less, Cr: 14.0% to 18.0%, Ni: 5.0% to 8.0%, Mo: 1.5% to 3.5%, Cu: 0.5% to 3.5%, Al: 0.10% or less, Nb: more than 0.20% and 0.50% or less, V: 0.20% or less, N: 0.15% or less, and O: 0.010% or less, on a percent by mass basis, wherein Cr+0.65Ni+0.6Mo+0.55Cu?20C?18.5 and Cr+Mo+0.3Si?43.3C?0.4Mn?Ni?0.3Cu?9N?11 are satisfied and subjecting the resulting steel pipe to a quenching treatment to heat to a temperature higher than or equal to the Ac3 transformation temperature and, subsequently, cool to a temperature of 100° C. or lower at a cooling rate higher than or equal to the air cooling rate and a tempering treatment to temper at a temperature lower than or equal to the Ac1 transformation temperature.

Abstract: A stainless steel contains, by mass %, C: 0.005% to 0.03%, Si: 0.05% to 1.0%, Mn: 0.1% to 4.0%, Ni: 3% to 8%, Cr: 20% to 35%, Mo: 0.01% to 4.0%, Al: 0.001% to 0.30%, N: 0.05% to 0.60%, one or more selected from Re: 2.0% or less, Ga: 2.0% or less, and Ge: 2.0% or less, and a balance consisting of Fe and impurities.

Abstract: An object of the present invention is to provide steel for blades with a significantly improved carbide concentration and a method for producing the same. The steel for blades has a metal composition consisting of, by mass, 0.55% to 0.8% C, not more than 1.0% Si, not more than 1.0% Mn, 12.0% to 14.0% Cr, and the balance of Fe with inevitable impurities, wherein the number of carbides in a ferrite structure of the steel for blades is 600 to 1,000 per an area of 100 ?m2.

Abstract: The present invention provides a fillet welded joint and a method of production of a fillet welded joint which can raise the productivity of the method of production of a fillet welded joint and a fillet welded joint without sacrificing the strength against fatigue fracture of the welded structural member. The fillet welded joint of the present invention is a fillet welded joint formed by fillet welding at least two metal members, wherein, on the surface of at least one of the metal members, the fillet welded joint comprises a press bead of a rib-shaped projection provided by press-forming so as to project upward to the side having a weld bead formed by the fillet welding, and part of the press bead contacts or overlaps the weld bead.

Abstract: There is provided a precipitation hardening stainless steel powder including, in percentage by mass: Si: ?1.0%; Mn: ?1.8%; Ni: 3.0 to 8.5%; Cr: 12.0 to 20.0%; Mo: 0.1 to 2.5%; Cu: 1.0 to 5.0% and/or Ti+Al: 1.0 to 5.0%; Nb+Ta?5C or Nb?5C; N?350 ppm; and the balance being Fe and incidental impurities. A sintered compact fabricated from the steel powder has a martensite content of 90% or more. The precipitation hardening stainless steel powder provides a sintered compact that exhibits high strength after aging.

Abstract: A multilayer electronic component includes an element body having an internal electrode layer and a dielectric layer. These layers are substantially parallel to a plane including a first axis and a second axis and are alternately laminated along a third axis direction. A pair of side surfaces facing each other in the first axis direction of the element body is respectively equipped with an insulating layer. A pair of end surfaces facing each other in the second axis direction of the element body is respectively equipped with an external electrode electrically connected to the internal electrode layer. The insulating layer has a mountain portion formed on a peripheral edge of the side surface and a plane portion of a central portion of the side surface.

Abstract: A sensor assembly is described herein. The sensor assembly includes a housing that includes an inner surface that defines a cavity within the housing, and a proximity sensor positioned within the cavity. The proximity sensor includes a first connector, a second connector, and a substantially planar sensing coil that extends between the first connector and the second connector. The sensing coil extends outwardly from the first connector such that the second connector is radially outwardly from the first connector.

Abstract: An endless-belt shaped heating element is produced by: dispersing annealed stainless-steel fibers in the heat-resistant resin or a precursor thereof; and, producing a molded article of the heat-resistant resin in which the annealed stainless-steel fibers are dispersed.

Abstract: A cold rolled and hardened martensitic austenitic stainless steel strip for flapper valves in compressors is made from steel combining, in weight %(wt. %), the following elements: C: 0.3-0.5, Si: 0.2-0.8, Mn: 0.2-1.0, Cr: 12.0-15.0, Mo: 0.50-2.00, N: 0.02-0.15, and V: 0.01-0.20. The steel strip has a matrix consisting of tempered martensite and between 5 and 15 volume % austenite and a tensile strength (Rm) of 1970-2300 MPa. The steel strip has a thickness of 0.07-3 mm and a width of ?500 mm.

Abstract: A method of manufacturing a steam turbine rotor which includes an ultra-high temperature side portion in which ultra-high temperature steam flows and a high temperature side portion in which high temperature steam flows, the manufacturing method including the steps of: preparing a first electrode having a chemical composition corresponding to a chemical composition of a heat resistant alloy making up the ultra-high temperature side portion and a second electrode having a chemical composition corresponding to a chemical composition of the high temperature side portion; tentatively joining together joints of the electrodes, with the joints of the electrodes made smaller in cross sectional area than other electrode portions; subjecting the tentatively joined first and second electrodes to an ESR process to obtain an ESR ingot and forging the ingot into a shape of a rotor to obtain a rotor forging; and heat-treating the rotor forging to obtain a rotor blank and manufacturing the steam turbine rotor from the rotor

Abstract: The present disclosure is directed and formulations and methods to provide alloys having relative high strength and ductility. The alloys may be provided in seamless tubular form and characterized by their particular alloy chemistries and identifiable crystalline grain size morphology. The alloys are such that they include boride pinning phases. In what is termed a Class 1 Steel the alloys indicate tensile strengths of 700 MPa to 1400 MPa and elongations of 10-70%. Class 2 Steel indicates tensile strengths of 800 MPa to 1800 MPa and elongations of 5-65%. Class 3 Steel indicates tensile strengths of 1000 MPa to 2000 MPa and elongations of 0.5-15%.

Abstract: A cost effective ferritic stainless steel exhibits improved corrosion resistance comparable to that observed on Type 304L steel. The ferritic stainless steel is substantially nickel-free, dual stabilized with titanium and columbium, and contains chromium, copper, and molybdenum.

Abstract: A stainless steel material having compositions which contain on the basis of percent by mass, C from 0.04 to 0.12%, Ni from 0 (including a case of no addition) to 5.0%, Cr from 12.0 to 17.0%, N from 0.0 to 0.10%, Si from 0.2 to 2.0%, Mn at 2.0% or less, Cu from 0.0 to 2.0%, P at 0.06% or less, S at 0.006% or less, with residue being Fe and unavoidable impurities. Further, a parent phase has any one of a single phase structure of ferrite phase or martensite phase and a diploid phase structure of ferrite phase and martensite phase. An end of the base material is melt-welded as a joint to form a pipe. The parent phase is provided with carbide uniformly separated at grain boundaries and within grains, with a dissolved amount of C being 0.03% by mass or less.

Abstract: A hot-rolled stainless steel sheet having excellent hardness and low-temperature impact properties, in which a ferrite is formed with martensite as a matrix structure, is manufactured by a steel manufacturing process, a continuous casting process, and a hot-rolling process. The hot-rolled stainless steel sheet comprises C, N, Si, Mn, Cr, Ni, Ti, Nb, Mo, and the remainder being Fe and other inevitable impurities, wherein C is 0.01 to 0.03 wt %, Cr is 11 to 14 wt %, Ti is 0.1 to 0.2 wt %, and Nb is 0.1 to 0.2 wt %. The ferrite stability (FS) expressed by the following [formula 1] is 5 to 50, and a ferrite is formed with martensite as a matrix structure. [Formula 1] 4 FS=?215?619C?16.6Mn+23.7Cr?36.8Ni+42.2Mo+96.2Ti+67Nb?237N+17.2Si, wherein the numerical value of each component described in [Formula 1] denotes the content (wt %) of each component.

Abstract: The invention relates to an austenitic stainless steel with improved pitting corrosion resistance and improved strength. The stainless steel contains in weight % less than 0, % carbon (C), 0,2-0,6% silicon (Si), 1.0-2.0% manganese (Mn), 19.0-21.0% chromium (Cr), 7.5-9.5% nickel (Ni), 0.4-1.4% molybdenum (Mo), less than 1.0% copper (Cu), 0.10-0.25% nitrogen (N), optionally less than 1.0% cobalt (Co), optionally less than 0.006% boron (B), and the rest being iron (Fe) and inevitable impurities.

Abstract: This disclosure relates to elongated needle assemblies and methods of their manufacture and use.

Abstract: In an exhaust gas purification apparatus or other apparatuses that are supplied with ammonia generated from a urea aqueous solution and causes selective reduction and purification of nitride oxides, a shot peening treatment is applied to a welded portion of its exhaust pipe which is made of a ferritic stainless steel plate and through which exhaust gas containing ammonia and hydrogen passes. By shot peening the welded portion of the exhaust pipe, a tensile residual stress in the welded portion of the exhaust pipe can be replaced with a compressive residual stress, and further the diameter of metal crystal grains in the welded portion can be reduced. In this way, the durability of the exhaust pipe can be improved.

Abstract: There is provided a heat resistant ferritic steel including a base material including, by mass percent, C: 0.01 to 0.3%, Si: 0.01 to 2%, Mn: 0.01 to 2%, P: at most 0.10%, S: at most 0.03%, Cr: 7.5 to 14.0%, sol.Al: at most 0.3%, and N: 0.005 to 0.15%, the balance being Fe and impurities, and an oxide film that is formed on the base material and contains 25 to 97% of Fe and 3 to 75% of Cr. This heat resistant ferritic steel is excellent in photoselective absorptivity and oxidation resistance.

Abstract: The present invention relates to duplex ferritic austenitic stainless steel for the use chemical industry for nitric acid environments wherein good uniform corrosion resistance and high strength are required. The microstructure of the stainless steel has 35-65 volume % of ferrite, preferably 45-55 volume % of ferrite, the balance being austenite. The chemical composition contains less than 0.03 weight % carbon, less than 1 weight % silicon, less than 3 weight % manganese, 26-29.5 weight % chromium, 5-8.5 weight % nickel, 1-3 weight % molybdenum, 0.25-0.35 weight % nitrogen, 1-3 weight % copper, the rest being iron and inevitable impurities occurring in stainless steels.

Abstract: There is provided an austenitic stainless steel tube containing, by mass percent, 14 to 28% of Cr and 6 to 30% of Ni, wherein the steel tube has a metal micro-structure, in which an average dislocation density, which is determined by XRD measurement using a Co tube, is 3.0×1014/m2 or higher, on the inner surface side of the steel tube. The crystal grain size of the steel tube is preferably 50 ?m or smaller. The steel tube of the present invention is suitable as a steel tube used in power-generating plants.

Abstract: The disclosure provides a creep resistant alloy having an overall composition comprised of iron, chromium, molybdenum, carbon, manganese, silicon, nickel, vanadium, niobium, nitrogen, tungsten, cobalt, tantalum, boron, copper, and potentially additional elements. In an embodiment, the creep resistant alloy has a molybdenum equivalent Mo(eq) from 1.475 to 1.700 wt. % and a quantity (C+N) from 0.145 to 0.205. The overall composition ameliorates sources of microstructural instability such as coarsening of M23C6carbides and MX precipitates, and mitigates or eliminates Laves and Z-phase formation. A creep resistant martensitic steel may be fabricated by preparing a melt comprised of the overall composition followed by at least austenizing and tempering. The creep resistant alloy exhibits improved high-temperature creep strength in the temperature environment of around 650° C.

Abstract: There is provided a flux-cored wire containing flux within a stainless steel or mild steel outer cover for use in stainless steel welding and gas-shielded arc welding using a shielding gas. The flux-cored wire contains, based on the total mass of the flux-cored wire, predetermined amounts of C, Si, Mn, P, S, Cr, Ti, and O. The remainder are Fe and incidental impurities. The shielding gas is pure Ar gas.

Abstract: The present invention is directed to a stainless steel brake disc which is excellent in toughness, corrosion resistance, and wear resistance, and comprises, in % by mass, 0.030 to 0.080% of C, 0.05% to 1.0% of Si, 1.0 to 1.5% of Mn, 0.035% or less of P, 0.015% or less of S, 11.0 to 14.0% of Cr, 0.01 to 0.50% of Ni, 0.001 to 0.15% of V, less than 0.1% of Nb, 0.05% or less of Ti, 0.05% or less of Zr, 0.05% or less of Al, 0.015 to 0.060% of N, 0.0002% or more and 0.0050% or less of B, and 0.0080% or less of O, wherein an AT value of equation 1 is 0.055 to 0.090, equation 2 is satisfied, a ferrite phase fraction, in which an IQ value of an EBSD pattern is 4,000 or more, is 1% to 15%, a Charpy impact value is 50 J/cm2 or more, and hardness is 32 to 38 HRC. C+0.8(N?B)??(1) PV=1.2Ti+0.8Zr+Nb+1.1Al+O?0.

Abstract: A duplex stainless steel containing, by mass %: C: not more than 0.03%, Si: not more than 0.3%, Mn: not more than 3.0%, P: not more than 0.040%, S: not more than 0.008%, Cu: 0.2 to 2.0%, Ni: 5.0 to 6.5%, Cr: 23.0 to 27.0%, Mo: 2.5 to 3.5%, W: 1.5 to 4.0%, and N: 0.24 to 0.40%, the balance being Fe and impurities, wherein a ? phase susceptibility index X (=2.2Si+0.5Cu+2.0Ni+Cr+4.2Mo+0.2W) is not more than 52.0; a strength index Y (=Cr+1.5Mo+10N+3.5W) is not less than 40.5; and a pitting resistance equivalent PREW (=Cr+3.3(Mo+0.5W)+16N) is not less than 40. This duplex stainless steel is excellent in corrosion resistance and embrittlement cracking resistance.

Abstract: The invention relates to a spacer (8) to be sandwiched between first and second glass sheets (5) of a vacuum glazing panel, such as to maintain a first space between the glass sheets, which space forms a first cavity (4) under a vacuum of less than 1 mbar, a sealing joint (1) being positioned on the periphery of the glass sheets enclosing the first cavity. According to the invention, one such spacer (8) comprises cold-worked austenitic stainless steel.

Abstract: A nitrogen-rich two-phase stainless steel that has corrosion resistance equal to that of standard type of two-phase stainless steel and is not susceptible to corrosion in a welding heat-affected part, wherein the austenite phase area ratio is 40-70%, the PI value expressed by formula (1) is 30-38, the NI value expressed by formula (2) is 100-140, and the ?pre expressed by formula (3) is 1350-1450. (1) PI=Cr+3.3Mo+16N (2) NI=(Cr+Mo)/N.

Abstract: The chemical composition of a stainless steel in accordance with the present invention consists of C: not more than 0.05%, Si: not more than 0.5%, Mn: 0.01 to 0.5%, P: not more than 0.04%, S: not more than 0.01%, Cr: more than 16.0 and not more than 18.0%, Ni: more than 4.0 and not more than 5.6%, Mo: 1.6 to 4.0%, Cu: 1.5 to 3.0%, Al: 0.001 to 0.10%, and N: not more than 0.050%, the balance being Fe and impurities, and satisfies Formulas (1) and (2). Also, the micro-structure thereof contains a martensitic phase and a ferritic phase having a volume ratio of 10 to 40%, and the ferritic phase distribution ratio is higher than 85%. Cr+Cu+Ni+Mo ?25.5??(1) ?8 ?30(C+N)+0.5Mn+Ni+Cu/2+8.2?1.

Abstract: The present invention provides a lean duplex stainless steel able to suppress the drop in corrosion resistance and toughness of a weld heat affected zone comprising, by mass %, C: 0.06% or less, Si: 0.1 to 1.5%, Mn: 2.0 to 4.0%, P: 0.05% or less, S: 0.005% or less, Cr: 19.0 to 23.0%, Ni: 1.0 to 4.0%, Mo: 1.0% or less, Cu: 0.1 to 3.0%, V: 0.05 to 0.5%, Al: 0.003 to 0.050%, O: 0.007% or less, N: 0.10 to 0.25%, and Ti: 0.05% or less, having a balance of Fe and unavoidable impurities. An Md30 value is 80 or less, an Ni-bal is ?7.1 to 4, an austenite phase area percentage is 40 to 70%, and a 2×Ni+Cu is 3.5 or more: Md30=551?462×(C+N)?9.2×Si?8.1×Mn?29×(Ni+Cu)?13.7×Cr?18.5×Mo?68×Nb; Ni-bal=(Ni+0.5Mn+0.5Cu+30C+30N)?1.1(Cr+1.5Si+Mo+W)+8.2 and N(%)?0.37+0.03×(Ni-bal).

Abstract: A getter structure and method wherein a layer of seed material is deposited on a predetermined region of a surface of a structure under conditions to form a plurality of nucleation sites on a surface of the structure. The nucleation sites have an average height over the surface area of the predetermined region of less than one molecule thick. Subsequently a getter material is deposited over the surface to form a plurality of getter material members projecting outwardly from the nucleation sites.

Abstract: The present invention relates to a cast steel alloy for producing cast parts with ferritic structure, wherein the alloy contains iron (Fe), carbon (C), chromium (Cr) and molybdenum (Mo). An increased resistance to intercrystalline corrosion is obtained when the alloy additionally contains titanium (Ti) and niobium (Nb).

Abstract: A heat-resistant, ferritic cast steel having excellent melt flowability, gas defect resistance, toughness and machinability, which has a composition comprising by mass, C: 0.32-0.45%, Si: 0.85% or less, Mn: 0.15-2%, Ni: 1.5% or less, Cr: 16-23%, Nb: 3.2-4.5%, Nb/C: 9-11.5, N: 0.15% or less, S: (Nb/20?0.1) to 0.2%, W and/or Mo: 3.2% or less in total (W+Mo), the balance being Fe and inevitable impurities, and a structure in which the area ratio of a eutectic (?+NbC) phase of ? ferrite and Nb carbide (NbC) is 60-80%, and the area ratio of manganese chromium sulfide (MnCr)S is 0.2-1.2%, and an exhaust member made thereof.

Abstract: A method of processing a metal alloy includes heating to a temperature in a working temperature range from a recrystallization temperature of the metal alloy to a temperature less than an incipient melting temperature of the metal alloy, and working the alloy. At least a surface region is heated to a temperature in the working temperature range. The surface region is maintained within the working temperature range for a period of time to recrystallize the surface region of the metal alloy, and the alloy is cooled so as to minimize grain growth. In embodiments including superaustenitic and austenitic stainless steel alloys, process temperatures and times are selected to avoid precipitation of deleterious intermetallic sigma-phase. A hot worked superaustenitic stainless steel alloy having equiaxed grains throughout the alloy is also disclosed.

Abstract: Provided a build-up welding material which contains C: 0.2 to 1.5 mass %, Si: 0.5 to 2 mass %, Mn: 0.5 to 2 mass %, Cr: 20 to 40 mass %, Mo: 2 to 6 mass %, Ni: 0.5 to 6 mass %, V: 1 to 5 mass % and W: 0.5 to 5 mass %, with the balance being Fe and unavoidable impurities.

Abstract: A dual phase stainless steel pipe includes tensile yield strength YSLT of 689.1 MPa to 1000.5 MPa in a pipe axis direction of the dual phase stainless steel pipe, in which the tensile yield strength YSLT, a compressive yield strength YSLC in the pipe axis direction, a tensile yield strength YSCT in a pipe circumferential direction of the dual phase stainless steel pipe, and a compressive yield strength YSCC in the pipe circumferential direction satisfy all Expressions (1) to (4), 0.90?YSLC/YSLT?1.11??(1) 0.90?YSCC/YSCT?1.11??(2) 0.90?YSCC/YSLT?1.11??(3) 0.90?YSCT/YSLT?1.11??(4).

Abstract: A steel material has a chemical composition containing, by mass %, C: 0.005% or more and 0.06% or less, Si: 0.05% or more and 0.5% or less, Mn: 0.2% or more and 1.8% or less, Cr: 15.5% or more and 18.0% or less, Ni: 1.5% or more and 5.0% or less, V: 0.02% or more and 0.2% or less, Al: 0.002% or more and 0.05% or less, N: 0.01% or more and 0.15% or less, O: 0.006% or less, and further contains one or more of Mo: 1.0% or more and 3.5% or less, W: 3.0% or less and Cu: 3.5% or less, in which Cr+0.65Ni+0.60Mo+0.30W+0.55Cu-20C?19.5 and Cr+Mo+0.50W+0.30Si-43.5C-0.4Mn—Ni-0.3Cu-9N?11.5 are satisfied, is made into a seamless steel tube by performing heating and hot rolling.

Abstract: The invention concerns steels having excellent resistance over time, in a corrosive atmosphere due to oxidizing environments such as, for example, fumes or water vapor, under high pressure and/or temperature. The invention concerns a steel composition for special applications, said composition containing, by weight, about 1.8 to 11% of chromium (and preferably between about 2.3 and 10% of chromium), less than 1% of silicon, and between 0.20 and 0.45% of manganese. It has been found that it is possible to adjust the contents of the composition based on a predetermined model, selected to obtain substantially optimal properties with respect to corrosion in specific conditions of high temperature performances. Said model can involve as additive of as residue at least one element selected among molybdenum, tungsten, cobalt, and nickel.

Abstract: The present invention is directed to a heat-resistant austenitic stainless steel sheet comprising, by mass %, C: 0.03% to 0.06%, N: 0.1% to 0.3%, Si: 1% or less Mn: 3% or less, P: 0.04% or less, S: 0.03% or less, Ni: 5 to 12%, Cr: 15 to 20%, Al: 0.01% to 0.1%, Nb: 0.05% to 0.3%, V: 0.05% to 0.30%, Ti: 0.03% or less, (Nb+V)/(C+N):2 or less and further a balance of Fe and unavoidable impurities, and wherein an amount of precipitates mainly comprised of carbonitrides is 1% or less.

Abstract: Ferritic stainless steel sheet for an exhaust part which has little deterioration in strength even if undergoing long term heat history and is low in cost, excellent in heat resistance and workability characterized by containing, characterized by containing, by mass %, C: less than 0.010%, N: 0.020% or less, Si: over 0.1% to 2.0%, Mn: 2.0% or less, Cr: 12.0 to 25.0%, Cu: over 0.9 to 2%, Ti: 0.05 to 0.3%, Nb: 0.001 to 0.1%, Al: 1.0% or less, and B: 0.0003 to 0.003%, having a Cu/(Ti+Nb) of 5 or more, and having a balance of Fe and unavoidable impurities.