LED CURABLE LIQUID RESIN COMPOSITIONS FOR ADDITIVE FABRICATION

Abstract

Disclosed is a photocurable resin composition for additive fabrication comprising a polymerizable component that is polymerizable by free-radical polymerization, cat ionic polymerization, or both free-radical polymerization and cationic polymerization, and a photoinitiating system capable of initiating the free-radical polymerization, cationic polymerization, or both free-radical polymerization and cationic polymerization. The photocurable resin composition is a liquid at about 25° C., and is capable of curing to provide a solid upon irradiation with light emitted from a light emitting diode (LED), wherein the light has a wavelength of from about 100 nm to about 900 nm. Also disclosed is a three-dimensional article prepared from the photocurable resin composition for additive fabrication, and a process for preparing three-dimensional articles by additive fabrication.

Description

FIELD OF THE INVENTION

The present invention relates to photocurable resin compositions used in additive fabrication applications.

BACKGROUND OF THE INVENTION

Additive fabrication processes for producing three dimensional articles are known in the field. Additive fabrication processes utilize computer-aided design (CAD) data of an object to build three-dimensional parts layer-by-layer. These three-dimensional parts may be formed from liquid resins, powders, or other materials.

A non-limiting example of an additive fabrication process is stereolithography (SL). Stereolithography is a well-known process for rapidly producing models, prototypes, patterns, and production parts in certain applications. SL uses CAD data of an object wherein the data is transformed into thin cross-sections of a three-dimensional object. The data is loaded into a computer which controls a laser beam that traces the pattern of a cross section through a liquid radiation curable resin composition contained in a vat, solidifying a thin layer of the resin corresponding to the cross section. The solidified layer is recoated with resin and the laser beam traces another cross section to harden another layer of resin on top of the previous layer. The process is repeated layer by layer until the three-dimensional object is completed. When initially formed, the three-dimensional object is, in general, not fully cured and therefore may be subjected to post-curing, if required. An example of an SL process is described in U.S. Pat. No. 4,575,330.

There are several types of lasers used in stereolithography, ranging from 193 nm to 355 nm in wavelength. The use of bulky and expensive gas lasers to cure liquid radiation curable resins is well known. The delivery of laser energy in a stereolithography system can be Continuous Wave (CW) or Q-switched pulses. CW lasers provide continuous laser energy and can be used in a high speed scanning process. However, their output power is limited which reduces the amount of curing that occurs during object creation. As a result the finished object will need additional post process curing. In addition, excess heat could be generated at the point of irradiation which may be detrimental to the resin. Further, the use of a laser requires scanning point by point on the resin which can be time-consuming.

Light emitting diodes (LEDs) are semiconductor devices which utilize the phenomenon of electroluminescence to generate light. LEDs consist of a semiconducting material doped with impurities to create a p-n junction capable of emitting light as positive holes join with negative electrons when voltage is applied. The wavelength of emitted light is determined by the materials used in the active region of the semiconductor. Typical materials used in semiconductors of LEDs include, for example, elements from Groups 13 (III) and 15 (V) of the periodic table. These semiconductors are referred to as III-V semiconductors and include, for example, GaAs, GaP, GaAsP, AlGaAs, InGaAsP, AlGaInP, and InGaN semiconductors. Other examples of semiconductors used in LEDs include compounds from Group 14 (IV-IV semiconductor) and Group 12-16 (II-V1). The choice of materials is based on multiple factors including desired wavelength of emission, performance parameters, and cost.

Early LEDs used gallium arsenide (GaAs) to emit infrared (IR) radiation and low intensity red light. Advances in materials science have led to the development of LEDs capable of emitting light with higher intensity and shorter wavelengths, including other colors of visible light and UV light. It is possible to create LEDs that emit light across a wide wavelength spectrum, for example, from a low of about 100 nm to a high of about 900 nm. Typically, LED UV light sources currently emit light at wavelengths between 300 and 475 nm, with 365 nm, 390 nm, and 395 nm being common peak spectral outputs. See textbook,“Light-Emitting Diodes” by E. Fred Schubert, 2″ Edition, © E. Fred Schubert 2006, published by Cambridge University Press.

Several manufacturers offer LED lamps for commercial curing applications. For example, Phoseon Technology, Summit UV, Honle UV America, Inc., IST Metz GmbH, Jenton International Ltd., Lumos Solutions Ltd., Solid UV Inc., Seoul Optodevice Co., Ltd., Spectronics Corporation, Luminus Devices Inc., and Clearstone Technologies, are some of the manufacturers offering LED lamps for curing ink-jet printing compositions, PVC floor coating compositions, metal coating compositions, plastic coating composition, and adhesive compositions.

LED curing devices are used in dental work. An example of such a device is the ELIPAR™ FreeLight 2 LED curing light from 3M ESPE. This device emits light in the visible region with a peak irradiance at 460 nm. LED equipment is also being tested for use in the ink-jet printing, including, for example, by IST Metz.

Although LED lamps are available, photocurable compositions suitable for additive fabrication and curable by the use of LED light are not well known commercially. For example, U.S. Pat. No. 7,211,368 reportedly discloses a liquid stereolithography resin comprising a first urethane acrylate oligomer, a first acrylate monomer, a polymerization modifier, a second urethane acrylate oligomer different from the first urethane acrylate oligomer, and a stabilizer. The first urethane acrylate oligomer is an aliphatic polyester urethane diacrylate oligomer, the first acrylate monomer is ethoxylated (3) trimethylolpropane acrylate, and the polymerization modifier is selected from the group consisting of isobornyl acrylate, ethoxylated (5) pentaerythritol tetraacrylate, an aliphatic urethane acrylate, tris-(2-hydroxyethyl)isocyanurate triacrylate, and mixtures thereof. The resin includes 5-35 weight % of an aliphatic polyester urethane diacrylate oligomer and 0.5-25 weight % ethoxylated (3) trimethylolpropane acrylate, wherein the resin includes 15-45 weight % ethoxylated (5) pentaerythritol tetraacrylate. However, the '368 patent indicates that a laser is used to cure the resin. Further, the '368 patent fails to disclose the use of an acid generating photoinitiator, such as a cationic photoinitiator.

More recently, some attention has been given to the use of LEDs in additive fabrication processes. U.S. Pat. No. 6,927,018 and U.S. Patent Application Publication No. 2005/0227186 purportedly provide a method, article of manufacture and system for fabricating an article using photo-activatable building material. The method according to the '018 patent and the '186 publication includes the steps of applying a layer of the photo-activatable building material to a preselected surface, scanning the layer using a plurality of light-emitting centers to photo-activate the layer of photo-activatable building material in accordance with a predetermined photo-initiation process to obtain polymerization of the building material. Scanning is accomplished at a predetermined distance using a predetermined light intensity, and repeating the steps of applying the layer. Each layer is applied to an immediately previous layer, and the layer is scanned with the plurality of light-emitting centers to polymerize the building material until the article is fabricated. While the '018 patent and the '186 publication mention UV LEDs and laser diodes as suitable light-emitting centers, they fail to disclose detailed information on photo-activatable building material suitable for LED cure.

U.S. Pat. No. 7,270,528 purportedly discloses a flash curing system for solid freeform fabrication which generates a plurality of radiation emitting pulses that forms a planar flash. The planar flash initiates curing of a curable material dispensed by a solid freeform fabrication apparatus. The '528 patent, while mentioning UV light-emitting diodes (LED) lamps in the specification, sets forth examples where a flash lamp is used to cure the resin composition. The resin composition illustrated in the '528 patent does contain a cationically curable monomer or a cationic photoinitiator.

U.S. Patent Application Publication No. 2008/0231731 or 2008/0169589 or European Patent Application No. EP 1950032 purportedly discloses a solid imaging apparatus that includes a replaceable cartridge containing a source of build material and an extendable and retractable flexible transport film for transporting the build material layer-by-layer from the cartridge to the surface of a build in an image plane. If desired, the apparatus can produce a fully reacted build. A high intensity UV source is said to cure the build between layers. The above publications state that the solid imaging radiation that is used to cure the build material can be “any actinic radiation which causes a photocurable liquid to react to produce a solid, whether a visible or UV source or other source,”

International Patent Publication No. WO 2008/118263 is directed to a system for building a three-dimensional object based on build data representing the three-dimensional object, wherein the system includes an extrusion head that deposits a radiation-curable material in consecutive layers at a high deposition rate. The radiation-curable material of each of the consecutive layers is cooled to a self-supporting state. The system is said to include a radiation source that selectively exposes portions of the consecutive layers to radiation at a high resolution in accordance with the build data. It is stated that the exposure head includes a linear array of high resolution, UV light-emitting diodes (LEDs). P71-1464 CUREBAR™ and P150-3072 PRINTHEAD™ are described as examples of suitable UV-radiation sources for the exposure head. The '263 publication fails to describe exemplary photocurable formulations suitable for curing by LED light in an additive fabrication process.

International Patent Publication No. WO 2005/103121, entitled “Method for photocuring of Resin Compositions”, assigned to DSM IP Assets B.V., describes and claims Methods for Light Emitting Diode (LED) curing of a curable resin composition containing a photoinitiating system, characterized in that the highest wavelength at which absorption maximum of the photoinitiating system occurs (λ_{Max PIS}) is at least 20 nm below, and at most 100 nm below, the wavelength at which the emission maximum of the LED occurs (λ_LED). The invention in this PCT patent application relates to the use of LED curing in structural applications, in particular in applications for the lining or relining of objects, and to objects containing a cured resin composition obtained by LED curing. This invention provides a simple, environmentally safe and readily controllable method for (re)lining pipes, tanks and vessels, especially for such pipes and equipment having a large diameter, in particular more than 15 cm. The specification does not describe LED radiation curable photocurable resins.

U.S. Patent Application Publication No. 2007/0205528 reportedly discloses an optical molding process wherein the radiation source used is a non-coherent source of radiation. The '528 publication indicates that the photocurable compositions are formulated so as to enable the production of three-dimensional articles having better performance when irradiated with conventional (non-coherent) UV rather than with Laser UV, and states that the photocurable compositions disclosed are more appropriate for UV non-coherent irradiation than for Laser UV. While the '528 publication mentions that “the exposure system uses irradiation from non-coherent light sources, e.g., a xenon fusion lamp, or light emitting diode bars,” the exemplified exposure was reportedly carried out according to the method of WO 00/21735, which is said to describe an apparatus and a method wherein the photosensitive material is exposed to a light source illuminating a cross-section of a material by at least two modulator arrangements of individually controllable light modulators.

U.S. Patent Application Publication No. 2009/0267269A or WO 2009/132245 reportedly discloses a continuous-wave (CW) ultraviolet (UV) curing system for solid freeform fabrication (SFF), wherein the curing system is configured to provide an exposure of UV radiation for one or more layers of UV-curable material. It is reported that one or more UV exposures may initiate curing of a curable material in the layer dispensed by a solid freeform fabrication apparatus. According to the '269 or '245 publication, one approach to provide the single or multiple UV exposures is the use of one or more UV LEDs, which generate UV radiation without generating any substantial amounts of infrared (IR) radiation at the same time.

The foregoing shows that there is an unmet need to provide photocurable resin compositions for additive fabrication which are capable of curing by irradiation by LED light.

BRIEF SUMMARY OF THE INVENTION

The invention provides a photocurable resin composition for additive fabrication comprising a polymerizable component that is polymerizable by free-radical polymerization, by cationic polymerization, or by both free-radical polymerization and cationic polymerization, and a photoinitiating system capable of initiating the free-radical polymerization, cationic polymerization, or both free-radical polymerization and cationic polymerization. The invention also provides a three-dimensional article comprising a cured resin composition which is obtained by curing the photocurable resin composition for additive fabrication, and a method of curing the photocurable resin composition for additive fabrication.

In an embodiment, wherein the ratio by weight of cationic photoinitiator to free-radical photoinitiator is less than about 4.0.

In another embodiment, the ratio by weight of cationic polymerizable component to free-radical polymerizable component is less than about 7.0.

In another embodiment, greater than at least 30 wt % of the ingredients in the photocurable resin composition for additive fabrication are bio-based, rather than petroleum based.

In an aspect, the invention provides a photocurable resin composition for additive fabrication comprising a polymerizable component that is polymerizable by free-radical polymerization, by cationic polymerization, or by both free-radical polymerization and cationic polymerization, and a photoinitiating system capable of initiating the free-radical polymerization, cationic polymerization, or both free-radical polymerization and cationic polymerization; wherein the photocurable resin composition for additive fabrication is a liquid at about 25° C., and is capable of curing to provide a solid upon irradiation with light emitted from a light emitting diode (LED), wherein the light has a wavelength of from about 100 nm to about 900 nm; and wherein the liquid photocurable resin composition for additive fabrication has a Critical Exposure (Ec) and a Depth of Penetration (Dp) as measured on a layer of the resin composition for additive fabrication as the composition is curing upon exposure to LED light, wherein Ec is less than about 6.0 seconds and Dp is ¼ to 4 times the thickness of the layer.

In another aspect, the invention provides a three-dimensional article comprising a cured photocurable resin, wherein the cured photocurable resin is obtained by curing a photocurable resin composition for additive fabrication by irradiating it with light emitted from a light emitting diode (LED) light having a wavelength from about 100 nm to about 900 nm; the photocurable resin composition for additive fabrication comprising: a polymerizable component that is polymerizable by free-radical polymerization, cationic polymerization, or both free-radical polymerization and cationic polymerization, and a photoinitiating system capable of initiating the free-radical polymerization, cationic polymerization, or both free-radical polymerization and cationic polymerization; wherein the photocurable resin composition is a liquid at about 25° C., and is capable of curing to provide a solid upon irradiation with light emitted from a light emitting diode (LED), wherein the light has a wavelength of from about 100 nm to about 900 nm, and wherein the liquid photocurable resin composition has a Critical Exposure (Ec) and a Depth of Penetration (Dp) as measured on a layer of the photocurable resin composition as the composition is curing, wherein Ec is from about 0.01 seconds to about 6.0 seconds and Dp is ¼ to 4 times the thickness of the layer.

In a further aspect, the invention provides a process for making a three-dimensional article comprising the steps of: forming and selectively curing a layer of a photocurable resin composition by irradiation with a light emitting diode (LED) light having a wavelength from about 100 nm to about 900 nm, the photocurable resin composition comprising: a polymerizable component that is polymerizable by free-radical polymerization, cationic polymerization, or both free-radical polymerization and cationic polymerization, and a photoinitiating system capable of initiating the free-radical polymerization, cationic polymerization, or both free-radical polymerization and cationic polymerization; wherein the photocurable resin composition is a liquid at about 25° C., and is capable of curing to provide a solid upon exposure to a light emitting diode (LED) light having a wavelength of from about 100 nm to about 900 nm, and wherein the liquid photocurable resin composition has a Critical Exposure (Ec) and a Depth of Penetration (Dp) as measured on a layer of the photocurable resin composition as the composition is curing, wherein Ec is from about 0.01 seconds to about 6.0 seconds and Dp is ¼ to 4 times the thickness of the layer; and repeating the steps of forming and selectively curing a layer of the photocurable resin composition a plurality of times to obtain the three-dimensional article.

DETAILED DESCRIPTION OF THE INVENTION

The present invention provides a LED photocurable resin composition for additive fabrication comprising a polymerizable component that is polymerizable by at least one of a free-radically initiated polymerization and a cationically initiated polymerization, and a photoinitiating system capable of initiating the polymerization of a free-radically polymerizable component and/or the cationically polymerizable component. The photocurable resin composition for additive fabrication of the invention is characterized by one or more advantages, for example, rapid cure and improved mechanical properties of the resulting cured resin and the three-dimensional article.

In accordance with an embodiment, the photocurable resin composition is a liquid at about 25° C., and is capable of curing to provide a solid upon irradiation with light emitted from a light emitting diode (LED), wherein the light has a wavelength of from about 100 nm to about 900 nm.

The wavelength of the light can be in the UV or visible region or higher into the infrared region. In the UV range, UVA, UVB, and UVC are possible, which are characterized by the wavelength of from about 320 to about 400 nm, from about 280 to about 320 nm, and from about 100 to about 280 nm, respectively.

The photocurable resin composition for additive fabrication is highly photosensitive. For example, it has a Critical Exposure (Ec) and a Depth of Penetration (Dp) as measured on a layer of the photocurable resin composition as the composition is curing, wherein Ec is from about 0.01 seconds to about 6.0 seconds and Dp is about ¼ to about 4 times the thickness of the layer. In an embodiment, the wavelength of the LED light is 365 nm.

In embodiments, Ec is about 0.01 seconds to about 1, 2, 3, 4, 5, or 6 seconds. In embodiments, Dp is about ¼ to about 2 times the thickness of the layer. In an embodiment, Ec is from about 0.01 seconds to about 2.0 seconds.

The photosensitivity of the liquid formulations was determined by using a technique similar to the so-called WINDOWPANES™ technique, a technique known to those skilled in the art of stereolithography. In this technique, single-layer test specimens are produced by using different amounts of exposure energies to cure the liquid formulation to solid, and the solid resin layer thicknesses obtained are measured. The resulting layer thickness is plotted on a graph against the natural logarithm of the irradiation energy used to provide a “working curve.” The slope of this curve is termed Dp (given in mm or mils). The energy value at which the curve passes through the x-axis is termed Ec (and is the energy at which gelling of the material just takes place; P. Jacobs, Rapid Prototyping and Manufacturing, Soc. of Manufacturing Engineers, 1992, p. 270 ff.). Alternatively, the exposure time (in seconds) rather than the exposure energy (in mW/cm²) is used for calculating the Ec values when the intensity of the irradiation light is constant, as in the case of using LED light as the light curing sources.

In a particular embodiment, Dp is from about 1 to about 8 mils, more particularly from about 1 to about 7 mils, and in embodiments, from about 1 mil to about 7 mils or from about 2 to about 5 mils, even more particularly from about 2 mils to about 4 mils.

Embodiments of the invention include photocurable resin compositions which display advantageous mechanical properties such as storage modulus as it is curing. For example, the photocurable resin composition, as it is curing has a storage shear modulus (G′) value greater than 1.0×10⁵ Pa, e.g., from about 5.0×10⁵ Pa to about 1.0×10⁶ Pa or to about 1.0×10⁷ Pa, when measured on a Real Time-Dynamic Mechanical Analyzer (RT-DMA) with an 8 mm plate and a sample gap of 0.10 mm at 3.9 seconds from the beginning of light exposure of 44-50 mW/cm² light intensity for 1.0 second. In some embodiments, the G′ value is from about 6.0×10⁵ Pa to about 9.0×10⁵ Pa, and in some other embodiments, the G′ value is from about 7.0×10⁵ Pato about 8.0×10⁵ Pa.

In accordance with an embodiment, the photocurable resin composition for additive fabrication includes at least one free-radical polymerizable component and at least one cationic polymerizable component.

In accordance with an embodiment of the invention, the photocurable resin composition for additive fabrication of the invention comprises at least one free-radical polymerizable component, that is, a component which undergoes polymerization initiated by free radicals. The free-radical polymerizable components are monomers, oligomers, and/or polymers; they are monofunctional or polyfunctional materials, i.e., have 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 20, 30, 40, 50, 100, or more functional groups that can polymerize by free radical initiation, may contain aliphatic, aromatic, cycloaliphatic, arylaliphatic, heterocyclic moiety(ies), or any combination thereof. Examples of polyfunctional materials include dendritic polymers such as dendrimers, linear dendritic polymers, dendrigraft polymers, hyperbranched polymers, star branched polymers, and hypergraft polymers; see US 2009/0093564 A1. The dendritic polymers may contain one type of polymerizable functional group or different types of polymerizable functional groups, for example, acrylates and methacrylate functions.

Examples of free-radical polymerizable components include acrylates and methacrylates such as isobornyl (meth)acrylate, bornyl (meth)acrylate, tricyclodecanyl (meth)acrylate, dicyclopentanyl (meth)acrylate, dicyclopentenyl (meth)acrylate, cyclohexyl (meth)acrylate, benzyl (meth)acrylate, 4-butylcyclohexyl (meth)acrylate, acryloyl morpholine, (meth)acrylic acid, 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate, methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, isopropyl (meth)acrylate, butyl (meth)acrylate, amyl (meth)acrylate, isobutyl (meth)acrylate, t-butyl (meth)acrylate, pentyl (meth)acrylate, caprolactone acrylate, isoamyl (meth)acrylate, hexyl (meth)acrylate, heptyl (meth)acrylate, octyl (meth)acrylate, isooctyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, nonyl (meth)acrylate, decyl (meth)acrylate, isodecyl (meth)acrylate, tridecyl (meth)acrylate, undecyl (meth)acrylate, lauryl (meth)acrylate, stearyl (meth)acrylate, isostearyl (meth)acrylate, tetrahydrofurfuryl (meth)acrylate, butoxyethyl (meth)acrylate, ethoxydiethylene glycol (meth)acrylate, benzyl (meth)acrylate, phenoxyethyl (meth)acrylate, polyethylene glycol mono(meth)acrylate, polypropylene glycol mono(meth)acrylate, methoxyethylene glycol (meth)acrylate, ethoxyethyl (meth)acrylate, methoxypolyethylene glycol (meth)acrylate, methoxypolypropylene glycol (meth)acrylate, diacetone (meth)acrylamide, beta-carboxyethyl (meth)acrylate, phthalic acid (meth)acrylate, dimethylaminoethyl (meth)acrylate, diethylaminoethyl (meth)acrylate, butylcarbamylethyl (meth)acrylate, n-isopropyl (meth)acrylamide fluorinated (meth)acrylate, 7-amino-3,7-dimethyloctyl (meth)acrylate.

Examples of polyfunctional free-radical polymerizable components include those with (meth)acryloyl groups such as trimethylolpropane tri(meth)acrylate, pentaerythritol (meth)acrylate, ethylene glycol di(meth)acrylate, bisphenol A diglycidyl ether di(meth)acrylate, dicyclopentadiene dimethanol di(meth)acrylate, [2-[1,1-dimethyl-2-[(1-oxoallyl)oxy]ethyl]-5-ethyl-1,3-dioxan-5-yl]methyl acrylate; 3,9-bis(1,1-dimethyl-2-hydroxyethyl)-2,4,8,10-tetraoxaspiro[5.5]undecane di(meth)acrylate; dipentaerythritol monohydroxypenta(meth)acrylate, propoxylated trimethylolpropane tri(meth)acrylate, propoxylated neopentyl glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, polyethylene glycol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, polybutanediol di(meth)acrylate, tripropyleneglycol di(meth)acrylate, glycerol tri(meth)acrylate, phosphoric acid mono- and di(meth)acrylates, C₇-C₂₀ alkyl di(meth)acrylates, tris(2-hydroxyethyl)isocyanurate tri(meth)acrylate, tris(2-hydroxyethyl)isocyanurate di(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol hexa(meth)crylate, tricyclodecane diyl dimethyl di(meth)acrylate and alkoxylated versions (e.g., ethoxylated and/or propoxylated) of any of the preceding monomers, and also di(meth)acrylate of a diol which is an ethylene oxide or propylene oxide adduct to bisphenol A, di(meth)acrylate of a diol which is an ethylene oxide or propylene oxide adduct to hydrogenated bisphenol A, epoxy (meth)acrylate which is a (meth)acrylate adduct to bisphenol A of diglycidyl ether, diacrylate of polyoxyalkylated bisphenol A, and triethylene glycol divinyl ether, and adducts of hydroxyethyl acrylate.

In accordance with an embodiment, the polyfunctional (meth)acrylates of the polyfunctional component may include all methacryloyl groups, all acryloyl groups, or any combination of methacryloyl and acryloyl groups. In an embodiment, the free-radical polymerizable component is selected from the group consisting of bisphenol A diglycidyl ether di(meth)acrylate, ethoxylated or propoxylated bisphenol A or bisphenol F di(meth)acrylate, dicyclopentadiene dimethanol di(meth)acrylate, [2-[1,1-dimethyl-2-[(1-oxoallyl)oxy]ethyl]-5-ethyl-1,3-dioxan-5-yl]methyl acrylate, dipentaerythritol monohydroxypenta(meth)acrylate, dipentaerythritol hexa(meth)crylate, propoxylated trimethylolpropane tri(meth)acrylate, and propoxylated neopentyl glycol di(meth)acrylate, and any combination thereof.

In another embodiment, the free-radical polymerizable component is selected from the group consisting of bisphenol A diglycidyl ether diacrylate, dicyclopentadiene dimethanol diacrylate, [2-[1,1-dimethyl-2-[(1-oxoallyl)oxy]ethyl]-5-ethyl-1,3-dioxan-5-yl]methyl acrylate, dipentaerythritol monohydroxypentaacrylate, propoxylated trimethylolpropane triacrylate, and propoxylated neopentyl glycol diacrylate, and any combination thereof.

In specific embodiments, the photocurable resin compositions for additive fabrication of the invention include one or more of bisphenol A diglycidyl ether di(meth)acrylate, dicyclopentadiene dimethanol di(meth)acrylate, dipentaerythritol monohydroxypenta(meth)acrylate, propoxylated trimethylolpropane tri(meth)acrylate, and/or propoxylated neopentyl glycol di(meth)acrylate, and more specifically one or more of bisphenol A diglycidyl ether diacrylate, dicyclopentadiene dimethanol diacrylate, dipentaerythritol monohydroxypentaacrylate, propoxylated trimethylolpropane triacrylate, and/or propoxylated neopentyl glycol diacrylate.

The photocurable resin composition for additive fabrication can include any suitable amount of the free-radical polymerizable component, for example, in certain embodiments, in an amount up to about 95% by weight of the composition, in certain embodiments, up to about 50% by weight of the composition, and in further embodiments from about 5% to about 25% by weight of the composition.

In accordance with an embodiment, the photocurable resin compositions for additive fabrication of the invention comprise at least one cationically polymerizable component, that is, a component which undergoes polymerization initiated by cations or in the presence of acid generators. The cationically polymerizable components may be monomers, oligomers, and/or polymers, and may contain aliphatic, aromatic, cycloaliphatic, arylaliphatic, heterocyclic moiety(ies), and any combination thereof. Suitable cyclic ether compounds can comprise cyclic ether groups as side groups or groups that form part of an alicyclic or heterocyclic ring system.

The cationic polymerizable component is selected from the group consisting of cyclic ether compounds, cyclic acetal compounds, cyclic thioethers compounds, spiro-orthoester compounds, cyclic lactone compounds, and vinyl ether compounds, and any combination thereof.

Examples of cationically polymerizable components include cyclic ether compounds such as epoxy compounds and oxetanes, cyclic lactone compounds, cyclic acetal compounds, cyclic thioether compounds, Spiro orthoester compounds, and vinylether compounds. Specific examples of cationically polymerizable components include bisphenol A diglycidyl ether, bisphenol F diglycidyl ether, bisphenol S diglycidyl ether, brominated bisphenol A diglycidyl ether, brominated bisphenol F diglycidyl ether, brominated bisphenol S diglycidyl ether, epoxy novolac resins, hydrogenated bisphenol A diglycidyl ether, hydrogenated bisphenol F diglycidyl ether, hydrogenated bisphenol S diglycidyl ether, 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexanecarboxylate, 2-(3,4-epoxycyclohexyl-5,5-spiro-3,4-epoxy)-cyclohexane-1,4-dioxane, bis(3,4-epoxycyclohexylmethyl)adipate, vinylcyclohexene oxide, 4-vinylepoxycyclohexane, vinylcyclohexene dioxide, limonene oxide, limonene dioxide, bis(3,4-epoxy-6-methylcyclohexylmethyl)adipate, 3,4-epoxy-6-methylcyclohexyl-3′,4′-epoxy-6′-methylcyclohexanecarboxylate, ε-caprolactone-modified 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexane carboxylates, trimethylcaprolactone-modified 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexane carboxylates, β-methyl-δ-valerolactone-modified 3,4-epoxycyclohexcylmethyl-3′,4′-epoxycyclohexane carboxylates, methylenebis(3,4-epoxycyclohexane), bicyclohexyl-3,3′-epoxide, bis(3,4-epoxycyclohexyl) with a linkage of —O—, —S—, —SO—, —SO₂—, —C(CH₃)₂—, —C(CBr₃)₂—, —C(CF₃)₂—, —C(CCl₃)₂—, or —CH(C₆H₅)—, dicyclopentadiene diepoxide, di(3,4-epoxycyclohexylmethyl)ether of ethylene glycol, ethylenebis(3,4-epoxycyclohexanecarboxylate), epoxyhexahydrodioctylphthalate, epoxyhexahydro-di-2-ethylhexyl phthalate, 1,4-butanediol diglycidyl ether, 1,6-hexanediol diglycidyl ether, neopentylglycol diglycidyl ether, glycerol triglycidyl ether, trimethylolpropane triglycidyl ether, polyethylene glycol diglycidyl ether, polypropylene glycol diglycidyl ether, polyglycidyl ethers of polyether polyol obtained by the addition of one or more alkylene oxides to aliphatic polyhydric alcohols such as ethylene glycol, propylene glycol, and glycerol, diglycidyl esters of aliphatic long-chain dibasic acids, monoglycidyl ethers of aliphatic higher alcohols, monoglycidyl ethers of phenol, cresol, butyl phenol, or polyether alcohols obtained by the addition of alkylene oxide to these compounds, glycidyl esters of higher fatty acids, epoxidated soybean oil, epoxybutylstearic acid, epoxyoctylstearic acid, epoxidated linseed oil, epoxidated polybutadiene, 1,4-bis[(3-ethyl-3-oxetanylmethoxy)methyl]benzene, 3-ethyl-3-hydroxymethyloxetane, 3-ethyl-3-(3-hydroxypropyl)oxymethyloxetane, 3-ethyl-3-(4-hydroxybutyl)oxymethyloxetane, 3-ethyl-3-(5-hydroxypentyl)oxymethyloxetane, 3-ethyl-3-phenoxymethyloxetane, bis((1-ethyl(3-oxetanyl))methyl)ether, 3-ethyl-3-((2-ethylhexyloxy)methyl)oxetane, 3-ethyl-((triethoxysilylpropoxymethyl)oxetane, 3-(meth)-allyloxymethyl-3-ethyloxetane, (3-ethyl-3-oxetanylmethoxy)methylbenzene, 4-fluoro-[1-(3-ethyl-3-oxetanylmethoxy)methyl]benzene, 4-methoxy-[1-(3-ethyl-3-oxetanylmethoxy)methyd-benzene, [1-(3-ethyl-3-oxetanylmethoxy)ethyl]phenyl ether, isobutoxymethyl(3-ethyl-3-oxetanylmethyl)ether, 2-ethylhexyl(3-ethyl-3-oxetanylmethyl)ether, ethyldiethylene glycol(3-ethyl-3-oxetanylmethyl)ether, dicyclopentadiene (3-ethyl-3-oxetanylmethyl)ether, dicyclopentenyloxyethyl(3-ethyl-3-oxetanylmethyl)ether, dicyclopentenyl(3-ethyl-3-oxetanylmethyl)ether, tetrahydrofurfuyl(3-ethyl-3-oxetanylmethyl)ether, 2-hydroxyethyl(3-ethyl-3-oxetanylmethyl)ether, 2-hydroxypropyl(3-ethyl-3-oxetanylmethyl)ether, and any combination thereof. Examples of polyfunctional materials that are cationically polymerizable include dendritic polymers such as dendrimers, linear dendritic polymers, dendrigraft polymers, hyperbranched polymers, star branched polymers, and hypergraft polymers with epoxy or oxetane functional groups. The dendritic polymers may contain one type of polymerizable functional group or different types of polymerizable functional groups, for example, epoxy and oxetane functions.

In embodiments of the invention, the cationic polymerizable component is at least one selected from the group consisting of a cycloaliphatic epoxy and an oxetane. In a specific embodiment, the cationic polymerizable component is an oxetane, for example, an oxetane containing 2 or more than 2 oxetane groups. In another specific embodiment, the cationic polymerizable component is a cycloaliphatic epoxy, for example, a cycloaliphatic epoxy with 2 or more than 2 epoxy groups.

In an embodiment, the epoxide is 3,4-epoxycyclohexylmethyl-3′,4-epoxycyclohexanecarboxylate (available as CELLOXIDE™ 2021 P from Daicel Chemical, or as CYRACURE™ UVR-6105 from Dow Chemical), hydrogenated bisphenol A-epichlorohydrin based epoxy resin (available as EPONEX™ 1510 from Hexion), 1,4-cyclohexanedimethanol diglycidyl ether (available as HELOXY™ 107 from Hexion), a mixture of dicyclohexyl diepoxide and nanosilica (available as NANOPDX™), and any combination thereof.

The above-mentioned cationically polymerizable compounds can be used singly or in combination of two or more thereof.

The photocurable resin composition for additive fabrication can include any suitable amount of the cationic polymerizable component, for example, in certain embodiments, in an amount up to about 95% by weight of the composition, and in certain embodiments, up to about 50% by weight of the composition. In further embodiments the amount of the cationic polymerizable component is from about 5% to about 70% by weight of the composition. In further embodiments from about 5% to about 25% by weight of the composition

In accordance with an embodiment, the polymerizable component of the photocurable resin composition for additive fabrication is polymerizable by both free-radical polymerization and cationic polymerization. An example of such a polymerizable component is a vinyloxy compound, for example, one selected from the group consisting of bis(4-vinyloxybutyl)isophthalate, tris(4-vinyloxybutyl) trimellitate, and combinations thereof. Other examples of such a polymerizable component include those that contain an acrylate and an epoxy group, or an acrylate and an oxetane group, on a same molecule.

In embodiments, the photocurable resin composition for additive fabrication of the present invention includes a photoinitiating system. The photoinitiating system can be a free-radical photoinitiator or a cationic photoinitiator or a photoinitiator that contains both free-radical initiating function and cationic initiating function on the same molecule. The photoinitiator is a compound that chemically changes due to the action of light or the synergy between the action of light and the electronic excitation of a sensitizing dye to produce at least one of a radical, an acid, and a base.

Typically, free radical photoinitiators are divided into those that form radicals by cleavage, known as “Norrish Type I” and those that form radicals by hydrogen abstraction, known as “Norrish type II”. The Norrish type II photoinitiators require a hydrogen donor, which serves as the free radical source. As the initiation is based on a bimolecular reaction, the Norrish type II photoinitiators are generally slower than Norrish type I photoinitiators which are based on the unimolecular formation of radicals. On the other hand, Norrish type II photoinitiators possess better optical absorption properties in the near-UV spectroscopic region. Photolysis of aromatic ketones, such as benzophenone, thioxanthones, benzil, and quinones, in the presence of hydrogen donors, such as alcohols, amines, or thiols leads to the formation of a radical produced from the carbonyl compound (ketyl-type radical) and another radical derived from the hydrogen donor. The photopolymerization of vinyl monomers is usually initiated by the radicals produced from the hydrogen donor. The ketyl radicals are usually not reactive toward vinyl monomers because of the steric hindrance and the delocalization of an unpaired electron.

To successfully formulate a photocurable resin composition for additive fabrication, it is necessary to review the wavelength sensitivity of the photoinitiator(s) present in the composition to determine if they will be activated by the LED light chosen to provide the curing light.

In accordance with an embodiment, the photocurable resin composition for additive fabrication includes at least one free radical photoinitiator, e.g., those selected from the group consisting of benzoylphosphine oxides, aryl ketones, benzophenones, hydroxylated ketones, 1-hydroxyphenyl ketones, ketals, metallocenes, and any combination thereof.

In an embodiment, the photocurable resin composition for additive fabrication includes at least one free-radical photoinitiator selected from the group consisting of 2,4,6-trimethylbenzoyl diphenylphosphine oxide and 2,4,6-trimethylbenzoyl phenyl, ethoxy phosphine oxide, bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide, 2-methyl-1-[4-(methylthio)phenyl]-2-morpholinopropanone-1,2-benzyl-2-(dimethylamino)-1-[4-(4-morpholinyl)phenyl]-1-butanone, 2-dimethylamino-2-(4-methyl-benzyl)-1-(4-morpholin-4-yl-phenyl)-butan-1-one, 4-benzoyl-4′-methyl diphenyl sulphide, 4,4′-bis(diethylamino) benzophenone, and 4,4′-bis(N,N′-dimethylamino)benzophenone (Michler's ketone), benzophenone, 4-methyl benzophenone, 2,4,6-trimethyl benzophenone, dimethoxybenzophenone, 1-hydroxycyclohexyl phenyl ketone, phenyl (1-hydroxyisopropyl)ketone, 2-hydroxy-1-[4-(2-hydroxyethoxy)phenyl]-2-methyl-1-propanone, 4-isopropylphenyl(1-hydroxyisopropyl)ketone, oligo-[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone], camphorquinone, 4,4′-bis(diethylamino)benzophenone, benzyl dimethyl ketal, bis(eta 5-2-4-cyclopentadien-1-yl) bis[2,6-difluoro-3-(1H-pyrrol-1-yl)phenyl]titanium, and any combination thereof.

For LED light sources emitting in the 300-475 nm wavelength range, especially those emitting at 365 nm, 390 nm, or 395 nm, examples of suitable free-radical photoinitiators absorbing in this area include: benzoylphosphine oxides, such as, for example, 2,4,6-trimethylbenzoyl diphenylphosphine oxide (Lucirin TPO from BASF) and 2,4,6-trimethylbenzoyl phenyl, ethoxy phosphine oxide (Lucirin TPO-L from BASF), bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide (Irgacure 819 or BAPO from Ciba), 2-methyl-1-[4-(methylthio)phenyl]-2-morpholinopropanone-1 (Irgacure 907 from Ciba), 2-benzyl-2-(dimethylamino)-1-[4-(4-morpholinyl)phenyl]-1-butanone (Irgacure 369 from Ciba), 2-dimethylamino-2-(4-methyl-benzyl)-1-(4-morpholin-4-yl-phenyl)-butan-1-one (Irgacure 379 from Ciba), 4-benzoyl-4′-methyl diphenyl sulphide (Chivacure BMS from Chitec), 4,4′-bis(diethylamino) benzophenone (Chivacure EMK from Chitec), and 4,4′-bis(N,N′-dimethylamino)benzophenone (Michler's ketone). Also suitable are mixtures thereof.

Additionally, photosensitizers are useful in conjunction with photoinitiators in effecting cure with LED light sources emitting in this wavelength range. Examples of suitable photosensitizers include: anthraquinones, such as 2-methylanthraquinone, 2-ethylanthraquinone, 2-tertbutylanthraquinone, 1-chloroanthraquinone, and 2-amylanthraquinone, thioxanthones and xanthones, such as isopropyl thioxanthone, 2-chlorothioxanthone, 2,4-diethylthioxanthone, and 1-chloro-4-propoxythioxanthone, methyl benzoyl formate (Darocur MBF from Ciba), methyl-2-benzoyl benzoate (Chivacure OMB from Chitec), 4-benzoyl-4′-methyl diphenyl sulphide (Chivacure BMS from Chitec), 4,4′-bis(diethylamino)benzophenone (Chivacure EMK from Chitec).

It is possible for LED UV light sources to be designed to emit light at shorter wavelengths. In embodiments, a photosensitizer is used when curing with LED light sources emitting at wavelengths from between about 100 and about 300 nm. When photosensitizers, such as those previously listed are present in the formulation, other photoinitiators absorbing at shorter wavelengths can be used. Examples of such photoinitiators include: benzophenones, such as benzophenone, 4-methyl benzophenone, 2,4,6-trimethyl benzophenone, and dimethoxybenzophenone, and, 1-hydroxyphenyl ketones, such as 1-hydroxycyclohexyl phenyl ketone, phenyl (1-hydroxyisopropyl)ketone, 2-hydroxy-1-[4-(2-hroxyethoxy)phenyl]-2-methyl-1-propanone, and 4-isopropylphenyl(1-hydroxyisopropyl)ketone, benzil dimethyl ketal, and oligo-[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone] (Esacure KIP 150 from Lambeth).

LED light sources can also be designed to emit visible light. For LED light sources emitting light at wavelengths from about 475 nm to about 900 nm, examples of suitable free radical photoinitiators include: camphorquinone, 4,4′-bis(diethylamino)benzophenone (Chivacure EMK from Chitec), 4,4′-bis(N,N′-dimethylamino)benzophenone (Michler's ketone), bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide (Irgacure 819 or BAPO from Ciba), metallocenes such as bis(eta 5-2-4-cyclopentadien-1-yl) bis[2,6-difluoro-3-(1H-pyrrol-1-yl)phenyl]titanium (Irgacure 784 from Ciba), and the visible light photoinitiators from Spectra Group Limited, Inc. such as H-Nu 470, H-Nu-535, H-Nu-635, H-Nu-Blue-640, and H-Nu-Blue-660. It is often desirable to employ a photosensitizer with a photoinitiator for LED light sources emitting between 475 nm and 900 nm.

In one embodiment of the instant claimed invention, the light emitted by the LED is UVA radiation, which is radiation with a wavelength between about 320 and about 400 nm. In one embodiment of the instant claimed invention, the light emitted by the LED is UVB radiation, which is radiation with a wavelength between about 280 and about 320 nm. In one embodiment of the instant claimed invention, the light emitted by the LED is UVC radiation, which is radiation with a wavelength between about 100 and about 280 nm.

The photocurable resin composition for additive fabrication can include any suitable amount of the free-radical photoinitiator, for example, in certain embodiments, in an amount up to about 15% by weight of the composition, in certain embodiments, up to about 10% by weight of the composition, and in further embodiments from about 1% to about 5% by weight of the composition.

In accordance with an embodiment, the photocurable resin composition for additive fabrication includes a photoinitiating system that is a photoinitiator having both cationic initiating function and free radical initiating function.

In accordance with an embodiment, the photocurable resin composition for additive fabrication includes a cationic photoinitiator. The cationic photoinitiator generates photoacids upon irradiation of light. They generate Brönsted or Lewis acids upon irradiation. Any suitable cationic photoinitiator can be used, for example, those selected from the group consisting of onium salts, halonium salts, iodosyl salts, selenium salts, sulfonium salts, sulfoxonium salts, diazonium salts, metallocene salts, isoquinolinium salts, phosphonium salts, arsonium salts, tropylium salts, dialkylphenacylsulfonium salts, thiopyrilium salts, diaryl iodonium salts, triaryl sulfonium salts, sulfonium antimonate salts, ferrocenes, di(cyclopentadienyliron)arene salt compounds, and pyridinium salts, and any combination thereof. Onium salts, e.g., iodonium salts, sulfonium salts and ferrocenes, have the advantage that they are thermally stable. Thus, any residual photoinitiator does not continue to cure after the removal of the irradiating light. Cationic photoinitiators offer the advantage that they are not sensitive to oxygen present in the atmosphere.

The photocurable resin composition for additive fabrication of the invention includes at least one cationic photoinitiator, wherein the cationic photoinitiator is selected from the group consisting of aromatic diazonium salts, aromatic sulfonium salts, aromatic iodonium salts, metallocene based compounds, aromatic phosphonium salts and silanol aluminium complexes, and any combination thereof. In an embodiment, the cationic photoinitiator is selected from the group consisting of aromatic sulfonium salts, aromatic iodonium salts, and metallocene based compounds, and any combination thereof. In another embodiment, the cationic photoinitiator is selected from the group consisting of triarylsulfonium salts, diaryliodonium salts, and metallocene based compounds, and any combination thereof.

In a particular embodiment, the cationic photoinitiator has an anion selected from the group consisting of BF₄⁻, AsF₆⁻, SbF₆⁻, PF₆⁻, B(C₆F₅)₄⁻, perfluoroalkylsulfonates, perfluoroalkylphosphates, and carborane anions.

In an embodiment, the cationic photoinitiator has a cation selected from the group consisting of aromatic sulfonium salts, aromatic iodonium salts, and metallocene based compounds with at least an anion selected from the group consisting of SbF₆⁻, PF₆⁻, B(C₆F₅)₄⁻, perfluoroalkylsulfonates, perfluoroalkylphosphates, and (CH₆B₁₁Cl₆)⁻.

In a particular embodiment, the cationic photoinitiator is an aromatic sulfonium salt based cationic photoinitiator selected from the group consisting of 4-(4-benzoylphenylthio)phenyldiphenylsulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-hydroxyethyloxyphenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-chlorophenyl)sulfonium hexafluoroantimonate, 4-[4-(3-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-methylphenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-hydroxyethylphenyl)sulfonium hexafluoroantimonate, 4-[4-(4-hydroxyethyloxybenzoyl)phenylthio]phenylbis(4-fluoro phenyl)sulfonium hexafluoroantimonate, 4-[4-(4-hydroxyethyloxybenzoyl)phenylthio]phenyldiphenylsulfonium hexafluoroantimonate, 4-[4-(4-hydroxyethyloxybenzoyl)phenylthio]phenylbis(4-hydroxyethyloxyphenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-methoxyethoxyphenyl)sulfonium hexafluoroantimonate, 4-[4-(3-methoxybenzoyl)phenylthio]phenyldiphenylsulfonium hexafluoroantimonate, 4-[4-(3-methoxycarbonylbenzoyl)phenylthio]phenyldiphenylsulfonium hexafluoroantimonate, 4-[4-(2-hydroxymethylbenzoyl)phenylthio]phenyldiphenylsulfonium hexafluoroantimonate, 4-[4-(4-methylbenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-[4-(4-) phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-[4-(4-fluorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-[4-(2-methoxycarbonylbenzoyl)phenylthio]phenylbis(4-fluoro phenyl)sulfonium hexafluoroantimonate, bis[4-(diphenylsulfonio)phenyl]sulfide bishexafluorophosphate, bis[4-(diphenylsulfonio)phenyl]sulfide bistetrafluoroborate, bis[4-(diphenylsulfonio)phenyl]sulfide tetrakis(pentafluorophenyl)borate, diphenyl-4-(phenylthio)phenylsulfonium hexafluorophosphate, diphenyl-4-(phenylthio)phenylsulfonium tetrafluoroborate, diphenyl-4-(phenylthio)phenylsulfonium tetrakis(pentafluorophenyl)borate, triphenylsulfonium hexafluorophosphate, triphenylsulfonium hexafluoroantimonate, triphenylsulfonium tetrafluoroborate, triphenylsulfonium tetrakis(pentafluorophenyl)borate, bis[4-(di(4-(2-hydroxyethoxy))phenylsulfonio)phenyl]sulfide bishexafluorophosphate, bis[4-(di(4-(2-hydroxyethoxy))phenylsulfonio)phenyl]sulfide bistetrafluoroborate, and bis[4-(di(4-(2-hydroxyethoxy))phenylsulfonio)phenyl]sulfide tetrakis(pentafluorophenyl)borate, and any combination thereof.

In another embodiment, the cationic photoinitiator is an aromatic iodonium salt based cationic photoinitiator selected from the group consisting of diphenyliodonium hexafluorophosphate, diphenyliodonium hexafluoroantimonate, diphenyliodonium tetrafluoroborate, diphenyliodonium tetrakis(pentafluorophenyl)borate, bis(dodecylphenyl)iodonium hexafluorophosphate, bis(dodecylphenyl)iodonium hexafluoroantimonate, bis(dodecylphenyl)iodonium tetrafluoroborate, bis(dodecylphenyl)iodonium tetrakis(pentafluorophenyl)borate, 4-methylphenyl-4-(1-methylethyl)phenyliodonium hexafluorophosphate, 4-methylphenyl-4-(1-methylethyl)phenyliodonium hexafluoroantimonate, 4-methylphenyl-4-(1-methylethyl)phenyliodonium tetrafluoroborate, and 4-methylphenyl-4-(1-methylethyl)phenyliodonium tetrakis(pentafluorophenyl)borate, and any combination thereof.

In certain embodiments, the cationic photoinitiator is selected from the group consisting of tetrakis(pentafluorophenyl)borate or hexafluoroantimonate salt of 4-(4-benzoylphenylthio)phenyldiphenylsulfonium, 4-(4-benzoylphenylthio)phenylbis(4-hydroxyethyloxyphenyl)sulfonium, 4-(4-benzoylphenylthio)phenylbis(4-fluorophenyl)sulfonium, 4-(4-benzoylphenylthio)phenylbis(4-chlorophenyl)sulfonium, 4-[4-(3-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium, 4-[4-(2-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium, (4-thiophenoxyphenyl)diphenylsulfonium, S,S,S′,S′-tetraphenylthiobis(4,1-phenylene)disulfonium, triphenylsulfonium, (chlorophenyl)diphenylsulfonium, chloro[S-(phenyl)thianthrenium], S-(phenyl)thianthrenium, diphenyl-4-(4′-thiophenoxy)thiophenoxyphenylsulfonium, phenyldi(4-thiophenoxyphenyl)sulfonium, S-(4-thiophenoxyphenyl)thianthrenium, and (thiodi-4,1-phenylene)bis[bis[4-(2-hydroxyethoxy)phenyl]sulfonium, tris(4-(4-acetylphenyl)thiophenyl)sulfonium, bis(4-dodecylphenyl)iodonium, [4-[(2-hydroxytetradecyl)oxy]phenyl]phenyliodonium, (4-methylphenyl)[4-[[2-[[[[3-(trifluoromethyl)phenyl]amino]carbonyl]oxy]tetradecyl]oxy]phenyl]iodonium, bis(4-dodecylphenyl)iodonium, [4-(1-methylethyl)phenyl](4-methylphenyl)iodonium, and any combination thereof.

In an illustrative embodiment, the photocurable resin composition for additive fabrication includes a cationic photoinitiator selected from the group consisting of triarylsulfonium SbF₆⁻, triarylsulfonium borate, tris(4-(4-acetylphenyl)thiophenyl)sulfonium tetrakis(pentafluorophenyl)borate, diaryliodonium borate, iodonium [4-(1-methylethyl)phenyl](4-methylphenyl)-tetrakis(pentafluorophenyl)borate, and any combination thereof. A normucleophilic anion serves as the counterion. Examples of such anions include BF₄⁻, AsF₆⁻, SbF₆⁻, PF₆⁻, B(C₆F₅)₄⁻, perfluoroalkylsulfonates, perfluoroalkylphosphates, and carborane anions such as (CH₆B₁₁Cl₆)⁻.

Examples of cationic photoinitiators useful for curing at 300-475 nm, particularly at 365 nm UV light, without a sensitizer include 4-[4-(3-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-[4-(3-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium tetrakis(pentafluorophenyl)borate, and tris(4-(4-acetylphenyl)thiophenyl)sulfonium tetrakis(pentafluorophenyl)borate (GSID4480-1 also known as IRGACURE® PAG 290) from Ciba used in some of the example compositions.

In some embodiments it is desirable for the photocurable resin composition for additive fabrication to include a photosensitizer. The term “photosensitizer” is used to refer to any substance that either increases the rate of photoinitiated polymerization or shifts the wavelength at which polymerization occurs; see textbook by G. Odian, Principles of Polymerization, 3^rd Ed., 1991, page 222. Examples of photosensitizers include those selected from the group consisting of methanones, xanthenones, pyrenemethanols, anthracenes, pyrene, perylene, quinones, xanthones, thioxanthones, benzoyl esters, benzophenones, and any combination thereof. Particular examples of photosensitizers include those selected from the group consisting of [4-[(4-methylphenyl)thio]phenyl]phenyl⁻methanone, isopropyl-9H-thioxanthen-9-one, 1-pyrenemethanol, 9-(hydroxymethyl)anthracene, 9,10-diethoxyanthracene, 9,10-dimethoxyanthracene, 9,10-dipropoxyanthracene, 9,10-dibutyloxyanthracene, 9-anthracenemethanol acetate, 2-ethyl-9,10-dimethoxyanthracene, 2-methyl-9,10-dimethoxyanthracene, 2-t-butyl-9,10-dimethoxyanthracene, 2-ethyl-9,10-diethoxyanthracene and 2-methyl-9,10-diethoxyanthracene, anthracene, anthraquinones, 2-methylanthraquinone, 2-ethylanthraquinone, 2-tertbutylanthraquinone, 1-chloroanthraquinone, 2-amylanthraquinone, thioxanthones and xanthones, isopropyl thioxanthone, 2-chlorothioxanthone, 2,4-diethylthioxanthone, 1-chloro-4-propoxythioxanthone, methyl benzoyl formate, methyl-2-benzoyl benzoate, 4-benzoyl-4′-methyl diphenyl sulphide, 4,4′-bis(diethylamino) benzophenone, and any combination thereof.

Additionally, photosensitizers are useful in combination with photoinitiators in effecting cure with LED light sources emitting in the wavelength range of 300-475 nm. Examples of suitable photosensitizers include: anthraquinones, such as 2-methylanthraquinone, 2-ethylanthraquinone, 2-tertbutylanthraquinone, 1-chloroanthraquinone, and 2-amylanthraquinone, thioxanthones and xanthones, such as isopropyl thioxanthone, 2-chlorothioxanthone, 2,4-diethylthioxanthone, and 1-chloro-4-propoxythioxanthone, methyl benzoyl formate (Darocur MBF from Ciba), methyl-2-benzoyl benzoate (Chivacure OMB from Chitec), 4-benzoyl-4′-methyl diphenyl sulphide (Chivacure BMS from Chitec), 4,4′-bis(diethylamino)benzophenone (Chivacure EMK from Chitec).

In an embodiment, the photosensitizer is a fluorone, e.g., 5,7-diiodo-3-butoxy-6-fluorone, 5,7-diiodo-3-hydroxy-6-fluorone, 9-cyano-5,7-diiodo-3-hydroxy-6-fluorone, or a photosensitizer is

and any combination thereof.

The photocurable resin composition for additive fabrication can include any suitable amount of the photosensitizer, for example, in certain embodiments, in an amount up to about 10% by weight of the composition, in certain embodiments, up to about 5% by weight of the composition, and in further embodiments from about 0.05% to about 2% by weight of the composition.

When photosensitizers are employed, other photoinitiators absorbing at shorter wavelengths can be used. Examples of such photoinitiators include: benzophenones, such as benzophenone, 4-methyl benzophenone, 2,4,6-trimethyl benzophenone, and dimethoxybenzophenone, and 1-hydroxyphenyl ketones, such as 1-hydroxycyclohexyl phenyl ketone, phenyl (1-hydroxyisopropyl)ketone, 2-hydroxy-1-[4-(2-hydroxyethoxy)phenyl]-2-methyl-1-propanone, and 4-isopropylphenyl(1-hydroxyisopropyl)ketone, benzil dimethyl ketal, and oligo-[2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propanone] (Esacure KIP 150 from Lamberti). These photoinitiators when used in combination with a photosensitizer are suitable for use with LED light sources emitting at wavelengths from about 100 nm to about 300 nm.

LED light sources that emit visible light are also known. For LED light sources emitting light at wavelengths greater than about 400 nm, e.g., from about 475 nm to about 900 nm, examples of suitable photoinitiators include: camphorquinone, 4,4′-bis(diethylamino) benzophenone (Chivacure EMK from Chitec), 4,4′-bis(N,N′-dimethylamino)benzophenone (Michler's ketone), bis(2,4,6-trimethylbenzoyl)-phenylphosphineoxide (Irgacure 819 or BAPO from Ciba), metallocenes such as bis(eta 5-2-4-cyclopentadien-1-yl)bis[2,6-difluoro-3-(1H-pyrrol-1-yl)phenyl]titanium (Irgacure 784 from Ciba), and the visible light photoinitiators from Spectra Group Limited, Inc. such as H-Nu 470, H-Nu-535, H-Nu-635, H-Nu-Blue-640, and H-Nu-Blue-660.

A photosensitizer or co-initiator may be used to improve the activity of the cationic photoinitiator. It is for either increasing the rate of photoinitiated polymerization or shifting the wavelength at which polymerization occurs. The sensitizer used in combination with the above-mentioned cationic photoinitiator is not particularly limited. A variety of compounds can be used as photosensitizers, including heterocyclic and fused-ring aromatic hydrocarbons, organic dyes, and aromatic ketones. Examples of sensitizers include compounds disclosed by J. V. Crivello in Advances in Polymer Science, 62, 1 (1984), and by J. V. Crivello & K. Dietliker, “Photoinitiators for Cationic Polymerization” in Chemistry & technology of UV & EB formulation for coatings, inks & paints. Volume III, Photoinitiators for free radical and cationic polymerization. by K. Dietliker; [Ed. by P.K.T. Oldring], SITA Technology Ltd, London, 1991. Specific examples include polyaromatic hydrocarbons and their derivatives such as anthracene, pyrene, perylene and their derivatives, thioxanthones, α-hydroxyalkylphenones, 4-benzoyl-4′-methyldiphenyl sulfide, acridine orange, and benzoflavin.

There are a large number of known and technically proven cationic photoinitiators that are suitable. They include, for example, onium salts with anions of weak nucleophilicity. Examples are halonium salts, iodosyl salts or sulfonium salts, such as are described in published European patent application EP 153904 and WO 98/28663, sulfoxonium salts, such as described, for example, in published European patent applications EP 35969, 44274, 54509, and 164314, or diazonium salts, such as described, for example, in U.S. Pat. Nos. 3,708,296 and 5,002,856. All eight of these disclosures are hereby incorporated in their entirety by reference. Other cationic photoinitiators are metallocene salts, such as described, for example, in published European applications EP 94914 and 94915, which are both hereby incorporated in their entirety by reference.

A survey of other current onium salt initiators and/or metallocene salts can be found in “UV Curing, Science and Technology”, (Editor S. P. Pappas, Technology Marketing Corp., 642 Westover Road, Stamford, Conn., U.S.A.) or “Chemistry & Technology of UV & EB Formulation for Coatings, Inks & Paints”, Vol. 3 (edited by P. K. T. Oldring).

Suitable ferrocene type cationic photoinitiators include, for example, di(cyclopentadienyliron)arene salt compounds of formula (I) as disclosed in Chinese Patent No. CN 101190931:

wherein anion MXn is selected from BF4, PF6, SbF6, AsF6, (C6F5)₄B, C104, CF3SO3, FSO3, CH3SO3, C4F9SO3, and Ar is a fused ring or polycyclic arene.

Other illustrative ferrocene type cationic photoinitiators include, for example, (η6-Carbazole)(η5-cyclopenta-dienyl) iron hexafluorophosphate salts, specifically [cyclopentadiene-Fe—N-butylcarbazole]hexafluoro-phosphate (C4-CFS PF6) and [cyclopentadiene-Fe—N-octyl-carbazole]hexafluorophosphate (C8-CFS PF6), bearing C4 and C8 alkyl chains, respectively, on the nitrogen atom (see Polymer Eng. & Science (2009), 49(3), 613-618); ferrocenium dication salts, e.g., biphenyl bis[(π-cyclopentadienyl)iron]hexafluorophosphate ([bis(Cp-Fe)-biphenyl](PF6)₂) and straight cyclopentadien-iron-biphenyl hexafluorophosphate ([Cp-Fe-biphenyl]+PF6−) as disclosed in Chinese J. Chem. Engnrng (2008), 16(5), 819-822 and Polymer Bulltn (2005), 53(5-6), 323-331; cyclopentadienyl-Fe-carbazole hexafluorophosphate ([Cp-Fe-carbazole]+PF6−), cyclopentadienyl-Fe—N-ethylcarbazole hexafluorophosphate ([Cp-Fe-n-ethylcarbazole]+PF6−) and cyclopentadienyl-Fe-aminonaphthalene hexafluorophosphate ([Cp-Fe-aminonaphthalene]+PF6−) as disclosed in J Photochem. & Photobiology, A: Chemistry (2007), 187(2-3), 389-394 and Polymer Intnl (2005), 54(9), 1251-1255; alkoxy-substituted ferrocenium salts, for example, [cyclopendadien-Fe-anisole]PF6, [cyclopendadien-Fe-anisole]BF4, [cyclopendadien-Fe-diphenylether]PF6, [cyclo-pendadien-Fe-diphenylether]BF4, and [cyclopendadien-Fe-diethoxy-benzene]PF6, as disclosed in Chinese J. of Chem Engnrng (2006), 14(6), 806-809; cyclopentadiene-iron-arene tetrafluoroborates, for example, cyclopentadiene-iron-naphthalene tetrafluoroborate ([Cp-Fe-Naph] BF4) salt, as disclosed in Imaging Science J (2003), 51(4), 247-253; ferrocenyl tetrafluoroborate ([Cp-Fe-CP]BF4), as disclosed in Ganguang Kexue Yu Guang Huaxue (2003), 21(1), 46-52; [CpFe(η6-tol)]BF4, as disclosed in Ganguang Kexue Yu Guang Huaxue (2002), 20(3), 177-184, Ferrocenium salts (η6-α-naphthoxybenzene) (η5-cyclopentadienyl)iron hexafluorophosphate (NOFC-1) and (η6-β-naphthoxybenzene)(η5-cyclopentadienyl)iron hexafluorophosphate (NOFC-2), as disclosed in Int. J. of Photoenergy (2009), Article ID 981065; (η6-Diphenyl-methane) (η5-cyclopentadienyl) iron hexafluorophosphate and (η6-benzophenone) (η5-cyclopenta-dienyl)iron hexafluorophosphate, as disclosed in Progress in Organic Coatings (2009), 65(2), 251-256; [CpFe(η6-isopropyl-benzene)]PF6, as disclosed in Chem Comm (1999), (17), 1631-1632; and any combination thereof.

Suitable onium type cationic photoinitiators include, for example, iodonium and sulfonium salts, as disclosed in Japanese Patent JP 2006151852. Other illustrative onium type photoinitiators include, for example, onium salts such as, diaryliodonium salts, triarylsulfonium salts, aryl-diazonium salts, ferrocenium salts, diarylsulfoxonium salts, diaryl-iodoxonium salts, triaryl-sulfoxonium salts, dialkylphenacyl-sulfonium salts, dialkylhydroxy-phenylsulfonium salts, phenacyl-triarylphosphonium salts, and phenacyl salts of heterocyclic nitrogen-containing compounds, as disclosed in U.S. Pat. Nos. 5,639,413; 5,705,116; 5,494,618; 6,593,388; and Chemistry of Materials (2002), 14(11), 4858-4866; aromatic sulfonium or iodonium salts as disclosed in U.S. Patent Application No. 2008/0292993; diaryl-, triaryl-, or dialkylphenacylsulfonium salts, as disclosed in US2008260960 and J. Poly Sci, Part A (2005), 43(21), 5217; diphenyl-iodonium hexafluorophosphate (Ph2I+PF6−), as disclosed in Macromolecules (2008), 41(10), 3468-3471; onium salts using onium salts using less toxic anions to replace, e.g., SbF6−. Mentioned are anions: B(C6F5)4−, Ga(C6F5)4− and perfluoroalkyl fluorophosphate, PFnRf(6-n)-, as disclosed in Nettowaku Porima (2007), 28(3), 101-108; Photoactive allyl ammonium salt (BPEA) containing benzophenone moiety in the structure, as disclosed in Eur Polymer J (2002), 38(9), 1845-1850; 1-(4-Hydroxy-3-methylphenyl) tetrahydrothiophenium hexafluoroantimonate, as disclosed in Polymer (1997), 38(7), 1719-1723; and any combination thereof.

Illustrative iodonium type cationic photoinitiators include, for example, diaryliodonium salts having counterions like hexafluorophosphate and the like, such as, for example, (4-n-pentadecyloxy-phenyl)phenyliodonium hexafluoroantimonate, as disclosed in US2006041032; diphenyliodonium hexafluorophosphate, as disclosed in U.S. Pat. No. 4,394,403 and Macromolecules (2008), 41(2), 295-297; diphenyliodonium ions as disclosed in Polymer (1993), 34(2), 426-8; Diphenyliodonium salt with boron tetrafluoride (Ph2I+BF4−), as disclosed in Yingyong Huaxue (1990), 7(3), 54-56; SR-1012, a diaryldiodonium salt, as disclosed in Nuclear Inst. & Methods in Physics Res, B (2007), 264(2), 318-322; diaryliodonium salts, e.g., 4,4′-di-tert-butyldiphenyl-iodonium hexafluoroarsenate, as disclosed in J Polymr Sci, Polymr Chem Edition (1978), 16(10), 2441-2451; Diaryliodonium salts containing complex metal halide anions such as diphenyliodonium fluoroborate, as disclosed in J Polymr Sci, Poly Sympos (1976), 56, 383-95; and any combination thereof.

Illustrative sulfonium type cationic photoinitiators include, for example, UVI 6992 (sulfonium salt) as disclosed in Japanese patent JP2007126612; compounds of the formula:

where R1-2=F; R3=isopropyl; R4=H; X=PF6, as disclosed in Japanese patent JP10101718; thioxanthone-based sulfonium salts, e.g., of the formula:

as disclosed in U.S. Pat. No. 6,054,501; (Acyloxyphenyl)sulfonium salts of the type R₃−xS+R_3x A−, where A− is a non-nucleophilic anion such as AsF₆—, and R₃ may be the phenyl group shown below:

as disclosed in U.S. Pat. Nos. 5,159,088; 9,10-dithiophenoxyanthracene alkyldiarylsulfonium salts, e.g., ethylphenyl(9-thiophenoxy-anthracenyl-10) sulfonium hexafluoroantimonate, and the like, as disclosed in U.S. Pat. No. 4,760,013; etc.; triphenylsulfonium hexafluorophosphate salt, as disclosed in U.S. Pat. No. 4,245,029; S,S-dimethyl-S-(3,5-dimethyl-2-hydroxyphenyl)sulfonium salts, as disclosed in J Poly Sci, Part A (2003), 41(16), 2570-2587; Anthracene-bound sulfonium salts, as disclosed in J Photochem & Photobiology, A: Chemistry (2003), 159(2), 161-171; triarylsulfonium salts, as disclosed in J Photopolymer Science & Tech (2000), 13(1), 117-118 and J Poly Science, Part A (2008), 46(11), 3820-29; S-aryl-S,S-cycloalkylsulfonium salts, as disclosed in J Macromol Sci, Part A (2006), 43(9), 1339-1353; dialkylphenacylsulfonium salts, as disclosed in UV & EB Tech Expo & Conf, May 2-5, 2004, 55-69 and ACS Symp Ser (2003), 847, 219-230; Dialkyl(4-hydroxyphenyl)sulfonium salts, and their isomeric dialkyl(2-hydroxyphenyl)sulfonium salts, as disclosed in ACS 224th Natnl Meeting, Aug. 18-22, 2002, POLY-726; Dodecyl(4-hydroxy-3,5-dimethylphenyl)methylsulfonium hexafluorophosphate and similar alkyl analogs other than dodecyl. Tetrahydro-1-(4-hydroxy-3,5-dimethylphenyl)thiophenium hexafluorophosphate and tetrahydro-1-(2-hydroxy-3,5-dimethylphenyl)thiophenium hexafluorophosphate, as disclosed in ACS Polymer Preprints (2002), 43(2), 918-919; photoinitiators with the general structure Ar′S+CH3(C12H25)SbF6−, where Ar′ is phenacyl (I), 2-indanonyl (II), 4-methoxyphenacyl (III), 2-naphthoylmethyl (IV), 1-anthroylmethyl (V), or 1-pyrenoylmethyl (VI), as disclosed in J Polymr Sci, Part A (2000), 38(9), 1433-1442; Triarylsulfonium salts Ar3S+MXn− with complex metal halide anions such as BF4−, AsF6−, PF6−, and SbF6−, as disclosed in J Polymr Sci, Part A (1996), 34(16), 3231-3253; Dialkylphenacylsulfonium and dialkyl(4-hydroxyphenyl)sulfonium salts, as disclosed in Macromolecules (1981), 14(5), 1141-1147; Triarylsulfonium salts R2R1S+MFn− (R, R1=Ph or substituted phenyl; M=B, As, P; n=4 or 6) and the sulfonium salt of formula (I):

as disclosed in J. Polymr. Sci, Polymr Chem Edition (1979), 17(4), 977-99; aromatic sulfonium salts with, e.g., PF6− anion, e.g., UVI 6970, as disclosed in JP 2000239648; and any combination thereof.

Suitable pyridinium type cationic photoinitiators include, for example, N-ethoxy 2-methylpyridinium hexafluorophosphate (EMP+PF6−), as disclosed in Turkish J of Chemistry (1993), 17(1), 44-49; Charge-transfer complexes of pyridinium salts and aromatic electron donors (hexamethyl-benzene and 1,2,4-trimethyoxy-benzene), as disclosed in Polymer (1994), 35(11), 2428-31; N,N′-diethoxy-4,4′-azobis(pyridinium)hexafluorophosphate (DEAP), as disclosed in Macromolecular Rapid Comm (2008), 29(11), 892-896; and any combination thereof.

Other suitable cationic photoinitiators include, for example, Acylgermane based photoinitiator in the presence of onium salts, e.g., benzoyltrimethylgermane (BTG) and onium salts, such as diphenyl-iodonium hexafluorophosphate (Ph2I+PF6−) or N-ethoxy-2-methyl-pyridinium hexafluorophosphate (EMP+PF6−), as disclosed in Macromolecules (2008), 41(18), 6714-6718; Di-Ph diselenide (DPDS), as disclosed in Macromolecular Symposia (2006), 240, 186-193; N-phenacyl-N,N-dimethyl-anilinium hexafluoroantimonate (PDA+SbF6−), as disclosed in Macromol Rapid Comm (2002), 23(9), 567-570; Synergistic blends of: diaryliodonium hexafluoro-antimonate (IA) with tolylcumyl-iodonium tetrakis(pentafluoro-phenyl)borate (IB), and cumenecyclopentadienyliron(II) hexafluorophosphate with IA and IB, as disclosed in Designed Monomers and Polymers (2007), 10(4), 327-345; Diazonium salts, e.g., 4-(hexyloxy)-substituted diazonium salts with complex anions, as disclosed in ACS Symp Series (2003), 847, 202-212; 5-Arylthianthrenium salts, as disclosed in J Poly Sci, Part A (2002), 40(20), 3465-3480; and any combination thereof.

Other suitable cationic photoinitiators include, for example, triarylsulfonium salts such as triarylsulfonium borates modified for absorbing long wavelength UV. Illustrative examples of such modified borates include, for example, SP-300 available from Denka, tris(4-(4-acetylphenyl)thiophenyl)sulfonium tetrakis(pentafluorophenyl)borate (GSID4480-1 or Irgacure PAG-290) available from Ciba/BASF, and those photoinitiators disclosed in WO1999028295; WO2004029037; WO2009057600; U.S. Pat. No. 6,368,769 WO2009047105; WO2009047151; WO2009047152; US 20090208872; and U.S. Pat. No. 7,611,817.

Preferred cationic photoinitiators include a mixture of: bis[4-diphenylsulfoniumphenyl]sulfide bishexafluoroantimonate; thiophenoxyphenylsulfonium hexafluoroantimonate (available as Chivacure 1176 from Chitec); tris(4-(4-acetylphenyl)thiophenyl)sulfonium tetrakis(pentafluorophenyl)borate (GSID4480-1 from Ciba/BASF), iodonium, [4-(1-methylethyl)phenyl](4-methylphenyl)-, tetrakis(pentafluorophenyl)borate (available as Rhodorsil 2074 from Rhodia), 4-[4-(2-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate (as SP-172) and SP-300 (both available from Adeka).

The photocurable resin composition for additive fabrication can include any suitable amount of the cationic photoinitiator, for example, in certain embodiments, in an amount up to about 50% by weight of the composition, in certain embodiments, up to about 20% by weight of the composition, and in further embodiments from about 1% to about 10% by weight of the composition. In a further embodiment from about 0.4 wt % to about 6.5 wt % of the composition. In an embodiment, the above ranges are particularly suitable for use with epoxy monomers.

In accordance with an embodiment, the photocurable resin composition for additive fabrication can further include a chain transfer agent, particularly a chain transfer agent for a cationic monomer. The chain transfer agent has a functional group containing active hydrogen. Examples of the active hydrogen-containing functional group include an amino group, an amide group, a hydroxyl group, a sulfo group, and a thiol group. In an embodiment, the chain transfer agent terminates the propagation of one type of polymerization, i.e., either cationic polymerization or free-radical polymerization and initiates a different type of polymerization, i.e., either free-radical polymerization or cationic polymerization. In accordance with an embodiment, chain transfer to a different monomer is a preferred mechanism. In embodiments, chain transfer tends to produce branched molecules or crosslinked molecules. Thus, chain transfer offers a way of controlling the molecular weight distribution, crosslink density, thermal properties, and/or mechanical properties of the cured resin composition.

Any suitable chain transfer agent can be employed. For example, the chain transfer agent for a cationic polymerizable component is a hydroxyl-containing compound, such as a compound containing 2 or more than 2 hydroxyl-groups. In an embodiment, the chain transfer agent is selected from the group consisting of a polyether polyol, polyester polyol, polycarbonate polyol, ethoxylated or propoxylated aliphatic or aromatic compounds having hydroxyl groups, dendritic polyols, hyperbranched polyols. An example of a polyether polyol is a polyether polyol comprising an alkoxy ether group of the formula [(CH₂)_nO]_m, wherein n can be 1 to 6 and m can be 1 to 100.

A particular example of a chain transfer agent is polytetrahydrofuran such as TERATHANE™.

The photocurable resin composition for additive fabrication can include any suitable amount of the chain transfer agent, for example, in certain embodiments, in an amount up to about 50% by weight of the composition, in certain embodiments, up to about 30% by weight of the composition, and in certain other embodiments from about 10% to about 20% by weight of the composition.

The photocurable resin composition for additive fabrication of the invention can further include one or more additives selected from the group consisting of bubble breakers, antioxidants, surfactants, acid scavengers, pigments, dyes, thickneners, flame retardants, silane coupling agents, ultraviolet absorbers, resin particles, core-shell particle impact modifiers, soluble polymers and block polymers, organic, inorganic, or organic-inorganic hybrid fillers of sizes ranging from about 8 nanometers to about 50 microns.

Stabilizers are often added to the compositions in order to prevent a viscosity build-up, for instance a viscosity build-up during usage in a solid imaging process. Preferred stabilizers include those described in U.S. Pat. No. 5,665,792, the entire disclosure of which is hereby incorporated by reference. Such stabilizers are usually hydrocarbon carboxylic acid salts of group IA and IIA metals. Most preferred examples of these salts are sodium bicarbonate, potassium bicarbonate, and rubidium carbonate. Rubidium carbonate is preferred for formulations of this invention with recommended amounts varying between 0.0015 to 0.005% by weight of composition. Alternative stabilizers include polyvinylpyrrolidones and polyacrylonitriles. Other possible additives include dyes, pigments, fillers (e.g. silica particles—preferably cylindrical or spherical silica particles—, talc, glass powder, alumina, alumina hydrate, magnesium oxide, magnesium hydroxide, barium sulfate, calcium sulfate, calcium carbonate, magnesium carbonate, silicate mineral, diatomaceous earth, silica sand, silica powder, titanium oxide, aluminum powder, bronze powder, zinc powder, copper powder, lead powder, gold powder, silver dust, glass fiber, titanic acid potassium whisker, carbon whisker, sapphire whisker, beryllia whisker, boron carbide whisker, silicon carbide whisker, silicon nitride whisker, glass beads, hollow glass beads, metaloxides and potassium titanate whisker), antioxidants, wetting agents, photosensitizers for the free-radical photoinitiator, chain transfer agents, leveling agents, defoamers, surfactants and the like.

In accordance with an embodiment of the invention, the photocurable resin composition for additive fabrication contains the polymerizable components such that the desired photosensitivity is obtained by choosing an appropriate ratio of the initiators and/or polymerizable components. The ratio of the components and of the initiators affect the photosensitivity, speed of curing, degree of curing, crosslink density, thermal properties (e.g., T_g), and/or mechanical properties (e.g., tensile strength, storage modulus, loss modulus) of the photocurable resin composition for additive fabrication or of the cured article.

Accordingly, in an embodiment, the ratio by weight of cationic photoinitiator to free-radical photoinitiator (CPI/RPI) is less than about 4.0, preferably from about 0.1 to about 2.0, and more preferably from about 0.2 to about 1.0.

In accordance with an embodiment, the photocurable resin composition for additive fabrication has a ratio by weight of cationic polymerizable component to free-radical polymerizable component (CPC/RPC) is less than about 7.0, or less than about 5.0, e.g., from about 0.5 to about 2.0, and more preferably from about 1.0 to about 1.5.

In accordance with an embodiment, the photocurable resin composition for additive fabrication is free or substantially free of antimony-containing initiator (less than 1.5% by weight).

The present invention further provides a three-dimensional article comprising a cured photocurable resin composition for additive fabrication, wherein the cured photocurable resin composition for additive fabrication is obtained by curing a photocurable resin composition for additive fabrication by irradiating it with light emitted from a light emitting diode (LED) light having a wavelength from about 100 nm to about 900 nm.

The present invention further provides a process for making a three-dimensional article comprising the steps of forming and selectively curing a layer of a photocurable resin composition for additive fabrication by irradiation with a light emitting diode (LED) light having a wavelength from about 100 nm to about 900 nm, the photocurable resin composition and repeating the steps of forming and selectively curing a layer of the photocurable resin composition a plurality of times to obtain the three-dimensional article.

As used herein, the term “renewable resource material” is defined as a starting material that is not derived from petroleum but as a starting material derived from a plant including the fruits, nuts and/or seeds of plants. These plant derived materials are environmentally friendly and biologically based materials. Thus, these starting materials are also frequently called “bio-based” materials or “natural oil” materials.

Further to the understood definition of “bio-based,” according to the FRSIA(Farm Security and Rural Investment Act), “biobased products” are products determined by the U.S. Secretary of Agriculture to be “commercial or industrial goods (other than food or feed) composed in whole or in significant part of biological products, forestry materials, or renewable domestic agricultural materials, including plant, animal or marine materials.

Biobased content may be determined by testing to ASTM Method D6866-10, STANDARD TEST METHODS FOR DETERMINING THE BIOBASED CONTENT OF SOLID, LIQUID, AND GASEOUS SAMPLES USING RADIOCARBON ANALYSIS. This method, similar to radiocarbon dating, compares how much of a decaying carbon isotope remains in a sample to how much would be in the same sample if it were made of entirely recently grown materials. The percentage is called the product's biobased content.

Persons of ordinary skill in the art of photocurable resin compositions for additive fabrication are aware of how to select ingredients and understand whether the ingredient is bio-based or petroleum based. What is different now is the sheer abundance of bio-based raw materials suitable for use in photocurable resin compositions for additive fabrication. For example, bio-based raw materials can be found in polyols and other ingredients.

In embodiments of the invention, the photocurable resin compositions for additive fabrication comprise at least 30 wt % of bio-based ingredients, rather than petroleum based ingredients. In other embodiments, the photocurable resin compositions for additive fabrication comprise at least 40 wt % of bio-based ingredients, rather than petroleum based ingredients.

The following examples further illustrate the invention but, of course, should not be construed as in any way limiting its scope.

Examples 1-56

These examples illustrate embodiments of the photocurable resin compositions for additive fabrication. Tables 1A-1D describe the various components of the photocurable resin compositions for additive fabrication illustrated in Tables 2-7.

TABLE 1A
Trade Name	CAS RN	Function in Formula	Chemical Descriptor	Supplier
1-pyrenemethanol	24463-15-8	Photosensitizing agent	1-pyrenemethanol	Sigma Aldrich
9-anthracenemethanol	1468-95-7	Photosensitizing agent	9-(Hydroxymethyl)anthracene	Sigma Aldrich
NK Ester A-DOG	87320-05-6	Free radical polymerizable	[2-[1,1-dimethyl-2-[(1-oxoallyl)oxy]ethyl]-5-ethyl-	Kowa
		monomer or oligomer	1,3-dioxan-5-yl]methyl acrylate
Anthracene	120-12-7	Photosensitizing agent	Anthracene	Sigma Aldrich
Anthracure UVS 1101	68818-86-0	Photosensitizing agent	9,10-Diethoxy-anthracene,	Kawaski Kasei
BYK A 501	proprietary mixture	Bubble breaker	Naphtha/methoxy propanol acetate	BYK-Chemie
CD 406	67905-41-3	Free radical polymerizable	1,4-Cyclohexanedimethanol diacrylate	Sartomer
		monomer or oligomer
CD 536	87320-05-6	Free radical polymerizable	2-Propenoic acid, [2-[1,1-dimethyl-2-[(1-oxo-2-	Sartomer
		monomer or oligomer	propenyl)oxy]ethyl]-5-ethyl-1,3-dioxan-5-yl]methyl ester
Celloxide 2021P	25085-98-7; 2386-	Cationic polymerizable	(3′,4′-Epoxycyclohexylmethyl) 3,4-	Daicel Chemical
	87-0	monomer or oligomer	epoxycyclohexanecarboxylate
Chivacure 1176	159120-95-3	Photoacid generator	A mixture of: bis[4-	Chitec
	(mixture)		diphenylsulfoniumphenyl]sulfide
			bishexafluoroantimonate;
			thiophenoxyphenylsulfonium hexafluoroantimonate
			and propylene carbonate.
CHDM	105-08-8	Chain transfer agent for	1,4-Cyclohexanedimethanol	Eastman
		cationic monomers		Chemical
Chivacure BMS	83846-85-9	Photosensitizing agent	[4-[(4-methylphenyl)thio]phenyl]phenyl-methanone	Chitec
Chivacure ITX	75081-21-9	Photosensitizing agent	Isopropyl-9H-thioxanthen-9-one	Chitec

TABLE 1B
Trade Name	CAS RN	Function in Formula	Chemical Descriptor	Supplier
COPIKEM 14 ORANGE	67697-75-0	Color change dye	3-[N,N-bis(4-octylphenyl)amino]-3-(4-	Hilton Davis
			dimethylaminophenyl)phthalide
Darocur 1173	7473-98-5	Free radical generator	1-Hydroxy-1-methylethyl phenyl ketone	Ciba
EBECRYL 3700	4687-94-9	Free radical	Bisphenol A diglycidyl ether diacrylate	Cytec
		polymerizable monomer
		or oligomer
EPONOX 1510	30583-72-	Cationic polymerizable	Hydrogenated bisphenol A-epichlorohydrin based	Hexion
	3/13410-58-7	monomer or oligomer	epoxy resin
GRILONIT F713	26951-52-0	Cationic polymerizable	Poly(oxy-1,4-butanediyl), a-(oxiranylmethyl)-w-	EMS
		monomer or oligomer	(oxiranylmethoxy)-
Irgacure PAG 290	Not known	Photoacid generator	tris(4-(4-acetylphenyl)thiophenyl)sulfonium	Ciba/BASF
(GSID 4480-1)			tetrakis(pentafluorophenyl)borate
Heloxy 107	14228-73-0	Cationic polymerizable	1,4-Cyclohexanedimethanol diglycidyl ether	Hexion
		monomer or oligomer
Intermediate DG-0049	proprietary	Pigment dispersion for	Pigment dispersion for color effects	Desotech
	mixture	color effects
Irgacure 184	947-19-3	Free radical generator	1-Hydroxy-1-cyclohexyl phenyl ketone	Ciba
IRGANOX 1035	41484-35-9	Antioxidant	Benzenepropanoic acid, 3,5-bis(1,1-	Ciba
			dimethylethyl)-4-hydroxy-, thiodi-2,1-ethanediyl
			ester
Kayarad R 684	42594-17-2	Free radical	Dicyclopentadienedimethanol diacrylate	Nippon
		polymerizable monomer		Kayaku
		or oligomer

TABLE 1C
Trade Name	CAS RN	Function in Formula	Chemical Descriptor	Supplier
Longnox 10	6683-19-8	Antioxidant	Pentaerythritol tetrakis[(3,5-di-tert-butyl-4-	Longchem
			hydroxyphenyl)propionate]	C&S Int.
Orange Pigment	proprietary	Pigment dispersion for		Desotech
	mixture	color effects
OXT-101	3047-32-3	Cationic polymerizable	3-Ethyl-3-oxetanemethanol	Toagosei
		monomer or oligomer
OXT-121	142627-97-2	Cationic polymerizable	1,4-Bis[(3-ethyl-3-	Toagosei
		monomer or oligomer	oxetanylmethoxy)methyl]benzene
OXT-221	18934-00-4	Cationic polymerizable	3,3′-[Oxybis(methylene)]bis[3-ethyl-oxetane	Toagosei
		monomer or oligomer
Polyvinyl pyrrolidone	9003-39-8	Acid scavenger	Poly[N-vinylpyrrolidinone]; PVP	Sigma Aldrich
Red Pigment	proprietary	Pigment dispersion for		Desotech
	mixture	color effects
Rhodorsil 2074	178233-72-2	Photoacid generator	Iodonium, [4-(1-methylethyl)phenyl](4-	Rhodia
			methylphenyl)-, tetrakis(pentafluorophenyl)borate
Rubidium carbonate	584-09-8	Acid scavenger	Dirubidium carbonate; Rb2CO3	Sigma Aldrich
Silwet L 7600	mixture	Leveling agent	Polyalkyleneoxide modified polydimethylsiloxane	Momentive
SR 399	60506-81-2	Free radical	Dipentaerythritol monohydroxypentaacrylate	Sartomer
		polymerizable monomer
		or oligomer
SR 492	53879-54-2	Free radical	Propoxylated trimethylolpropane triacrylate	Sartomer
		polymerizable monomer
		or oligomer

TABLE 1D
Trade Name	CAS RN	Function in Formula	Chemical Descriptor	Supplier
SR 9003	84170-74-1	Free radical	Propoxylated neopentyl glycol diacrylate	Sartomer
		polymerizable monomer
		or oligomer
TERATHANE 1000	25190-06-1	Chain transfer agent for	Poly(tetramethylene ether) glycol	Invista
		cationic monomers
VEctomer ® VE 4010	130066-57-8	Cationic polymerizable	Bis(4-vinyloxybutyl) isophthalate	Vertellus
		monomer or oligomer
VEctomer ® VE 5015	196109-17-8	Cationic polymerizable	Tris[4-(vinyloxy)butyl] trimellitate	Vertellus
		monomer or oligomer

TABLE 2
Composition	Example 1	Example 2	Example 3	Example 4	Example 5	Example 6	Example 7	Example 8	Example 9
Name	Part	Part	Part	Part	Part	Part	Part	Part	Part
EBECRYL-3700	25.000	19.659	19.659	19.659	19.659	25.000	25.000	25.000	24.611
CD 406	7.000					7.000	7.000	7.000
Kayarad R 684									6.891
Kowa A-DOG
SR492
VEctomer ® VE 5015
VEctomer ® VE 4010
Celloxide 2021P	36.000	54.040	54.04	54.04	54.04	43.910	41.620	39.215	42.034
OXT-101		8.603	8.603	8.603	8.603
OXT-221
OXT-121
TERATHANE-1000	25.000	10.463	10.463	10.463	10.463	17.085	19.375	21.780	19.568
Chivacure 1176
GSID4480-1 CPI	4.000
Rhodorsil 2074		0.750	1	1.5	2	2.000	2.000	2.000	1.969
Irgacure 184	3.000	4.259	4.005	3.5025	3	3.000	3.000	3.000	2.953
Darocur 1173
Chivacure BMS		2.000	2	2	2	2.000	2.000	2.000	1.969
Chivacure ITX
1-pyrenemethanol
9-anthracenemethanol
Anthracure UVS 1101
Longnox 10		0.001	0.005	0.0075	0.01
PVP		0.005	0.005	0.005	0.005	0.005	0.005	0.005	0.005
Rubidium carbonate
Silwet L 7600		0.200	0.2	0.2	0.2
BYK A 501		0.020	0.02	0.02	0.02
Total	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000

TABLE 3
	Example	Example	Example	Example	Example	Example	Example	Example	Example
Composition	10	11	12	13	14	15	16	17	18
Name	Part	Part	Part	Part	Part	Part	Part	Part	Part
EBECRYL-3700	25.000	25.000	25.000				32.000
CD 406	7.000	7.000	7.000
Kayarad R 684				32.000	16.000			32.000	16.000
Kowa A-DOG					16.000	32.000		0.000	16.000
SR492
VEctomer ® VE 5015
VEctomer ® VE 4010
Celloxide 2021P	42.698	46.920	49.570	46.920	46.920	41.055	41.055	41.055	41.055
OXT-101						6.212	6.212	6.212	6.212
OXT-221
OXT-121
TERATHANE-1000	19.877	14.075	11.425	14.075	14.075	10.948	10.948	10.948	10.948
Chivacure 1176
GSID4480-1 CPI
Rhodorsil 2074	2.000	2.000	2.000	2.000	2.000	1.553	1.553	1.553	1.553
Irgacure 184	3.000	3.000	3.000	3.000	3.000	6.213	6.213	6.213	6.213
Darocur 1173
Chivacure BMS		2.000	2.000	2.000	2.000	1.553	1.553	1.553	1.553
Chivacure ITX	0.420
1-pyrenemethanol
9-anthracenemethanol
Anthracure UVS 1101
Longnox 10						0.116	0.116	0.116	0.116
PVP	0.005	0.005	0.005	0.005	0.005	0.008	0.008	0.008	0.008
Rubidium carbonate
Silwet L 7600						0.311	0.311	0.311	0.311
BYK A 501						0.031	0.031	0.031	0.031
Total	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000

TABLE 4
	Example	Example	Example	Example	Example	Example	Example	Example	Example
Composition	19	20	21	22	23	24	25	26	27
Name	Part	Part	Part	Part	Part	Part	Part	Part	Part
EBECRYL-3700
CD 406
Kayarad R 684	29.009		29.009	48.102
Kowa A-DOG		28.510
SR492
VEctomer ® VE 5015									38.000
VEctomer ® VE 4010			35.726	24.208				52.780
Celloxide 2021P	33.018	33.018	25.045	16.970	89.280	48.780	40.000	37.000	28.330
OXT-101	3.995	3.995	3.995	3.995	3.995	3.995	3.995	3.995	3.995
OXT-221	27.752	27.752				41.000			24.200
OXT-121							50.530
TERATHANE-1000
Chivacure 1176
GSID4480-1 CPI
Rhodorsil 2074	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
Irgacure 184	4.000	4.000	4.000		4.000	4.000	4.000	4.000
Darocur 1173				4.000					4.000
Chivacure BMS	1.000	1.500	1.000	1.500	1.500	1.000		1.000
Chivacure ITX							0.250		0.250
1-pyrenemethanol
9-anthracenemethanol
Anthracure UVS 1101
Longnox 10	0.005	0.005	0.005	0.005	0.005	0.005	0.005	0.005	0.005
PVP
Rubidium carbonate
Silwet L 7600	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
BYK A 501	0.020	0.020	0.020	0.020	0.020	0.020	0.020	0.020	0.020
Total	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000

TABLE 5
	Example	Example	Example	Example	Example	Example	Example	Example	Example
Composition	28	29	30	31	32	33	34	35	36
Name	Part	Part	Part	Part	Part	Part	Part	Part	Part
EBECRYL-3700				17.343	24.936	24.924	17.536	17.237	24.449
CD 406					6.982	6.979			6.846
Kayarad R 684	32.796	56.22
Kowa A-DOG			32.796
SR492	23.424		23.424
VEctomer ® VE 5015
VEctomer ® VE 4010
Celloxide 2021P	26.432	26.432	26.432	53.283	35.01	34.993	53.878	52.959	34.326
OXT-101	3.999	3.999	3.999	8.483			8.577	8.431
OXT-221
OXT-121
TERATHANE-1000	7.049	7.049	7.049	10.317	24.936	24.924	10.432	10.254	24.449
Chivacure 1176				4.023	3.391	3.39	4.068	3.998	3.325
GSID4480-1 CPI								2	2.2
Rhodorsil 2074	1	1	1
Irgacure 184	4	4	4	4.93	4.489	4.486	4.985	4.9	4.401
Chivacure BMS	1	1	1
1-pyrenemethanol				1.4
9-anthracenemethanol					0.25
Anthracure UVS 1101						0.3	0.3
Longnox 10	0.075	0.075	0.075
PVP	0.005	0.005	0.005	0.005			0.005	0.005
Rubidium carbonate					0.005	0.005			0.005
Silwet L 7600	0.2	0.2	0.2	0.197			0.199	0.196
BYK A 501	0.02	0.02	0.02	0.02			0.02	0.02
Total	100	100	100	100	100	100	100	100	100

TABLE 6
	Example	Example	Example	Example	Example	Example	Example	Example	Example	Example
Composition	37	38	39	40	41	42	43	44	45	46
Component	Part	Part	Part	Part	Part	Part	Part	Part	Part	Part
Ebecryl 3700	25.000				16.000
SR 399						6.353	7.000	6.353	8.198	8.216
Sartomer 9003									4.099	4.108
CD 406	7.000
Kayarad R 684		16.000	32.000			25.647		25.647
Kowa A-DOG		16.000		32.000	16.000		25.000
Epon 1510	43.990	43.990	43.990	43.990	43.990	43.990	43.990		63.003	63.142
Heloxy 107								43.990
OXT-101	16.000	16.000	16.000	16.000	16.000	16.000	16.000	16.000	16.957	16.994
Chivacure 1176
Rhodorsil PI 2074	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.004
1-Pyrenemethanol
9-Anthracene-
methanol
Anthracure
UVS 1101
Anthracene
Irgacure 184	4.000	4.000	4.000	4.000	4.000	4.000	4.000	4.000	2.799	2.806
Darocur 1173
Chivacure BMS	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.004
Longnox 10	0.010	0.010	0.010	0.010	0.010	0.010	0.010	0.010	0.500	0.501
Polyvinyl									0.005	0.005
pyrrolidone
Silwet L7600									0.200	0.200
BYK A501									0.020	0.020
Intermediate									0.220
DG-0049
Total	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000

TABLE 7
	Example	Example	Example	Example	Example	Example	Example	Example	Example	Example
Composition	47	48	49	50	51	52	53	54	55	56
Component	Part	Part	Part	Part	Part	Part	Part	Part	Part	Part
Ebecryl 3700
SR 399	8.292	8.292	8.292	8.292	8.292	7.822	7.905	7.909	7.909	8.014
Sartomer 9003	4.147	4.147	4.147	4.147	4.147	3.911	3.953	3.955	3.955	4.007
CD 406
Kayarad R 684
Kowa A-DOG
Epon 1510	64.051	64.051	64.051	64.051	64.051	60.420	61.064	61.094	61.094	62.266
Heloxy 107
OXT-101	17.191	17.191	17.191	17.191	17.191	16.217	16.389	16.398	16.398	16.555
Chivacure 1176						4.831	4.883	4.885	4.885	1.547
Rhodorsil PI 2074	1.545	2.045	2.045	1.045	1.045					0.516
1-Pyrenemethanol						1.400
9-Anthracene-							0.350			0.350
methanol
Anthracure								0.300
UVS 1101
Anthracene									0.300
Irgacure 184	1.75	0.5	2	1.5	3	3.747	3.787	3.789	3.789	1.200
Darocur 1173										4.000
Chivacure BMS	1.273	2.023	0.523	2.023	0.523
Longnox 10	1.307	1.307	1.307	1.307	1.307	1.233	1.246	1.246	1.246	1.255
Polyvinyl	0.005	0.005	0.005	0.005	0.005	0.005	0.005	0.005	0.005	0.005
pyrrolidone
Silwet L7600	0.209	0.209	0.209	0.209	0.209	0.197	0.199	0.199	0.199	0.201
BYK A501	0.021	0.021	0.021	0.021	0.021	0.020	0.020	0.020	0.020	0.020
Intermediate	0.209	0.209	0.209	0.209	0.209	0.197	0.199	0.199	0.199	0.063
DG-0049
Total	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000	100.000

Example 57

This Example illustrates some of the properties of the photocurable resin composition for additive fabrication embodiments set forth in Examples 1-56. Tables 8-26 set forth the Dp, Ec, and E3-E5 values and Table 27 sets forth the CPI/RPI and CPC/RPC values.

The photosensitivity of the compositions are evaluated by measuring Critical Energy (Ec) values, Depth of Penetration (Dp) values, and Storage Shear Modulus (G′) upon exposure to curing light. The Ec and Dp values are measured using a photo cure speed test using LED light (365 nm). The G′ values were measured using a StressTech Rheometer manufactured by Reologicia Instruments AB, Sweden. Each of the methods are summarized below.

The photo cure speed test using 365 nm LED light is used to measure values for Ec and Dp. A single UV LED “bare bulb” (Model No. NCSUO33A; Nichia Corporation, Japan) having a peak wavelength of 365 nm is used as the LED light source in a light curing apparatus, wherein the single LED light is bottom-mounted on a flat surface inside a 30° C. chamber and positioned in an upward-looking arrangement and pointing vertically. The LED light is powered by a 3.30 V/0.050 A DC output from a Programmable Power Supply (Model No. PSS-3203; GW Instek).

A 10-mil sheet of polyester film (Melinex #515, Polybase Mylar D, 0.010 gauge) is placed at a distance of 12 mm above from the bottom of the LED light bulb. A drop of the liquid resin is placed on the polyester film over the center of the LED light. The resin is exposed to the LED light through the polyester film for a specific time interval. The process is repeated with fresh resin for 2, 4, 6, 8, 10 second exposure times or up to 12, 16, or 20 seconds for slow curing resin formulations.

After exposure to the LED light, the sample is allowed to age inside the 30° C. chamber for at least 15 minutes, after which time any uncured resin is removed from the exposed areas by blotting with a Kimwipe EX-L (Kimberly Clark). A thickness measurement is then taken on the center of the exposed area using an ABSOLUTE Digimatic Indicator (Model ID-C112CE, Mitutoyo Corporation, Japan). The measured thickness of each sample is plotted as a function of the natural logarithm of the exposure time. The depth of penetration (Dp; mil) of the resin composition is the slope of the least squares fit line. The Ec (sec) is the X-axis crossing point (Y=0) of the line. The E₃, E₄, or E₅ is, respectively, the time (in seconds) required to produce a layer having a thickness of 3, 4, or 5 mils, respectively.

Alternatively, when the intensity of the incident light (mW/cm²) from the light source on the resin surface is known, the exposure energy (mJ/cm²) rather than the exposure time (in seconds) is used for calculating the Dp and Ec values.

The tensile properties (tensile strength, percent elongation at break, and modulus) of cured samples of the photocurable resin compositions for additive fabrication are tested on films, where applicable, using a universal testing instrument, Instron Model 4201 equipped with a suitable personal computer and Instron software to yield values of tensile strength, percent elongation at break, and elastic modulus. The tensile test is performed on the Instron with a crosshead speed of 1.00 inch/min and a crosshead jaw separation of 2.00 inches in a 50% relative humidity room at room temperature. Samples are prepared for testing by curing the liquid resin composition applied on Mylar (0.01 gauge) with a 5 mil square draw bar, and cured on an unfiltered Fusion D bulb (600W) in nitrogen with an exposure of 300 mJ/cm². The cured film samples were cut within 1 hour of cure to have 0.5×4″ strips and conditioned in a 50% relative humidity room at RT for 24 hours before the tensile test was performed. Tensile test data was not performed for Examples 1-5, 13-27, 31-36, and 45-56.

Real Time Dynamic Mechanical Analysis (RT-DMA)

Real Time Dynamic Mechanical Analysis (RT-DMA), including the storage shear modulus (G′), is carried out under ambient lab conditions (20-23° C. and 25-35% RH), on compositions undergoing curing using a StressTech Rheometer (Reologicia Instruments AB, Sweden) with an 8 mm plate, a gap of 0.1 mm or 0.05 mm, as specified in the Tables 15-23, and modified to include a mercury lamp light source (OMNICURE Series 2000 available from EXFO), fitted with a 365 nm interference filter (also available from EXFO) placed in the light path and a liquid-filled light guide for conveying light from the source to the rheometer. The 365 nm interference filter produces the spectral output shown in FIG. 1. The samples are evaluated under the following parameters: 10 s of equilibrium time; frequency of 10 Hz; 44-50 mW/cm2 light intensity (as specified in the Tables 15-23) by the IL 1400 radiometer with XRL140B detector (International Light, Newburyport, Mass.); 1.0 s exposure that starts at 2.1 seconds from the beginning of data collection; FFT smoothing of curves; G′ taken at 2.5, 2.7, 3, 4, and 6 s from the beginning of data collection by using the accompanying software for data analysis.

FIG. 2 shows a schematic of the RT-DMA apparatus. The photocurable resin composition (1) is placed on a plane (2). The amount of liquid resin used should be approximately the amount indicated in the figure. The plane is a quartz plate that is sold with the StressTech Rheometer. The 8 mm plate (3) is positioned with a 0.1 mm gap (4) between the plate and the plane. The gap is set via the software accompanying the StressTech Rheometer. Light (5) is provided though the plane (2). Please see the publication “Dynamic Mechanical Analysis of UV-Curable Coatings While Curing” by Robert W. Johnson available at http://reologicainstruments.com/PDF%20files/BobJohnsonUVpaper.pdf, and hereby incorporated by reference in its entirety, for more information on RT-DMA. G′ data was not measured for Examples 45-56.

	TABLE 8
	Example 1	Example 2	Example 3	Example 4	Example 5	Example 6	Example 7	Example 8	Example 9
Dp (mil)	3.53	2.72	2.73	2.62	2.78	2.79	2.95	2.91	2.78
Ec (s)	1.13	1.27	0.94	0.81	0.97	0.77	0.70	0.71	1.00
E3 (s)	2.64	3.81	2.83	2.53	2.85	2.27	1.93	2.00	2.95
E4 (s)	3.50	5.50	4.08	3.71	4.09	3.25	2.71	2.82	4.24
E5 (s)	4.65	7.95	5.88	5.43	5.85	4.65	3.80	3.98	6.07

	TABLE 9
	Example	Example	Example	Example	Example	Example	Example	Example	Example
	10	11	12	13	14	15	16	17	18
Dp (mil)	1.85	2.60	2.66	3.37	3.40	3.99	3.39	3.75	3.50
Ec (s)	0.36	0.75	0.80	0.84	0.77	0.82	0.72	0.75	0.68
E3 (s)	1.79	2.38	2.48	2.04	1.87	1.74	1.75	1.67	1.60
E4 (s)	3.08	3.50	3.61	2.75	2.51	2.23	2.34	2.18	2.13
E5 (s)	5.28	5.15	5.26	3.70	3.36	2.87	3.15	2.85	2.83

	TABLE 10
	Example	Example	Example	Example	Example	Example	Example	Example	Example
	19	20	21	22	23	24	25	26	27
Dp (mil)	5.79	4.59	7.12	4.96	3.32	6.70	4.19	5.90	4.40
Ec (s)	0.92	0.69	0.80	0.82	1.33	0.91	0.69	1.18	1.23
E3 (s)	1.55	1.34	1.22	1.50	3.27	1.43	1.41	1.97	2.44
E4 (s)	1.84	1.66	1.40	1.84	4.42	1.66	1.79	2.33	3.07
E5 (s)	2.18	2.06	1.61	2.25	5.98	1.93	2.27	2.76	3.85

	TABLE 11
	Example	Example	Example	Example	Example	Example	Example	Example	Example
	28	29	30	31	32	33	34	35	36
Dp (mil)	5.98	6.84	6.47	1.95	1.63	2.23	2.33	5.69	5.42
Ec (s)	1.06	1.36	1.30	0.63	1.69	0.98	1.04	1.15	1.22
E3 (s)	1.75	2.10	2.06	2.92	10.66	3.78	3.77	1.96	2.13
E4 (s)	2.07	2.43	2.41	4.88	19.71	5.92	5.79	2.33	2.56
E5 (s)	2.45	2.82	2.81	8.14	36.43	9.27	8.89	2.78	3.08

	TABLE 12
	Exam-	Exam-	Exam-	Exam-	Exam-	Exam-
	ple 37	ple 38	ple 39	ple 40	ple 41	ple 42
Dp (mil)	2.44	3.64	3.38	3.87	2.88	3.60
Ec (s)	0.62	0.77	0.73	0.74	0.76	0.75
E3 (s)	2.11	1.76	1.78	1.61	2.16	1.72
E4 (s)	3.17	2.31	2.39	2.09	3.05	2.28
E5 (s)	4.78	3.04	3.22	2.70	4.32	3.01

	TABLE 13
	Example 43	Example 44	Example 45	Example 46	Example 47	Example 48	Example 49	Example 50
Dp (mil)	4.05	3.38	2.83	2.89	4.15	3.01	9.04	2.80
Ec (s)	0.77	0.59	0.88	0.91	1.39	1.19	2.00	1.19
E3 (s)	1.62	1.44	2.53	2.57	2.86	3.24	2.79	3.47
E4 (s)	2.08	1.94	3.59	3.63	3.63	4.52	3.12	4.96
E5 (s)	2.66	2.61	5.12	5.13	4.62	6.30	3.48	7.08

	TABLE 14
	Exam-	Exam-	Exam-	Exam-	Exam-	Exam-
	ple 51	ple 52	ple 53	ple 54	ple 55	ple 56
Dp (mil)	7.62	3.09	2.38	2.47	3.32	2.86
Ec (s)	1.69	2.36	4.34	1.81	5.31	5.57
E3 (s)	2.51	6.22	15.31	6.09	13.12	15.92
E4 (s)	2.86	8.59	23.31	9.12	17.74	22.59
E5 (s)	3.26	11.87	35.48	13.67	23.97	32.04

TABLE 15
Time (sec)	Storage shear modulus (G′; Pa)
Seconds	50 mW/cm2/1 sec exposure; 0.10 mm gap
after light on	Example 1	Example 2	Example 3	Example 4	Example 5
0.4	1.27E+03	1.43E+03	1.58E+03	7.70E+02	1.23E+03
0.6	5.51E+03	1.23E+03	4.40E+03	1.33E+03	2.87E+03
0.9	1.19E+05	1.79E+04	6.75E+04	3.81E+04	5.74E+04
1.9	6.27E+05	1.21E+05	2.25E+05	2.25E+05	2.26E+05
3.9	1.03E+06	1.74E+05	3.46E+05	3.74E+05	3.91E+05

TABLE 16
Time (sec)
Seconds	Storage shear modulus (G′; Pa)
after	44 mW/cm2/1 sec exposure; 0.05 mm gap
light on	Example 6	Example 7	Example 8	Example 9	Example 10
0.4	3.10E+02	3.10E+02	1.99E+05	3.10E+02	2.45E+04
0.6	1.98E+04	1.61E+04	5.43E+05	1.61E+04	2.14E+05
0.9	2.23E+05	2.23E+05	1.34E+06	2.23E+05	8.33E+05
1.9	9.38E+05	9.38E+05	2.41E+06	9.38E+05	1.65E+06
3.9	1.47E+06	1.46E+06	4.16E+06	1.48E+06	2.74E+06

TABLE 17
Time (sec)	Storage shear modulus (G′; Pa)
Seconds after	44 mW/cm2/1 sec exposure; 0.10 mm gap
light on	Example 11	Example 12	Example 13	Example 14
0.4	7.67E+02	8.70E+02	2.74E+03	7.87E+02
0.6	5.27E+02	1.02E+03	7.15E+03	5.83E+03
0.9	3.08E+04	2.66E+04	8.01E+04	1.34E+05
1.9	2.48E+05	2.18E+05	3.86E+05	7.53E+05
3.9	3.57E+05	3.05E+05	6.58E+05	1.41E+06

TABLE 18
Time (sec)	Storage shear modulus (G′; Pa)
Seconds after	44 mW/cm2/1 sec exposure; 0.10 mm gap
light on	Example 15	Example 16	Example 17	Example 18
0.4	1.82E+03	1.03E+03	2.87E+03	8.24E+03
0.6	7.70E+04	2.13E+04	3.17E+04	7.29E+04
0.9	5.61E+05	2.48E+05	2.57E+05	3.71E+05
1.9	2.40E+06	7.92E+05	1.02E+06	1.30E+06
3.9	3.90E+06	1.17E+06	1.59E+06	2.04E+06

TABLE 19
Storage shear modulus (G′; Pa) 47 mW/cm2/1 sec exposure; 0.10 mm gap
Example 19	Example 20	Example 21	Example 22	Example 23
2.53E+03	1.59E+04	8.35E+04	3.97E+04	1.66E+03
2.14E+04	1.03E+04	4.30E+05	3.19E+05	1.66E+03
1.87E+05	8.46E+04	1.10E+06	1.36E+06	1.66E+03
6.75E+05	2.71E+05	2.55E+06	3.93E+06	1.66E+03
1.05E+06	4.23E+05	2.96E+06	5.41E+06	1.66E+03

TABLE 20
Time (sec)
Seconds after	Storage shear modulus (G′; Pa) 47 mW/cm2/1 sec exposure; 0.10 mm gap
light on	Example 24	Example 25	Example 26	Example 27	Example 28	Example 29	Example 30
0.4	1.47E+03	1.75E+03	1.14E+03	1.82E+03	2.11E+04	7.20E+04	1.90E+04
0.6	1.65E+03	1.36E+03	1.14E+03	1.82E+03	4.09E+05	6.20E+05	3.57E+05
0.9	1.22E+03	1.27E+03	1.14E+03	1.82E+03	2.48E+06	2.96E+06	1.85E+06
1.9	1.78E+03	1.27E+03	1.14E+03	1.82E+03	5.58E+06	9.45E+06	6.37E+06
3.9	5.61E+04	1.80E+04	1.14E+03	1.82E+03	1.08E+07	1.27E+07	9.31E+06

TABLE 21
Time (sec)
Seconds after	Storage shear modulus (G′; Pa) 50 mW/cm2/1 sec exposure; 0.10 mm gap
light on	Example 31	Example 32	Example 33	Example 34	Example 35	Example 36
0.4	1.52E+03	1.31E+03	1.17E+03	1.22E+03	1.15E+03	3.06E+03
0.6	9.97E+02	1.14E+03	1.26E+03	1.24E+03	1.07E+04	7.69E+04
0.9	1.21E+03	9.07E+02	4.95E+03	1.78E+03	9.93E+04	4.56E+05
1.9	1.75E+03	1.49E+03	7.42E+04	2.42E+04	2.77E+05	1.58E+06
3.9	3.82E+03	1.75E+03	1.09E+05	3.29E+04	4.59E+05	2.54E+06

TABLE 22
Time (sec)
Seconds	Storage shear modulus (G′; Pa) 44 mW/cm2/1 sec exposure; 0.05 mm gap
after light on	Example 37	Example 38	Example 39	Example 40	Example 41	Example 42	Example 43	Example 44
0.4	8.67E+03	1.89E+05	7.71E+04	1.00E+05	4.46E+04	3.12E+05	8.28E+05	6.64E+05
0.6	1.12E+05	5.94E+05	4.52E+05	5.02E+05	2.50E+05	8.90E+05	1.11E+06	2.29E+06
0.9	4.62E+05	1.40E+06	1.46E+06	1.56E+06	9.16E+05	1.71E+06	1.97E+06	3.56E+06
1.9	1.10E+06	2.94E+06	2.73E+06	2.86E+06	1.64E+06	2.66E+06	3.30E+06	5.30E+06
3.9	1.63E+06	4.36E+06	4.56E+06	4.37E+06	2.66E+06	4.90E+06	4.86E+06	5.15E+06

TABLE 23
Time (sec)
Seconds after	Storage shear modulus (G′; Pa) 44 mW/cm2/1 sec exposure; 0.10 mm gap
light on	Example 37	Example 38	Example 39	Example 40	Example 41	Example 42	Example 43	Example 44
0.4	1.14E+03	5.17E+03	1.14E+03	6.31E+03	9.45E+02	2.57E+04	6.07E+03	2.75E+04
0.6	1.16E+03	2.77E+04	1.16E+03	2.32E+04	2.85E+03	1.25E+05	5.31E+04	3.05E+05
0.9	1.82E+04	2.22E+05	1.82E+04	2.44E+05	6.57E+04	6.39E+05	5.11E+05	1.19E+06
1.9	1.87E+05	8.47E+05	1.87E+05	1.12E+06	3.89E+05	2.20E+06	2.11E+06	3.17E+06
3.9	2.74E+05	1.26E+06	2.76E+05	1.79E+06	6.83E+05	3.19E+06	3.00E+06	4.21E+06

TABLE 24
Tensile test on thin cured strips (24 h after cure)
	Example 6	Example 7	Example 8	Example 9	Example 10	Example 11	Example 12
Elastic Modulus (MPa)	1403	1023	666	537	1030	2262	1892
Elongation at Break (%)	5.8	10.9	19.5	14.6	7.9	2.9	2.2
Tensile Strength (MPa)	44.2	32.4	26.5	17.8	35.7	51.9	35.8

TABLE 25
Tensile test on thin cured strips (24 h after cure)
	Example 28	Example 29	Example 30
Elastic Modulus (MPa)	1674	1968	1590
Elongation at Break (%)	4.9	3.3	2.1
Tensile Strength (MPa)	50.6	49.9	29.6

TABLE 26
Tensile test on thin cured strips (24 hrs after cure)
	Example	Example	Example	Example	Example	Example	Example	Example
	37	38	39	40	41	42	43	44
Elastic Modulus (MPa)	1811	1685	1844	1692	1769	1681	1786	394
Elongation at Break (%)	2.5	1.5	1.9	1.1	2.5	1.6	0.9	14.4
Tensile Strength (MPa)	39.1	22.1	28.7	18.1	38.4	24.5	14.2	19.0

TABLE 27
Example No.	CPI/RPI	CPC/RPC
1	1.33	1.13
2	0.18	3.19
3	0.25	3.19
4	0.43	3.19
5	0.67	3.19
6	0.67	1.37
7	0.67	1.30
8	0.67	1.23
9	0.67	1.33
10	0.67	1.33
11	0.67	1.47
12	0.67	1.55
13	0.67	1.47
14	0.67	1.47
15	0.25	1.48
16	0.25	1.48
17	0.25	1.48
18	0.25	1.48
19	0.25	2.23
20	0.25	2.27
21	0.25	2.23
22	0.25	0.94
23	0.25	N/A
24	0.25	N/A
25	0.25	N/A
26	0.25	N/A
27	0.25	N/A
28	0.25	0.54
29	0.25	0.54
30	0.25	0.54
31	0.82	3.56
32	0.76	1.10
33	0.76	1.10
34	0.82	3.56
35	1.22	3.56
36	1.26	1.10
37	0.50	1.87
38	0.50	1.87
39	0.50	1.87
40	0.50	1.87
41	0.50	1.87
42	0.50	1.87
43	0.50	1.87
44	0.50	1.87
45	0.71	6.50
46	0.71	6.50
47	0.88	6.53
48	4.09	6.53
49	1.02	6.53
50	0.70	6.53
51	0.35	6.53
52	1.29	6.53
53	1.29	6.53
54	1.29	6.53
55	1.29	6.53
56	0.40	6.56

Comparative Example 1

This comparative example illustrates the results obtained when curing a typical laser curable resin with LED light. A solid state laser emitting at 354.7 nm is used, with 1 mil scan spacing, 65 mW/cm² power, and 58 kHz frequency, for obtaining the Ec and Dp values from the “working curve” by using WINDOWPANES™ technique. The LED is a single UV LED “bare bulb” (Model No. NCSUO33A; Nichia Corporation, Japan) having a peak wavelength of 365 nm and is used as the LED light source in a light curing apparatus, wherein the single LED light is bottom-mounted on a flat surface inside a 30° C. chamber and positioned in an upward-looking arrangement and pointing vertically. The LED light is powered by a 3.30 V/0.050 A DC output from a Programmable Power Supply (Model No. PSS-3203; GW Instek).

The composition of Comparative Example 1 is shown in Table 28. Ec and Dp data, as determined using the previously mentioned methods, when cured with both laser light and LED light is shown in Table 29.

TABLE 28
Comparative Example 1
Component      wt %
Ebecryl 3700   20
Celloxy 2021P  70.78
Chivacure 1176 5
Irgacure 184   4
Silwet 7600    0.2
BYK A501       0.02
Total          100

	TABLE 29
	Laser Light	LED Light
	Ec	6.89 mJ/cm2	0.45 seconds
	Dp	4.10 mils	19.05 mils

All references, including publications, patent applications, and patents, cited herein are hereby incorporated by reference to the same extent as if each reference were individually and specifically indicated to be incorporated by reference and were set forth in its entirety herein.

The use of the terms “a” and “an” and “the” and similar referents in the context of describing the invention (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to,”) unless otherwise noted. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention.

Preferred embodiments of this invention are described herein, including the best mode known to the inventors for carrying out the invention. Variations of those preferred embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect skilled artisans to employ such variations as appropriate, and the inventors intend for the invention to be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above-described elements in all possible variations thereof is encompassed by the invention unless otherwise indicated herein or otherwise clearly contradicted by context.

Claims

1. A photocurable resin composition for additive fabrication comprising a polymerizable component that is polymerizable by free-radical polymerization, cationic polymerization, or both free-radical polymerization and cationic polymerization, and a photoinitiating system capable of initiating the free-radical polymerization, cationic polymerization, or both free-radical polymerization and cationic polymerization;

wherein the photocurable resin composition is a liquid at about 25° C., and is capable of curing to provide a solid upon irradiation with light emitted from a light emitting

diode (LED), wherein the light has a wavelength of from about 100 nm to about 900 nm, preferably from 200 nm to about 600 nm, more preferably from about 280 nm to about 500 nm, more preferably from about 300 nm to about 475 nm, more preferably from about 340 nm to about 415 nm, preferably having a peak at about 365 nm, and

wherein the liquid photocurable resin composition has a Critical Exposure (Ec) and a Depth of Penetration (Dp) as measured on a layer of the photocurable resin composition as the composition is curing, wherein Ec is from about 0.01 seconds to about 6.0 seconds and Dp is ¼ to 4 times, preferably from ⅓ to 3 times, the thickness of the layer.

2. The photocurable resin composition for additive fabrication of claim 1, wherein the Dp is from about 1 to about 8 mils, preferably from about 1 to about 7 mils, more preferably from about 2 to about 7 mils.

3. The photocurable resin composition for additive fabrication of claim 1, wherein the photocurable resin composition as it is curing with a light intensity of 50 mW/cm2 for 1.0 second has a storage shear modulus (G′) value of greater than about 1.0×105 Pa, preferably from about 1.0×105 Pa to about 1.0×107 Pa, more preferably from about 5.0×106 Pa to about 1.0×107 Pa when it is measured at 3.9 seconds from the start of light exposure on a Real Time-Dynamic Mechanical Analyzer (RT-DMA) with an 8 mm plate at a sample gap of 0.10 mm.

4. The photocurable resin composition for additive fabrication of claim 1, wherein the photocurable resin composition for additive fabrication comprises at least one free-radical photoinitiator, preferably selected from the group consisting of benzoylphosphine oxides, aryl ketones, benzophenones, hydroxylated ketones, 1-hydroxyphenyl ketones, ketals, metallocenes, and any combination thereof, more preferably selected from the group consisting of 2,4,6-trimethylbenzoyl diphenylphosphine oxide and 2,4,6-trimethylbenzoyl phenyl, ethoxy phosphine oxide, bis(2,4,6-tnmethylbenzoyl)-phenylphosphineoxide, 2-methyl-1-[4-(methylthio)phenyl]-2-morpholinopropanone-I, 2-benzyl-2-(dimethylamino)-I-[4-(4-morpholinyl)phenyl]-1-butanone, 2-dimethylamino-2-(4-methyl-benzyl)-1-(4-morpholin-4-yl-phenyl)-butan-I-one, 4-benzoyl-4′-methyl diphenyl sulphide, 4,4′-bis(diethylamino)benzophenone, and 4,4′-bis(N,N′-dimethylamino) benzophenone (Michler's ketone), benzophenone, 4-methyl benzophenone, 2,4,6-trimethyl benzophenone, dimethoxybenzophenone, 1-hydroxycyclohexyl phenyl ketone, phenyl (1-hydroxyisopropyl)ketone, 2-hydroxy-1-[4-(2-hydroxyethoxy)phenyl]-2-methyl-1-propanone, 4-isopropylphenyl(1-hydroxyisopropyl)ketone, oligo-[2-hydroxy-2-methyl-I-[4-(I-methylvinyl)phenyl]propanone], camphorquinone, 4,4′-bis(diethylamino)benzophenone, benzil dimethyl ketal, bis(eta 5-2-4-cyclopentadien-I-yl) bis[2,6-difluoro-3-(IH-pyrrol-I-yl)phenyl]titanium, and any combination thereof.

5. The photocurable resin composition for additive fabrication of claim 1, wherein the photoinitiating system is a photoinitiator having both cationic initiating function and free radical initiating function.

6. The photocurable resin composition for additive fabrication of claim 1 wherein the photocurable resin composition for additive fabrication comprises at least one cationic photoinitiator, preferably selected from the group consisting of onium salts, halonium salts, iodosyl salts, selenium salts, sulfonium salts, sulfoxonium salts, diazonium salts, metallocene salts, isoquinolinium salts, phosphonium salts, arsonium salts, tropylium salts, dialkylphenacylsulfonium salts, thiopyrilium salts, diaryl iodonium salts, triaryl sulfonium salts, sulfonium antimonate salts, ferrocenes, di(cyclopentadienyliron)arene salt compounds, and pyridinium salts, and any combination thereof, more preferably selected from the group consisting of aromatic diazonium salts, aromatic sulfonium salts, aromatic iodonium salts, metallocene based compounds, aromatic phosphonium salts and silanol aluminium complexes, more preferably selected from the group consisting of aromatic sulfonium salts, aromatic iodonium salts, and metallocene based compounds, even more preferably selected from the group consisting of triarylsulfonium salts, diaryliodonium salts, and metallocene based compounds.

7. The photocurable resin composition for additive fabrication of claim 1, wherein the cationic photoinitiator is at least one with an anion selected from the group consisting of BF4−, AsF6−, SbF6−, PF6−, B(C6F6)4−, perfluoroalkylsulfonates, perfluoroalkylphosphates, and carborane anions.

8. The photocurable resin composition for additive fabrication of claim 1 wherein the cationic photoinitiator is at least one cation selected from the group consisting of aromatic sulfonium salts, aromatic iodonium salts, and metallocene based compounds with at least an anion selected from the group consisting of SbF6−, PF6−, B(C6F5)4−, perfluoroalkylsulfonates, perfluoroalkylphosphates, and (CH6B11Cl6)−.

9. The photocurable resin composition for additive fabrication of claim 1, wherein the cationic photoinitiator is an aromatic sulfonium salt based cationic photoinitiator selected from the group consisting of 4-(4-benzoylphenylthio)phenyldiphenylsulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-hydroxyethyloxyphenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-chlorophenyl)sulfonium hexafluoroantimonate, 4-[4-(3-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-methylphenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-hydroxyethylphenyl)sulfonium hexafluoroantimonate, 4-[4-(4-hydroxyethyloxybenzoyl)phenylthio]phenylbis(4-fluoro phenyl)sulfonium hexafluoroantimonate, 4-[4-(4-hydroxyethyloxybenzoyl)phenylthio]phenyldiphenylsulfonium hexafluoroantimonate, 4-[4-(4-hydroxyethyloxybenzoyl)phenylthio]phenylbis(4-hydroxyethyloxyphenyl)sulfonium hexafluoroantimonate, 4-(4-benzoylphenylthio)phenylbis(4-methoxyethoxyphenyl)sulfonium hexafluoroantimonate, 4-[4-(3-methoxybenzoyl)phenylthio]phenyldiphenylsulfonium hexafluoroantimonate, 4-[4-(3-methoxycarbonylbenzoyl)phenylthio]phenyldiphenylsulfonium hexafluoroantimonate, 4-[4-(2-hydroxymethylbenzoyl)phenylthio]phenyldiphenylsulfonium hexafluoroantimonate, 4-[4-(4-methylbenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-[4-(4-)phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-[4-(4-fluorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium hexafluoroantimonate, 4-[4-(2-methoxycarbonylbenzoyl)phenylthio]phenylbis(4-fluoro phenyl)sulfonium hexafluoroantimonate, bis[4-(diphenylsulfonio)phenyl]sulfide bishexafluorophosphate, bis[4-(diphenylsulfonio)phenyl]sulfide bistetrafluoroborate, bis[4-(diphenylsulfonio)phenyl]sulfide tetrakis(pentafluorophenyl)borate, diphenyl-4-(phenylthio)phenylsulfonium hexafluorophosphate, diphenyl-4-(phenylthio)phenylsulfonium tetrafluoroborate, diphenyl-4-(phenylthio)phenylsulfonium tetrakis(pentafluorophenyl)borate, triphenylsulfonium hexafluorophosphate, triphenylsulfonium hexafluoroantimonate, triphenylsulfonium tetrafluoroborate, triphenylsulfonium tetrakis(pentafluorophenyl)borate, bis[4-(di(4-(2-hydroxyethoxy))phenylsulfonio)phenyl]sulfide bishexafluorophosphate, bis[4-(di(4-(2-hydroxyethoxy))phenylsulfonio)phenyl]sulfide bistetrafluoroborate, and bis[4-(di(4-(2-hydroxyethoxy))phenylsulfonio)phenyl]sulfide tetrakis(pentafluorophenyl)borate.

10. The photocurable resin composition for additive fabrication of claim 1 wherein the cationic photoinitiator is an aromatic iodonium salt based cationic photoinitiator selected from the group consisting of diphenyliodonium hexafluorophosphate, diphenyliodonium hexafluoroantimonate, diphenyliodonium tetrafluoroborate, diphenyliodonium tetrakis(pentafluorophenyl)borate, bis(dodecylphenyl)iodonium hexafluorophosphate, bis(dodecylphenyl)iodonium hexafluoroantimonate, bis(dodecylphenyl)iodonium tetrafluoroborate, bis(dodecylphenyl)iodonium tetrakis(pentafluorophenyl)borate, 4-methylphenyl-4-(1-methylethyl)phenyliodonium hexafluorophosphate, 4-methylphenyl-4-(1-methylethyl)phenyliodonium hexafluoroantimonate, 4-methylphenyl-4-(1-methylethyl)phenyliodonium tetrafluoroborate, and 4-methylphenyl-4-(1-methylethyl)phenyliodonium tetrakis(pentafluorophenyl)borate.

11. The photocurable resin composition for additive fabrication of claim 1, wherein the cationic photoinitiator is selected from the group consisting of tetrakis(pentafluorophenyl)borate or hexafluoroantimonate salt of 4-(4-benzoylphenylthio)phenyldiphenylsulfonium, 4-(4-benzoylphenylthio)phenylbis(4-hydroxyethyloxyphenyl)sulfonium, 4-(4-benzoylphenylthio)phenylbis(4-fluorophenyl)sulfonium, 4-(4-benzoylphenylthio)phenylbis(4-chlorophenyl)sulfonium, 4-[4-(3-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium, 4-[4-(2-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium, (4-thiophenoxyphenyl)diphenylsulfonium, S,S,S′,S′-tetraphenylthiobis(4,1-pheny lene)disulfonium, triphenylsulfonium, (chlorophenyl)diphenylsulfonium, chloro[S-(phenyl)thianthrenium], S-(phenyl)thianthrenium, diphenyl-4-(4′-thiophenoxy)thiophenoxyphenylsulfonium, phenyldi(4-thiophenoxyphenyl)sulfonium, S-(4-thiophenoxyphenyl)thianthrenium, and (thiodi-4,1-phenylene)bis[bis[4-(2-hydroxyethoxy)phenyl]sulfonium, tris(4-(4-acetylphenyl)thiophenyl)sulfonium, bis(4-dodecylphenyl)iodonium, [4-[(2-hydroxytetradecyl)oxy]phenyl]phenyliodonium, (4-methylphenyl)[4-[[2-[[[[3-(trifluoromethyl)phenyl]amino]carbonyl]oxy]tetradecyl]oxy]phenyl]iodonium, bis(4-dodecylphenyl)iodonium, [4-(1-methylethyl)phenyl](4-methylphenyl)iodonium, and any combination thereof.

12. The photocurable resin composition for additive fabrication of claim 1, wherein the cationic photoiniator is a sulfonium borate photoinitiator, more preferably a triarylsulfonium borate, more preferably tris(4-(4-acetylphenyl)thiophenyl)sulfonium tetrakis(pentafluorophenyl)borate or 4-[4-(3-chlorobenzoyl)phenylthio]phenylbis(4-fluorophenyl)sulfonium tetrakis(pentafluorophenyl)borate.

13. The photocurable resin composition for additive fabrication of claim 1, wherein the polymerizable component is polymerizable by both free-radical polymerization and cationic polymerization.

14. The photocurable resin composition for additive fabrication of claim 1, wherein the polymerizable component is a vinyloxy compound, preferably selected from the group consisting of bis(4-vinyloxybutyl)isophthalate, tris(4-vinyloxybutyl)trimellitate, and combinations thereof.

15. The photocurable resin composition for additive fabrication of claim 1, which further includes a photosensitizer, preferably selected from the group consisting of methanones, xanthenones, pyrenemethanols, anthracenes, quinones, xanthones, thioxanthones, benzoyl esters, benzophenones, and any combination thereof, more preferably selected from the group consisting of [4-[(4-methylphenyl)thio]phenyl]phenyl-methanone, isopropyl-9H-thioxanthen-9-one, 1-pyrenemethanol, 9-(hydroxymethyl)anthracene, 9,10-diethoxyanthracene, anthracene, anthraquinones, 2-methylanthraquinone, 2-ethylanthraquinone, 2-tertbutylanthraquinone, 1-chloroanthraquinone, 2-amylanthraquinone, thioxanthones and xanthones, isopropyl thioxanthone, 2-chlorothioxanthone, 2,4-diethylthioxanthone, 1-chloro-4-propoxythioxanthone, methyl benzoyl formate, methyl-2-benzoyl benzoate, 4-benzoyl-4′-methyl diphenyl sulphide, 4,4′-bis(diethylamino)benzophenone, and any combination thereof.

16. The photocurable resin composition for additive fabrication of claim 15, wherein the photosensitizer is a fluorone, preferably selected from the group consisting of 5,7-diiodo-3-butoxy-6-fluorone, 5,7-diiodo-3-hydroxy-6-fluorone, 9-cyano-5,7-diiodo-3-hydroxy-6-fluorone, and any combination thereof.

17. The photocurable resin composition for additive fabrication of claim 1, which further includes a chain transfer agent, preferably a chain transfer agent for a cationic polymerizable component which is preferably a hydroxyl-containing compound, more preferably a compound containing 2 or more than 2 hydroxyl-groups, preferably the chain transfer agent is selected from the group consisting of a polyether polyol, polyester polyol, polycarbonate polyol, ethoxylated or propoxylated aliphatic or aromatic compounds having hydroxyl groups, dendritic polyols, or hyperbranched polyols, more preferably a polyether polyol comprising an alkoxy ether group of the formula [(CH2)nO]m, wherein n can be 1 to 6 and m can be 1 to 100, or polytetrahydrofuran.

18. The photocurable resin composition for additive fabrication of claim 1, which further includes one or more additives selected from the group consisting of bubble breakers, antioxidants, surfactants, acid scavengers, pigments, dyes, thickneners, flame retardants, silane coupling agents, ultraviolet absorbers, resin particles, core-shell particle impact modifiers, soluble polymers and block polymers.

19. The photocurable resin composition for additive fabrication of claim 1, wherein the ratio by weight of cationic photoinitiator to free-radical photoinitiator is less than about 4.0, preferably from about 0.1 to about 4.0, preferably from about 0.1 to about 2.0, more preferably from about 0.1 to about 1.5, more preferably from about 0.2 to about 1.0.

20. The photocurable resin composition for additive fabrication of claim 1, wherein the photocurable resin composition is free or substantially free of antimony-containing initiator.

21. The photocurable resin composition for additive fabrication of claim 1, wherein the ratio by weight of cationic polymerizable component to free-radical polymerizable component is less than about 7.0, preferably from about 0.5 to about 6.5, more preferably from about 1.0 to about 6.5, more preferably from about 0.5 to about 2.0, more preferably from about 1.0 to about 1.5.

22. The photocurable resin composition for additive fabrication of claim 1, wherein at least about 30 wt %, preferably 40 wt %, of the ingredients in the photocurable resin for additive fabrication are bio-based, rather than petroleum based.

23. A three-dimensional article comprising a cured photocurable resin, wherein the cured photocurable resin is obtained by curing the photocurable resin composition for additive fabrication of claim 1 by irradiating it with light emitted from a light emitting diode (LED) light having a wavelength from about 100 nm to about 900 nm, preferably from 200 nm to about 600 nm, more preferably from about 280 nm to about 500 nm, more preferably from about 300 nm to about 475 nm, preferably having a peak at about 365 nm.

24. A process for making a three-dimensional object comprising the steps of forming and selectively curing a layer of the photocurable resin composition for additive fabrication of claim 1 by irradiation with light from a light emitting diode (LED) having a wavelength from about 100 nm to about 900 nm, preferably from 200 nm to about 600 run, more preferably from about 280 nm to about 500 nm, more preferably from about 300 nm to about 475 nm, preferably having a peak at about 365 nm, and repeating the steps of forming and selectively curing a layer of the photocurable resin composition a plurality of times to obtain a three-dimensional object.