(Co)polymers based on vinyl units and use thereof in electroluminescent devices

Abstract

This invention relates to (co)polymers which contain at least one repeat chain unit of the general formula (1) or (2) and optionally contain repeat units of the general formula (3) 1

Description

[0001] Light-emitting components for electronics and photonics are today mainly developed using inorganic semiconductors, such as gallium arsenide. Punctual display elements may be produced using such substances. Devices of a large area are not possible.

[0002] In addition to semiconductor light emitting diodes, electroluminescent devices based on vapour-deposited low molecular weight organic compounds are also known (U.S. Pat. No. 4,539,507, U.S. Pat. No. 4,769,262, U.S. Pat. No. 5,077,476P). With these materials too, as a consequence of the production process, it is only possible to produce small LEDs. Furthermore, these electroluminescent devices have elevated production costs and only a very short service life.

[0003] Polymers such as poly(p-phenylenes) and poly(p-phenylene-vinylenes) are described as electroluminescent: Adv. Mater. 4 (1992) no. 1; J. Chem. Soc., Chem. Commun. 1992, pages 32-34; Polymer, 1990, volume 31, 1137; Physical Review B, volume 42, no. 18, 11670 or WO 90/13148.

[0004] In contrast to the fully conjugated polymers, non fully conjugated polycondensation products with luminescent structural units are described in electroluminescent devices (Macromol. Chem. Phys. 195, 2023-2037 (1994)).

[0005] The present invention provides polymers for the production of electroluminescent devices, which polymers are based on a well known basic structure, such as polystyrene and polyacrylate, with covalently bonded luminophoric units in the side chains. Due to their simple production process and ready processability, such polymers are of great technical interest with regard to use as electroluminescent materials. Electroluminescent devices containing these (co)polymers are distinguished by elevated light intensities and a broad range of colour hues. The advantages of the (co)polymers according to the invention are, for example, that

[0006] 1. light intensity may purposefully be modified by varying the concentration of luminophore,

[0007] 2. colour hues may be adjusted by combining different monomers containing luminophores,

[0008] 3. the morphology and electrical properties of the polymer layers may be optimised by the incorporation of suitable side chain units.

[0009] The present invention relates to (co)polymers which contain at least one repeat chain unit of the general formula (1) or (2) and optionally contain repeat units of the general formula (3) 2

[0010] in which

[0011] R1, R2 and R3 mutually independently mean hydrogen or C1-C6 alkyl,

[0012] M denotes CN or C1-C30 alkoxycarbonyl, C1-C30 (di)alkyl-aminocarbonyl, C1-C30 alkylcarbonyl, which may each be substituted by hydroxy or C1-C6 alkoxycarbonyl, and furthermore denotes phenyl, naphthyl, anthracenyl, pyridyl or carbazolyl, which may each be substituted by residues from the group halogen, hydroxy, silyl, C1-C30 alkyl, C6-C,8 aryl, C1-C30 alkoxy, C1-C30 alkoxycarbonyl, C1-C30 acyloxy and C1-C30 alkylcarbonyl,

[0013] L1 and L2 mean a photoluminescent residue,

[0014] wherein the proportion of structural units of the formula (3) is 0 to 99.5, preferably 40 to 99.5 mol.% and the proportion of structural units (1) and/or (2) is in each case 0.5 to 100, preferably 0.5 to 60 mol.% and the molar proportions add up to 100%.

[0015] In the above-stated formulae, R1, R2 and R3 mutually independently preferably mean hydrogen, methyl or ethyl.

[0016] M preferably denotes CN or C1-C15 alkoxycarbonyl, C1-C15 (di)alkylaminocarbonyl, C1-C15 alkylcarbonyl, which may each be substituted by hydroxy or methoxycarbonyl, ethoxycarbonyl, n- or iso-propoxycarbonyl, and furthermore denotes phenyl, naphthyl, anthracenyl, pyridyl or carbazolyl, which may each be substituted by residues from the group chlorine, bromine, hydroxy, silyl, C1-C6 alkyl, C1-C6 alkoxy, C1-C6 alkoxycarbonyl, C1-C6 acyloxy and C1-C6 alkylcarbonyl, phenyl optionally substituted by methyl, ethyl, n- or iso-propyl.

[0017] L1 and L2 mutually independently denote a photoluminescent residue which is based on the skeleton of a fluorescent dye which is selected from the group of coumarins of the formula (4) 3

[0018] pyrenes of the formula (5) 4

[0019] 1,8-naphthalimides of the formula (6) 5

[0020] 1,8-naphthaloylene-1,2-benzimidazoles of the formulae (7a) and (7b) 6

[0021] phenothiazines or phenoxazines of the formula (8) 7

[0022] with X1=O or S,

[0023] benzopyrones of the formula (9) 8

[0024] carbazoles, fluorenes, dibenzothiophenes and -furans of the formula (10) 9

[0025] with X2=NR23, CH2, S or O, wherein R23 denotes hydrogen or C1-C6 alkyl, preferably hydrogen or C1-C4 alkyl,

[0026] oxazoles, 1,3,4-oxadiazoles of the formula (11) 10

[0027] with X3=CH or N

[0028] benzoquinolines of the formula (12) 11

[0029] 9,10-bis-(phenylethynyl)anthracenes of the formula (13) 12

[0030] fluorones of the formula (14) 13

[0031] 9,10-diphenylanthracene of the formula (15) 14

[0032] 2-styrylbenzazole of the formula (16) 15

[0033] with X4=O, S, Se or CH2,

[0034] wherein

[0035] R4 denotes hydrogen, C1-C30 alkyl, C6-C18, aryl, C7-C24 aralkyl or C1-C30 alkoxy or 16

[0036] wherein

[0037] R43 and R44 mutually independently denote hydrogen, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, which may each be substituted by hydroxy, amino, carboxy or C1-C4 alkoxycarbonyl, or

[0038] R43 and R44, together with the nitrogen atom to which they are attached, may mean a morpholine, piperidine, pyrrolidine or piperazine ring, which may bear one or two substituents from the group methyl, ethyl and phenyl,

[0039] R5 denotes hydrogen, cyano, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, C1-C30 alkoxy, C2-C12 acyl, C1-C12 alkoxycarbonyl, C1-C12 (di)alkylaminocarbonyl,

[0040] R6 denotes hydrogen, cyano, C1-C30 alkyl, C6-C, aryl, C7-C24 aralkyl, C1-C30 alkoxy or 17

[0041] wherein Z denotes a group OR45 or 18

[0042] R45, R46 and R47 mutually independently denote C1-C30 alkyl, C6-C18 aryl or C7-C24 aralkyl, wherein the aromatic rings may additionally be further substituted by halogen, C1-C6 alkyl, C1-C6 alkoxy,

[0043] R7, R8 and R9 mutually independently mean hydrogen, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, C1-C30 alkoxy, cyano, C2-C12 acyl, C1-C12 alkoxycarbonyl, C1-C12 (di)alkyl-aminocarbonyl or an amino group with one or two C1-C6 alkyl groups,

[0044] R10 means hydrogen, cyano, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, C1-C30 alkoxy, amino, C2-C12 acyl, C1-C12 alkoxycarbonyl, C1-C12 (di)alkylaminocarbonyl,

[0045] R11 denotes hydrogen, halogen, nitro, C1-C4 alkoxycarbonyl, C1-C4 acyl, C8-C24 aralkenyl, unsubstituted amino, or amino identically or differently mono- or disubstituted by C1-C30 alkyl, C6-C18 aryl or C7-C24 aralkyl,

[0046] R11 furthermore denotes morpholinyl, piperidinyl, pyrrolidinyl or piperazinyl, which may bear one or two substituents selected from methyl, ethyl and/or phenyl,

[0047] R12 denotes hydrogen, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl or C1-C30 alkoxy,

[0048] R13 denotes hydrogen, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, C1-C30 alkoxy or 19

[0049] wherein

[0050] R49 and R50 mutually independently denote C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl or

[0051] R49 and R50, together with the nitrogen atom to which they are attached, moreover denote a morpholinyl, piperidinyl, pyrrolidinyl or piperazinyl, which may bear one or two identical or different substituents selected from methyl, ethyl and phenyl,

[0052] R14 and R15 mutually independently mean hydrogen, cyano, halogen, nitro, C1-C30 alkyl, C1-C30 alkoxy, C6-C18 aryl or C7-C24 aralkyl, C1-C12 alkoxycarbonyl, C2-C12 acyl, C1-C12 (di)alkylaminocarbonyl, C1-C6 (di)alkylamino,

[0053] R17 and R23 mutually independently mean hydrogen, C1-C30 alkyl, C6-C18 aryl or C7-C24 aralkyl and

[0054] R16, R18 to R23 and R24 to R40 mutually independently mean hydrogen, cyano, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, C1-C30 alkoxy, an amino group with one or two C1-C6 alkyl groups, unsubstituted amino, C2-C12 acyl, C1-C12 alkoxycarbonyl or C1-C12 (di)alkylaminocarbonyl, wherein the aliphatic carbon chains, such as, for example, alkyl, alkoxy, alkylamino, aralkyl, in the residues R4 to R13, R16 to R40 may be interrupted by one or more, preferably one or two heteroatoms selected from oxygen, nitrogen and sulphur and/or by one or more, preferably one or two, phenylene rings, which may be substituted by C1-C4 alkyl and/or halogen,

[0055] and wherein furthermore the luminophore is attached to the polymer side chains via an oxygen, a hydroxy or carboxy group or a nitrogen of an amino or primary amino on the above-stated substituents.

[0056] In the above-stated residues R4 to R40, at least one aliphatic, aromatic or heterocyclic carbon chain per fluorescent dye bears at least one hydroxy, carboxy or optionally an amino group, preferably hydroxy, by means of which the covalent bond to the monomer is formed by the reaction of these groups with a reactive group (for example halogen) located on the monomer, c.f. production process. In the case of monomer (1), this attachment site is the methylene group on the phenyl ring (—CH2—Cl reacts). In the case of monomer (2), the attachment site is the carbonyl group (via —CO—Cl).

[0057] M in particular denotes phenyl, naphthyl, anthracenyl, pyridyl or carbazolyl, which may each be substituted by hydroxy, silyl, C1-C4 alkyl, optionally by phenyl substituted by methyl, ethyl, n- or iso-propyl, by C1-C4 alkoxy, C1-C6 alkoxycarbonyl, C1-C6 acyloxy or C1-C6 alkylcarbonyl.

[0058] L1 and L2 in particular mutually independently denote a fluorescent dye residue selected from the group of coumarins of the formula (4), pyrenes of the formula (5), 1,8-naphthalimides of the formula (6), 1,8-naphthaloylene-1,2-benzimidazoles of the formula (7), phenothiazines or phenoxazines of the formula (8), carbazoles and fluorenes of the formula (10).

[0059] R4 preferably presents C1-C6 alkyl, C6-C10 aryl or C]-C6 alkoxy or 20

[0060] wherein

[0061] R43 and R44 preferably independently represent C1-C6 alkyl, C6-C10 aryl which may each be substituted by hydroxy and/or amino or

[0062] R43 and R44 together with the nitrogen atom to which they are attached may mean a morpholine, piperidine, pyrrolidine or piperazine ring which may bear one or two substituents from the group methyl, ethyl and phenyl.

[0063] R5 preferably denotes hydrogen or cyano,

[0064] R6 preferably denotes hydrogen, C1-C6 alkyl, C6-C10 aryl oder C1-C6 alkoxy or 21

[0065] wherein Z denotes a group OR45 or 22

[0066] and

[0067] R45, R46 and R47 independently preferably represent C1-C6 alkyl or C6-C10 aryl, in particular phenyl or naphthyl,

[0068] R7, R5 and R9 independently preferably represent hydrogen, C1-C6 alkyl, C6-C1O aryl, C1-C6 alkoxy or cyano,

[0069] R10 preferably denotes hydrogen, cyano, C1-C6 alkyl, C6-C10 aryl, in particular phenyl or naphthyl, C2-C4 acyl oder C1-C6 alkoxycarbonyl,

[0070] R11 preferably denotes hydrogen, halogen, nitro, C1-C4 alkoxycarbonyl, C1-C4 acyl, C8-C24 aralkenyl or amino identically or differently mono- or disubstituted by C1-C6 alkyl, C6-C10 aryl, in particular phenyl or naphthyl,

[0071] R11 furthermore denotes morpholinyl, piperidinyl, pyrrolidinyl or piperazinyl which may bear one or two substituents selected from methyl, ethyl or phenyl,

[0072] R12 preferably denotes C1-C6 alkyl, C6-C10 aryl, in particular phenyl or naphthyl, or C7-C12 aralkyl.

[0073] R13 preferably denotes hydrogen, C1-C6 alkyl, C6-C10 aryl, in particular phenyl or naphthyl, or C1-C6 alkoxy or 23

[0074] wherein

[0075] R49 and R50 independently preferably denote C1-C6 alkyl, C6-C10 aryl, in particular phenyl or naphthyl, or

[0076] R49 und R50 together with the nitrogen atom to which they are attached, moreover denote a morpholinyl, piperidinyl, pyrrolidinyl or piperazinyl, which may bear one or two identical or different substituents selected from methyl, ethyl and phenyl,

[0077] R14 and R15 independently preferably represent hydrogen, cyano, halogen, nitro, C1-C6 alkyl, C1-C6 alkoxy, C6-C10 aryl, in particular phenyl or naphthyl,

[0078] R17 and R23 independently preferably represent hydrogen, C1-C6 alkyl, C6-C10 aryl.

[0079] R16, R18 to R22 and R24 to R40 independently preferably represent hydrogen, cyano, C1-C6 alkyl, C6-C10 aryl, C1-C6 alkoxy, amino substituted by one or two C1-C6 alkyl groups, unsubstituted amino,

[0080] wherein the aliphatic carbon chains such as e.g. alkyl, alkoxy, Alkylamino, aralkyl, in the residues of R4 to R13, R16 to R40 may be interrupted by a heteroatom, selected from oxygen, nitrogen and sulphur and/or a phenyl ring.

[0081] Alkyl residues, for example, in alkyl, alkoxy, alkoxycarbonyl or (di)alkylamino are exemplified by methyl, ethyl, n- or iso-propyl, n-, iso- or tert.-butyl. Aryl represents in particular phenyl and naphthyl. Aralkyl represents in particular phenyl-C1-C4-alkyl, z.B. phenylmethyl, phenylethyl or naphthyl-C1-C4-alkyl, e.g. naphthylmethyl, naphthylethyl.

[0082] The present invention furthermore relates to a process for the production of the above-stated (co)polymers which contain at least one repeat chain unit of the general formula (1) or (2) and optionally repeat units of the general formula (3), 24

[0083] wherein the residues have the above-stated meanings,

[0084] wherein the corresponding monomers of the formula (20) or (21) are produced 25

[0085] from a fluorescent dye functionalised with an OH, COOH or NH group, which dye contains the structure of L,

[0086] and a styrene or acrylic acid derivative of the formulae (22) and (23) 26

[0087] in which

[0088] R1 and R2 have the above-stated range of meaning and

[0089] R41 denotes a halogen atom, preferably Cl or Br,

[0090] R42 denotes a halogen atom, preferably Cl or Br, a hydroxy or C1-C6 alkoxy group,

[0091] in the presence of a base, preferably triethylamine, pyridine or an alkali metal alkoxide and these monomers are then polymerised, optionally in the presence of units of the formula (3) as comonomers.

[0092] The reaction of the fluorescent dyes functionalised with an OH, carboxyl or NH group generally proceeds at temperatures of −30° C. to 100° C., preferably from 0° C. to 60° C.

[0093] Polymerisation processes are described in the literature. They may proceed by ionic or free-radical polymerisation. Anionic polymerisation may, for example, be initiated by initiators such as butyllithium or lithiumnapthalide. Free-radical polymerisation may be initiated by, for example, free-radical initiators, such as for example azo initiators or peroxides, preferably AIBN (azoisobutyro-nitrile) or dibenzoyl peroxide. The polymers may be produced using bulk methods or in suitable solvents such as benzene, toluene, tetrahydrofuran, dioxane, ethyl acetate, xylene, chlorobenzene, 1-methoxy-2-propyl acetate, chlorinated hydrocarbons, acetone etc., at temperatures of 20-250° C.

[0094] Production of the (co)polymers according to the invention is illustrated by way of example by the following reaction scheme: 27

[0095] In this scheme, the methacrylate (26) is initially produced starting from 3-(6-hydroxyhexoxycarbonyl)-7-diethylamino-coumarin (24) and methacryloyl chloride (25) together with triethylamine at 0° C. to room temperature. The methacrylate (26) may be polymerised in chlorobenzene at 100° C. in the presence of n-butyl acrylate (27) as a comonomer together with AIBN as free-radical initiator to form the copolymer (28). The preferred molar percentage x of comonomer (26) is between 0.5 and 60%.

[0096] Production of the polymers or copolymers according to the invention may furthermore be illustrated by way of example by the following reaction scheme: 28

[0097] In this scheme, the styrene derivative (31) is first produced at 0° C. to room temperature in a phase transfer catalysed reaction starting from phenothiazine (29) and m/p-vinylbenzene chloride (30) together with sodium hydroxide and tributylammonium hydrogen sulphite in a catalytic quantity. The styrene derivative (31) may be polymerised in toluene at 80° C. to 100° C. in the presence of m/p-methylstyrene (32) as comonomer together with AIBN as free-radical initiator to form the copolymer (33). The preferred molar percentage x of comonomer (31) is between 0.5 and 60%.

[0098] Production of the polymers or copolymers according to the invention may furthermore be illustrated by way of example by the following reaction scheme: 29

[0099] In this scheme, the methacrylate (35) is first produced at 0° C. to room temperature starting from 4/5-(N-methyl-N-hydroxyethyl)amino-1,8-naphthoylene- 1′,2′-benzimidazole (34) (only 4-isomer shown) and methacryloyl chloride (25) together with triethylamine. The methacrylate (35) may be polymerised in chlorobenzene at 80° C in the presence of N-vinylcarbazole (36) as comonomer together with AIBN as free-radical initiator to form the copolymer (37). The preferred molar percentage x of comonomer (35) is between 0.5 and 60%.

[0100] Production of the polymers or copolymers according to the invention may furthermore be illustrated by way of example by the following reaction scheme: 30

[0101] In this scheme, the styrene derivative (39) is first produced at room temperature in tetrahydrofuran starting from N-isoamyl-4-(N-methyl-N-hydroxyethyl)amino-1,8-naplithalimide (38) and mip-vinylbenzyl chloride (30) together with potassium tert.-butylate. The styrene derivative (39) may be polymerised in toluene at 100° C. together with AIBN as free-radical initiator to form the homopolymer (40).

[0102] The styrene derivative (39) may also be copolymerised with a comonomer such as, for example, N-vinylcarbazole, styrene, n-butyl acrylate etc..

[0103] (Co)polymers of the present invention have molecular weights, determined by gel permeation chromatography, in the range from 500 to 1 million g/mol, preferably of 800 to 500000 g/mol.

[0104] Some of the fluorescent dyes functionalised with OH, SH or NH (c.f. definition of residue L), which are necessary for the production of the (co)polymers according to the invention, are known.

[0105] The coumarin derivatives of the following formula (4a) are novel: 31

[0106] wherein

[0107] R43 and R44 mutually independently denote hydrogen, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, which may each be substituted by hydroxy, amino, carboxy or C1-C4 alkoxycarbonyl or

[0108] R43 and R44, together with the nitrogen atom to which they are attached, may mean a morpholine, piperidine, pyrrolidine or piperazine ring, which may bear one or two substituents from the group methyl, ethyl and phenyl, and

[0109] Z denotes a group OR45 or 32

[0110] wherein

[0111] R45 means C1-C30 alkyl, C6-C18 aryl or C7-C24 aralkyl, which are each substituted by at least one hydroxy group and wherein the aromatic rings may additionally be substituted by halogen, C1-C6 alkyl C1-C6 alkoxy and

[0112] R46 and R47 mutually independently denote C1-C30 alkyl C6-C18 aryl or C7-C24 aralkyl, each optionally hydroxy-substituted, wherein at least one of the residues R46 or R47 has a hydroxy group and wherein the aromatic rings may additionally be substituted by halogen, C1-C6 alkyl, C1-C6 alkoxy.

[0113] The coumarin derivatives of the formula (4a) according to the invention bear at least one hydroxy group by means of which they may be chemically bonded to the polymer side chains.

[0114] In the formula (4a), R43 and R44 mutually independently preferably denote hydrogen or C1-C16 alkyl, optionally substituted by hydroxy, amino, carboxy and/or C1-C4 alkoxycarbonyl, each unsubstituted, or phenyl, naphthyl, phenyl-C1-C4-alkyl or naphthyl-C1-C4-alkyl substituted by C1-C4 alkyl, hydroxy, amino, carboxy, C1-C4 alkoxycarbonyl, chlorine and/or bromine.

[0115] R43 and R44 in particular denote C1-C6 alkyl or phenyl optionally substituted by hydroxy, amino or carboxy,

[0116] Z in the above-stated formula (4a) denotes OR45 or NR46R47, wherein R45 preferably denotes C1-C16 alkyl, phenyl, naphthyl, phenyl-C1-C4-alkyl or naphthyl-C1-C4-alkyl, which are each substituted by at least one hydroxy group, and wherein the aromatic rings may additionally be substituted by halogen, C1-C6 alkyl, C1-C6 alkoxy,

[0117] R46 and R47 mutually independently preferably denote C1-C16 alkyl, phenyl, naphthyl, phenyl-C1-C4-alkyl or naphthyl-C1-C4-alkyl, each optionally substituted by hydroxy, wherein at least one of the residue R46 or R47 has a hydroxy group and the aromatic rings may additionally also be substituted by halogen, C1-C6 alkyl C1-C6 alkoxy

[0118] R45 particularly preferably denotes a C1-C12 alkyl substituted by a hydroxy group.

[0119] R46 and R47 mutually independently particularly preferably denote C1-C12 alkyl optionally substituted by a hydroxy group, wherein at least one of the residues R46 and R47 has a hydroxy group.

[0120] The novel coumarin derivatives of the formula (4a), 33

[0121] wherein R43, R44 and Z have the above-stated meaning, may be produced by,

[0122] a) in the event that Z denotes —OR45, producing the malonic acid derivative of the formula (III) 34

[0123] preferably in a single vessel process from the Meldrums acid of the formula (I) 35

[0124] and an alcohol of the formula (II)

R45—OH  (II)

[0125] optionally in the presence of a diluent, such as for example toluene, xylene or mesitylene with catalysis by, for example, p-toluenesulphonic acid at temperatures in the range from 20 to 250° C., preferably from 80 to 150° C.,

[0126] and then reacting this malonic acid derivative with a salicylic aldehyde of the formula (IV) 36

[0127] wherein R43, R44, R45 have the above-stated meaning,

[0128] optionally in the presence of a diluent, such as for example toluene, xylene, mesitylene, with catalysis by, for example, piperidine acetate at temperatures of 50 to 250° C., preferably of 80 to 140° C., and,

[0129] b) in the event that Z denotes 37

[0130] by reacting a salicylic aldehyde of the formula (IV), a secondary amine of the formula (V) and a malonic acid derivative of the formula (VI) 38

[0131] in which

[0132] R43, R44, R46 and R47 have the above-stated meaning and

[0133] R48 denotes C1-C6 alkyl,

[0134] optionally in the presence of a diluent, such as for example toluene, xylene or mesitylene, with catalysis by, for example, piperidine acetate at temperatures of 50 to 250° C., preferably of 80 to 140° C.

[0135] When performing the process a) according to the invention, 2-10 mol, preferably 3-6 mol of alcohol of the formula (1I) are generally used for each mol of Meldrums acid, and 0.5-1.0, preferably 0.9-1.0 mol of salicylic aldehyde of the formula (IV) is generally used for each mol of malonic acid derivative of the formula (III).

[0136] When performing the process b) according to the invention, 2-20, preferably 5-10 mol of secondary amine and 1-2, preferably 1.2-1.5 mol of malonic acid derivative of the formula (VI) are generally used per mol of salicylic aldehyde of the formula (IV).

[0137] Production of the coumarin derivatives of the formula (4a) according to the invention, where Z=OR45, by way of a Knoevenagel condensation reaction and subsequent cyclisation is illustrated by way of example by the following reaction scheme: 39

[0138] In this scheme, bis-(6-hydroxyhexyl) malonate is first produced by reacting the Meldrums acid and 1,6-hexanediol in the presence of catalytic quantities of p-toluene-sulphonic acid with elimination of acetone and water. The bis-(6-hydroxyhexyl) malonate is then combined with 4-diethylaminosalicylic aldehyde in the presence of catalytic quantities of piperidine acetate to form the desired 3-(6-hydroxyhexoxycarbonyl)-7-diethylaminocoumarin.

[0139] Production of the coumarin derivatives of the formula (4a) according to the invention, where Z=NR46R47, is illustrated by way of example by the following reaction scheme: 40

[0140] In this scheme, 4-diethylaminosalicylic aldehyde is reacted with diethyl malonate and 2-(methylamino)ethanol in the presence of catalytic quantities of piperidine acetate. The desired 3-[(N-hydroxyethyl-N-methyl)aminocarbonyl]-7-diethylamnino-coumarin is obtained.

[0141] The starting products of the formulae (I), (II), (III), (IV), (V) and (VI) are compounds which are generally known in organic chemistry.

[0142] The following 1,8-naphthalimide derivatives of the formulae (6a), (7a-1) and (7b-1) are also novel: 41

[0143] in which

[0144] R11′ denotes hydrogen, halogen, nitro, C1-C4 alkoxycarbonyl, C1-C4 acyl, C8-C24 aralkenyl, unsubstituted amino or amino identically or differently mono- or disubstituted by C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, wherein the above-stated carbon chains may themselves be substituted by hydroxy and/or carboxy,

[0145] R11′ furthermore denotes morpholinyl, piperidinyl, pyrrolidinyl or piperazinyl, which may bear one or two substituents selected from methyl, ethyl and/or phenyl,

[0146] R12′ denotes hydrogen or C1-C30 alkyl, C1-C30 alkoxy, C6-C18 aryl, C7-C24 aralkyl, which may be mono- or polysubstituted by hydroxy and/or carboxy,

[0147] and at least one of the residues R11 or R12 has a hydroxy or carboxy group,

[0148] R49′ and R50′ mutually independently denote C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, which may be substituted by hydroxy, wherein at least one of the residues R49 or R50′ has a hydroxy or carboxy group.

[0149] R49′ and R50′, together with the nitrogen atom to which they are attached, moreover denote morpholinyl, piperidyl, pyrrolidyl or piperazinyl, which may bear one or two identical or different substituents selected from methyl, ethyl and phenyl and have at last one hydroxy or carboxy group,

[0150] R14 and R15 mutually independently mean hydrogen, halogen, cyano, nitro, C1-C30 alkyl, C1-C30 alkoxy, C6-C18 aryl, C7-C24 aralkyl, C1-C12 alkoxycarbonyl, C2-C12 acyl or C1-C6 (di)alkylamino.

[0151] The 1,8-naphthalimide derivatives of the formulae (6a), (7a-1) and (7b-1) according to the invention bear at least one hydroxy or one carboxy group, preferably a hydroxy group, by means of which they may be chemically bonded to the polymer side chains.

[0152] In the above-stated formula (6a),

[0153] R11′ preferably denotes hydrogen, chlorine, bromine, nitro, methoxycarbonyl, ethoxycarbonyl, n- or iso-propoxy-carbonyl, methylcarbonyl, ethylcarbonyl, n- or iso-propylcarbonyl, amino, amino identically or differently mono- or disubstituted by C1-C15 alkyl, phenyl, naphthyl, phenyl-C1-C4-alkyl or naphthenyl-C1-C4-alkyl, in each case optionally substituted by methyl and/or ethyl, wherein the above-stated carbon chains may themselves by substituted by hydroxy, R11′ furthermore preferably denotes morpholinyl, piperidinyl, pyrrolidinyl or piperazinyl, which may bear one or two substituents selected from hydroxy, methyl, ethyl and/or phenyl.

[0154] R12′ preferably denotes C1-C15 alkyl, phenyl or phenyl-C1-C6-alkyl, which may be substituted by hydroxy and the aromatic rings may additionally be substituted by halogen, C1-C6 alkyl and/or C1-C6 alkoxy.

[0155] R11′ in particular denotes chlorine, bromine, amino which is identically or differently mono- or disubstituted by C1-C15 alkyl, morpholinyl, piperidinyl, pyrrolidinyl or piperazinyl, wherein the above-stated carbon chains may themselves by substituted by hydroxy.

[0156] R12′ in particular denotes C1-C12 alkyl, phenyl optionally substituted by halogen, C1-C6 alkyl, C1-C6 alkoxy, which may bear a hydroxy group.

[0157] At least one of the residues R11′ and R12′ must have a hydroxy group.

[0158] R49′ and R50′ in the formulae (7a-1) and (7b-1) mutually independently preferably denote C1-C15 alkyl, phenyl, phenyl-C1-C6-alkyl, naphthyl, naphthyl-C1-C6-alkyl, which may be mono- or poly-, in particular monosubstituted by hydroxy, wherein at least one of the residues R49′ or R50′ has a hydroxy group.

[0159] R49′ and R50′, together with the nitrogen atom to which they are attached, moreover preferably denote piperidinyl or piperazinyl, which may bear one or two identical or different substituents selected from methyl, ethyl and phenyl and have at least one hydroxy or carboxy group,

[0160] R14 and R15 in the formulae (7a-1) and (7b-1) mutually independently preferably denote hydrogen, halogen, C1-C15 alkyl, C1-C15 alkoxy, C1-C4 alkoxycarbonyl, C1-C4 acyl or di(C1-C6-alkyl)amino, phenyl, phenyl-C1-C6-alkyl, naphthyl or naphthyl-C1-C6-alkyl in each case substituted by methyl and/or ethyl.

[0161] R49′ and R50′ in particular denote C1-C12 alkyl, phenyl, phenyl-C1-C6 alkyl, which may be substituted by a hydroxy group, wherein at least one of the residues R49′ or R50′ has a hydroxy group.

[0162] R14 and R15 in particular denote hydrogen, halogen, C1-C12 alkyl, C1-C12 alkoxy, di(C1-C6-alkyl)amino, phenyl.

[0163] The number of hydroxy groups and/or carboxy groups is at least one, but there may also be up to four hydroxy and/or carboxy groups.

[0164] The aromatic rings in the above-stated residues may be identically or differently mono- to penta-, preferably mono- to trisubstituted by the stated substituents.

[0165] The aliphatic carbon chains, such as for example alkyl, alkoxy, alkylamino, aralkyl in R43, R44, R45, R46 and R47, R11′, R12′, R45′, R50′ may be interrupted by one or more, preferably one or two heteroatoms selected from oxygen, nitrogen and sulphur, and/or by one or more, preferably one or two phenylene rings, which may be substituted by C1-C4 alkyl and/or halogen.

[0166] A process for the production of novel 1,8-naphthalimide derivatives of the formula (6a) 42

[0167] in which

[0168] R11′ and R12′ have the above-stated meaning,

[0169] is characterised in that either

[0170] a) a 1,8-naphthalic anhydride of the formula (VII) and a primary amine of the formula (VIII), 43

[0171] are reacted together at 50 to 250° C., preferably at 90 to 140° C., optionally in the presence of diluents, such as for example acetic acid, butanol, chlorobenzene, toluene or xylene or,

[0172] b) in the event that R11′ in formula (6a) means an unsubstituted, mono- or disubstituted amino or cyclic amino, a 1,8-naphthalimide of the formula (6a-1) 44

[0173] in which

[0174] R11′ denotes halogen, preferably chlorine, bromine or iodine, or nitro,

[0175] which is produced from a 1,8-naphthalic anhydride of the formula (VIIA) and a primary amine of the formula (VIII) 45

[0176] in which R11′ and R12′ have the above stated meaning,

[0177] at temperatures of 50 to 250° C., preferably of 90 to 140° C., optionally in the presence of diluents, such as for example acetic acid, butanol, chlorobenzene, toluene or xylene,

[0178] and the resultant compound of the formula (6a-1) is then reacted with a primary or secondary amine or piperidine, morpholine, pyrrolidine or piperazine, which may bear one or two substituents selected from methyl, ethyl and/or phenyl, or with an aqueous ammonia solution, optionally in the presence of solvents, such as for example methoxy-ethanol or butanol, optionally with catalysis by, for example, a copper(II) salt at temperatures of 50 to 250° C., preferably of 100 to 150° C.

[0179] A process for the production of novel 1,8-naphthalimide derivatives of the formula (7a-1) and (7b-1) (process C), 46

[0180] in which

[0181] R14, R15, R49′ and R50′ have the above-stated meaning,

[0182] wherein a 1,8-naphthalimide derivative of the formula (IXa and b), 47

[0183] in which

[0184] R14, R15 and R11″ have the above range of meaning,

[0185] is produced from a 1,8-naphthalic anhydride of the formula (VIIa) 48

[0186] in which R11″ has the above-stated meaning,

[0187] and an o-phenylenediamine of the formula (X) 49

[0188] in which R14 and R15 have the above-stated meanings, at temperatures of 50 to 250° C., preferably of 90 to 140° C., optionally in the presence of solvents, such as for example acetic acid, butanol, chlorobenzene, toluene or xylene and the 1,8-naphthalimide derivative of the formula (IXa and b) is then reacted with a secondary amine of the formula (XI), 50

[0189] in which R49′ and R50′ have the above-stated meaning,

[0190] with catalysis by, for example, a copper(II) salt at temperatures of 50 to 250° C., preferably of 100 to 150° C., optionally in the presence of a solvent, such as for example methoxyethanol or butanol.

[0191] When performing the process a) according to the invention for the production of the 1,8-naphthalimide derivatives of the formula (6a), 1 to 1.8 mol, preferably 1.2 to 1.4 mol of primary amine of the formula (VIII) are generally used per mol of compound of the formula (VII).

[0192] When performing the process b) according to the invention for the production of the 1,8-naphthalimide derivatives of the formula (6a-1), I to 1.8 mol, preferably 1.2 to 1.4 of the primary amine of the formula (VIII) are generally used per mol of compound of the formula (VIIa) and 1.2 to 5 mol, preferably 2 to 2.5 mol of the corresponding primary, secondary or cyclic amine are use per mol of compound of the formula (6a-1).

[0193] Production of the 1,8-naphthalimide derivatives of the formula (6a), processes (a) and (b), according to the invention is illustrated by way of example by the following reaction scheme: 51

[0194] In this scheme, the 4-chloro-N-hydroxyethyl-1,8-naphthalimide is first produced by the reaction of 4-chloronaphthalic anhydride and 2-aminoethanol. The 4-chloro-N-hydroxyethyl-1,8-naphthalimide is then combined with piperidine in the presence of a catalytic quantity of a copper(II) salt to form the desired N-hydroxyethyl-4-piperidino-1,8-naphthalimide.

[0195] When performing the process C) according to the invention for the production of the 1,8-naphthalimide derivatives of the formula (7a-1) and (7b-1), 1 to 1.8 mol, preferably 1.2 to 1.4 mol of the o-phenylenediamine of the formula (X) are generally used per mol of compound of the formula (VIIa) and 1.2 to 5 mol, preferably 2 to 2.5 mol of the secondary amine of the formula (XI) per mol of compound (IXa-b).

[0196] Production of the 1,8-naphthalimide derivatives according to the invention of the formulae (7a-1 and 7b-1) is illustrated by way of example by the following reaction scheme: 52

[0197] In this scheme, the 4/5-chloro-1,8-naphthoylene-1′,2′-benzimidazole, which occurs as an isomeric mixture (approximately 3:1), is first produced by the reaction of 4-chloronaphthalic anhydride and o-phenylenediamine. The 4/5-chloro-1,8-naphthoylene-1′,2′-benzimidazole is then combined with 2-(methylamino)ethanol in the presence of a catalytic quantity of a copper(II) salt to form the desired 4/5-(N-methyl-N-hydroxyethyl)amino-1,8-naphthoylene-1′,2′-benzimidazole.

[0198] The starting products of the formulae (VII), (VIII), (VIIa), (X) and (XI) for the production of the compounds according to the invention of the formula are compounds which are generally known in organic chemistry.

[0199] The styrene and acrylic acid derivatives of the formulae (22) and (23) which are also necessary for the production of the (co)polymers according to the invention are generally known compounds.

[0200] The (co)polymers according to the invention are distinguished by their luminescent properties and film-forming capacity and may be applied onto suitable substrates by casting, knife coating or spin coating. The products exhibit photoluminescence on irradiation both in solutions and as films. The (co)polymers of the present invention are suitable for the production of electroluminescent displays.

[0201] The invention thus relates to the use of the (co)polymers described above in the luminescent layer of an electroluminescent device, which is characterised in that

[0202] an electroluminescent layer is located between two electrodes,

[0203] at least one of the two electrodes is transparent in the visible range of the spectrum,

[0204] light in the frequency range of 200 to 2000 nm is emitted when a direct voltage in the range of 0.1 to 100 volts is applied,

[0205] one or more interlayers may additionally be arranged between the electroluminescent layer and the electrodes.

[0206] These interlayers are known from the literature (c.f. Appl. Phys. Lett., 57, 531 (1990)) and are described therein as HTL (hole transport layer) and ETL (electron transport layer). The purpose of such interlayers is inter alia to increase the intensity of electroluminescence.

[0207] The electroluminescent polymers according to the invention may also be used in the electroluminescent layer as a mixture with each other or with at least one further material. This further material may be an inert binder, charge transporting substances as described in EP-A 532 798 or EP-A 564 224, or mixture of inert binders and charge transporting substances.

[0208] The mixtures of the polymers according to the invention and a further material are distinguished inter alia that they are film-forming and may be applied in large areas onto suitable substrates by casting, knife coating or spin coating. Suitable substrates are transparent supports such as glass or plastic films (for example polyester, such as polyethylene terephthalate or polyethylene naphthalate, polycarbonate, polysulphone, polyimide films).

[0209] The inert binder preferably comprises soluble, transparent polymers, such as for example polycarbonates, polystyrene, polyvinylpyridine, polymethylphenylsiloxane and polystyrene copolymers such as SAN, polysulphones, polyacrylates, polyvinylcarbazole, polymers and copolymers of vinyl acetate and vinyl alcohol.

EXAMPLES

Example 1

[0210] 1. Production of 3-(6-hydroxyhexoxycarbonyl)-7-diethylaminocoumarin, formula (24) in the reaction scheme

[0211] A solution of bis-(6-hydroxyhexyl) malonate in 1,6-hexanediol is prepared by heating a mixture of 21.6 g (0.15 mol) of Meldrums acid, 59 g (0.50 mol) of 1,6-hexanediol and 0.28 g (1.5 mmol) of p-toluene-sulphonic acid monohydrate for 2 hours at 140° C.

[0212] The resultant solution is then combined with 26.0 g (0.135 mol) of 4-diethylaminosalicylic aldehyde, 0.7 ml of piperidine and 0.1 ml of acetic acid. The reaction mixture is stirred for 3 hours at 110° C. and, once cool, combined with 300 ml of water. The suspension is extracted with dichloromethane. The organic phase is evaporated and the residue recrystallised from toluene.

[0213] 40.2 g (83% of theoretical) of 3-(6-hydroxyhexoxy-carbonyl)-7-diethylaminocoumarin are obtained as yellow crystals with a melting point of 85 to 86° C.

[0214] 2. Production of the 3-(6-methacryloxyhexoxycarbonyl)-7-diethylaminocoumarin, formula (26) in the reaction scheme

[0215] 8.36 g (0.08 mol) of methacryloyl chloride (25) are added dropwise with stirring and cooling with iced water to a solution of 16.3 g (0.045 mol) of 3-(6-hydroxyhexoxycarbonyl)-7-diethylaminocoumarin (24) and 10.0 g (0.10 mol) of freshly distilled triethylamine in 50 ml of dry tetrahydrofuran. The reaction mixture is stirred for 5 hours at room temperature. The reaction mixture is then treated with 200 ml of water and 200 ml of methylene chloride. Once the phases have separated, the aqueous phase is extracted twice more with 100 ml portions of methylene chloride. The combined organic extracts are washed until neutral and dried with sodium sulphate. Once the solvent has been removed by vacuum distillation, the residue is adsorptively filtered through a short silica gel column with diethyl ether as the mobile solvent. Once the solvent has been removed by distillation, 17.6 g (92% of theoretical) of a pale yellow oil are obtained.

[0216] 3. Production of the copolymer according to formula (28) in the reaction scheme with x=13 mol.%, y=87 mol.%

[0217] A solution of 5.0 g (0.012 mol) of 3-(6-methacryloxy-hexoxycarbonyl)-7-diethylaminocoumarin (26), 10.0 g (0.078 mol) of n-butyl acrylate (27) and 0.15 g (0.91 mmol) of AIBN in 80 ml of dry chlorobenzene are degassed under a vacuum and then stirred for 3 hours at 100° C under nitrogen. The polymerisation mixture is then reinitiated with 0.15 g (0.91 mmol) of AIBN in three portions within 3 hours. The solution is then added dropwise to 100 ml of methanol with stirring and the suspension is then suction filtered. The crude product is precipitated twice more from a methylene chloride/methanol mixture. Yield 12.7 g (85% of theoretical).

Example 2

[0218] 1. Production of N-(m/p-vinylbenzyl)phenothiazine, formula (31)

[0219] 100 ml of 45% sodium hydroxide solution is added with stirring at 0° C. to a mixture of 20 g (0.10 mol) of phenothiazine (29), 18.4 g (0.12 mol) of m/p-vinylbenzyl chloride (30) and 3.39 g (0.01 mol) of tributylammonium hydrogen sulphite in 100 ml of isobutyl methyl ketone. The reaction mixture is vigorously stirred for 4 hours at room temperature and then diluted with 100 ml of water and 150 ml of isobutyl methyl ketone. Once the phases have separated, the organic solution is washed until neutral and dried with sodium sulphate. The solution is then adsorptively filtered through a short silica gel column with diethyl ether as the mobile solvent. Once the solvent has been removed, 30 g (95% of theoretical) of a pale yellow oil are obtained.

[0220] 2. Production of the copolymer of the formula (33), with x=28 mol. %, y=72 mol. %

[0221] 8.0 g (80% of theoretical) of the copolymer (33) may be produced in a similar manner to the method described in example 1 from 5.0 g (0.016 mol) of N-(m/p-vinylbenzyl)phenothiazine (31), 5.0 g (0.042 mol) of m/p-methylstyrene (32) and a total of 0.15 g (0.91 mmol) of AIBN with toluene as the solvent.

Example 3

[0222] 1. 4/5-(N-methyl-N-hydroxyethyl)amino-1,8-naphthoylene-1′,2′-benzimidazole is obtained in a similar manner to example 5, section 1 from 4/5-chloro-1,8-naphthoylene-1,2-benzimidazole in an 82% yield as red-brown crystals of a melting point of 168-169° C.

[0223] 2. Production of 4/5-(N-methyl-N-methacryloxethyl)amino-1,8-naphthoylene-1′,2′-benzimidazole, formula (35)

[0224] 6.3 g (90% of theoretical) of the methacrylate (35) are produced in a similar manner to the process described in example I starting from 5.83 g (0.017 mol) of 4/5-(N-methyl-N-hydroxyethyl)amino-1,8-naphthoylene-1′,2′-benzimidazole (34) and 3.24 g (0.031 mol) of methacryloyl chloride (25). The reaction mixture is worked up by treatment with water and the resultant suspension is suction filtered. The crude product is recrystallised from toluene at low temperature.

[0225] 3. Production of the copolymer according to formula (37), in which x=55 mol. %, y=45 mol. %

[0226] In a similar manner to the method described in example 1, 4.8 g (87% of theoretical) of the copolymer (37) may be produced from 4.0 g (9.7 mmol) of 4/5-(N-methyl-N-methacryloxyethyl)amino-1,8-naphthoylene-1′2′-benzimidazole (35), 1.5 g (7.8 mmol) of N-vinylcarbazole (36) and a total of 50 mg (0.30 mmol) of AIBN with chlorobenzene as the solvent.

Example 4

[0227] 1. N-isoamyl-4-(N-methyl-N-hydroxyethyl)amino-1,8-naphthalamide 53

[0228] is obtained in a similar manner to example 5, section I from 4-chloro-N-isoamyl-1,8-naphthalimide and 2-(methylamino)ethanol in a 71% yield as yellow to brown crystals of a melting point of 117-118° C.

[0229] 2. Production of the N-isoamyl-4-(N-methyl-N-m/p-vinylbenzyloxyethyl)-amino-1,8-naphthalimide (39)

[0230] A solution of 10.2 g (0.03 mol) of N-isoamyl-4-(N-methyl-N-hydroxy-ethyl)amino-1,8-naphthalimide (38) in 30 ml of dry tetrahydrofuran is added dropwise under nitrogen at 5° C to a stirred solution of 4.0 g (0.036 mol) of potassium tert.-butylate in 40 ml of dry tetrahydrofuran. The mixture is stirred for a further 5 hours at room temperature. 5.0 g (0.033 mol) of m/p-vinylbenzyl chloride (30) are then added dropwise at room temperature to the red-brown coloured solution. After 3 hours, the reaction mixture is treated with 200 ml of water and 300 ml of methylene chloride. Once the phases have separated, the aqueous phase is extracted twice more with 100 ml portions of methylene chloride. The combined organic extracts are washed until neutral and dried with sodium sulphate. Once the solvent has been removed by vacuum distillation, the residue is adsorptively filtered through a short silica gel column with diispropyl ether as the mobile solvent, wherein an initial run with a small quantity of mip-vinyl-benzyl chloride is removed. Once the solvent has been removed by distillation, 9.6 g (70% of theoretical) of a yellow oil are obtained.

[0231] 3. Production of the homopolymer according to formula (40)

[0232] In a similar manner to the method described in example 1, 2.3 g (77% of theoretical) of the homopolymer (40) may be produced from 3.0 g (6.6 mmol) of N-isoamyl-4-(N′-methyl-N-m/p-vinylbenzyloxyethyl)-amino-1,8-naphthalimide (39) and a total of 30 mg (0.18 mmol) of AIBN with toluene as the solvent.

[0233] 4. Production of the electroluminescent device

[0234] ITO-coated glass (manufactured by Balzers) is cut into substrates of dimensions 20×30 mm and cleaned. Cleaning is performed in the following sequence of stages:

[0235] 1. 15 minutes rinsing in distilled water and Falterol in ultrasound bath,

[0236] 2. 2×15 minutes' rinsing in ultrasound bath, each time with fresh distilled water,

[0237] 3. 15 minutes rinsing with ethanol in ultrasound bath,

[0238] 4. 2×15 minutes rinsing in ultrasound bath, each time with fresh acetone,

[0239] 5. drying on lint-free lens cleaning cloths.

[0240] A 1% solution of the polymer according to formula (40) (example 4) in 1,2-dichloroethane is filtered (0.2 &mgr;m filter, Sartorius). The filtered solution is distributed on the ITO glass with a spin coater at 1000 rpm. The thickness of the dry film is 110 nm and the Ra value of the surface is 5 nm (Alpha-Step 200 stylus profilometer from Tencor Inst.).

[0241] The film produced in this manner is then provided with Al electrodes by vapour deposition. To this end, isolated 3 mm diameter dots of Al are vapour-deposited onto the film using a perforated mask. A pressure of below 10-5 mbar prevails in the vapour deposition device (Leybold) during deposition.

[0242] The ITO layer and the Al electrode are connected to an electrical supply via electrical supply lines. When the voltage is increased, an electric current flows through the device and the described layer electroluminesces. Electroluminescence is in the yellow/green range of the spectrum and occurs with an ITO contact of positive polarity.

Example 5

[0243] 1. Production of N-hydroxyethyl-4-piperidinyl-1,8-naphthalimide

[0244] A mixture of 20.0 g (0.073 mol) of 4-chloro-N-hydroxyethyl-1,8-naphthalimide, 25.8 g (0.30 mol) of piperidine, 2.0 g of copper(II) sulphate and 200 ml of ethylene glycol monomethyl ether is refluxed for 2 hours while being stirred. The solution is cooled to room temperature and then combined with 1 liter of water. The suspension is extracted with dichloromethane. The organic phase is evaporated and the residue recrystallised from toluene. 16 g (68% of theoretical) of brown crystals of a melting point of 152-153° C. are obtained.

[0245] 2. Production of N-(m/p-vinylbenyloxyethyl)-4-piperidyl-1,8-naphthalimide, formula (42)

[0246] In a similar manner to the method described in example 4, 6.4 g (73% of theoretical) of N-(m/p-vinylbenzyl-oxyethyl)-4-piperidyl- 1,8-naphthalimide (42) may be produced from 6.48 g (0.020 mol) of N-hydroxyethyl-4-piperidyl-1,8-naphthalimide (41) and 3.6 g (0.024 mol) of m/p-vinylbenzyl chloride (30).

[0247] 3. Production of the copolymer of the formula (44) with x=1.2 mol.% and y=98.8 mol.%

[0248] In a similar manner to the method described in example 1, 2.5 g (79% of theoretical) of the copolymer (44) may be produced from 0.16 g (0.36 mmol) of N-(m/p-vinylbenzyloxyethyl)-4-piperidyl-1,8-naphthalimide (42), 3.0 g (28.8 mmol) of styrene (43) and a total of 30 mg (0.18 mmol) of AIBN with toluene as the solvent. 54

Example 6

[0249] 1. Production of the copolymer of the formula (45) with x=1 mol. % and y=99 mol. %

[0250] In a similar manner to the method described in example 1, 4.15 g (96% of theoretical) of the copolymer (45) may be produced from 0.10 g (0.22 mmol) of N-isoamyl-4-(N-methyl-N-m/p-vinylbenzyloxyethyl)amino-1,8-naphthalimide (39), 4.20 g (21.8 mmol) of N-vinyl-carbazole (36) and a total of 30 mg (0.18 mmol) of AIBN with toluene as the solvent. 55

[0251] 2. Production of an electroluminescent device

[0252] Production process as described in example 4. The dry film thickness of the copolymer of the formula (45) is 144 nm and the Ra value of the surface is 12 nm. Electroluminescence is in the yellow-green range of the spectrum.

Claims

1. (Co)polymers which contain at least one repeat chain unit of the general formula (1) or (2) and optionally contain repeat units of the general formula (3) 56

in which

R1, R2 and R3 mutually independently mean hydrogen or C1-C6 alkyl,

M denotes CN or C1-C30 alkoxycarbonyl, C1-C30 (di)alkyl-aminocarbonyl, C1-C30 alkylcarbonyl, which may each be substituted by hydroxy or C1-C6 alkoxycarbonyl and furthermore denotes phenyl, naphthyl, anthracenyl, pyridyl or carbazolyl, which may each be substituted by residues from the group halogen, hydroxy, silyl, C1-C30 alkyl, C6-C18 aryl, C1-C30 alkoxy, C1-C30 alkoxycarbonyl, C1-C30 acyloxy and C1-C30 alkylcarbonyl,

L1 and L2 mean a photoluminescent residue,

wherein the proportion of structural units of the formulae (1) and/or (2) is in each case 0.5 to 100 mol.%, and (3) 0 to 99.5 mol.%, and the molar percentages add up to 100.

2. (Co)polymers according to

claim 1, wherein

L1 and L2 mutually independently denote a photoluminescent residue which is based on the skeleton of a fluorescent dye which is selected from the group of coumarins of the formula (4) 57

pyrenes of the formula (5) 58

1,8-naphthalimides of the formula (6) 59

1,8-naphthaloylene-1,2-benzimidazoles of the formulae (7a) and (7b) 60

phenothiazines or phenoxazines of the formula (8) 61

with X=O or S,

benzopyrones of the formula (9) 62

carbazoles, fluorenes, dibenzothiophenes and -furans of the formula (10) 63

with X2=NR23, CH2, S or O, wherein R23 denotes hydrogen or C1-C6 alkyl,

oxazoles, 1,3,4-oxadiazoles of the formula (1I) 64

with X3=CH or N

benzoquinolines of the formula (12) 65

9,10-bis-(phenylethynyl)anthracenes of the formula (13) 66

fluorones of the formula (14) 67

9,10-diphenylanthracene of the formula (15) 68

2-styrylbenzazole of the formula (16) 69

with X4=O, S, Se or CH2,

wherein

R4 denotes hydrogen, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl or C1-C30 alkoxy or 70

wherein

R43 and R44 mutually independently denote hydrogen, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, which may each be substituted by hydroxy, amino, carboxy or C1-C4 alkoxycarbonyl, or

R43 and R44, together with the nitrogen atom to which they are attached, may mean a morpholine, piperidine, pyrrolidine or piperazine ring, which may bear one or two substituents from the group methyl, ethyl and phenyl,

R5 denotes hydrogen, cyano, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, C1-C30 alkoxy, C2-C,2 acyl, C1-C12 alkoxycarbonyl, C1-C12 (di)-alkylaminocarbonyl,

R6 denotes hydrogen, cyano, C1-C30 alkyl, C6-Cl8 aryl, C7-C24 aralkyl, C1-C30 alkoxy or 71

wherein Z denotes a group OR45 or 72

and

R45, R46 and R47 mutually independently denote C1-C30 alkyl, C6-C18 aryl or C7-C24 aralkyl, wherein the aromatic rings may additionally be further substituted by halogen, C1-C6 alkyl, C1-C6 alkoxy,

R7, R5 and R9 mutually independently mean hydrogen, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, C1-C30 alkoxy, cyano, C2-C12 alkoxycarbonyl, C1-C12 (di)alkylaminocarbonyl or an amino group with one or two C1-C6 alkyl groups,

R10 means hydrogen, cyano, C1-C30 alkyl, C6-Cl, aryl, C7-C24 aralkyl, C1-C30 alkoxy, amino, an amino group with one or two C1-C6 alkyl groups, C2-C12 acyl, C1-C12 alkoxycarbonyl, C1-C12 (di)alkylaminocarbonyl,

R11 denotes hydrogen, halogen, nitro, C1-C4 alkoxycarbonyl, C1-C4 acyl, C8-C24 aralkenyl, unsubstituted amino, or amino identically or differently mono- or disubstituted by C1-C30 alkyl, C6-C18 aryl or C7-C24 aralkyl,

R11 furthermore denotes morpholinyl, piperidinyl, pyrrolidinyl or piperazinyl, which may bear one or two substituents selected from methyl, ethyl and/or phenyl,

R12 denotes hydrogen, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl or C1-C30 alkoxy,

R13 denotes hydrogen, C1-C30 alkyl, C6-C18, aryl, C7-C24 aralkyl, C1-C30 alkoxy or 73

wherein

R49 and R50 mutually independently denote C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl or

R49 and R50, together with the nitrogen atom to which they are attached, moreover denote a morpholinyl, piperidinyl, pyrrolidinyl or piperazinyl, which may bear one or two identical or different substituents selected from methyl, ethyl and phenyl,

R14 and R15 mutually independently mean hydrogen, cyano, halogen, nitro, C1-C30 alkyl, C1-C30 alkoxy, C6-C18 aryl or C7-C24 aralkyl, C1-C12 alkoxycarbonyl, C2-C12 acyl, C1-C12 (di)alkylaminocarbonyl, C1-C6 (di)alkylamino,

R17 means hydrogen, C1-C30 alkyl, C6-C18 aryl or C7-C24 aralkyl and

R16, R18 to R22 and R24 to R40 mutually independently mean hydrogen, cyano, C1-C30 alkyl, C6-C18 aryl, C7-C24 aralkyl, C1-C30 alkoxy, an amino group with one or two C1-C6 alkyl groups, unsubstituted amino, C2-C12 acyl, C1-C12 alkoxycarbonyl or C1-C12 (di)alkylaminocarbonyl, wherein the aliphatic carbon chains, such as, for example, alkyl, alkoxy, alkylamino, aralkyl, in the residues R4 to R13, R16 to R40 may be interrupted by one or more, preferably one or two heteroatoms selected from oxygen, nitrogen and sulphur and/or by one or more, preferably one or two, phenylene rings, which may be substituted by C1-C4 alkyl and/or halogen,

and wherein furthermore the luminophore is attached to the polymer side chains via an oxygen, a hydroxy or carboxy group or a nitrogen of an amino or primary amino on the above-stated substituents.

3. (Co)polymers according to

claim 1, wherein the proportion of structural units of the formulae (1) and/or (2) is 0.5 to 60 mol.% and optionally of the formula (3) 40 to 99.5 mol.%.

4. (Co)polymers according to

claim 1, wherein L denotes a fluorescent dye selected from the group of coumarins of the formula (4), pyrenes of the formula (5), 1,8-naphthalimides of the formula (6), 1,8-naphthoyl-ene-1′,2′-benzimidazoles of the formula (7), phenothiazines or phenoxazines of the formula (8), carbazoles and fluorenes of the formula (10).

5. Process for the production of (co)polymers of the formula (1) according to

claim 1, wherein monomers of the formula (20) or (21) are produced 74

from a fluorescent dye functionalised with an OH, COOH or NH group, which dye contains the structure of L,

and a styrene or acrylic acid derivative of the formulae (22) and (23) 75

in which

R1 and R2 have the above-stated range of meaning and

R41 denotes halogen,

R42 denotes halogen, a hydroxy or C1-C6 alkoxy group,

in the presence of a base and these monomers are then polymerised, optionally in the presence of units of the formula (3) as comonomers.

6. Use of the (co)polymers of the formula (1) according to

claim 1 for the production of electroluminescent devices.

7. Electroluminescent device which contains (co)polymers according to

claim 1 as the electroluminescent substance.

8. Electroluminescent device according to

claim 7 containing two electrodes, between which is located an electroluminescent layer, which contain the (co)polymers as the electroluminescent layer, and wherein one or more interlayers may be arranged between the electroluminescent layer and the electrodes.