Abstract: A bactericidal composition comprising inorganic fillers having modified surface with submicrometric particles of a metal and/or salts thereof. Use of the composition in the preparation of latex paints, solvent based paints, powder paints, plasterings, putties, pre-dosed renderings and hydrophobic mass additives.

Abstract: Coatings including pigments comprising substrate particles with ultrafine metal oxide particles deposited on the surfaces thereof and made by a plasma process are disclosed. The substrate particles may comprise an oxide such as SiO2, Al2O3, Bi2O3 and the like. The ultrafine metal oxide particles may be partially oxidized such as Cu2O, Ti3O4 and the like. The pigments may be used in coating compositions in which the substrate particles substantially match the refractive index of the coating composition base, and the ultrafine metal oxide particles provide the desired reflectance characteristics for the coating.

Abstract: An aqueous pigment dispersion is produced by ultrafinely dispersing a pigment dispersion mixture, which has been obtained by mixing at least a pigment and a dispersant in an aqueous medium, with microbeads having diameters of not smaller than 0.02 mm but smaller than 0.2 mm. A color composition for a color filter is produced by dispersing a mixture of a pigment, a dispersant, a resin varnish and a solvent with the microbeads in a mill.

Abstract: The present invention provides a manufactured aggregate material that converts waste materials and/or recyclable materials into construction material. By mixing waste materials with an acid solution and a metal oxide solution, any harmful contaminates in the waste materials are encapsulated and rendered into hard pellets that are suitable for use in conglomerates or composites such as concrete. The manufactured aggregate material may be adjusted for moisture content, density, heat capacity, and other parameters.

Abstract: A process for preparing a polymer powder by evaporating the volatile constituents from an aqueous dispersion of a film-forming polymer P, wherein prior to the evaporation of the volatile constituents the aqueous polymer dispersion still comprises drying assistants T, present in an amount of from 0.1 to 80% by weight, based on the polymer P of the dispersion, and there being used as drying assistant T polyvinylformamide. The polyvinylformamide used preferably has a K value (KW), determined by the method of Fikentscher in accordance with DIN 53726, of from 5 to 50.

Abstract: The present invention provides a transparent inorganic oxide dispersion which makes it possible to improve the refractive index and mechanical characteristics and to maintain transparency by modifying the surface of inorganic oxide particles with a surface modifier having one or more reactive functional groups; and an inorganic oxide particle-containing resin composition in which the transparent inorganic oxide dispersion and a resin are compositely integrated by the polymerization reaction, a composition for sealing a light emitting element, a light emitting element, and a method for producing an inorganic oxide particle-containing resin composition; and a hard coat film which has high transparency and makes it possible to improve a refractive index and tenacity, an optical functional film, an optical lens and an optical component.

Abstract: A process for producing nanoparticles incorporating ions selected from groups 13, 16, and 11 or 12 of the periodic table, and materials produced by the process. In an embodiment, the process includes effecting conversion of a nanoparticle precursor composition comprising group 13, 16, and 11 or 12 ions to the material of the nanoparticles in the presence of a selenol compound. Other embodiments include a process for fabricating a thin film including nanoparticles incorporating ions selected from groups 13, 16, and 11 or 12 of the periodic table as well as a process for producing a printable ink formulation including the nanoparticles.

Abstract: A color filter composition comprises a mixture of a binder and a monomer in a predetermined ratio, a pigment, and a solvent. The predetermined ratio is a ratio of the binder to the monomer and ranges from about 50:50 to about 60:40. The color filter composition further comprises a solid powder having a weight percent in the color filter composition ranging from about 12% to about 18%, wherein the solid powder includes the pigment. The pigment has a weight percent in the solid powder ranging from about 28% to about 38%.

Abstract: A low emissive camouflage flake including a metal layer having thermal reflective properties in, at least one side of the metal layer is coated with a colored coating having thermal transparency properties. A method for manufacturing low emissive camouflage flakes. A skin camouflage for providing visual and thermal camouflage to a user thereof. A method for manufacturing a skin camouflage for providing visual and thermal camouflage to a user thereof. A camouflage paint for providing visual and thermal camouflage to an object on which the paint is applied. A method for manufacturing a camouflage paint for providing visual and thermal camouflage to an object on which the paint is applied.

Abstract: A corrosion inhibiting pigment includes nanoscale reservoirs (nanoreservoirs) of corrosion inhibitor for active corrosion protection of metallic products and structures, wherein the nanoreservoirs include a polymer or polyelectrolyte shell which is sensitive to a specific trigger and capable of releasing the inhibitor after action of the trigger. An anti-corrosive coating with self-healing properties includes the pigment, methods for preparing the pigment, in particular by layer-by-layer deposition, as well as methods of use of the pigment.

Abstract: A surface coating composition which exhibits low solar absorption and preferential emission at wavelengths corresponding to atmospheric windows in the infra-red regions is provided by the addition of microspheres to a composition containing a solar reflective pigment.

Abstract: A particulate metal oxide having the mean length of the primary particles in the range from 50 to 90 nm, the mean width of the primary particles in the range from 5 to 20 nm, and the median volume particle diameter of the secondary particles is less than 45 nm. The metal oxide can be used in a sunscreen product that exhibits both effective UV protection and improved transparency.

Abstract: The present invention relates to the use of nanoparticles for the preparation of water-based dispersion adhesives, and especially the use of finely divided barium sulfate therein. The nanoparticles can be used with or without chemical modification. Adhesives of this kind feature improved properties, examples being improved cohesion in conjunction with comparable adhesion and higher heat resistance. Preference is given to dispersion adhesives based on polyacrylate, polyurethane, and epoxy resin.

Abstract: The invention relates to a metallic effect pigment, which metallic effect pigment has a substantially homogeneous chemical composition comprising at least one metal M and having an average content of oxygen of from 25 to 58 atomic percent, based on the total content of M and oxygen. The invention further relates to a method for the production of said metallic effect pigment.

Abstract: The present invention relates to compositions for functional films, and more particularly to compositions for functional films such as a heat ray screening film compatible with hydrolic or alcoholic and anti-hydrolic resin binder, a near infrared screening film, a chrominance correcting film, a conductive film, a magnetic film, a ferromagnetic film, a dielectric film, a ferroelectric film, an electrochromic film, an electroluminescence film, an insulating film, a reflecting film, a reflection preventing film, a catalyst film, a photocatalyst film, a light selectively absorbing film, a hard film, and a heat resisting film, films formed therefrom, and a method of forming the compositions and the films.

Abstract: Solid, low dust pigment compositions are formed i by mixing pigments with certain polymer stabilizers under conditions wherein the stabilizers are in a liquefied state. The pigment compositions are easily handled and have a high color yield when incorporated into polymer substrates. In many cases, the color development attained is not readily achievable using pigment compositions comprising conventional carriers.

Abstract: The present invention is directed to the provision of premixed aqueous compositions which are used to provide a paint composition of varying finish characteristics at the point of sale. Thus, the merchant distributing the paint composition made from the subject premixed compositions need only maintain inventory of four compositions. The particular compositions which are the subject of the invention exhibit stable characteristics during storage in their respective reservoirs. The compositions include a pigment composition, a dispersant thickening agent, a high resin content binder, and a low resin content binder. The compositions are combined in differing amounts to produce paint compositions being suitable for either interior or exterior use and having differing sheens, quality levels, and color bases.

Abstract: The invention submitted concerns anticorrosive pigments of aluminum orthophosphate, their application as anticorrosive pigments in coating agents, as well as a method for their manufacturing.

Abstract: The present invention includes a paint or coating composition comprising an organic pigment or dye complexed to the surface of a layered or fibrous inorganic clay. A wide variety of paint colors can be obtained by varying the pH during the preparation as well as by varying the synthesis conditions and changing particle size of the clay. The paint has unprecedented stability.

Abstract: The present invention includes a paint or coating composition comprising an organic pigment or dye complexed to the surface of a layered or fibrous inorganic clay. A wide variety of paint colors can be obtained by varying the pH during the preparation as well as by varying the synthesis conditions and changing particle size of the clay.

Abstract: Metal oxide particle agglomerates prepared by adding an aluminum phosphate agglomerating agent with mixing to an aqueous dispersion of metal oxide nanoparticles to form an aqueous homogeneous dispersion of nanoparticles and agglomerating agent and then adjusting the pH of the dispersion with mixing to about 3.5 to about 6.5 to produce the particle agglomerates and use of the particle agglomerates to prepare ink receptive coatings, as catalysts, as reinforcing fillers, as polishing abrasives and as flattening agents.

Abstract: A composition includes a compound selected from the group consisting of formula (I), (III), and (IV). The compound of formula (I) is: wherein A is N, C, or S; the A-R5 bond is a single bond or a double bond; R1 is H, —NH2, or —S-aryl; R2 is H or together with R3 form a fused bicyclic group; R3 is H, or together with R2 form a fused bicyclic group, or together with R4 and R5 form a fused tricyclic group; R4 is H, or together with R3 and R5 form a fused tricyclic group, or R5 is H, O, or together with R3 and R4 form a fused tricyclic group; R6 is H, OH, —NH-alkyl, or —NH-aryl; R7 is H; R8 is H, —O-aryl, or halogen; and R9 is H, NH2, —NH-alkyl, —NH-aryl, OH, or —S-aryl.

Abstract: Disclosed are a process for producing a suspension of hydrophobic oxidic particles which has a defined, adjustable viscosity, which comprises suspending low structured hydrophobic oxidic particles in at least one organic suspension agent and then adding from 0.05% to 15% by weight based on the suspension medium of high structured hydrophobic oxidic particles, a suspension of hydrophobic oxidic particles which has a defined, adjustable viscosity and the use thereof for producing soil and water repellent coatings on articles.

Abstract: Dental composite filler materials comprise particles coated via an atomic layer deposition (ALD) process. The coating material has a different composition than the core particle. The difference in composition permits fine control over the refractive index of the coated particles, allowing good matching tooth enamel and to the binder materials used in the composite.

Abstract: The present invention relates to inkjet ink pigments having surface counter-ions replaced with other counter-ions with larger size and/or hydrophobicity. The effect of the replacement is to decrease pigment-ink-vehicle-separation in the inkjet ink printing process.

Abstract: A dispersion containing zinc oxide particles having a dispersion particle size of (i) median volume particle diameter in the range from 70 to 130 nm, (ii) less than 16% by volume of particles having a volume diameter of less than 35 nm below the median volume particle diameter, and (iii) more than 84% by volume of particles having a volume diameter of less than 57 nm above the median volume particle diameter. The zinc oxide dispersion can be used in a sunscreen product that exhibits both effective UV protection and improved transparency. The zinc oxide is particularly suitable for use in combination with transparent titanium dioxide.

Abstract: A liquid coating material in the form of a water-in-oil dispersion which is curable with actinic radiation, is substantially or completely free from organic solvents and has a pH<5, comprising (A) at least one constituent selected from the group consisting of low molecular mass, oligomeric, and polymeric organic compounds which contain at least one group which can be activated with actinic radiation, and also air-drying and oxidatively drying alkyd resins, (B) at least one acidic ester of polyphosphoric acid and at least one compound (b1) containing at least one hydroxyl group and at least one group which can be activated with actinic radiation, (C) at least one acidic ester of monophosphoric acid and at least one compound (c1) containing at least one hydroxyl group and at least one group which can be activated with actinic radiation, and (D) at least one acidic, corrosion-inhibiting pigment based on polyphosphoric acid; process for its preparation, and its use as a coil coating primer.

Abstract: A pearlescent pigment, wherein the pigment is an inorganic material and the color of a homogeneous coating of the pigment, measured over a white background, is selected from the group consisting of: a CIELAB L* value of about 30 or less and a chroma value of about 3 or less; a CIELAB hue angle, hab, from about 50 to about 80 degrees, wherein L* is not more than about 85, and the chroma value is greater than 22; a CIELAB hue angle, hab, from about 80 to about 275 degrees, wherein L* is not more than about 80, and the chroma value is greater than about 10; and a CIELAB hue angle, hab, from not less than about 275 to not more than about 50 degrees, wherein L* is not more than about 85, and the chroma value is greater than about 9. The pigments may be used in a variety of applications including cosmetics, plastics, automotive, or architectural coatings.

Abstract: The present invention provides a dye loaded zeolite material comprising: a) at least one zeolite crystal having straight through uniform channels each having a channel axis parallel to, and a channel width transverse to, a c-axis of crystal unit cells; b) closure molecules having an elongated shape and consisting of a head moiety and a tail moiety, the tail moiety having a longitudinal extension of more than a dimension of the crystal unit cells along the c-axis and the head moiety having a lateral extension that is larger than said channel width and will prevent said head moiety from penetrating into a channel; c) a channel being terminated, in generally plug-like manner, at least at one end thereof located at a surface of the zeolite crystal by a closure molecule hose tail moiety penetrates into said channel and whose head moiety substantially occludes said channel end while projecting over said surface; and d) an essentially linear arrangement of luminescent dye molecules enclosed within a terminated chann

Abstract: Disclosed herein is a method of calcining particulate material, such as kaolin. The method comprises providing a feed mixture comprising a particulate material, such as hydrous kaolin, wherein at least a portion of the particulate feed is coated with a liquid fuel. The method further comprises heating the particulate feed mixture to calcine the particulate feed and burn the liquid fuel to form a calcined product. The liquid fuel coating can act as a secondary, indirect heat source for calcining. The overall calcining temperatures and/or times can be reduced as a result of adding the liquid fuel.

Abstract: A photocurable ink for ink-jet printing, including: a photopolymerizable compound; a pigment; and a dispersing agent, wherein the photopolymerizable compound is a radical polymerizable compound; an amine value of the pigment (AMp) is larger than an acid value of the pigment (ACp); and an acid value of the dispersing agent (ACd) is larger than an amine value of the dispersing agent (AMd).

Abstract: The invention submitted concerns anticorrosive pigments of aluminum orthophosphate, their application as anticorrosive pigments in coating agents, as well as a method for their manufacturing.

Abstract: Goniochromatic luster pigments comprising at least one dielectric low-refractive interference-colored layer which includes a polar organic solvent which can interact with the layer material via functional groups.

Abstract: Various systems and methods are provided for the conditioning and/or colorization of a coating. In one embodiment, a packet is provided that is constructed from a material dissolvable in the coating. The packet contains a quantity of dry powder substance, the dry powder substance being pretreated to disperse in the coating. The quantity of the dry powder substance in the packet imparts a predefined quality to a predefined volume of the coating when the packet is added to the predefined volume of the coating, the integrity of the packet is compromised by at least partial dissolution so that the dry powder substance is released, and the dry powder substance is substantially dispersed in the coating.

Abstract: The present invention relates to nano sized sulfide compounds of cerium and a process for the preparation thereof. More particularly, the present invention provides novel nano sized particles of cerium sulfide as well as a novel process for the preparation of nano sized sulfide compounds of cerium by the bioreduction of cerium sulfate or cerium acetate, without resorting to chemical methods. A bioprocess is disclosed to treat trivalent Cerium salt with sulfate-reducing bacteria (SRB) under controlled conditions to obtain a biomass, which is subjected to staggered heating upto a temperature of 600-1500° C. The sulfide of Cerium is finally separated for application in pigment industry.

Abstract: A pure pearl powder preparation method of preparing a pure pearl powder by: (a) preparing pearl and washing the prepared pearl to remove sands and other, and then infusing the washed pearl in milk/soybean milk till that the milk/soybean milk becomes rancid, (b) washing the pearl with water to remove foul smell from the pearl, and then drying the pearl, and crushing the pearl into a superfine pearl powder, and (c) mixing the superfine pearl powder thus obtained with water in a high-speed mixer to form a pearl powder suspension, and then drawing the pearl powder suspension out of the mixer through a sieve over 100 mesh, and then drying the collected pearl powder suspension at low temperature to obtain the desired pure pearl powder.

Abstract: Methods for the preparation of inorganic nanoparticles capable of fluorescence, wherein the nanoparticles consist of a host material that comprises at least one dopant. The synthesis of the invention in organic solvents allows to gain a considerably higher yield compared to the prior art synthesis in water. All kinds of objects can advantageously be marked and reliably authenticated by using an automated method on the basis of a characteristic emission. Further, the size distribution of the prepared nanoparticles is nartower which renders a subsequent size-selected separation process superfluous.

Abstract: A curable film-forming composition is provided comprising (i) 10 to 90 percent by weight based on the total weight of resin solids in the film-forming composition of a crosslinking agent; (ii) 10 to 90 percent by weight of a polymer containing a plurality of functional groups reactive with the crosslinking agent; and (iii) 5 to 85 percent by volume of particles having a mean particle size less than 100 nm. The particles comprise 1 to 99 percent by weight of at least one metal oxide wherein the metal is selected from zinc, titanium, cerium, manganese, bismuth, copper, zirconium and iron. A multi-component composite coating composition is also provided, comprising a pigmented basecoat and a clear coat. The basecoat and/or clearcoat may be derived from the curable film-forming composition described above. Also provided are coated substrates in which the curable coating compositions or the multi-component composite coating compositions described above are applied to a substrate and cured to form a cured coating.

Abstract: A particulate metal oxide having the mean length of the primary particles in the range from 50 to 90 nm, the mean width of the primary particles in the range from 5 to 20 nm, and the median volume particle diameter of the secondary particles is less than 45 nm. The metal oxide can be used in a sunscreen product that exhibits both effective UV protection and improved transparency.

Abstract: A liquid composition, active curing additive for water or solvent borne surface coatings and sealants such: latex products, paints, putties, caulks, sports track and court construction, asphalt or coal tar seal coating, asphalt paving, micro-seal, roof tars, asphalt emulsions, crack sealants, and the like is provided. The additive functions to significantly reduce the amount of time required for the surface coating to cure and thereby allows the coated or sealed surface to be quickly returned to service. Preferably, the additive is composed of a composition of water; calcium chloride granules; citric acid granules; and an ammonium dispersing composition. Alternatively, aluminum sulfate may be utilized in place of calcium chloriade and citric acid.

Abstract: A process for preparing a modified pigment having attached at least one organic group is described. This process comprises the step of reacting a dried mixture comprising a pigment having attached at least one reactive group and a modifying agent. The dried mixture is reacted under high intensity mixing conditions for a time and temperature sufficient to form the modified pigment.

Abstract: A flaky pigment excellent in leafing properties and in adhesion between pigment particles and a coating (resin) was obtained by coating the surface of a flaky pigment with a coupling agent and a phosphate having a perfluoroalkly group or a silane compound. Accordingly, the flaky pigment is excellent as a pigment for coating or printing ink of which brightness and durability are required.

Abstract: Presented are methods for reducing energy consumption by coating external vertical walls of a building with a wall paint comprising reflective metal oxide pigments. Methods for painting external vertical walls as well as compositions comprising base paint combined with reflective metal oxide pigments are also presented.

Abstract: Described herein are embedded pigments consisting of a labile chromophore englobed in a coating of refractory and transparent material formed by nanomolecular particles, also described are oxides of refractory and transparent materials in the form of nanoparticles and their use for coating labile chromophores or ceramic surfaces.

Abstract: A particulate metal oxide having a mean length of the primary particles in the range from 50 to 90 nm, the mean width of the primary particles in the range from 5 to 20 nm, and the median volume particle diameter of the secondary particles is less than 45 nm. The metal oxide can be used in a sunscreen product that exhibits both effective UV protection and improved transparency.

Abstract: The present invention includes a paint or coating composition comprising an organic pigment or dye complexed to the surface of a layered or fibrous inorganic clay. A wide variety of paint colors can be obtained by varying the pH during the preparation as well as by varying the synthesis conditions and changing particle size of the clay. The paint has unprecedented stability.

Abstract: A body pigment with a good skin feel for cosmetics is provided which has an appropriate crumbling property and combines slipping property and adhesiveness without compromising oil absorption. The body pigment is comprised of a metal-containing compound and has a structure in which leaf-shaped flakes are combined and/or intersected.

Abstract: The invention relates to a non-dusting homogeneous pigment preparation notable in that it comprises at least 40% by weight of one or more effect pigments, from 0.5 to 50% by weight of water and/or an organic solvent or solvent mixture and from 0.5 to 59.5% by weight of a styrene-modified polyacrylate resin having an acid number >90 mg KOH/g, and to its use to produce dry preparations.

Abstract: A pigment dispersion liquid comprises pigment particles dispersed in a dispersion medium, the difference (D90?D10) between D90 and D10 being not more than 25 nm, wherein D90 and D10 represent the primary particle size that the pigment particles having a primary particle size up to and including D90 account for 90% by number of the total pigment particles, and the particle size that the pigment particles having a primary particle size up to and including D10 account for 10% by number of the total pigment particles, respectively, in the integral of the primary particle size distribution function dG=f(D)dD of the pigment particles in which G is a particle number (%) and D is a primary particle size (nm).

Abstract: The present invention provides a dye loaded zeolite material comprising: a) at least one zeolite crystal having straight through uniform channels each having a channel axis parallel to, and a channel width transverse to, a c-axis of crystal unit cells; b) closure molecules having an elongated shape and consisting of a head moiety and a tail moiety, the tail moiety having a longitudinal extension of more than a dimension of the crystal unit cells along the c-axis and the head moiety having a lateral extension that is larger than said channel width and will prevent said head moiety from penetrating into a channel; c) a channel being terminated, in generally plug-like manner, at least at one end thereof located at a surface of the zeolite crystal by a closure molecule hose tail moiety penetrates into said chanel and whose head moiety substantially occludes said channel end while projecting over said surface; and d) an essentially linear arrangement of luminescent dye molecules enclosed within a terminated channe