Abstract: The present invention provides stainless steel foil for flexible display use which enables fabrication of a TFT substrate for display use which is superior in shape recovery after being rolled up or bent and which is high in surface flatness and is characterized by having a thickness of 20 ?m to 200 ?m, a surface roughness Ra of 50 nm or less, and a shape recovery of a distortion angle of 10° or less after being wound around a 30 mm diameter cylinder.

Abstract: A metallic glass laminate of the present invention is characterized in that a metallic glass layer of amorphous phase is formed on the substrate surface, and there is no continuous pore (pinhole) through the metallic glass layer. The metallic glass laminate is preferably obtained by solidification and lamination of at least part of the metallic glass powder in the molten state or in the supercooled liquid state on the substrate surface. Because of the dense metallic glass layer of homogenous amorphous phase, the functionalities of metallic glass such as corrosion resistance and wear resistance can be satisfactorily provided. A thick and a large-area metallic glass layer can be formed. The metallic glass layer can also be formed into various shapes within the supercooled liquid temperature range. In addition, a metallic glass bulk can be obtained by removing the substrate.

Abstract: The present disclosure is generally directed to a personal grooming product or device (e.g., foil shaver, rotary shaver, etc.) having a metal coating on one or more surfaces thereof, the grooming product being designed for contacting the skin (e.g., the human hand or face, or the skin of an animal, such as during the act of pet grooming). More specifically, the present disclosure is directed to a personal grooming product or device having a layer of some measurable thickness on such a surface, wherein the layer comprises or contains a tarnish resistant, hypoallergenic and/or antimicrobial silver-containing alloy.

Abstract: A sliding device 1 is constituted of a swash plate 3 including a first sliding surface 3A and a semispherical shoe 4 sliding with the swash plate 3. The swash plate 3 is constituted of a base material 3B of high strength brass containing Mn and Si, and very small granular Mn—Si compounds 6 are exposed on an inside of the base material 3B and on the first sliding surface 3A (surface of the base material 3B). The above described swash plate 3 increases in exposure amount of the Mn—Si compounds 6 exposed on the first sliding surface 3A by applying etching to the base material 3B after cutting the base material 3B. The sliding device 1 is favorable in seizure resistance and has a low manufacturing cost as compared with conventional sliding devices.

Abstract: A method for creating a nanostructure according to one embodiment includes depositing material in a template for forming an array of nanocables; removing only a portion of the template such that the template forms an insulating layer between the nanocables; and forming at least one layer over the nanocables. A nanostructure according to one embodiment includes a nanocable having a roughened outer surface and a solid core. A nanostructure according to one embodiment includes an array of nanocables each having a roughened outer surface and a solid core, the roughened outer surface including reflective cavities; and at least one layer formed over the roughened outer surfaces of the nanocables, the at least one layer creating a photovoltaically active p-n junction. Additional systems and methods are also presented.

Abstract: Vapor plasma deposition of titanium (Ti) metal onto a substrate forms a structured surface that exhibits enhanced cell attachment properties. Initially deposited round nanoparticulate surface structures develop tentacles with a spine or thorn-like appearance upon continued deposition under special conditions. The density and size of the formed spinulose particles can be controlled by timing the deposition intervals. A significant increase in osteoblast, fibroblast and endothelial cell attachment is observed on Ti spinulose surfaces compared to attachment on nanoparticulate surfaces lacking spinulous nanostructure.

Abstract: It is an object of the present invention to provide a Ag—Pd—Cu—Ge type silver alloy which can form a reflective electrode film having such two characteristics that it is very reduced in the lowering of reflectance caused by thermal deterioration and has resistant to yellowing caused by sulfurization even after a heating step in a process of producing a color liquid crystal display. The silver alloy according to the present invention includes a composition containing at least four elements including Ag as its major component, 0.10 to 2.89 wt % of Pd, 0.10 to 2.89 wt % of Cu and 0.01 to 1.50 wt % of Ge, and the total amount of Pd, Cu and Ge is 0.21 to 3.00 wt %.

Abstract: Methods of forming hydrophobic surfaces or structures include spraying droplets of a material onto features on a surface of a substrate and at least partially coating the features with a material formed from the droplets. Methods of forming fuel or electrolytic cells include forming a plurality of features in a surface of a conductive plate within a channel therein, and configuring the surface of the conductive plate within the channel to be hydrophobic. Additional methods of forming fuel or electrolytic cells include forming a substrate having a surface comprising at least one channel therein, forming a plurality of features on a surface of the substrate within the at least one channel, spraying droplets of a material onto the substrate, and at least partially coating the features with a metal layer formed from the droplets. Hydrophobic structures such as, for example, conductive electrodes for fuel and electrolytic cells are fabricated using such methods.

Abstract: Methods and compositions relating to the preparation of structurally and compositionally modulated composite surfaces that can potentially reduce friction and increase resistance to wear and scuffing in rolling, rotating and sliding bearing applications. Preparation of nano-to-micro size pores, holes, or dimples on a given solid surface and filling them with soft or hard coatings at desired thickness to achieve such properties.

Abstract: A magnesium alloy material such as a magnesium alloy cast material or a magnesium alloy rolled material, excellent in mechanical characteristics and surface precision, a producing method capable of stably producing such material, a magnesium alloy formed article utilizing the rolled material, and a producing method therefor. The magnesium material producing method includes a melting step of melting a magnesium alloy in a melting furnace to obtain a molten metal, a transfer step of transferring the molten metal from the melting furnace to a molten metal reservoir, and a casting step of supplying a movable mold with the molten metal from the molten metal reservoir, through a pouring gate, and solidifying the molten metal to continuously produce a cast material. Parts are formed by a low-oxygen material having an oxygen content of 20 mass % or less. The cast material is given a thickness of from 0.1 to 10 mm.

Abstract: Provided is a core metal including a shaft through-hole allowing a shaft to be inserted thereinto, and a resin locking portion allowing a resin to be locked and fixed, the shaft through-hole having a thicker periphery formed on a periphery of a prepared hole allowing the shaft to be inserted thereinto so as to project on any one of or both a front surface and a back surface of the metal material. The prepared hole and the thicker periphery are molded by subjecting a flat metal material automatically transferred with use of a press machine to drawing, drilling, and thickening.

Abstract: The invention relates to a microperforated metal foil and to a process for the preparation thereof which is characterized in that a self-supporting metal foil is perforated with a needle-punching machine.

Abstract: One embodiment includes non-catalyticly forming a nanowire on a substrate from an organometallic vapor without application of any type of reduction agent. The nanowire is grown during this formation in a direction away from the substrate and is freestanding during growth. The nanowire has a first dimension of 500 nanometers or less and a second dimension extending from the substrate to a free end of the nanowire at least 10 times greater than the first dimension. In one form, the organometallic vapor includes copper and the nanowire essentially consists of elemental copper, a copper alloy, or oxide of copper. Alternatively or additionally, the nanowire is of a monocrystalline structure.

Abstract: A plated material 5, containing: on a conductive substrate 1, an underlayer 2 composed of nickel and the like; an intermediate layer 3 composed of Cu or a Cu alloy being provided thereon; and an outermost layer 4 composed of a Cu—Sn intermetallic compound being provided thereon; and an electric or electronic part using the same.

Abstract: A crystallographically textured metallic substrate includes surfaces for connection and for receiving a thin layer deposit, and is made up of an alloy presenting a cubic crystalline system with centered faces and a predominantly cubic crystallographic texture {100}<001>, the receiving surface including grains mainly presenting crystallographic planes {100} parallel to the receiving surface. The alloy is iron-nickel with weight % relative to total weight: Ni?30%, Cu?15%, Cr?15%, Co?12%, Mn?5%, S<0.0007%, P<0.003%, B<0.0005%, Pb<0.0001%, and in the alloy: 34%?(Ni+Cr+Cu/2+Co/2+Mn). The alloy includes up to 1% in weight of one or several deoxidizing elements chosen among silicon, magnesium, aluminium and calcium, the rest of the elements in the alloy being iron and impurities.

Abstract: Refurbishing used or damaged engineering components is performed using a subtractive surface engineering process to remove material from worn or damaged critical surfaces. The method involves initially performing the process on the component to remove a first quantity of material from the surfaces, inspecting the surface of the component to determine the extent of damage and subsequently further performing the process to remove a further quantity of material if necessary.

Abstract: To produce an ultra-thin copper foil with a carrier foil that microscopic crystal grains can be deposited without being affected by the surface roughness of a carrier foil, etching can be performed until an ultra-fine width such that line/space is 15 mum or less, and the microscopic line and a wiring board have large peel strength even after line of 15 mum is etched. An ultra-thin copper foil wherein a carrier foil, a peeling layer, an ultra-thin copper foil are laminated in this order, the ultra-thin copper foil (before roughening treatment is performed) is an electrolytic copper foil that surface roughness of 2.5 mum as ten point height of roughness profile, and the minimum distance between peaks of salients of a based material is 5 mum or more. Moreover, the surface of the ultra-thin copper foil is performed roughening treatment.

Abstract: An copper alloy strip material for electrical/electronic components according to the present invention is characterized in that such the copper alloy strip material for electrical/electronic components includes: Ni as between 1.5 mass % and 4.0 mass %; Si as between 0.3 mass % and 1.5 mass %; and the balance being Cu and unavoidable impurities, wherein a mean roughness Ra of a surface roughness is not larger than 0.3 ?m regarding the strip in a direction as right angle to a direction of a rolling therefor, a maximum height Ry thereof is not higher than 3.0 ?m regarding the same therein, and there is positioned a peak position regarding a frequency curve, that represents a concave component of the surface roughness and/or a convex component thereof, at the plus side (the side for the convex component) comparing to an average value of the curve for meaning the surface roughness.

Abstract: Provided are a steel plate for a refrigerator door and a method for manufacturing the steel plate. The steel plate includes a stainless steel plate provided on and forming an exterior of a refrigerator door with a vertical length of 1250 mm or more. The stainless steel plate surface is processed to form a finished texture oriented in a horizontal direction with respect to the refrigerator door. The method includes cutting a section from a rolled stainless steel plate base material corresponding in length to a length of a refrigerator door, rotating the cut section by a 90° angle, and surface processing through grinding a surface of the cut section in a direction perpendicular to a rolled direction thereof.

Abstract: A hub ring and/or an outer ring constituting a bearing device for a wheel, which is formed of a steel which contains 0.45 to 0.70 mass % of C and at least one of V, Nb and Ti in a total amount of 0.3 mass % or less, wherein a micro structure of a part being not surface-hardening-treated contains a ferrite in 15 to 30 area % and contains a particulate ferrite.

Abstract: The present invention relates to the use of the A286 alloy grade for the manufacture of a sheet, optionally surfaced, making it possible to obtain a conducting plate of mono polar or bipolar type for a fuel cell element. The invention also relates to this optional surface treatment process, which comprises a cold-rolling step followed by a continuous annealing step in an oxidizing atmosphere and by an acid pickling step.

Abstract: Provided are a metal layer laminate that includes a roughened metal surface layer having a surface profile capable of strongly adhering to resin materials even when the surface roughness is small, and a simple method for producing a metal layer laminate having good adhesion to resin materials such as a resin substrate for a metal layer and an insulating resin film formed on the surface of a metal wiring portion. The metal layer laminate includes a metal layer, a resin thin film, and a roughened metal surface layer, wherein the resin thin film and the roughened metal surface layer are formed on the surface of the metal layer, a fractal-shaped interface structure appears between the resin thin film and the roughened metal surface layer, when the metal layer laminate is cut in a normal direction, and the interface structure has a fractal dimension of 1.05 to 1.

Abstract: The present invention provides an aluminum alloy sheet for press forming, having the crystallo-graphic texture in which the orientation density of CR orientation ({001}<520>) is higher than that of any orientation other than the CR orientation. The orientation density of the CR orientation is preferably 10 or more (random ratio). The orientation densities of all orientations other than the CR orientation are preferably less than 10. The aluminum alloy sheet is preferably made of an Al—Mg—Si alloy.

Abstract: The present invention provides a metal clad laminate or a resin coated metal foil having a metal foil whose both surfaces are not substantially roughening-treated and an insulating resin composition layer using generally used insulating resin, and a printed wiring board and a manufacturing method thereof, in which the metal clad laminate or the resin coated metal foil is used, the reliability and circuit formability are high, and the conductor loss is extremely low.

Abstract: The object is to provide copper foil of high adhesion even when the roughness Rz of a nodular surface of the copper foil is low, and a method of manufacturing the copper foil. To achieve this object, there is adopted a copper foil which is characterized in that an area coefficient C(S), which is defined by A(S)/B(S) from a three-dimensional surface area A(S), which is obtained by performing three-dimensional measurement of a surface area of a nodular surface of a copper foil sample S under a laser microscope, and from a measuring region area B(S), which is an area of a measuring region of the three-dimensional surface area A(S), and a roughness Rz(S) of a nodular surface of the copper foil sample S, which is measured by a stylus-type roughness meter, have a relationship of equation (1) below, and in that the roughness Rz(S) is 1.0 ?m to 3.0 ?m, 0.5×Rz(S)+0.5?C(S)??(1) where Rz(S) is a numerical value represented by ?m.

Abstract: The present invention provides a metal clad laminate or a resin coated metal foil having a metal foil whose both surfaces are not substantially roughening-treated and an insulating resin composition layer using generally used insulating resin, and a printed wiring board and a manufacturing method thereof, in which the metal clad laminate or the resin coated metal foil is used, the reliability and circuit formability are high, and the conductor loss is extremely low.

Abstract: A coating system is used on an engine component having an outer surface configured to be exposed to a first plurality of particles impinging against the outer surface at an angle within a first angle range and a second plurality of particles impinging at an angle in a second angle range. The system includes a bond layer overlying the engine component outer surface, a first erosion-resistant layer comprising a first material that is more resistant to erosion by particles impinging the component outer surface at an angle within the first angle range than by particles impinging within the second angle range, an interlayer overlying the first erosion-resistant layer, and a second erosion-resistant layer comprising a second material that is more resistant to erosion by particles impinging the component outer surface at an angle within the second angle range than by particles impinging within the first angle range.

Abstract: An iron-based sintered body with a rustproof function comprises a layer containing 0.01 to 5 at % of indium on the surface of the iron-based sintered body, or an iron-based sintered body with a rustproof function contains 0.01 to 5 at % of indium throughout the sintered body, and the iron-based sintered body having iron as its principal component is manufactured by performing sintering in a gas atmosphere containing indium vapor or indium. Thereby obtained is an iron-based sintered body, as well as the manufacturing method thereof, capable of easily improving the rustproof effect without having to hardly change the conventional process.

Abstract: A superconducting tape is disclosed, including a substrate having a first surface and a second surface opposite the first surface, the substrate including a plurality of indicia provided on the first surface spaced apart along a length of the substrate; and a superconductor layer overlying the second surface. Also disclosed are components incorporating superconducting tapes, methods for manufacturing same, and methods for using same.

Abstract: Hollow, cylindrical, seamless metal master for producing seamless diffuser sheets of preselected length and width. Additional aspects of the invention include a hollow cylindrical seamless invertable elastomeric master and method of making the same and an apparatus and process for effecting variable diffuser recording in photosensitive medium.

Abstract: A faux stainless steel sheet material of ferrous carbon sheet steel core is polished in a polishing apparatus comprising a series of commercially available polishing heads each of which utilizes a polishing belt of a predetermined grit mesh and size, belt speed, belt oscillations transverse to the sheet steel conveyed direction, at predetermined conveyance rate of the sheet steel and pressure. The polishing heads scratch the material surface wherein the scratches mimic a stainless steel finish such as #4 stainless steel finish (80 mesh). An example and sample are described in one embodiment of the invention.

Abstract: An electrode surface coating and method for manufacturing the electrode surface coating comprising a conductive substrate; and one or more surface coatings comprising one or more of the following metals titanium, niobium, tantalum, ruthenium, rhodium, iridium, palladium, or gold, or an alloy of two or more metals, or a combination of two or more alloys or metal layers thereof having an increase in the surface area of 5 times to 500 times of the corresponding surface area resulting from the basic geometric shape.

Abstract: A metallic part made from a metallic plate by a punching process, includes a highly reflective first surface, a second surface opposite to the first surface, and a side surface connecting the first surface to the second surface. The first surface is high reflective. The first surface and the side surface cooperatively form a sharp-cornered edge in a boundary thereof. The side surface has a plurality of milling traces.

Abstract: A surface treated copper foil with improved adhesion to the insulating resin of a copper-clad laminate for higher frequency applications contains a copper foil provided with a heat-resistant layer and an olefin-based silane coupling agent layer sequentially on at least one side thereof. An anticorrosive treatment may be performed after the heat resistance treatment. The copper foil is preferably an electrolytic copper foil, and these layers can be provided on the S side and/or the M side thereof. The copper foil has an adequate adhesive strength, even without the roughening treatment that has been performed in the past. A film of zinc, zinc-tin, zinc-nickel, zinc-cobalt, copper-zinc, copper-nickel-cobalt, or nickel-cobalt can be used favorably as the heat-resistant layer, and a film that has undergone a zinc-chromate or a chromate treatment can be used favorably as the anticorrosive layer.

Abstract: A strip for the production of a substrate for lithographic printing plates consisting of aluminum or an aluminum alloy and has at least to some extent a microcrystalline surface layer as a result of hot and/or cold roll passes. When analyzed in a two-dimensional microprobe analysis according to the mapping method of a surface region of the microcrystalline surface of the strip, the surface portion having an intensity ratio I/Ibulk(avg) of greater than 3 in the spectral range of the K?1 line of the X-ray emission spectrum of oxygen of the measured microcrystalline surface layer is less than 10%, preferably less than 7%, wherein, during the two-dimensional microprobe analysis, an excitation voltage of 15 kV, a beam current of 50 nA and a beam cross section of 1 ?m is used with a step size of 16.75 ?m for the electron beam.

Abstract: The present invention provides personal ornaments having as an outermost layer a white ornamental coating film having platinum or a platinum alloy formed by dry-plating, including: an ornament base article made of a metal or ceramic, an underlayer formed on the surface on the base article, an abrasion resistant layer formed on the surface of the underlayer by dry-plating, and an ornamental coating layer having platinum or platinum alloy formed on the surface of the abrasion resistant layer by dry-plating. Also, the present invention provides personal ornaments having a coloring layer including an abrasion-resistant layer, a mixture layer and an outermost layer, the outermost layer being a white hard coating film having a noble metal or a noble metal alloy formed by dry-plating on the surface of the mixture layer.

Abstract: The metallic luster of a stainless steel material is uniformly controlled by forming minute elevations and depressions on the surface of a stainless steel molding material that has been press-formed or roll-formed.

Abstract: High strength aluminum alloy sheet having superior surface roughening and formability suitable for home electrical appliances and automobile outer panels and other structural materials and a method of production of the same are provided. High strength aluminum alloy sheet having a chemical composition containing Mg: 2.0 to 3.3 mass %, Mn: 0.1 to 0.5 mass %, and Fe: 0.2 to 1.0 mass %, having a balance of unavoidable impurities and Al, and having an Si among the unavoidable impurities of less than 0.20 mass % and having an average circle equivalent diameter of intermetallic compounds of 1 ?m or less, having an area ratio of intermetallic compounds of 1.2% or more, having an average diameter of recrystallized grains of 10 ?m or less, and having a tensile strength of 220 MPa or more.

Abstract: An Au plated film 12 is formed on the surface of a plate-formed metal base 13 composed of a metal less noble than Au, and the product is cut along a planned cutting line 18 reflecting a contour of a desired component, to thereby form a separator 10. Thus-formed separator 10 has the Au plated film 12 formed on the main surface 10a thereof, and has a cutting plane 16 formed as an end face 16 stretched up to the main surface 10a. The metal base 13 exposes in a part of the cutting plane 16, in a width of the exposed region of 1 mm or less. This is successful in providing a metal component for fuel cell which is satisfactory in the corrosion resistance and allows easy fabrication at low costs, a method of manufacturing the same, and also in providing a fuel cell having thus-fabricated metal component for fuel cell.

Abstract: An article has a surface, at least a portion of which has a local radius of curvature of about 1000 nm or less. For example, the article may be a nanoparticle or a surface, a portion of which has a roughness characterized by a radius of curvature of about 1000 nm or less. A monolayer coating disposed on the surface includes a plurality of ligands organized into ordered domains having a characteristic size of less than or about equal to 10 nm.

Abstract: A method of treating the surface of copper is provided to ensure adhesive strength between the surface of copper and an insulating layer without forming irregularities exceeding 1 ?m on the surface of copper and to improve insulation reliability between wirings. A copper whose surface is treated by the above surface treating method is also provided. The method of treating the surface of copper comprises the surface of copper comprising the steps of: forming a metal nobler than copper discretely on the surface of copper; and subsequently oxidizing the surface of copper by using an alkaline solution containing an oxidant.

Abstract: A thermal spray composition and method of deposition for abradable seals for use in gas turbine engines, turbochargers and steam turbines. The thermal spray composition includes a solid lubricant and a ceramic preferably comprising 5 to 60 wt % total of the composition in a ratio of 1:7 to 20:1 of solid lubricant to ceramic, the balance a matrix-forming metal alloy selected from Ni, Co, Cu, Fe and Al and combinations and alloys thereof. The solid lubricant is at least one of hexagonal boron nitride, graphite, calcium fluoride, lithium fluoride, magnesium fluoride, barium fluoride, tungsten disulfide and molybdenum disulfide particles. The ceramic includes at least one of albite, illite, quartz and alumina-silica.

Abstract: A steel product with a high austenite grain coarsening temperature having less than 0.4% carbon, less than 0.06% aluminium, less than 0.01% titanium, less than 0.01% niobium, and less than 0.02% vanadium by weight, and having fine oxide particles containing silicon and iron distributed through the steel microstructure having an average particle size less than 50 nanometers and may be between 5 and 30 nanometers. The steel product may have fine oxide particles distributed through the microstructure capable of restricting ferrite recrystallization for strain levels up to at least 10.0%, for temperatures up to 750° C. with holding times up to 20 minutes. The steel product may be made by continuous casting of steel strip introduced between the casting rolls to form a casting pool of molten carbon steel having a total oxygen content of at least 70 ppm usually less than 250 ppm, and a free oxygen content 20 and 60 ppm, counter rotating the casting rolls.

Abstract: A method of preparing the surface of a porous metal substrate to receive a membrane. The method does not substantially decrease the average bulk porosity of the metal substrate. A hydrogen separation membrane supported on the porous metal substrate. A cold spray is used to reduce surface variance. Exposure to an ion beam may also be used after application on the cold spray to prepare the surface of the substrate for membrane deposition.

Abstract: A thermal module directly press-forged from magnesium alloy is disclosed having a peripheral wall, a recessed chamber surrounded by the peripheral wall. The body is made of magnesium alloy by means of softening magnesium alloy with heat and then press forging softened magnesium alloy into the desired shape.

Abstract: An outwardly grown diffusion aluminide bondcoat is formed on a superalloy substrate and has higher concentrations of Al and Pt and lower concentrations of harmful impurities (e.g. Mo, W, Cr, Ta, S, etc.) at an outermost region of the bondcoat than at an innermost region thereof adjacent the substrate. The bondcoat is pretreated prior to deposition of a ceramic thermal insulative layer in a manner that reduces grain boundary ridges on the outermost bondcoat surface without adversely affecting the outermost region thereof, and then is heat treated to thermally grow a stable alpha alumina layer on the bondcoat prior to deposition of a ceramic layer.

Abstract: A composite casting for a wear resistant surface, comprising a base composed of a ductile material; and a plurality of wear resistant inserts embedded in said base and composed of a carbide-containing wear resistant alloy which after casting is hot strained by forging or rolling, said inserts being arranged in said base rows so that said inserts of each subsequent one of said rows overlap gaps between said inserts of a preceding one of said rows and (or) said inserts should be positioned with their side bases at a degree (relative to the movement of the abrasive material) of no less than 20°, which would prevent the wear of the ductile base of the composite castings.

Abstract: A warm-rolled, annealed, polycrystalline, cube-textured, {100}<100>, FCC-based alloy substrate is characterized by a yield strength greater than 200 MPa and a biaxial texture characterized by a FWHM of less than 15° in all directions.

Abstract: A silicon oxycarbide coating remains hydrophilic for a significantly longer period of time, on the order of several months, when both (i) the coating index of refraction is 1.70 or more and (ii) the coating thickness is 350 ? or more.

Abstract: The metal film of the present invention is a dense film of a single crystal that has very low surface roughness and very good crystal orientation because an arithmetic mean roughness of the surface is not larger than 2 nm and a (111) peak intensity of X-ray diffraction is not less than 20 times the sum of all other peaks. Also the metal oxide film of the present invention is a dense film that includes less oxygen defects and almost no voids therein because a content of a non-oxidized metal is not higher than 1 mole % of a metal component that constitutes the metal oxide and a packing density is 0.98 or higher.