Method for making an aromatic polycarbonate

This invention relates to an extrusion method preparing polycarbonates from a solution of an oligomeric polycarbonate. A mixture of bis(methyl salicyl)carbonate (BMSC), BPA and a transesterification catalyst are first equilibrated at moderate temperatures to provide a solution of polycarbonate oligomer in methyl salicylate. The solution is then fed to a devolatilizing extruder, where the polymerization reaction is completed and the methyl salicylate solvent is removed. The solution comprising the oligomeric polycarbonate can also be pre-heated under pressure to a temperature above the boiling point of methyl salicylate and subsequently fed to a devolatilizing extruder equipped for rapid flashing off the solvent. The method provides polycarbonate with greater efficiency than the corresponding process in which unreacted monomers are fed to the extruder. Additionally, the method of the invention does not require the isolation of a precursor polycarbonate comprising ester-substituted phenoxy terminal groups.

Skip to: Description  ·  Claims  ·  References Cited  · Patent History  ·  Patent History
Description
RELATED APPLICATION

This application is a continuation-in-part of copending U.S. application Ser. No. 10/167,901 filed Jun. 12, 2002 now abandoned which is incorporated herein by reference.

BACKGROUND OF THE INVENTION

This invention relates to a method of preparing polycarbonate. More particularly the method relates to a method whereby a solution comprising a solvent and an oligomeric polycarbonate is introduced into a devolatilizing extruder wherein the oligomeric polycarbonate is converted into high molecular weight polycarbonate while simultaneously removing the solvent. More particularly, the instant invention relates to the formation under mild conditions of polycarbonates having extremely low levels of Fries rearrangement products, a high level of endcapping and low levels of residual solvent.

Polycarbonates, such as bisphenol A polycarbonate, are typically prepared either by interfacial or melt polymerization methods. The reaction of a bisphenol such as bisphenol A (BPA) with phosgene in the presence of water, a solvent such as methylene chloride, an acid acceptor such as sodium hydroxide and a phase transfer catalyst such as triethylamine is typical of the interfacial methodology. The reaction of bisphenol A with a source of carbonate units such as diphenyl carbonate at high temperature in the presence of a catalyst such as sodium hydroxide is typical of currently employed melt polymerization methods. Each method is practiced on a large scale commercially and each presents significant drawbacks.

The interfacial method for making polycarbonate has several inherent disadvantages. First it is a disadvantage to operate a process which requires phosgene as a reactant due to obvious safety concerns. Second it is a disadvantage to operate a process which requires using large amounts of an organic solvent because expensive precautions must be taken to guard against any adverse environmental impact. Third, the interfacial method requires a relatively large amount of equipment and capital investment. Fourth, the polycarbonate produced by the interfacial process is prone to having inconsistent color, higher levels of particulates, and higher chloride content, which can cause corrosion.

The melt method, although obviating the need for phosgene or a solvent such as methylene chloride requires high temperatures and relatively long reaction times. As a result, by-products may be formed at high temperature, such as the products arising by Fries rearrangement of carbonate units along the growing polymer chains. Fries rearrangement gives rise to undesired and uncontrolled polymer branching which may negatively impact the polymer's flow properties and performance. The melt method further requires the use of complex processing equipment capable of operation at high temperature and low pressure, and capable of efficient agitation of the highly viscous polymer melt during the relatively long reaction times required to achieve high molecular weight.

Some years ago, it was reported in U.S. Pat. No. 4,323,668 that polycarbonate could be formed under relatively mild conditions by reacting a bisphenol such as BPA with the diaryl carbonate formed by reaction phosgene with methyl salicylate. The method used relatively high levels of transesterification catalysts such as lithium stearate in order to achieve high molecular weight polycarbonate. High catalyst loadings are particularly undesirable in melt polycarbonate reactions since the catalyst remains in the product polycarbonate following the reaction. The presence of a transesterification catalyst in the polycarbonate may shorten the useful life span of articles made therefrom by promoting increased water absorption, polymer degradation at high temperatures and discoloration.

In copending U.S. applications Ser. Nos. 09/911,439 and 10/167903, now issued as U.S. Pat. Nos. 6,420,512 and 6,506,871 respectively, extrusion of a mixture of an ester-substituted diaryl carbonate, such as bis-methyl salicyl carbonate, a dihydroxy aromatic compound, such as bisphenol A, and a transesterification catalyst, such as tetrabutylphosphonium acetate (TBPA), afforded high molecular weight polycarbonate. The extruder employed was equipped with one or more vacuum vents to remove by-product ester-substituted phenol. Similarly, a precursor polycarbonate having ester-substituted phenoxy endgroups, for example methyl salicyl endgroups, when subjected to extrusion afforded a polycarbonate having a significantly increased molecular weight relative to the precursor polycarbonate. The reaction to form a higher molecular weight polycarbonate may be catalyzed by residual transesterification catalyst present in the precursor polycarbonate, or by a combination of any residual catalyst and an additional catalyst such as TBPA introduced in the extrusion step. Fries rearrangement products were not observed in the product polycarbonates.

Although the methods described in copending U.S. application Ser. Nos. 09/911,439 and 10/167,903 (now issued as U.S. Pat. Nos. 6,420,512 and 6,506,871 respectively) represent significant enhancements in the preparation of polycarbonate relative to older methods, additional improvements are needed. For example, it would be highly desirable to increase the throughput rate of starting materials through the extruder in order to achieve greater efficiency. In addition, it would be highly desirable to avoid having to isolate a precursor polycarbonate having ester-substituted phenoxy endgroups prior to its extrusion to afford a higher molecular weight polycarbonate.

BRIEF SUMMARY OF THE INVENTION

The present invention provides a method for the preparation of polycarbonate, said method comprising extruding in the presence of a transesterification catalyst at one or more temperatures in a temperature range between about 100° C. and about 400° C. a solution comprising a solvent and an oligomeric polycarbonate, said extruding being carried out on an extruder equipped with at least one vent adapted for solvent removal, said oligomeric polycarbonate comprising polycarbonate repeat units derived from at least one dihydroxy aromatic compound, said oligomeric polycarbonate comprising ester substituted phenoxy terminal groups having structure I
wherein R1 is a C1-C20 alkyl group, C4-C20 cycloalkyl group, or C4-C20 aryl group; R2 is independently at each occurrence a halogen atom, cyano group, nitro group, C1-C20 alkyl group, C4-C20 cycloalkyl group, C4-C20 aryl group, C1-C20 alkoxy group, C4-C20 cycloalkoxy group, C4-C20 aryloxy group, C1-C20 alkylthio group, C4-C20 cycloalkylthio group, C4-C20 arylthio group, C1-C20 alkylsulfinyl group, C4-C20 cycloalkylsulfinyl group, C4-C20 arylsulfinyl group, C1-C20 alkylsulfonyl group, C4-C20 cycloalkylsulfonyl group, C4-C20 arylsulfonyl group, C1-C20 alkoxycarbonyl group, C4-C20 cycloalkoxycarbonyl group, C4-C20 aryloxycarbonyl group, C2-C60 alkylamino group, C6-C60 cycloalkylamino group, C5-C60 arylamino group, C1-C40 alkylaminocarbonyl group, C4-C40 cycloalkylaminocarbonyl group, C4-C40 arylaminocarbonyl group, or C1-C20 acylamino group; and b is an integer 0-4.

The present invention further relates to a method for preparing solutions comprising an ester substituted phenol solvent and an oligomeric polycarbonate, and the conversion of said oligomeric polycarbonate into high molecular weight polycarbonate with simultaneous removal said solvent, said method comprising:

    • Step (I) heating a mixture comprising at least one dihydroxy aromatic compound, an ester substituted diaryl carbonate and a transesterification catalyst at a temperature in a range between about 100° C. and about 300° C. to provide a solution of an oligomeric polycarbonate in an ester substituted phenol solvent; and
    • step (II) extruding said solution of oligomeric polycarbonate in said ester substituted phenol at one or more temperatures in a range between about 100° C. and about 400° C., and at one or more screw speeds in a range between about 50 and about 1200 rpm, said extruding being carried out on an extruder comprising at least one vent adapted for solvent removal.

In another aspect the present invention relates to a polycarbonate prepared according to the method of the invention, said polycarbonate having a very high level of endcapping, a very low level of Fries product, and a very low level of residual solvent.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a devolatilizing extruder and feed system suitable for use according to the method of the present invention.

FIG. 2 illustrates an alternative configuration for a devolatilizing extruder and feed system suitable for use according to the method of the present invention.

FIG. 3 illustrates yet another devolatilizing extruder and feed system suitable for use according to the method of the present invention.

 DETAILED DESCRIPTION OF THE INVENTION

The present invention may be understood more readily by reference to the following detailed description of preferred embodiments of the invention and the examples included therein. In the following specification and the claims which follow, reference will be made to a number of terms which shall be defined to have the following meanings.

The singular forms “a”, “an” and “the” include plural referents unless the context clearly dictates otherwise.

“Optional” or “optionally” means that the subsequently described event or circumstance may or may not occur, and that the description includes instances where the event occurs and instances where it does not.

As used herein, the term “oligomeric polycarbonate” refers to a polycarbonate oligomer having a number average molecular weight of less than 5000 daltons and includes oligomeric polycarbonates comprising polycarbonate repeat units derived from one or more dihydroxy aromatic compounds.

As used herein, when describing an oligomeric polycarbonate, the expression “polycarbonate repeat units derived from at least one dihydroxy aromatic compound” means a repeat unit-incorporated into an oligomeric polycarbonate by reaction of a dihydroxy aromatic compound with a source of carbonyl units, for example the reaction of bisphenol A with bis(methyl salicyl)carbonate.

As used herein, the term “high molecular weight polycarbonate” means polycarbonate having a number average molecular weight, Mn, of 8000 daltons or more.

As used herein, the term “solvent” can refer to a single solvent or a mixture of solvents.

As used herein, the term “solution comprising a solvent and an oligomeric polycarbonate” refers to a liquid comprising an oligomeric polycarbonate, said liquid comprising at least 10 percent by weight solvent.

As used herein, the term “melt polycarbonate” refers to a polycarbonate made by the transesterification of a diaryl carbonate with a dihydroxy aromatic compound.

“BPA” is herein defined as bisphenol A or 2,2-bis(4-hydroxyphenyl)propane.

As used herein the term “Fries product” is defined as a structural unit of the product polycarbonate which upon hydrolysis of the product polycarbonate affords a carboxy-substituted dihydroxy aromatic compound bearing a carboxy group adjacent to one or both of the hydroxy groups of said carboxy-substituted dihydroxy aromatic compound. For example, in bisphenol A polycarbonate prepared by a melt reaction method in which Fries reaction occurs, the Fries product includes those structural features of the polycarbonate which afford 2-carboxy bisphenol A upon complete hydrolysis of the product polycarbonate.

The terms “Fries product” and “Fries group” are used interchangeably herein.

The terms “Fries reaction” and “Fries rearrangement” are used interchangeably herein.

The terms “double screw extruder” and “twin screw extruder” are used interchangeably herein.

As used herein the term “monofunctional phenol” means a phenol comprising a single reactive hydroxy group.

The terms “vent port” and “vent” are used interchangeably herein.

The term “atmospheric vent” as used herein is meant to indicate a vent which is operated at or near atmospheric pressure. Thus, an atmospheric vent being operated under a slight vacuum, such as that commonly designated “house vacuum”, is meant to fall within the ambit of the term “atmospheric vent”.

As used herein the term “aliphatic radical” refers to a radical having a valence of at least one comprising a linear or branched array of atoms which is not cyclic. The array may include heteroatoms such as nitrogen, sulfur and oxygen or may be composed exclusively of carbon and hydrogen. Examples of aliphatic radicals include methyl, methylene, ethyl, ethylene, hexyl, hexamethylene and the like.

As used herein the term “aromatic radical” refers to a radical having a valence of at least one comprising at least one aromatic group. Examples of aromatic radicals include phenyl, pyridyl, furanyl, thienyl, naphthyl, phenylene, and biphenyl. The term includes groups containing both aromatic and aliphatic components, for example a benzyl group. Aromatic radicals are further illustrated by radicals which comprise both aromatic and cycloaliphatic structural components. For example, the radical 4-cyclohexylphenyl is ranked herein as an aromatic rather than a cycloaliphatic radical.

As used herein the term “cycloaliphatic radical” refers to a radical having a valence of at least one comprising an array of atoms which is cyclic but which is not aromatic. The array may include heteroatoms such as nitrogen, sulfur and oxygen or may be composed exclusively of carbon and hydrogen. Examples of cycloaliphatic radicals include cyclopropyl, cyclopentyl, cyclohexyl, tetrahydrofuranyl and the like.

The present invention provides a method of preparing polycarbonates whereby a solution comprising an oligomeric polycarbonate in a solvent, said oligomeric polycarbonate comprising ester substituted phenoxy endgroups having structure I, is extruded through an extruder adapted to remove solvent. The method of the invention effects both the conversion of the oligomeric polycarbonate to a product polycarbonate having higher molecular weight, and a separation of the solvent initially present in the solution of the oligomeric polycarbonate from the product polycarbonate. Additionally, the method provides for the removal of other volatile materials which may be present in the initial solution of oligomeric polycarbonate, or formed as by-products as the oligomeric polycarbonate is transformed in the extruder to the product polycarbonate.

The oligomeric polycarbonate comprises polycarbonate repeat units and terminal phenoxy endgroups having structure I. Terminal phenoxy endgroups having structure I include ester substituted phenoxy endgroups generally. Ester substituted phenoxy endgroups are exemplified by the 2-ethoxycarbonylphenoxy group, 2-propoxycarbonylphenoxy group, 4-chloro-2-methoxycarbonylphenoxy group, and the 4-cyano-2-methoxycarbonylphenoxy group. Among the various ester substituted phenoxy terminal groups, the 2-methoxycarbonylphenoxy group II is frequently preferred.

The oligomeric polycarbonate comprises repeat units derived from at least one dihydroxy aromatic compound. Dihydroxy aromatic compounds are illustrated by dihydroxy benzenes, for example hydroquinone (HQ), 2-methylhydroquinone, resorcinol, 5-methylresorcinol and the like; dihydroxy naphthalenes, for example 1,4-dihydroxynathalene, 2,6-dihydroxynaphthalene, and the like; and bisphenols, for example bisphenol A and 4,4′-sulfonyldiphenol. The oligomeric polycarbonate typically contains polycarbonate repeat units derived from at least one bisphenol, said polycarbonate repeat units having structure III
wherein R3-R10 are independently a hydrogen atom, halogen atom, nitro group, cyano group, C1-C20 alkyl group, C4-C20 cycloalkyl group, or C6-C20 aryl group; W is a bond, an oxygen atom, a sulfur atom, a SO2 group, a C1-C20 aliphatic radical, a C6-C20 aromatic radical, a C6-C20 cycloaliphatic radical, or the group
wherein R11 and R12 are independently a hydrogen atom, C1-C20 alkyl group, C4-C20 cycloalkyl group, or C4-C20 aryl group; or R11 and R12 together form a C4-C20 cycloaliphatic ring which is optionally substituted by one or more C1-C20 alkyl, C6-C20 aryl, C5-C21 aralkyl, C5-C20cycloalkyl groups, or a combination thereof.

Repeat units having structure III are illustrated by repeat units present in bisphenol A polycarbonate, bisphenol M polycarbonate, bisphenol C polycarbonate, and the like.

In one embodiment of the present invention the oligomeric polycarbonate comprises repeat units having structure IV
said repeat units IV being derived from bisphenol A. In an alternate embodiment of the present invention the oligomeric polycarbonate comprises repeat units having structures IV and V
said repeat units V being derived from 4,4′-sulfonyldiphenol.

The solution of the oligomeric polycarbonate used according to the method of the present invention comprises at least one solvent. The solvent may be a single solvent or a mixture of solvents. Typically the solvent present in the solution of the oligomeric polycarbonate comprises from about 10 percent by weight to about 99 percent by weight, preferably from about 10 percent by weight to about 70 percent by weight of the solution. For example a solution of oligomeric bisphenol A polycarbonate comprising phenoxy endgroups II dissolved in methyl salicylate, said solution being about 40 percent by weight of said oligomeric polycarbonate and about 60 percent by weight methyl salicylate. Alternatively the solution may comprise more than one solvent, for example a solution of oligomeric bisphenol A polycarbonate comprising phenoxy endgroups II dissolved in a mixture of ortho-dichlorobenzene (ODCB) and methyl salicylate, said solution being about 40 percent by weight of said oligomeric polycarbonate, 30 percent by weight ODCB, and about 30 percent by weight methyl salicylate.

In one embodiment of the present invention the solvent employed according to the method of the present invention comprises at least one ester substituted phenol having structure VI
wherein R1, R2, and b are defined as in structure I. Examples of ester-substituted phenols having structure VI include methyl salicylate, ethyl salicylate, butyl salicylate, 4-chloro methyl salicylate, and mixtures thereof. Solvent VI may be recovered and reused. For example, ester substituted phenols such as VI may be recovered, purified, and reacted with phosgene to make ester substituted diaryl carbonates which in turn can be used to prepare oligomeric polycarbonates comprising terminal phenoxy groups having structure I. Typically, purification of the recovered ester substituted phenol is efficiently carried out by distillation.

The solvent used according to the method of the present invention optionally comprises a halogenated aliphatic solvent, a halogenated aromatic solvent, a non-halogenated aromatic solvent, a non-halogenated aliphatic solvent, or a mixture thereof. Halogenated aromatic solvents are illustrated by ortho-dichlorobenzene (ODCB), chlorobenzene and the like. Non-halogenated aromatic solvents are illustrated by toluene, xylene, anisole, phenol; 2,6-dimethylphenol; and the like. Halogenated aliphatic solvents are illustrated by methylene chloride; chloroform; 1,2-dichloroethane; and the like. Non-halogenated aliphatic solvents are illustrated by ethanol, acetone, ethyl acetate, cyclohexanone, and the like.

In one embodiment of the present invention the solvent employed comprises a mixture of a halogenated aromatic solvent and an ester substituted phenol, for example a mixture of ortho-dichlorobenzene (ODCB) and methyl salicylate.

The transesterification catalyst used according to the present invention may be any catalyst effective in promoting chain growth of the oligomeric polycarbonate during the extrusion. The transesterification catalysts for use according to the method of the present invention may comprise onium catalysts such as a quaternary ammonium compound, a quaternary phosphonium compound, or a mixture thereof.

Quaternary ammonium compounds suitable for use as transesterification catalysts according to the method of the present invention include quaternary ammonium compounds having structure VII
wherein R13-R16 are independently a C1-C20 alkyl group, C4-C20 cycloalkyl group, or a C4-C20 aryl group; and X− is an organic or inorganic anion.

Quaternary ammonium compounds VII are illustrated by tetamethylammonium hydroxide, tetrabutylammonium acetate, tetrabutylammonium hydroxide, and the like.

Quaternary phosphonium compounds suitable for use as transesterification catalysts according to the method of the present invention include quaternary phosphonium compounds having structure VIII
wherein R17-R20 are independently a C1-C20 alkyl group, C4-C20 cycloalkyl group, or a C4-C20 aryl group; and X− is an organic or inorganic anion.

Quaternary phosphonium compounds VIII are illustrated by tetamethylphosphonium hydroxide, tetrabutylphosphonium acetate, tetrabutylphosphonium hydroxide, and the like.

In structures VII and VIII, the anion X− is typically an anion selected from the group consisting of hydroxide, halide, carboxylate, phenoxide, sulfonate, sulfate, carbonate, and bicarbonate. With respect to transesterification catalysts having structures VII and VIII, where X− is a polyvalent anion such as carbonate or sulfate it is understood that the positive and negative charges in structures VII and VIII are properly balanced. For example, in tetrabutylphosphonium carbonate where R17-R20 in structure VIII are each butyl groups and X− represents a carbonate anion, it is understood that X− represents ½(CO3−2).

In one embodiment, the transesterification catalyst used is a combination of a quaternary ammonium compound, a quaternary phosphonium compound, or a mixture thereof, with at least one alkali metal hydroxide, alkaline earth metal hydroxide, or a mixture thereof. For example, a mixture of tetrabutylphosphonium acetate and sodium hydroxide.

Other transesterification catalysts that may be used according to the method of the present invention include one or more alkali metal salts of carboxylic acids, one or more alkaline earth salts of a carboxylic acid, and mixtures thereof. Such transesterification catalysts are illustrated by simple salts of carboxylic acids such as sodium acetate, calcium stearate and the like. Additionally, alkali metal and alkaline earth metal salts of organic polyacids may serve as efficient transesterification catalysts according to the method of the present invention. Alkali metal and alkaline earth metal salts of organic polyacids, such as ethylene diamine tetracarboxylate, may be employed. Salts of organic polyacids are illustrated by disodium magnesium ethylenediamine tetracarboxylate (Na2Mg EDTA).

In one embodiment of the present invention the transesterification catalyst comprises at least one salt of a non-volatile acid. By “non-volatile” it is meant that the acid from which the catalyst is made has no appreciable vapor pressure under melt polymerization conditions. Examples of non-volatile acids include phosphorous acid, phosphoric acid, sulfuric acid, and metal “oxo acids” such as the oxo acids of germanium, antimony, niobium and the like. Salts of non-volatile acids useful as melt polymerization catalysts according to the method of the present invention include alkali metal salts of phosphites; alkaline earth metal salts of phosphites; alkali metal salts of phosphates; alkaline earth metal salts of phosphates, alkali metal salts of sulfates, alkaline earth metal salts of sulfates, alkali metal salts of metal oxo acids, and alkaline earth metal salts of metal oxo acids. Specific examples of salts of non-volatile acids include NaH2PO3, NaH2PO4, Na2HPO4, KH2PO4, CaH2PO4, Cs2HPO4, NaKHPO4, NaCsHPO4, KCsHPO4, Na2SO4, NaHSO4, NaSbO3, LiSbO3, KSbO3, Mg(SbO3)2, Na2GeO3, K2GeO3, Li2GeO3, MgGeO3, Mg2GeO4, and mixtures thereof.

Typically the transesterification catalyst is employed in an amount corresponding to between about 1.0×10−8 and about 1×10−3, preferably between about 1.0×10−6 and about 2.5×10−4 moles of transesterification catalyst per mole of polycarbonate repeat units derived from aromatic dihydroxy compound present in the oligomeric polycarbonate.

Typically, the oligomeric polycarbonate employed is prepared in a step involving heating a dihydroxy aromatic compound with an ester substituted diaryl carbonate in the presence of a transesterification catalyst. Thus, the reactants are combined in a vessel in a ratio between about 0.95 and 1.3 moles, preferably between about 1.0 and about 1.05 moles of ester substituted diaryl carbonate per mole of dihydroxy aromatic compound. The amount of transesterification catalyst employed is between about 1.0×10−8 and about 1×10−3, preferably between about 1.0×10−6 and about 2.5×10−4 moles of transesterification catalyst per mole of dihydroxy aromatic compound employed. Upon heating the mixture at one or more temperatures in a range from about 100° C. to about 400° C., preferably from about 100° C. to about 300° C., and still more preferably from about 100° C. to about 250° C. reaction occurs to produce a solution comprising an equilibrium mixture of product oligomeric polycarbonate, by-product ester substituted phenol (solvent), transesterification catalyst, and low levels of the starting materials, dihydroxy aromatic compound and ester substituted diaryl carbonate. This is referred to as “equilibrating” the reactants. Typically the equilibrium strongly favors the formation of product oligomeric polycarbonate and by-product ester substituted phenol and only traces of the starting materials are observed. The “equilibrated” product mixture may then be introduced into a devolatilizing extruder to effect removal of the by-product ester substituted phenol solvent while converting the oligomeric polycarbonate into a higher molecular weight product polycarbonate. Because, the transesterification catalyst is typically neither consumed in the equilibration step nor removed prior to extrusion, there is typically no need to add additional catalyst during extrusion. Where no additional catalyst is added, the amount of catalyst present during extrusion step (expressed in terms of moles catalyst per mole of polycarbonate repeat units in the oligomeric polycarbonate) will closely approximate the amount of catalyst used in the equilibration step, expressed in moles catalyst per mole dihydroxy aromatic compound.

Typically the ester substituted diaryl carbonate will have structure IX
wherein R1, R2, and b are defined as in structure I. In addition, the dihydroxy aromatic compound is typically, though not always, at least one bisphenol having structure X
wherein R3-R10 and W are defined as in structure III.

In one embodiment, the method of the present invention comprises:

    • Step (I) heating a mixture comprising at least one dihydroxy aromatic compound, an ester substituted diaryl carbonate and a transesterification catalyst at a temperature in a range between about 100° C. and about 300° C. to provide a solution of an oligomeric polycarbonate in an ester substituted phenol solvent; and
    • Step (II) extruding said solution of oligomeric polycarbonate in said ester substituted phenol at one or more temperatures in a range between about 100° C. and about 400° C., and at one or more screw speeds in a range between about 50 and about 1200 rpm, said extruding being carried out on an extruder comprising at least one vent adapted for solvent removal.

In some instances it may be desirable to remove a portion of the ester-substituted phenol formed during the equilibration of the monomers. This may be effected conveniently by heating the mixture of monomers and the transesterification catalyst under vacuum, typically from about 0.01 atmospheres to about 0.9 atmospheres, and distilling off a portion of the ester substituted phenol. As ester substituted phenol is distilled from the mixture undergoing the equilibration reaction, the molecular weight of the oligomeric polycarbonate will tend to increase. If sufficient ester substituted phenol by-product is removed, the number average molecular weight (Mn) of the polycarbonate product may be in excess of 5000 daltons and in some instances in excess of 8000 daltons. Thus, in one aspect of the present invention a mixture comprising at least dihydroxy aromatic compound is reacted with at least one ester substituted diaryl carbonate in the presence of a transesterification catalyst at a temperature between about 100° C. and about 300° C. and a portion of the by-product ester substituted phenol is removed by distillation. The equilibration product may be a mixture comprising an ester substituted phenol solvent and a polycarbonate comprising terminal phenoxy groups having structure I and having a number average molecular weight in excess of 5000 daltons. This equilibration product is then fed to a devolatilizing extruder wherein the polycarbonate is converted to still higher molecular weight product polycarbonate, said product polycarbonate having a high level of endcapping, a low level of Fries product, and a low level of residual solvent. In one embodiment of the present invention, a portion of the ester substituted phenol formed during equilibration is distilled from the mixture undergoing equilibration and a like amount of ODCB is added to provide a solution comprising a polycarbonate having a number average molecular weight in excess of 5000 daltons, ester substituted phenol and ODCB. This solution is then fed to a devolatilizing extruder wherein the polycarbonate is converted to a product polycarbonate having a higher molecular weight, said product polycarbonate having a Fries content of under 10 ppm, an endcapping level of at least 97%, and less than 1 percent by weight solvent. Typically, in instances in which the polycarbonate formed in the equilibration reaction has a number average molecular weight in excess of 5000 daltons, it will have a Mn value in a range between 5000 daltons and about 15000 daltons.

Oligomeric polycarbonates comprising ester substituted terminal phenoxy groups I may be prepared by a variety of other methods in addition to the equilibration method described. For example, oligomeric bischloroformates of bisphenols may be prepared by reaction of one or more bisphenols with phosgene under interfacial conditions in a methylene chloride water mixture at low pH. Such bischloroformates may then be further reacted under interfacial conditions with an ester substituted phenol, for example methyl salicylate, to afford an oligomeric polycarbonate comprising ester substituted terminal phenoxy groups in methylene chloride solution. The product oligomeric polycarbonate in solution may then be subjected to the method of the present invention. Catalysts employed during the interfacial reaction are typically removed from the solution of the oligomeric polycarbonate in a series of washing steps in which the methylene chloride solution of the oligomeric polycarbonate is washed repeatedly with water to remove sodium chloride. Under such circumstances, additional catalyst may be required and may be added during or just prior to the extrusion step.

In one embodiment, a monofunctional phenol chainstopper is added to a solution of an oligomeric polycarbonate comprising ester substituted phenoxy terminal groups, said oligomeric polycarbonate being prepared using the equilibration technique described herein. The solution is then subjected to extrusion devolatilization to afford a product polycarbonate incorporating terminal phenoxy groups derived from said chainstopper. Suitable monofunctional phenol chainstoppers include p-cumylphenol and cardanol.

The extruder used according to the method of the present invention is of the devolatilizing extruder type. That is, it is an extruder adapted for separating substantial amounts of solvent from a polymer-solvent mixture. The extruder, therefore must possess at least one and preferably a greater number of vents adapted for solvent removal. FIG. 1, FIG. 2 and FIG. 3 illustrate devolatilizing extruders and feed systems suitable for use according to the method of the present invention. In one embodiment of the invention (illustrated here with reference to FIG. 1) reactants, ester substituted diaryl carbonate, dihydroxy aromatic compound and a transesterification catalyst are combined in a reaction vessel 10 and heated at a temperature in a range between about 100° C. and about 300° C., preferably between about 150° C. and about 250° C., at a pressure between about 1 atmosphere and about 10 atmospheres, preferably between about 1 and about 2 atmospheres, to provide a solution of an oligomeric polycarbonate in an ester substituted phenol. The solution is transferred by means of a gear pump 14 via piping 17 which is directly plumbed into a fourteen barrel, vented, twin screw extruder 20, said extruder possessing screw design 30. The extruder is operated at a temperature between about 100° C. and about 400° C., preferably between about 200° C. and about 350° C., at a screw speed between about 50 and about 1200 rpm. The solution is introduced into the upstream edge of barrel one 22. The segmentations along the extruder indicate the transitions from one extruder barrel to the next. Barrel two is labeled 24. (The remaining barrels 3-14 are not labeled.) The extruder screw design 30 consists of conveying screw elements illustrated by 32 and mixing sections which include an initial mixing section 34 and four zones of intense mixing 36. The extruder is equipped with four atmospheric vents 40, said vents being connected to a manifold 42 for removal of ester substituted phenol solvent and other volatile by-products formed as the oligomeric polycarbonate is converted into product polycarbonate within the extruder. Solvent vapors and other volatile by-products are condensed in a shell and tube condenser 44 which is attached to a source of house vacuum 46. The extruder is further equipped with two vacuum vents 50. Vacuum vents 50 are connected via a cold trap 52 to a vacuum pump 54. As mentioned, the extruder comprises four mixing sections which provide for intense mixing of the contents of the extruder. These are indicated in the screw design 30 as the mixing sections labeled 36. Mixing sections labeled 36 in the screw design correspond to reaction zones 26 of the extruder. Said reaction zones are believed to provide for enhanced rates of polycarbonate chain growth relative to other domains within the extruder.

In an alternate embodiment of the invention (illustrated here with reference to FIG. 2) reactants, ester substituted diaryl carbonate, dihydroxy aromatic compound and a transesterification catalyst are combined in a reaction vessel 10 and heated at a temperature in a range between about 100° C. and about 300° C., preferably between about 150° C. and about 250° C., at a pressure between about 0.0001 and about 10 atmospheres,i preferably between about 0.001 and about 2 atmospheres, to provide a solution of an oligomeric polycarbonate in an ester substituted phenol. The reaction vessel 10 is adapted for operation at either subambient, ambient or elevated pressure, and is equipped with a mixer 11. The reaction vessel 10 is connected via a solvent recovery manifold 12 to a condenser 44. The solution is transferred by means of a gear pump 14 through a heat exchanger 15 wherein the solution is superheated. Heat exchanger 15 is linked to pressure control valve 16 which is directly plumbed into a fourteen barrel, vented, twin screw extruder 20, said extruder possessing screw design 30. The extruder is operated at a temperature between about 100° C. and about 400° C., preferably between about 200° C. and about 350° C., at a screw speed between about 50 and about 1200 rpm. The solution is introduced into the upstream edge of barrel one 22. The segmentations along the extruder indicate the transitions from one extruder barrel to the next. Barrel two is labeled 24. (The remaining barrels 3-14 are not labeled.) The extruder screw design 30 consists of conveying screw elements illustrated by 32 and mixing sections which include an initial mixing section 34 and four zones of intense mixing 36. The extruder is equipped with four atmospheric vents 40, said vents being connected to a manifold 42 for removal of ester substituted phenol solvent and other volatile by-products formed as the oligomeric polycarbonate is converted into product polycarbonate within the extruder. Solvent vapors and other volatile by-products are condensed in a shell and tube condenser 44 which is attached to a source of house vacuum 46. The extruder is further equipped with two vacuum vents 50. Vacuum vents 50 are connected via a cold trap 52 to a vacuum pump 54. As mentioned, the extruder comprises four mixing sections which provide for intense mixing of the contents of the extruder. These are indicated in the screw design 30 as the mixing sections labeled 36. Mixing sections labeled 36 in the screw design corresponds to reaction zones 26 of the extruder. Said reaction zones are believed to provide for enhanced rates of polycarbonate chain growth relative to other domains within the extruder.

In yet another embodiment of the invention (illustrated here with reference to FIG. 3) monomers; ester substituted diaryl carbonate, and dihydroxy aromatic compound, are combined in a vessel 1 and heated at a temperature in a range between about 100° C. and about 300° C., preferably between about 150° C. and about 250° C., to provide a molten mixture of monomers which is transferred forward into the system the system by means of gear pump 14 through. Vessel 1 is optimally equipped with a means for stirring the molten mixture. Flow meter 2 provides for accurate metering of the molten mixture of monomers into the downstream sections of the system. A transesterification catalyst may be added to the molten mixture of monomers at point 3 or directly into vessel 1. The molten mixture of monomers optionally comprising a transesterification catalyst is introduced via static mixture 4 into heat exchanger 15 and from thence into reaction vessel 10. Reaction vessel 10 comprises at least one stirrer 11 and is adapted for removal of ester substituted phenol solvent formed as the monomers equilibrate to form a solution comprising an oligomeric polycarbonate, said oligomeric polycarbonate comprising ester-substituted phenoxy endgroups. Ester-substituted phenol solvent is removed via solvent removal manifold 12 which is attached to condenser 44, cold trap 52 and vacuum pump 54. Reaction vessel 10 is further adapted for introduction of additional monomers, catalyst or solvents at one or more of points 17 and 18. Typically the solution of oligomeric polycarbonate is heated to a temperature between about 150° C. and 300° C. The solution of oligomeric polycarbonate is then transferred via gear pump 14 via pressure control valve 16 which is directly plumbed into the feed inlet zone of a fourteen barrel, vented, twin screw, devolatilizing extruder 20, said extruder possessing screw design 30. The extruder is operated at a temperature between about 100° C. and about 400° C., preferably between about 200° C. and about 350° C., at a screw speed between about 50 and about 1200 rpm. The solution is introduced into the upstream edge of barrel 3. The segmentations along the extruder indicate the transitions from one extruder barrel to the next. Barrel two is labeled 24. (The remaining barrels 3-14 are not labeled.) The extruder screw design 30 consists of conveying screw elements illustrated by 32 and mixing sections which include an initial mixing section 34 and four zones of intense mixing 36. The extruder is equipped with an atmospheric vent 40 connected to manifold 42 for removal of ester substituted phenol solvent and other volatiles. Solvent vapors and other volatile by-products are condensed in a shell and tube condenser 44 which may be attached to a source of house vacuum or operated at atmospheric pressure. Atmospheric vent 40 is positioned so that at least one kneading block 34 is interposed between the feed inlet zone (the zone directly under pressure control valve 16) and the atmospheric vent. This interposition of the kneading block between the feed inlet zone and the atmospheric vent serves to prevent entrainment of solids out through the atmospheric vent by escaping solvent vapors. The extruder 20 is further equipped with four vacuum vents 50. Here again, a kneading block 34 is interposed between the feed inlet zone the vacuum vents in order to prevent the entrainment of solids by the rapidly escaping solvent vapors. Vacuum vents are located over conveying elements 32 to minimize the movement of polymer into the vents themselves. Vacuum vents 50 are connected via solvent manifolds 42, condensers 44, and cold traps 52, to vacuum pumps 54. As mentioned, the extruder comprises four mixing sections which provide for intense mixing of the contents of the extruder. These are indicated in the screw design 30 as the mixing sections labeled 36. Mixing sections labeled 36 in the screw design correspond to reaction zones 26 of the extruder. The reaction zones 26 are believed to provide for enhanced rates of polycarbonate chain growth relative to other domains within the extruder. Additionally, the system illustrated in FIG. 3 comprises optional water injection inlets 60 which provide for enhanced removal of volatile components from the polycarbonate being prepared. Finally, the extruder is equipped with one or more sensors 70 which may be used to monitor melt temperature, die pressure, torque or other system parameters which in turn may be used as when operating the system according to a closed loop control strategy. For example, because melt temperature, die pressure and torque are strongly dependent upon the molecular weight of the product polycarbonate, sensors monitoring melt temperature and torque might indicate that additional monomer or catalyst should be added upstream (e.g. at inlet 17) in order to reduce or increase the molecular weight of the product polycarbonate emerging from the extruder die face.

The extruder used according to the method of the present invention, which may be a single screw or multiple screw extruder is typically operated at one or more temperatures in a range between about 100° C. and about 400° C. and at one or more screw speeds in a screw speed range, said range being between about 50 revolutions per minute (rpm) and about 1200 rpm, preferably between about 50 rpm and about 500 rpm.

Extruders suitable for use according to the method of the present invention include co-rotating intermeshing double screw extruders, counter-rotating non-intermeshing double screw extruders, single screw reciprocating extruders, and single screw non-reciprocating extruders.

It is a general principle of extruder operation that as the feed rate is increased a corresponding increase in the screw speed must be made in order to accommodate the additional material being fed. Moreover, the screw speed determines the residence time of the material being fed to the extruder, here the solution of the oligomeric polycarbonate and transesterification catalyst. Thus the screw speed and feed rate are typically interdependent. It is useful to characterize this relationship between feed rate and screw speed as a ratio. Typically the extruder is operated such that the ratio of starting material introduced into the extruder in pounds per hour to the screw speed expressed in rpm falls within a range of from about 0.01 to about 100, preferably from about 0.05 to about 5. For example, the ratio of feed rate to screw speed where the solution of comprising an oligomeric polycarbonate and transesterification catalyst are being introduced at 1000 pounds per hour into an extruder be in operated at 400 rpm is 2.5. The maximum and minimum feed rates and extruder screw speeds are determined by, among other factors, the size of the extruder, the general rule being the larger the extruder the higher the maximum and minimum feed rates.

As noted, in one embodiment of the present invention, a mixture of an oligomeric polycarbonate comprising endgroups having structure I and a solvent is heated under pressure to produce a “superheated” solution, meaning that the temperature of said superheated solution is greater than the boiling point of the solvent at atmospheric pressure. Typically, the temperature of the superheated oligomeric polycarbonate will be between about 2° C. and about 200° C. higher than the boiling point of the solvent at atmospheric pressure. In instances where there are multiple solvents present, the solution of oligomeric polycarbonate is “superheated” with respect to at least one of the solvent components. Where the solution of oligomeric polycarbonate contains significant amounts of both high and low boiling solvents, it may be advantageous to superheat the solution of oligomeric polycarbonate with respect to all solvents present (i.e. above the boiling point at atmospheric pressure of the highest boiling solvent). Superheating of the solution of the oligomeric polycarbonate may be achieved by heating the mixture under pressure, typically at a pressure less than about 10 atmospheres but greater than one atmosphere. Superheated solutions of oligomeric polycarbonates are conveniently prepared in pressurized heated feed tanks, pressurized heat exchangers, extruders, pressurized reaction vessels and the like. The superheated solution is then introduced into a devolatilizing extruder through a pressure control valve, the pressure control valve having a cracking pressure higher than atmospheric pressure. The backpressure generated by the pressure control valve prevents evaporation of the solvent prior to introducing the solution into the extruder. Typically, the pressure control valve is attached (plumbed) directly to the extruder and serves as the principal feed inlet of the extruder. In one embodiment of the present invention in which the oligomeric polycarbonate comprising ester-substituted phenoxy endgroups is introduced into a devolatilizing extruder as a superheated solution, the extruder is equipped with at least one side feeder.

In one embodiment, the extruder in combination with the side feeder is equipped with one or more atmospheric vents in close proximity to the principal feed inlet comprising the pressure control valve. The side feeder is typically positioned in close proximity to the pressure control valve through which the superheated oligomeric polycarbonate is introduced into the extruder. The side feeder comprises at least one atmospheric vent. Alternatively, the pressure control valve through which the superheated oligomeric polycarbonate is introduced may be-attached to the side feeder itself in which instance the pressure control valve is attached to the side feeder at a position between the point of attachment of the side feeder to the extruder and the atmospheric vent located on the side feeder. In yet another alternative embodiment, the superheated solution of oligomeric polycarbonate may be introduced through multiple pressure control valves which may be attached to the side feeder, the extruder, or to both extruder and side feeder. The heated zones of the extruder are typically operated at one or more temperatures between about 100° C. and about 400° C. The expression “wherein the extruder is operated at a temperature between about 100° C. and about 400° C.” refers to the heated zones of the extruder, it being understood that the extruder may comprise both heated and unheated zones.

The superheated solution of oligomeric polycarbonate passes through the pressure control valve into the feed zone of the extruder which due to the presence of the aforementioned atmospheric vents is at atmospheric pressure. The solvent present in the superheated solution of oligomeric polycarbonate undergoes sudden and rapid evaporation thereby effecting at least partial separation of the oligomeric polycarbonate and the solvent. The solvent vapors emerge through the atmospheric vents. The atmospheric vents are attached to a solvent vapor manifold and condenser in order to recover solvent and prevent its adventitious release. Additionally, the extruder is equipped with at least one vent operated at subatmospheric pressure which serves to remove solvent not removed through the atmospheric vents. Vents operated at subatmospheric pressure are referred to herein as “vacuum vents” and are maintained at from about 1 to about 30, preferably from about 10 to about 29 inches of mercury as measured by a vacuum gauge measuring vacuum (as opposed to a pressure gauge measuring pressure). Typically, at least two vacuum vents are preferred.

Extruders suitable for use in embodiments of the present invention wherein a superheated oligomeric polycarbonate solution is being fed include co-rotating intermeshing double screw extruders, counter-rotating non-intermeshing double screw extruders, single screw reciprocating extruders, and single screw non-reciprocating extruders.

In some instances, it may be found that the product polycarbonate prepared according to the method of the present invention is of insufficient molecular weight or retains too much of the solvent originally present in the solution of the oligomeric polycarbonate. In such instances, simply subjecting the product polycarbonate to a second extrusion on the same or a different devolatilizing extruder typically results in a product polycarbonate having an increased molecular weight and a reduced level of residual solvent. Thus, in one embodiment of the present invention, a solution of an oligomeric polycarbonate comprising terminal groups having structure I and a solvent is subjected to devolatilization extrusion at a temperature between about 100° C. and about 400° C. on an extruder equipped with at least one vent adapted for solvent removal to provide an initial product polycarbonate. The initial product polycarbonate is then introduced into a second extruder, said second extruder being equipped with at least one vacuum vent. The second extruder is operated at a temperature in a range between about 100° C. and about 400° C., and at a screw speed in a range between about 50 and about 1200 rpm.

The method of the present invention may be carried out in a batch or continuous mode. In one embodiment, the method of the present invention is carried out as a batch process wherein monomers and transesterification catalyst are equilibrated in a batch reactor to form a solution of the oligomeric polycarbonate. This solution is then fed to a devolatilizing extruder and the product polycarbonate is isolated until the solution is consumed. Alternatively, the method of the present invention may be carried out as a continuous process wherein the monomers and catalyst are continuously fed to, and the solution of oligomeric polycarbonate is continuously removed from a continuous reactor. Thus a mixture of BMSC, BPA and transesterification catalyst may be fed to one end of a tube reactor heated to a temperature between about 160° C. and about 250° C. A solution of an oligomeric polycarbonate comprising phenoxy endgroups II emerges at the opposite end of the tube reactor and is fed to a devolatilizing extruder from which emerges the product polycarbonate.

It is understood, especially for melt reactions of the type presented in the instant invention, that purity of the monomers employed may strongly affect the properties of the product polycarbonate. Thus, it is frequently desirable that the monomers employed be free of, or contain only very limited amounts of, contaminants such as metal ions, halide ions, acidic contaminants and other organic species. This may be especially true in applications such as optical disks, (e.g. compact disks) where contaminants present in the polycarbonate can affect disk performance. Typically the concentration of metal ions, for example iron, nickel, cobalt, sodium, and postassium, present in the monomer should be less than about 10 ppm, preferably less than about 1 ppm and still more preferably less than about 100 parts per billion (ppb). The amount of halide ion present in the polycarbonate, for example fluoride, chloride and bromide ions, should be minimized in order to inhibit the absorption of water by the product polycarbonate as well as to avoid the corrosive effects of halide ion on equipment used in the preparation of the polycarbonate. Certain applications, for example optical disks, may require very low levels of halide ion contaminants. Preferably, the level of halide ion present in each monomer employed should be less than about 1 ppm. The presence of acidic impurities, for example organic sulfonic acids which may be present in bisphenols such as BPA, should be minimized since only minute amounts of basic catalysts are employed in the oligomerization and subsequent polymerization steps. Even a small amount of an acidic impurity may have a large effect on the rate of oligomerization and polymerization since it may neutralize a substantial portion of the basic catalyst employed. Lastly, the tendency of polycarbonates to degrade at high temperature, for example during molding, with concomitant loss of molecular weight and discoloration correlates strongly with the presence of contaminating species within the polycarbonate. In general, the level of purity of a product polycarbonate prepared using a melt reaction method such as the instant invention will closely mirror the level of purity of the starting monomers.

Product polycarbonates prepared by the method of the present invention frequently contain only very low levels of Fries products. In many cases no Fries product is detectable when the polycarbonate is subjected to a Fries product analysis. The Fries product analysis is carried out by completely hydrolyzing the polycarbonate and analyzing the hydrolysis product by HPLC. For bisphenol A polycarbonate produced by the method of the present invention, the level of Fries product is a value expressed as parts 2-carboxy bisphenol A per million parts of the product bisphenol A polycarbonate which was subjected to hydrolysis. For bisphenol A polycarbonates prepared using the method of the present invention this value is frequently zero or very close to it.

The product polycarbonates prepared according to the method of the present invention are found to have very high levels, frequently 97 percent or higher, of endcapping. Typically product polycarbonates will be from about 97 to about 99 percent endcapped. Free hydroxyl groups at the polycarbonate chain ends are typically comprise less than about 100 ppm of the total polymer weight. Two types of free hydroxyl chain ends are typically observed for polycarbonates prepared according to the method of the present invention from BPA and BMSC: hydroxyl groups attached to a BPA residue (“BPA OH”), and hydroxyl groups attached to a salicyl ester residue (“salicyl OH”). Typically, the concentration of “BPA OH” endgroups is less than about 100 ppm based on the total weight of the product polymer. Likewise, the concentration of “salicyl OH” is typically less than about 100 ppm. Endgroups bearing “salicyl OH” groups have the structure indicated by structure XI
and are quantified by nuclear magnetic resonance spectroscopy (NMR). It should be noted that the concentrations of hydroxyl endgroups and percent endcapping described above refers to product polycarbonate and not the oligomeric polycarbonate. Additionally, in instances in which the product polycarbonate has been prepared by first equilibrating a mixture of an ester substituted diaryl carbonate with one or more dihydroxy aromatic compounds to afford a solution comprising an oligomeric polycarbonate and subsequently subjecting said solution to extrusion on a devolatilizing extruder, the concentrations of hydroxyl endgroups and percent endcapping in the product polycarbonate will reflect the molar ratio of ester substituted diaryl carbonate to total dihydroxy aromatic compound. Typically, this ratio should be in a range between about 1.01 and about 1.1. Typically, the product polycarbonate prepared by the method of the present invention will contain only very small amounts of residual starting dihydroxy aromatic compound (generally less than about 20 ppm) and ester substituted diaryl carbonate (generally less than about 350 ppm).

The product polycarbonates prepared by the method of the present invention may optionally be blended with any conventional additives used in thermoplastics applications, such as preparing molded articles. These additives include UV stabilizers, antioxidants, heat stabilizers, mold release agents, coloring agents, antistatic agents, slip agents, anti-blocking agents, lubricants, anticlouding agents, coloring agents, natural oils, synthetic oils, waxes, organic fillers, inorganic fillers, and mixtures thereof. Typically, it is preferable to form a blend of the polycarbonate and additives which aid in processing the blend to form the desired molded article, such as an optical article. The blend may optionally comprise from 0.0001 to 10% by weight of the desired additives, more preferably from 0.0001 to 1.0% by weight of the desired additives.

Examples of UV absorbers include, but are not limited to, salicylic acid UV absorbers, benzophenone UV absorbers, benzotriazole UV absorbers, cyanoacrylate UV absorbers and mixtures thereof.

Examples of the aforementioned heat-resistant stabilizers, include, but are not limited to, phenol stabilizers, organic thioether stabilizers, organic phosphite stabilizers, hindered amine stabilizers, epoxy stabilizers and mixtures thereof. The heat-resistant stabilizer may be added in the form of a solid or liquid.

Examples of the mold-release agents include, but are not limited to natural and synthetic paraffins, polyethylene waxes, fluorocarbons, and other hydrocarbon mold-release agents; stearic acid, hydroxystearic acid, and other higher fatty acids, hydroxyfatty acids, and other fatty acid mold-release agents; stearic acid amide, ethylenebisstearamide, and other fatty acid amides, alkylenebisfatty acid amides, and other fatty acid amide mold-release agents; stearyl alcohol, cetyl alcohol, and other aliphatic alcohols, polyhydric alcohols, polyglycols, polyglycerols and other alcoholic mold release agents; butyl stearate, pentaerythritol tetrastearate, and other lower alcohol esters of fatty acids, polylydric alcohol esters of fatty acids, polyglycol esters of fatty acids, and other fatty acid ester mold release agents; silicone oil and other silicone mold release agents, and mixtures of any of the aforementioned.

The coloring agent may be either pigments or dyes. Inorganic coloring agents and organic coloring agents maybe used separately or in combination in the invention.

The polycarbonates prepared by the method of the present invention may be random copolymers, block copolymers, branched or linear When the product polycarbonate is branched a suitable branching agent, such as THPE, 9-carboxyoctadecandioic acid, or 1,3,5-trihydroxybenzene is employed. For example, the inclusion of about 0.02 moles of THPE per mole of BPA in the equilibration reaction of 1 mole of BPA with 1.03 moles of BMSC to form an a solution comprising an oligomeric polycarbonate in methyl salicylate, and subsequent extrusion of the solution on a devolatilizing extruder according to the method of the present invention will provide a branched bisphenol A polycarbonate.

Molded articles, such as a molded optical article, comprising the polycarbonates prepared by the method of the present invention, may be obtained by conventional molding techniques, for example injection molding and compression molding. Additionally molded articles may be prepared from a blend of the product polycarbonate with one or more additional polymers. Such blends, typically prepared using extrusion methods, may be molded using conventional techniques. Injection molding is the more preferred method of forming the molded article.

Because the polycarbonates prepared by the method of the present invention possess advantageous properties such as high impact strength, high clarity, low water absorption, good processability and low birefrigence, they can be advantageously utilized to produce optical articles. End-use applications for the optical article of the invention include, but are not limited to, a digital audio disk, a digital versatile disk, an optical memory disk, a compact disk, an ASMO device and the like; optical lenses, such as contact lenses, lenses for glasses, lenses for telescopes, and prisms; optical fibers; magneto optical disks; information recording media; information transferring media; disks for video cameras, disks for still cameras and the like.

The polycarbonates prepared by the method of the present invention may function as the medium for data storage, i.e. the data may be fixed onto or into the polycarbonate. The polycarbonate may also function as the substrate onto which a data storage medium is applied. Further, some combination of both functions may be employed in a single device, as for instance when the polycarbonate is imprinted with tracking to aid in reading a data storage medium which is applied to the polycarbonate.

EXAMPLES

The following examples are set forth to provide those of ordinary skill in the art with a detailed description of how the methods claimed herein are evaluated, and are not intended to limit the scope of what the inventors regard as their invention. Unless indicated otherwise, parts are by weight, temperature is in ° C.

Molecular weights are reported as number average (Mn) or weight average (Mw) molecular weight and were determined by gel permeation chromatography (GPC) analysis, using a polycarbonate molecular weight standard to construct a broad standard calibration curve against which polymer molecular weights were determined. The temperature of the gel permeation columns was about 25° C. and the mobile phase was chloroform.

Fries content was measured by the KOH methanolysis of resin and is reported as parts per million (ppm). The Fries content was determined as follows. First, 0.50 grams of polycarbonate was dissolved in 4.0 ml of THF (containing p-terphenyl as internal standard). Next, 3.0 mL of 18% KOH in methanol was added to this solution. The resulting mixture was stirred for two hours at room temperature. Next, 1.0 mL of acetic acid was added, and the mixture was stirred for 5 minutes. Potassium acetate by-product was allowed to crystallize over 1 hour. The solid was filtered off and the resulting filtrate was analyzed by high performance liquid chromatography (HPLC) using p-terphenyl as the internal standard.

Concentrations of “BPA-OH” and “salicyl-OH” endgroups were measured by 31P-NMR. Terminal hydroxy groups were first derivatized with 2-chloro-1,3,2-dioxaphospholane (Aldrich). The concentration of residual methyl salicylate was measured by 31P-NMR or by gel permeation chromatography.

Examples 1-5

Solutions of oligomeric polycarbonate in methyl salicylate were prepared by equilibrating a mixture of bis(methyl salicyl)carbonate (BMSC), bisphenol A (BPA) and transesterification catalyst, tetrabutylphosphonium acetate (TBPA), at a temperature in a range between about 160° C. and about 220° C. in a batch melt reactor under a nitrogen atmosphere. The reaction mixture was stirred and heated until equilibrium was reached. Equilibrium was reached in about 80 minutes at about 165° C. and in about 10 minutes at about 220° C. At equilibrium, the solution of oligomeric polycarbonate prepared from mixtures of BMSC (1.03 moles BMSC per mole BPA), BPA and TBPA (2.5×10−4 moles per mole BPA) was about 45 percent by weight polycarbonate oligomer and about 54 to about 55 percent by weight methyl salicylate.

TABLE 1 SOLUTIONS OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE Equili- Oligo- Mole TBPA bration meric Exam- [BMSC]/ Catalyst per Temper- Time to Polycar- ple [BPA] Mole BPA ature Equilibrium bonate Mn 1 1.03 2.5 × 10−4 220° C. 10 minutes 1385 2 1.03 2.5 × 10−4 210° C. 18 minutes 1474 3 1.03 2.5 × 10−4 195° C. 30 minutes 1670 4 1.03 2.5 × 10−4 180° C. 52 minutes 1849 5 1.03 2.5 × 10−4 160° C. 90 minutes 2090

Examples 1-5 in Table 1 illustrate both the characteristics of the equilibrated solution at different temperatures and document the truly oligomeric nature of the material being fed to the extruder. The column heading “[BMSC]/[BPA]” indicates the molar ratio of BMSC and BPA employed in the equilibration reaction. The heading “Mn” indicates the number average molecular weight as determined by gel permeation chromatography measured using a polycarbonate molecular weight standard. Values of Mn are given in daltons. The data in Table 1 illustrate the speed at which equilibration of the reactants can be achieved. Example 1 indicates that solid reactants can be converted into a solution of an oligomeric polycarbonate and transesterification catalyst in methyl salicylate solvent in as little as ten minutes. Because residence times in the extruder are short (from about 0.5 to about 2 minutes on the equipment being used in the Examples which follow), the overall process of converting starting monomers into product polycarbonate can be achieved in under 15 minutes.

Examples 6-101

Solutions of oligomeric bisphenol A polycarbonate in methyl salicylate were prepared as in Examples 1-5 at an equilibration temperature of about 160° C. using as a catalyst either TBPA alone (as in Examples 1-5) or a combination of TBPA with sodium hydroxide. The amount of catalyst employed was 2.5×10−4 moles TBPA per mole BPA and (when present) 2×106 moles sodium hydroxide per mole BPA. Following the equilibration reaction, the solution was transferred by means of nitrogen pressure (about 80 psi) to a gear pump which pumped the solution via an insulated pipe connected directly (hard plumbed) to the upstream edge of barrel one of a 25 millimeter diameter, 14 barrel, co-rotating intermeshing twin screw extruder having a length to diameter ratio of 56. The extruder comprised 6 vents V1-V6 located at the upstream edges of barrel four (V1, vacuum or atmospheric vent), barrel five (V2, optionally closed but at times operated as atmospheric or vacuum vent), barrel seven (V3, vacuum vent), barrel nine (V4, vacuum vent), barrel eleven (V5, vacuum vent) and barrel thirteen (V6, vacuum vent). Vent V1 was operated at atmospheric pressure or alternatively under a slight vacuum (5-10 in. Hg, as measured by a vacuum gauge). Vacuum vents V3 and V4 were operated at moderate vacuum (10-28 in. Hg). Vacuum vents V5 and V6 were operated at moderate to high (>29 in Hg) vacuum. When operated at slight to moderate vacuum (5-28 in Hg), vacuum was supplied to vents V2-V6 with “house” vacuum. In a number of instances, vacuum vent V6 or vacuum vents V5 together with V6 were operated under high (i.e. “full”) vacuum (˜29 in. Hg. as measured by a vacuum gauge). The vacuum vents were connected through solvent recovery manifold and condenser systems to their respective sources of vacuum. In instances in which either V6 alone or V5 and V6 were operated at “full” vacuum, the vent or vents being operated at “full” vacuum were connected via a cold trap to a vacuum pump. Vents V1 and V3-V6 were equipped with type “C” vent port inserts. Vent port inserts are available from the Werner & Pfleiderer Company. Vent port inserts differ in the cross sectional area available for the solvent vapors to escape the extruder: Type “A” inserts are the most restrictive (smallest cross section) and Type “C” are the cast restrictive (largest cross section). As noted, V2 was kept closed in some instances and remained open in others. The screw design comprised conveying elements under the feed inlet and all vents. The screw design further comprised kneading blocks in four “reaction zones” (zones comprising screw elements providing intense mixing) located between vents. The four reaction zones were located between V2 and V3, between V3 and V4, between V4 and V5, and between V5 and V6 respectively. The data in Tables 2-5 below demonstrate the effects of changes in reaction conditions on the properties of the product polycarbonate.

TABLE 2 EXTRUSION OF SOLUTION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, BMSC/BPA = 1.017, Catalyst = TBPA + NaOH Vacuum level at Vent Mass Flow Melt Screw Die (in. Hg) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 6 atm 10 22 22 22 40/17.6 29 288 104 16.3 7 Atm. 18 26 25 25 40/17.6 35 290 104 242 8 Atm. 15 26 25 25 46/20.2 42 293 144 329 9 Atm. 15 26 25 25 50/22.0 50 302 200 347 10  Atm. 15 26 25 25 55/24.2 51 308 248 342 11  Atm. 15 26 25 25 55/24.2 50 306 248 316 Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm) 6 256/277/277/280/280/280/281/281/280 22779/10042/2.268 9792 7 254/278/277/280/280/280/281/280/280 25295/11167/2.265 6115 8 245/279/278/280/280/280/281/280/280 26930/11938/2.256 4419 9 241/279/279/280/280/280/284/281/280 27063/11921/2.270 4544 10  238/279/278/280/280/280/283/281/280 26683/11629/2.295 4948 11  236/280/279/280/280/280/280/280/280 26474/11622/2.278 4296

In Examples 6-11 (Table 2) the ratio of BMSC to BPA employed in the equilibration reaction was 1.017. The catalyst employed for the equilibration reaction was a mixture of tetrabutylphosphonium acetate and sodium hydroxide. The oligomeric polycarbonate in methyl salicylate (MS) solution was found to have a weight average molecular weight, Mw, of 6865 daltons and a number average molecular weight, Mn, of 2980 daltons. In Examples 6-11 the polycarbonate emerging from the extruder was observed to be clear and free of color. Following pelletization the level of residual methyl salicylate present in the product polycarbonate was determined by gas chromatography. The data provided in Examples 6-11 illustrate that polycarbonate may be prepared using the method of the present invention and that the product so obtained contains less than about 1 percent by weight methyl salicylate (MS).

TABLE 3 EXTRUSION OF SOLUTION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, BMSC/BPA = 1.02, Catalyst = TBPA + NaOH Vacuum level at Vent Mass Flow Melt Screw Die (in. Hg) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 12 Atm. 26 27 25 29 40/17.6 62 307 154 520 13  5 27 27 25 29 40/17.6 74 312 182 558 14 15 28 28 28 29 40/17.6 74 313 182 576 15 12 28 28 28 29 40/17.6 54 299 118 562 ppm Molecular Weight OH % Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI total Endcap (ppm) 12 249/303/282/280/281/280/280/282/281 31545/14191/2.223 115 95.2 1046.8 13 249/316/282/281/281/280/282/280/280 33106/14788/2.239 103 95.5 752.1 14 249/283/276/280/280/280/281/280/280 35070/15568/2.253  98 95.5 643.9 15 250/273/273/279/279/280/276/279/280 31437/14026/2.241 186 92.3 1403.2

In Examples 12-15 the solution of the oligomeric polycarbonate in methyl salicylate was prepared from a mixture of BMSC and BPA. The molar ratio of BMSC to BPA was 1.02. The catalyst employed in the equilibration step was a mixture of TBPA and sodium hydroxide. The data in Table 3 illustrate that use of higher levels of vacuum provides higher molecular weight polycarbonate containing still lower levels of residual methyl salicylate than is observed in Examples 6-11.

TABLE 4 EXTRUSION OF SOLUTION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE BMSC/BPA = 1.025, Catalyst = TBPA + NaOH Vacuum level at Vent Mass Flow Melt Screw Die (in. Hg) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 16 12 28 28 29 29 40/17.6 55 295 106 486 17 10 28 28 29 29 40/17.6 62 293 106 508 18 10 28 28 29 29 46/20.2 60 302 133 592 19  5 28 28 29 29 46/20.2 60 302 150 599 Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm) 16 252/278/278/280/280/280/282/281/270 30670/13858/2.213 922.8 17 251/291/292/281/281/280/280/280/265 31436/13215/2.211 770.2 18 248/289/290/280/280/280/281/280/265 32470/14647/2.217 654.3 19 248/290/290/280/280/280/280/280/265 31944/14369/2.223 704.4

In Examples 16-19 the solution of the oligomeric polycarbonate in methyl salicylate was prepared from a mixture of BMSC and BPA. The molar ratio of BMSC to BPA was 1.025. The catalyst employed in the equilibration step was a mixture of TBPA and sodium hydroxide. During the extrusion step vents V5 and V6 were connected to a vacuum pump via a cold trap. Vents V1-V4 were connected to the “house vacuum” via a solvent recovery manifold and condenser. Vent V2 was employed and was connected to the same solvent recovery system and house vacuum as were vents V1, V3 and V4. The vacuum level at which V2 was operated was not determined, however.

TABLE 5 EXTRUSION OF SOLUTION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, BMSC/BPA = 1.03, Catalyst = TBPA + NaOH Vacuum level at Vent Mass Flow Melt Screw Die (in. Hg) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 20 13 28 28 29 29 40/17.6 37 284 114 250 21 13 28 28 29 29 40/17.6 37 285 114 235 22 12 28 28 29 29 40/17.6 50 301 230 181 23 10 28 28 29 29 40/17.6 56 313 351 152 24 10 28 28 29 29 40/17.6 58 325 464 123 ppm Molecular Wt. OH % Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI total Endcap (ppm) 20 246/281/280/280/280/280/281/279/270 24456/11218/2.180 45 98.5 720.8 21 252/281/280/280/280/280/279/280/270 24237/11095/2.184 68 97.8 1003.9  22 253/280/280/280/281/280/284/281/271 25247/11527/2.190 48 98.4 559.4 23 252/280/280/280/281/280/285/280/270 26102/11891/2.195 23 99.2 307.1 24 251/281/281/281/281/280/283/281/270 26863/12030/2.233 18 99.4 183.4

Examples 20-24 illustrate the application of the method of the present invention to a solution of an oligomeric polycarbonate prepared from a mixture of BMSC and BPA having an initial molar ratio of 1.03 moles BMSC to BPA. The catalyst employed in the equilibration reaction was a mixture of tetrabutylphosphonium acetate and sodium hydroxide. Vacuum vent V2 was employed as in Examples 16-19 but the precise pressure at which it was operated was not determined. As in previous Examples, the product polycarbonates of Examples 20-24 were clear and free of color when inspected visually. The column heading “ppm OH total” refers to the concentration of “BPA-OH” and “salicyl-OH” present in the product polycarbonate as determined by 31P-NMR following derivatization with 2-chloro-1,3,2-dioxaphospholane. The column heading “% Endcap” refers to the percentage of the product polycarbonate chain ends which do not terminate in either “BPA-OH” or “salicyl-OH” groups. The data in Table 5 provide evidence that a very high level of endcapping is achieved using the method of the present invention and that the concentration of terminal OH groups in the product polycarbonate is very low.

TABLE 6 EXTRUSION OF SOLUTION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, BMSC/BPA = 1.03, Catalyst = TBPA ONLY Vacuum level at Vent Mass Flow Melt Screw Die (in. Hg) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 25 14 28 28 29 29 40/17.6 35 282 113 286 26 14 28 28 29 29 40/17.6 35 283 113 280 27 12 28 28 29 29 40/17.6 46 298 229 238 28 14 28 28 29 29 40/17.6 54 313 355 183 29 14 28 28 29 29 40/17.6 56 325 464 149 30 14 28 28 29 29 70/30.7 48 323 464 209 Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm) 25 257/280/280/280/280/280/278/280/265 24549/11261/2.180 1134.4  26 285/280/280/280/280/280/279/280/265 24795/11367/2.181 959.5 27 257/280/280/280/280/280/283/280/265 25776/11797/2.184 402.2 28 256/280/280/280/281/280/284/281/265 26544/11656/2.277 216.8 29 255/280/281/281/281/280/283/281/265 26967/12255/2.200 148.9 20 251/276/277/278/278/280/280/280/265 26070/11877/2.195 435.9

Examples 25-30 illustrate the application of the method of the invention to a solution of an oligomeric polycarbonate prepared using only tetrabutyl phosphonium acetate and no sodium hydroxide. Here again, reasonably high molecular weight polycarbonate is obtained upon extrusion of the solution. Vacuum vent V2 was employed as in Examples 16-19 but the precise pressure at which it was operated was not determined. As in previous Examples the product polycarbonates of Examples 25-30 were clear and free of color when inspected visually. The data in Table 6 also reveal a high correlation between product polycarbonate molecular weight, feed rate and extruder screw speed. Thus, for data taken from Examples 25-30, if the product polycarbonate weight average molecular weight, Mw, is plotted against the feed rate in pounds per hour divided by the extruder screw speed in revolutions per minute an excellent linear correlation is observed. Similarly, if the residual methyl salicylate concentration in parts per million is plotted against the feed rate divided by the screw speed, an excellent linear correlation is observed.

Examples 31-37 Preparation of Copolymers

In Examples 31-37 copolymers were obtained by first equilibrating a mixture of bis(methyl salicyl)carbonate (BMSC), bisphenol A (BPA), and hydroquinone (HQ). The ratio of bis(methyl salicyl)carbonate to the total number of moles of the dihydroxy aromatic compounds bisphenol A and hydroquinone was 1.017. The equilibration was carried out as in Examples 1-5 and the resultant solution in methyl salicylate was extruded on an extruder configured as in Examples 6-11. The catalyst was a mixture of TBPA and sodium hydroxide. The temperature of the solution of the oligomeric copolycarbonate fed to the extruder was about 160° C. and was introduced into the extruder using a positive displacement pump. Examples 31-35 employed 20 mole percent hydroquinone (based on the total number of moles of BPA and HQ) in the equilibration step. Examples 36 and 37 employed 40 mole percent hydroquinone (based on the total number of moles of BPA and HQ) in the equilibration step. Data for the preparation of the copolycarbonates are provided in Table 7.

TABLE 7 EXTRUSION OF SOLUTION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, BMSC/(BPA and HQ) = 1.017, Catalyst = TBPA + NaOH Vacuum level at Vent Mass Flow Melt Screw Die (in. Hg) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 31 Atm 21 21 21 25 ˜12 57 315 138 347 32 Atm 21 21 21 25 ˜12 58 306 138 637 33 Atm 21 21 21 23 30 16 301 138 251 34 Atm 21 21 21 24 20 31 288 138 250 35 Atm 21 21 21 25 36 14 285 138 181 36 Atm 22 22 22 25 ˜15 43 315 140 275 37 Atm 21 21 21 24 15 17 308 118  31 Molecular Weight Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI 31 245/271/271/301/321/320/332/331/270 30600/13000/2.4 32 239/271/270/300/311/310/311/311/270 34700/14800/2.3 33 233/261/261/296/308/310/308/309/270 22500/9800/2.3 34 235/271/267/289/289/290/288/288/270 22400/9700/2.3 35 233/266/262/287/289/289/289/289/270 19400/8900/2.2 36 237/272/267/291/311/310/331/330/270 29400/13400/2.2 37 239/273/267/313/311/311/331/330/271 18900/8800/2.1

Examples 31-37 illustrate the use of the present invention for the preparation of copolycarbonates.

Examples 38-50 were run in order to demonstrate the consistency of the method of the present invention. A solution of an oligomeric polycarbonate was prepared as in Example 5. The molar ratio of BMSC to BPA was 1.03. The transesterification catalyst was tetrabutylphosphonium acetate (TBPA, 2.5×10−4 moles TBPA per mole BPA). The extruder was configured as in Examples 16-19. The data presented in Table 8 illustrate consistent molecular weight build in the conversion of the oligomeric polycarbonate into the product polycarbonate.

TABLE 8 EXTRUSION OF SOLUTION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, BMSC/(BPA) = 1.03, Catalyst = TBPA ONLY Vacuum @ Vents Mass Flow Melt Screw Die (in. Hg) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 38 12 28 28 29 29 40/17.6 38 289 201 155 39 12 28 28 29 29 40/17.6 38 289 201 159 40 12 28 28 29 29 40/17.6 39 289 201 166 41 12 28 28 29 29 20/17.6 39 289 201 173 42 12 28 28 29 29 40/17.6 39 290 201 177 43 12 28 28 29 29 40/17.6 40 290 201 183 44 12 25 28 29 29 40/17.6 39 291 201 192 45 12 25 28 29 29 40/17.6 39 292 201 181 46 14 28 28 29 29 40/17.6 41 292 201 188 47 14 28 28 29 29 40/17.6 41 292 201 209 48 14 28 28 29 29 40/17.6 42 292 201 214 49 14 28 28 29 29 40/17.6 42 293 201 214 50 14 28 28 29 29 40/17.6 42 293 201 200 Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm) 38 258/281/281/280/281/280/282/281/265 23194/10642/2.333 647.9 39 257/280/280/280/280/280/281/280/265 23551/10693/2.202 648 40 257/280/280/280/280/280/281/280/265 23978/10978/2.184 594.1 41 257/280/280/280/280/280/280/280/265 23926/11117/2.152 614.9 42 257/280/280/280/280/280/280/280/265 23861/10709/2.228 722 43 257/280/280/280/280/280/280/280/265 23961/10915/2.195 590.6 44 257/280/280/280/280/280/280/280/265 24318/11194/2.172 667 45 257/280/280/280/280/280/280/280/266 24192/11339/2.134 655.2 46 257/280/280/280/280/280/280/280/265 24348/11007/2.212 613.4 47 257/280/280/280/280/280/280/280/265 24717/11317/2.184 644.5 48 257/280/280/280/280/280/280/280/265 24826/11317/2.194 743.3 49 257/280/280/280/280/280/280/280/265 24987/11412/2.190 662.6 50 257/280/280/280/280/280/280/280/265 24878/11375/2.187 698

In Examples 38-50 a single batch of oligomeric polycarbonate in methyl salicylate solution was extruded and the polycarbonate which emerged from the extruder was sampled at six-minute intervals over the course of two hours.

In Examples 51-74 a solution of an oligomeric polycarbonate prepared as in Example 5 was extruded on the same devolatilizing extruder used in Examples 38-50. The ratio of BMSC to BPA was 1.02. Examples 51-71 demonstrate the level of consistency achieved. As in Examples 38-50, a single solution of oligomeric polycarbonate was fed to the extruder for a period of about 2 hours. Examples 51-74 represent samples of the product polycarbonate collected about every six minutes as the product polycarbonate emerged from the extruder. The molecular weight and level of residual methyl salicylate were determined for each sample. Examples 72-74 demonstrate that the process may be operated at higher feed rates than the 17.6 pounds of solution per hour used in Examples 51-71. Examples 72 and 73 demonstrate that feed rates as high as 35.1 and 41.6 pounds of solution per hour may be used without sacrificing the molecular weight of the product polycarbonate. Moreover, low levels of residual methyl salicylate may be maintained. Example 74 highlights the effect of screw speed on product polycarbonate molecular weight and the level of residual methyl salicylate contained in the product polycarbonate.

TABLE 9 EXTRUSION OF SOLUTION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, BMSC/(BPA) = 1.02, Catalyst = TBPA ONLY Vacuum @ Vents Mass Flow Melt Screw Die (in. Hg) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 51 15 28 28 29 29 40/17.6 65 302 200 477 52 15 28 28 29 29 40/17.6 65 304 199 486 53 15 28 28 29 29 40/17.6 66 304 199 506 54 15 28 28 29 29 40/17.6 67 304 199 488 55 15 28 28 29 29 40/17.6 67 305 199 496 56 15 28 28 29 29 40/17.6 66 305 199 504 57 15 28 28 29 29 40/17.6 67 305 199 507 58 15 28 28 29 29 40/17.6 67 306 199 521 59 15 28 28 29 29 40/17.6 67 306 199 512 60 15 28 28 29 29 40/17.6 67 306 199 519 61 15 28 28 29 29 40/17.6 67 307 199 523 62 15 28 28 29 29 40/17.6 67 307 199 550 63 15 28 28 29 29 40/17.6 67 308 199 500 64 15 28 28 29 29 40/17.6 67 308 199 524 65 15 28 28 29 29 40/17.6 67 308 199 496 66 15 28 28 29 29 40/17.6 67 308 199 550 67 15 28 28 29 29 40/17.6 67 308 199 535 68 15 28 28 29 29 40/17.6 67 308 199 523 69 15 28 28 29 29 40/17.6 67 309 199 548 70 15 28 28 29 29 40/17.6 67 308 199 562 71 15 28 28 29 29 40/17.6 67 309 199 596 72 15 28 28 29 29 80/35.1 62 372 655 73 15 28 28 29 29 95/41.6 53 365 655 74 15 28 28 29 29 40/17.6 69 369 650 Residual Total Actual Barrel Temperatures Molecular Weight MS % OH/“MS” Example (° C.) Mw/Mn/PDI (ppm) Endcap OH 51 257/280x5/282/280/265 31417/14266/2.202 428.3 52 256/280x7/265 31470/13923/2.260 53 255/280x7/265 31597/13989/2.259 481.7 54 255/280x7/265 31678/14010/2.261 476.3 55 255/280x7/265 31766/14063/2.259 486.7 56 255/280x7/265 32002/14136/2.264 532.6 57 256/280x2/281/280x4/265 32008/14354/2.230 477.5 58 256/280x7/265 32109/14409/2.228 434.5 59 256/280x7/265 32631/14369/2.271 569.6 60 256/280x7/265 32569/14352/2.269 470.9 61 256/280x7/265 32314/14225/2.272 499.2 62 257/280x7/265 32964/14524/2270 4775 63 256/280x6/281/266 32417/14293/2.268 604.4 64 256/280x7/281/265 32884/14464/2.274 509.5 65 256/280x7/265 32725/14394/2.274 513.8 66 256/280x7/265 32930/14499/2.271 493.2 67 256/280x7/265 33647/14571/2.309 493.1 68 256/280x7/265 33752/16821/2.007 535.8 69 256/280x7/265 32809/14406/2.277 527.2 70 256/280x7/265 32794/14363/2.283 505.9 97.9 49/16 71 256/280x7/265 33202/14488/2.292 529.6 72 256/280x7/265 33604/14619/2.299 309.9 98.5 36/10 73 256/280x7/265 33143/15448/2.145 416.9 97.7 51/13 74 256/280x7/265 35339/14654/2.412 62.6 99.2 19/0 

In Table 9 the column heating “Total OH/“MS” OH” provides the total concentration of OH endgroups (expressed in ppm) present in the product polycarbonate (numerator) and the measured concentration of “salicyl-OH” groups (“MS” OH) expressed in parts per million (denominator). The data demonstrate very high levels of product polycarbonate endcapping. The product polycarbonate of example 70 was analyzed for the presence of residual monomer. Less than 350 ppm residual BMSC, and less than 20 ppm residual BPA were found in the product polycarbonate.

Examples 75-80 illustrate the method of the invention in which a chain stopper, p-cumylphenol was included in the equilibration step. Thus BMSC, BPA and p-cumylphenol (0.03 mole per mole BPA) were equilibrated as in Example 5 to provide a solution of an oligomeric polycarbonate in methyl salicylate. The molar ratio of BMSC to BPA was 1.03. As in Examples 38-50, a single solution of the oligomeric polycarbonate was fed to the extruder configured as in Examples 16-19. Examples 75-80 represent samples of the product polycarbonate which were collected at regular intervals over a period of about 1.5 hours. The molecular weight and level of residual methyl salicylate determined for each sample. Data for Examples 75-80 are gathered in Table 10 and demonstrate the successful use of a chain stopper to control molecular weight within the context of the present invention.

TABLE 10 EXTRUSION OF SOLUTION OF PCP-CHAINSTOPPED OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, PCP LEVEL = 0.03 MOLE PER MOLE BPA, BMSC/(BPA) = 1.03, Catalyst = TBPA ONLY Vacuum @ Vents Mass Flow Melt Screw Die (in. Hg.) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 75 15 25 25 29 29 40/17.6 20 282 125 65 76 22 28 27 29 29 40/17.6 30 288 200 60 77 22 28 28 29 29 40/17.6 35 296 299 40 78 22 28 28 29 29 40/17.6 39 304 402 35 79 22 28 28 29 29 40/17.6 41 311 503 32 80 25 28 28 29 29 30/13.2 34 288 201 65 Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm) 75 264/278/280x5/282/265 19572/8847/2.212 1442.8 76 260/280x2/281x2/280/281x2/265 20298/9185/2.210 1158.7 77 257/280/281x3/280/283/282/265 20546/9315/2.206 934.5 78 254/280/281x3/280/284/281/265 20922/9486/2.206 723.7 79 253/280/281x2/282/280/285/282/265 21007/9516/2.208 595.5 80 257/280/279x2/278/280/274/277/264 21718/9839/2.207 618.8

Examples 81-86 illustrate the use of the method of the invention to obtain a polycarbonate comprising methyl salicyl endgroups and a very low level of residual solvent in a single extrusion step. Thus BMSC and BPA were equilibrated as in Example 5 to provide a solution of an oligomeric polycarbonate in methyl salicylate. The molar ratio of BMSC to BPA was 1.035. As in Examples 38-50, a single solution of the oligomeric polycarbonate was fed to the extruder configured as in Examples 16-19. Examples 81-86 represent samples of the product polycarbonate which were collected at regular intervals over a period of about 1.5 hours. The molecular weight and level of residual methyl salicylate were determined for each sample. Data for Examples 81-86 are gathered in Table 11 and demonstrate that still lower levels of residual methyl salicylate can be achieved by increasing the melt temperature and screw speed. The product polycarbonate was very clear and colorless throughout the experiment giving rise to the Examples in Table 11.

TABLE 11 EFFECT OF SCREW SPEED AND MELT TEMPERATURE ON PRODUCT POLYCARBONATE EXTRUSION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, BMSC/(BPA) = 1.035, Catalyst = TBPA ONLY Vacuum @ Vents Mass Flow Melt Screw Die (in. Hg.) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 81 15 28 28 29 29 40/17.6 35 294 251 31 82 15 28 28 29 29 40/17.6 26 281 125 56 83 15 28 28 29 29 40/17.6 42 304 378 17 84 15 28 28 29 29 40/17.6 43 315 500 12 85 25 28 28 29 29 40/17.6 47 324 630  8 86 15 28 28 29 29 99/43.4 37 324 630 66 Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm) 81 255/279/272/280/281/280/285/282/280 21711/9728/2.232 298.9 82 257/280/272/279/279/280/277/278/279 21815/9760/2.235 583.7 83 255/281/275/281x4/283/281 22417/10012/2.239 165.4 84 254/281/279/282x2/280/285/284/281 22589/9487/2.381 102.5 85 252/282/283x3/280/288/283/281 22874/10196/2.243 66.2 86 248/273/274/276/279/280/286/283/281 21689/9692/2.238 40.9

Examples 87-90 further illustrate the use of the method of the invention to obtain a polycarbonate comprising methyl salicyl endgroups and a very low level of residual solvent in a single extrusion step in the context of a still higher initial molar ratio of BMSC to BPA. BMSC and BPA were equilibrated as in Example 5 to provide a solution of an oligomeric polycarbonate in methyl salicylate. The molar ratio of BMSC to BPA was 1.0375. As in Examples 38-50, a single solution of the oligomeric polycarbonate was fed to the extruder configured as in Examples 16-19. Examples 87-90 represent samples of the product polycarbonate which were collected at regular intervals over a period of about 1.5 hours. The molecular weight and level of residual methyl salicylate determined for each sample. Data for Examples 87-90 are gathered in Table 12 and demonstrate that very low levels of residual methyl salicylate can be achieved by increasing the melt temperature and screw speed. The lower molecular weight of the product polycarbonate reflects the higher level of BMSC employed. The product polycarbonate was very clear and colorless throughout the experiment giving rise to the Examples in Table 12.

TABLE 12 EFFECT OF SCREW SPEED AND MELT TEMPERATURE ON PRODUCT POLYCARBONATE, EXTRUSION OF OLIGOMERIC POLYCARBONATE IN METHYL SALICYLATE, BMSC/(BPA) = 1.0375, Catalyst = TBPA ONLY Vacuum @ Vents Mass Flow Melt Screw Die (in. Hg.) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 87 15 28 28 29 29 40/17.6 15 276 125 TLTM* 88 17 28 28 29 29 40/17.6 25 282 250 TLTM  89 20 28 28 29 29 40/17.6 30 290 374 TLTM  90 21 28 28 29 29 40/17.6 33 297 501 TLTM  Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm) 87 259/269/266/279/280x2/282/280/266 16233/7385/2.198 588 88 253/281/277/280x5/265 16500/7706/2.141 262 89 250/280/281x3/280/282/281/265 17008/7182/2.368 93.1 90 249/280/281x3/280/283/281/265 17149/7773/2.206 59.1 *TLTM = too low to measure.

Examples 91-94 illustrate the preparation of copolycarbonates using the method of the present invention. The copolycarbonates are characterized as having a high level of methyl salicyl endgroups, very low Fries group concentrations, and a low level of residual solvent. The solution of oligomeric copolycarbonate employed in Examples 91-93 was prepared as follows. A mixture of hydroquinone (0.2 moles HQ per 0.8 mole BPA), BPA and BMSC (1.02 moles BMSC per 0.8 mole of BPA) was equilibrated as in Example 5. TBPA (2.5×10−4 moles TBPA per 0.8 mole BPA) was used as the catalyst to provide a solution of an oligomeric copolycarbonate in methyl salicylate. The molar ratio of BMSC to BPA+HQ was 1.02. The solution of oligomeric polycarbonate used in Example 94 was prepared as follows. A mixture of hydroquinone (0.35 moles HQ per 0.65 mole BPA), BPA and was equilibrated as in Example 5. TBPA (2.5×10−4 moles TBPA per 0.65 mole BPA) was used as the catalyst to provide a solution of an oligomeric copolycarbonate in methyl salicylate. The molar ratio of BMSC to BPA+HQ was 1.015. The two solutions were fed sequentially to an extruder configured as in Examples 16-19. Examples 91-94 represent samples of the product copolycarbonate which were collected at regular intervals over a period of about 1.5 hours. The molecular weight and level of residual methyl salicylate were determined for each sample. Data for Examples 91-94 are gathered in Table 13 and demonstrate the formation of copolycarbonates using the method of the present invention. The product copolycarbonates were clear but had a slightly yellow color.

TABLE 13 COPOLYCARBONATES OF BPA & HQ BMSC/(BPA + HQ) = 1.02 (EXAMPLES 91-93), AND 1.015 (EXAMPLE 94), Catalyst = TBPA ONLY Vacuum @ Vents Mass Flow Melt Screw Die (in. Hg.) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 91 15 28 28 29 29 40/17.6 52 296 127 447 92 15 28 28 29 29 50/22.0 53 315 250 356 93 15 28 28 29 29 50/22.0 51 329 375 254 94 21 28 28 29 29 40/17.6 57 316 298 325 Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm) 91 229/282/272/280/279/280/278/278/280 30355/13295/2.283 1241.5 92 234/280/272/280x3/281/282/281 30242/13320/2.270 1076 93 244/280/273/281x3/283x2/281 30429/13338/2.281 1048.6 94 250/280/276/280x3/281/278/279 30156/13012/2.318 761.1

Examples 95-97 illustrate the use of the method of the present invention for the preparation of copolycarbonates containing about 30 mole percent polycarbonate repeat units are derived from biphenol (BP=4,4′-dihydroxybiphenyl) and about 70 mole percent are derived from bisphenol A (BPA). The solution of oligomeric copolycarbonate employed in Examples 95-97 was prepared as follows. A mixture of biphenol (0.3 moles BP per 0.7 mole BPA), BPA and BMSC (1.015 moles BMSC per 0.7 mole of BPA) was equilibrated as in Example 5. TBPA (2.5×10−4 moles TBPA per 0.7 mole BPA) was used as the catalyst to provide a solution of an oligomeric copolycarbonate in methyl salicylate. The molar ratio of BMSC to the total number of moles of BPA+HQ was 1.015. The solution was fed to a devolatilizing extruder configured as in Examples 16-19. Examples 95-97 represent samples of the product copolycarbonate which were collected at regular intervals over a period of about 1.5 hours. The molecular weight and level of residual methyl salicylate were determined for each sample. Data for Examples 95-97 are gathered in Table 14 and are consistent with the formation of copolycarbonates comprising both BP and BPA residues. The product copolycarbonate samples were clear and had no visible yellowness. The molecular weights observed for the copolycarbonate samples were lower than anticipated, prompting a post extrusion examination of the reaction vessel in which the initial equilibration of monomers was conducted. It was observed that some of the biphenol, a relatively insoluble dihydroxy aromatic compound, did not dissolve during the equilibration reaction. This effectively gave a molar ratio of BMSC to the combined number of moles of BP and BPA which was higher than 1.015. The molecular weights observed for the product polycarbonates are more consistent with a molar ratio of BMSC to BP+BPA of about 1.037. (See for example, the data provided in Table 12 for the preparation of bisphenol A polycarbonate in which the molar ratio of BMSC to BPA was 1.0375.)

TABLE 14 COPOLYCARBONATES: 70% BPA & 30% BIPHENOL (BP) BMSC/(BPA + BP) = 1.015. Catalyst = TBPA ONLY Vacuum @ Vents Mass Flow Melt Screw Die (in. Hg.) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi) 95 24 28 28 29 29 40/17.6 45 302 350 106  96 24 28 28 29 29 40/17.6 44 302 350 94 97 26 28 28 29 29 40/17.6 42 300 401 40 Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm) 95 256/305/284/282/281/280/283/281/265 19691/9264/2.125 1835 96 261/302/290/280x3/281/280/265 19415/9031/2.150 2004 97 263/300/290/280x5/265 17867/8486/2.105 1942

Examples 98-101 illustrate the use of the method of the present invention for the preparation of copolycarbonates containing polycarbonate repeat units derived from 4,4′-sulfonyldiphenol (BPS) and bisphenol A (BPA). The solution of oligomeric copolycarbonate employed in Examples 98-99 was prepared as follows. A mixture of 4,4′-sulfonyldiphenol (0.2 moles BPS per 0.8 mole BPA), BPA and BMSC (1.02 moles BMSC per 0.8 mole of BPA) was equilibrated as in Example 5. TBPA (2.5×10−4 moles TBPA per 0.8 mole BPA) was used as the catalyst to provide a solution of an oligomeric copolycarbonate in methyl salicylate. The molar ratio of BMSC to BPA+BPS was 1.02. The solution of oligomeric polycarbonate used in Examples 100-101 was prepared as follows. A mixture of BPS (0.40 moles BPS per 0.60 mole BPA), BPA and BMSC (1.022 moles BMSC per 0.6 mole of BPA) was equilibrated as in Example 5. TBPA (2.5×10−4 moles TBPA per 0.60 mole BPA) was used as the catalyst to provide a solution of an oligomeric copolycarbonate in methyl salicylate. The molar ratio of BMSC to BPA+BPS was 1.022. The two solutions were fed sequentially to an extruder configured as in Examples 16-19. Examples 98-101 represent samples of the product copolycarbonate which were collected at regular intervals over a total time period of about 3.0 hours. The molecular weight and level of residual methyl salicylate were determined for each sample. Data for Examples 9 8-101 are gathered in Table 15 and are consistent with the formation of copolycarbonate comprising both BPA and BPS derived repeat units using the method of the present invention.

TABLE 15 COPOLYCARBONATES: 20% and 40% 4,4′-SULFONYLDIPHENOL (BPS) BMSC/(BPA + BPS) = 1.02-1.022, Catalyst = TBPA ONLY Vacuum @ Vents Mass Flow Melt Screw Die (in. Hg.) Rate Torque Temperature speed Pressure Example V1 V3 V4 V5 V6 (rpm)/(lb/hr) (%) (° C.) (rpm) (psi)  98 15 28 28 29 29 40/17.6 80 324 200 744  99 15 28 28 29 29 40/17.6 79 323 200 690 100 16 28 28 29 29 35/15.4 76 334 225 615 101 17 28 28 29 29 35/15.4 80 330 201 694 Molecular Weight Residual MS Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI (ppm)  98 246/280/279/280x3/273/280x2 37069/15446/2.40 556  99 251/280x5/281/280/280 37031/15227/2.43 522 100 249/281/280/281x2/280/286/281/281 39014/13708/2.85 578 101 252/280x8 38194/13843/2.76 563

Example 102

A solution of oligomeric polycarbonate is prepared as in Example 5 and is heated to a temperature of about 160° C. in a feed tank under a nitrogen atmosphere (50-60 psig N2). Nitrogen is used to provide enough pressure to feed the pump head of a gear pump in communication with the feed tank by means of heated transfer lines. Additionally, the polymer-solvent mixture further comprises the commercial stabilizers IRGAFOS 168 (about 0.12 percent by weight based on the weight of the oligomeric polycarbonate) and IRGANOX 1010 (about 0.10 percent by weight based on the weight of the oligomeric polycarbonate). The solution is transferred from the heated feed tank by means of the gear pump at a rate of about 30 pounds of solution per hour to a heat exchanger maintained at about 265° C. The solution emerges from the heat exchanger at a temperature of about 240° C. and is then fed through a pressure control valve plumbed into the upstream edge of barrel 3 of a 10-barrel, 25 mm diameter, co-rotating, intermeshing twin-screw extruder having a length to diameter ratio (LID) of about 56. The cracking pressure of the pressure release valve is electronically controlled such that a steady stream of the superheated solution of the oligomeric polycarbonate is introduced into the extruder, the heated zones of which are maintained at a temperatures in a range between about 260° C. and about 290° C. The feed rate to the extruder is about 30 pounds per hour. The transfer lines between the heat exchanger and the pressure control valve are heated such that the temperature of the solution as it is introduced into the extruder through the pressure control valve is about 20° C. higher than the boiling point of methyl salicylate (boiling point 221° C.). The extruder is operated at a screw speed of about 460 rpm. The extruder is further equipped at barrel two with a side feeder positioned orthogonal to the barrel of the extruder. The side feeder is not heated, has an L/D of about 10, and comprises two screws consisting of forward conveying elements only. At the end most distant from the extruder barrel, the side feeder is equipped with a single atmospheric vent (V1). The conveying elements of the screws of the side feeder are configured to convey toward the extruder and away from the side feeder vent. The extruder is further equipped with two additional atmospheric vents at barrel 1 (V2) and barrel 4 (V3) and vacuum vents (vents operated at subatmospheric pressure) at barrel 6 (V4) and barrel 8 (V5). The three atmospheric vents, two on the extruder and one of the side feeder, are each connected to a solvent removal and recovery manifold comprising solvent vapor removal lines, a condenser and liquid solvent receiving vessel. The vacuum vents are similarly adapted for solvent recovery. Recovered ester substituted phenol may be purified by distillation or other means and recycled to prepare additional ester substituted diaryl carbonate. The extruder screw elements consist of both conveying elements and kneading elements. All of the conveying elements in both the extruder and the side feeder are forward flighted conveying elements. Kneading elements include neutral, forward flighted and rearward flighted kneading elements depending on functions. In barrels 2 and 3 of the extruder, kneading blocks consisting of forward and neutral flighted kneading elements are employed. The extruder screws are equipped with melt seals consisting of kneading blocks made up of rearward flighted kneading elements. The melt seals are located at barrels 5, and 7. The vacuum vents are located downstream of the melt seals on barrel 6 and barrel 8 and are operated at vacuum levels of about 28 inches of mercury (a vacuum gauge indicating full vacuum, or zero absolute pressure, would read about 30 inches of mercury). The product polycarbonate which emerges from the die face (melt temperature about 325° C.) of the extruder is stranded and pelletized. The pelletized product polycarbonate is found to have a weight average molecular weight, Mw, in excess of about 20000 daltons (GPC analysis) and to contain less than about 1 percent by weight residual ester substituted phenol. The product polycarbonate has a high level of endcapping and contains less than about 100 ppm Fries product.

General Procedure for Examples 103-181

A 30-gallon titanium reactor was used to melt the monomers, to mix the molten monomers with the catalyst and to pre-react (equilibrate) the monomers in the presence of the catalyst to form a solution comprising oligomeric polycarbonate dissolved in methyl salicylate. The heat needed for the melting of the monomers and the heating of the resulting solution to the desired temperature was provided by a stream of heating oil heated to about 210° C. which could be circulated inside the heating jacket of the reactor. The reactor could be pressurized to about 80 psi of absolute pressure with nitrogen gas. The reactor was also adapted for operation under vacuum, for use in those cases where a portion of the methyl salicylate by-product produced in the equilibration reaction was removed from the solution prior to its introduction into the devolatilizing extruder. The reaction vessel was connected to a shell-and-tube condenser attached to a receiver and vacuum outlet. Methyl salicylate distilled from, the reaction vessel was collected in the receiver. The receiver was mounted on a sensitive scale that monitored and measured the amount of methyl salicylate removed from the reactor in those instances when stripping was performed. A high power agitator inside the reactor was used to homogenize the initial reactive mixture of monomers and catalyst. The agitator could also be used to mix in additional monomers and catalyst during the operation of the process. Efficient mixing was found to be advantageous in experiments in which an inorganic filter, such as fumed silica or nanoclays was to be incorporated into the product polycarbonate. The agitator provided a uniform dispersion of the inorganic filler in the solution of the bligomeric polycarbonate in methyl salicylate prior to its introduction into the extruder and conversion to high molecular weight polycarbonate comprising the inorganic filler. A positive displacement, gear-type, pump, connected to the bottom of the reactor was used to transfer the solution of oligomeric polycarbonate in methyl salicylate from the reactor to the extruder at the desired rate. In some instances a 10-foot long, double-tube heat exchanger was inserted between the pump and the extruder in order to control the temperature of the solution of oligomeric polycarbonate. Typically, the temperature of the solution introduced into the extruder was between about 170° C. and 250° C. A pressure control valve (RESEARCH pressure control valve available from Badger Meter Inc.), hard-plumbed to the extruder at barrel No. 1, was located immediately downstream of the heat exchanger. The pressure control valve was used to isolate the extruder from the feed delivery system. The feed delivery system and the extruder were typically operated at different pressures. Thus, the feed delivery system on the upstream side of the pressure control valve was typically operated at a positive pressure while the pressure in the feed inlet zone of the extruder was typically below atmospheric pressure. The “set” or “cracking” pressure of the valve could be adjusted based on the discharge temperature of the solution exiting the heat exchanger, with higher solution temperatures typically requiring higher set pressures to control the rate of methyl salicylate flash evaporation as the solution of oligomeric polycarbonate encountered the feed inlet zone of the extruder. The extruder was a ZSK 25 mm co-rotating, intermeshing twin-screw extruder having 14 barrels and a length to diameter ratio (L/D) of about 56. The extruder was equipped with six vent ports, V1-V6 which could be operated at different levels of vacuum in order to remove the substantial amounts of the methyl salicylate solvent present in each solution of oligomeric polycarbonate employed. The absolute pressure at these vent ports was adjusted to balance devolatilization efficiency with the possibility of foaming of the solution due to the sudden vaporization of the solvent. Vent ports V1 and V2 were operated under slight vacuum whereas vent ports V3-V6 were operated under full vacuum. Vent ports V1-V6 were located along the length of the extruder at barrel 4 (V1), barrel 5 (V2), barrel 7 (V3), barrel 9 (V4), barrel 11 (V5), and barrel 13 (V6) respectively. The screw configuration used is shown in FIG. 2.

In Examples 103-105 the catalyst, tetrabutylphosphonium acetate (TBPA) was used in an amount corresponding to about 2.5×10−4 moles of catalyst per mole of bisphenol A employed. A mixture of BMSC (1.02 mole per mole BPA), BPA and catalyst was charged to the reactor and heated to a temperature of about 180° C. for a period of about 1 hour to achieve a homogeneous solution in methyl salicylate of an oligomeric BPA polycarbonate comprising methyl salicyl endgroups corresponding to structure II. The solution was about 55 percent by weight methyl salicylate. The solution was transferred using a gear pump through a heat exchanger and pressure control valve into the inlet zone of the devolatilizing extruder. The solution which emerged from the heat exchanger had a temperature about 9 to 16 degrees higher than the temperature of the solution in the reactor. Extruder vent port pressures, rate of introduction of the solution into the extruder (See “Mass Flow Rate (lb/hr)” Table 16) and other operating conditions are given in Table 16. The vent port pressure for vent 2 (V2) (not shown) was identical to that of V1. The column heading “Die P (psi)” indicates the pressure measured at the extruder die face.

TABLE 16 BISPHENOL A HOMOPOLYCARBONATES: BMSC/BPA = 1.02, Catalyst = TBPA ONLY Vacuum @ Vents Mass Screw T feed in T feed (in. Hg.) Flow Rate Torque Melt speed Die P Reactor before Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) P. Value (° C.) 103 13 28 28 29 29 25 56 304 194 283 179 188 104 13 25 28 29 29 25 54 301 179 298 179 188 105 16 28 28 29 29 20 58 300 150 285 176 192 Residual BPA Salicyl Actual Barrel MS OH OH % Example Temperature (° C.) Mw/Mn (ppm)1 (ppm)1 (ppm)1 Endcap 103 251/281/280x6/281 29669/13122 1133 88 21 96 104 254/280x5/278/279/280 29896/13239 1176 105  30 95 105 251/281x2/280x3/279x2/280 31597/13912  851 82 27 96 1Determined by 31P-NMR

The data for Examples 103-105 indicate that the high molecular weight polycarbonate was achieved under the extruder conditions selected. Moreover, residual methyl salicylate (MS) solvent levels (See “Residual MS (ppm)” in Table 16) in the product polycarbonate samples are low. The product polycarbonate is highly (95 to 96%) endcapped (See “% Endcap” in Table 16). From hydroxyl groups present in the product polycarbonate were shown by 31P-NMR to be attached to terminal bisphenol A groups (See “BPA OH (ppm)” and terminal salicyl groups (i.e. groups having structure IX) (See “Salicyl OH (ppm) in Table 16).

Examples 106-109 were carried out as in Examples 103-105 with the exception that the catalyst employed was a combination of 2.5×10−4 moles of tetramethylammonium hydroxide (TMAH) and 1×10−6 moles of sodium hydroxide per mole of BPA employed. Data for the extruder conditions employed and product polycarbonate properties is given in Table 17 below. The data in Table 17 demonstrate that high molecular weight BPA polycarbonate comprising methyl salicyl terminal groups II may be achieved under the extruder conditions selected using a combination of TMAH and sodium hydroxide as the transesterification catalyst.

TABLE 17 BISPHENOL A HOMOPOLYCARBONATES: BMSC/BPA = 1.02, Catalyst = TMAH and NaOH Solution Vacuum @ Vents Mass Screw T feed in T feed (in. Hg.) Flow Rate Torque Melt speed Die P Reactor before Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) P. Value (° C.) 106 16 28 28 29 29 20 69 303 130 564 180 182 107 16 28 28 29 29 20 73 309 130 702 182 182 108 17 28 28 29 29 20 74 310 130 781 175 181 109 17 28 28 29 29 20 77 311 130 770 172 179 Actual Barrel Example Temperatures (° C.) Mw/Mn/PDI Residual MS (ppm)1 106 255/280x8 31481/13033/2.415  980 107 257/280x8 33766/14490/2.330  922 108 258/280x8 34787/15086/2.306 1066 109 259/281/280x7 34875/14052/2.482 1063 1Determined by GPC

Examples 110-112 were carried out on an extruder configured as in Examples 103-105 and illustrate the use of the method of the present invention to prepare copolycarbonates. The starting monomers; BPA, hydroquinone (HQ), and BMSC were charged to the reactor together with the transesterification catalyst tetrabutylphosphonium acetate TBPA, 1.0×10−4 mole per mole BPA and HQ combined). The mixture was heated and stirred under a nitrogen atmosphere for about 1 hour at about 195° C. to produce a solution of an oligomeric polycarbonate comprising BPA structural units, HQ structural units, and methyl salicyl endgroups having structure II. The molar ratio of hydroquinone to total bisphenol (moles BPA+HQ combined) was about 0.4 and the ratio of moles BMSC to the moles of BPA and HQ combined was about 1.015. The polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography.

TABLE 18 BISPHENOL A-HYDROQUINONE COPOLYCARBONATES: BMSC/(BPA + HQ) = 1.015, Catalyst = TBPA ONLY, HQ/(HQ + BPA) = 0.40 Solution Vacuum @ Vents Mass Screw T feed in T feed (in. Hg.) Flow Rate Torque Melt speed Die P Reactor before Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) P. Value (° C.) 110 20 28 28 29 29 20 40 303 201 89 195 203 111 20 28 28 29 29 20 32 298 201 140  195 203 112 20 28 28 29 29 20 22 292 202 89 194 203 Residual BPA HQ Salicyl Actual Barrel MS OH OH OH % Example Temperature (° C.) Mw/Mn (ppm)1 (ppm)2 (ppm)2 (ppm)2 Endcap 110 266/280x5/283/280x2 25978/11411 1624.8 364 268 157 73 111 264/280x5/279/279/280 22091/9666 1987.5 499 353 258 68 112 262/280x8 19071/18033 1590.8 673 441 384 65 1Determined by GPC 2Determined by 31P-NMR

Examples 113-115 were carried out on an extruder configured as in Examples 103-105 and illustrate the use of the method of the present invention to prepare copolycarbonates comprising structural units derived from methylhydroquinone and BPA. The starting monomers; BPA, methylhydroquinone (MeHQ), and BMSC were charged to the reactor together with the transesterification catalyst tetrabutylphosphonium acetate (TBPA, 1.0×10−4 mole per mole BPA and MeHQ combined). The mixture was heated to between about 175 and about 190° C. and stirred under a nitrogen atmosphere for about 1 hour to produce a solution of an oligomeric polycarbonate comprising BPA structural units, MeHQ structural units, and methyl salicyl endgroups having structure II. The molar ratio of methylhydroquinone to total bisphenol (BPA+MeHQ) was about 0.9 and the ratio of moles BMSC to the moles of BPA and MeHQ combined was about 1.02. The transparent, slightly darkened polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography.

TABLE 19 BPA-METHYLHYDROQUINONE COPOLYCARBONATES: BMSC/(BPA + MeHQ) = 1.02, Catalyst = TBPA, MeHQ/(BPA + MeHQ) = 0.9 Solution Vacuum @ Vents Mass Screw T feed in T feed (in. Hg.) Flow Rate Torque Melt speed Reactor before Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (° C.) P. Value (° C.) 113 25 28 28 29 29 20 36 294 201 188 179 114 25 28 28 29 29 20 36 295 201 184 194 115 28 28 28 29 29 20 40 300 251 173 190 Example Actual Barrel Temperatures (C.) Mw/Mn/PDI Residual MS (ppm)1 113 252/280x5/284/280x2 24818/10530/2.357 1525 114 251/280x5/279/280x2 26949/11385/2.367 1466 115 250/280x2/281/280x2/281x2/280 29145/11871/2.455 1078 1Determined by GPC

Examples 116-117 were carried out on an extruder configured as in Examples 103-105 and illustrate the use of the method of the present invention to prepare copolycarbonates comprising structural units derived from methylhydroquinone and BPA. The starting monomers; BPA, methylhydroquinone (MeHQ), and BMSC were charged to the reactor together with the transesterification catalyst tetramethylammonium hydroxide (TMAH, 2.5×10−4 mole per mole BPA and MeHQ combined) and sodium hydroxide (NaOH, 1×10−6 moles NaOH per mole BPA and MeHQ combined). The mixture was heated to about 185° C. and stirred under a nitrogen atmosphere for about 1 hour to produce a solution of an oligomeric polycarbonate comprising BPA structural units, MeHQ structural units, and methyl salicyl endgroups having structure II. The molar ratio of methylhydroquinone to total bisphenol (moles BPA+MeHQ) was about 0.8 and the ratio of moles BMSC to the moles of BPA and MeHQ combined was about 1.015. The transparent, slightly pinkish polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography.

TABLE 20 BPA-MeHQ COPOLYCARBONATES: BMSC/(BPA + MeHQ) = 1.015, Catalyst = TMAH-NaOH, MeHQ/(BPA + MEHQ) = 0.8 Solution Vacuum @ Vents Mass Screw T feed in T feed (in. Hg.) Flow Rate Torque Melt speed Die P Reactor before Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) P. Value (° C.) 116 20 28 28 29 29 20 57 303 145  66 186 187 117 21 28 28 29 29 25 44 303 177 122 183 184 Example Actual Barrel Temperatures (C.) Mw/Mn/PDI Residual MS (ppm)1 116 246/280/281x2/280x2/286/281x2 45341/19373/2.340 571 117 243/280x5/279/280x2 33964/15199/2.235 1203.8 1Determined by GPC

Examples 118-120 were carried out on an extruder configured as in Examples 103-105 and illustrate the use of the method of the present invention to prepare copolycarbonates comprising structural units derived from hydroquinone and BPA. The starting monomers, BPA, hydroquinone (HQ), and BMSC were charged to the reactor together with the transesterification catalyst tetramethylammonium hydroxide (TMAH, 2.5×10−4 mole per mole BPA and HQ combined) and sodium hydroxide (NaOH, 2×10−6 moles NaOH per mole BPA and HQ combined). The mixture was heated to about 175° C. and stirred under a nitrogen atmosphere for about 1 hour to produce a solution of an oligomeric polycarbonate comprising BPA structural units, HQ structural units, and methyl salicyl endgroups having structure II. The molar ratio of hydroquinone to BPA was about 2 to 8 and the ratio of moles BMSC to the moles of BPA and HQ combined was about 1.024. The transparent, water-white polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography. In Table 21 the abbreviation “TLTM” means “too low to measure”.

TABLE 21 BISPHENOL A-HYDROQUINONE COPOLYCARBONATES: BMSC/(BPA + HQ) = 1.024, Catalyst = TMAH-NaOH, HQ/(BPA + HQ) = 0.2 Solution Vacuum @ Vents Mass Screw T feed in T feed (in. Hg.) Flow Rate Torque Melt speed Die P Reactor before Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) P. Value (° C.) 118 19 28 26 29 29 20 74 310 177 TLTM 174 174 119 19 28 26 29 29 20 74 311 177 TLTM 173 174 120 19 28 26 29 29 20 73 311 177 TLTM 174 174 Residual BPA HQ Salicyl Actual Barrel MS OH OH OH % Example Temperatures (° C.) Mw/Mn (ppm)1 (ppm)1 (ppm)1 (ppm)1 Endcap 118 244/280x8 35511, 15855 423 48 13 13 97 119 244/280x7/281 37028, 16257 454 55 17 13 96 120 244/280x7/281 37684, 16480 451 73 20 24 94 1Determined by 31P-NMR

The product copolycarbonate of Example 118 was further characterized by proton and 13C-NMR and shown thereby to comprise about 0.8 mole percent
(relative to BPA derived repeat units) repeat units having structure XII wherein methyl salicylate has been fully incorporated into the backbone of the polycarbonate chain. In addition, these NMR studies revealed the presence of methyl carbonate terminal groups XIII
in the product copolycarbonate of Example 118 in an amount corresponding to about 0.93 mole percent relative to BPA derived repeat units (i.e. 0.93 mmole of structural unit XIII per 100 moles of BPA derived repeat units). Finally, these NMR studies on the product copolycarbonate of Example 118 revealed presence of methyl ether terminal groups having structure XIV in an amount corresponding to about 0.39 moles per 100 moles
of bisphenol A derived repeat units (i.e. 0.39 mole percent relative to all BPA derived repeat units present in the product copolycarbonate).

Examples 119-121 were carried out on an extruder configured as in Examples 103-105 and illustrate the use of the method of the present invention to prepare polycarbonate terpolymers comprising structural units derived from hydroquinone, methylhydroquinone and BPA. The starting monomers; BPA, hydroquinone (HQ), methylhydroquinone (MeHQ), and BMSC were charged to the reactor together with the transesterification catalyst tetramethylammonium hydroxy (TMAH, 2.5×10−4 mole per mole BPA, HQ and MeHQ combined) and sodium hydroxide (NaOH, 1×10−6 moles NaOH per mole BPA, HQ and MeHQ combined). The mixture was heated to about 195° C. and stirred under a nitrogen atmosphere for about 1 hour to produce a solution of an oligomeric polycarbonate comprising BPA structural units, HQ structural units, MeHQ structural units, and methyl salicyl endgroups having structure II. The mixture of bisphenols employed comprised about 40 mole percent BPA, 40 mole percent HQ and 20 mole percent MeHQ. The ratio of moles BMSC to the moles of BPA, HQ and MeHQ combined was about 1.015 (i.e. moles BMSC/(moles BPA+moles HQ+moles MeHQ)=1.015). The transparent, lightly colored polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography.

TABLE 22 POLYCARBONATE TERPOLYMERS COMPRISING 40% BPA, 40% HQ, AND 20% MeHQ: BMSC/(BPA + HQ + MeHQ) = 1.015, Cat. = TMAH-NaOH Solution Vacuum @ Vents Mass Flow Screw T feed in T feed (in. Hg.) Rate Torque Melt speed Die P Reactor before Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) P. Valve (° C.) 119 22 28 28 29 29 20 27 290 181 22 195 198 120 18 25 27 29 29 20 18 288 270 13 195 194 121 25 28 28 29 29 18 16 285 213 10 192 198 Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI Residual MS (ppm)1 119 249/279/280x4/292/280x2 21054/8675/2.427 996 120 248/280x3/279/280/279x2/280 17495/7187/2.434 804 121 252/280x5/279/280x2 15809/6405/2.468 771 1Determined by GPC

Examples 122-124 were carried out on an extruder configured as in Examples 103-105 and illustrate the use of the method of the present invention to prepare polycarbonate terpolymers comprising structural units derived from biphenol, methylhydroquinone and BPA. The starting monomers; biphenol (BP), methylhydroquinone (MeHQ), bisphenol A (BPA), and BMSC were charged to the reactor together with the transesterification catalyst tetramethylammonium hydroxide (TMAH, 2.5×10−4 mole per mole BP, MeHQ and BPA combined) and sodium hydroxide (NaOH, 2.0×10−6 moles NaOH per mole BP, MeHQ and BPA combined). The mixture was heated to about 170° C. and stirred under a nitrogen atmosphere for about 1 hour to produce a solution of an oligomeric polycarbonate comprising BP structural units, MeHQ structural units, BPA structural units, and methyl salicyl endgroups having structure II. The oligomeric polycarbonate fed to the extruder was characterized by GPC (Mw=5584, and Mn=2115). The mixture of bisphenols employed comprised about 33 mole percent BP, about 33 mole percent MeHQ, and about 33 mole percent BPA. The ratio of moles BMSC to the moles of BP, MeHQ and BPA combined was about 1.028 (i.e. moles BMSC/(moles BP+moles MeHQ+moles BPA)=1.028). The solution introduced into the extruder was about 59 percent by weight methyl salicylate. The transparent, lightly colored polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography.

TABLE 23 POLYCARBONATE TERPOLYMERS COMPRISING 33% BP, 33% MeHQ, AND 33% BPA; BMSC/(BP + MeHQ + BPA) = 1.028; Cat. = TMAH-NaOH Solution T feed Vacuum @ Vents Mass Flow Screw T feed before (in. Hg.) Rate Torque Melt speed Die P in Reactor P. Valve Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi)1 (° C.) (° C.) 122 17 28 25 29 29 20 57 300 145 TLTM 173 174 123 22 28 25 29 29 20 61 301 145 TLTM 172 174 124 22 28 25 29 29 20 54 301 145 TLTM 172 174 Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI Residual MS (ppm)2 122 252/280/272/280x3/279/280/290 29202/13381/2.182 605.1 123 251/280/273/280x5/290 29555/13410/2.204 657 124 250/280/272/280x5/290 30183/13445/2.245 726 1“TLTM” indicates die pressure was “too low to measure”, 2Determined by GPC

Examples 125-127 were carried out on an extruder configured as in Examples 103-105 and illustrate the use of the method of the present invention to prepare polycarbonate terpolymers comprising structural units derived from resorcinol, hydroquinone and BPA. The starting monomers, resorcinol (RS), hydroquinone (HQ), bisphenol A (BPA), and BMSC were charged to the reactor together with the transesterification catalyst tetramethylammonium hydroxide. (TMAH, 2.5×10−4 mole per mole RS, HQ and BPA combined) and sodium hydroxide (NaOH, 2.0×10−6 moles NaOH per mole RS, HQ and BPA combined). The mixture was heated to about 165° C. and stirred under a nitrogen atmosphere for about 1 hour to produce a solution of an oligomeric polycarbonate comprising RS structural units, HQ structural units, BPA structural units, and methyl salicyl endgroups having structure II. The oligomeric polycarbonate was characterized by GPC (Mw=1778, and Mn=645). The mixture of bisphenols employed comprised about 33 mole percent RS, about 33 mole percent HQ, and about 33 mole percent BPA. The ratio of moles BMSC to the moles of RS, HQ and BPA combined was about 1.02 (i.e. moles BMSC/(moles RS+moles HQ+moles BPA)=1.02). The solution introduced into the extruder was about 61 percent by weight methyl salicylate. The transparent, slightly orange copolycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography.

TABLE 24 POLYCARBONATE TERPOLYMERS COMPRISING 33% RS, 33% HQ, AND 33% BPA; BMSC/(RS + HQ + BPA) = 1.02; Cat. = TMAH-NaOH Solution T feed Vacuum @ Vents Mass Flow Screw T feed before (in. Hg.) Rate Torque Melt speed Die P in Reactor P. Valve Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi)1 (° C.) (° C.) 125 21 29 29 29 29 20 39 298 175 TLTM 168 171 126 22 29 29 29 29 20 44 298 175 TLTM 168 173 127 22 29 29 29 29 20 40 299 175 TLTM 163 175 Example Actual Barrel Temperatures (° C.) Mw/Mn/PDI Residual MS (ppm)2 125 246/277/267/280x3/284/281/280 30160/13521/2.231 417 126 241/280/268/280x6 27410/12202/2.246 319 127 241/280/268/280x5/279 29787/13423/2.219 1164  1“TLTM” indicates die pressure was “too low to measure”. 2Determined by GPC

Examples 128-130 were carried out on an extruder configured as in Examples 103-105 and illustrate the use of the method of the present invention to prepare branched copolycarbonates comprising structural units derived from biphenol, and BPA. The starting monomers, bisphenol (BP), bisphenol A (BPA), BMSC and branching agent 1,1,1,-tris (4-hydroxyphenol)ethane (THPE) were charged to the reactor together with the transesterification catalyst tetramethylammonium hydroxide (TMAH, 2.5×10−4 mole per mole BP and BPA combined) and sodium hydroxide (NaOH, 2.0×10−6 moles NaOH per mole BP and BPA combined). The mixture was heated to about 180° C. and stirred under a nitrogen atmosphere for about 1 hour to produce a solution of a branched oligomeric polycarbonate comprising BP structural units, BPA structural units, THPE structural units, and methyl salicyl endgroups having structure II. The mixture of bisphenols employed comprised about 40 mole percent BP, and about 60 mole percent BPA. The ratio of THPE to total bisphenols was about 0.0025 (i.e. mole THPE/(moles BP+moles BPA)=0.0025). The ratio of moles BMSC to the moles of BP and BPA combined was about 1.03 (i.e. moles BMSC/(moles BP+moles BPA)=1.03). During the experiment the pressure on the upstream side of the pressure control valve was about 20 psi. The transparent, slightly colored, branched copolycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography.

TABLE 25 BRANCHED BISPHENOL A-BIPHENOL COPOLYCARBONATES BMSC/(BPA + BP) = 1.03; Catalyst = TMAH-NaOH, 60% BPA, 40% BP Solution T feed Vacuum @ Vents Mass Flow Screw T feed before (in. Hg.) Rate Torque Melt speed Die P in Reactor P. Valve Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) (° C.) 128 19 28 28 29 29 20 49 304 200 TLTM 180 185 129 19 28 28 29 29 20 47 301 176 TLTM 179 186 130 20 28 28 29 29 20 47 302 176 TLTM 176 186 Residual BP/MS BPA Salicyl Actual Barrel MS OH OH OH % Example Temperatures (° C.) Mw/Mn (ppm)1 (ppm)2 (ppm)2 (ppm)2 Endcap 128 253/280x6/281/290 23636/10760 562 70 15 3 99 129 251/280x5/279/280/290 23551/10674 646 83 19 3 99 130 251/280x7/290 23588/10533 693 92 21 3 99 1Determined by GPC 2Determined by 31P-NMR

The polycarbonate samples of Examples 128-130 were characterized by 31P-NMR following derivatization with 2-chloro-1,3,2-dioxaphospholane. The column headings “BP/MS OH (ppm)” refers to the combined amount in parts per million of OH groups attributable to residual methyl salicylate solvent together with OH groups attributable to biphenol OH polymer endgroups. The concentration of hydroxy groups present in the product copolycarbonate is expressed in parts “OH” group per million parts of copolycarbonate. Because the 31P signal for 1,3,2-dioxaphospholane-derivatized free methyl salicylate (MS) overlapped with the signal for the 1,3,2-dioxaphospholane derivatized biphenol endgroups the concentration of “free methyl salicylate OH” and “biphenol endgroup OH” is given as the sum of the two concentrations. The concentration of methyl salicylate itself, as opposed to the concentration of methyl salicylate OH groups, was determined independently by GPC. Similarly, the column headings “Salicyl OH (ppm)” and “BPA OH (ppm)” refers to the concentration of OH groups attributable to salicyl OH groups (See structure XI) and OH groups attached to bisphenol A endgroups expressed in parts “OH group” (Formula weight=17) per million parts product copolycarbonate.

Examples 131-135 were carried out on an extruder configured as in Examples 103-105 and illustrate the use of the method of the present invention to prepare bisphenol A polycarbonate comprising an inorganic filler, fumed silica. The starting monomers, bisphenol A (BPA), and BMSC, and treated fumed silica were charged to the reactor together with the transesterification catalyst, tetrabutyl-phosphonium acetate (TBPA, 1.5×10−4 mole per mole BPA) and sodium hydroxide (NaOH, 2.0×10−6 moles NaOH per mole BPA). The fumed silica was added in an amount calculated to produce a product polycarbonate comprising 5 percent by weight fumed silica. The mixture heated to about 190-195° C. and stirred under a nitrogen atmosphere for about 1 hour to produce a solution of a oligomeric BPA polycarbonate comprising BPA structural units and methyl salicyl endgroups having structure II, in which was suspended the fumed silica. The ratio of moles BMSC to the moles of BPA was about 1.019. During the experiment comprising Examples 131-135 the pressure on the upstream side of the pressure control valve was about 20 to 50 psi. The opaque white polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography.

TABLE 26 BPA POLYCARBONATES COMPRISING FUMED SILICA: BMSC/(BPA) = 1.019, Catalyst = TBPA and NaOH, 5% FUMED SILICA Solution T feed Vacuum @ Vents Mass Flow Screw T feed before (in. Hg.) Rate Torque Melt speed Die P in Reactor P. Valve Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) (° C.) 131 25 28 28 29 29 22 43 305 250 TLTM 192 198 132 23 28 28 29 29 22 41 306 250 14 193 198 133 23 28 28 29 29 22 41 305 250 21 192 198 134 23 28 28 29 29 22 39 304 250 23 194 198 135 22 28 28 29 29 22 37 304 250 31 193 189 Residual BPA Salicyl Actual Barrel MS OH OH % Example Temperatures (° C.) Mw/Mn (ppm)1,2 (ppm)2 (ppm)2 Endcap 131 264/280/281/280/281/280/281x3 25340/11005 13092 322 130 85 132 261/279/280x7 25967/11013 15032 352 171 83 133 261/280x8 25678/10749 31691 — — — 134 260/280x8 24402/9806 14092 438 252 80 135 261/280x8 24256/10107 19141 — — — 1Determined by GPC 2Determined by 31P-NMR

The product polycarbonates of Examples 131, 132 and 134 were further characterized by 31P-NMR following derivatization with 2-chloro-1,3,2-dioxaphospholane. Typically, analysis using 31P-NMR provides a lower value of residual methyl salicylate, “Residual MS (ppm)” than does analysis by GPC. The 31P-NMR value is typically considered to be more accurate than the value obtained using GPC. The product polycarbonates of Examples 131, 132 and 134 were further analyzed by proton and 13C-NMR. The product polycarbonate of Example 132 was shown thereby to comprise about 1.5 mole percent (relative to BPA derived repeat units) repeat units having structure XII wherein methyl salicylate has been fully incorporated into the backbone of the polycarbonate chain. The product polycarbonates of Examples 131, 132, and 134 were also shown by these NMR studies to comprise methyl carbonate terminal groups XIII in amounts corresponding to between about 0.80 and 0.85 mole percent relative to BPA derived repeat units (i.e. from about 0.80 to about 0.85 mole of structural unit XIII per 100 moles of BPA derived repeat units). Finally, these NMR studies on the product polycarbonates of Examples 131, 132 and 134 revealed the presence of methyl ether terminal groups having structure XIV in amounts corresponding to from about 0.30 to about 0.50 moles structure XIV per 100 moles of bisphenol A derived repeat units (i.e. about 0.30-0.50 mole percent relative to all BPA derived repeat units present in the product polycarbonate. Additional polymerizations were carried out in a manner identical to that employed in Examples 131-135 with the exception that less (2 percent fumed silica in the product polycarbonate) or more (10 percent fumed silica in the product polycarbonate) fumed silica was employed. The results were substantially the same as those observed for Examples 131-135.

Examples 136-143 were carried out on an extruder configured as in Examples 103-105 and illustrate the effect of feed temperature and prolonged heating on the quality of the product polycarbonate prepared using the method of the present invention. The starting monomers; bisphenol A (BPA) and BMSC were charged to the reactor together with the transesterification catalyst, tetrabutylphosphonium acetate (TBPA, 2.5×10−4 mole per mole BPA) and sodium hydroxide (NaOH, 1.0×10−6 moles NaOH per mole BPA). The mixture was heated in a range between about 180-220° C. over the course of the experiment comprised by Examples 136-143. It should be noted that the solution of oligomeric polycarbonate being transformed into the product polycarbonates of Examples 136-143 was heated for progressively longer periods of time at progressively higher temperatures over the course of the experiment. Thus, the product polycarbonate of Example 136 was exposed to much milder conditions (lower temperature and shorter heating time) than those conditions to which the product polycarbonate of Example 143 (higher temperature and longer heating time) was subjected. The solution of the oligomeric BPA polycarbonate comprising BPA structural units and methyl salicyl endgroups having structure II was stirred under a nitrogen atmosphere over the course of the experiment. The ratio of moles BMSC to the moles of BPA was about 1.02. The solution introduced into the extruder was about 55 by weight methylisalicylate. During the experiment comprising Examples 136-143 the pressure on the upstream side of the pressure control valve was about 46 psi. The polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography.

TABLE 27 EFFECT OF HEATING TIME AND TEMPERATURE ON PRODUCT BPA POLYCARBONATES BMSC/(BPA) = 1.02, Catalyst = TBPA and NaOH Solution T feed Vacuum @ Vents Mass Flow Screw T feed before (in. Hg.) Rate Torque Melt speed Die P in Reactor P. Valve Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) (° C.) 136 20 28 28 29 29 25 63 303 150 521 179 184 137 20 28 28 29 29 25 63 303 150 561 179 183 138 20 28 28 29 29 25 67 306 150 701 191 200 139 20 28 28 29 29 25 65 305 150 651 196 218 140 20 28 28 29 29 25 64 306 150 663 205 242 141 20 28 28 29 29 25 57 304 150 631 210 255 142 20 28 28 29 29 25 41 300 150 393 214 255 143 20 28 28 29 29 25 29 293 150 263 219 259 Residual BPA Salicyl MS OH OH % Example Actual Barrel Temperatures (° C.) Mw/Mn (ppm)1 (ppm)2 (ppm)2 Endcap 136 256/280x8 30065/14043 1049  76  19 96 137 256/280x5/279/280x2 30337/14010 1213 — — — 138 261/281/280x7 32273/14278 1297 — — — 139 251/280x8 35780/14787 1020  90  35 95 140 263/281/280x7 31389/14312 1015 — — — 141 265/281/280x7 30720/14112  999 — — — 142 268/281/280x4/278/279/280 29396/15083 — 150 192 85 143 269/281/280x2/279/280/277/279/280 23164/10580 1146 266 435 78 1Determined by GPC 2Determined by 31P-NMR

The product polycarbonates were found to have suffered molecular weight loss under conditions of higher temperature and longer heating time (See Examples 142 and 143). Moreover, 31P-NMR following derivatization with 2-chloro-1,3,2-dioxaphospholane revealed that the prolonged heating at the higher temperatures of Examples 142 and 143 resulted in product polycarbonates having a higher number of BPA and salicyl hydroxyl endgroups and a correspondingly lower “% Endcap”. In addition, the product polycarbonate of Example 143 was shown by 1H-NMR and 13C-NMR to comprise elevated levels of methyl carbonate terminal groups XIII (about 1.7 moles of structural unit XIII per 100 moles of BPA derived repeat units), methyl ether terminal groups having structure XIV (about 3.3 moles of structural unit XIV per 100 moles of BPA derived repeat units), and “internal” salicyl groups (repeat units having structure XII wherein methyl salicylate has been fully incorporated into the backbone of the polycarbonate chain). The “internal salicyl groups were found to be present in an amount corresponding to about 3.9 moles of repeat units XII per 100 moles of BPA derived repeat units. These data and the data presented in Table 27 indicate that structural features of the product polycarbonate prepared by the method of the present invention may be controlled by varying the temperature at which the equilibration reaction is carried out and the length of time the solution of oligomeric polycarbonate is heated prior to its introduction into the devolatilizing extruder. It is believed that additional control of product polycarbonate structural features may be exerted by judicious selection of the transesterification catalyst employed.

Examples 144-153 were carried out on an extruder configured as in Examples 103-105 and illustrate the effect of concentrating the feed solution of oligomeric polycarbonate prior to extrusion, and the effect of extruder throughput rate on the quality of the product polycarbonate prepared using the method of the present invention. The starting monomers; bisphenol A (BPA) and BMSC were charged to the reactor together with the transesterification catalyst, tetrabutylphosphonium acetate (TBPA, 2.5×10−4 mole per mole BPA) and sodium hydroxide (NaOH, 1.0×10−6 moles NaOH per mole BPA). The mixture was heated initially to about 190-195° C. to produce a solution of oligomeric polycarbonate comprising about 55 percent by weight methyl salicylate. This was fed to the extruder to establish a baseline performance (See Examples 144 and 145) after which, extrusion was interrupted and a portion of the methyl salicylate was distilled under reduced pressure from the reactor until the concentration of methyl salicylate in the solution was reduced to about 35 percent by weight. Extrusion was then recommended and the polycarbonates of Examples 146 and 147 were collected at the extruder die face. Extrusion was again discontinued and additional methyl salicylate was distilled from the reactor under reduced pressure. The resultant solution of oligomeric polycarbonate comprising methyl salicyl endgroups II had the following characteristics.

Weight % of MS Salicyl in feed BPA OH OH solution Mw Mn (ppm)1 (ppm)1 % EC Feed in 22.3 5941 2393 2546 929 76 Examples 148-153 1Determined by 31P-NMR

The effect of extruder throughput rate was determined by gradually increasing the rate at which the solution of the oligomeric polycarbonate was presented to the extruder over the course of Examples 144-153. In each of Examples 144-153 the polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography. As the throughput rate was increased the amount of residual methyl salicylate in the product polycarbonate was observed to increase. Moreover, higher throughput rates resulted in lower product polycarbonate molecular weights and lower percent endcap (“% EC”). The entire experiment comprising Examples 144-153 was carried out over the course of about six hours.

TABLE 28 EFFECT OF FEED CONCENTRATION AND THROUGHPUT RATE ON PRODUCT BPA POLYCARBONATES: BMSC/(BPA) = 1.02, Catalyst = TBPA AND NaOH Solution T feed Vacuum @ Vents Mass Flow Screw T feed before (in. Hg.) Rate Torque Melt speed Die P in Reactor P-Valve Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) (° C.) 144 12 25 28 29 29 45 52 331 350 557 193 204 145 12 25 28 29 29 30 54 316 235 562 197 215 146 20 28 28 29 29 23 59 320 236 477 218 214 147 20 28 28 29 29 34.6 50 326 351 393 220 214 148 23 28 28 29 29 18.8 46 311 233 367 215 214 149 21 28 28 29 29 28.1 43 318 350 353 216 216 150 21 28 28 29 29 35 39 323 451 311 218 216 151 20 28 28 29 29 42 35 324 550 279 218 216 152 20 28 28 29 29 50 33 329 675 244 216 217 153 20 28 28 29 29 60 30 334 800 214 215 217 Weight % of MS in Residual BPA Salicyl Ex- feed MS OH OH % ample solution Actual Barrel Temperatures (° C.) Mw/Mn (ppm)1 (ppm)1 (ppm)1 EC 144 55 252/278x2/280x3/286/282/280 29276/12666 1333 136  38 94 145 55 256/282/280x4/278x2/280 30833/13256 1379 151  44 92 146 35 272/278/280x2/281/280/288/284/282 31373/13398 1260 205 113 87 147 35 266/279/280x4/282/280/279 28495/12172 1493 289 170 84 148 22 276/278/280x2/281/280/288/284/282 26929/11515 1419 316 240 81 149 22 273/279/280x4/285/281/280 24844/10682 1851 367 264 80 150 22 272/279/280x4/283/281/280 23079/9926 2136 411 307 79 151 22 270/280x7/279 22021/9480 2597 484 341 77 152 22 269/279/280x5/281/280 21060/9068 2937 537 372 76 153 22 267/279/280x4/281x2/280 19614/8420 3433 601 411 75 1Determined by 31P-NMR

Examples 154-163 were carried out on an extruder configured as in Examples 103-105 and illustrate the stable operation of the method of the present invention using a concentrated feed solution of the oligomeric polycarbonate in methyl salicylate. Moreover, Examples 154-163 illustrate the effect of feed temperature and throughput rate on the molecular weight of the product polycarbonate. The starting monomers, bisphenol A (BPA) and BMSC were charged to the reactor together with the transesterification catalyst, tetramethyl-ammonium hydroxide (TMAH, 1.0×10−4 mole per mole BPA) and sodium hydroxide (NaOH, 2.0×10−6 moles NaOH per mole BPA). The mixture was heated initially to about 175-180° C. to produce a solution of oligomeric polycarbonate comprising about 55 percent by weight methyl salicylate. The solution was then fed to the extruder to establish a baseline performance (See Example 154) after which, extrusion was interrupted and a portion of the methyl salicylate was distilled under reduced pressure from the reactor until the concentration of methyl salicylate in the solution was reduced to about 35 percent by weight. The resultant solution of oligomeric polycarbonate comprising methyl salicyl endgroups II was sampled twice during the Experiment constituted by Examples 155 through 163 and the results compared with the solution immediately after its preparation and prior to the removal of any methyl salicylate formed during the equilibration of the starting monomers (See “Feed in Example 154”). As can be seen the molecular weight of the oligomeric polycarbonate remains reasonably stable over the course of the experiment (Compare “Feed in Example 155” with “Feed in Example 163”).

Weight % of MS in feed solution Mw Mn Feed in 56 5483 2566 Example 154 Feed in 37.2 5839 2722 Example 155 Feed in 35.5 5789 2658 Example 163

Following concentration of the feed solution, extrusion was recommended and the polycarbonates of Examples 155 to 163 were collected at the extruder die face. In each of Examples 154-163 the polycarbonate emerging from the die face was pelletized and characterized. Molecular weights were determined by gel permeation chromatography. The data in Table 29 illustrate that stable production of high quality polycarbonate may be achieved using a concentrated feed solution and illustrate the beneficial effects of lower reactor temperature. The extruder used according to the method of the present invention serves two roles; (1) the extruder effects solvent removal, and (2) the extruder functions as a polymerization reactor for the conversion of the oligomeric polycarbonate starting material into high molecular weight polycarbonate. Concentrating the solution fed to the extruder is seen as beneficial in that it allows greater leeway in apportioning these two functions.

TABLE 29 EFFECT OF CONCENTRATING THE SOLUTION OF OLIGOMERIC POLYCARBONATE ON PRODUCT BPA POLYCARBONATES: BMSC/(BPA) = 1.025, Catalyst = TMAH AND NaOH Solution T feed Vacuum @ Vents Mass Flow Screw T feed before (in. Hg.) Rate Torque Melt speed Die P in Reactor P-Valve Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (psi) (° C.) (° C.) 154 20 28 26 29 29 20 56 301 200 TLTM 176 175 155 17 28 26 29 29 15 67 309 218 TLTM 179 212 156 17 28 26 29 29 20 60 308 218 TLTM 176 208 157 17 28 26 29 29 25 62 324 357 TLTM 175 206 158 20 28 26 29 29 30 58 322 357 TLTM 174 204 159 17 28 26 29 29 35 58 328 429 TLTM 174 203 160 16 28 26 29 29 40 56 340 554 TLTM 175 202 161 17 28 25 29 29 45 54 345 626 TLTM 176 201 162 17 28 25 29 29 45 53 351 700 TLTM 178 202 163 25 28 26 29 29 15 69 305 218 TLTM 178 211 Weight % Residual of MS in MS Example feed solution Actual Barrel Temperatures (° C.) Mw/Mn (ppm)1 154 56   250/278/273/280/281/280/285/282/281 27668/12470 491 155 37.2 268/279/281x2/282/280/287/281/280 30826/13653 465 156 nd2 265/277/279x2/281/280/285/281/280 29905/13342 672 157 nd2 262/278/280x2/282/280/287/284/280 29434/13090 567 158 nd2 259/278/279/280x3/284/282/280 28690/12756 688 159 nd2 257/278/279x2/281/280/283/282/280 28214/12481 1071  160 nd2 255/278/280/279/281/280/284/285/280 28831/12815 639 161 nd2 253/279/280x4/283/284/280 28308/12609 1410  162 nd2 252/280/281/280x3/283x2/280 28540/12604 803 163 35.5 257/283/281x2/279/280/272/271/279 31133/13788 345 1Determined by 31P-NMR 2Value was not determined but was believed to correspond to between about 37.2 and 35.5 weight percent methyl salicylate. BPA OH Salicyl OH Salicyl Structure Structure Structure Example (ppm)1 (ppm)1 % EC OH2 MS2 XIII2 XIV2 XII2 154 27 12 99 0.018 0.11 0.21 0.04 155 29  5 99 0.007 0.15 0.31 0.09 156 42 13 98 0.020 0.15 0.32 0.09 157 40 13 98 0.019 0.16 0.28 0.09 0.5 158 60 19 97 0.029 0.20 0.27 0.09 159 72 20 97 0.030 0.21 0.30 0.10 0.8 160 64 19 97 0.028 0.22 0.35 0.11 161 75 21 96 0.031 0.23 0.37 0.10 0.6 162 61 15 97 0.022 0.21 0.38 0.13 163 29 11 98 0.016 0.11 0.42 0.17 1.0 1Determined by 31P-NMR, 2Expressed in moles per 100 moles of BPA-containing structural units

It is noteworthy that over time, the concentration of by-product structures XII, XIII and XIV increases in the product polycarbonate. This is strong evidence for the proposition that prolonged heating at higher temperatures is the responsible for the appearance of these by-product structures.

Examples 164-181 were carried out on an extruder configured as in Examples 103-105 and illustrate both the consistency of stable operation of the process of the present invention as well as the potential for using extruder torque and extruder melt temperature as key process control criteria when using the method of the present invention. The starting monomers, bisphenol A (BPA) and BMSC were charged to the reactor together with the transesterification catalyst, tetramethyl-ammonium hydroxide (TMAH, 2.5×10−4 mole per mole BPA). No sodium hydroxide was employed. The mixture was heated initially to about 160-165° C. to produce a solution of oligomeric polycarbonate comprising about 55 percent by weight methyl salicylate. In Examples 164-170, the molar ratio of BMSC to BPA was varied from about 1.018 to about 1.03, by addition of BMSC monomer to the equilibrated mixture of oligomers in the reactor. The molecular weights of the product polycarbonates varied accordingly. In Examples 170 to 181 the molar ratio of BMSC to BPA was held constant at 1.03. The process was run for about an hour at the BMSC to BPA molar ratio of 1.03 in order to study short-term consistency of the process. The product emerging from the extruder die face was sampled every five minutes giving a total of 12 product polycarbonate samples (Examples 170-181) which were analyzed by gel permeation chromatography. The data reveal the remarkable stability of the process of the present invention, the standard deviation of the weight average molecular weight, Mw, being less than 1 percent of the average value of Mw for Examples 170-181. The standard deviation of the residual methyl salicylate value was somewhat higher and reflects the relatively high standard deviation associated with methyl salicylate quantitation by GPC. (The standard deviation in the measurement of a chloroform solution containing 1000 ppm of methyl salicylate was about 75 ppm or about 7.5% of the average value determined.). In Table 30 the symbol “″” indicates that the value was not recorded but should not have been different significantly different from the value preceding it.

TABLE 30 PROCESS CONTROL USING MELT TEMPERATURE AND TORQUE AS KEY PROCESS CONTROL CRITERIA: CATALYST = TMAH Solution T feed Vacuum @ Vents Mass Flow Screw T feed before (in. Hg.) Rate Torque Melt speed in Reactor P-Valve Example V1 V3 V4 V5 V6 (lb/hr) (%) (° C.) (rpm) (° C.) (° C.) 164 20 29 29 29 29 20 53 313 179 163 168 165 20 29 29 29 29 20 51 310 179 162 168 166 20 29 29 29 29 20 46 306 174 163 168 167 20 29 29 29 29 20 42 304 174 164 168 168 20 29 29 29 29 20 39 301 174 164 168 169 20 29 29 29 29 20 34 299 175 162 168 170 20 29 29 29 29 20 31 297 175 163 168 171 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ 172 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ 173 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ 174 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ 175 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ 176 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ 177 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ 178 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ 179 21 29 29 29 29 20 30 296 175 163 168 180 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ 181 ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ ″ Residual BMSC/BPA MS Example Ratio Actual Barrel Temperatures (° C.) Mw/Mn/PDI2 (ppm)1,3 164 1.018 235/283/275/281/281/280/296/283/281 35893/15144/2.370 1247 165 1.02 239/281x2/280x3/286/280x2 34685/14716/2.357 1360 166 1.022 242/280x8 32795/13974/2.347 1528 167 1.024 243/280x8 30469/13134/2.320 1595 168 1.026 244/280x5/271/280x2 28457/12386/2.298 1983 169 1.028 245/280x8 26980/11774/2.291 1515 170 1.03 246/280x5/281/280x2 25535/11184/2.283 1465 171 1.03 ″ 25234/11068/2.280 1523 172 1.03 ″ 25142/11052/2.275 1545 173 1.03 ″ 25111/11033/2.276 1687 174 1.03 ″ 24891/10916/2.280 1727 175 1.03 ″ 24922/10937/2.279 1825 176 1.03 ″ 25039/10988/2.279 1759 177 1.03 ″ 25254/11048/2.286 1488 178 1.03 ″ 25449/11148/2.283 1504 179 1.03 247/280x8 25479/11133/2.289 1557 180 1.03 ″ 25301/11061/2.287 1499 181 1.03 ″ 25184/11015/2.286 1796 1Determined by GPC, 2The standard deviation of the weight average molecular weight, Mw, was 208 daltons calculated for Examples 170-181. 3The standard deviation of the residual methyl salicylate present in the product polycarbonate wads 134 ppm calculated for Examples 170-181.

The data in Table 30 show that melt temperature and torque may be used as a part of a closed-loop control strategy to monitor and control the molecular weight of the product polycarbonate produced by the method of the present invention. In the experiment comprised by Examples 164-181 differences in molecular weight that are larger than about 1% can be considered statistically meaningful when this strategy is used to quantify differences in molecular weight produced by mixtures containing different molar ratios of carbonate/bisphenol. The standard deviation observed in these measurements can be considered remarkable considering that these measurements included not only the variability associated with the process itself but also contained the error associated with the evaluation of the molecular weight and residual methyl salicylate content of these samples.

The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood by those skilled in the art that variations and modifications can be effected within the spirit and scope of the invention.

Claims

1. A method for the preparation of polycarbonate, said method comprising extruding in the presence of a transesterification catalyst at one or more temperatures in a temperature range between about 100° C. and about 400° C. a solution comprising a solvent and an oligomeric polycarbonate, said extruding being carried out on an extruder equipped with at least one vent adapted for solvent removal, said oligomeric polycarbonate comprising polycarbonate repeat units derived from at least one dihydroxy aromatic compound, said oligomeric polycarbonate comprising ester substituted phenoxy terminal groups having structure I wherein

R1 is a C1-C20 alkyl group, C4-C20 cycloalkyl group, or C4-C20 aryl group;
R2 is independently each occurrence a halogen atom, cyano group, nitro group, C1-C20 alkyl group, C4-C20 cycloalkyl group, C4-C20 aryl group, C1-C20 alkoxy group, C4-C20 cycloalkoxy group, C4-C20 aryloxy group, C1-C20 alkylthio group, C4-C20 cycloalkylthio group, C4-C20 arylthio group, C1-C20 alkylsulfinyl group, C4-C20 cycloalkylsulfinyl group, C4-C20 arylsulfinyl group, C1-C20 alkylsulfonyl group, C4-C20 cycloalkylsulfonyl group, C4-C20 arylsulfonyl group, C1-C20 alkoxycarbonyl group, C4-C20 cycloalkoxycarbonyl group, C4-C20 aryloxycarbonyl group, C2-C60 alkylamino group, C6-C60 cycloalkylamino group, C5-C60 arylamino group, C1-C40 alkylaminocarbonyl group, C4-C40 cycloalkylaminocarbonyl group, C4-C40 arylaminocarbonyl group, or C1-C20 acylamino group; and b is an integer 0-4.

2. A method according to claim 1 wherein said ester substituted phenoxy terminal groups have structure II

3. A method according to claim 1 wherein said polycarbonate repeat units derived from at least one dihydroxy aromatic compound comprise repeat units having structure III wherein R3-R10 are independently a hydrogen atom, halogen atom, nitro group, cyano group, C1-C20 alkyl group, C4-C20 cycloalkyl group, or C6-C20 aryl group; W is a bond, an oxygen atom, a sulfur atom, a SO2 group, a C1-C20 aliphatic radical, a C6-C20 aromatic radical, a C6-C20 cycloaliphatic radical, or the group wherein R11 and R12 are independently a hydrogen atom, C1-C20 alkyl group, C4-C20 cycloalkyl group, or C4-C20 aryl group; or R11 and R12 together form a C4-C20 cycloaliphatic ring which is optionally substituted by one or more C1-C20 alkyl, C6-C20 aryl, C5-C21 aralkyl, C5-C20 cycloalkyl groups, or a combination thereof.

4. A method according to claim 1 wherein said polycarbonate repeat units derived from at least one dihydroxy aromatic compound comprise repeat units derived from bisphenol A, said bisphenol A derived repeat units having structure IV, and optionally repeat units having structure V

5. A method according to claim 1 wherein said solvent comprises from about 10 to about 99 percent by weight of said solution.

6. A method according to claim 1 wherein said solvent comprises at least one ester substituted phenol having structure VI wherein

R1 is a C1-C20 alkyl group, C4-C20 cycloalkyl group, or C4-C20 aryl group;
R2 is independently at each occurrence a halogen atom, cyano group, nitro group, C1-C20 alkyl group, C4-C20 cycloalkyl group, C4-C20 aryl group, C1-C20 alkoxy group, C4-C20 cycloalkoxy group, C4-C20 aryloxy group, C1-C20 alkylthio group, C4-C20 cycloalkylthio group, C4-C20 arylthio group, C1-C20 alkylsulfinyl group, C4-C20 cycloalkylsulfinyl group, C4-C20 arylsulfinyl group, C1-C20 alkylsulfonyl group, C4-C20 cycloalkylsulfonyl group, C4-C20 arylsulfonyl group, C1-C20 alkoxycarbonyl group, C4-C20 cycloalkoxycarbonyl group, C4-C20 aryloxycarbonyl group, C2-C60 alkylamino group, C6-C60 cycloalkylamino group, C5-C60 arylamino group, C1-C40 alkylaminocarbonyl group, C4-C40 cycloalkylaminocarbonyl group, C4-C40 arylaminocarbonyl group, or C1-C20 acylamino group; and b is an integer 0-4.

7. A method according to claim 6 wherein said solvent further comprises a halogenated aromatic solvent, a halogenated aliphatic solvent, a non-halogenated aromatic solvent, a non-halogenated aliphatic solvent, or a mixture thereof.

8. A method according to claim 1 wherein said solvent comprises methyl salicylate.

9. A method according to claim 8 wherein said solvent further comprises ortho-dichlorobenzene.

10. A method according to claim 1 wherein said transesterification catalyst comprises a quaternary ammonium compound, a quaternary phosphonium compound, or a mixture thereof.

11. A method according to claim 10 wherein said quaternary ammonium compound has structure VII wherein R13-R16 are independently a C1-C20 alkyl group, C4-C20 cycloalkyl group, or a C4-C20 aryl group; and X− is an organic or inorganic anion.

12. A method according to claim 11 wherein said anion is selected from the group consisting of hydroxide, halide, carboxylate, phenoxide, sulfonate, sulfate, carbonate, and bicarbonate.

13. A method according to claim 11 wherein said quaternary ammonium compound is tetramethylammonium hydroxide.

14. A method according to claim 10 wherein said phosphonium compound has structure VIII wherein R17-R20 are independently a C1-C20 alkyl group, C4-C20 cycloalkyl group, or a C4-C20 aryl group; and X− is an organic or inorganic anion.

15. A method according to claim 14 wherein said anion is selected from the group consisting of hydroxide, halide, carboxylate, phenoxide sulfonate, sulfate, carbonate, and bicarbonate.

16. A method according to claim 14 wherein said quaternary phosphonium compound is tetrabutylphosphonium acetate.

17. A method according to claim 10 wherein said transesterification catalyst further comprises at least one alkali metal hydroxide, alkaline earth hydroxide, or mixture thereof.

18. A method according to claim 1 wherein said transesterification catalyst comprises at least one alkali metal hydroxide, at least one alkaline earth hydroxide, or mixture thereof.

19. A method according to claim 18 wherein said alkali metal hydroxide is sodium hydroxide.

20. A method according to claim 1 wherein said transesterification catalyst comprises at least one alkali metal salt of a carboxylic acid, alkaline earth salt of a carboxylic acid, or a mixture thereof.

21. A method according to claim 20 in which said alkali metal salt of a carboxylic acid is Na2Mg EDTA.

22. A method according to claim 1 wherein said transesterification catalyst comprises at least one salt of a non-volatile inorganic acid.

23. A method according to claim 22 wherein said salt of a non-volatile acid is at least one salt selected from the group consisting of NaH2PO3, NaH2PO4, Na2HPO4, KH2PO4, CaH2PO4, Cs2HPO4, NaKHPO4, NaCsHPO4, and KCsHPO4.

24. A method according to claim 1 wherein said transesterification catalyst is present in an amount corresponding to between about 1.0×10−8 and about 1×10−3 moles of transesterification catalyst per mole of polycarbonate repeat units derived from aromatic dihydroxy compound present in the oligomeric polycarbonate.

25. A method according to claim 1 wherein said solution further comprises a monofunctional phenol chainstopper.

26. A method according to claim 25 wherein said chainstopper is p-cumylphenol.

27. A method according to claim 1 wherein said extruder has a screw speed, said solution being introduced into said extruder at a feed rate, said feed rate and said screw speed having a ratio, said extruder being operated such that the ratio of feed rate is pounds per hour to the screw speed expressed in revolutions per minute falls within a range of from about 0.01 to about 100.

28. A method according to claim 27 wherein the screw speed is in a range between about 50 and about 1200 revolutions per minute.

29. A method according to claim 27 wherein said extruder is equipped with at least one vacuum vent.

30. A method according to claim 27 wherein said extruder is selected from the group consisting of a co-rotating intermeshing double screw extruder, a counter-rotating non-intermeshing double screw extruder; a single screw reciprocating extruder, and a single screw non-reciprocating extruder.

31. A method according to claim 1 further comprising the steps of

Step (A) heating the solution comprising the solvent and the oligomeric polycarbonate to a temperature greater than the boiling point of said solvent, said boiling point being the boiling point of said solvent at atmospheric pressure, said heating being carried out at a pressure greater than atmospheric pressure to provide a superheated mixture of oligomeric polycarbonate and solvent; and
Step (B) introducing said superheated mixture of oligomeric polycarbonate and solvent into the extruder through at least one pressure control valve.

32. A method according to claim 31 wherein said extruder is selected from the group consisting of a co-rotating intermeshing double screw extruder, a counter-rotating non-intermeshing double screw extruder, a single screw reciprocating extruder, and a single screw non-reciprocating extruder.

33. A method according to claim 31 wherein said extruder is equipped with at least one vacuum vent and optionally one or more vents operated at about atmospheric pressure, said extruder being equipped with at least one side feeder, said side feeder being equipped with at least one vent, said vent being operated at atmospheric pressure.

34. A method according to claim 33 wherein said extruder is selected from the group consisting of a co-rotating, intermeshing double screw extruder, a counter-rotating, non-intermeshing double screw extruder, a single screw reciprocating extruder, and a single screw non-reciprocating extruder.

35. A method according to claim 1 further comprising removing a product polycarbonate from said extruder.

36. A method according to claim 35 wherein said product polycarbonate is introduced into a second extruder, said second extruder comprising at least one vacuum vent, said second extruder being operated at a temperature in a range between about 100° C. and about 400° C., and a screw speed in a range between about 50 rpm and about 1200 rpm.

37. A method according to claim 36 wherein said second extruder is selected from the group consisting of a co-rotating intermeshing double screw extruder, a counter-rotating non-intermeshing double screw extruder, a single screw reciprocating extruder, and a single screw non-reciprocating extruder.

38. A method for preparing polycarbonate, said method comprising:

Step (I) heating a mixture comprising at least one dihydroxy aromatic compound, an ester substituted diaryl carbonate and a transesterification catalyst at a temperature in a range between about 100° C. and about 300° C. to provide a solution of an oligomeric polycarbonate in an ester substituted phenol solvent; and
Step (II) extruding said solution of oligomeric polycarbonate in said ester substituted phenol at one or more temperatures in a range between about 100° C. and about 400° C., and at one or more screw speeds in a range between about 50 and about 1200 rpm, said extruding being carried out on an extruder comprising at least one vent adapted for solvent removal.

39. A method corresponding to claim 38 wherein in Step (I) the ester substituted diaryl carbonate is employed in an amount corresponding to between about 0.95 and about 1.05 moles per mole of said dihydroxy aromatic compound.

40. A method according to claim 38 wherein said transesterification catalyst is present in an amount corresponding to between about 1.0×10−8 and about 1×10−3 moles of transesterification catalyst per mole of said dihydroxy aromatic compound.

41. A method according to claim 38 wherein said ester-substituted diaryl carbonate has structure IX wherein R1 is independently at each occurrence C1-C20 alkyl group, C4-C20 cycloalkyl group, or C4-C20 aryl group; R2 is independently at each occurrence a halogen atom, cyano group, nitro group, C1-C20 alkyl group, C4-C20 cycloalkyl group, C4-C20 aryl group, C1-C20 alkoxy group, C4-C20 cycloalkoxy group, C4-C20 aryloxy group, C1-C20 alkylthio group, C4-C20 cycloalkylthio group, C4-C20 arylthio group, C1-C20 alkylsulfinyl group, C4-C20 cycloalkylsulfinyl group, C4-C20 arylsulfinyl group, C1-C20 alkylsulfonyl group, C4-C20 cycloalkylsulfonyl group, C4-C20 arylsulfonyl group, C1-C20 alkoxycarbonyl group, C4-C20 cycloalkoxycarbonyl group, C4-C20 aryloxycarbonyl group, C2-C60 alkylamino group, C6-C60 cycloalkylamino group, C5-C60 arylamino group, C1-C40 alkylaminocarbonyl group, C4-C40 cycloalkylaminocarbonyl group, C4-C40 arylaminocarbonyl group, or C1-C20 acylamino group; and b is independently at each occurrence an integer 0-4.

42. A method according to claim 41 wherein said ester substituted diaryl carbonate is bis(methyl salicyl)carbonate.

43. A method according to claim 38 wherein said dihydroxy aromatic compound has structure X wherein R3-R10 are independently a hydrogen atom, halogen atom, nitro group, cyano group, C1-C20 alkyl group, C4-C20 cycloalkyl group, or C6-C20 aryl group; W is a bond, an oxygen atom, a sulfur atom, a SO2 group, a C1-C20 aliphatic radical, a C6-C20 aromatic radical, a C6-C20 cycloaliphatic radical, or the group wherein R11 and R12 are independently a hydrogen atom, C1-C20 alkyl group, C4-C20 cycloalkyl group, or C4-C20 aryl group; or R11 and R12 together form a C4-C20 cycloaliphatic ring which is optionally substituted by one or more C1-C20 alkyl, C6-C20 aryl, C5-C21 aralkyl, C5-C20 cycloalkyl groups, or a combination thereof.

44. A method according to claim 38 wherein said at least one dihydroxy aromatic compound comprises hydroquinone and bisphenol A.

45. A product polycarbonate prepared by the method of claim 44.

46. A molded article comprising the polycarbonate of claim 45.

47. A method according to claim 38 wherein said at least one dihydroxy aromatic compound comprises bisphenol A and 4,4′-sulfonyldiphenol.

48. A product polycarbonate prepared by the method of claim 47.

49. A molded article comprising the polycarbonate of claim 48.

50. A method for preparing polycarbonate, said method comprising:

Step (I) heating a mixture of bisphenol A, bis(methyl salicyl)carbonate and a transesterification catalyst at a temperature in a range between 100° C. and 300° C. a pressure between about 0.1 and about 10 atmospheres to provide a solution of an oligomeric bisphenol A polycarbonate in methyl salicylate, said bis(methyl salicyl)carbonate being present in an amount corresponding to between about 0.95 and about 1.05 moles bis(methylsalicyl)carbonate per mole bisphenol A, said transesterification catalyst being present in an amount corresponding to between 1×10−8 and 1×10−3 moles transesterification catalyst per mole bisphenol A, said oligomeric polycarbonate comprising methoxy carbonyl phenoxy terminal groups; and
Step (II) extruding said solution of oligomeric bisphenol A polycarbonate in methyl salicylate at one or more temperatures in a range between about 100° C. and about 400° C., and at one or more screw seeds in a range between about 50 and about 1200 rpm.

51. A method according to claim 50 wherein the transesterification catalyst comprises tetrabutylphosphonium acetate.

52. A polycarbonate prepared by the method of claim 50, said polycarbonate comprising less than 10 ppm Fries product.

53. A polycarbonate according to claim 50, said polycarbonate having a percent endcapping of about at least 90 percent.

54. A polycarbonate according to claim 50, said polycarbonate having a percent endcapping of about at least 97 percent.

55. A molded article comprising the polycarbonate of claim 50.

56. A molded article according to claim 55 which is an optical disk.

57. A method for the preparation of polycarbonate, said method comprising extruding in the presence of a transesterification catalyst at one or more temperatures in a temperature range between about 100° C. and about 400° C. a solution comprising a solvent and a polycarbonate, said extruding being carried out on an extruder equipped with at least one vent adapted for solvent removal, said polycarbonate comprising polycarbonate repeat units derived from at least one dihydroxy aromatic compound, said polycarbonate comprising ester substituted phenoxy terminal groups having structure I wherein

R1 is a C1-C20 alkyl group, C4-C20 cycloalkyl group, or C4-C20 aryl group;
R2 is independently at each occurrence a halogen atom, cyano group, nitro group, C1-C20 alkyl group, C4-C20 cycloalkyl group, C4-C20 aryl group, C1-C20 alkoxy group, C4-C20 cycloalkoxy group, C4-C20 aryloxy group, C1-C20 alkylthio group, C4-C20 cycloalkylthio group, C4-C20 arylthio group, C1-C20 alkylsulfinyl group, C4-C20 cycloalkylsulfinyl group, C4-C20 arylsulfinyl group, C1-C20 alkylsulfonyl group, C4-C20 cycloalkylsulfonyl group, C4-C20 arylsulfonyl group, C1-C20 alkoxycarbonyl group, C4-C20 cycloalkoxycarbonyl group, C4-C20 aryloxycarbonyl group, C2-C60 alkylamino group, C6-C60 cycloalkylamino group, C5-C60 arylamino group, C1-C40 alkylaminocarbonyl group, C4-C40 cycloalkylaminocarbonyl group, C4-C40 arylaminocarbonyl group, or C1-C20 acylamino group; and b is an integer 0-4.

58. A method according to claim 57 wherein said polycarbonate has a number average molecular weight of at least 5000 daltons.

59. A method of forming a polycarbonate wherein the method comprises,

extruding in the presence of a transesterification catalyst at one or more temperatures in a temperature range between about 100° C. and about 400° C. a solution comprising a solvent and an oligomeric polycarbonate, said extruding being carried out on an extruder equipped with at least one vent adapted for solvent removal, said oligomeric polycarbonate comprising polycarbonate repeat units of structure III:
wherein R3-R10 are independently a hydrogen atom, halogen atom, nitro group, cyano group, C1-C20 alkyl group, C1-C20 cycloalkyl group, or C6-C20 aryl group; and W is a SO2 group,
said oligomeric polycarbonate comprising ester substituted phenoxy terminal groups having structure I
wherein R1 is a C1-C20 alkyl group, C1-C20 cycloalkyl group, or C1-C20 aryl group; R2 is independently at each occurrence a halogen atom, cyano group, nitro group, C1-C20 alkyl group, C1-C20 cycloalkyl group, C4-C20 aryl group, C1-C20 alkoxy group, C1-C20 cycloalkoxy group, C1-C20 aryloxy group, C1-C20 alkylthio group, C1-C20 cycloalkylthio group, C1-C20 arylthio group, C1-C20 alkylsulfinyl group, C4-C20 cycloalkylsulfinyl group, C4-C20 arylsulfinyl group, C1-C20 alkylsulfonyl group, C1-C20 cycloalkylsulfonyl group, C1-C20 arylsulfonyl group, C1-C20 alkoxycarbonyl group, C1-C20 cycloalkoxycarbonyl group, C1-C20 aryloxycarbonyl group, C3-C60 alkylamino group, C6-C60 cycloalkylamino group, C5-C60 arylamino group, C1-C40 alkylaminocarbonyl group, C4-C40 cycloalkylaminocarbonyl group, C4-C40 arylaminocarbonyl group, or C1-C20 acylamino group; and b is an integer 0-4,
said solvent comprising an ester substituted phenol having structure VI,
wherein R1 and R2 are defined above.

60. A method according to claim 59, wherein the repeat units having structure III are compounds of structure V:

61. A method according to claim 59 wherein said polycarbonate repeat units further comprise repeat units derived from bisphenol A, said bisphenol A derived repeat units having structure IV,

62. A method according to claim 61 wherein the repeat units having structure III are compounds of structure V:

63. A method for preparing polycarbonate, said method comprising:

Step (I) heating a mixture comprising a dihydroxy aromatic compound, an ester substituted diaryl carbonate and a transesterification catalyst at a temperature in a range between about 100° C. and about 300° C. to provide a solution of an oligomeric polycarbonate in an ester substituted phenol solvent, wherein the dihydroxy compound has the structure,
wherein R3-R10 are independently a hydrogen atom, halogen atom, nitro group, cyano group, C4-C20 alkyl group, C1-C20 cycloalkyl group, or C6-C20 aryl group; and W is a SO2 group; and
Step (II) extruding said solution of oligomeric polycarbonate in said ester substituted phenol at one or more temperatures in a range between about 100° C. and about 400° C., and at one or more screw speeds in a range between about 50 and about 1200 rpm, said extruding being carried out on an extruder comprising at least one vent adapted for solvent removal.

64. A method according to claim 63, wherein the dihydroxy aromatic compound comprises 4,4′-sulfonyldiphenol.

65. The method of claim 64, wherein the mixture further comprises a second dihydroxy aromatic compound, wherein the second dihydroxy aromatic compound comprises bisphenol A.

66. The method of claim 63, wherein the mixture further comprises a second dihydroxy aromatic compound, wherein the second dihydroxy aromatic compound comprises bisphenol A.

67. A method for preparing polycarbonate, said method comprising:

Step (I) heating a mixture of bisphenol A and 4,4′-sulfonyldiphenol, bis(methyl salicyl)carbonate and a transesterification catalyst at a temperature in a range between 100° C. and 300° C., a pressure between about 0.1 and about 10 atmospheres to provide a solution of an oligomeric bisphenol A and 4,4′-sulfonyldiphenol copolycarbonate in methyl salicylate, said bis(methyl salicyl)carbonate being present in an amount corresponding to between about 0.95 and about 1.05 moles bis(methyl salicyl)carbonate per (mole bisphenol A+mole 4,4′-sulfonyldiphenol), said transesterification catalyst being present in an amount corresponding to between 1×10−8 and 1×10−3 moles transesterification catalyst per (mole bisphenol A+mole 4,4′-sulfonyldiphenol), said oligomeric polycarbonate comprising methoxy carbonyl phenoxy terminal groups; and
Step (II) extruding said solution of oligomeric bisphenol A and 4,4′-sulfonyldiphenol copolycarbonate in methyl salicylate at one or more temperatures in a range between about 100° C. and about 400° C., and at one or more screw speeds in a range between about 50 and about 1200 rpm.

68. A method for the preparation of polycarbonate, said method comprising extruding in the presence of a transesterification catalyst at one or more temperatures in a temperature range between about 100° C. and about 400° C. a solution comprising a solvent and a polycarbonate, said extruding being carried out on an extruder equipped with at least one vent adapted for solvent removal, said polycarbonate comprising polycarbonate repeat units derived from a dihydroxy aromatic compound having the structure,

wherein R3-R10 are independently a hydrogen atom, halogen atom, nitro group, cyano group, C1-C20 alkyl group, C4-C20 cycloalkyl group, or C6-C20 aryl group; and W is a SO2 group; said polycarbonate comprising ester substituted phenoxy terminal groups having structure I,
wherein R1 is a C1-C20 alkyl group, C1-C20 cycloalkyl group, or C1-C20 aryl group; R2 is independently at each occurrence a halogen atom, cyano group, nitro group, C1-C20 alkyl group, C1-C20 cycloalkyl group, C4-C20 aryl group, C1-C20 alkoxy group, C1-C20 cycloalkoxy group, C1-C20 aryloxy group, C1-C20 alkylthio group, C1-C20 cycloalkylthio group, C1-C20 arylthio group, C1-C20 alkylsulfinyl group, C4-C20 cycloalkylsulfinyl group, C4-C20 arylsulfinyl group, C1-C20 alkylsulfonyl group, C1-C20 cycloalkylsulfonyl group, C1-C20 arylsulfonyl group, C1-C20 alkoxycarbonyl group, C4-C20 cycloalkoxycarbonyl group, C4-C20 aryloxycarbonyl group, C2-C60 alkylamino group, C6-C60 cycloalkylamino group, C5-C60 arylamino group, C1-C40 alkylaminocarbonyl group, C4-C40 cycloalkylaminocarbonyl group, C4-C40 arylaminocarbonyl group, or C1-C20 acylamino group; and b is an integer 0-4.

69. A composition comprising:

(a) a polycarbonate comprising repeat units of structure III:
wherein R3-R10 are independently a hydrogen atom, halogen atom, nitro group, cyano group, C1-C20 alkyl group, C4-C20 cycloalkyl group, or C6-C20 aryl group; and W is a SO2 group,
(b) a residue indicative of an ester substituted diaryl carbonate used in a melt transesterification reaction to produce the polycarbonate, wherein the residue indicative of an activated diaryl carbonate is selected from the group consisting of: (i) polymer units within the polycarbonate having the structure,  wherein R1 is a C1-C20 alkyl group, C4-C20 cycloalkyl group, or C4-C20 aryl group; R2 is independently at each occurrence a halogen atom, cyano group, nitro group, C1-C20 alkyl group, C1-C20 cycloalkyl group, C4-C20 aryl group, C1-C20 alkoxy group, C1-C20 cycloalkoxy group, C1-C20 aryloxy group, C1-C20 alkylthio group, C4-C20 cycloalkylthio group, C4-C20 arylthio group, C1-C20 alkylsulfinyl group, C4-C20 cycloalkylsulfinyl group, C4-C20 arylsulfinyl group, C1-C20 alkylsulfonyl group, C4-C20 cycloalkylsulfonyl group, C4-C20 arylsulfonyl group, C1-C20 alkoxycarbonyl group, C4-C20 cycloalkoxycarbonyl group, C4-C20 aryloxycarbonyl group, C2-C60 alkylamino group, C6-C60 cycloalkylamino group, C5-C60 arylamino group, C1-C40 alkylaminocarbonyl group, C4-C40 cycloalkylaminocarbonyl group, C4-C40 arylaminocarbonyl group, or C1-C20 acylamino group; and b is an integer 0-4, (ii) oligomers within the composition with oligomer units having the structure,  wherein R1 and R2 are defined above, (iii) an ester-substituted phenol within the composition having the structure,  wherein R1 and R2 are defined above, and (iv) an ester substituted diaryl carbonate within the composition having the structure,  wherein R1 and R2 are defined above.

70. The composition of claim 69, wherein the repeat units having structure III are compounds of structure V:

71. The composition of claim 70, wherein the polycarbonate further comprises repeat units derived from bisphenol A, said bisphenol A derived repeat units having structure IV,

72. The composition of claim 69, wherein the polycarbonate further comprises repeat units derived from bisphenol A, said bisphenol A derived repeat units having structure IV,

73. The composition of claim 69, wherein residue (iii) is present and is methyl salicylate.

74. The composition of claim 69, wherein residue (iv) is present and is bismethylsalicylcarbonate.

Referenced Cited
U.S. Patent Documents
926206 June 1909 Morse
1260407 March 1918 Lachmann et al.
1897144 February 1933 Prouty
1905458 April 1933 Gaffney
2616563 November 1952 Hebb
2770924 November 1956 Mead et al.
3120432 February 1964 Aldrich
3392513 July 1968 Hedin
3426513 February 1969 Bauer
3485671 December 1969 Stephens
3513642 May 1970 Cornett
3533327 October 1970 Hagerty
3618302 November 1971 Cornett
3771294 November 1973 Ronning
3850816 November 1974 Koch
3953184 April 27, 1976 Stockford et al.
4133658 January 9, 1979 Callewyn
4198290 April 15, 1980 Summers
4201256 May 6, 1980 Truhan
4223748 September 23, 1980 Barendsen
4232487 November 11, 1980 Brown
4234274 November 18, 1980 Hoshall
4246013 January 20, 1981 Truhan et al.
4323668 April 6, 1982 Brunelle
4326864 April 27, 1982 Sittler
4344538 August 17, 1982 Fujisawa et al.
4367665 January 11, 1983 Terpstra et al.
4572726 February 25, 1986 Van Abbema
4576072 March 18, 1986 Terpstra et al.
4581050 April 8, 1986 Krantz
4600410 July 15, 1986 Baillie et al.
4735639 April 5, 1988 Johnstone
4917712 April 17, 1990 Crigler
5080697 January 14, 1992 Finke
5106488 April 21, 1992 Jonasson
5163786 November 17, 1992 Christianson
5254147 October 19, 1993 Finke
5271751 December 21, 1993 Lagler
5606767 March 4, 1997 Crlenjak et al.
5696222 December 9, 1997 Kaneko et al.
6300459 October 9, 2001 Kaneko et al.
6339109 January 15, 2002 Day et al.
6420512 July 16, 2002 McCloskey et al.
6434784 August 20, 2002 Wisser
6471751 October 29, 2002 Semanderes et al.
6506781 January 14, 2003 Cobb et al.
Foreign Patent Documents
0738579 October 1996 EP
0976772 February 2000 EP
980861 February 2000 EP
1114841 July 2001 EP
1191049 March 2002 EP
WO 02060855 August 2002 WO
Patent History
Patent number: RE40697
Type: Grant
Filed: Jan 31, 2006
Date of Patent: Apr 7, 2009
Assignee: Sabic Innovative Plastics IP B.V. (Bergen Op Zoom)
Inventors: Norberto Silvi (Clifton Park, NY), Mark Howard Giammattei (Selkirk, NY), Patrick Joseph McCloskey (Watervliet, NY), Alberto Nisoli (Albany, NY), James Day (West Palm Beach, FL), Narayan Ramesh (Evansville, IN), Paul Michael Smigelski, Jr. (Schenectady, NY), Paul Russell Wilson (Latham, NY)
Primary Examiner: Terressa Boykin
Attorney: Marina Larson & Associates, LLC
Application Number: 11/345,691